Abstract
In this paper, a silver ion-selective electrode material with lower detection limit is presented. The electrode is based on 22.5As2S3-22.5Ag2S-55AgCl chalcohalide glass membranes. The low detection limit decreases from the micromolar range of the original Ag2S-As2S3 electrode to the nanomolar level (1.89 nM) by introducing AgCl. The addition of AgCl increases the conductivity of the glasses and improves the analytical properties of electrodes because of the joint effects of Ag+ and Cl- on network structure of the glass. The super-Nernstian response behavior was observed for the partially crystallized electrode. The electrode containing AgCl also possesses a high selectivity (except for Hg2+), fast response and good stability.
Similar content being viewed by others
Introduction
During the last four decades, much attention has been attracted to the problem of heavy metal pollution on environments and the humankind1,2. Heavy metals can be emitted by both natural and anthropogenic sources, including a variety of industrial resources, such as mining sites, foundries and smelters, combustion by-products and traffics3,4,5. In particular, heavy metal ions are apt to combine with the body’s biomolecules to form strong and stable chemical bonds, thus interfering with the normal metabolic processes of human beings1. To ensure human safety, implementation of targeted investigations on monitoring heavy metal contents in environmental solutions becomes one of the most pressing demands of the day.
To determine the heavy-metal ions (for examples Cu2+, Fe3+, Cd2+, Pb2+ and Ag+ etc.) in solutions, different analytical devices have been studied and developed in the past years6,7,8,9. Ion-selective electrodes (ISEs) are among the most effective devices due to merits of low cost, high reproducibility10,11,12,13 and low detection limits14,15,16. In fact, many instruments could not detect monovalent silver ions (Ag+) which makes Ag+-selective electrode become more significant. Chalcogenide (ChG) glasses represent one class of functional membranes for analysis and control of waste water or monitoring programs of rivers and lakes polluted with industrial elements and chemical industries17,18. Compared with their crystalline counterparts, ChG glass membranes have advantages of high selectivity, excellent lifetime and good chemical durability in strong acids and oxidizing agent media19,20. However, the low detection limit of the conventional Ag+-ISEs based on ChG glasses was only in the micromolar range21,22, and this has greatly restricted the application of Ag+-ISEs for determination of Ag+ ions at trace levels. It is known that halogen atoms in ChG glasses often act as a glass network terminal, and interrupt the glass network, resulting in the more open structure. Therefore, the largely improved transport property of monovalent ions is expected with addition of halides into ChG glasses23,24. In this paper, we try to explore the effect of AgCl addition on conductivity and ion transport performance of Ag2S-As2S3 glass, thereby obtaining an electrode that can be used for Ag+ ion trace detection.
Materials and Methods
Chalcohalide ChH glasses synthesis
Glasses with compositions (mol%) of (100-x)/2As2S3-(100-x)/2Ag2S-xAgCl were prepared by conventional melt-quenching method. The as-prepared samples are noted as G0, G45, G50, G55, and G60 for x = 0, 45, 50, 55, 60, respectively25. High-purity (AR) elements (As, S) and compounds (AgCl, Ag2S) were used as starting materials. The weighed batches (2 g) were evacuated in cleaned quartz ampoules under a vacuum of 0.10–0.01 Pa. The sealed ampoules were heated at 920 °C for 15 hrs in a rocking furnace, and then cooled down to 700 °C. The melts were finally quenched in the water from 700 °C to room temperature. The obtained glass samples were then annealed at 100 °C for 4 hrs to release the stress induced during quenching.
Electrode preparation
The bulk glasses were cut into discs (1 mm thick and 5 mm in diameter) as electrode membranes to prepare the all-solid-state electrode. All membranes were thoroughly polished with fine abrasive powder to obtain plane-parallel plates. A silver wire was then soldered to the membranes inner surface by using conductive silver paste, while insulation coating ink was smeared on the non-working surface except one end of the silver wire and the outer surface of membranes. After that the Ag+-ISE was put into the drying closet until the ink being dry. The working area was about 19.6 mm2.
Characterization of materials
X-ray diffraction (XRD) patterns, Raman spectra and scanning electron microscopy (SEM) were used for analysis of glass formation and structure, and electrochemical impedance spectroscopy (EIS) was measured to characterize electrical conductivity of materials. XRD patterns (MAX R1, precision ± 0.02°; Rigaku, Tokyo, Japan) were recorded on powder samples at 40 kV and 100 mA using Cu Kα radiation to identify the type of crystallites. Raman spectra (InVia-Reflex, precision≈1 cm−1, Renishaw, UK) were performed with a laser of 785 nm as the excitation source. SEM micrographs were obtained using a Hitachi S-4800 scanning electron microscope with the accelerating voltage of 1 kV. The surface of glasses was sputter coated with gold layer before measurement. EIS spectra were measured at the open circuit potential, and data were collected at a frequency range of 1MHz-1mHz.
Electromotive force (EMF) measurements
The potentiometric measurements were performed by CHI660e Electrochemical Work Station with a two-electrode system in magnetically stirred solutions at ambient temperature (25 °C). The Ag/AgCl reference electrode was applied with 3 M KCl as reference electrolyte solution and the all-solid-state Ag+- ISE as a working electrode. The salt bridge with 0.1 M KNO3 as electrolyte was used to avoid contamination. All EMF values were corrected for liquid junction potentials according to the Henderson equation26 where activity coefficients were obtained from the Debye-Huckel approximation. The experiments were performed in two 50 mL beakers pretreated in 0.1 M HNO3. The KNO3 (0.1 M) was used as an ionic strength adjustor, and the constant pH value (pH = 6) of the test solution was maintained. EIS of ion-selective electrodes were measured using a three-electrode system, and a platinum electrode was used as the counter electrode.
Results and Discussion
Characterization of the materials
It has been reported that the optimum ratio of Ag2S to As2S3 in the binary As2S3-Ag2S glass system varied from 1:1 to 2:1 when it was used as electrode materials27. In the present work, the 1:1 ratio was chosen and AgCl incorporated as a network modifier. Figure 1 presents XRD patterns and Raman spectra of all as-prepared samples where ever characterized G45, G50 and G5528 are also included for comparison as a whole. Results demonstrate again the greater crystallization tendency of G55 relative to other samples, but its crystal diffraction peaks seem weaker compared with ref.28. This is because an amount of batches for the re-prepared samples in this work (2 g) was less than that in previous work (4 g)28 due to the reduced diameter of quartz ampoules (5 mm). Thus it allows the glass melts to have a greater contact area so as to quench in amorphous state more easily. This inevitably leads to a decrease in the glass crystallinity of G55 and accordingly the change of the Raman spectrum as to be discussed afterwards.
It is seen from Fig. 1(a) that there are broad diffraction bands for G0, G45 and G50, indicating glassy state of these samples. However, several weak crystalline peaks appear for G55 and become more intense for G60. According to the location of these XRD peaks by comparison with the JCPDS standard card as shown at the bottom of the figure, they belong to AgCl crystal phase.
Raman spectra of all samples are normalized at 375 cm−1 and results are shown in Fig. 1(b). For each sample, Raman spectrum was measured three times and showed similar profiles, indicating the trustworthy homogeneity of as-prepared samples. Similar to the previous reports29,30, the structural network of the stoichiometric glass AgAsS2 (G0) consists of 3-membered rings As3S6 molecular fragments, where each ring is connected to three silver atoms29. The band at ~375 cm−1 is attributed to the asymmetric stretching vibration of As-S bonds with non-bridging S atoms30, while two bands at ~310 cm−1 and ~340 cm−1 are assigned respectively to As-S-As vibrations of pyramidal units denoting chair like configuration of rings31, and the stretching vibration of As-S bonds with bridging S atoms in the AsS3 pyramids32. It is noted that the intensity of bands at 310 cm−1 and 340 cm−1 decreases gradually with the AgCl content from 0 to 55 mol% most probably due to the joint effects of Cl− and Ag+ on the network structure of the glass. On one hand, Cl− ions can act as a glass network terminal to replace some bridging S to bond with As, leading to formation of the mixed AgyAs[S3-yCly] pyramids33. On the other, an increase in Ag content induces more Ag-S bonds which have the larger bond length (2.6 Å) than the substituted As-S bonds (2.3 Å), making glass network more open34. Nevertheless, the band intensity of G60 at 310 cm−1 and 340 cm−1 increases slightly compared with G50 and G55, and this phenomenon is most likely associated with precipitation of AgCl crystals from the glass matrix, thus weakening the effect of Cl− and Ag+ on the glass network.
Figure 2(a) shows EIS spectra of all samples exposed to 0.1 M KNO3 electrolytes solution. The EIS is fitted according to the equivalent circuit35,36 as shown in Fig. 2(b), where Rs stands for solution resistance, Rb for membrane bulk resistance related to high frequency semicircle, Cg for geometric capacity of membrane, Rct for charge-transfer resistance, and CPEdl for constant phase element. It is clear that experimental curves (dotted lines) are consistent closely to equivalent circuit fitting curves (solid lines), while each fitting parameter has a lower fitting error (<10%), indicating the reliable fit.
Table 1 presents the fitted circuit parameters of all samples. Compared with the AgCl-free electrode (G0), the electrodes containing AgCl show the reduced bulk resistance (Rb) by about two orders of magnitude, consistent with the expected results. It has been reported extensively that the number of carriers increases with the addition of halides in ChG and oxide systems25,37. Since the silver cations responsible for the transport of the current come from the ionic dissociation of Ag2S and AgCl in this matrix25, the charge carriers increase with the increased AgCl content. As demonstrated by Raman spectra in Fig. 1(b), the addition of AgCl makes the glass network more open, which is beneficial for ion migrate24, thus increasing the electrode conductivity. It is worth mentioning that for AgCl containing samples, the Rb value does increase with the increased AgCl content. Our previous studies on crystallization kinetics of G45 and G50 show that precipitated crystals experienced an evolution from AgCl (G45) to Ag3AsS3 (G50) phases after thermal treatment at the same condition28. It implies that the molecular fragments Ag3AsS3 in the glass matrix become dominant with the increase of AgCl content. As a result, the amount of removable Ag+ decreases and conductivity is accordingly reduced. In addition, crystallization is known to increase the conductivity of the glass38, so that G60 has the smallest Rb value. Similar phenomenon also occurs in the low-frequency part of the EIS spectra for samples with different AgCl content, which will be discussed later in conjunction with electrode performance.
Dynamic response of ISEs
The electrode response curve was constructed by plotting the potential values versus log a(Ag+), and the calibration curves of all electrodes are shown in Fig. 3. Different concentrations of AgNO3 standard solutions were prepared by using deionized aqueous solution. The Ag+ ion concentrations for the dynamic curve test were adjusted by using a 10 μL micro-injector to add different concentrations of AgNO3 standard solution to a 0.1 M KNO3 electrolyte solution with a constant volume. According to the IUPAC recommendations, the lower detection limit can be obtained from an intersection of two straight lines of the calibration curve39, as shown by the dotted lines in Fig. 3. The sensitivity, linear response range and low detection limit for all samples are summarized in Table 2.
It can be seen from Table 2 that the electrochemical properties of G0 are similar to previously reported results40, while AgCl addition makes the analytical characteristics of G45, G50 and G55 much superior, where G55 exhibits the lowest detection limit (1.89 nM). To the best of our knowledge, this is the lowest detection limit for Ag+ in the ChG/ChH glass ISEs presented to date23,40,41. By combining with above EIS and Raman spectra, we attribute an improvement of electrode performance induced by AgCl addition to the increased conductivity and an enhanced ion migration due to a more open structure. On the other hand, G55 does not show the lowest bulk resistance (Rb) compared with G45 and G50, indicating that conductivity is not the only factor that influences the performance of the electrode. It is known that the competition of interfering ions with the primary ions is one of reasons for the apparent loss of EMF at low Ag+ activity to hinder the further improvement of the low detection limit42. A charge-transfer resistance (Rct) obtained from analysis on the low-frequency part of the impedance spectrum provides information about the easiness for electron/ion transfer at the electrode-solution interface36. As shown in Table 1, G55 has a larger Rct than G45 and G50, suggesting that the transfer of K+ ion at the electrode interface is difficult. Consequently, the detection limit of G55 is lower than G45 and G50 owing to the weaker K+ ion interference.
Another impressive observation is the super-Nernstian response behavior for the partially crystallized electrode G60. Additional SEM measurements were carried out to explore the origin of the super-Nernstian response. As shown in Fig. 4(a–d), fresh sections of G0, G45, G50 and G55 look homogeneous without indication of phase separation, while that of G60 (e) exhibits a large number of micron-sized island-like substances, which, according to XRD patterns in Fig. 1(a), belong to AgCl crystals. After soaking in a 0.1 M KNO3 solution for 48 hours, the island-like substances disappear (f), indicating the complete dissolution of AgCl crystals. The membrane dissolution process of G60 is also supported by the much increased double layer capacitance (CPEdl, Table 1) due to possible contribution of dissolution-induced capacitive reactance. For comparison with Fig. 3(e), the calibration curve of G60 after 48-hour immersion treatment was measured as shown in Fig. 5. It is obvious that after soaking the super-Nernstian response of G60 disappears, demonstrating that super-Nernstian response behavior relates to the precipitated island-like AgCl crystals. Actually, similar super-Nernstian reactivity was once reported on solid-state copper ISEs in high concentrations of chloride media43. It was believed that the reduction of Cu2+ occurred at the surface of the electrode with concomitant oxidation of the mixed sulfide electrode material when the cuprous ion was stabilized by chloride complexation, leading to super-Nernstian response. In the present case, the chloride ion concentration in the electrolyte solution was relatively high due to the dissolution of the island-like AgCl crystals on the electrode surface.Thus, at the low Ag+ concentration, the question arises as whether the similar chloride complexation (AgCln) occurs in solution to make the EMF response to the solution activity independent on the Ag+ activity. Further exploration for more supporting data is needed to give an answer to this question.
Response time and effect of pH value
Response time (RT) is defined as the time that the measured potential value reaches more than 95% of its final value (t95%)44. We measured RT of G0 and G55 electrodes which show the decreased values along with the increase of AgNO3 concentration and become stable in less than 5 s at the relatively high concentration (Table 3). As the ion exchange on the electrode surface is usually rapid, the RT is actually controlled by the ions transport times. Thus a longer RT at the low Ag+ activity could be considered due to the small diffusion driving force of the diffusion layer from which the electrode surface is separated, making the ion transport very slow43.
The effect of pH value on electrodes G55 and G0 is also studied as shown in Fig. 6, where the pH value was adjusted with KOH and dilute HNO3 solutions by using a 10 μL micro-injector. The volume of the electrolyte solution can be regarded as constant due to a smaller volume of standard solution added. The final H+ concentration (CH) in the solution after each addition was calculated by the following equation:
where \({{\rm{c}}^{\prime} }_{H}\) is the original concentration of H+ ions calculated from the original pH value, \({{\rm{v}}}_{b}\) and \({{\rm{c}}}_{b}\) are the volume and concentration of standard HNO3 solution added, respectively, and V is the total volume of electrolyte solution. The pH value can be calculated using the following formula:
A similar method can be used to obtain the pH value in the alkaline solution range.
It can be seen that the potential of G0 is independent of pH value in the range of 4 ≤ pH ≤ 10, while G55 shows a slightly narrower range about 4 ≤ pH ≤ 9. For G0, in fact, a lot of visible precipitants (AgOH) appear when the pH value reaches 11, corresponding to the potential reduction in the alkaline range. For G55, however, the potential is reduced when less precipitation occurs (9 ≤ pH ≤ 10), suggesting more sensitive to Ag+ concentration. Moreover, a monotonous reduction of electrode potentials occurs with the decreased pH value, and this is attributed to inverted-Nernstian response caused by the hydrogen ion (H+). A generalized model for “non-Nernstian” responses of ISEs can be used to define the response slope S as follows45:
where aI and \([{{\rm{I}}}^{{Z}_{I}}]\) are the activity of \({{\rm{I}}}^{{Z}_{I}}\,\)in the sample solution and the concentration of \({{\rm{I}}}^{{Z}_{I}}\,\)in the membrane phase, respectively. ZI is the charge of the \({{\rm{I}}}^{{Z}_{I}}\), and the R, T, and F have their usual meanings. With the decrease in pH value, a lot of small-radius H+ ions enter modified surface layer18 (MSL) of membrane, resulting in the sharp increase in H+ concentration of MSL (∂log \([{{\rm{I}}}^{{Z}_{I}}]\)/ ∂ log aI > 1), and inducing an inverted-Nernstian response (see Eq. 3)45.
Selectivity, reproducibility and stability
According to the IUPAC recommendations, the selectivity coefficients were determined with the fixed interference method (FIM)39,46,47,48,49,50. The AgNO3 was added to the background electrolyte solution containing constant ionic activity (1 mM) of NaNO3, Sr(NO3)2, Ba(NO3)2, Cu(NO3)2, Zn(NO3)2, Mn(NO3)2, Cd(NO3)2, Co(NO3)2, Hg(NO3)2 and Al(NO3)3, respectively, until a linear response slope to the Ag+ is observed.
The selectivity coefficients were obtained by using following equation51:
where \({a}_{A{g}^{+}}(DL)\) and \({a}_{J}(BG)\,\,\)are activities of Ag+ at the detection limit and of the interfering ions in the background electrolyte solution, respectively, while ZJ is the charge of the interfering ion. The calculated logs of selectivity coefficients are listed in Table 4.
Results show that G55 and G0 exhibit high selectivity for Ag+ ion over other ions except for Hg2+ ion. According to previously reported work on the response of the ChG/ChH glass to Hg2+ ion21,52,53, it is believed that21 the Hg2+ ions interact with the soluble sulfide (or/and halide) formed by the membrane dissolution with subsequent formation of mercury-sulfide (or/and mercury-halide) complexes on the membrane surface, so that the electrode becomes in response to mercury ions. In other words, the detection of Ag+ ions by the electrode is almost impossible when a large amount of Hg2+ ions are co-present.
Reproducibility of the electrode performance was evaluated on two G55 samples which show a standard potential values within ±20 mV and slope values within ±2.1 mV/dec, indicating excellent reproducibility. The linear range remain unchanged after holding for 1 month, indicating good long-term stability. Moreover, the present glass ISEs are easily restored by simply polishing while retaining high reproducibility and stability.
Conclusions
A simple fabrication procedure was used to make solid contact ion-selective electrodes based on AgCl-Ag2S-As2S3 ChH glass/alloy for the detection of Ag+ ions. The experimental results indicate that the electrode with 55 mol% AgCl has a lower detection limit than AgCl-free electrode due to increased conductivity and the more open structure. Both AgCl-free and AgCl-containing samples show a high selectivity (except for Hg2+), fast response time, good stability, a reasonable reproducibility, and can be used for silver ion trace detection in the appropriate conditions. Moreover, the super-Nernstian response behavior was observed from the partially crystalized sample which is related to the dissolution of island-like crystals precipitated from glass matrix.
Data Availability
All data generated or analyzed during this study are included in this published article.
References
Duruibe, J. O. & Ogwuegbu, M. O. C. Heavy metal pollution and human biotoxic effects. International Journal of Physical Sciences. 2, 112–8 (2007).
Gupta, V. K. et al. Electrochemical Analysis of Some Toxic Metals by Ion-Selective Electrodes. Critical Reviews in Analytical Chemistry. 41, 282–313 (2011).
Rodríguez Martín, J. A., De Arana, C., Ramos-Miras, J. J., Gil, C. & Boluda, R. Impact of 70 years urban growth associated with heavy metal pollution. Environmental Pollution. 196, 156–63 (2015).
Wang, Y. et al. Assessment of heavy metals in sediments from a typical catchment of the Yangtze River, China. Environmental Monitoring and Assessment. 172, 407–17 (2011).
Ali, M. M., Ali, M. L., Islam, M. S. & Rahman, M. Z. Preliminary assessment of heavy metals in water and sediment of Karnaphuli River, Bangladesh. Environmental Nanotechnology, Monitoring & Management. 5, 27–35 (2016).
Gupta, V. K., Jain, A. K., Maheshwari, G., Lang, H. & Ishtaiwi, Z. Copper(II)-selective potentiometric sensors based on porphyrins in PVC matrix. Sensors and Actuators B: Chemical. 117, 99–106 (2006).
Gupta, V. K., Jain, A. K., Kumar, P., Agarwal, S. & Maheshwari, G. Chromium(III)-selective sensor based on tri-o-thymotide in PVC matrix. Sensors and Actuators B: Chemical. 113, 182–6 (2006).
Gupta, V. K., Prasad, R., Kumar, P. & Mangla, R. New nickel(II) selective potentiometric sensor based on 5,7,12,14-tetramethyldibenzotetraazaannulene in a poly(vinyl chloride) matrix. Analytica Chimica Acta. 420, 19–27 (2000).
Gupta, V. K. et al. Cadmium (II) ion sensing through p-tert-butyl calix[6]arene based potentiometric sensor. Journal of Molecular Liquids. 195, 65–8 (2014).
Gupta, V. K., Jain, A. K. & Kumar, P. PVC-based membranes of N,N′-dibenzyl-1,4,10,13-tetraoxa-7,16-diazacyclooctadecane as Pb(II)-selective sensor. Sensors and Actuators B: Chemical. 120, 259–65 (2006).
Gupta, V. K., Jain, S. & Chandra, S. Chemical sensor for lanthanum(III) determination using aza-crown as ionophore in poly(vinyl chloride) matrix. Analytica Chimica Acta. 486, 199–207 (2003).
Gupta, V. K. et al. A novel copper (II) selective sensor based on Dimethyl 4, 4′ (o-phenylene) bis(3-thioallophanate) in PVC matrix. Journal of Molecular Liquids. 174, 11–6 (2012).
Gupta, V. K., Jain, A. K., Agarwal, S. & Maheshwari, G. An iron(III) ion-selective sensor based on a μ-bis(tridentate) ligand. Talanta. 71, 1964–8 (2007).
Legin, A. V., Bychkov, E. A. & Vlasov, Y. G. Thin-layer chemical sensors based on chemically deposited and modified chalcogenide glasses. Sensors and Actuators B: Chemical. 15, 184–7 (1993).
Gupta, V. K., Singh, A. K., Al Khayat, M. & Gupta, B. Neutral carriers based polymeric membrane electrodes for selective determination of mercury (II). Analytica Chimica Acta. 590, 81–90 (2007).
Gupta, V. K., Jain, A. K. & Maheshwari, G. Aluminum(III) selective potentiometric sensor based on morin in poly(vinyl chloride) matrix. Talanta. 72, 1469–73 (2007).
Schöning, M. J. & Kloock, J. P. About 20 Years of Silicon-Based Thin-Film Sensors with Chalcogenide Glass Materials for Heavy Metal Analysis: Technological Aspects of Fabrication and Miniaturization. Electroanalysis. 19, 2029–38 (2007).
Vassilev, V. S. & Boycheva, S. V. Chemical sensors with chalcogenide glassy membranes. Talanta. 67, 20–7 (2005).
Vlasov, Y. G., Bychkov, E. A. & Medvedev, A. M. Copper ion-selective chalcogenide glass electrodes. Analytica Chimica Acta. 185, 137–58 (1986).
Tarantov, Y. A., Vlasov, Y. G., Mesentsev, Y. A. & Averyanov, Y. L. Physical and chemical processes in ISFETs with chalcogenide membranes. Sensors and Actuators B: Chemical. 1, 390–4 (1990).
Miloshova, M. et al. Tracer and surface spectroscopy studies of sensitivity mechanism of mercury ion chalcogenide glass sensors. Sensors and Actuators B: Chemical. 57, 171–8 (1999).
Tomova, R., Assa, J., Stoycheva-Topalova, R. & Buroff, A. As2S3 and AgI thin layers as ion sensitive membranes. Journal of Non-Crystalline Solids. 260, 195–8 (1999).
Moroz, M. V., Prokhorenko, M. V. & Moroz, V. M. Ag0.225Ge0.260S0.515-AgBr glasses. Inorganic Materials. 50, 532–6 (2014).
Robinel, E., Carette, B. & Ribes, M. Silver sulfide based glasses (I). Glass forming regions, structure and ionic conduction of glasses in GeS2-Ag2S and GeS2-Ag2S-AgI systems. Journal of Non-Crystalline Solids. 57, 49–58 (1983).
Kawamoto, Y. & Nishida, M. Ionic conduction in As2S3-Ag2S, GeS2-GeS-Ag2S and P2S5-Ag2S glasses. Journal of Non-Crystalline Solids. 20, 393–404 (1976).
Izutsu, K., Arai, T. & Hayashijima, T. Liquid junction potential between different solvents: a junction with an alkaline earth metal salt as electrolyte. Journal of Electroanalytical Chemistry. 426, 91–5 (1997).
Vlasov, Y. G., Moskvin, L. N., Bychkov, E. A. & Golikov, D. V. Silver bromide based chalcogenide glassy-crystalline ion-selective electrodes. Analyst. 114, 185–90 (1989).
Li, L. et al. Study on crystallization behavior of novel silver chloride based chalcogenide glasses. Journal of Alloys and Compounds. 706, 48–55 (2017).
Andrikopoulos, K. S. et al. Nanoindentation and Raman studies of phase-separated Ag-As-S glasses. Applied Physics Letters. 99, 171911 (2011).
Kyriazis, F. et al. Effect of silver doping on the structure and phase separation of sulfur-rich As–S glasses: Raman and SEM studies. Journal of Non-Crystalline Solids. 355, 2010–4 (2009).
Hasapis, T. C. et al. Vibrational Properties of Silver-doped Arsenic Chalcogenide Bulk Glasses. AIP Conference Proceedings. 1203, 283–8 (2010).
Wágner, T., Vlček, M., Kasap, S. O., Vlček, M. & Frumar, M. Changing the composition of Ag-As-S amorphous films using photo-induced solid state reaction. Journal of Non-Crystalline Solids. 284, 168–73 (2001).
Bréhault, A. et al. Influence of NaX (X = I or Cl) additions on GeS2-Ga2S3 based glasses. Journal of Solid State Chemistry. 220, 238–44 (2014).
Bychkov, E. & Price, D. L. Neutron diffraction studies of Ag2S-As2S3 glasses in the percolation and modifier-controlled domains. Solid State Ionics. 136, 1041–8 (2000).
Armstrong, R. D., Covington, A. K. & Evans, G. P. Mechanistic studies of the valinomycin-based potassium-selective electrode using AC impedance methods. Journal of Electroanalytical Chemistry and Interfacial Electrochemistry. 159, 33–40 (1983).
Liu, C. et al. A solid-contact Pb2+- selective electrode based on electrospun polyaniline microfibers film as ion-to-electron transducer. Electrochimica Acta. 231, 53–60 (2017).
Reggiani, J.-C., Malugani, J.-P. & Bernard, J. Étude des systèmes vitreux AgPO3 - AgX (X = I, Br, Cl) par calorimetrie de dissolution. Corrélation entre l’activité thermodynamique de Ag X et la conductivité ionique du verre. J Chim Phys. 75, 849–54 (1978).
Sales, B. C. Novel thermoelectric materials. Current Opinion in Solid State and Materials Science. 2, 284–9 (1997).
Buck, R. P. & Lindner, E. Recommendations for nomenclature of ionselective electrodes (IUPAC Recommendations 1994). Pure and Applied Chemistry. 66, 2527–36 (1994).
Vlasov, Y. G. Sensor R&D in the former Soviet Union. Sensors and Actuators B: Chemical. 15, 6–15 (1993).
Schubert, J. et al. Chalcogenide-based thin film sensors prepared by pulsed laser deposition technique. Applied Physics A. 69, S803–S5 (1999).
Nägele, M., Bakker, E. & Pretsch, E. General Description of the Simultaneous Response of Potentiometric Ionophore-Based Sensors to Ions of Different Charge. Analytical Chemistry. 71, 1041–8 (1999).
Westall, J. C., Morel, F. M. M. & Hume, D. N. Chloride interference in cupric ion selective electrode measurements. Analytical Chemistry. 51, 1792–8 (1979).
Bakker, E., Bühlmann, P. & Pretsch, E. Carrier-Based Ion-Selective Electrodes and Bulk Optodes. 1. General Characteristics. Chemical Reviews. 97, 3083–132 (1997).
Amemiya, S., Bühlmann, P. & Odashima, K. A Generalized Model for Apparently “Non-Nernstian” Equilibrium Responses of Ionophore-Based Ion-Selective Electrodes. 1. Independent Complexation of the Ionophore with Primary and Secondary Ions. Analytical Chemistry. 75, 3329–39 (2003).
Gupta, V. K., Singh, A. K., Mehtab, S. & Gupta, B. A cobalt(II)-selective PVC membrane based on a Schiff base complex of N,N′-bis(salicylidene)-3,4-diaminotoluene. Analytica Chimica Acta. 566, 5–10 (2006).
Gupta, V. K., Sethi, B., Sharma, R. A., Agarwal, S. & Bharti, A. Mercury selective potentiometric sensor based on low rim functionalized thiacalix [4]-arene as a cationic receptor. Journal of Molecular Liquids. 177, 114–8 (2013).
Vassilev, V., Tomova, K. & Boycheva, S. Pb (II)-ion-selective electrodes based on chalcogenide glasses. Journal of Non-Crystalline Solids. 353, 2779–84 (2007).
Vassilev, V., Hadjinikolova, S. & Boycheva, S. Zn (II)-ion-selectiveelectrodes based on GeSe2-Sb2Se3-ZnSe glasses. Sensors and Actuators B: Chemical. 106, 401–6 (2005).
Vlasov, Y. G. New solid-state ion-selective electrodes-Sensors for chemical analysis of solutions. Fresenius’ Journal of Analytical Chemistry. 335, 92–9 (1989).
Bakker, E., Pretsch, E. & Bühlmann, P. Selectivity of Potentiometric Ion Sensors. Analytical Chemistry. 72, 1127–33 (2000).
Radic, N. The Potential Response Of Copper (II) Sulfide Ion Selective Electrode To Hg (II) Ions In Aqueous Solution. Analytical Letters. 14, 1125–33 (1981).
Radić, N. Potentiometric response of a commercial (Ag2S + PbS)-membrane selective electrode to Hg(II) in aqueous solution. Microchimica Acta. 85, 209–18 (1985).
Acknowledgements
This study was supported by Shanghai Leading Academic Discipline Project (No. B502), Shanghai Key Laboratory Project (08DZ2230500), and the National Natural Science Foundation of China (NSFC51572081, 51572082).
Author information
Authors and Affiliations
Contributions
L. Li and G. Chen* conceived the experiments. L. Li, H. Yin, Y. Wang and J. Zheng conducted experiments of the glass synthesis and characterization. L. Li carried out electrode preparation and performance testing. L. Li, H. Zeng and G. Chen analyzed the data. L. Li and G. Chen wrote the paper.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Li, L., Yin, H., Wang, Y. et al. A chalcohalide glass/alloy based Ag+ ion - selective electrode with nanomolar detection limit. Sci Rep 7, 16752 (2017). https://doi.org/10.1038/s41598-017-17032-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-17032-7
- Springer Nature Limited