Abstract
In order to understand the physical properties of materials it is necessary to determine the 3D positions of all atoms. There has been significant progress towards this goal using electron tomography. However, this method requires a relatively high electron dose and often extended acquisition times which precludes the study of structural dynamics such as defect formation and evolution. In this work we describe a method that enables the determination of 3D atomic positions with high precision from single high resolution electron microscopic images of graphene that show dynamic processes. We have applied this to the study of electron beam induced defect coalescence and to long range rippling in graphene. The latter strongly influences the mechanical and electronic properties of this material that are important for possible future applications.
Similar content being viewed by others
Introduction
For studies of defect dynamics in graphene and related 2D materials there is a need for a method that can recover time resolved three-dimensional information in real space. Electron tomography has been demonstrated using aberration corrected Scanning Transmission Electron Microscopy (STEM)1, 2 and Transmission Electron Microscopy (TEM)3, 4, but this method requires a large number of images making it unsuitable for the observation of dynamic processes.
In this letter we present a method that can be used to determine the 3D positions of individual atoms in a graphene sheet from a single TEM image and subsequently to track their motion. This “snapshot’ method provides the four dimensional information (three spatial and the time domain (x, y, z, t)) necessary for the understanding of certain dynamic processes. As an example, the interaction of high-energy electrons with monolayer graphene causes variations in both bond lengths and angles leading to elastic deformations and the migration of defects5, 6. We report initial applications of this approach to studies of the long range rippling of monolayer graphene and to defect coalescence and motion.
The discovery of graphene as the first truly 2D crystal contradicted the Mermin–Wagner theorem7 which states that 3D fluctuations can destroy long-range order in 2D crystals. Subsequent theoretical calculations have shown that a monolayer graphene sheet is stabilized by 3D rippling with amplitudes of order less than 0.1 nm and wavelengths of order 8 nm8, 9. It has also been reported that the rippling amplitude depends on the size of individual graphene flakes10. Experiments, using electron diffraction of μm sized flakes of monolayer graphene have revealed rippling attributed to thermal fluctuations with a wavelength of order 5–10 nm but with amplitudes estimated of order 1nm10. Additional studies using TEM11 and STEM12, 13 imaging have also revealed local rippling in mono and multi layer graphene and distortions around defects14 and tears and cracks in graphene sheets15. Understanding rippling dynamics is crucial for detailed descriptions of stability and electronic transport16, 17 in graphene. Dislocation induced rippling has also been measured using a geometric phase analysis18.
Results
Experimental conditions for imaging
Graphene was synthesised by atmospheric pressure chemical vapour deposition (CVD). Full details of the synthesis and transfer onto TEM specimen grids are described elsewhere19. Our method was applied to a time-series of ten TEM images (Fig. 1 and Extended data Fig. 1) of graphene flakes supported on perforated Si3N4 membranes, recorded with plane wave illumination using the aberration corrected Oxford-JEOL JEM-2200MCO FEGTEM20, 21 on a 4k × 4k CCD at an accelerating voltage of 80 kV, using an energy spread of 2220 meV and with a dose of 104e−nm−2. The dose used is higher than that reported for imaging MoS2 nanosheets22 and was limited by the requirement of recording images with sufficiently high signal to noise for further analysis. The sampling was 0.00861 nm per pixel and the exposure used was 1 second. During data acquisition the CCD gain, and dark field correction remained constant. The field of view containing ca. 500 carbon atoms in each frame, was ca. 3.5 nm × 3.5 nm and frames were recorded at ca. 1 s intervals with a 1 s exposure. Under certain conditions HREM images of a planar thin sample contain 3D information about the sample in that the vertical position of an atom affects the intensity in the image, equivalent to a defocus offset.
Time series of HRTEM images of graphene. Ten image sequence recorded at an accelerating voltage = 80 kV, with 1 s intervals and with a dose = 104e−nm−2 for each image. Atoms around defect sites are highlighted in colour; red and yellow show respectively the initial 5-8-5 ring defects and blue the merged 5-8-4-8-4-8-5 extended defect. The scale bar is equivalent to 1 nm. Each image field contains approximately 500 carbon atoms.
Determination of the z height
The algorithm used to determine the z-height of single atom is based on the projected charge density (PCD) approximation23, 24 which is valid for the material studied. Vertically displacing a carbon atom, considered as a phase object, over a distance Δz, in the presence of small values of high order residual aberrations, gives rise to a change in image intensity, ΔI which is dependent only on defocus and can be described by the PCD approximation23, 24 (1), where the λ is the wavelength of incident electron, σ is an interaction constant, ε o is the permittivity of vacuum, ε the relative permittivity and ρ(x, y) is the projected charge density which is related to the projected potential V(x, y) by the Poisson equation.
In (1), ΔΙ is the experimental intensity after subtraction of the background intensity (measured in the center of the hexagonal ring of C atoms). Hence, using (1) the vertical displacement of an atom, Δz can be determined using the change in ΔΙ and a calculated value of ρ(x, y). A calculated value for ρ(x, y) can be evaluated from a plot of simulated values for ΔΙ calculated using the multislice method24,25,26 for a graphene monolayer layer at defoci from 0 to 0.5 nm (blue line in Extended data Fig. 2). For these calculations gmax = 20 nm−1 corresponding to the experimental information limit and from (1) the fitted slope is proportional to (λσ/2π) ρ(x, y)/εε ο , where ρ(x, y)/εε ο is 70.9 eVÅ−1 in this case.
In principle, the analysis described above could be applied to thicker samples such as bilayer graphene, provided that the underlying projected charge density (PCD) approximation remains valid. However, to calculate a general upper thickness bound for the PCD approximation is materials dependent and would require extensive image simulations which are outside the scope of the current paper.
Experimental Errors
Experimentally, measurements of the image intensity are affected by the presence of noise, residual aberrations and sample tilt and therefore these factors also limit the precision of this approach in the determination of Δz (see also Methods-I and II and Extended data Figs 2 and 3). In addition, the mean displacement squares < u2 > , and hence the Debye-Waller factors of carbon atoms at defect sites compared to those in the pristine graphene lattice are expected to be different as atoms at defect sites are less coordinated, which may further affect the precision of this approach (for details see also Methods-III and Extended data Fig. 4).
For an aberration corrected instrument the residual higher order aberrations are small and hence their contribution to the measurement error is negligible (~3 pm, see also Methods-I) compared to that due to noise in the data. The intensities in images of single layer graphene are also less sensitive to the effects of sample tilt as the reciprocal space rel-rods are extended compared to those in a thicker crystal. Sample tilt introduces a globally inclined defocus plane which is automatically accounted for by equation (1). Sample tilt can however also introduce atom displacements and distortions of the local hexagonal symmetry in the case of double layer graphene used to validate our calibration of the Stobbs factor (see also Methods-II). Overall, as will be described later residual aberrations, sample tilt and Debye Waller factors lead to a combined error of 3–7 pm in the determination of the z-height. It is worth also noting that the electron beam interaction may soften the potential4 and therefore affect the determination of Δz. In this work the relatively high dose used was driven by a need to record data with sufficiently high signal to noise to validate the method described. However, in future using high speed direct electron detectors it should be possible to work under lower dose conditions which will provide useful insights into true structural kinetic effects.
It has been established that even in the absence of residual aberrations and specimen tilt there is a contrast mismatch between experimental and calculated high resolution TEM images known as the Stobbs factor27,28,29. Hence, using calculated values of ρ(x, y) and experimental values of ΔI leads to a systematic error in the calculation of Δz. However, for the case of monolayer graphene for which the thickness is known exactly the Stobbs’ factor can be calibrated by quantitatively comparing simulated and experimental image intensities (Fig. 2). Before calibration of the Stobbs factor S = I sim /I exp the simulated or experimental background intensity, respectively, in the center of the hexagonal ring of C atoms was subtracted from the intensities Isim and Iexp. Figure 2a and b show the background subtracted simulated image at Δz = 0 and the corresponding experimental motif averaged from different locations in the single layer region. The Stobbs factor, S was then measured from the intensity ratio between simulated and averaged experimental motifs I sim /I exp (Fig. 2). The respective intensity profiles are shown in Fig. 2c. This Stobbs factor S was then used to correct the simulated PCD to obtain an estimate for the experimental PCD. For the data reported here, S = 1.18 and this value was subsequently used to calibrate the vertical displacements.
The validity of this calibration was confirmed experimentally using a sample region containing a flat double-layer graphene sheet (Fig. 3) which has a theoretical spacing between the layers of 0.335 nm and which acts as a control. Within the image field shown there are three types of atom: those in the bottom layer that are not superimposed with those in the upper layer (green dots), those in the upper layer that are not superimposed with those in the bottom layer (red dots) and those in the two layers that are superimposed (blue dots, brightest peaks) (Fig. 3(a)). There is evidence for some atom displacement from perfect hexagonal symmetry in the region shown in Fig. 3(a) suggesting either small local specimen tilt or small residual aberrations. However, as already described (See also Methods I and II) neither of these have a significant effect on the calibration accuracy. In total, 55 and 316 atoms were analyzed, for the top and bottom layers respectively and their intensity histogram and corresponding Δz calculated from equation (1) are shown in Fig. 3b and c, respectively.
Validation of the calibration. (a) Image of graphene showing both monolayer and bilayer regions. Green dots indicate atoms in the bottom layer and blue and red dots indicate atoms in the top layer. Atoms indicated in red are those not superimposed with atoms in the bottom layer. Recorded with a sampling of 0.00861 nm per pixel, exposure time = 1 s, dose = 104 e−nm−2 at 80 kV. (b) Histogram of intensities at the centres of the hexagonal ring of C atoms (valley black, from 3106 pixels), top layer (red, 55 atoms) and bottom layer (green, 316 atoms). (c) Histogram of vertical displacements of atoms in the top layer (red) and bottom layer (green).
The error in the measurement of the vertical displacement arising from noise in the data was statistically estimated as follows. Extended data Fig. 5a shows an experimental image of single carbon atom. The position of this atom was located using a fitted 2D Gaussian function and the intensity was extracted from a 3 × 3 pixel area (Extended data Fig. 5b. The quantity δ(ΔI) is defined as the deviation in the experimental intensity, ΔI exp from the fitted Gaussian intensity, ΔI ideal and hence, the error in Δz, δ(Δz) can be calculated using equation (1). Extended data Fig. 5c shows δ(Δz) for 20 atoms. From the spread in this data we estimate that the error in the vertical displacement due to noise is 23 pm. In contrast, the errors due to residual aberrations, the Debye Waller factor and sample tilt are estimated to be 3–7 pm (see Methods-I, II and III), which are much smaller than that due to noise. Overall our measured value of the vertical separation in the bilayer region is 0.353 ± 0.03 nm which is in good agreement with the theoretical value of 0.335 nm. The atomic vibrations in graphene are significantly faster than the acquisition time of 1 second. Therefore, the experiments reported measure a “time averaged” value of Δz within a 1 s period with an error bar of 30 pm. Even at this time resolution there is evidence for a time dependence in Δz for individual atoms. Extended data Fig. 5d shows this time dependent motion in the z-direction for a single atom within a time-series of images in which the measured changes in Δz between some members in the series is greater than δ(Δz).
Discussion
Figure 4(a) shows projected structures and superimposed models of two defects present in sub areas extracted from three images within the ten-member series. These defects are composed of 5 and 8-member rings as previously reported5, 6, 30. These two defects are stable in frames 1–5 (Fig. 1 and Extended data Fig. 1), and subsequently migrate in frames 6 and 7 and finally merge in frame 8 to form an extended line defect containing 4-member rings30 which is stable in frames 9 and 10 (Fig. 1 and Extended data Fig. 1).
3D analysis of local defect structures. (a) Enlarged views of sub-regions from images 6, 7 and 8 in the time series showing the interaction of two defects together with superimposed structure models. (b) Rippled structure of the defects in frames 6, 7 and 8 together with the fitted local curvature of the graphene lattice and associated errors. (c) Visualization of long range oscillations of the extended graphene sheet using a hyper-surface fitted to the experimental data. The z-height is enlarged 10 times for clarity.
Using the method as described these images of graphene were analysed to determine (x, y, z) for each carbon atom around the defect sites shown in Fig. 4(a), as shown in Fig. 4(b) and (c). The z height histograms for frames 6, 7 and 8 are shown in Extended data Fig. 6. A third order polynomial f(x, y) was used to fit the three dimension coordinates of the carbon atoms to a hyper-surface with, f(x, y) the z-height values determined from the experimental data and with the two dimensional atomic positions (x, y) determined from fitted Gaussian functions. This shows that the defects are initially non-planar and the local curvature of the graphene lattice around the defect is reduced as the defects merge. The final extended defect is approximately planar in agreement with previously reported Density Functional Theory calculations30.
Time dependent variations in the bond lengths and bond angles at each C-C pair have also been measured and compared with those in the perfect graphene lattice for each frame in the time sequence of images (Extended data Fig. 7). This reveals that the bond lengths and angles around the 8-fold rings are distorted compared to the perfect lattice in agreement with previously published calculations30, consistent with the defect region accommodating elastic strain.
Using the same image series, we have also measured the long range rippling of the extended graphene sheet. From measurements of the vertical positions of all atoms in the images it is clear that the sheet oscillates (Fig. 4(c)). These oscillations have been analysed as a function of time for the ten-member image series (Extended data Fig. 8), giving values of 0.03 ± 0.005 nm and 6.96 ± 0.66 nm respectively for the amplitude and wavelength in close agreement with previously reported experimental and simulated data from a similar sample size8, 10,11,12,13. Movies showing the dynamics of these oscillations are provided in Supplementary information (Supplementary information Movie 1).
Conclusions
In this letter we have described a method for the determination of temporarily resolved 3D atomic positions from a series of single high resolution TEM images. Currently, the temporal resolution was limited by the acquisition and readout times of the conventional CCD detector used31, but using currently available direct CMOS sensors32 this can be extended to ms time intervals. The use of this type of detector operating in a counting mode will also enable lower electron dose rates whilst maintaining a sufficient signal to noise ratio in the data, potentially enabling studies of intrinsic structural changes, under conditions where beam induced effects have been shown to be suppressed22. We have initially applied this to the study of electron beam induced defect coalescence and to long range rippling in graphene, both taking advantage of a defined number of single atom species, in projection in monolayer and bilayer sheets to quantify the vertical displacements. However, the methods described could be applied to other 2D materials provided that the underlying projected charge density approximation remains valid which will ultimately set an upper bound on sample thickness.
Methods
Contributions of Residual Aberrations to the Image Intensity
The residual aberrations present in the experimental data were measured during corrector adjustment as; A1 = 2.2 nm, A2 = 23.25 nm, A3 = 278.2 nm, B2 = 26.34 nm and C3 = −1.162μm giving rise to an overall phase shift χ( g ) given by:
The image intensity (Extended data Fig. 2) due to the above residual aberrations can be also be calculated using the multislice method24,25,26 and compared to the intensity (Extended data Fig. 2) in the absence of these aberrations. Extended data Fig. 2 shows that the experimental values for A1, A2, B2 and C3 leads to only a small change δ(ΔI) in the slope of ΔΙ vs Δz (Equation 1) corresponding to an error of 3 pm in the determination of Δz. The parameters used for the multislice simulations are given in Extended Data Table I.
Contribution of Sample Tilt to the Image Intensity
To examine the effects of sample tilt on the image intensity simulated images of bilayer graphene at zero and five degrees tilt were calculated using the multislice method24,25,26 as shown in extended data Fig. 3a and b. Extended data Fig. 3c plots these simulated intensities, in the absence of residual aberrations vs. tilt angle for atoms in the top and bottom layers. From the vertical positions, Δz of the top and bottom atoms calculated using equation (1) the separation d cal can be calculated as the difference in height. The error in the layer spacing δd = d cal − d ideal as a function of tilt angle is given in extended data Fig. 3d and is of order 3 pm.
The Effect of Debye-Waller Factors on the Image Intensity
The mean displacement, <u2> of carbon atoms at the sample edge and in a perfect hexagonal ring have been measured independently from a reconstructed exit wave of a monolayer graphene sheet (Extended data Fig. 4a) using a previously reported method33. The value of <u2> averaged from typically 6000 atoms is ca. 150pm2 which is in good agreement with the value (~120pm2) measured using electron diffraction34. Histograms of <u2> from atoms in pristine hexagonal rings (190 atoms) and at the edge (130 atoms) where the atoms are under coordinated are given in extended data Fig. 4b. The value of <u2> of atoms at the edge extends to 0.2 Å2 as edge atoms are under coordinated. However, <u2> values of atoms in the defect sites and in pristine regions are indistinguishable. The values of the <u2> from the defect regions can be calculated35 for a temperature range 100–300 K, and with a defect concentration of 0.05% to 0.1%, <u2> lies between 0.05Å2 and 2Å2. We have quantitatively evaluated the effect of variations in the Debye-Waller factor on the image intensity δ(ΔI) with a reference, ΔI using <u2> = 0.01 Å2 as shown in extended data Fig. 4c which gives a maximum error in ΔI, corresponding ton <u2> = 2.0 of 7.2 pm in the determination of Δz.
References
Van Aert, S., Batenberg, K. J., Rossell, M. D., Erni, R. & Van Tendeloo, G. Three-dimensional atomic imaging of crystalline nanoparticles. Nature. 470, 347–377 (2011).
Xu, R. et al. Three-dimensional coordinates of individual atoms in materials revealed by electron tomography. Nature Materials 14, 1099–1103 (2015).
Midgely, P.A. & Dunin Borkowski, R.E. Electron tomography and holography in materials science. Nature Materials 8, 271–280 (2009).
Saghi, Z. & Midgely, P.A. Electron tomography in the (S)TEM: from nanoscale morphological analysis to 3D atomic imaging. Ann. Rev. Mater. Res. 42, 59–79 (2012).
Robertson, A. W. et al. Spatial control of defect creation in graphene at the nanoscale. Nat. Commun. 3, 1144 (2012).
Warner, J. H. et al. Dislocation-driven deformations in graphene. Science 337, 209–212 (2012).
Mermin, N. D. Crystalline Order in 2 dimensions. Phys. Rev. 176, 250 (1968).
Fasolino, A., Los, J. H. & Katsnelson, M. I. Intrinsic ripples in graphene. Nat. Mater. 6, 858–861 (2007).
O’Hare, A., Kusmartsev, F. V. & Kugel, K. I. A. Stable “Flat” Form of two-dimensional crystals: could graphene, silicene, germanene be minigap semiconductors? Nano Letts. 12, 1045–1052 (2012).
Meyer, J. C. et al. The structure of suspended graphene sheets. Nature 446, 60–63 (2007).
Wang, W. L. et al. Direct imaging of atomic-scale ripples in few-layer graphene. Nano Letts. 12(5), 2278–2282 (2012).
Bangert, U., Gass, M. H., Bleloch, A. L., Nair, R. R. & Geim, A. K. Manifestation of ripples in freestanding graphene in lattice images obtained in an aberration-corrected scanning transmission electron microscope. Phys. Stat. Sol. A 206(6), 1117–1122 (2009).
Gass, M. H. et al. Free-standing graphene at atomic resolution. Nature Nanotechnology 3, 676–681 (2008).
Meyer, J. C. et al. Direct imaging of lattice atoms and topological defects in graphene membranes. Nano Letts. 8(11), 3582–3586 (2008).
Kim, K. et al. Ripping graphene: preferred directions. Nano Letts. 12, 293–297 (2011).
Zhang, Y. B., Tan, Y. W., Stormer, H. L. & Kim, P. Experimental observation of the quantum Hall effect and Berry’s phase in graphene. Nature 438, 201–204 (2005).
Novoselov, K. S. et al. Two-dimensional gas of massless Dirac fermions in graphene. Nature 438, 197–200 (2005).
Warner, J. H. et al. Rippling graphene at the nanoscale through dislocation addition. Nano Letts. 13, 4937–4944 (2013).
Fan, Y., He, K., Tan, H., Speller, S. & Warner, J. H. Crack-free growth and transfer of continuous mono-layer graphene grown on melted copper. Chem. Mater. 26, 4984–4991 (2014).
Hutchison, J. L. et al. A versatile double aberration corrected, energy filtered TEM/STEM for materials science. Ultramicroscopy 103, 7–15 (2005).
Mukai, M. et al. Development of a 200 kV field emission gun with a double Wien filter monochromator. Ultramicroscopy 140, 37–43 (2014).
Barton, B. et al. Atomic resolution phase contrast imaging and in-line holography using variable voltage and dose rate. Microsc. and Microanl. 18(5), 1856–1857 (2012).
Lynch, D. F., Moodie, A. F. & O’Keefe, M. The use of the charge-density approximation in the interpretation of lattice images. Acta Crystallogr. A31, 300–307 (1975).
Cowley, J. M. & Moodie, A. F. Fourier images. IV. The phase grating. Proc. Phys. Soc. London 76, 378–384 (1960).
Cowley, J. M. & Moodie, A. F. The scattering of electrons by atoms and crystals. I. A new theoretical approach. Acta Crystallogr. 10, 609–619 (1957).
Goodman, P. & Moodie, A. F. Numerical evaluation of N-beam wave functions in electron scattering by the multislice method. Acta Crystallogr. A30, 280–290 (1974).
Howie, A. Hunting the Stobbs factor. Ultramicroscopy 98, 73–79 (2003).
Hytch, M. J. & Stobbs, W. M. Quantitative comparison of high resolution TEM images with image simulations. Ultramicroscopy 53, 191–203 (1994).
Boothroyd, C. B. Quantification of high-resolution electron microscope images of amorphous carbon. Ultramicroscopy 83, 159–168 (2000).
Warner, J. H., Lee, G.-D., He, K., Robertson, A. W. & Kirkland, A. I. Bond length and charge density variations within extended arm chair defects in graphene. ACS Nano 7, 9860–9866 (2013).
Meyer, R. R. & Kirkland, A. I. The effects of electron and photon scattering on signal and noise transfer properties of scintillators in CCD cameras used for electron detection. Ultramicroscopy 75, 23–33 (1998).
McMullan, G., Faruqi, A. R., Clare, D. & Henderson, R. Comparison of optimal performance at 300 keV of three direct electron detectors for use in low dose electron microscopy. Ultramicroscopy 147, 156–163 (2014).
Van Dyck, D., Jinschek, J. R. & Chen, F-R. ‘Big bang’ tomography as a route to atomic resolution electron tomography. Nature 486, 243–246 (2012).
Allen, C. S. et al. Temperature dependence of atomic vibrations in mono-layer graphene. J. Appl. Phys. 118, 074302 (2015).
Thomas, S., Mrudul, M. S., Ajith, K. M. & Valsakumar, M. C. Young’s modulus of defective graphene sheet from intrinsic thermal vibrations. J. Phys.: Conf. Ser. 759, 012048 (2016).
Acknowledgements
A.I.K. and J.W. acknowledge financial support from EPSRC (Platform Grants EP/F048009/1 and EP/K032518/1) and from the EU (ESTEEM2 (Enabling Science and Technology through European Electron Microscopy), 7th Framework Program of the European Commission. D.V.D. acknowledges financial support from the Fund for Scientific Research - Flanders (FWO) under Project Nos. VF04812N and G.0188.08. F.R.C. acknowledges support from NSC 96-2628-E-007-017-MY3 and NSC 101-2120-M-007-012-CC1.
Author information
Authors and Affiliations
Contributions
A.I.K. and J.W. recorded the HRTEM image series using the JEOL 2200MCO and designed the experiments. D.V.D. developed the theory. L.G.C. and F.R.C. developed the program codes to test the theory and analysed the experimental data. All authors drafted and commented on the paper.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Chen, LG., Warner, J., Kirkland, A.I. et al. Snapshot 3D Electron Imaging of Structural Dynamics. Sci Rep 7, 10839 (2017). https://doi.org/10.1038/s41598-017-10654-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-10654-x
- Springer Nature Limited
This article is cited by
-
A 3D map of atoms in 2D materials
Nature Materials (2020)