Abstract
Photocatalytic CO2 conversion promises an ideal route to store solar energy into chemical bonds. However, sluggish electron kinetics and unfavorable product selectivity remain unresolved challenges. Here, an ionic liquid, 1-ethyl-3-methylimidazolium tetrafluoroborate, and borate-anchored Co single atoms were separately loaded on ultrathin g-C3N4 nanosheets. The optimized nanocomposite photocatalyst produces CO and CH4 from CO2 and water under UV–vis light irradiation, exhibiting a 42-fold photoactivity enhancement compared with g-C3N4 and nearly 100% selectivity towards CO2 reduction. Experimental and theoretical results reveal that the ionic liquid extracts electrons and facilitates CO2 reduction, whereas Co single atoms trap holes and catalyze water oxidation. More importantly, the maximum electron transfer efficiency for CO2 photoreduction, as measured with in-situ μs-transient absorption spectroscopy, is found to be 35.3%, owing to the combined effect of the ionic liquid and Co single atoms. This work offers a feasible strategy for efficiently converting CO2 to valuable chemicals.
Similar content being viewed by others
Introduction
The worldwide consensus on carbon neutrality is driving the rapid development of technologies for CO2 conversions1,2. Recent research efforts have been devoted to photocatalytic CO2 conversion in pure water as a competitive route to produce valuable chemicals. However, it remains a huge challenge to construct efficient and stable photocatalytic systems3. Graphic carbon nitride (g-C3N4, CN), especially two-dimension nanosheets with controllable morphology, has emerged as a promising group of organic semiconductor photocatalysts, owing to its low cost, visible-light response, and robust nature. Notably, the negatively positioned conduction band (CB) imparts the photoelectrons of CN sufficient thermodynamic energy for the reduction of CO2. Nevertheless, its photocatalytic performance still suffers from fast charge carrier recombination as well as the lack of catalytic sites. Therefore, the photocatalyst design of CN-based photocatalysts is expected to prolong electron lifetime and improve CO2 reduction selectivity.
Loading suitable cocatalysts on CN is one of the most feasible strategies to simultaneously prolong the electron lifetime and introduce catalytic sites4,5,6. Ionic liquids (ILs) as a class of molten salts are composed of large, asymmetric organic cations and inorganic anions. The inherent features such as favorable dissolving/adsorbing ability, structural diversity, non-inflammability, wide electrochemical window, and high ion conductivity endow ILs with widespread applications7,8. Focusing on the typical imidazolium ILs, it is noted that the electronic structure of the imidazolium cation comprises a delocalized 3-center-4-electron conjunction across the N1-C2-N3 moiety, a double bond between C4 and C5 at the opposite side of the ring and a weak delocalization in the central region9,10. This would enable the cations to extract and stabilize electrons. Thus, it could be deduced that when using imidazolium IL as the surface modifier for a semiconductor, the imidazolium cation might extract electrons from the excited semiconductor. Moreover, imidazolium ILs have been comprehensively exploited to facilitate electrocatalytic CO2 reduction as appealing alternatives for conventional electrolytes/solvents11. Except for favorable CO2 adsorbing capability, research interest in imidazolium ILs mainly stems from their catalytic function for activating CO212,13,14. Many relevant works highlight the role of imidazolium ILs as cocatalysts. For example, 1-ethyl-3-methylimidazolium tetrafluoroborate ([emim][BF4])15 was reported capable of reducing the initial barrier of CO2 conversion while suppressing the H2 evolution reaction, which improved the selectivity of electrochemical CO2 conversion16. Based upon the above analysis, loading a tiny amount of IL [emim][BF4] on CN as the cocatalyst could prolong the lifetime of electrons and enable selective CO2 reduction.
In another aspect, a simultaneous introduction of another cocatalyst for capturing the holes and catalyzing the water oxidation could further prolong the electron lifetime. As extensively explored cocatalysts in photocatalysis, transition metal oxides like Co oxide, etc., perform dual-functions of hole trapper and catalyst for water photooxidation17,18. Inspired by the hot concept of single-atom catalysis, tailoring nanoscale Co oxide to the O-coordinated Co single atoms would shorten the hole transfer distance hence accelerating the hole-trapping process19. Moreover, Co single atoms might promote the activation of water to facilitate hole-initiated water photooxidation20. Referring to the reported synthesis of borate-mediated O-coordinated Ni single atoms on CN21, it is feasible to construct O-coordinated Co single atoms on the borate-modified CN (Co-bCN) as cocatalyst.
To sum up, CN nanosheets co-loaded by IL [emim][BF4] and borate-anchored Co single atoms (IL/Co-bCN) are promising photocatalysts to realize high-efficiency selective CO2 reduction in water. Although in some works ILs have been utilized as surface modifiers22, combining IL with single-atom sites to construct a photocatalytic system is an interesting attempt. More importantly, it is critical to clarify the individual effects and potential synergistic effects of two cocatalysts/modifiers on electron kinetics for CO2 photoreduction. Transient absorption spectroscopy (TAS) is known as a powerful technique to elucidate the charge carrier kinetics for photocatalysts23. The multi-electron transfer involved in CO2 photoreduction occurs at the timescales of microseconds to seconds. Therefore, the μs-TAS under reaction conditions, namely in situ μs-TAS, is applicable for investigating the multi-electron reduction process, however, which remains unexplored.
Here, IL [emim][BF4] and borate-anchored Co single atoms were co-loaded on ultrathin CN nanosheets to obtain IL/Co-bCN nanocomposites, respectively forming spatially separated reduction domains and oxidation domains. The optimal nanocomposite applied in the CO2 photoreduction exhibited 9- and 42-fold CO2 conversion rates compared with those of bCN and CN, respectively, and provided nearly 100% selectivity towards CO2 reduction with CO and CH4 as products. IL was found capable of extracting electrons and enabling selective CO2 reduction, while Co single atoms were proved to trap holes and catalyze water oxidation. By in situ μs-TAS, the electron transfer efficiency (ETE) of IL/Co-bCN was quantified to be 35.3%. In addition, the linear correlation between electron transfer rate (ETR) and the loading amount of IL was discovered for the IL-catalyzed CO2 photoreduction. This work has provided an efficient approach for enhanced artificial photosynthesis and an investigation paradigm using in situ TAS.
Results
Synthesis of co-modified g-C3N4 nanosheets by IL and Co single atoms
The IL/Co-bCN photocatalyst with dual-cocatalysts was synthesized as the procedures illustrated in Fig. 1. Using melamine and cyanuric acid as the raw material, pristine CN was fabricated by the H-bonding-induced self-assembling process followed by calcination. The second calcination with subsequent acid treatment for pristine CN resulted in ultrathin porous CN nanosheets (denoted as CN for short in the following discussion). With boric acid as the boron source, uniform borate species were modified on CN (bCN) driven by the dative B-N coordination through a low-temp hydrothermal process21. Next, the aqueous Co(NO3)2 solution was dropwise added into the aqueous bCN suspension under continuous stirring and ultrasound. As the previously reported synthetic method for Ni single atoms, the O-coordinated Co single atoms were constructed on bCN (Co-bCN) via the ion exchange between Co2+ with protons of supported borate species21.
On the other hand, since the hydrogen atoms bonding with the carbon atoms in [emim]+ are natural hydrogen donors24, they might form H-bonds with the sp2 nitrogen atoms of CN with large electronegativity. Accordingly, IL [emim][BF4] could be assembled on the exposed CN surface of Co-bCN to result in the IL/Co-bCN photocatalysts25, forming the separated reduction domains and oxidation domains.
Photocatalytic CO2 conversion
The activities of as-synthesized samples were evaluated for the gas-phase CO2 photoreduction under irradiation by the 300 W Xenon lamp (Fig. 2a). By altering the boric acid amount, the best performance for bCN was obtained with CO, CH4, and H2 (3.9, 1.7 and 1.7 μmol g−1 h−1) as the reduction products (Supplementary Fig. 1a). After introducing Co single atoms, optimal Co-bCN was acquired with the largest O2 production rate (867.5 μmol g−1 h−1) and CO2 conversion rate (20.6 μmol g−1 h−1) for the photocatalytic water oxidation and CO2 reduction, respectively (Supplementary Fig. 1b and c). Moreover, compared with CoOx-CN obtained by directly loading Co-oxo species on CN, borate-mediated Co single atoms demonstrate superiority as cocatalysts. While although the introduction of Co single atoms could facilitate the CO2 photoconversion, H2 was still evolved (9.7 μmol g−1 h−1) as an undesired by-product. The loading of typical ILs like 1-ethyl-3-methyl imidazolium hexafluorophosphate ([emim][PF6]), 1-ethyl-3-methylimidazolium bis (trifluoromethyl) sulfonylimide ([emim][NTF2]), 1-butyl-3-methylimidazolium tetrafluoroborate ([bmim][BF4]), and [emim][BF4] on bCN resulted in a series of IL-modified bCN nanocomposites. The chemical structures of ILs are shown in Supplementary Fig. 2. All samples, especially the [emim][BF4] one, greatly enhanced the photoactivity for CO2 photoreduction (Supplementary Fig. 1d).
a Photoreduction of CO2 and protons on bCN, IL/bCN, Co-bCN, and IL/Co-bCN under UV–vis light irradiation. Right Y-axis (green) indicates the product selectivity for CO2 photoreduction. b Oxygen evolution on bCN, IL/bCN, Co-bCN, and IL/Co-bCN during CO2 photoreduction. c Mass spectrum of the products from 13CO2 photoreduction by IL/Co-bCN. d Recycle test of IL/Co-bCN for the photocatalytic CO2 conversion. Data in panels a and b are presented as the mean ± standard deviation (s.d.) from three independent experiments.
The best IL/bCN ([emim][BF4]-modified sample) produces CO and CH4 with production rates of 12.3 and 2.8 μmol g−1 h−1, respectively (Supplementary Fig. 1e). Next, adopting the most effective [emim][BF4] of different amounts to modify Co-bCN could obtain a series of co-modified samples. The best one, denoted as IL/Co-bCN for short in the following discussion, provides the CO and CH4 production rates of 40.5 and 6.3 μmol g−1 h−1, respectively, noteworthily without any H2 evolution (Fig. 2a and Supplementary Fig. 1f; corresponding gas chromatography raw data is included in Supplementary Fig. 3). This suggests the introduction of [emim][BF4] could improve CO2 reduction selectivity and inhibit H2 evolution, consistent with the discoveries in the IL-facilitated electrochemical CO2 reduction11. Remarkably, optimal IL/Co-bCN could provide 9- and 42-fold CO2 conversion rates of those for bCN and CN with nearly 100% selectivity towards CO2 reduction. Besides, all typical samples are found to produce approximately stoichiometric O2 without other oxidation products like H2O2, etc. (Fig. 2b), indicating a complete cycle of the photocatalytic reaction between CO2 and water.
To confirm that the reduction products be derived from CO2, the photoreduction of 13C-labeled CO2 was conducted over the IL/Co-bCN. The dominant peak of 13CO (m/z = 29) and a small peak of 13CH4 (m/z = 17) were observed in the selective ion detection chromatography spectrum (Fig. 2c, raw data in Supplementary Fig. 4), testifying the evolved CO and CH4 over IL/Co-bCN originate from the photoreduction of CO2. Moreover, four consecutive runs were then carried out over IL/Co-bCN and the photoactivity for each run shows a negligible decrease (Fig. 2d), reflecting the robust nature of IL/Co-bCN under reaction conditions. The superiority of IL/Co-bCN is then demonstrated by the comparison with the representative cocatalyst-involved CN-based photocatalysts for CO2 reduction (Supplementary Table 1). Obviously, IL/Co-bCN, exhibits the most competitive photoactivity especially in terms of apparent quantum yield (1.00%, 405 nm) and CO2 reduction selectivity, thanks to the co-loading of IL and Co single atoms.
Structural characterizations
In the X-ray diffraction (XRD) patterns (Supplementary Fig. 5a), two characteristic diffraction peaks of CN at 13.1 and 27.3º are assigned to the in-planar repeated tri-s-triazine units (100) and the (002) interlayer stacking, respectively26. Compared with CN, bCN, and Co-bCN show no extra peaks due to either boron oxide or Co oxide, indicating the high dispersion of supported boron oxo- and Co species. For IL/Co-bCN, well-maintained peaks of CN indicate the introduction of IL does not change the crystalline structure of CN. The UV–vis diffuse reflectance spectra (DRS) show that neither IL nor Co species influence light absorption (Supplementary Fig. 5b). Besides, the specific surface area only decreases after loading IL due to the coverage (Supplementary Fig. 5c–f). Following this, the morphology of the samples was explored by transmission electron microscopy (TEM) and atomic force microscopy (AFM). As Supplementary Fig. 6a, CN takes on ultrathin silky nanosheets with random mesopores, in accordance with its specific surface area. For Co-bCN and CoOx-CN as a reference, no aggregates or particles could be observed in the TEM images (Supplementary Fig. 6b, c), indicating the high dispersion of both-type cobalt species. However, as shown by the photocatalytic performances, the borate-mediated Co single atoms are advantageous cocatalysts over the Co-oxo species in CoOx-CN. Compared with CN or Co-bCN (Supplementary Fig. 6d, e), the morphology and thickness of IL/Co-bCN (Fig. 3a and Supplementary Fig. 6f) remain nearly unchanged, once again proving the high dispersion of supported Co species and IL ion pairs on CN surface. The energy dispersive X-ray (EDX) mapping (Fig. 3b) images evidence the homogeneous state of C, N, B, O, Co and F elements, demonstrating the uniform distribution of borate species, Co species, and [BF4]− anions on CN for IL/Co-bCN.
a TEM image of IL/Co-Bcn. b The corresponding EDX mapping images of elemental C, N, B, O, Co, and F of IL/Co-bCN. Scale bar: 200 nm. c The HAADF-STEM image of Co-bCN. Note: dots in orange circles indicate single Co atoms. Scale bar: 5 nm. d Normalized XANES spectra of Co-bCN, CoO, and Co foil, respectively, at the Co K-edge. e Fourier transformation of EXAFS spectra at the Co K-edge. f The corresponding EXAFS fitting curves of single-atom Co-bCN. Inset: simulated structure model of Co-bCN.
The atomic-resolution high-angle-annular-dark-field scanning transmission electron microscopy (HAADF-STEM) image of Co-bCN was collected to disclose the specific distribution status of Co species. The isolated dots marked by orange circles are attributed to Co single atoms, undoubtedly proving the atomic dispersion of Co species on bCN (Fig. 3c).
According to the position of the rising edge of the Co K-edge X-ray absorption near edge structure (XANES) spectra, the oxidation state of Co single atoms for Co-bCN was determined with CoO and Co foil as contrast (Fig. 3d). The spectral line shape and the absorption edge position resemble those of CoO, indicating Co single atoms are in the valance of around +2. The Fourier transform of the extended X-ray absorption fine structure (EXAFS) spectra in Fig. 3e demonstrates that no first-shell Co-Co contribution exists, evidencing the single-atom state of Co species instead of metallic Co nanoparticles or clusters. The EXAFS data fitting results indicate the main peak is at about 2.0 Å, which value is close to the Co-O bond length of CoO (Fig. 3f and Supplementary Table 2)27,28. In addition, the coordination number of the Co single atom is determined to be five. Accordingly, the theoretical model of single Co sites was simulated and shown in Fig. 3f inset (bond lengths are shown in Supplementary Fig. 7a)29. To be specific, the O atoms of borate species along with water and hydroxyl groups coordinate with the Co atom, resulting in a five-O-coordinated Co single-atom site, which is denoted as a single Co (II)-O5 site. Interestingly, the brightness of individual dots on IL/Co-bCN in the HADDF-STEM image (Supplementary Fig. 7b) maintains, implying the introduction of IL does not influence the distribution of Co single atoms. This might be on account of the as-proposed separated domains for IL and Co single atoms on the CN surface. Besides, the chemical states of typical samples were also characterized by the X-ray photoelectron spectra (XPS) (Supplementary Fig. 8 and Supplementary Table 3). In the Co 2p spectra, similar to the Co 2p peaks of CoOx-CN, the Co 2p1/2 (795.8 eV) and Co 2p3/2 (780.3 eV) peaks with their satellites for Co-bCN are attributed to the oxidized cobalt in +2 valence, which is consistent with the XANES results30. By contrast, the binding energy (BE) of the Co 2p peaks of IL/Co-bCN shows a negligible shift, indicating IL do not affect the chemical state of Co single atoms. Moreover, the atomic concentration of Co for Co-bCN and IL/Co-bCN are almost identical, which further evidences the loading of IL does not affect Co single-atom sites (Supplementary Table 3). The F 1s peaks of IL/bCN and IL/Co-bCN locate at the same BE, attributed to the [BF4]− anion, suggesting IL ions are successfully introduced on CN and no strong chemical interaction exists between the [BF4]− anions and Co single atoms.
To validate the inferred H-bonding interaction between IL and CN in IL/Co-bCN, a simplified IL/CN model was set up by the molecular dynamics (MD) simulation. The simulation results reveal that the IL/CN system is stable (Supplementary Fig. 9a–d). The H-atoms bonding to C2, C4, and C5 (Supplementary Fig. 9e and f) in the [emim]+ ring could form H-bonds with the sp2 N atoms of CN. Despite the H-bonding interaction between [emim]+ and borate species might exist as the simulated IL/bCN model (Supplementary Fig. 10), the interaction between IL and CN in IL/Co-bCN is predominantly via the H-bonding between the [emim]+ and CN due to the advantageous dispersion rate of sp2 N atoms over the borate species.
Roles of IL and Co single atoms
The effects of IL and Co single atoms on the charge carrier properties were investigated by the photochemical and photophysical techniques. In the electron paramagnetic resonance (EPR) spectra under illumination, the signal intensities from 5, 5-dimethyl-l-pyrroline N-oxide (DMPO)-·OH adducts, where DMPO is used as the spin-trapping agent, are found to increase as the same order with the photocatalytic activities (bCN < IL/bCN < Co-bCN < IL/Co-bCN) (Supplementary Fig. 11a). Generally, the ·OH radicals are produced by photooxidation of water, hence which amount could reflect the efficiency of charge separation. Therefore, the EPR spectra for detecting DMPO-·OH adducts indicate that either IL or Co single atoms could improve the charge separation and the combination of two modifiers for IL/Co-bCN leads to the maximum improvement. Moreover, steady-state photoluminescence (PL) spectra and electrochemical impedance spectroscopy (EIS) agree well with the above conclusion (Supplementary Fig. 11b and c). To further distinguish the individual modulating features of IL and Co single atoms on the charge carriers of CN, the atmosphere-control surface photovoltage spectroscopy (AC-SPS) was performed on bCN, IL/bCN, and Co-bCN31. As Supplementary Fig. 12a, a negligible SPS signal of bCN was detected in the atmosphere of N2 due to the intrinsic poor charge separation. The signal intensities of IL/bCN in different atmospheres decrease as the order of O2 > air > N2, where O2 shows a positive effect on the charge separation. Since O2 is a well-known electron scavenger32, it can be inferred IL attract the photoelectrons to improve the charge separation (Supplementary Figure 12b)7. For Co-bCN, the signal intensities in different atmospheres decrease as the order of N2 > air > O2, as opposed to that for IL/bCN, where O2 is found to impose a negative effect. This suggests that Co single atoms trap holes instead of electrons to facilitate the charge separation (Supplementary Fig. 12c)33.
As another key factor, the catalytic functions of IL and Co single atoms, significantly determining catalytic efficiencies and selectivity, were investigated by collecting the electrochemical reduction/oxidation curves. In the electrochemical reduction system bubbled with CO2, IL/bCN shows the smallest onset potential for CO2 reduction, evidencing IL exerts the catalytic ability to activate CO2 molecules (Fig. 4a). This agrees with the reported catalytic effect of IL in electrocatalytic CO2 reduction34. While in the electrochemical oxidation system bubbled with N2, Co-bCN displays the smallest oxidation onset potential, confirming that Co single atoms could catalyze water oxidation (Fig. 4b). Accordingly, the enhanced photoactivity of IL/Co-bCN originates from the combined effect of IL for extracting electrons as well as catalyzing selective CO2 reduction and Co single atoms for capturing holes as well as catalyzing water oxidation.
a Electrochemical reduction curves of CN, bCN, and IL/bCN in the CO2-bubbled system. b Electrochemical oxidation curves of CN, bCN, and Co-bCN in the N2-bubbled system. c Fitted parameter for an assumed power-law decay (ITAS∝(t-t0)−β) of bCN, Co-bCN, and IL/bCN in the gaseous mixture of N2/H2O vapor, excited by pulsed 355 nm and monitored at 900 nm. d In situ μs-TAS spectra over IL/Co-bCN in the gaseous mixture of N2/H2O vapor or CO2/H2O vapor, excited by pulsed 355 nm and monitored at 900 nm. e Electron transfer rates (ETRs) versus IL amount on IL/bCN (black circle) and IL/Co-bCN (red square). The rate constant is obtained from the slope of the linear fit, whereas the background rate is taken from the intercept. f Differential charge density diagram of the CO2 + IL/CN system with isosurface value of 0.003 e/Å3.
To acquire a deep insight into the photocatalytic reaction mechanism over IL/Co-bCN, μs-TAS was employed to study the charge dynamics (Supplementary Fig. 13). The positive TAS signals of CN spanning the entire visible and near-IR regions are attributed to photoexcited electrons, while the hole contribution to the TAS signal is negligible35,36. Therefore, it is feasible to directly monitor the electron kinetics of CN but to indirectly observe hole transfer also by detecting the electron signal. The wavelength-dependent TAS signal of CN was measured with the addition of triethanolamine (TEOA) as a well-known efficient hole scavenger in order to verify the electron fingerprint regions35,36. Considering the TAS signal intensity increases as the wavelength, 900 nm as the fingerprint of the electrons was selected to be the detecting wavelength (Supplementary Fig. 14). As Fig. 4c, the μs-TAS curves for electron decay kinetics of bCN, Co-bCN, and IL/bCN at 900 nm are well fitted by a power law function of ITAS(t)∝(t-t0)−β, where β (0 < β < 1) represents the fitting stretching exponent, as evidenced by the linear decay on a log–log plot with a trapping-detrapping dynamics23,35,36,37,38. The fitting yields a β value of bCN, which is between those of IL/bCN and Co-bCN. Moreover, the half-lifetime denoted as t50 is defined as the time when 50% of the initial excited state population decayed by half, representing the average kinetic decay constant of the TAS curves. Therefore, it is reasonable to employ t50 to evaluate the electron kinetic decay process37,38. The intrinsic decay of bCN yields a representative electron t50 of 29.1 μs. Compared to bCN, the TAS amplitude of IL/bCN at the initial time decreases from 0.007 to 0.006 with a shorter electron lifetime (t50 = 22.5 μs), suggesting that electron transfer from bCN to IL. In contrast, Co-bCN shows higher TAS amplitude than that of bCN (increasing from 0.007 to 0.009) with a longer electron lifetime (t50 = 37.6 μs), inferring holes are trapped by Co single atoms. To evaluate the hole-trapping ability of Co single atom, the electron decay kinetics of Co-bCN was compared with that of bCN with methanol (MeOH) added as an efficient hole scavenger (the moles of MeOH are identical with those for cobalt in Co-bCN). It is observed Co-bCN (t50 = 37.6 μs) exhibits a longer t50 than bCN with MeOH added (t50 = 31.9 μs) (Supplementary Fig. 15), which suggests that Co single atoms possess a stronger ability to extract holes than MeOH. Overall, the modulating features of IL and Co single atoms were verified to be effective electron extractors and hole trappers, respectively.
Following the charge dynamics observation, the subsequent issue lies in understanding the kinetics mechanism of CO2 photoreduction, which is crucial to designing photocatalytic materials. By far, the kinetic mechanisms of CO2 photoreduction remain unclear, due to the inadequate fundamental understanding of charge carrier kinetics in a real reaction system. In situ μs-TAS is a powerful technique to elucidate the charge carrier kinetics of the photocatalysts by monitoring the reaction process39. Time-dependent observation of CO2 reduction could reveal insight into the depopulation mechanisms of the charge state of samples. The in situ TAS kinetics for specific samples was collected by imputing gaseous mixture of CO2/H2O vapor into the sample cell to mimic the CO2 reduction conditions, respectively. Besides, the measurements by imputing gaseous mixture of N2/H2O vapor were performed as a contrast. The TAS signal at 900 nm measures the population of the electron state that decays following the power law to the ground state through radiative and non-radiative processes with the rate of 1/t50 (N2) = kR + kNR and 1/t50 (CO2) = kR + kNR + kET in the presence of N2/H2O vapor and CO2/H2O vapor, respectively, where kR and kNR were introduced as the intrinsic radiative rate and nonradiative rate on bCN, respectively, and the kET for the ETR, which indicates the electron transfer rate from the photocatalyst to CO2. The electron transfer efficiency (ETE) during the CO2 reduction is expressed by the following equation:40,41,42
Based on Eq. (1), it can be inferred that boosting the ETE for CO2 reduction, which describes the effectiveness of the electron transfer processes, can be achieved by facilitating the electron capture by CO2 on the basis of the prolonged electron lifetime of bCN by hole trapping. The ETE for CO2 reduction was calculated based on Eq. 1 and presented in Supplementary Fig. 16. The ETE of bCN is as low as ~0.7%, indicating that CO2 could hardly capture electrons from bCN. The TAS decay of IL/bCN distinctly becomes fast with a t50 of ∼16.5 μs in the presence of CO2, indicating that IL open the channel for CO2 to capture electrons and serve as good catalytic activation sites for CO2 reduction. While after the Co single-atom modification, although the electron lifetime was prolonged, the ETE of ~3.2% is still limited. By contrast, the maximum ETE reaches ∼35.3% for IL/Co-bCN as calculated according to the TAS kinetics in Fig. 4d, which is around 93-fold of that for CN (0.3%). Therefore, the photoactivity enhancement of IL/Co-bCN is attributed to the high ETE contributed by IL based on prolonged electron lifetime due to the hole-trapping function of Co single atoms.
To elucidate IL-catalyzed CO2 reduction kinetics, the quantitative effect of IL was examined on the ETR, which was calculated based on the formula of kET = 1/t50(CO2) − 1/t50(CO2)41,42. Based on the above TAS results, IL has been verified to function as a favorable electron acceptor and also a catalyst for CO2 reduction, however, which has seldom been investigated in photocatalysis. Thus, the quantitative relationship between the loading amount of IL and the corresponding ETR was further explored. The ETR values on the xIL/bCN and xIL/Co-bCN, where x indicates the loading amount of IL, are calculated based on the analysis of their TAS decay curves (Supplementary Figs. 17 and 18), and summarized in Supplementary Tables 4 and 5, respectively. For IL/bCN, the ETR increases with the IL amount, indicating that the IL modification greatly accelerates electron transfer kinetics (Fig. 4e). Moreover, the ETR as a function of the IL amount can be well fitted by the first-order kinetics of kET = Kc43,44, where c and K represent the IL amount and the rate constant, respectively, implying the photocatalytic CO2 reduction with IL as the catalytic sites might obey the first-order principle. The fitting yields a large rate constant of 2.4 × 107 M−1 s−1 on IL/bCN photocatalyst. Besides, the kinetic analysis also informs us of a slow background reaction rate k0 of 238 s−1, due to the weak CO2 activation in the absence of IL. By the co-modification of IL and Co single atoms, the reaction rate constant increases up to 3.3 × 107 M−1 s−1, owing to prolonged electron lifetime and the promoted CO2 activation by the synergistic effects of two cocatalysts.
Moreover, the theoretical analysis by combining the density functional theory (DFT) calculation and MD simulation was performed to further validate the modulating features of two cocatalysts. For the simulated Co-bCN model (Supplementary Fig. 19a and b), the differential charge density diagram and hole distribution of excited Co-bCN (Supplementary Fig. 19c and d) indicate the region around Co single atoms is in positive charge after excitation, proving Co single atoms can trap holes. On the other hand, the electrons of the IL/CN system predominantly distribute at the [emim]+ ring and the IL/CN interface, indicating ILs might extract the photoelectrons (Supplementary Fig. 9c and d). Furthermore, when CO2 exists, the direct adsorption of CO2 on CN is found unstable (Supplementary Fig. 20). While for the equilibrium geometry of the CO2 + IL/CN system, the CO2 molecule tends to locate near the bonding region between IL and CN. By comparing the adsorption distance and interaction energy, the CO2 adsorption for the CO2 + IL/CN system is more stable than that for the CO2 + CN system (Supplementary Fig. 21). The electron density of the CO2 + IL/CN system shows that the electron populations are larger on the side of [emim]+, again manifesting IL could extract electrons (Fig. 4f).
To uncover the whole photocatalytic reaction mechanism, especially the catalytic reduction process, the adsorption of reactants was examined on typical samples by FTIR. The saturated adsorption spectra of the gaseous CO2/H2O vapor mixture for bCN, IL/bCN, and Co-bCN were separately collected under dark conditions (Supplementary Fig. 22a–c, Fig. 5a). Generally, the bands at 2350 and 3400 cm−1 demonstrate the adsorption of CO2 and water, respectively. The adsorption capacity for CO2 on IL/bCN (Fig. 5a, the left panel) is greatly enhanced compared with bCN or Co-bCN. This is because CO2 is prone to bind with imidazolium cations to form adducts, which has been comprehensively reported12,13,14. Compared with bCN and IL/bCN, Co-bCN shows an obviously enlarged peak area (Fig. 5a, the right panel), demonstrating promoted adsorption capacity of water over Co single atoms. Therefore, IL/Co-bCN with both cocatalysts shows the simultaneously promoted adsorption with CO2 and water, providing the foundation for efficient photocatalytic conversion.
a FTIR spectra for adsorption of gaseous mixture of CO2/H2O vapor on IL/bCN (left panel) and Co-bCN (right panel) in dark, respectively. b In situ FTIR spectra for the CO2 photoreduction process on IL/Co-bCN. c Illustration of the proposed photocatalytic mechanism of CO2 photoconversion over IL/Co-bCN under UV–vis light irradiation.
Furthermore, to detect the intermediates involved in the photocatalytic CO2 reduction catalyzed by IL/Co-bCN, in situ FTIR measurements were performed on typical samples under reaction conditions. The infrared peak intensities of bCN show minor changes as the extension of the irradiation time, reflecting its weak photoactivity for CO2 reduction (Supplementary Fig. 22d). For IL/bCN and Co-bCN, the most remarkable difference between the two individual modified samples is that the peak intensity of COOH* regarded as the key intermediate for CO2 reduction becomes larger when IL is involved (Supplementary Fig. 22e and f).
For IL/Co-bCN, the peak appearing at 1080 cm−1 is ascribed to CHO*, which is the intermediate correlated with the formation of CH445,46. The intermediates including CO32− (1326 and 1382 cm−1), HCO3* (1243, 1408, and 1458 cm−1) and COOH* (1554 and 1638 cm−1) are also detected (Fig. 5b). For the identical duration, the peak areas of IL/Co-bCN assigned to HCO3*, CO32− and COOH* are obviously the largest among all tested samples, indicating the advantage of bi-functionalization on the photocatalytic CO2 reduction. In addition, the in situ FTIR spectra using 13CO2 instead of 12CO2 further verified the production of key intermediates as mentioned above, supporting the speculative photocatalytic CO2 reduction process mechanism on IL/Co-bCN (Supplementary Fig. 23).
Discussion
On the basis of the above results and analysis, a possible mechanism for CO2 photoreduction over IL/Co-bCN is proposed in Fig. 5c. Under UV–vis light irradiation, Co single atoms would trap holes and catalyze water oxidation, which prolongs the electron lifetime. While the [emim]+ cations on CN can extract photoelectrons to further prolong their lifetime and catalyze CO2 reduction. For the specific CO2 reduction process catalyzed by imidazolium ILs, it is proposed that carboxylation at the C2 position of imidazolium cations would occur, which is triggered by the reaction with CO2. The formation of the corresponding CO2-imidazolium adduct has been verified by 13C-nuclear magnetic resonance (NMR) in some works47,48,49,50,51,52,53. In addition, C4 and C5 atoms are also possible binding positions for CO254. Combining these discoveries and the detected intermediates by in situ FTIR, the CO2 reduction pathway with [emim]+ as cocatalyst was illustrated, where the C2 atom of [emim]+ is showcased as the binding position. In particular, CO2 would bind with the C2 atom of N-heterocyclic carbene intermediate derived from reduced [emim]+ by one electron, resulting in the CO2-[emim] adduct. A subsequent reduction of the CO2-[emim] adduct by one electron leads to the formation of the COOH*-[emim] adduct, which is then attacked by one proton to generate the CO-[emim] adduct and one water molecule. Eventually, the attack by one proton enables the production of CO meanwhile [emim] turns back to [emim]+. As supplementary, the minor portion of CO-[emim] adduct is inferred to be attacked by continuous multiple electrons and protons to produce CH455. In addition, IL might generate a positively charged interfacial layer to repel protons hence inhibiting the H2 evolution56.
To summarize, co-loading of IL [emim][BF4] and borate anchored Co (II)-O5 single sites on CN resulted in IL/Co-bCN photocatalysts, forming spatially separated reduction domains and oxidation domains. The optimized photocatalyst realized 42-fold CO2 conversion rate of that for CN and nearly 100% selectivity towards CO2 reduction. IL was evidenced to attract electrons and facilitate CO2 reduction, whereas Co single atoms could extract holes and catalyze water oxidation, supported by experimental results and theoretical simulation. Employing in situ μs-TAS, the ETE on IL/Co-bCN for photocatalytic CO2 reduction was quantified to be 35.3%, which is 93-fold of that for CN. The effectively accelerated electron kinetics is attributed to the combined effect of IL and Co single atoms. Moreover, the linear correlation between IL loading amount and ETR is discovered for the IL-catalyzed CO2 photoreduction. Thus, this work provides a comprehensive insight into electron kinetics for photocatalysis.
Methods
Material preparation
All chemicals and reagents were of analytical grade and used without further purification, which can be found in Supplementary Information (Material preparation). Deionized water used in all the experiments has a resistivity of 18.1 MΩ cm.
Synthesis of bulk CN
Melamine (10 g) and cyanuric acid (4 g) were dispersed in deionized water (500 mL) and mixed under continuous stirring at 80 °C for 3 h. The mixture was cooled to room temperature, centrifuged at 4000 rpm for 5 min, and then dried at 80 °C for 12 h. The as-obtained powder was calcinated in a tube furnace from room temperature to 520 °C at a rate of 1 °C min−1 for 4 h under the N2 atmosphere to obtain bulk g-C3N4 (bulk CN).
Synthesis of ultrathin CN
Bulk CN underwent two-time calcination in the semi-closed porcelain boat at 500 °C for 2 h in the air atmosphere. After natural cooling to room temperature, the as-obtained fluffy product was treated with HNO3 solution (5 mol L−1) and then dried for 12 h in the vacuum at 80 °C to obtain ultrathin CN.
Synthesis of boric acid modified CN (bCN)
Ultrathin CN (0.5 g) was dispersed in deionized water (30 mL) under stirring and ultrasound for 1 h to result in an aqueous CN suspension. A desired volume of aqueous boric acid solution (0.05 mol L−1) was added into the CN suspension followed by stirring and ultrasound for 3 h. The as-obtained mixture was further transferred into a stainless-steel vessel and kept at 120 °C for 2 h. After cooling to room temperature naturally, the solid powder was centrifuged (8000 rpm), washed with absolute ethanol, and then dried in the vacuum at 60 °C. The samples were represented by xbCN, in which x% indicates the mass ratio (9, 12, and 15%) of boric acid relative to CN.
Synthesis of Co-single-atom modified bCN (Co-bCN)
As-obtained bCN (0.2 g) was dispersed in deionized H2O (100 mL) under stirring and ultrasound for 0.5 h to result in aqueous bCN suspension. A certain volume of aqueous Co(NO3)2 solution was dropwise added into the bCN suspension. The as-obtained liquid mixture was stirred in the water bath at 80 °C for 3 h. Finally, the solid powder was centrifuged (8000 rpm), washed with absolute ethanol thoroughly, and dried in the vacuum at 60 °C. The samples were represented by yCo-bCN, where y × 10−5 indicates the concentration (1.0 × 10−5, 1.5 × 10−5, and 2.1 × 10−5 mol L−1) of Co(NO3).
Synthesis of IL-modified bCN (IL/bCN)
An even mixture of [emim][BF4]and MeOH with an IL concentration of 5 mmol L−1 was prepared. As-obtained bCN (0.05 g) was introduced in the IL/ MeOH solution of the desired volume to result in uniform suspension under ultrasound conditions. Afterward, the suspension was dried in a vacuum oven at 80 °C for 12 h. As-synthesized samples were denoted as mIL/bCN, where m indicates the concentration (0.5, 0.625, and 0.75 mmol L−1) of IL. For the modification of other ILs ([emim][PF6]), [bmim][BF4], and [emim][NTF2]), identical synthetic procedures were performed as above.
Synthesis of IL-modified Co-bCN (IL/Co-bCN)
The synthetic procedure is the same as that for IL/bCN by replacing bCN with optimal Co-bCN. As-synthesized samples were denoted as nIL/Co-bCN, where n indicates the concentration (0.5, 0.625, and 0.75 mmol L−1) of IL.
Characterisations
The X-ray powder diffraction (XRD) patterns of the samples were measured with a Bruker D8 Advance diffractometer, using Cu Ka radiation. The UV–vis absorption spectra of the samples were measured with a Model Shimadzu UV2550 spectrophotometer, using BaSO4 as a reference. The Fourier transform infrared (FTIR) spectra of the samples were collected with a Bruker Equinox 55 Spectrometer, using KBr as diluents. The FTIR spectra in the figures have been normalized to the background before and after the main features. The X-ray photoelectron spectroscopy (XPS) technique was used to detect the surface composition and elemental chemical state of the samples, by using a Model VG ESCALAB apparatus with an Mg K X-ray source, and the binding energies were calibrated with respect to the signal for adventitious carbon (binding energy = 284.6 eV). The morphology of the samples was analyzed by transmission electron microscopy (TEM) on the FEI Tecnai G2 S-Tw in an instrument with an acceleration voltage of 200 kV. The thickness of the samples was analyzed by Atomic force microscopy (AFM) on a multimode nanoscope VIII instrument (Bruker) with mica as the base. The high-angle annular dark field scanning transmission electron microscopy (HAADF-STEM) images were collected on the FEI Titan 60–300 electron microscope equipped with a spherical aberration corrector. X-ray absorption spectroscopy (XAS) measurements were conducted at BL12B1 of Taiwan Beam Line in the SPring-8. The electron-storage ring was operated at 8 GeV with a current of 100 mA. A Si (111) double-crystal monochromator was employed for the energy selection with the resolution dE/E better than 2 × 10−4 at elemental edges. All XAS spectra were recorded at room temperature in fluorescence (for sample) and transmission (for reference) mode.
Photocatalysis measurements
For the photocatalytic CO2 reduction test, the powder sample (0.05 g) was dispersed on filter paper contained in a cylindrical quartz reactor. Pure water (3 mL) was added below the holder, providing humidity while avoiding direct contact with the samples. The reactor system was then filled with the gaseous mixture of CO2/H2O by bubbling pure CO2 (15 bar) through deionized water following the complete evacuation and equilibrated for 20 min. When the adsorption reached equilibrium, the reactor system was irradiated with the 300 W Xenon lamp as the light source and the light output power was measured by a MEIKONG TN99D calibrated photodetector. Meanwhile, the circulating water was applied to control the temperature of the photocatalytic reduction at room temperature. The environment temperature (25 oC) and relative humidity (50%) were controlled to be constant by the air conditioner. The gaseous product mixture (0.25 mL) was withdrawn from the headspace of the reaction cell at given time intervals for the quantitative analysis of carbon-containing reduction products by the gas chromatograph (GC-7920, CEAULIGHT) with flame ionization detector (FID). Similarly, the gaseous mixture (0.25 mL) was also withdrawn for the quantitative analysis of produced H2 and O2 during the CO2 photoconversion by the gas chromatograph (GC-2002, KE CHUANG) equipped with the thermal conductivity detector (TCD). The isotopic experiment also followed similar procedures, but CO2 was replaced by 13CO2 (Yuejia Gas, Guangdong, China). The products were detected by the gas chromatography-mass spectrometer (GC-7890B/MS5977A, Agilent, America). For the photocatalytic water oxidation test for yCo-bCN, 50 mg of photocatalyst powder was well dispersed in an aqueous solution (100 mL) containing AgNO3 (0.01 mol L−1) as an electron scavenger and La2O3 (0.2 g) as a pH buffer agent. The gaseous product (0.25 mL) was withdrawn for the quantitative analysis of O2 also by the gas chromatograph (GC-2002, KE CHUANG) equipped with the thermal conductivity detector (TCD).
Data availability
The authors declare that the data that supports the findings of this manuscript can be found in the Supplementary Information and are available free of charge or available from the corresponding author upon request. The source data underlying Figs. 2a–d, 3d–f, 4a–e and 5a, b on the experimental as well as the source data underlying Fig. 4f on the theoretical simulation of CO2 + IL/CN system are provided as a Source Data file. Source data are provided with this paper.
References
Zhou, L. Q. et al. A high-performance oxygen evolution catalyst in neutral-pH for sunlight-driven CO2 reduction. Nat. Commun. 10, 4081 (2019).
Wang, Y., Chen, E. & Tang, J. Insight on reaction pathways of photocatalytic CO2 conversion. ACS Catal. 12, 7300–7316 (2022).
Collado, L. et al. Unravelling the effect of charge dynamics at the plasmonic metal/semiconductor interface for CO2 photoreduction. Nat. Commun. 9, 4986 (2018).
Zheng, Y., Chen, Y., Gao, B., Lin, B. & Wang, X. Black phosphorus and carbon nitride hybrid photocatalysts for photoredox reactions. Adv. Funct. Mater. 30, 2002021 (2020).
Yang, P., Wang, R., Zhou, M. & Wang, X. Photochemical construction of carbonitride structures for red-light redox catalysis. Angew. Chem. Int. Ed. 57, 8674–8677 (2018).
Huang, C. et al. Unraveling fundamental active units in carbon nitride for photocatalytic oxidation reactions. Nat. Commun. 12, 320 (2021).
Wang, S. & Wang, X. Imidazolium ionic liquids, imidazolylidene heterocyclic carbenes, and zeolitic imidazolate frameworks for CO2 capture and photochemical reduction. Angew. Chem. Int. Ed. 55, 2308–2320 (2016).
Yang, Q. et al. Ionic liquids and derived materials for lithium and sodium batteries. Chem. Soc. Rev. 47, 2020–2064 (2018).
Hunt, P. A., Kirchner, B. & Welton, T. Characterising the electronic structure of ionic liquids: an examination of the 1-butyl-3-methylimidazolium chloride ion pair. Chem 12, 6762–6775 (2006).
Weingartner, H. Understanding ionic liquids at the molecular level: facts, problems, and controversies. Angew. Chem. Int. Ed. 47, 654–670 (2008).
Lin, J., Ding, Z., Hou, Y. & Wang, X. Ionic liquid co-catalyzed artificial photosynthesis of CO. Sci. Rep. 3, 1056 (2013).
Rosen, B. A. et al. Ionic liquid-mediated selective conversion of CO2 to CO at low overpotentials. Science 334, 643–644 (2011).
Qadir, M. I. et al. Reverse semi-combustion driven by titanium dioxide-ionic liquid hybrid photocatalyst. ChemSusChem 13, 5580–5585 (2020).
Peng, Y., Szeto, K. C., Santini, C. C. & Daniele, S. Study of the parameters impacting the photocatalytic reduction of carbon dioxide in ionic liquids. ChemPhotoChem 5, 1–7 (2021).
Zhu, X. et al. High-efficiency perovskite solar cells with imidazolium-based ionic liquid for surface passivation and charge transport. Angew. Chem. Int. Ed. 60, 4238–4244 (2021).
Yu, S. & Jain, P. K. Plasmonic photosynthesis of C1-C3 hydrocarbons from carbon dioxide assisted by an ionic liquid. Nat. Commun. 10, 2022 (2019).
Qarechalloo, S., Naseri, N., Salehi, F. & Moshfegh, A. Z. Simply tuned and sustainable cobalt oxide decorated titania nanotubes for photoelectrochemical water splitting. Appl. Surf. Sci. 464, 68–77 (2019).
Chang, X. et al. Enhanced surface reaction kinetics and charge separation of p–n heterojunction Co3O4/BiVO4 photoanodes. J. Am. Chem. Soc. 137, 8356–8359 (2015).
Babucci, M., Guntida, A. & Gates, B. C. Atomically dispersed metals on well-defined supports including zeolites and metal-organic frameworks: structure, bonding, reactivity, and catalysis. Chem. Rev. 120, 11956–11985 (2020).
Zhang, H. H. et al. Polar O-Co-P surface for bimolecular activation in catalytic hydrogen generation. Energ. Environ. Mater. 0, 1–10 (2022).
Wang, Y. et al. Construction of six-oxygen-coordinated single Ni sites on g-C3N4 with boron-Oxo species for photocatalytic water-activation-induced CO2 reduction. Adv. Mater. 33, 2105482 (2021).
Ren, W. et al. Confinement of ionic liquids at single-Ni-sites boost electroreduction of CO2 in aqueous electrolytes. ACS Catal. 10, 13171–13178 (2020).
Tang, J., Durrant, J. R. & Klug, D. R. Mechanism of photocatalytic water splitting in TiO2. Reaction of water with photoholes, Importance of charge carrier dynamics, and evidence for four-hole chemistry. J. Am. Chem. Soc. 130, 13885–13891 (2008).
Hunt, P. A., Ashworth, C. R. & Matthews, R. P. Hydrogen bonding in ionic liquids. Chem. Soc. Rev. 44, 1257–1288 (2015).
Putz, M. V., Russo, N. & Sicilia, E. About the Mulliken electronegativity in DFT. Theor. Chem. Acct. 114, 38–45 (2005).
Kang, Y. et al. An amorphous carbon nitride photocatalyst with greatly extended visible-light-responsive range for photocatalytic hydrogen generation. Adv. Mater. 27, 4572–4577 (2015).
Tang, C. et al. Tailoring acidic oxygen reduction selectivity on single-atom catalysts via modification of first and second coordination spheres. J. Am. Chem. Soc. 143, 7819–7827 (2021).
Yin, P. et al. Single cobalt atoms with precise N-coordination as superior oxygen reduction reaction catalysts. Angew. Chem. Int. Ed. 128, 1–7 (2016).
Yang, T. et al. A theoretical investigation on CO oxidation by single-atom catalysts M-1/-Al2O3 (M=Pd, Fe, Co, and Ni). Chemcatchem 9, 1222–1229 (2017).
Yang, Y. et al. In situ grown single-atom cobalt on polymeric carbon nitride with bidentate ligand for efficient photocatalytic degradation of refractory antibiotics. Small 16, 2001634 (2020).
Feng, J. et al. Efficient wide-spectrum photocatalytic overall water splitting over ultrathin molecular nickel phthalocyanine/BiVO4 Z-scheme heterojunctions without noble metals. Appl. Catal. B: Environ. 295, 126260 (2021).
Zhan, H. Y. et al. Photocatalytic O2 activation and reactive oxygen species evolution by surface B-N bond for organic pollutants degradation. Appl. Catal. B. 310, 121329 (2022).
Hu, K. et al. Synergetic subnano Ni‐ and Mn‐Oxo clusters anchored by chitosan oligomers on 2D g‐C3N4 boost photocatalytic CO2 reduction. Sol. RRL 5, 2000472 (2020).
Tateno, H., Nakabayashi, K., Kashiwagi, T., Senboku, H. & Atobe, M. Electrochemical fixation of CO2 to organohalides in room-temperature ionic liquids under supercritical CO2. Electrochim. Acta 161, 212–218 (2015).
Godin, R., Wang, Y. O., Zwijnenburg, M. A., Tang, J. W. & Durrant, J. Time-resolved spectroscopic investigation of charge trapping in carbon nitrides photocatalysts for hydrogen generation. J. Am. Chem. Soc. 139, 5216–5224 (2017).
Kasap, H. et al. Solar-driven reduction of aqueous protons coupled to selective alcohol oxidation with a carbon nitride–molecular Ni catalyst system. J. Am. Chem. Soc. 138, 9183–9192 (2016).
Miao, T. J. & Tang, J. W. Characterization of charge carrier behavior in photocatalysisusing transient absorption spectroscopy. J. Chem. Phys. 152, 194201 (2020).
Corby, S., Rao, R. R., Steier, L. & Durrant, J. The kinetics of metal oxide photoanodes from charge generation to catalysis. Nat. Rev. Mater. 6, 1136–1155 (2021).
Wang, Y. et al. Unique hole-accepting carbon-dots promoting selective carbon dioxide reduction nearly 100% to methanol by pure water. Nat. Commun. 11, 2531 (2020).
Kongkanand, A., Tvrdy, K., Takechi, K., Kuno, M. & Kamat, P. V. Quantum dot solar cells. Tuning photoresponse through size and shape control of CdSe-TiO2 architecture. J. Am. Chem. Soc. 130, 4007–4015 (2008).
Tvrdy, K., Frantsuzov, P. A. & Kamat, P. V. Photoinduced electron transfer from semiconductor quantum dots to metal oxide nanoparticles. Proc. Natl Acad. Sci. USA 108, 29–34 (2011).
Sun, J., Zhao, J. & Masumoto, Y. Shell-thickness-dependent photoinduced electron transfer from CuInS2/ZnS quantum dots to TiO2 films. Appl. Phys. Lett. 102, 053119 (2013).
Wang, X., Shi, H. & Szanyi, J. Controlling selectivities in CO2 reduction through mechanistic understanding. Nat. Commun. 8, 513 (2017).
James, W. et al. Electrochemical reduction of CO2 to CO catalyzed by a bimetallic palladium complex. Organometallics 25, 3345–3351 (2006).
Wang, B. et al. Sacrificing ionic liquid-assisted anchoring of carbonized polymer dots on perovskite-like PbBiO2Br for robust CO2 photoreduction. Appl. Catal. B. 254, 551–559 (2019).
Li, X. et al. Selective visible-light-driven photocatalytic CO2 reduction to CH4 mediated by atomically thin CuIn5S8 layers. Nat. Energy 4, 690–699 (2019).
Sun, L., Ramesha, G. K., Kamat, P. V. & Brennecke, J. F. Switching the reaction course of electrochemical CO2 reduction with ionic liquids. Langmuir 30, 6302–6308 (2014).
Zhao, S. F., Horne, M., Bond, A. M. & Zhang, J. Is the imidazolium cation a unique promoter for electrocatalytic reduction of carbon dioxide? J. Phys. Chem. C. 120, 23989–24001 (2016).
Lau, G. P. S. et al. New insights into the role of imidazolium-based promoters for the electroreduction of CO2 on a silver electrode. J. Am. Chem. Soc. 138, 7820–7823 (2016).
Qadir, M. I. et al. Photocatalytic reverse semi-combustion driven by ionic liquids. ChemSusChem 12, 1011–1016 (2019).
Wei, C., Jiang, K., Fang, T. & Liu, X. Effects of anions and alkyl chain length of imidazolium-based ionic liquids at the Au (111) surface on interfacial structure: a first-principles study. GreenChE 2, 402–411 (2021).
Tan, X, Sun, X. & Han, B. Ionic liquid-based electrolytes for CO2 electroreduction and CO2 electroorganic transformation. Natl. Sci. Rev. 9, nwab022 (2022).
Brennecke, J. F. & Gurkan, B. E. Ionic liquids for CO2 capture and emission reduction. J. Phys. Chem. Lett. 1, 3459–3464 (2010).
Asadi, M. et al. Robust carbon dioxide reduction on molybdenum disulphide edges. Nat. Commun. 5, 4470 (2014).
Kang, X. et al. Highly efficient electrochemical reduction of CO2 to CH4 in an ionic liquid using a metal–organic framework cathode. Chem. Sci. 7, 266–273 (2016).
Wagner, A., Sahm, C. D. & Reisner, E. Towards molecular understanding of local chemical environment effects in electro- and photocatalytic CO2 reduction. Nat. Catal. 3, 775–786 (2020).
Acknowledgements
L.B. and L.J. acknowledge NSFC projects (Grant No: U1805255 and U2102211). L.X. and J.T. are thankful for UK EPSRC (EP/S018204/2), Leverhulme Trust (RPG-2017-122), Royal Society Newton Advanced Fellowship grant (NAF\R1\191163), and Royal Society Leverhulme Trust Senior Research Fellowship (SRF\R1\21000153). We thank Dr. Cailing Chen for collecting HAADF-STEM images and Dr. Shibo Xi for performing the XAS and EXAFS tests. We also thank Dr. Haochun Yin, Ms Ling Sun, and Dr. Zhenlong Zhao for the materials synthesis and discussion.
Author information
Authors and Affiliations
Contributions
L.B., J.T., and L.J. conceived and supervised the entire project. Y.L. and B.Q. prepared the materials and carried out the photocatalytic activity tests and materials characterizations. H.H.H. and F.B. carried out the molecular dynamics simulation. J.S. and X.Z. carried out the TAS measurements and analysis. Y.L. did TEM, HRTEM, FTIR analysis. L.B. and L.X. did the XAS, EXAFS and HAADF-STEM image analysis. L.X. discussed the reaction mechanism. Y.L., J.S., and L.B. wrote the manuscript. All authors contributed to the discussion and revisions.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks ZhengMing Sun and the other, anonymous, reviewers for their contribution to the peer review of this work.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Liu, Y., Sun, J., Huang, H. et al. Improving CO2 photoconversion with ionic liquid and Co single atoms. Nat Commun 14, 1457 (2023). https://doi.org/10.1038/s41467-023-36980-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-023-36980-5
- Springer Nature Limited
This article is cited by
-
Solvent-free selective hydrogenation of nitroaromatics to azoxy compounds over Co single atoms decorated on Nb2O5 nanomeshes
Nature Communications (2024)
-
Photocatalytic CO2 reduction to CO by Cobalt(II) Pyridinyl-1,3,5-Triazine-Diamine complexes
Transition Metal Chemistry (2024)