Abstract
Large-area, pinhole-free CH3NH3PbI3 perovskite thin films were successfully fabricated on 5 cm × 5 cm flexible indium tin oxide coated polyethylene naphthalate (ITO-PEN) substrates through a sequential evaporation/spin-coating deposition method in this research. The influence of the rate-controlled evaporation of PbI2 films on the quality of the perovskite layer and the final performance of the planar-structured perovskite solar cells were investigated. An ultrafast evaporation rate of 20 Å s−1 was found to be most beneficial for the conversion of PbI2 to CH3NH3PbI3 perovskite. Based on this high-quality CH3NH3PbI3 film, a resultant flexible perovskite solar sub-module (active area of 16 cm2) with a power conversion efficiency of more than 8% and a 1.2 cm2 flexible perovskite solar cell with a power conversion efficiency of 12.7% were obtained.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Introduction
Flexible, lightweight photovoltaic devices can be employed in numerous emerging areas, such as bendable displays, conformable sensors, biodegradable electronic devices, portable electronic chargers and wearable electronic textiles, thus attracting considerable attention from both research institutes and industries1. Among all the traditional and new-generation photovoltaic technologies, perovskite solar cells containing metal halide perovskite materials as an absorber have exhibited advantages that include high efficiency, low cost and low-temperature fabrication, which can guarantee the compatibility with most flexible substrates and practical applications2,3,4.
Currently, the certified power conversion efficiency (PCE) records of perovskite solar cells on rigid substrate can achieve over 22% with an area of 0.1 cm2, 19.7% with an area of 1 cm2 and 12.1% with an area of 36.1 cm2 (module), respectively5,6. Flexible perovskite solar cells (F-PSCs) can also reach PCE over 18% in an area of 0.1 cm2 7. However, most studies on F-PSCs are based on a typical size of approximately only 0.1 cm2. The PCEs of large-area flexible perovskite solar cells, especially flexible perovskite solar modules, still lag behind those of small-area devices8,9,10. Therefore, fabricating an efficient F-PSC with a reasonable size, for example, not less than 5 cm × 5 cm, is essential for enabling PSCs to become commercially available. In all steps of F-PSC module/sub-module fabrication, preparing pinhole-free, uniform perovskite films with large areas and high reproducibility is the most important challenge. This is because either the widely used metal halide predecessor PbI2 or the resultant perovskite materials, such as CH3NH3PbI3 (MAPbI3), demonstrate specific solution crystallization processes in which the nucleation rates do not match the crystallization rates11. Various modified spin-coating techniques, such as “gas-assisted nucleation”12, “solvent engineering”13, and “vacuum flashing”14 methods have been invented to form homogenous perovskite films directly from the perovskite precursor solution for application in small-area devices. However, the possibility to scale up these methods remains questionable because of the complexity of processing. In the case of methods involving the vapor phase, Liu et al. demonstrated that a homogeneous perovskite film could be obtained from dual-source evaporation, giving a high PCE of 15.4% in the corresponding device15. Unfortunately, this promising approach faced problems of a high vapor pressure and easy decomposition of the organic salt caused by the control of CH3NH3I (MAI). Fu et al. employed a hybrid sequential deposition method with evaporated PbI2 and a CH3NH3I solution16, yielding a semi-transparent solar cell with a steady-state efficiency of 14.2% along with a 72% average transmittance in the near-infrared region, which ensures that this strategy has a good prospect.
Herein, a hybrid sequential deposition method was adopted to fabricate module-sized perovskite films on flexible substrates. The effects of the PbI2 deposition rates on the quality of the perovskite films and device performance were investigated. At an ultrafast rate of 20 Å s−1, large-area flexible perovskite solar cells with an active area of 1.2 cm2 were prepared that achieved an efficiency of 12.7%. In addition, a flexible perovskite solar module with an active area of 16 cm2 on a 25 cm2 ITO-PEN substrate exhibited a PCE of more than 8%. Combining the merits of the low cost, short processing time, full coverage of the substrate, and high module performance, the PbI2 film fabricated via ultrafast thermal evaporation holds promise for facilitating the development of industrial-scale perovskite solar cells.
Results
In this research, fullerene C60 was selected as an electron transport material (ETL) and first evaporated onto a indium tin oxide-coated polyethylene naphthalate (ITO-PEN) flexible substrate17. Then, PbI2 was evaporated on this amorphous C60 layer at various controlled deposition rates within the range of 0.5 Å s−1 to 40 Å s−1, which could be easily adjusted by controlling the evaporation source temperature. Using this thermal evaporation method, a uniform PbI2 layer with a precisely controllable amount over a large area could be deposited.
Under the naked eyes, all these evaporated PbI2 films exhibit a uniform color and an ultrasmooth surface (see Fig. S1 in the supplementary information). However, under scanning electron microscopy (SEM), the microscopic morphologies of the PbI2 films vary slightly for the different evaporation rates. It has been reported that the structural properties of evaporated PbI2 thin films can be adjusted by varying the deposition conditions, such as the substrate materials, substrate temperature and evaporation rates18,19,20. To impart more significant differences in the PbI2 films and in the subsequent perovskite films and devices, the deposition rates were fixed at 0.5 Å s−1 (R1), 20 Å s−1 (R2) and 40 Å s−1 (R3) for detailed investigation. Figure 1(a–c) shows the surface morphologies of the thermally evaporated PbI2 films at deposition rates of R1, R2 and R3. The PbI2 film prepared with a deposition rate of 0.5 Å s−1 is smooth, compact and nearly free of pinholes, as shown in Fig. 1(a). In addition, at the rate of 20 Å s−1, the PbI2 film is still smooth but less compact. A porous surface and some pinholes can be seen in Fig. 1(b). When the deposition rate increased to 40 Å s−1, the film became rough, and many PbI2 nanoplates formed on the top surface, as shown in Fig. 1(c), which is similar to the morphology of the crystallized substrate15. These nanoplates are randomly arranged perpendicular to the substrate, which can create a large degree of porosity.
X-ray diffraction measurement (XRD) was employed to further investigate the microstructure of the PbI2 films. As shown in Fig. 1(d), all the evaporated PbI2 layers demonstrate a preferential (001) orientation compared with the raw PbI2 powder (R0). In the magnified XRD patterns, as the deposition rate rising up, the full width at half maximum (FWHM) of the peak increases slightly. To give a quantitative analysis, the average crystalline sizes of the PbI2 films were calculated by the Scherer equation using the (001) diffraction peak through the formula reported elsewhere and shown in Supplementary Table S1. Clearly, these calculated values of crystalline sizes are smaller than the submicron-scaled grain sizes observed from the SEM images19. The PbI2 film deposited at a rate of R1 has the smallest (001) FWHM, meaning it has the largest crystalline size, which forms the most compact layer in Fig. 1(a). Compared with the R1-based sample, the R2-based sample has more pores in the thin film. However, upon further increasing the deposition rate to R3, a rough surface is formed. In brief, by varying the deposition rate, the morphology and microstructure of the PbI2 film can be controlled in this work. Moreover, higher deposition rates correspond to shorter deposition times, which is good for manufacturing.
To understand the transformation from PbI2 to MAPbI3 perovskite, the deposition-rate-dependent PbI2 films with different porosities were then transformed to perovskite films by spin-coating the MAI solution and annealing21,22. It has been demonstrated that perovskite films fabricated on an amorphous substrate, such as the [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) layer, obtained by here described always contain residual PbI2 16,23. However, the performance of the final device can still be efficient if the amount of residue is controlled14. Figure 2(a–c) shows the XRD patterns of the different perovskite films. The PbI2 peaks at 12.7° indicate the incomplete conversion from PbI2 to MAPbI3, which causes variations in the stoichiometry of the resultant films. It was reported that the penetration depth of CH3NH3I into a compact PbI2 layer is limited to a few tens of nanometer from the surface24,25,26. For the low deposition rate of R1, a distinct peak for PbI2 can be seen in Fig. 2(a), which is ascribed to the inhibition of MAI diffusion caused by the formation of a compact MAPbI3 perovskite film on the PbI2 surface. At the rate of R2, the fabricated film shows a strong perovskite peak with the weakest peak for PbI2 among the three samples. It is assumed that the pores on the surface of the PbI2 film facilitate the permeation of MAI, which is beneficial for the conversion of PbI2 to perovskite. Figure 2(e) shows that a uniform perovskite film without pinholes is formed across the entire SEM image of the top surface. In contrast, the R3-based film shows an obvious residual PbI2 XRD peak that is even stronger than the perovskite peak, as illustrated in Fig. 2(c). Thus, a high-quality perovskite film could be fabricated by controlling the deposition rate of PbI2 at R2.
As the key material in perovskite solar cells, the perovskite films fabricated with different PbI2 deposition rates also have an important influence on the final photovoltaic performance. We first verified the principle of fabricating planar PSCs on a rigid substrate with the structure glass/ITO/C60/perovskite/spiro-OMeTAD/MoO3/Au27. The details of the fabrication process are described in the methods section. Except for the different deposition rates of PbI2 films, the other conditions were kept the same for all cells. The photovoltaic performance of the PSCs based on different deposition rates of PbI2 were measured under AM 1.5 G (100 mW cm−2) light illumination with a metal mask of 0.16 cm2, and illustrated in Fig. 3(a–d). The evolution of the device performance is consistent with the trends in the film and crystal quality observed from the SEM and XRD data. Compared with the devices fabricated at R1, all the photovoltaic parameters increased for the devices based on the R2 film due to the improved conversion to perovskite. This result is consistent with research from other groups, where the optimized performance was obtained for a higher PbI2 deposition rate28. However, when the deposition rate increased to 40 Å s−1, the device PCE decreased due to the presence of more unreacted PbI2 in the perovskite film. In contrast, the samples fabricated from the R1- and R3-based films exhibit smaller J sc values and lower FFs, which is caused by the less complete transfer reaction from PbI2 to perovskite. The presence of a small amount of residual PbI2 is observed in many of the high-efficiency devices reported in the literature. Beneficial effects such as grain boundary passivation and hole-blocking effects have been proposed29,30. The J-V characteristics deliver a short-circuit current density (J sc ) of 19.8 mA cm−2, an open circuit voltage (V oc ) of 1.00 V, a fill factor (FF) of 0.76 and an efficiency of 15.04% for the device fabricated from the film prepared at a 20 Å s−1 deposition rate of PbI2. With the high-quality perovskite thin film, small-area devices using the optimized method show an average PCE of 13.7% ± 0.7%. It has been reported that planar perovskite solar cells are more susceptible to the hysteresis effect31,32. Thus, the perovskite solar cells based on the R2 deposition rate were measured under both reverse and forward scans and exhibited an almost negative hysteresis.
(a) Statistical distributions of V oc , J sc , FF and the corresponding PCE of the different groups of perovskite solar cells; the device photovoltaic parameters were determined from reverse scanning. Each group consists of 15 cells. (e) J-V curves of the devices fabricated from the films prepared at different PbI2 deposition rates. (f) Device performance distribution for 60 devices in three batches.
Considering that the materials and techniques used above are all processed at low temperature (not higher than 150 °C), we directly applied these techniques to an ITO-PEN substrate without any modification. The photovoltaic characteristics of the flexible MAPbI3 devices with the above-optimized fabrication parameters and the same measurement conditions are shown in Fig. 4(a) and summarized in Table 1. The small-area flexible device shows PCEs of 13.9% under the reverse scan (V oc to J sc ) and 13.8% under the forward scan (J sc to V oc ). The inset of Fig. 4(a) shows a corresponding steady-state efficiency of 14.0% at a bias close to the initial maximum power point of 0.81 V. During a 60 second illumination period, the unencapsulated device shows a stable photocurrent density and PCE as a function of time. Figure 4(b) shows a typical external quantum efficiency curve (EQE) of the device. The integrated short-circuit current density is 18.5 mA cm−2 under the AM 1.5 G spectrum, which matches well with the J-V results. Upscaling the fabrication process, large area flexible device with an active area of 1.2 cm2 can be obtained as in Fig. 4(d). It shows a V oc of 1.02 V, a J sc of 18.4 mA cm−2, an FF of 0.68 and thus a PCE of 12.8% under the reverse scan. And under the forward scan, the device shows a V oc of 1.02 V, a J sc of 18.6 mA cm−2, an FF of 0.66 and thus a PCE of 12.5%. The EQE spectra at three spots located at the center and two corners of the device were measured and show small variations in the J sc , as shown in Fig. 4(e), which provides evidence for the uniformity of the perovskite film over a large area. Compared with the small-area device, an increase in the active area from 0.16 cm2 to 1.2 cm2 resulted in a 4% lower FF, which we ascribe to the series resistance of the ITO. In addition, long term stability test of the flexible perovskite solar cells was performed and the cells showed promising result with only 10% PCE decrease over 1000 h in Fig. 4(c). Besides highly electron selectivity and low temperature process, C60 as ETL has been proven with good stability in perovskite solar cells17,33.
(a) J-V curve of the flexible perovskite solar cell with a metal mask of 0.16 cm2; the inset is the steady-state PCE at a bias of 0.81 V. (b) The corresponding EQE curve. (c) Long-term stability of the device with an area of 0.16 cm2 stored in a glovebox. (d) J-V curve of the flexible perovskite solar cell (calculated area: 1.2 cm2) without the metal mask. (e) EQE curves of the device at three selected spots. (f) The steady-state photocurrent density and PCE of the large-area perovskite solar cells (1.2 cm2) at a bias of 0.78 V.
From the results shown above, we can confirm that pinhole-free and uniform perovskite layers with good electrical properties were obtained using the sequential evaporation/spin-coating process, and therefore, flexible perovskite solar modules were fabricated. The module of the flexible perovskite solar cell had a large size of 5 cm × 5 cm, which was composed of 5 serially connected sub-cells with a 3.2 cm2 aperture area for each. In a two-step patterning process with a femtosecond laser, the sub-cells were combined in a standard serial interconnection geometry, as shown in Fig. 5(a). After coating the module with hole transport material (HTM), a femtosecond laser was used to cut the ETL/perovskite/HTM layer, and then the electrode was evaporated to connect each sub-cell. Figure 5(b) shows the I-V curve of the flexible perovskite solar module. When measured under the reverse scan, the module exhibits a V oc of 5.10 V (equivalent V oc 1.02 V), a I sc of 49.1 mA (equivalent J sc 15.3 mA), an FF of 0.55 and thus a PCE of 8.6%. When measured under the forward scan, the module exhibits a V oc of 5.14 V (equivalent V oc 1.03 V), a I sc of 51.2 mA (equivalent J sc 16.0 mA), and an FF of 0.50, resulting in a PCE of 8.2%. Compared with a typical 1.2-cm2-area device, the module shows decreased J sc and FF values, which may be due to the interconnected width of the series resistance (a series resistance of 76 Ω) contributed by ITO. To verify the efficiency from the I-V curves, the steady-state output at a bias of 2.85 V was measured. The flexible module shows a nearly constant PCE of 7.6% during the measurement under the 100 mW cm−2 illumination shown in Supplementary Fig. S3.
(a) Scheme showing the interconnection of the sub-cells in the perovskite thin film solar module with the patterning of the ITO bottom contact (P1) and the series connection of adjacent cells (P2). (b) I-V curve of the perovskite solar module with a calculated area of 16 cm2 tested under 100 mW cm−2 illumination. (c) Normalized performance of the flexible perovskite solar module versus the number of bending cycles; bending the module parallel to the etching line (B1), perpendicular to the etching line (B2), and in both of the above two directions (B3).
A circular bending test was carried out on the flexible perovskite solar module to check the reliability. The module was tested with a radius of curvature of 32 mm in three different bending tests: bending parallel to the etching line, perpendicular to the etching line and both parallel and perpendicular to the etching line. The flexible devices exhibit decreased photovoltaic performance with bending the module, as shown in Fig. 5(c). The significant change in the flexible module performance upon multiple bending cycles originates from the decreased FF, which drops to 80% of its initial performance after 600 cycles in Supplementary Fig. S4. Most of the layers in the device, except for the ITO film, had high flexibility34. Specifically, the resistance of the ITO-PEN substrate was tested as a function of the number of bending cycles. The results clearly show a trend of increasing resistance with increasing number of bending cycles, as shown in Supplementary Table S2. This increasing resistance of ITO is in consistent with the decreased FF of the module.
Discussion
In conclusion, we have demonstrated a promising sequential deposition method for preparing CH3NH3PbI3 films at an ultrafast PbI2 evaporation rate of 20 Å s−1, through which we obtained uniform and pinhole-free perovskite films in a short time. The rate-controlled PbI2 deposition was investigated in detail, and devices were fabricated on flexible substrates. A 16 cm2 flexible perovskite solar module based on the MAPbI3 film deposited from an optimized PbI2 film was fabricated and had an efficiency of more than 8%. This strategy shows great potential for paving the way to the manufacture of large perovskite solar modules.
Methods
Materials
Unless specified otherwise, all chemicals were purchased from either Alfa Aesar or Sigma-Aldrich and used as received. 2,2′,7,7′-Tetrakis-(N,N-di-4-methoxyphenylamino)-9,9′-spirobi-fluorenes (spiro-OMeTAD) was purchased from Shenzhen Feiming Science and Technology Co., Ltd., and MAI was purchased from Xi’an Polymer Light Technology Co., Ltd.
Preparation of devices
Indium tin oxide coated glass (ITO-Glass) and polyethylene naphthalate (ITO-PEN) were patterned by a femtosecond laser, followed by ultrasonic cleaning in detergent water, deionized water and ethanol for 15 min each. The substrates were then dried under an N2 flow and treated with plasma for 5 min to remove any organic residues. Fullerene C60 was thermally evaporated onto the ITO-coated substrates with a thickness of 10 nm under a deposition pressure of 8 × 10–6 mbar at a deposition rate of 0.1 Å s−1. The 160 nm PbI2 films were then thermally evaporated on the C60 underlayer with controlled deposition rates within the range between 0.5 Å s−1 and 40 Å s−1, as monitored by a quartz crystal microbalance sensor. After the PbI2 deposition process, the samples were transferred to a spin coater in an N2-filled glovebox for the subsequent chemical conversion steps. A 56 mg ml−1 methyl-ammonium iodide (MAI) solution in ethanol containing 24 μl of 2-methoxyethanol was spread on the whole PbI2 film and then spin-coated at a rate of 3000 rpm for 30 s. The yellow film turned brown during the spin-coating and was then annealed at 150 °C on a hotplate outside of the glovebox for 10 min. To prepare the HTM layer, a solution of spiro-OMeTAD dissolved in ethyl acetate35 (41.6 mg ml−1, 17 μl ml−1 4-tert-butylpyridine, 7.8 μl ml−1 stock solution of 500 mg ml−1 lithium bis trifluoromethylsulfonyl imide in acetonitrile) was dropped onto the perovskite layer while spinning at a rotation rate of 2000 rpm. For the modules, P1 patterning of the module was performed with a femtosecond laser (Wuhan Hongtuo). After the HTM layer was deposited, the C60/perovskite/spiro-OMeTAD layers were fully removed to ensure low contact resistance at the interconnected space through P2 patterning. Finally, 10 nm MoO3 and 60 nm Au were successively evaporated through a properly designed mask under high vacuum (4 × 10−6 mbar) to complete the devices for tests.
Characterization
The photocurrent density-voltage characteristics of the devices were measured with a scan rate of 0.01 V s−1 under standard simulated AM 1.5 G illumination (100 mW cm−2) using a solar simulator (Oriel 94023 A, 300 W), which was calibrated using a standard Si solar cell (Oriel, VLSI standards). The external quantum efficiency (EQE) curves were obtained using monochromatic incident light produced by a power source (Pharos Technology) with a monochromator. Data acquisition was accomplished under DC mode with a power meter. The morphologies and microstructures of the deposited PbI2 films and perovskite films were investigated using a field-emission scanning electron microscope (FE-SEM, Zeiss Ultra Plus) and an X-ray diffractometer (XRD, D8 Advance).
References
Boland, J. J. Flexible electronics: Within touch of artificial skin. Nature Mater. 9, 790–792 (2010).
Snaith, H. J. Perovskites: the emergence of a new era for low-cost, high –efficiency solar cells. J. Phys. Chem. Lett. 4, 3623–3630 (2013).
Stranks, S. D. & Snaith, H. J. Metal-halide perovskites for photovoltaic and light-emitting devices. Nature Nanotech. 10, 391–402 (2015).
Ye, M. et al. Recent advancements in perovskite solar cells: flexibility, stability and large scale. J. Mater. Chem. A. 4, 6755–6771 (2016).
Yang, W. S. et al. Iodide management in formamidinium-lead-halide–based perovskite layers for efficient solar cells. Science 356, 1376–1379 (2017).
Chen, H. et al. A solvent- and vacuum-free route to large-area perovskite films for efficient solar modules. Nature 550, 92–95 (2017).
Bi, C. et al. Efficient flexible solar cell based on composition-tailored hybrid perovskite. Adv. Mater. 29, 1605900 (2017).
Giacomo, F. D. et al. Flexible perovskite photovoltaic modules and solar cells based on atomic layer deposited compact layers and UV-irradiated TiO2 scaffolds on plastic substrates. Adv. Energy. Mater. 5, 1401808 (2015).
Zhou, P. et al. Ultrasonic Spray-coating of large-scale TiO2 compact layer for efficient flexible perovskite solar cells. Micromachines 8, 55 (2017).
Park, M. et al. High-performance flexible and air-stable perovskite solar cells with a large active area based on poly (3-hexylthiophene) nanofibrils. J. Mater. Chem. A. 4, 11307–11316 (2016).
Zhou, Y. et al. Room-temperature crystallization of hybrid-perovskite thin films via solvent–solvent extraction for high-performance solar cells. J. Mater. Chem. A. 3, 8178–8184 (2015).
Huang, F. et al. Gas-assisted preparation of lead iodide perovskite films consisting of a monolayer of single crystalline grains for high efficiency planar solar cells. Nano Energy 10, 10–18 (2014).
Jeon, N. J. et al. Solvent engineering for high-performance inorganic–organic hybrid perovskite solar cells. Nature Mater. 13, 897–903 (2014).
Li, X. et al. A vacuum flash–assisted solution process for high-efficiency large-area perovskite solar cells. Science 353, 58–62 (2016).
Liu, M., Johnston, M. B. & Snaith, H. J. Efficient planar heterojunction perovskite solar cells by vapour deposition. Nature 501, 395–398 (2013).
Fu, F. et al. Low-temperature-processed efficient semi-transparent planar perovskite solar cells for bifacial and tandem applications. Nat. Commun. 6, 8932 (2015).
Wojciechowski, K. et al. C60 as an efficient n-type compact layer in perovskite solar cells. J. Phys. Chem. Lett. 6, 2399–2405 (2015).
Schieber, M. et al. Structural changes during vapor-phase deposition of polycrystalline-PbI2 films. J. Cryst. Growth 310, 3168–3173 (2008).
Jamil, S. S. & Mousa, A. M. Structural and optical properties of lead iodide thin films prepared by vacuum evaporation method. Eng. & Tech. journal 29 (2011).
Ghosh, T. et al. Optical and structural properties of lead iodide thin films prepared by vacuum evaporation method. Cryst. Res. Technol. 43, 959–963 (2008).
Werner, J. et al. Efficient near-infrared-transparent perovskite solar cells enabling direct comparison of 4-terminal and monolithic perovskite/silicon tandem cells. Acs. Energy. Lett. 1, 474–480 (2016).
Werner, J. et al. Efficient monolithic perovskite/silicon tandem solar cell with cell area >1 cm2. J. Phys. Chem. Lett. 7, 161–166 (2016).
Fu, F. et al. Controlled growth of PbI2 nanoplates for rapid preparation of CH3NH3PbI3 in planar perovskite solar cells. Physica status solidi (a) 212, 2708–2717 (2015).
Burschka, J. et al. Sequential deposition as a route to high-performance perovskite-sensitized solar cells. Nature 499, 316–319 (2013).
Xiao, Z. et al. Efficient, high yield perovskite photovoltaic devices grown by interdiffusion of solution-processed precursor stacking layers. Energ. Environ. Sci. 7, 2619–2623 (2014).
Liang, K. et al. Synthesis and characterization of organic–inorganic perovskite thin films prepared using a versatile two-step dipping technique. Chem. Mater. 10, 403–411 (1998).
Sanehira, E. M. et al. Influence of electrode interfaces on the stability of perovskite solar cells: reduced degradation using moox/al for hole collection. ACS Energy Lett. 1, 38–45 (2016).
Ioakeimidis, A. et al. Effect of PbI2 deposition rate on two-step PVD/CVD all-vacuum prepared perovskite. J. Solid. State. Chem. 244, 20–24 (2016).
Lee, Y. H. et al. Unraveling the Reasons for Efficiency Loss in Perovskite Solar Cells. Adv. Funct. Mater 25, 3925–3933 (2015).
Chen, Q. et al. Controllable self-induced passivation of hybrid lead iodide perovskites toward high performance solar cells. Nano Lett. 14, 4158–4163 (2014).
Bi, C., Yuan, Y., Fang, Y. & Huang, J. Low‐Temperature Fabrication of Efficient Wide‐Bandgap Organolead Trihalide Perovskite Solar Cells. Adv. Energ.Mater. 5, 1401616 (2015).
Snaith, H. J. et al. Anomalous Hysteresis in Perovskite Solar Cells. J.Phys. Chem. Lett 5, 1511–1515 (2014).
Ahn, N. et al. Trapped charge-driven degradation of perovskite solar cells. Nature Communications 7, 13422 (2016).
Wang, C. et al. Low-temperature plasma-enhanced atomic layer deposition of tin oxide electron selective layers for highly efficient planar perovskite solar cells. J. Mater. Chem. A. 4, 12080–12087 (2016).
Bu, T. et al. Synergic Interface Optimization with Green Solvent Engineering in Mixed Perovskite Solar Cells. Adv. Energ. Mater. 7, 1700576 (2017).
Acknowledgements
The authors benefitted from useful discussions with W. Li. This work was supported in part by the NSFC51702243, NSFC51672202, MOST2016YFB0303701, Technological Innovation Key Project of Hubei Province (2016AAA041) and Fundamental Research Funds for the Central Universities (WUT: 2016IVA089, 2016IVA085, 2016III030, 20410785,40122008, and 2017III022).
Author information
Authors and Affiliations
Contributions
Yong Peng conceived the idea; Kunpeng Li and Junyan Xiao initiated this work; Yong.Peng, Kunpeng.Li and Junyan Xiao designed the research program; Wangnan Li, Xinxin Yu and Tianhui Li prepared the films and performed optical characterization; Kunpeng Li, Da Xiao, Jiang He and Peng Zhou fabricated the devices and performed the measurements; Zhiliang Ku, Jie Zhong and Fuzhi Huang conducted the XRD and SEM measurements; Kunpeng Li, Junyan Xiao, Yong Peng and Yi-bing Cheng. wrote the paper; and all authors discussed and revised the paper.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Li, K., Xiao, J., Yu, X. et al. An efficient, flexible perovskite solar module exceeding 8% prepared with an ultrafast PbI2 deposition rate. Sci Rep 8, 442 (2018). https://doi.org/10.1038/s41598-017-18970-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-18970-y
- Springer Nature Limited
This article is cited by
-
Review of flexible perovskite solar cells for indoor and outdoor applications
Materials for Renewable and Sustainable Energy (2024)
-
Universal passivation strategy to slot-die printed SnO2 for hysteresis-free efficient flexible perovskite solar module
Nature Communications (2018)