Abstract
Establishing dependable, cost-effective electrical connections is vital for enhancing device performance and shrinking electronic circuits. MXenes, combining excellent electrical conductivity, high breakdown voltage, solution processability, and two-dimensional morphology, are promising candidates for contacts in microelectronics. However, their hydrophilic surfaces, which enable spontaneous environmental degradation and poor dispersion stability in organic solvents, have restricted certain electronic applications. Herein, electrohydrodynamic printing technique is used to fabricate fully solution-processed thin-film transistors with alkylated 3,4-dihydroxy-L-phenylalanine functionalized Ti3C2Tx (AD-MXene) as source, drain, and gate electrodes. The AD-MXene has excellent dispersion stability in ethanol, which is required for electrohydrodynamic printing, and maintains high electrical conductivity. It outperformed conventional vacuum-deposited Au and Al electrodes, providing thin-film transistors with good environmental stability due to its hydrophobicity. Further, thin-film transistors are integrated into logic gates and one-transistor-one-memory cells. This work, unveiling the ligand-functionalized MXenes’ potential in printed electrical contacts, promotes environmentally robust MXene-based electronics (MXetronics).
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Solution processible two-dimensional (2D) materials as electrical contacts offer several crucial advantages over conventional vacuum-deposited metals, such as processing under ambient conditions, large-area fabrication, scalability, cost-effectiveness, compatibility with flexible substrates, and non-damaging to the underneath surface1,2. Titanium carbide MXene, denoted as Ti3C2Tx (with Tx representing –O, –OH, halogen, or chalcogen), has shown immense potential in various applications due to its 2D morphology and exceptional physicochemical properties3,4,5,6,7,8,9,10. Its facile solution processability facilitates the seamless integration of controlled geometry thin films, simplifying architectural design and device manufacturing1,11,12,13,14,15,16. Chemically tunable electrical conductivity and high current-carrying capacity make MXenes well-suited for deployment as electrodes in microelectronics, thin-film transistors (TFTs), and memory devices, defining a novel domain known as MXetronics5,17,18,19,20,21,22,23,24,25. However, the hydrophilic nature of MXenes remains a notable concern when considering their utilization in electronic circuits. These concerns primarily arise from two factors. Firstly, their propensity to interact with atmospheric water and oxygen raises apprehensions regarding the potential gradual deterioration of structural and compositional integrity, consequently impacting the electrical properties of MXene nanosheets26. Secondly, their hydrophilic tendencies contribute to poor dispersion stability in volatile organic solvents. This is crucial for avoiding undesirable coffee-ring effects during film deposition and necessitating low drying temperatures27,28. Notably, certain device fabrication processes are mandated to use such organic solvents29.
Considering that the solution-processed films consist of an assembly of overlapping MXene nanosheets, the electron transport properties at the interface significantly influence the performance of MXene-based electronic devices. The presence of voids and intercalants impair the inter-flake electron transport properties of MXene film. For instance, thin films of MXene nanosheets synthesized by the minimally intensive layer delamination (MILD) method, renowned for producing high-quality nanosheets, contain Li+ ions as intercalants. These hydrophilic Li+ ions facilitate the water molecules’ penetration through the voids in the MXene film, entrapping them within the interlayer space30,31. Besides causing the degradation of MXene, the intercalated water may obstruct the efficient flow of charge carriers between the nanosheets in the MXene film. Consequently, MXene-based devices have yet to demonstrate stable performance under harsh atmospheric conditions30. Hence, the imperative challenge lies in modifying MXene nanosheet surface characteristics to achieve dispersion stability in volatile organic solvents, enhance oxidation resistance, mitigate moisture-induced swelling, and facilitate inter-flake electron transport. Tackling these challenges is crucial for MXenes’ effective use in printed electronic devices.
Several strategies have been devised to modify MXene nanosheets, exploiting their surface terminal groups for interactions with metal ions, organic molecules, and polymers through hydrogen bonding, covalent bonding, and electrostatic interactions31,32,33,34,35,36,37. While some of these strategies enhance MXene dispersion in organic solvents, they often come at the cost of decreased electrical conductivity due to polymers or organic molecules obstructing inter-flake charge transport32,36,38. Recent efforts utilized catechol-based ligands to impart hydrophobic characteristics to MXene surfaces without sacrificing the essential electrical properties of MXene films39. Notably, alkylated 3,4-dihydroxy-L-phenylalanine (ADOPA) ligands, featuring a catechol-based head group and a hydrophobic tail that forms hydrogen bonds with MXene surfaces, enabled MXene nanosheet dispersion in volatile organic solvents such as ethanol and acetone39. The ADOPA-functionalized MXene (AD-MXene) films retained over 90% electrical conductivity (6,404 S cm−1) of the pristine MXene films (6900 S cm−1). Furthermore, benefitting from the hydrophobic nature of ADOPA ligands, AD-MXene films exhibited excellent oxidation stability and electrical conductivity retention under 85 °C at 85% relative humidity (RH) conditions for 20 days39.
Here, we employ AD-MXene to print TFT circuit electrodes—source, drain, and gate. Electrohydrodynamic (EHD) printing technique was chosen for the TFTs fabrication through localized delivery of AD-MXene electrodes, zinc-tin-oxide (ZTO) active layer, and fluoro-co-hexafluoropropylene (PVDF-HFP)-based dielectrics. EHD printing offers advantages, including finer pattern features and compatibility with various materials and ink viscosities compared to conventional printing techniques40,41,42,43,44,45. However, EHD printing requires low-surface-tension solvents and cannot use MXenes dispersed in high-surface-tension water (72.8 dyne cm–1)29. High-surface-tension solvents require a higher operating voltage, which is associated with voltage risks29,46,47. Ethanol’s lower surface tension (22.0 dyne cm–1) allows EHD printing at reduced voltages, making the excellent dispersion stability of AD-MXene in ethanol (up to 5 mg mL–1) advantageous for producing MXene-based highly conductive electrodes29. Unlike the existing literature, the AD-MXene electrodes don’t require complex post-fabrication strategies to avoid environmental degradation48. There is no need to add a binder to the ink, which is detrimental to the electrode conductivity, to enhance the electrode’s adhesion and avoid the coffee-ring effects28. The performance of AD-MXene electrodes was compared with those of vacuum-deposited Au and Al electrodes. Furthermore, ADOPA ligands block moisture ingress, providing excellent environmental stability in TFTs with AD-MXene electrodes. They showed negligible changes in their transfer and output characteristics and bias stabilities, even after 30 days of exposure to 60% RH at 25 °C. Finally, we assess AD-MXene’s potential for integrated circuits, evaluating logic gates (complementary inverter, NAND, and NOR) and memory cells constructed using all-printed AD-MXene electrodes, ZTO active layers, and PVDF-HFP dielectrics.
Results and discussion
Properties of AD-MXene
As illustrated in Fig. 1a, the AD-MXene ink for EHD printing was prepared through facile mixing of aqueous dispersion of MXene with ethanol dispersion of ADOPA ligand at room temperature for around one hour and subsequent replacement of solvent with ethanol via centrifugation. The ADOPA ligand spontaneously adsorbed onto MXene due to its catechol head strong hydrogen-bonding and π-electron interactions with MXene surface functional groups, and the hydrophobic tail of ADOPA ligand enables the excellent dispersion of obtained AD-MXene in ethanol. The X-ray photoelectron spectroscopy (XPS) spectra for the Ti 2 p, O 1 s, C 1 s, and N 1 s core levels of AD-MXene and pristine MXene are shown in Fig. 1b and Supplementary Fig. 1. Due to primary amine moiety in ADOPA, AD-MXene shows a clear peak around 399.9 eV in the N 1 s region, confirming the attachment of ADOPA (Fig. 1b). To investigate further the interlayer structure and alignment of MXene sheets in the film, the X-ray diffraction (XRD) patterns of both pristine MXene and AD-MXene films were recorded as shown in Supplementary Fig. 2. The (002) peak shift from 7.32° to 6.38° was observed, corresponding to a d-spacing expansion from 1.22 nm to 1.36 nm, resulting from attached ligands. Compared to pristine MXene with poor dispersion properties in ethanol, AD-MXene shows excellent dispersion, as shown in Fig. 1c. The field emission scanning electron microscope (FE-SEM) image in Fig. 1d shows a representative AD-MXene flake from a batch with an average lateral size of 1.81 μm. Due to the enhanced hydrophobicity after ADOPA functionalization, our previous study has shown that AD-MXene is environmentally stable for an extended time, compared to pristine waterborne MXene, which is otherwise susceptible to water uptake and subsequent environmental degradation39. This has also been proven to be true in electronic devices with AD-MXene exposed to the surface, where a recent study shows that chemical sensors based on AD-MXene retained their performance for over 6 weeks of exposure in ambient environments49.
Electrical properties of EHD-printed AD-MXene electrodes
As shown in Fig. 2a, the as-prepared ethanol-based AD-MXene ink was loaded into EHD printing equipment and then ejected through the nozzle tip by applying an electric field between the nozzle and the substrate. The printing conditions were optimized by examining the jetting behavior and tuning the working distance (distance from the nozzle tip to the substrate) and the applied electric field. Four jetting behaviors, such as dripping, micro-dripping, cone-jet, and multi-jet, were noticed when the working distance and applied voltage were tuned in the ranges of 100–600 μm and 0.5–3.0 kV, respectively (Fig. 2b). The AD-MXene ink was printed into line-shaped patterns on a SiO2/Si wafer at conditions optimized for uniform jetting in the stable cone-jet mode. These precise conditions encompassed a nozzle size of 185 μm, a printing speed of 10 mm s−1, a controlled flow rate of 1.3 μL min–1, and an applied voltage of 1.3 kV, all sustained at a working distance of 450 µm.
Optical microscope and cross-sectional FE-SEM images revealed the increased thickness of AD-MXene lines with increased printing cycles from 1 to 10 (Supplementary Figs. 3, 4). Further, atomic force microscopy (AFM) analysis revealed the gradual increase of average surface roughness (Ra) of AD-MXene lines with an increase in the number of printing cycles, and the Ra was observed to be 7.8 nm for lines fabricated with 10 printing cycles (Supplementary Fig. 5). Characteristic current-voltage curves of AD-MXene electrodes revealed that the increase in the thickness of lines (or number of printing cycles) enabled the enhanced current flow. In contrast, the increase in channel length decreased the current (Fig. 2c, d). Therefore, the EHD printing of AD-MXene with a controlled number of printing cycles and channel lengths may enable the facile fabrication of conductive wires/resistors of circuitries. The electrical conductivity of the AD-MXene electrode (length = 1 mm, width = 320 μm, and thickness = 190 nm) fabricated by 10 cycles of printing was observed to be 5579 S cm−1, which was almost equal to that of the AD-MXene film fabricated using vacuum-assisted filtration. This is because the ADOPA ligands facilitated the alignment of AD-MXene flakes during the EHD printing process and enabled the printed AD-MXene electrodes to have excellent electrical conductivity (Supplementary Fig. 4). We hypothesize that the ligand’s planar alignment and strong π-electron interaction with the MXene surface facilitated the inter-flake electron transport; as a result, the AD-MXene films exhibited electrical conductivity almost equal to that of pristine MXene film despite having ADOPA ligands as intercalants39. Notably, the conductivity of AD-MXene electrode (5579 S cm−1) is considerably higher than previously reported poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) electrodes (0.2–1200 S cm–1)50, reduced graphene oxide-based electrodes (590 S cm–1)51, and pristine MXene electrode (2600 S cm–1)23. Besides, printing AD-MXene electrodes is more favorable as it doesn’t require post-treatments, unlike other metal-based (Cu, Ag, Zn, etc.) inks52,53,54. The AD-MXene electrode designed in the square spiral pattern through continuous writing with the AD-MXene ink revealed the compatibility of AD-MXene ink for EHD printing of complex circuits (Fig. 2e).
Performance of AD-MXene as electrodes of TFTs
The excellent compatibility of the AD-MXene ink for EHD printing and the high electrical conductivity of printed AD-MXene lines motivated us to investigate the effectiveness of AD-MXene as electrical contacts of TFTs. Therefore, we fabricated a TFT, wherein the AD-MXene was printed as source and drain electrodes on the ZTO active material deposited on SiO2/Si substrate (Fig. 3a). ZTO was selected as an active layer due to its cost-effectiveness, solution processability, and potential as alternative to expensive indium-based counterparts55. Fig. 3b shows the transfer characteristics of TFTs prepared with AD-MXene electrodes deposited at different numbers of EHD printing cycles. All devices showed typical n-type transfer characteristics during ± 40 V of gate voltage (VG) sweep (source to drain voltage (VD) = 40 V). The increased number of AD-MXene electrode printing cycles enhanced the transfer performance of TFTs due to the improvement in electrical conductivity through the formation of denser network of AD-MXene electrode (Fig. 3b). The field-effect mobility (μFET) values were determined from ID1/2 vs. VG plots by following the equation: ID = μFETCiW(2 L)−1(VG − Vth)2, where ID, Ci, W, L, and Vth are drain current, areal capacitance, channel width, channel length, and threshold voltage, respectively. The μFET of devices gradually increased with an increase in the number of AD-MXene printing cycles or the thickness of MXene electrodes (Fig. 3c). For comparison, TFTs with vacuum-deposited Au and Al electrodes were also fabricated, and their performances were compared with that of AD-MXene devices (Fig. 3d–f). Figure 3e compares the transfer characteristics of ZTO-based TFT devices prepared with different source/drain electrodes (AD-MXene, Au, and Al). The ZTO TFT fabricated with AD-MXene source/drain electrodes exhibited better transfer characteristics than those fabricated with vacuum-deposited Al and Au electrodes. Hysteresis (the variation in the OFF-to-ON sweeping transfer curve compared to the ON-to-OFF transfer curve) was not observed for devices comprising Al and AD-MXene as source/drain electrodes. In contrast, the device with Au as source/drain electrodes exhibited poor electrical performance with hysteresis (Fig. 3e). Remarkably, the AD-MXene based TFT yielded considerably higher μFET of 3.24 cm2 V–1 s–1 than those based on Al (2.61 cm2 V–1 s–1) and Au (1.75 cm2 V–1 s–1) electrodes (Fig. 3f). The off-current value of the AD-MXene based TFT was somewhat higher than that of the Au device. This was probably attributed to a combination of factors such as gate leakage, subthreshold conduction, and trap states rather than the properties of the electrode material, all of which can be sufficiently optimized by device structure design and scale control of the printed electrode. Contact resistances of TFTs with different electrodes were extracted by the transfer length method from the width-normalized total resistance (RtotW) of TFTs as a function of channel length shown in Supplementary Fig. 6. Although the RtotW showed a linear relationship with the channel length for all TFTs, AD-MXene electrodes caused low resistance as compared to Au and Al electrodes. Therefore, given that the crystalline morphology underneath the ZTO semiconductor layer was the same for all electrodes, the observed differences in μFET values of devices must have originated due to the changes in contact resistances at the interface of channel and electrode. In other words, we infer that the solution-processed AD-MXene electrodes provided an excellent interface with the ZTO active layer deposited through the same solution route compared to vacuum-deposited Au and Al electrodes.
Performance of TFTs with different dielectric layers
The superiority and universality of AD-MXene electrodes was further demonstrated by utilizing them as gate, source, and drain electrodes in top-gate top-contact TFTs with PVDF-HFP and FPVDF-HFP dielectrics (Fig. 4). Insulating characteristics of PVDF-HFP and FPVDF-HFP dielectrics were evaluated before their integration in TFTs. To this end, metal-insulator-metal (MIM) capacitors with device structures of AD-MXene/PVDF-HFP/AD-MXene and AD-MXene/FPVDF-HFP/AD-MXene were fabricated by EHD-printing and their leakage current densities were measured (Supplementary Fig. 7a, b). The observed leakage current densities below 10−8 A cm−2 at an applied electric field strength of 4 MV cm−1 for both devices revealed the excellent insulation properties of PVDF-HFP and FPVDF-HFP dielectrics. Furthermore, the areal capacitances of PVDF-HFP and FPVDF-HFP dielectrics at 1 kHz were measured to be 34.2 and 41.8 nF cm−2, respectively (Supplementary Fig. 7c). The AD-MXene was coated on ZTO active layer as source/drain electrodes, after which PVDF-HFP or FPVDF-HFP was coated to form the dielectric layer. The EHD printing of AD-MXene as a gate electrode completed the fabrication of TFT with top-gate top-contact geometry, as the illustration and optical microscope images of devices shown in Fig. 4a. The transfer properties of TFTs with PVDF-HFP or FPVDF-HFP dielectrics were obtained in the saturation regime with VG sweep (±5 V) under VD of 5 V. In contrast to a counter-clockwise hysteresis displayed by the TFT with PVDF-HFP dielectric, no hysteresis was observed for the TFT with FPVDF-HFP dielectric. Due to their high dielectric constant (k) values and lack of functional groups that trap charges, PVDF-based polymers are usually employed as dielectrics to fabricate low-voltage-operating electrically stable TFTs56. The ferroelectric behavior of these dielectrics (such as PVDF-HFP), which arises due to the C-F dipoles rearrangement under a strong electric field, results in hysteresis during the operation of TFTs, as shown in Fig. 4b57. The size of the hysteresis can be decreased by controlling the crystallinity and crystallite size of the dielectrics, precisely, by decoupling the ferroelectric domains of dielectrics58. It was demonstrated that the ferroelectric behavior of the PVDF-HFP dielectric can be substantially decreased by adding the FPA-3F cross-linker58,59. Accordingly, negligible hysteresis was observed during the transfer operation of TFT with FPVDF-HFP dielectric layer (Fig. 4c). The electrical parameters of both TFTs, such as μFET, Vth, and ON/OFF current ratio (ION/IOFF) were extracted in the saturation regime of the transfer curves and summarized in Table 1. Positive bias-stress tests were performed on the TFTs to confirm the device reliability, where the Vth of n-type TFTs shifts towards the positive value under the applied positive gate-source voltage (Fig. 4d, e). The transfer characteristics recorded under the continuous applied bias of 5 V revealed TFTs’ good bias stability features. They ascertained the electrical robustness of both PVDF-HFP and FPVDF-HFP dielectrics. Therefore, the fabrication of TFTs with AD-MXene electrodes provides insights into the future manufacturing of MXene-based electronic devices with operational and chemical stability.
The transfer characteristics of the TFT with FPVDF-HFP dielectric were further investigated after one month of storage under 60% RH at 25 °C, as illustrated in Fig. 5a. Transfer curves (Fig. 5b), bias-stress test results (Fig. 5c, d), and measured parameters in Table 1 revealed that the exposure to relative humidity doesn’t significantly change the electrical performance of the TFT device. In addition to preserving the bias stability feature, the device maintained μFET, ION/IOFF ratio, and Vth values remained close to their initial values even after the exposure of 60% RH for 30 days. All these results confirmed the excellent stability of AD-MXene electrodes under humid conditions. To demonstrate the scalability of TFTs with AD-MXene electrodes, we fabricated a 7-inch wafer-scale TFT array using FPVDF-HFP dielectric. The digital photograph of the TFT array, along with the optical microscope image of an individual device, is displayed in Fig. 6a. All 64 TFTs in the array exhibited stable transfer curves under VG sweep from -5 V to 5 V. Furthermore, good output characteristics, i.e., linear/saturation switching with a stepwise increase in the VG, and excellent bias stability were observed for the TFT devices in the array (Supplementary Fig. 8). The μFET values calculated from the transfer curves of 64 TFTs were distributed in a small range, with an average μFET being 4.42 ± 0.18 cm2 V−1 s−1 (Fig. 6b).
Integration of TFTs for the fabrication of logic circuits
To demonstrate the practical applicability of AD-MXene electrodes, a high-performance complementary inverter was fabricated with TFTs comprising AD-MXene electrodes, FPVDF-HFP dielectric, and ZTO active layer. Figure 7a shows the schematic, top-view optical image, and circuit diagram of the complementary inverter fabricated by using two TFTs (load TFT and drive TFT), wherein the load transistor’s gate electrode was connected to the drain electrode, which was used as the power supply voltage (VDD). The typical voltage transfer (input–output) characteristics and corresponding inverter gains were investigated at a VDD of 5 V, as shown in Fig. 7b. Before the switching (or at low input voltage (VIN)), the inverter’s output voltage (VOUT) is almost equal to that of VDD. However, the high VIN enabled the sharp switching of the inverter’s VOUT from a high value to 0 V, and the VOUT was restored to a high value when the VIN decreased back to a low value. This voltage reversal feature of the inverter can transform “1” and “0” input logic states to “0” and “1” output states, respectively. It was also observed that voltage transfer curves of inverters fabricated with FPVDF-HFP dielectric didn’t present any hysteresis feature. This inverter exhibited a significantly higher voltage gain (dVOUT/dVIN) of 17.8.
The feasibility of prepared TFTs in constructing logic gates was further demonstrated by fabricating NAND and NOR logic gates (Fig. 7c, d). Assembling an additional drive TFT to NOT gate in series and parallel completes the fabrication of NOR and NAND logic gates, respectively. Figure 7c shows top-view optical images and circuit diagrams of NAND and NOR logic gates. The VOUT characteristics of both these logic gates were investigated at low-voltage-operation conditions (~3 V) against different combinations of input signals (VA and VB) (Fig. 7d). When at least one of the drive TFTs is turned OFF by maintaining 0 V input voltage, i.e., at logic input signal combinations of (0, 0), (1, 0), and (0, 1), the VOUT of the NAND logic gate becomes “VDD”, i.e., a logic output signal “1”. In other words, the VOUT of the NAND logic gate becomes “0 V” or logic state “0” if and only if both drive transistors are turned “ON” by applying VA = 3 V and VB = 3 V or the input logic signals combination (1, 1) (Fig. 7d). On the other hand, the VOUT of NOR gate, wherein the drive TFTs are connected in series, becomes a logic state “1” (VOUT = VDD) if and only if both TFTs are turned OFF by maintaining VA = 0 V and VB = 0 V or a logic input signal combination (0, 0). Any other combination of input voltages would turn ON at least one of the TFTs. As a result, the VOUT of the NOR gate becomes logic state “0” (VOUT = 0 V) (Fig. 7d).
Integration of TFTs for the fabrication of 1T1M device
PVDF and its copolymer, PVDF-HFP, are renowned for their ferroelectric behavior, primarily attributed to the reorientation of carbon–fluorine (C–F) dipoles under high electric fields. This trait allows a ferroelectric material to retain its polarization even after removing the electric field. On the other hand, in the case of FPVDF-HFP, which uses fluorophenyl azide to form the cross-links, the reorientation of the atoms was restricted. As a result, removing the electric field eliminated the polarization, allowing for stable driven transistor behavior. The hysteresis observed during the operation of TFT with PVDF-HFP dielectric is identical to that of conventional ferroelectric memory transistors (Fig. 4b). Hence, the feasibility of these TFTs for integrating memory devices was investigated. The transfer characteristics of TFT with PVDF-HFP dielectric were shifted depending on the applied constant positive and negative VG, as shown in Fig. 8a. In detail, shifting towards negative values was noted when increasing the constant positive VG (5 V, 10 V, and 20 V), while shifting towards positive values was noted when increasing the constant negative VG (-5 V, -10 V, and -20 V). Accordingly, the absolute Vth value shift towards positive and negative values increased with an increase in the constant negative and constant positive VG, respectively (Fig. 8b). Different ID values observed at VG = 0 V for constant positive and negative VG can act as ON- and OFF-states of the device, and are helpful for the information programming or erasing. The ON-state current of ≈10−6 A was measured after applying a constant positive voltage of 20 V, while the off-state current of ≈10−10 A was measured after applying a constant negative voltage of −20 V (Fig. 8c, d). The ON-state current allows the device to be programmed for information storage, while the erasing can be achieved with the OFF-state current. Further, upon increasing the erasing pulse width from 0.3 to 2 s, the transfer curve shifted in the positive VG direction. However, this tuning of pulse width didn’t result in any variation corresponding to ID at VG = 0 (Supplementary Fig. S9).
The prepared TFTs with PVDF-HFP and FPVDF-HFP dielectrics were used as memory TFT and control TFT, respectively, for fabricating one-transistor-one-memory (1T1M) cells. The 1T1M architecture was chosen to ensure a non-destructive read-out capability for ferroelectric memory cells. This design offers the advantage of separating the distinct programming/erasing and reading processes of the memory transistor by utilizing the control transistor. Figure 9a shows the schematic representation of the fabricated memory device along with an optical micrograph and circuit diagram. The gate voltage of the memory TFT can be applied depending on the signal of the control TFT. The dynamic behavior of the 1T1M device was examined by implementing multiple writing and reading processes, as shown in Fig. 9b. Programming/erasing and reading operations were distinctively selected by controlling bit line voltage (VBL) signal access to the memory transistor through applying word line voltages (VWL) of 20 V and –20 V, respectively. In detail, the control transistor was turned ON upon applying a VWL of 20 V; subsequently, this action triggered the transfer of the VBL signal to the gate electrode of the memory transistor. In this condition, both programming and erasing operations were accomplished by applying VBL as 20 V and –20 V, respectively. In contrast, the reading of the stored data was performed at VWL = –20 V, wherein the control transistor was turned OFF, and, as a result, the ID of the memory transistor remained at the same state irrespective of the VBL. This fabricated 1T1M cell exhibited good retention and cyclic endurance properties, as shown in Fig. 9c, d, respectively. After adjusting the memory cell to a programming or erasing state, the retention test was performed by monitoring the readout current as a function of time at VWL = −20 V. The device maintained ON and OFF currents for 104 s without much degradation in performance, which specified its high retention capability. The cycling stability test, which was conducted by recording the currents for repeated cycles of programming and erasing processes, revealed the switching stability and reliability of the device (Fig. 9d).
In summary, we demonstrated the patterning of alkylated 3,4-dihydroxy-L-phenylalanine (ADOPA) ligand functionalized MXene (AD-MXene) dispersions in ethanol by electrohydrodynamic (EHD) printing process. The excellent conductivity and facile processability of AD-MXene lines allowed their utilization as source, drain, and gate electrodes to fabricate all-solution processed thin-film transistors (TFTs) through EHD printing, wherein zinc-tin-oxide and PVDF-HFP or FPVDF-HFP were utilized as active and dielectric layers of TFTs, respectively. The performance of AD-MXene electrodes was higher than that of the vacuum-deposited Au and Al contacts. We demonstrated exceptional stability to TFTs under high humidity conditions due to hydrophobic ADOPA ligands’ ability to restrict moisture ingress. Furthermore, the robust operation of TFTs with AD-MXene electrodes facilitated the fabrications of high-performance complementary logic circuits (complementary inverter, NAND gate, and NOR gate) and a one-transistor-one-memory cell. Overall, this work proves that appropriately designed surface functionalized MXenes provide a pathway to environmentally stable printable MXene-based electronics (MXetronics).
Methods
ADOPA-MXene ink preparation
The syntheses of ADOPA ligand, MXene, and AD-MXene were carried out following our earlier report39.
Synthesis of ADOPA ligand
ADOPA ligand was synthesized by esterification of 3,4-dihydroxy-L-phenylalanine (DOPA) with hydrophobic 1H,1H,2H,2H-perfluoro-1-hexanol. Briefly, 0.2 M toluene (100 mL) solution containing 20 mmol of DOPA (3.94 g), 22 mmol of 1H,1H,2H,2H-perfluoro-1-hexanol (5.81 g), and 20 mmol of p-TsOH·H2O (3.80 g) was refluxed for 48 h under an Ar atmosphere using a Dean-Stark trap to remove water azeotropically. After the completion of the reaction, toluene was evaporated under vacuum to get the gel-like solid residue, which was thoroughly washed with saturated NaHCO3 and subsequently extracted with ethyl acetate. After that, the obtained ethyl acetate solution was washed with brine and dried over anhydrous MgSO4 to remove water. The resulting residue was dissolved in a small amount of hot ethyl acetate and crystallized from petroleum ether (60–90 °C) to produce ADOPA (6.56 g, 74%).
Synthesis of Ti3C2Tx MXene
The selective removal of Al layers from the Ti3AlC2 MAX precursor using the modified minimally intensive layer delamination (MILD) method facilitated the exfoliation of Ti3C2Tx MXene nanosheets. Briefly, 3 g of Ti3AlC2 MAX powder was stirred in 60 mL of 9 M HCl aqueous solution comprising 4.8 g of LiF for 24 h at 35 °C. The crude product obtained was washed several times via centrifugation (1246 × g for 5 min) until the supernatant’s pH reached ~6. Finally, delaminated Ti3C2Tx nanosheets were obtained by collecting the supernatant solution from the Ti3C2Tx dispersions subjected to centrifugation at 1246 × g for 30 min.
Preparation of AD-MXene ink
AD-MXene was synthesized by adding 35 mL of the as-prepared aqueous MXene dispersions (1 mg mL−1) into 10 mL of ethanol solution containing 3.5 mg of ADOPA under continuous stirring at room temperature. After a brief reaction, the solvent was exchanged with ethanol via centrifugation (10174 × g, 3 times) to obtain the AD-MXene dispersions in ethanol. The AD-MXene dispersions in ethanol were diluted to 5 mg mL−1 for further use.
Fabrication of TFTs
The TFT devices were fabricated on a heavily n-doped Si wafer with a 100 nm-thick thermally grown SiO2 layer. EHD printing was used to sequentially print active layers, source/drain electrodes, dielectrics, and gate electrodes to form TFTs with top-gate top-contact architecture. At first, SiO2/Si substrates were cleaned by immersing in boiling acetone, followed by sonication in acetone and isopropyl alcohol for 30 min each, dried under nitrogen gas, and further exposed to UV-ozone for 30 min to eliminate organic residues. The ZTO precursor solution was prepared by dissolving 0.4 M zinc acetate dehydrate and tin chloride (1:1 ratio) in 2-methoxyethanol. The SiO2/Si substrates were patterned with the ZTO active layer using EHD printing, and then the resulting film was annealed at 500 °C for 2 h to form the ZTO active layer. AD-MXene source and drain electrodes were patterned by printing AD-MXene ink via the cone-jet mode EHD printing process. The residual solvent from AD-MXene electrodes was removed through heat treatment at 120 °C. Afterward, either 7 wt% PVDF-HFP or FPVDF-HFP (a solution with a weight concentration of 7 wt% was prepared by dissolving PVDF-HFP and fluorophenyl azide (FPA-3F) in dimethylacetamide at a weight ratio of 95:5.) dielectric solutions were printed in direct contact mode (electrostatic-force-assisted dispensing), wherein the DC bias, flow rate, and working distance were 0.05 kV, 0.8 µL min−1, and 80 µm, respectively. The deposited dielectric layers were thermally annealed at 120 °C for 1 h. The film prepared (FPVDF-HFP) was subsequently cured by exposing it to UV light at a wavelength of 256 nm in the presence of N2 gas to solidify the dielectric layer. Finally, the EHD printing of the ADOPA-MXene gate electrode completed the device fabrication. For comparison, TFTs with conventional metal electrodes were fabricated by employing the same fabrication conditions except for replacing AD-MXene electrodes printing step with the vacuum-deposition of Au or Al electrodes with the thickness being the same as AD-MXene electrodes (190 nm). Channel length and width of the ZTO layer were 236 µm and 731 µm, respectively.
Characterizations
X-ray photoelectron spectroscopy measurements were performed on the ULVAC-PHI XPS instrument (Japan) with Al Kα radiation (1486.6 eV). X-ray diffraction (XRD) patterns of pristine MXene and AD-MXene were acquired using a D8 diffractometer (Bruker, USA) with a Cu Kα radiation source. UV-visible absorbance spectra were recorded on a V-670 instrument (Jasco, Japan). The AD-MXene flakes morphology and their arrangement in printed AD-MXene electrodes were examined using a field emission scanning electron microscope (JEOL, JSM-7610F). In contrast, the morphologies of printed AD-MXene electrodes and devices were studied using an optical microscope (Nikon ECLIPSE LV100ND). The dielectric performance was evaluated using an LCR meter and a Keithley 4200 SCS. The electrical characteristics of the TFTs and integrated devices (logic gates and 1T1M cells) were measured under vacuum (~10−3 Torr) using a Keithley 4200 SCS unit. The surface morphology and roughness of AD-MXene lines were measured by atomic force microscope (XE-100, Park systems) in non-contact mode.
Reporting summary
Further information on research design is available in the Nature Portfolio Reporting Summary linked to this article.
Data availability
The data supporting this study’s findings are available within the article and Supplementary Information. Source data are provided with this paper.
References
Conti, S. et al. Printed transistors made of 2D material-based inks. Nat. Rev. Mater. 8, 651–667 (2023).
Aydin, E. et al. Sputtered transparent electrodes for optoelectronic devices: Induced damage and mitigation strategies. Matter 4, 3549–3584 (2021).
Gogotsi, Y. & Anasori, B. The rise of MXenes. ACS Nano 13, 8491–8494 (2019).
Anasori, B., Lukatskaya, M. R. & Gogotsi, Y. 2D metal carbides and nitrides (MXenes) for energy storage. Nat. Rev. Mater. 2, 16098 (2017).
Xu, X., Guo, T., Lanza, M. & Alshareef, H. N. Status and prospects of MXene-based nanoelectronic devices. Matter 6, 800–837 (2023).
Nguyen, T. T. et al. Flexible and transparent MXene-platformed ultrafast photodetector for encrypted signal communication in self-powered operation. Nano Energy 109, 108331 (2023).
Murali, G. et al. A review on MXene synthesis, stability, and photocatalytic applications. ACS Nano 16, 13370–13429 (2022).
Shahzad, F. et al. Electromagnetic interference shielding with 2D transition metal carbides (MXenes). Science 353, 1137–1140 (2016).
Palei, S. et al. A review on interface engineering of MXenes for perovskite solar cells. Nano-Micro Lett. 15, 123 (2023).
You, H. R. et al. Organic solvent dispersible MXene integrated colloidal quantum dot photovoltaics. Adv. Energy Mater. 13, 2301648 (2023).
Zhang, C. et al. Additive-free MXene inks and direct printing of micro-supercapacitors. Nat. Commun. 10, 1795 (2019).
Shao, Y. et al. Room-temperature high-precision printing of flexible wireless electronics based on MXene inks. Nat. Commun. 13, 3223 (2022).
Zhang, Y.-Z. et al. MXene printing and patterned coating for device applications. Adv. Mater. 32, 1908486 (2020).
Sreenilayam, S. P., Ul Ahad, I., Nicolosi, V. & Brabazon, D. MXene materials based printed flexible devices for healthcare, biomedical and energy storage applications. Mater. Today 43, 99–131 (2021).
Piatti, E. et al. Charge transport mechanisms in inkjet-printed thin-film transistors based on two-dimensional materials. Nat. Electron 4, 893–905 (2021).
Pinilla, S., Coelho, J., Li, K., Liu, J. & Nicolosi, V. Two-dimensional material inks. Nat. Rev. Mater. 7, 717–735 (2022).
Lipatov, A. et al. High electrical conductivity and breakdown current density of individual monolayer Ti3C2Tx MXene flakes. Matter 4, 1413–1427 (2021).
Xu, J., Shim, J., Park, J.-H. & Lee, S. MXene electrode for the integration of WSe2 and MoS2 field effect transistors. Adv. Funct. Mater. 26, 5328–5334 (2016).
Lai, S., Jang, S. K., Cho, J. H. & Lee, S. Organic field-effect transistors integrated with Ti2CTx electrodes. Nanoscale 10, 5191–5197 (2018).
Wang, Z., Kim, H. & Alshareef, H. N. Oxide thin-film electronics using all-MXene electrical contacts. Adv. Mater. 30, 1706656 (2018).
Kim, H. et al. All-solution-processed quantum dot electrical double-layer transistors enhanced by surface charges of Ti3C2Tx MXene contacts. ACS Nano 15, 5221–5229 (2021).
Li, E. et al. MXene based saturation organic vertical photoelectric transistors with low subthreshold swing. Nat. Commun. 13, 2898 (2022).
Lyu, B. et al. Large-area MXene electrode array for flexible electronics. ACS Nano 13, 11392–11400 (2019).
Xu, X. et al. High-Yield Ti3C2Tx MXene–MoS2 integrated circuits. Adv. Mater. 34, 2107370 (2022).
Zhu, K. et al. The development of integrated circuits based on two-dimensional materials. Nat. Electron 4, 775–785 (2021).
Lipatov, A. et al. Effect of synthesis on quality, electronic properties and environmental stability of individual monolayer Ti3C2 MXene flakes. Adv. Electron Mater. 2, 1600255 (2016).
Maleski, K., Mochalin, V. N. & Gogotsi, Y. Dispersions of two-dimensional titanium carbide MXene in organic solvents. Chem. Mater. 29, 1632–1640 (2017).
Vural, M. et al. Inkjet printing of self-assembled 2D titanium carbide and protein electrodes for stimuli-responsive electromagnetic shielding. Adv. Funct. Mater. 28, 1801972 (2018).
Bae, J., Lee, J. & Hyun Kim, S. Effects of polymer properties on jetting performance of electrohydrodynamic printing. J. Appl. Polym. Sci. 134, 45044 (2017).
Chen, H. et al. Pristine titanium carbide MXene films with environmentally stable conductivity and superior mechanical strength. Adv. Funct. Mater. 30, 1906996 (2020).
Shekhirev, M. et al. Delamination of Ti3C2Tx nanosheets with NaCl and KCl for improved environmental stability of MXene films. ACS Appl Nano Mater. 5, 16027–16032 (2022).
Kim, D. et al. Nonpolar organic dispersion of 2D Ti3C2Tx MXene flakes via simultaneous interfacial chemical grafting and phase transfer method. ACS Nano 13, 13818–13828 (2019).
Krecker, M. C., Bukharina, D., Hatter, C. B., Gogotsi, Y. & Tsukruk, V. V. Bioencapsulated MXene flakes for enhanced stability and composite precursors. Adv. Funct. Mater. 30, 2004554 (2020).
Wu, X., Wang, Z., Yu, M., Xiu, L. & Qiu, J. Stabilizing the MXenes by carbon nanoplating for developing hierarchical nanohybrids with efficient lithium storage and hydrogen evolution capability. Adv. Mater. 29, 1607017 (2017).
Habib, T. et al. Oxidation stability of Ti3C2Tx MXene nanosheets in solvents and composite films. npj 2D Mater. Appl 3, 8 (2019).
Carey, M. et al. Dispersion and stabilization of alkylated 2D MXene in nonpolar solvents and their pseudocapacitive behavior. Cell Rep. Phys. Sci. 1, 100042 (2020).
Ling, Z. et al. Flexible and conductive MXene films and nanocomposites with high capacitance. Proc. Natl. Acad. Sci. USA 111, 16676–16681 (2014).
Shin, H., Lee, H., Seo, Y., Jeong, W. & Han, T. H. Grafting behavior of amine ligands for surface modification of MXene. Langmuir 39, 2358–2367 (2023).
Ko, T. Y. et al. Universal ligands for dispersion of two-dimensional MXene in organic solvents. ACS Nano 17, 1112–1119 (2023).
Onses, M. S., Sutanto, E., Ferreira, P. M., Alleyne, A. G. & Rogers, J. A. Mechanisms, capabilities, and applications of high-resolution electrohydrodynamic jet printing. Small 11, 4237–4266 (2015).
Galliker, P. et al. Direct printing of nanostructures by electrostatic autofocussing of ink nanodroplets. Nat. Commun. 3, 890 (2012).
Li, H. et al. Enhancing pulsed electrohydrodynamic printing frequency via high-order-mode ejection. Phys. Fluids 33, 081704 (2021).
Zhang, G. et al. Critical size/viscosity for coffee-ring-free printing of perovskite micro/nanopatterns. ACS Appl Mater. Interfaces 14, 14712–14720 (2022).
Jang, Y. et al. Non-contact printing of high aspect ratio Ag electrodes for polycrystalline silicone solar cell with electrohydrodynamic jet printing. Appl Phys. Lett. 102, 123901 (2013).
Kwon, H.-j et al. Overview of recent progress in electrohydrodynamic jet printing in practical printed electronics: focus on the variety of printable materials for each component. Mater. Adv. 2, 5593–5615 (2021).
Yu, M., Ahn, K. H. & Lee, S. J. Design optimization of ink in electrohydrodynamic jet printing: Effect of viscoelasticity on the formation of Taylor cone jet. Mater. Des. 89, 109–115 (2016).
Lim, S., Park, S. H., An, T. K., Lee, H. S. & Kim, S. H. Electrohydrodynamic printing of poly(3,4-ethylenedioxythiophene):poly(4-styrenesulfonate) electrodes with ratio-optimized surfactant. RSC Adv. 6, 2004–2010 (2016).
Zhou, H. et al. Overcoming the limitations of MXene electrodes for solution-processed optoelectronic devices. Adv. Mater. 34, 2206377 (2022).
Kim, S. et al. Instant self-assembly of functionalized MXenes in organic solvents: General fabrication to high-performance chemical gas sensors. Adv. Funct. Mater. 2310641 https://doi.org/10.1002/adfm.202310641 (2023).
Palumbiny, C. M. et al. The crystallization of PEDOT:PSS polymeric electrodes probed in situ during printing. Adv. Mater. 27, 3391–3397 (2015).
Parvez, K. et al. Electrochemically exfoliated graphene as solution-processable, highly conductive electrodes for organic electronics. ACS Nano 7, 3598–3606 (2013).
Li, Z. et al. Rational design of a printable, highly conductive silicone-based electrically conductive adhesive for stretchable radio-frequency antennas. Adv. Funct. Mater. 25, 464–470 (2015).
Feng, S., Tian, Z., Wang, J., Cao, S. & Kong, D. Laser sintering of Zn microparticles and its application in printable biodegradable electronics. Adv. Electron Mater. 5, 1800693 (2019).
Li, Z., Chang, S., Khuje, S. & Ren, S. Recent advancement of emerging nano copper-based printable flexible hybrid electronics. ACS Nano 15, 6211–6232 (2021).
Lee, Y. G. & Choi, W.-S. Electrohydrodynamic jet-printed zinc–Tin oxide TFTs and their bias stability. ACS Appl. Mater. Interfaces 6, 11167–11172 (2014).
Kim, M. J. et al. Universal three-dimensional crosslinker for all-photopatterned electronics. Nat. Commun. 11, 1520 (2020).
Lovinger, A. J. Ferroelectric polymers. Science 220, 1115–1121 (1983).
Yang, L. et al. Novel polymer ferroelectric behavior via crystal isomorphism and the nanoconfinement effect. Polymer 54, 1709–1728 (2013).
Kwon, H.-j et al. Facile photo-cross-linking system for polymeric gate dielectric materials toward solution-processed organic field-effect transistors: Role of a cross-linker in various polymer types. ACS Appl. Mater. Interfaces 12, 30600–30615 (2020).
Acknowledgements
This research was supported by the National Research Foundation of Korea (NRF) grant funded by the Korea government (MSIT): 2022M3J7A1062940 (S.J.P. and I.I.), 2022R1F1A1064314 (Y.J.J.), 2023R1A2C1004109 (S.J.P.), and 2020M3H4A3081819 (S.H.K.). This research was also supported by the Basic Science Research Program through the National Research Foundation of Korea (NRF), funded by the Ministry of Education: 2018R1A6A1A03023788 (I.I.) and 2021R1I1A1A01055790 (G.M.). This work was supported by the National Research Council of Science & Technology (NST) grant from the Korea government: CRC22031-000 (S.J.K.). This research was supported by Korea Electric Power Corporation: R21XO01-5 (S.J.P. and I.I.). This work was supported by the Leaders in Industry-University Cooperation Phase 3 (LINC 3.0) project funded by the South Korean Ministry of Education (S.J.P. and I.I.). T.Y.K., G.M., Y.H.P., and I.I. thank Nanoplexus Ltd, UK, for their support and valuable discussions.
Author information
Authors and Affiliations
Contributions
T.Y.K., H.Y., G.M., S.J.K., S.H.K., S.Y.L., and I.I. conceived the main ideas. T.Y.K., H.Y., and G.M. performed the overall experiments and characterizations. Y.H.P., J.Y.L., J.H.L., and D.J.Y. contributed to the characterization and discussed the overall experimental concepts. T.Y.K., G.M., Y.J.J., and I.I. drafted the manuscript. S.J.K., S.H.K., S.J.P., and Y.G. discussed the data, reviewed and edited the manuscript. I.I. supervised this study.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Karim Khan and Ping Ren for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ko, T.Y., Ye, H., Murali, G. et al. Functionalized MXene ink enables environmentally stable printed electronics. Nat Commun 15, 3459 (2024). https://doi.org/10.1038/s41467-024-47700-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-024-47700-y
- Springer Nature Limited