Abstract
To achieve adhesive and conformable wearable electronics, improving stretchable transparent electrode (STE) becomes an indispensable bottleneck needed to be addressed. Here, we adopt a nonuniform Young’s modulus structure with silver nanowire (AgNW) and fabricate a STE layer. This layer possesses transparency of >88% over a wide spectrum range of 400–1000 nm, sheet resistance below 20 Ω sq−1, stretchability of up to 100%, enhanced mechanical robustness, low surface roughness, and good interfacial wettability for solution process. As a result of all these properties, the STE enables the fabrication of a highly efficient ultraflexible wearable device comprising of both organic photovoltaic (OPV) and organic photodetector (OPD) parts with high mechanical durability and conformability, for energy-harvesting and biomedical-sensing applications, respectively. This demonstrates the great potential of the integration of OPVs and OPDs, capable of harvesting energy independently for biomedical applications, paving the way to a future of independent conformable wearable OPV/OPDs for different applications.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Introduction
Wearable organic photovoltaics (WOPVs) for self-powered electronic skins, human–machine interactions (HMIs), real-time health monitoring, internet of things (IoTs) require a strong and comfortable adhesion that adapts to the complexity of human’s skin movement without compromising their performance and lifetime1,2,3,4. Devices that can conform to the skin surface seamlessly would provide an accurate and precise measurement of any physiological signal of interest5. Numerous studies on flexible transparent electrodes have achieved mechanical bending durable OPV devices with performance comparable to indium tin oxide (ITO) analogs6,7,8. Among different flexible transparent electrodes7,9,10,11,12,13,14,15,16, silver nanowires (AgNWs) are perceived as the promising alternative for flexible OPV devices owing to some of its remarkable properties such as low percolation threshold, superior transparency, high electrical conductivity, and excellent flexibility17. Nonetheless, AgNW electrodes suffer from several shortcomings, such as high surface roughness and poor adhesion to substrates, leading to severe leakage current and poor mechanical robustness18. To improve device conformation to skin irregular surface stretches for portable and WOPV devices, the development of stretchable transparent electrodes (STEs) which utilizes a soft substrate as an interface between the device and human skin is of particular interest. Recently, the incorporation of grid-like AgNW electrode on the plastic polyethylene terephthalate (PET) substrates is shown to lower the surface roughness for highly efficient flexible single-junction and tandem OPV device2. The combination AgNW/PET device is also exhibited to have high bending durability at a bending radius of 3 mm and retained >90% of its initial efficiency after 1000 bending cycles19. These studies independently indicate the importance of the integration between AgNW and the underlying substrate to have a better adhesion for a highly robust WOPV device2,10,19. However, the plastic polymer substrates, such as PET, polyethylene naphthalate (PEN), perylene, and polyimide (PI)3,20 applied in these OPV devices, possessing Young’s moduli of 2.8–6.1 GPa21, are unable to utilize the stretchability of the AgNW network. While reports have shown that AgNWs integrated with more elastic polymers such as polydimethylsiloxane (PDMS), polyurethane (PU), and polyurethane acrylate (PUA), which have a similar Young’s modulus to the human body, enable the network to withstand a large stretchability of over 50%22,23,24,25, the poor chemical stability of the elastic polymer substrate remains a huge challenge for high-performance WOPV devices using AgNW-based STEs. To improve the chemical stability of the polymer, a lamination strategy was introduced that avoids the direct contact of chemical reagents, but this creates a high contact resistance, leading to a poor performance of the organic thin-film devices26. Other than focusing on the conformability of a substrate, the tensile strength has been shown to be one of the important indicators for the mechanical robustness and durability of the materials27.
Organic photodetectors (OPDs) with a near-infrared (NIR) absorbing bulk-heterojunction (BHJ) configuration on the other hand, has also attracted increasing attention for their potential in biomedical wearable electronic application5,28,29. In particular, NIR can play a prominent role in biomedical and clinical applications due to the deep penetration depth of NIR photons transmitting beyond the skin surface, making the high transparency of AgNW-based STE in the NIR region an appealing component in wearable OPDs (WOPDs) for biomedical sensing30. However, the demonstration of such conformable WOPDs based on AgNW electrodes has been scarce for biological sensing. To meet the requirements for wearable application, the electrode should achieve several vital features simultaneously: excellent conductivity and high transparency that are crucial for device performance; mechanical deformability/stretchability and robust flexibility for maintaining continuous conducting paths in dynamic operating environment; good chemical stability, and wettability for low-cost solution process; smooth surface for decreasing contact resistance and avoiding large leakage current2,17,21,31.
Here, we demonstrate the fabrication of AgNW-based STEs using a nonuniform Young’s modulus structure. The nonuniform Young’s modulus structure endows the STEs with enhanced mechanical durability and tensile strength, high chemical stability, and improved interfacial wettability for the organic active layers. The obtained electrode shows a sheet resistance below 20 Ω sq−1, transparency of >88% (including the substrate), surface roughness of 2.24 nm, and a stretchability of up to 100%, all of which meet the basic requirements for a wearable electronic application. The WOPV device fabricated using said STE achieved performance comparable to its traditional rigid ITO-based counterpart and maintained >96% of the initial power conversion efficiency (PCE) after 4000 bending cycles at an extreme bending radius of 0.5 mm, indicating excellent mechanical stability. The WOPD which adopts the same device structure and STE demonstrates a successful heart rate detection for biomedical application. Altogether, the study herein illustrates the potential of AgNW-based STE for conformal dual-purpose WOPD biomedical sensing and WOPV energy-harvesting devices.
Results and discussion
STE with nonuniform Young’s modulus structure
The procedure for fabricating the STE with nonuniform Young’s modulus structure is schematically displayed in Fig. 1a. AgNW network was fabricated onto an octadecyltrichlorosilane-modified glass (OTS/glass) via spin-coating. The OTS modification provides a low surface-energy interface32, which is beneficial for the subsequent mechanical peeling processes to obtain an embedded STE. Cross-linked polyvinyl alcohol (C-PVA) and PDMS were successively applied onto AgNW network to form a bilayer polymer substrate forming a nonuniform Young’s modulus matrix by the spin-coating process. Owing to the good mechanical stretchability and biocompatibility of PDMS, it has been widely utilized in skin-like and wearable electronics33. However, PDMS is hardly compatible with common organic solvent due to its poor chemical resistance and is a non-preferred solvent in the manufacturing process of various chemical treatments. C-PVA adopted here has been demonstrated with the advantages of flexibility, transparency, ultrathin, and biocompatibility in the previous reports34. Moreover, C-PVA is solvent-resistant, which remedies the shortage of PDMS. Finally, the whole electrode structure, including AgNW network, C-PVA, and PDMS, was easily peeled off from the OTS/glass and flipped over to form a STE. The upper right inset of Fig. 1a shows that the AgNW network is embedded in the nonuniform Young’s modulus polymer matrix composed of flexible C-PVA and elastic PDMS. The ultrathin C-PVA film acts as the buffer layer located between AgNW conductive layer and hydrophobic PDMS. The AgNW/C-PVA/PDMS electrode, employing the embedded structure, is coplanar and flat. The fabrication process for STE is simple and feasible, indicating a great potential for all-solution, low-cost fabrication.
Due to the excellent transparency of all the components (AgNW network, C-PVA, and PDMS) within the STE structure, the prepared electrode including the soft substrate presents an average transmittance (Tavg) of 88%, over the wide range of 400–1000 nm (Fig. 1b). Compared to commercial rigid transparent ITO electrode (Tavg of 85%) on glass, the stretchable transparent AgNW/C-PVA/PDMS electrode shows higher transparency, especially in the wavelength range of 600–1000 nm. Due to high tissue transparency in the NIR region, the stretchable transparent AgNW/C-PVA/PDMS electrode is promising for biological applications that require, in addition to high conformability, transparency in the NIR wavelength region35. As shown in Fig. 1c, the optical transparency and electrical properties of AgNW-based electrodes can be tuned by modulating the spinning speed. The sheet resistance (Rs) of AgNW network prepared by spin-coating at 2000 rpm was 12.2 ± 0.7 Ω sq−1 with Tavg of 84.2 ± 3.1%. When the spinning speed increased to 6000 rpm, the average transmittance and sheet resistance increased up to 90.7 ± 2.7% and 22.3 ± 0.5 Ω sq−1, respectively. Along with the increase of spinning speed, both thickness and AgNW area coverage decreased, and the resulted sparse network led to the increase of transmittance and sheet resistance. The thickness of the AgNW network obtained by different spinning speed can be found in Supplementary Table 1. The superior electrical conductivity and optical transparency of AgNW/C-PVA/PDMS which are comparable to the performances of commercial rigid ITO are much higher than those of CNTs and graphene reported36, indicating the application capability of stretchable transparent AgNW-based electrode in wearable optoelectronic devices. Considering the integration of AgNW-based STE into thin-film devices, surface roughness is another important factor that affects the device’s performance. The atomic force microscope (AFM) image in Fig. 1d presents that the surface roughness of AgNW/C-PVA/PDMS is 2.24 nm. The flat and smooth surface avoids severe leakage current caused by protruding nanowires in organic thin-film devices for the active layer of ~100 nm thickness. It is noteworthy that the voids within AgNW network are filled with C-PVA, which may enhance the adhesion and tightness at the wire–wire junctions, and prevent PDMS from directly contacting with organic solvents.
To investigate the mechanical properties of the polymer matrix, the tensile tests of C-PVA, PDMS, and C-PVA/PDMS were performed as illustrated in Fig. 1e. C-PVA with a high Young’s modulus of 1.3 GPa possesses a high tensile strength of 64.6 MPa, but poor stretchability with the elongation at break occurring at only 5.5% tensile strain; PDMS with a low Young’s modulus of 2.8 MPa has a stretchability up to 165%, but a low tensile strength of 4.8 MPa. Elongation at break is defined as (Lf − L0)/L0(100%), where L0 and Lf represent the original length and the length at the break, respectively. In comparison with pristine C-PVA and PDMS, the mechanical properties of combined C-PVA/PDMS have been prominently improved. The tensile strength and elongation at break of C-PVA/PDMS were 6.3 MPa and 252%, which increased 25% and 51.8% to that of PDMS. Obviously, C-PVA/PDMS hybrid polymer matrix with the nonuniform Young’s modulus structure makes up for the mechanical deficiency of C-PVA and PDMS. The cause may be that during the large tensile strain, amounts of impact energy on C-PVA/PDMS is dissipated by the cracks that occurred in C-PVA, which in turn improves the impact strength of the hybrid material. The optical images of C-PVA/PDMS under different tensile strains can be found in Supplementary Fig. 1. Despite the distinctly enhanced mechanical tensile strength of the hybrid polymer, Young’s modulus of C-PVA/PDMS (2.9 MPa) is still much approximate to PDMS (2.8 MPa). The low Young’s modulus is beneficial for realizing the soft conformal contact with expandable skins, tissues, and organs of the human being for bio-integrated electronic applications37. As can be seen in Fig. 1f, g, the STEs could be conformally coupled onto the human skin and kept seamless contact with the thumbprint and the wrinkled skin by Van der Waals force. Due to the high transparency, the STEs can also serve for invisible wearable electronics with esthetics. The enhanced mechanical properties make the electrode withstand various deformations, such as stretching, twisting, and crumpling. Due to the stress relief in a bilayer structure, the AgNW/C-PVA/PDMS electrode is able to recover from the crumpling without mechanical damage, which contributes greatly to effective manipulation during practical application. This strategy provides a simple and efficient approach by recombining the advantages of PDMS and C-PVA into the STE with a double-layered scheme, and achieves the polymer matrix combined high tensile strength and low Young’s modulus.
Furthermore, the electrical properties of flexible electrodes were evaluated under mechanical deformations. Figure 2a compares the electrical resistance changes of ITO/PET, AgNW/PDMS, and AgNW/C-PVA/PDMS electrodes under different outcurve-bending radii (r). For commercial flexible ITO/PET electrode, the relative change in resistance increased dramatically with bending radius decreased below 5 mm due to its brittle nature, whereas the conductivity of AgNW-based electrodes remained relatively stable even at the extremely small radius of 0.2 mm. Long-term reliability under cyclic mechanical stress is of great significance for the practical use of flexible electrodes. Taking this into account, the real-time bending measurement was conducted in Fig. 2b. At a constant bending radius of 5 mm, the AgNW-based embedded electrodes can withstand more than 4000 bending cycles without noticeable resistance variation. However, the resistance of ITO/PET had increased about ~40 times to its original resistance after the cyclic bending. The inset provides the partially enlarged views of the curves for AgNW/PDMS and AgNW/C-PVA/PDMS. The resistance dynamic range of AgNW/C-PVA/PDMS was much smaller than that of AgNW/PDMS during cyclic bending, indicating the positive effect of C-PVA interlayer for mechanical robustness and stability. Figure 2c, d also shows the beneficial effects of the C-PVA interlayer on the mechanical stretchability of the STEs. Figure 2c illustrates the measured resistance change of embedded AgNW/PDMS and AgNW/C-PVA/PDMS as a function of increasing tensile strain. The AgNW/PDMS showed a significant increase in resistance with the strain increasing over 40% in comparison with AgNW/C-PVA/PDMS electrode. During the cyclic stretch-release test employing 0–20% tensile strain, the resistance variation of AgNW/PDMS continuously increased as more cycles were completed (Fig. 2d). Clearly, the conductivity of AgNW/C-PVA/PDMS hold relatively stable during 4000 cycles of deformation, indicating good mechanical stability during the stretching and releasing cycles. As mentioned above, the hybrid C-PVA/PDMS polymer substrate showed better tensile strength than PDMS. The poor stability of AgNWs/PDMS electrodes may origin from the low strength of PDMS and vastly mismatched Young’s modulus between AgNW and PDMS. The ultrathin flexible C-PVA of 270 nm adopted here serving as an effective buffer layer between AgNW and PDMS due to the moderate Young’s modulus value between metallic materials and elastic polymer. Besides, the conductivity of the AgNW/C-PVA/PDMS electrodes did not decay at all even after conducting 50 tape tests without exfoliation (Supplementary Fig. 2), indicating the strong adhesion between PDMS and C-PVA thin films by noncovalent bonding. In Fig. 2e, the stretchable transparent AgNW/C-PVA/PDMS electrode, serving as the interconnectors of a yellow commercial LED, presents excellent conductivity under different tensile strains. During the stretching of the AgNW/C-PVA/PDMS interconnectors, the yellow LED showed bright yellow light, indicating the outstanding mechanical stretchability and good conductivity of the AgNW/C-PVA/PDMS conductor. The LED could be lit up even at the tensile strain of 72.4%, which met the basic elastic needs of the human body38,39.
Conformable OPVs with STEs for harvesting energy
Based on the AgNW/C-PVA/PDMS STEs, the conformable OPVs for harvesting energy were fabricated with inverted structure as shown in Fig. 3a. The conformable transparent AgNW/C-PVA/PDMS structure acts as both the bottom transparent electrode and the soft substrate. The typical efficient non-fullerene PM6:Y6 bulk heterojunction (BHJ) is employed here as the active layer of the ultraflexible conformable OPVs. Aluminum-doped zinc oxide (AZO) with the optimized aluminum atomic ratio of 3 at% was adopted as an electron transfer layer (ETL). Compared with traditional zinc oxide (ZnO) ETL, AZO fills the voids among nanowires and helps increase the short-circuit current density (Jsc) of the OPVs due to the better conductivity (Supplementary Fig. 3)40. The MoO3 (10 nm)/Ag (100 nm) was evaporated on the active layer as the anode. Figure 3b shows an energy-level diagram of the conformable OPVs. The representative current density-voltage (J–V) characteristics of the PM6:Y6-based OPVs with ITO/glass and AgNW/C-PVA/PDMS electrodes under 1 sun illumination are presented in Fig. 3c. The photovoltaic parameters of corresponding devices are summarized in Table 1. For the rigid cells with commercial ITO/glass (Rs of 12 Ω sq−1, Tavg of 85%) electrodes show a PCE of 15.8%, an open-circuit voltage (Voc) of 0.83 V, a Jsc of 24.9 mA cm−2, and a fill factor of 76.2%. The conformable cells based on AgNW/C-PVA/PDMS STEs (Rs of 18 Ω sq−1, Tavg of 90%) show a PCE of 15.2%, a Voc of 0.83 V, a Jsc of 25.0 mA cm−2, and a fill factor of 73.2%. The integrated Jsc values calculated using the external photovoltaic quantum efficiency (EQE) spectra (Supplementary Fig. 4) were 23.8 and 24.0 mA cm−2 for the OPV devices based on the ITO/glass and AgNW/C-PVA/PDMS electrodes, respectively. The results coincided with the Jsc measured under the solar simulator with a deviation <5%. It is seen that the performances of conformable OPVs are comparable to those of rigid ITO-based devices and has been at the top level among the reported flexible PM6:Y6 devices with inverted structure7,41,42.
The mechanical robustness and durability of the soft OPVs are evaluated as shown in Fig. 3d, e. The parameters of the conformable OPV devices almost remained unchanged, with an extreme bending radius down to 0.2 mm. The durability of conformable OPV devices was evaluated by employing cyclic bending tests with 4000 cycles at the bending radius of 0.5 mm (Fig. 3e), which is one order of magnitude lower than the most cyclic bending radii applied on the reported flexible OPVs2,7,19. The bending strain is estimated as ~3%. The inset presents the optical image of the conformal solar cells coiling around a needle. Moreover, the conformable OPVs based on the STEs retained over 96% of their original PCE throughout 4000 bending cycles, demonstrating extraordinary bending durability.
Conformable wearable OPDs with STEs for heart rate detection
Based on the same device structure as depicted above, highly flexible and conformable wearable organic photodetectors were also achieved for real-time heart rate detection as shown in Fig. 4, demonstrating the dual-use capacity of conformable OPV devices. Compared to traditional rigid detecting systems, the conformable photodetectors integrated with light sources are able to monitor heart rate through photoplethysmography (PPG) noninvasively for wearable health and wellness trackers with great convenience and comfort1. With the thin and soft AgNW/C-PVA/PDMS electrodes, the skin-like OPDs enable mechanical compatibility with soft tissues, as shown in Fig. 4a, the application for real-time biological signal detection was realized by conformally attaching the OPDs on the finger. Then the underneath incident red or NIR light first penetrates the finger and gets into the conformable photodetector. The transmitted light intensity changes along with the heartbeat due to the changing subcutaneous blood volume, and the electrical signal fluctuation of the detector occurs with the heartbeat28.
The EQE values of PM6:Y6 photodetectors with AgNW/C-PVA/PDMS and ITO/glass electrodes under different bias voltages are shown in Fig. 4b. Compared with traditional rigid ITO-based devices, the conformable OPDs with AgNW/C-PVA/PDMS electrodes present higher EQE values, especially in the wavelength of 700–900 nm due to the higher transparency of AgNW-based bottom electrodes. For example, the EQE value at 820 nm of the conformable device is 15.2% higher than that of ITO-based devices under the 0 V bias. The conformable devices behave with a very weak dependence on the bias voltage, indicating the efficient charge extraction. The spectral responsivity of the conformable and rigid devices measured under zero bias is shown in Supplementary Note 1 and Supplementary Fig. 543. The peak responsivity of the rigid device is 0.52 A W−1 at 850 nm. While the conformable device displays a higher responsivity of 0.54 A W−1 at 850 nm benefiting from the improved NIR EQE. The experimental dark current density (Jd) characteristics of OPD devices employing AgNW/C-PVA/PDMS and ITO/glass electrodes are shown in Fig. 4c. It was found that the Jd values for the two devices are comparable (5.9 × 10−10 and 3.3 × 10−10 A cm−2 at −0.1 V for AgNW/C-PVA/PDMS and ITO/glass devices, respectively). The ultra-low dark current density and the mechanical conformability of the OPD devices are in favor of achieving high-quality physiological signals for broad utility in biomedical applications44. To investigate the capability of photodetectors operating at a wide range of light intensities, the current density of the conformable device under 850 nm illumination with light intensity ranging from 0.12 nW cm−2 to 1.93 mW cm−2 are measured (Supplementary Fig. 6). Figure 4d shows that the current density exhibits broad linearity within the test range, and the linear dynamic range (LDR) is calculated as 129 dB (Supplementary Note 2)45, indicating the good light detect the capability of conformable OPD. Figure 4e shows the measured total noise under −0.1 V bias is frequency-independent at the low-frequency range, and the noise spectral density is around 1.05 × 10−14 A Hz−1/2 at 10 Hz, which is close to the calculated noise of 8.7 × 10−15 A Hz−1/2. The calculation can be found in Supplementary Note 3, which indicates that the noise is mainly dominated by the shot noise and Johnson noise. As shown in Fig. 4f, the corresponding D* profiles calculated using the noise current are derived according to Supplementary Note 4. The peak D* of the conformable OPD reaches 1.67 × 1013 Jones at 850 nm, which is comparable to commercial silicon-based photodiodes46.
Figure 4g, h shows the electrical signals of the conformal and rigid detectors with heartbeat under the 720 and 850 nm source light. Due to the reduced photon scattering, the sensing of optical signals at 850 nm wavelengths is more distinct for heart rate detection than that measured at 720 nm. At the same source light, the AgNW-based conformable device presents better sensing properties than ITO-based rigid devices, attributing to the high transparency in the NIR region and mechanical conformability. The calculated heart rate values from conformable and rigid OPDs are 69.6 and 67.1 beats per minute, respectively. The heart rate values with acceptable deviation <4% were observed. The demonstration of heart rate sensing highlights a potential application of AgNW-based conformable OPDs in wearable devices.
In summary, the STE made using an AgNW network with a nonuniform Young’s modulus structure has a high transmittance in the wide spectrum range, a low sheet resistance, an approaching ideal stretchability, a low surface roughness, and a superior interface wettability. The outstanding characteristics of the STEs enable the fabrication of a highly efficient conformal WOPV device, with high mechanical durability even at an extreme bending radius of 0.5 mm. The PCE of said device, comparable to its ITO analog maintained 96% of it after 4000 bending cycles. Utilizing the same WOPV device architecture, the conformable WOPD was successfully demonstrated for heart rate detection application, indicating STE potential for conformal dual-purpose wearable applications such as health monitoring WOPD and energy-harvesting WOPV device simultaneously, as demonstrated in the study herein. This study paves the way to realize multifunctional WOPV/OPDs that are not only wearable but more importantly, conformable to skin surface seamlessly in the future.
Methods
Electrode fabrication
A 0.25 wt% AgNW dispersion with a diameter of 30 nm was purchased from Gu’ NANO without further treatment. The AgNW dispersion was spin-coated onto the OTS-modified glass substrates, and the solvent was evaporated by annealing at 100 °C for 5 min. The cross-linked PVA was obtained by adding the cross-linking agent glutaraldehyde (Aladdin, 50 wt%) into PVA (Sigma-Aldrich) aqueous solution (6 wt%) with the volume ratio of 1:80. Then, C-PVA was spin-coated on the AgNW network at 7000 rpm for 60 s. The C-PVA substrate was annealed at 100 °C for 1 min on a hot plate to evaporate water. PDMS (Sylgard 184, Dow Corning) was prepared by mixing the base and the cross-linking curing agent in a weight ratio of 10:1, and then was spin-coated at 4000 rpm for 60 s on the C-PVA film, and the PDMS was cured at curing temperature of 100 °C for 5 min. After the PDMS was cured, the AgNW/C-PVA/PDMS embedded electrodes were peeled off from the OTS/glass.
Device fabrication
Conformable OPVs and OPDs were fabricated on the AgNW/C-PVA/PDMS electrodes. First, the free-standing AgNW/C-PVA/PDMS electrode with a thickness of ~30 μm was transferred onto a glass supporting substrate to form a flat surface for further device fabrication. Then, the AZO ETL (40 nm thick) was spin-coated onto the AgNW/C-PVA/PDMS with the spinning rate of 2500 rpm, followed by annealing at 150 °C for 10 min. The optimized sol–gel AZO solution was prepared by dissolving 0.44 g zinc acetate dehydrate, 0.0228 g aluminum nitrate nonahydrate, and 122 μL ethanolamine in 20 mL methoxyethanol. For OPV devices, PM6:Y6 active layer was prepared with a weight ratio of 1:1.2, and was deposited from 6 mg mL−1 PM6 concentration in chloroform solution (containing 0.5 vol% chloronaphthalene) at 2700 rpm for 30 s. For OPD devices, PM6:Y6 active layer was optimized with a weight ratio of 1:1.5, and was deposited from 10 mg mL−1 PM6 concentration in chloroform solution (containing 0.5 vol% chloronaphthalene) at 2000 rpm for 30 s. The blend film was annealed at 110 °C for 10 min in a glove box. The optimized thickness of PM6:Y6 active layer for OPV and OPD were 89 nm and 290 nm, respectively. The 10 nm MoO3 HTL and 100 nm Ag anode were thermally evaporated on the active layer through a mask (with a 0.0516 cm² area opening) in a vacuum chamber at a base pressure below 1 × 10−6 Pa. Finally, the flexible devices were obtained by peeling off from the supporting substrate. The lamination and delamination process can be found in Supplementary Fig. 7. The reference ITO/glass devices were fabricated with the same conditions.
Device characterization
The sheet resistance of the electrodes was measured using a four-point probe setup. The electrical properties under mechanical deformations were conducted using a lab-made apparatus and Keithley 2450 source meter. Tensile strength and elongation at break were measured with an INSTRON 3300 testing frame. The surface roughness of the embedded electrodes was analyzed by atomic force microscopy (Bruker, Germany). The thickness of the films was determined by a Dektak 150 surface profiler. The J–V curves of OPVs were performed under standard AM 1.5 G irradiation with a light intensity of 100 mW cm−2. Before the J–V test, a physical mask of an aperture with a precise area of 0.04 cm2 was used to define the OPV device area. The EQE spectra were acquired with a Solar Cell Spectral Response Measurement System QE-R3011 (Enlitech Co., Ltd). The light intensity at each wavelength was calibrated using a standard single-crystal Si photovoltaic cell. The Jd–V characteristics of the OPD devices were measured on a semiconductor parameter analyzer (Platform Design Automation, PDA FS380 Pro) in an electrically and optically shielded box. The device active area for OPD was 0.0516 cm2. The noise current from the device was first amplified by the current pre-amplifier (SR 570) and then digitized by a FFT spectrum analyzer (Stanford Research, SR785). The signal response was recorded using a digital oscilloscope (Tektronix TDS3052B). And a current pre-amplifier (Stanford Research, SR 570) was adopted to amplify the input signal and to bias the device simultaneously.
Data availability
All relevant data that support the findings of this study are available from authors upon reasonable request.
References
Jinno, H. et al. Self-powered ultraflexible photonic skin for continuous bio-signal detection via air-operation-stable polymer light-emitting diodes. Nat. Commun. 12, 2234 (2021).
Sun, Y. et al. Flexible organic photovoltaics based on water-processed silver nanowire electrodes. Nat. Electron. 2, 513–520 (2019).
Kim, J. et al. High performance flexible transparent electrode via one-step multifunctional treatment for Ag nanonetwork composites semi-embedded in low-temperature-processed substrate for highly performed organic photovoltaics. Adv. Energy Mater. 10, 1903919 (2020).
Xie, B., Chen, Z., Ying, L., Huang, F. & Cao, Y. Near-infrared organic photoelectric materials for light harvesting systems: organic photovoltaics and organic photodiodes. InfoMat 2, 57–91 (2020).
Park, S. et al. Ultraflexible near-infrared organic photodetectors for conformal photoplethysmogram sensors. Adv. Mater. 30, 1802359 (2018).
Meng, X. et al. A general approach for lab-to-manufacturing translation on flexible organic solar cells. Adv. Mater. 31, 1903649 (2019).
Koo, D. et al. Flexible organic solar cells over 15% efficiency with polyimide-integrated graphene electrodes. Joule 4, 1021–1034 (2020).
Qu, T.-Y. et al. Biomimetic electrodes for flexible organic solar cells with efficiencies over 16%. Adv. Optical Mater. 8, 2000669 (2020).
Kim, J.-y et al. Low-temperature processable high-performance D-A-type random copolymers for nonfullerene polymer solar cells and application to flexible devices. Adv. Energy Mater. 8, 1801601 (2018).
Chen, X. et al. Realizing ultrahigh mechanical flexibility and >15% efficiency of flexible organic solar cells via a “welding” flexible transparent electrode. Adv. Mater. 32, 1908478 (2020).
Seo, K.-W., Lee, J., Jo, J., Cho, C. & Lee, J.-Y. Highly efficient (>10%) flexible organic solar cells on PEDOT-free and ITO-free transparent electrodes. Adv. Mater. 31, 1902447 (2019).
Wu, H. et al. Electrospun metal nanofiber webs as high-performance transparent electrode. Nano Lett. 10, 4242–4248 (2010).
Jeon, I. et al. Direct and dry deposited single-walled carbon nanotube films doped with MoOx as electron-blocking transparent electrodes for flexible organic solar cells. J. Am. Chem. Soc. 137, 7982–7985 (2015).
Song, W. et al. Foldable semitransparent organic solar cells for photovoltaic and photosynthesis. Adv. Energy Mater. 10, 2000136 (2020).
Bergqvist, J. et al. Asymmetric photocurrent extraction in semitransparent laminated flexible organic solar cells. npj Flex. Electron. 2, 4 (2018).
Tang, H. et al. Highly conducting MXene-silver nanowire transparent electrodes for flexible organic solar cells. ACS Appl. Mater. Interfaces 11, 25330–25337 (2019).
Azani, M.-R., Hassanpour, A. & Torres, T. Benefits, problems, and solutions of silver nanowire transparent conductive electrodes in indium tin oxide (ITO)-Free flexible solar cells. Adv. Energy Mater. 10, 2002536 (2020).
Fan, X. Doping and design of flexible transparent electrodes for high-performance flexible organic solar cells: recent advances and perspectives. Adv. Funct. Mater. 31, 2009399 (2021).
Sun, Y. et al. Flexible high-performance and solution-processed organic photovoltaics with robust mechanical stability. Adv. Funct. Mater. 31, 2010000 (2021).
Yan, T. et al. 16.67% rigid and 14.06% flexible organic solar cells enabled by ternary heterojunction strategy. Adv. Mater. 31, 1902210 (2019).
Fukuda, K., Yu, K. & Someya, T. The future of flexible organic solar cells. Adv. Energy Mater. 10, 2000765 (2020).
Yan, C. et al. Stretchable and wearable electrochromic devices. ACS Nano 8, 316–322 (2014).
Liang, J., Tong, K. & Pei, Q. A water-based silver-nanowire screen-print ink for the fabrication of stretchable conductors and wearable thin-film transistors. Adv. Mater. 28, 5986–5996 (2016).
Yang, Y. et al. Facile fabrication of stretchable Ag nanowire/polyurethane electrodes using high intensity pulsed light. Nano Res. 9, 401–414 (2016).
Yao, S. et al. A wearable hydration sensor with conformal nanowire electrodes. Adv. Healthc. Mater. 6, 1601159 (2017).
Xu, J. et al. Highly stretchable polymer semiconductor films through the nanoconfinement effect. Science 355, 59–64 (2017).
Chen, Z. H., Fang, R., Li, W. & Guan, J. Stretchable transparent conductors: from micro/macromechanics to applications. Adv. Mater. 31, 1900756 (2019).
Xia, Y., Aguirre, L. E., Xu, X. & Inganäs, O. All-polymer high-performance photodetector through lamination. Adv. Electron. Mater. 6, 1901017 (2020).
Lochner, C. M., Khan, Y., Pierre, A. & Arias, A. C. All-organic optoelectronic sensor for pulse oximetry. Nat. Commun. 5, 5745 (2014).
Armin, A., Vuuren, R. D. J.-v, Kopidakis, N., Burn, P. L. & Meredith, P. Narrowband light detection via internal quantum efficiency manipulation of organic photodiodes. Nat. Commun. 6, 6343 (2015).
Wang, S., Oh, J. Y., Xu, J., Tran, H. & Bao, Z. Skin-inspired electronics: an emerging paradigm. Acc. Chem. Res. 51, 1033–1045 (2018).
Cui, N. et al. A photolithographic stretchable transparent electrode for an all-solution-processed fully transparent conformal organic transistor array. J. Mater. Chem. C. 7, 5385–5393 (2019).
Jeong, S. H., Zhang, S., Hjort, K., Hilborn, J. & Wu, Z. PDMS-based elastomer tuned soft, stretchable, and sticky for epidermal electronics. Adv. Mater. 28, 5830–5836 (2016).
Ren, H. et al. High-performance, ultrathin, ultraflexible organic thin-film transistor array via solution process. Small 14, 1801020 (2018).
Atkinson, J. & Goldthorpe, I. A. Near-infrared properties of silver nanowire networks. Nanotechnology 31, 365201 (2020).
Qin, J. et al. Recent progress in flexible and stretchable organic solar cells. Adv. Funct. Mater. 30, 2002529 (2020).
Dagdeviren, C. et al. Conformal piezoelectric systems for clinical and experimental characterization of soft tissue biomechanics. Nat. Mater. 14, 728 (2015).
Sun, Z. et al. Skin-like ultrasensitive strain sensor for full-range detection of human health monitoring. ACS Appl. Mater. Interfaces 12, 13287–13295 (2020).
Iqbal, S. M. A., Mahgoub, I., Du, E., Leavitt, M. A. & Asghar, W. Advances in healthcare wearable devices. npj Flex. Electron. 5, 9 (2021).
Stubhan, T. et al. Inverted organic solar cells using a solution processed aluminum-doped zinc oxide buffer layer. Org. Electron. 12, 1539–1543 (2011).
Kim, J. et al. High performance flexible transparent electrode via one-step multifunctional treatment for ag nanonetwork composites semi-embedded in low-temperature-processed substrate for highly performed organic photovoltaics. Adv. Energy Mater. 10, 1903919 (2020).
Zhang, W. et al. Graphene:silver nanowire composite transparent electrode based flexible organic solar cells with 13.4% efficiency. J. Mater. Chem. A 7, 22021 (2019).
Wang, X. et al. High-performance all-polymer photoresponse devices based on acceptor-acceptor conjugated polymers. Adv. Funct. Mater. 26, 6306–6315 (2016).
Jiang, Z. et al. Ultraflexible integrated organic electronics for ultrasensitive photodetection. Adv. Mater. Technol. 6, 2000956 (2020).
Zhao, Z., Xu, C., Niu, L., Zhang, X. & Zhang, F. Recent progress on broadband organic photodetectors and their applications. Laser Photonics Rev. 14, 2000262 (2020).
Yang, D. & Ma, D. Development of organic semiconductor photodetectors: from mechanism to applications. Adv. Optical Mater. 7, 1800522 (2019).
Acknowledgements
This work was financially supported by the National Key Research and Development Program of China (No. 2019YFA0705900) funded by MOST, the Basic and Applied Basic Research Major Program of Guangdong Province (No. 2019B030302007), the National Natural Science Foundation of China (No. 51521002), and Guangdong-Hong Kong-Macao joint laboratory of optoelectronic and magnetic functional materials (No. 2019B121205002).
Author information
Authors and Affiliations
Contributions
F.H. and N.C. conceived and designed the work. N.C. carried out conformable device fabrication and performed electrical and optical measurements. Y.S. and N.C. conducted characterization of OPD characterization and implemented heart rate detecting. F.H., C.N., and C.-H.T. wrote and revised the manuscript. K.Z., X.Y., S.D., and B.X. analyzed and interpreted the data. All authors discussed the results and commented on the final manuscript. F.H. supervised the project.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Cui, N., Song, Y., Tan, CH. et al. Stretchable transparent electrodes for conformable wearable organic photovoltaic devices. npj Flex Electron 5, 31 (2021). https://doi.org/10.1038/s41528-021-00127-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41528-021-00127-7
- Springer Nature Limited
This article is cited by
-
Fabrication of composite transparent conductive electrodes based on silver nanowires
Scientific Reports (2024)
-
Exploring cyclic olefin copolymer (COC) for flexible silver nanowire electrode
Scientific Reports (2024)
-
All-Polymer Solar Cells and Photodetectors with Improved Stability Enabled by Terpolymers Containing Antioxidant Side Chains
Nano-Micro Letters (2023)
-
A temperature responsive adhesive hydrogel for fabrication of flexible electronic sensors
npj Flexible Electronics (2022)
-
Thermoplastic elastomer enhanced interface adhesion and bending durability for flexible organic solar cells
npj Flexible Electronics (2022)