Abstract
The strongly enhanced electron–electron interactions in semiconducting moiré superlattices formed by transition metal dichalcogenide heterobilayers have led to a plethora of intriguing fermionic correlated states. Meanwhile, interlayer excitons in a type II aligned heterobilayer moiré superlattice, with electrons and holes separated in different layers, inherit this enhanced interaction and suggest that tunable correlated bosonic quasiparticles with a valley degree of freedom could be realized. Here we determine the spatial extent of interlayer excitons and the band hierarchy of correlated states that arises from the strong repulsion between interlayer excitons and correlated electrons in a WS2/WSe2 moiré superlattice. We also find evidence that an excitonic Mott insulator state emerges when one interlayer exciton occupies one moiré cell. Furthermore, the valley polarization of the excitonic Mott insulator state is enhanced by nearly one order of magnitude. Our study demonstrates that the WS2/WSe2 moiré superlattice is a promising platform for engineering and exploring new correlated states of fermion, bosons and a mixture of both.
Similar content being viewed by others
Data availability
Source data are provided with this paper. All other data that support the plots within this paper and other findings of this study are available from the corresponding authors upon reasonable request.
Code availability
The twisted bilayer structure construction, atomic relaxations and electronic band structure calculations presented in this paper were carried out using publicly available codes. Our findings can be fully reproduced by the use of these codes and by following the procedure outlined in the paper.
References
Regan, E. C. et al. Mott and generalized Wigner crystal states in WSe2/WS2 moiré superlattices. Nature 579, 359–363 (2020).
Tang, Y. et al. Simulation of Hubbard model physics in WSe2/WS2 moiré superlattices. Nature 579, 353–358 (2020).
Huang, X. et al. Correlated insulating states at fractional fillings of the WS2/WSe2 moiré lattice. Nat. Phys. 17, 715–719 (2021).
Xu, Y. et al. Correlated insulating states at fractional fillings of moiré superlattices. Nature 587, 214–218 (2020).
Jin, C. et al. Stripe phases in WSe2/WS2 moiré superlattices. Nat. Mater. 20, 940–944 (2021).
Li, T. et al. Quantum anomalous Hall effect from intertwined moiré bands. Nature 600, 641–646 (2021).
Li, T. et al. Continuous Mott transition in semiconductor moiré superlattices. Nature 597, 350–354 (2021).
Stansbury, C. H. et al. Visualizing electron localization of WS2/WSe2 moiré superlattices in momentum space. Sci. Adv. 7, eabf4387 (2021).
Hubbard, J. Electron correlations in narrow energy bands. Proc. R. Soc. Lond. Ser. A 276, 238–257 (1963).
Wu, F., Lovorn, T., Tutuc, E. & Macdonald, A. H. Hubbard model physics in transition metal dichalcogenide moiré bands. Phys. Rev. Lett. 121, 26402 (2018).
Wang, G. et al. Colloquium: excitons in atomically thin transition metal dichalcogenides. Rev. Mod. Phys. 90, 21001 (2018).
Xu, X., Yao, W., Xiao, D. & Heinz, T. F. Spin and pseudospins in layered transition metal dichalcogenides. Nat. Phys. 10, 343–350 (2014).
Mak, K. F. & Shan, J. Photonics and optoelectronics of 2D semiconductor transition metal dichalcogenides. Nat. Photon. 10, 216–226 (2016).
Bloch, I., Dalibard, J. & Zwerger, W. Many-body physics with ultracold gases. Rev. Mod. Phys. 80, 885–964 (2008).
Gemelke, N., Zhang, X., Hung, C. L. & Chin, C. In situ observation of incompressible Mott-insulating domains in ultracold atomic gases. Nature 460, 995–998 (2009).
Rivera, P. et al. Interlayer valley excitons in heterobilayers of transition metal dichalcogenides. Nat. Nanotechnol. 13, 1004–1015 (2018).
Jin, C. et al. Ultrafast dynamics in van der Waals heterostructures. Nat. Nanotechnol. 13, 994–1003 (2018).
Gersch, H. A. & Knollman, G. C. Quantum cell model for bosons. Phys. Rev. 129, 959–967 (1963).
Miao, S. et al. Strong interaction between interlayer excitons and correlated electrons in WSe2/WS2 moiré superlattice. Nat. Commun. 12, 3608 (2021).
Chen, D. et al. Tuning moiré excitons and correlated electronic states through layer degree of freedom. Nat. Commun. 13, 4810 (2022).
Chen, D. et al. Excitonic insulator in a heterojunction moiré superlattice. Nat. Phys. 18, 1171–1176 (2022).
Wang, X. et al. Intercell moiré exciton complexes in electron lattices. Nat. Mater. 22, 599–604 (2023).
Jin, C. et al. Identification of spin, valley and moiré quasi-angular momentum of interlayer excitons. Nat. Phys. 15, 1140–1144 (2019).
Xiong, R. et al. Correlated insulator of excitons in WSe2/WS2 moiré superlattices. Science 380, 860–864 (2023).
Yuan, L. et al. Twist-angle-dependent interlayer exciton diffusion in WS2–WSe2 heterobilayers. Nat. Mater. 19, 617–623 (2020).
Lagoin, C., Suffit, S., Baldwin, K., Pfeiffer, L. & Dubin, F. Mott insulator of strongly interacting two-dimensional semiconductor excitons. Nat. Phys. 18, 149–153 (2022).
Lagoin, C. et al. Extended Bose–Hubbard model with dipolar excitons. Nature 609, 485–489 (2022).
Sugawa, S. et al. Interaction and filling-induced quantum phases of dual Mott insulators of bosons and fermions. Nat. Phys. 7, 642–648 (2011).
Yu, H., Liu, G. B., Tang, J., Xu, X. & Yao, W. Moiré excitons: from programmable quantum emitter arrays to spin–orbit-coupled artificial lattices. Sci. Adv. 3, e1701696 (2017).
Yu, H., Liu, G.-B. & Yao, W. Brightened spin-triplet interlayer excitons and optical selection rules in van der Waals heterobilayers. 2D Mater. 5, 35021 (2018).
Kim, J. et al. Observation of ultralong valley lifetime in WSe2/MoS2 heterostructures. Sci. Adv. 3, e1700518 (2017).
Wang, X. et al. Light-induced ferromagnetism in moiré superlattices. Nature 604, 468–473 (2022).
Hao, K., Shreiner, R., Kindseth, A. & High, A. A. Optically controllable magnetism in atomically thin semiconductors. Sci. Adv. 8, eabq7650 (2022).
Naik, S., Naik, M. H., Maity, I. & Jain, M. Twister: construction and structural relaxation of commensurate moiré superlattices. Comput. Phys. Commun. 271, 108184 (2022).
Thompson, A. P. et al. LAMMPS—a flexible simulation tool for particle-based materials modeling at the atomic, meso, and continuum scales. Comput. Phys. Commun. 271, 108171 (2022).
Plimpton, S. et al. LAMMPS molecular dynamics simulator. Sandia National Laboratories https://lammps.org/ (2023).
Soler, J. M. et al. The SIESTA method for ab initio order-N materials simulation. J. Phys. Condens. Matter 14, 2745–2779 (2002).
Perdew, J. P. & Zunger, A. Self-interaction correction to density-functional approximations for many-electron systems. Phys. Rev. B 23, 5048–5079 (1981).
Acknowledgements
We thank C. Jin for the helpful discussions. Z.L. and S.-F.S. acknowledge support from NYSTAR through Focus Center-NY-RPI Contract C150117. The device fabrication was supported by the Micro and Nanofabrication Clean Room at Rensselaer Polytechnic Institute (RPI). S.-F.S. also acknowledges the support from NSF (Career Grant DMR-1945420, DMR-2104902 and ECCS-2139692). X.H., Q.W. and Y.-T.C. acknowledge support from NSF under awards DMR-2104805 and DMR-2145735. The optical spectroscopy measurements were supported by the Air Force Office of Scientific Research (AFOSR) under DURIP awards through Grants FA9550-20-1-0179 and FA9550-23-1-0084. I.M. acknowledges funding from the European Union’s Horizon 2020 Research and Innovation programme under the Marie Skłodowska-Curie Grant agreement no. 101028468. This work used the ARCHER2 UK National Supercomputing Service (https://www.archer2.ac.uk). S.T. acknowledges support from DOE-SC0020653, Applied Materials Inc., NSF CMMI 1825594, NSF DMR-1955889, NSF CMMI-1933214, NSF DMR-1904716, NSF 1935994 and NSF ECCS 2052527 and DMR 2111812. K.W. and T.T. acknowledge support from the Elemental Strategy Initiative conducted by the MEXT, Japan, Grant Numbers JPMXP0112101001 and JSPS KAKENHI, Grant Numbers 19H05790 and JP20H00354.
Author information
Authors and Affiliations
Contributions
S.-F.S. conceived the project. Y.M., Z.L. and D.C. fabricated heterostructure devices. Z.L., L.M., L.Y. and Y.M. performed the optical spectroscopy measurements. M.B. and S.T. grew the TMDC crystals. T.T. and K.W. grew the BN crystals. I.M. and J.L. performed the DFT calculations. S.-F.S., Y.-T.C., Z.L., Y.M., Xiaotong Chen and Xinyue Chen analysed the data. S.-F.S. and Y.-T.C. wrote the paper with input from all authors.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Physics thanks Nadine Leisgang, Fengcheng Wu and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Extended data
Extended Data Fig. 1 Zoom-ins of the doping-dependent PL spectra.
(a) and (b) are the Zoom-ins of doping-dependent PL spectra in Fig. 1c,d, respectively.
Extended Data Fig. 2 PL spectra of an H-stacked device showing more fractional fillings.
(a) and (b) are the doping-dependent PL spectra measured on device H5 using an excitation power of 0.2 µW and 300 µW, respectively. A CW laser with photon energy centered at 1.70 eV was used for the optical excitation, and all data were taken at a temperature of 5.0 K.
Extended Data Fig. 3 Power-dependent PL spectra for different R-stacked and H-stacked devices around n = 0.
(a), (b) and (c) are the power-dependent PL spectra of R-stacked devices R1, R2 and R3, respectively. (d), (e) and (f) are the power-dependent PL spectra of H-stacked devices H2, H3 and H4, respectively. Black, red, and blue line show PL spectra under low, medium, and high excitation power. A CW laser with photon energy centered at 1.96 eV was used for the optical excitation, and all data were taken at a temperature of 4–10 K.
Extended Data Fig. 4 Helicity-resolved doping-dependent PL spectra for R-stacked WS2/WSe2 moiré bilayers under different excitation powers.
(a) and (b) are the measured right (σ+) and left circularly (σ-) polarized doping-dependent PL spectra of device R1, under a σ+ excitation with the excitation power of 2 µW. (c) and (d) are σ+ and σ- PL spectra under a σ+ excitation with an excitation power of 390 µW. A CW laser with photon energy centered at 1.70 eV was used for the optical excitation, and all data were taken at a temperature of 5.0 K.
Extended Data Fig. 5 Helicity-resolved doping-dependent PL spectra for H-stacked moiré bilayers under different power.
(a) and (b) are the measured right (σ+) and left circularly (σ-) polarized doping-dependent PL spectra of device H1, under a σ+ excitation with an excitation power of 2 µW. (c) and (d) are σ+ and σ- PL spectra under a σ+ excitation with an excitation power of 390 µW. A CW laser with photon energy centered at 1.70 eV was used for the optical excitation, and all data were taken at a temperature of 5.0 K.
Extended Data Fig. 6 Helicity-resolved PL spectra of device R1 and H1 for various filling factors and under different excitation powers.
(a) and (b) are the PL spectra of device R1 at n = 0 under excitation powers of 2 µW and 390 µW, respectively. The red and blue lines represent measured right (σ+) and left circularly (σ-) polarized PL spectra, respectively, under the σ+ excitation. (c) and (d) are the PL spectra of device R1 at n = 3 under the excitation power of 2 µW and 390 µW, respectively. (e) and (f) are the PL spectra of device H1 at n = 0 with excitation power of 2 µW and 390 µW, respectively. These data are extracted from Extended Data Figs. 4 and 5. The data in (c) are offset for the clarity of presentation.
Supplementary information
Supplementary Information
Supplementary Sections 1–12, Figs. 1–11 and Table 1.
Source data
Source Data Fig. 1
Numerical source data for Fig. 1c–f.
Source Data Fig. 2
Numerical source data for Fig. 2a,b.
Source Data Fig. 3
Numerical source data for Fig. 3a,b,d,e.
Source Data Fig. 4
Numerical source data for Fig. 4a–d.
Source Data Extended Data Fig. 2
Numerical source data for Extended Data Fig. 2a,b.
Source Data Extended Data Fig. 3
Numerical source data for Extended Data Fig. 3a–f.
Source Data Extended Data Fig. 4
Numerical source data for Extended Data Fig. 4a–d.
Source Data Extended Data Fig. 5
Numerical source data for Extended Data Fig. 5a–d.
Source Data Extended Data Fig. 6
Numerical source data for Extended Data Fig. 6a–f.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Lian, Z., Meng, Y., Ma, L. et al. Valley-polarized excitonic Mott insulator in WS2/WSe2 moiré superlattice. Nat. Phys. 20, 34–39 (2024). https://doi.org/10.1038/s41567-023-02266-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s41567-023-02266-2
- Springer Nature Limited
This article is cited by
-
Tunable exciton valley-pseudospin orders in moiré superlattices
Nature Communications (2024)
-
When excitons crystallize
Nature Physics (2024)
-
Excitonic Complexes in Two-Dimensional Transition Metal Dichalcogenides
Nature Communications (2023)