Abstract
Collagens are the most abundant proteins of the extracellular matrix, and the hierarchical folding and supramolecular assembly of collagens into banded fibers is essential for mediating cell-matrix interactions and tissue mechanics. Collagen extracted from animal tissues is a valuable commodity, but suffers from safety and purity issues, limiting its biomaterials applications. Synthetic collagen biomaterials could address these issues, but their construction requires molecular-level control of folding and supramolecular assembly into ordered banded fibers, comparable to those of natural collagens. Here, we show an innovative class of banded fiber-forming synthetic collagens that recapitulate the morphology and some biological properties of natural collagens. The synthetic collagens comprise a functional-driver module that is flanked by adhesive modules that effectively promote their supramolecular assembly. Multiscale simulations support a plausible molecular-level mechanism of supramolecular assembly, allowing precise design of banded fiber morphology. We also experimentally demonstrate that synthetic fibers stimulate osteoblast differentiation at levels comparable to natural collagen. This work thus deepens understanding of collagen biology and disease by providing a ready source of safe, functional biomaterials that bridge the current gap between the simplicity of peptide biophysical models and the complexity of in vivo animal systems.
Similar content being viewed by others
Introduction
Collagens are fibrous proteins. They are the most abundant protein in animal tissues, are a valuable commodity as biomaterials, and are actively involved in biomechanical and biological processes, such as dissipating deformation stress of tissues1,2,3, inducing cell polarity during cell–matrix adhesion4, and directing bone mineralization5,6,7. Collagens have an unusual amino acid composition: rich in glycine (~30%) and proline (~15%)8, and thus do not follow globular protein folding rules such as hydrophobicity driven core formation, or presentation of a hydrophilic surface to avoid aggregation9. Collagens do not form common secondary structure units like α-helices or β-strands; instead they fold into triple-helices (Fig. 1a), where three polypeptide chains are tethered by a network of main-chain hydrogen bonds, not a hydrophobic core10,11. Subsequent to folding, thousands to millions of triple-helices undergo self-assembly to form crystalline supramolecular fibers, providing a foundation for the extracellular matrix9. Although collagens are among the most widely applied biomaterials (e.g., cosmetics, foods, sutures in surgery, and cell-culture substrates in tissue culture), their atypical structural features have hindered understanding of their folding and assembly mechanisms.
Type I collagen exists physiologically as a distinct supramolecular structure of banded fibers with a pattern of alternating dark and light bands that are unmistakable when imaged by an electron microscope9,12. This banding originates from an offset, parallel packing of triple-helices13,14,15,16 (Fig. 1b). The dark band is referred to as the gap region, caused by a void between consecutive triple-helices12. The light band is the overlap region between neighboring triple-helices. Natural Type I collagen forms robust banded fibers. It is sourced from animal tissues such as bovine skin or rat tails and is the major type of collagen used in biomedical research and industry17. However, animal-sourced Type I collagen suffers from drawbacks such as variable quality and purity, and the risk of prion contamination17,18. Synthetic collagens produced under controlled laboratory conditions could address these issues. However, it remains challenging to recapitulate the supramolecular assembly—and thus the banding pattern—of natural collagens19,20,21,22.
Here, we describe a class of synthetic banded fiber collagens, elucidate a detailed mechanism for banded fiber formation, and use these designed materials to experimentally probe the role of banding in promoting osteoblastic differentiation. Individual collagen polypeptide chains are constructed from two components: an adhesive module that promotes supramolecular assembly of folded triple-helices into a banded fiber, and a functional-driver module that can be altered to tailor the material behavior. By varying the lengths and sequences of the two modules, we can precisely specify the widths of the gap and overlap bands. The assembly mechanism is established using both atomistic models and coarse-grained simulations. This class of synthetic collagens advances our physical understanding of collagen supramolecular assembly from the nanometer to micron scale and provides a testbed for studying collagen biology and developing functional biomaterials.
Results
Modular design and fiber production
Adhesive modules were constructed from tripeptide repeats designed for electrostatic or hydrophobic inter-helical interactions (Fig. 1c). Hydrophobic adhesive modules were formed from tandem repeats of a motif: (Pro-Pro-Gly)n sequence, abbreviated as Pn. The electrostatic attachment was promoted using a basic domain composed of (Pro-Arg-Gly)n triplets and an acidic domain composed of (Glu-Pro-Gly)n triplets on either end of the functional driver, respectively abbreviated Rn and En. In the case of electrostatic adhesive modules, the total length was maintained at 15 residues with the remainder of the module composed of Pro-Pro-Gly triplets (Fig. 1c).
The functional-driver module is not responsible for assembly, and by design should be a largely unconstrained repeated Xaa-Yaa-Gly triplet sequence that can be tailored for specific applications. We explored the plasticity of the functional-driver sequence using fragments of Streptococcus pyogenes Scl2, a collagen-like bacterial protein with a triplet insertion23. Three fragments, referred to as A–C, were chosen for their similar lengths but different amino acid compositions and net charges24,25,26. Functional-driver modules constructed from combinations of fragments with varied compositions and lengths were inserted between two adhesive modules (Fig. 1c). Our nomenclature for the synthetic collagens is based on the arrangement of modules: for example, we use “R5BE5” for a variable domain constructed from the Scl2 B fragment flanked by electrostatic attachment modules and use “P10BBP10” for two tandem Scl2 B fragments flanked by ten Pro-Pro-Gly triplets. Complete sequences of all constructs are in Supplementary Table 1.
The folding and assembly protocol for the designed synthetic collagens parallels many aspects of natural collagen assembly. Type I collagen is expressed in the cell in a procollagen form, where the triple-helix is flanked by globular domains that assist in folding; these are subsequently cleaved prior to supramolecular assembly of banded fibers27. Bacterial Scl2 also has a globular domain (V-domain) that facilitates folding and expression24. We included the V-domain prior to the first adhesive module, separated by a trypsin cleavage site (Supplementary Table 1). Synthetic collagens folded into triple-helices within Escherichia coli cells. After expression and purification, the synthetic collagen was digested with trypsin to remove the V-domain28 and incubated at 4 °C for several days, allowing for supramolecular assembly into banded fibers. Details of protein production and validation are described in the “Methods” section and Supporting Information (Supplementary Figs. 1–3).
Controlling fiber morphology
According to the design scheme, the number of amino acids in the adhesive module should specify the length of the overlap region, and the functional-driver module size should determine the length of the gap. The first design studied—P10BP10—formed fibers with periodic light and dark bands, as observed in negative staining electron microscopy images (Fig. 1f). Assembly of banded fibers was robust, and reproducible multiple times under a variety of solution conditions including 50–150 mM NaCl concentrations, pH 3–11, incubation times from 0.5 to 70 days, and temperatures from 4 to 37 °C (Supplementary Figs. 4–6). Although P10BP10 assembles into fibers, micro-rheology experiments show fibers do not form a viscoelastic gel either at a low (1 mg mL−1) or high (5 mg mL−1) concentration (Supplementary Fig. 7).
In a triple-helix, each residue spans 0.29 nm along the super-helical axis, allowing one to estimate the size of a domain based on the length of its sequence. Band widths were ~10 nm (light) and 24.9 nm (dark), matching the expected sizes of the P10 (30 residues) and B (81 residues) sequences, respectively (Fig. 3c). Surface contour maps of P10BP10 banded fibers imaged by atomic force microscopy (AFM) showed the lighter bands were ~1 nm high, matching the diameter of a triple-helix (Fig. 1g, Supplementary Fig. 8). Combined, TEM and AFM support the design approach where the light bands (the overlap region) in P10BP10 are formed by adhesive modules, and the dark bands (the gap region) are formed by the functional-driver modules.
To investigate the three-dimensional morphology of synthetic collagen fibers, we generated P10BP10 and P10BBP10 fibers under the same conditions used for TEM and imaged the samples using a Talos Arctica cryo-electron microscope. Tomograms of P10BP10 fibers showed that collagen fibers form 3D bundles that are 500 – 800 nm in length and taper at the ends. These bundles exhibited a distinct 3D structure and periodic light and dark bands (Fig. 2a-c, Supplementary Mov. 1). Measurements of light bands (23.6 nm) and dark bands (9.5 nm) were consistent with dimensions of gap and overlap bandwidths respectively, but of opposite intensity as compared to TEM. Using Fourier transforms, we calculated the average periodicity to be 32.4 nm (Fig. 2d), consistent with measurements in real space (33.2 nm, Fig. 2b) and in AFM (32.7 nm, Supplementary Fig. 8). To examine the domain organization, we performed volume rendering of the P10BP10 fiber tomograms using UCSF Chimera and observed that collagen fibers within the bundles show a pattern of dense overlap zones and sparse gap zones (Fig. 2e, Supplementary Mov. 1). This observation further supports that the overlap region (dense zone) is formed by tightly stacked adhesive modules and that the gap region (sparse zone) is formed by loosely stacked functional-driver modules. Tomograms of P10BBP10 fibers revealed similar 3D fiber bundles and a characteristic periodic light and dark banding pattern with a 55.6 nm periodicity, consistent with observations in TEM (Supplementary Fig. 23, Supplementary Mov. 2). The light band widths of P10BBP10 were twice of that of P10BP10 fibers. The banded fibers formed by this class of synthetic collagens were also three-dimensional.
We tested our design approach by preventing supramolecular banded fiber assembly by several strategies: denaturing the triple-helix structure or altering the order of modules. The P10BP10 triple-helix unfolds with a transition temperature (Tm) of 52 °C (measured by CD—Supplementary Fig. 9j–l), and 55.2 °C measured by differential scanning calorimetry (DSC) (Supplementary Fig. 10c). Heating P10BP10 above the Tm prior to assembly prevented banded fiber formation (Supplementary Fig. 11). Synthetic collagens with alternate module topologies—i.e. containing one adhesive module before, in the middle of, or after the functional-driver B module (P10B, ½BP10½B and BP10)—folded into triple-helices (Supplementary Fig. 9a–c), but did not assemble into banded fibers. Thus, a folded triple-helix and a topology of two adhesive modules flanking a functional-driver are prerequisites for synthetic collagens that form banded fibers.
We show that one can independently target the properties of dark and light bands by varying the functional-driver and adhesive modules, respectively. The Scl2 B fragment was incorporated into PnBPn and R5BE5 designs, producing banded fibers where the dark band consisted of a width of around 24 nm, matching the calculated length of an 81-residue triple-helix. In our design, the composition of the functional-driver module is relatively unconstrained as long as it folds into a triple-helical structure. To test this, we used Scl2 fragments A and C as functional-driver modules that are of similar size to B, but their amino acid compositions are unique, with A having very few charges, and C rich in charged residues. All three designs, P10AP10, P10BP10, and P10CP10 readily assembled into fibers, with similar bandwidths (Fig. 3a–c, e, h and Supplementary Figs. 12, 13). Thus, the functional-driver module sequence can be modified without noticeably perturbing banded fiber morphology.
It should be possible to increase the width of the dark band by lengthening the functional driver. P10BBP10 and P10ABCP10 folded into triple-helices (Supplementary Fig. 9j–l, 10) and assembled into banded fibers. The dark bandwidths of P10BBP10 and P10ABCP10 were twice and three times that of P10BP10, while the light bandwidths were unchanged (Fig. 3e–h and Supplementary Fig. 13). Indeed, the 59 nm dark bandwidth of P10BBP10 is similar that of the Type I collagen 67 nm D-period9,12, showing one can engineer banded fibers with biologically relevant dimensions.
Molecular mechanism of adhesion
We explored two strategies of triple-helix adhesion based on modules composed of amino acids that make hydrophobic or electrostatic interactions. Briefly, we anticipated that the strengths of these interactions would scale with the size of the interface. To assess the size and energetic requirements for hydrophobically-driven assembly, we constructed a series of synthetic collagens of the form PnBPn, of varying lengths n = 5, 8, 10, and 12. All designs folded into triple-helices as measured by CD, with Tm values higher than the parent Scl2 domain28 (Supplementary Fig. 9d–f). Aggregation, but not banding, was observed for the P5 adhesive module in P5BP5 and P5BBP5 (Supplementary Fig. 14). When n ≥ 8, all PnBPn designs formed banded fibers (Fig. 3j–l and Supplementary Fig. 15), where the light bandwidth was directly proportional to n, confirming that the light band is formed by the adhesive modules.
Eight repeats of a Pro-Pro-Gly triplet were sufficient to promote assembly, suggesting an interaction threshold for adhesion-dependent on the size of the interface. To quantify this potential requirement, we computed interactions between pairs of triple-helical adhesive modules using the protCAD software platform29; note that protCAD was developed for structure-guided protein engineering, and enables sampling of intramolecular torsional rotations as well as intermolecular degrees of freedom. Interaction energies were scored using the AMBER ff14sb molecular mechanics force field30. Interhelical packing was optimized by sampling rigid body translational and rotational parameters31. In the optimized conformation, an extensive packing interface was generated between triple-helical ridges formed by the proline sidechains (Fig. 4a). As the module length, n, increased from 5 to 12 triplets, the calculated interaction energy score increased linearly from −30 to −70 kcal mol−1 (Fig. 4d and Supplementary Table 2). Based on these calculations, the interaction threshold for supramolecular assembly would lie somewhere between −30 and −50 kcal mol−1.
Electrostatic adhesion-driven assembly was also investigated. R5BE5 folded into triple-helices and assembled into banded fibers. The light band had a mean width of 5.8 nm, matching the expected dimensions of a 15-residue sequence. The dark bandwidths were consistent with that of Scl2 fragment B, unaltered by switching from hydrophobic to electrostatic adhesive domains (Fig. 3i–l and Supplementary Fig. 15). Designs with shorter electrostatic adhesive modules—R3BE3 and R1BE1—did not assemble into banded fibers. This further supports the plausibility of an energetic interaction threshold for the electrostatic-driven supramolecular assembly.
We again used protCAD to compute the interaction energy scores, this time with atomic models of electrostatic adhesive modules. In addition to inter-helical degrees of freedom, we also sampled sidechain rotameric states of the Arg and Glu amino acids. Electrostatic modules tended to associate at larger inter-helical distances than hydrophobic ones (Fig. 4a, b), likely accommodating the larger Arg and Glu sidechains at the interface. Decreased contributions from van der Waals packing forces due to greater inter-helical separations were compensated by electrostatic interactions. In the R5 + E5 calculations, Arg and Glu sidechains interdigitated, forming multiple strong (~3.3 Å) interhelical salt bridges (Fig. 4b–c). The interaction score was proportional to the number of charged residues in each adhesive module. Given that R3BE3 and R1BE1 did not form banded fibers, an interaction threshold for assembly between −30 and −50 kcal mol−1 apparently exists for electrostatically driven adhesion. This is the same range as for hydrophobic interactions, suggesting a common interaction threshold for supramolecular assembly across all designs.
It was thought that the functional-driver sequences derived from Scl2 might coincidentally contain regions that promote interhelical associations through hydrophobic or electrostatic interactions, which could confound our proposed mechanism for assembly. As atomistic calculations are impractical for evaluating all possible supramolecular interactions at this scale, we applied a discrete, primary sequence-based approach used previously to model natural collagen interactions20,32. Briefly, two sequences are aligned in a series of poses by shifting one amino acid at a time (Supplementary Fig. 16a). Interaction scores are calculated based on the number of hydrophobic and electrostatic contacts, allowing us to rank the different poses. As expected, when this calculation was applied to Type I collagen, the highest interaction scores occur at staggers every 231–236 residues (Supplementary Fig. 17), consistent with the length of D-spacing9,12. For synthetic collagens P10BP10, P10BBP10, and P10ABCP10, top-scoring poses comprised fully overlapping adhesive domains (Supplementary Fig. 16b, c). Therefore, interactions between the proline-rich adhesive modules, rather than incidental interactions between functional-driver modules, likely drive assembly.
Simulating supramolecular assembly
The multiscale structural features of natural collagens, from the atomic to the macroscopic, all contribute to biological activity27,33. When assembled in vitro—as would be done in tissue culture for example—animal collagens will form long banded fibers that are thicker in the middle and tapered at the ends34. This is consistent with an assembly pathway known as diffusion-limited aggregation (DLA)35, where individual triple-helices attach to a growing fiber at any point along its length (Supplementary Fig. 18). Micrographs of our synthetic collagens showed this anticipated morphology, indicating DLA as the likely operating mechanism of supramolecular assembly. It would be useful to predict supramolecular features on the micron scale for synthetic collagen assemblies composed of thousands or more triple-helices. As atomistic methods are computationally expensive at such scales, we used a minimalistic coarse-grained Monte Carlo DLA model, developed previously with Type I collagen35 and synthetic peptides36, to predict supramolecular features on the ten to hundred-micron scale.
DLA simulations were performed using coarse-grained models of synthetic collagens, where individual triple-helices were approximated as rigid rods composed of adhesive and functional driver modules (Fig. 4e, f). DLA simulations produced banded fibers consistent with the ones observed through TEM and cryoET: these were thicker in the middle and tapered at the ends. As expected, the coarse-grained models showed that the gap region dark bands formed by functional-driver modules had a lower packing density than the overlap regions (light bands) formed by the adhesive domains (Supplementary Fig. 19). These spaces would allow a negative TEM stain to infiltrate the gap regions and produce a darker color. Conversely, overlapping attachment domains had a higher density in DLA models, consistent with light bands resisting stain.
Models from DLA simulations were also compared to observed fiber thicknesses and lengths. Simulated fibers were generated for P10BP10 containing 50–3000 individual triple-helices (Supplementary Fig. 20). Simulated dimensions best-matched observations for fibers composed of ~1200 rods (Fig. 4g). The length and thickness of the simulated fibers increased with the number of rods (Supplementary Fig. 20). However, the aspect ratio (length/thickness) decreased only slightly, still close to the values extracted from TEM (Supplementary Fig. 21), consistent with previous diffusion models of collagen37. Simulated dimensions best-matched observations for fibers composed of ~1200 rods (Fig. 4g). These observations held for the longer P10BBP10 constructs. Only for the longest synthetic collagen, P10ABCP10, did the simulations significantly diverge from observations. This may be due to a number of factors, including potential deviations from a rigid rod approximation for long designs that would increase the anisotropy of diffusion38. It would be useful to explore alternate models of collagen that incorporate triple-helical flexibility39. These findings, including the edge case with P10ABCP10, demonstrate how coarse-grained modeling tools enhance our physical understanding of the collagen assembly process. In establishing DLA as the pathway from triple-helices to banded fibers, we can computationally sample module configurations, prior to studying them in the laboratory, showcasing the utility of synthetic collagens as a testbed for developing designer biomaterials.
Banded fibers support osteoblastic differentiation
Type I collagen is the primary extracellular matrix protein in bone, and its assembly into a banded fiber is known to be essential for osteogenesis and matrix mineralization5,6,40. We, therefore, tested whether the cell culture of osteoblast precursor MC3T3-E1 cells on synthetic collagens that form banded fibers would significantly promote cell adhesion and differentiation over related, non-banded protein substrates. Cell behaviors on synthetic banded fiber collagen substrates (P10BP10 and P10BBP10) were compared to related fiber-incompetent substrates (B and P5BP5). Type I collagen and bovine serum albumin (BSA) were included as positive and negative controls, respectively. Our results ultimately showed that cultured osteoblasts preferentially thrived and differentiated on synthetic banded collagen substrates.
Osteoblast viabilities and proliferation rates for all substrates were comparable (Fig. 5a), confirming that our synthetic collagens are biocompatible. Synthetic collagen banded fiber and Type I collagen substrates promoted higher cell adhesion than the banding-incompetent substrates and BSA control (Fig. 5b). Natural collagen could promote the formation of focal adhesion sites and recruitment of cytoplasmic actin-binding proteins (e.g., vinculin and α-actinin)41,42. We measured VCL and ACTN mRNA levels, and found that the presence of the banded fiber substrates promoted the transcription of both genes (Fig. 5c). Cytoskeletal phenotypes in response to cell adhesion were evident when we assayed cell spreading area and performed cytoskeletal staining with phalloidin (Fig. 5d, e). The cells which were adhered to the banded fiber substrates had larger spreading areas with more obvious cytoskeleton extension, and had prominent cell dendrites, indicating accelerated maturation of such cells (Fig. 5d, e).
The banded fiber substrates also promoted MC3T3-E1 cell differentiation into mature osteoblasts. Alkaline phosphatase (ALP) is an extracellular bone enzyme that increases the local concentration of inorganic phosphate and facilitates mineralization43, and is a typical biomarker of osteoblastic differentiation and incipient mineralization. ALP-stained areas for P10BP10 and P10BBP10 were comparable to that of Type I collagen and significantly larger than for the B, P5BP5, or BSA sample groups (Fig. 5f, g). The expression of RUNX2, an osteoblastic-specific transcription factor44, was induced by the synthetic banded fiber collagens P10BP10 at levels higher than that of the banding-incompetent substrate, BSA control, and even natural Type I collagen (Fig. 5h).
The similar outcomes of cells on P10BP10 and P10BBP10 suggest that common features of these two designs and that of Type I collagen stimulate differentiation. We hypothesize that the banding of the synthetic collagen fibers aligns the engineered integrin binding sites (GFPGER) in the fragment B45 (see sequences in Supplementary Table 1), resulting in clustering of cell receptors, promoting and downstream signaling (Supplementary Fig. 24)46.
Synthetic collagens that form banded fibers enhanced cell compatibility of MC3T3-E1 osteoblast precursor cells, and promoted the expression of osteoblastic differentiation markers ALP and RUNX2 in these cells, consistent with observations that the supramolecular structure of natural collagens is actively involved in osteogenesis and bone mineralization5,6,40. Previous studies have reported that collagen from animal models with osteogenesis-relevant diseases (e.g., osteogenesis imperfecta (OI) and osteopenia) display aberrant Type I collagen banding47,48,49. Reported issues from the industry regarding the purity and quality of animal-extracted collagens also limit both the precision of data and the confidence in results from experiments addressing the pathogenic impacts of aberrant collagen structures. In addition, by engineering disease-causing mutations into collagen modules designed based on hypotheses from clinical or biological insights, synthetic collagens can be further used to investigate the molecular mechanisms of cell–matrix interactions in osteogenesis, as well as pathogenesis-related mechanisms in great detail.
Discussion
We designed, modeled, and tested an innovative class of synthetic collagens comprising an adhesive module to promote supramolecular assembly into classic collagen banded fibers, and a functional-driver module that can be precisely tailored to obtain desired material behaviors. The robust expression and assembly of these banded fibers for a range of materials with different combinations of modules can provide pure, safe, and functionally designable collagen biomaterials. Our demonstration that P10BP10 and P10BBP10 could promote the differentiation of MC3T3-E1 osteoblast precursor cells at levels comparable to natural collagen confirms that these banded fibers are valuable as biomedical research tools and as a testbed for designer functional biomaterials. Although the designed collagens did not form hydrogels, they still can be potentially used as coating materials on metal implants50. It may be possible to design functional drivers that promote the formation of a supramolecular viscoelastic gel.
Computational models that accurately recapitulate the supramolecular assembly process for these fibrous proteins represent a major conceptual advance to better define the rules governing the supramolecular assembly of natural collagen. Specifically, we have established energetic interaction thresholds between adhesive modules and have set up a coarse-grained DLA model to help understand how protein length and composition dictate the morphology of assembled fibers. Notably, we show that extended proline-rich sequences can be used to modulate the strength of intra-fiber adhesion, and changing the lengths of adhesive and functional-driver modules can vary the period of fiber banding at biologically relevant scales.
Functionally designable synthetic collagens with tunable banding morphologies provide an unprecedented tool for exploring collagen–collagen and collagen–cell interactions in biology and disease. To date, investigations of collagen diseases such as OI have largely depended on animal models, where the specific role of collagen cannot be studied in isolation47,48,49, or on collagen peptides and fragments33, which do not recapitulate the supramolecular nature of natural collagen fibers. These designs provide a supramolecular platform for hosting OI mutations of interest, enabling characterization of their precise impacts in disrupting collagen fiber assembly and during osteogenesis. Our synthetic banded fibers provide a flexible platform that fills the gap between simplified biophysical models of collagen-like peptides and complex in vivo systems of model animals and can foster discoveries about collagen-involved biological and pathological processes.
Methods
Plasmid construction, protein expression, and purification
Synthetic genes of the designed collagens (Supplementary Table 1), which contained a 5’ (NcoI) and 5’UTR ([GC]) and 3’ (BamHI), were optimized for the E. coli expression system. For each designed collagen, its gene was cloned into the pColdIII-Tu vector through NcoI and BamHI. The pColdIII-Tu vector was obtained from pColdIII site-directed mutation of the NdeI to NcoI by primer S1 (CTCGAGGGATCCGAATTCA) and A1 (GAGCTCCATGGGCACTTTG). All verified constructs were transformed into E. coli BL21 (DE3) (Supplementary Fig. 1). The primary seed culture (1 mL) was used to inoculate 100 mL of TB medium containing 100 µg mL−1 ampicillin at 37 °C cultured for 24 h. The bacteria liquid was cooled to 25 °C and induced with 1 mM IPTG. After 10 h incubation, cells were further cooled to 15 °C for 14 h51. Cells were harvested by centrifugation at 4 °C. The cell pellets were resuspended in binding buffer (20 mM NaPO4, 500 mM NaCl, 10 mM imidazole, pH 7.4), lysed with sonication, centrifugated at 10,000×g for 20 min at 4 °C and filtered with the microporous membrane (0.45 μm) to remove the cell debris. The designed collagen with a His6 tag at N-terminus was purified with 5 mL HisTrap HP column using the stepwise increasing concentrations of imidazole (130, 160, and 400 mM). The globular folding domain, V-domain, of the designed collagen was removed by incubating with trypsin at 1:1000 (w:w) ratio at 25 °C overnight, which was dialyzed and freeze-dried. As the trypsin is autolyzed into fragments within several hours52, the fragments were eliminated from the protein solutions with the dialysis. The molecular weights and purity (>95%) of the designed collagens were validated by SDS–PAGE and MALDI-TOF mass spectrometry (Supplementary Figs. 2 and 3).
Circular dichroism (CD) spectroscopy
CD Spectra were obtained via an applied photophysics chirascan with a Peltier temperature controller, using quartz cuvettes with 1 mm path length (Model 110-OS, Hellma USA). Protein solutions (1 mg mL−1 in 10 mM PB buffer) were equilibrated at 4 °C for ~24 h before measurements. Wavelength scans were collected at 4 °C from 190 to 260 nm (step 1 nm, averaging time 5 s). For temperature transition experiments from 4 to 80 °C, the ellipticity was monitored at 220 nm at an average heating rate of 1 °C for 6 min−1 with 8 s equilibration time. The first derivative of the melting curves was used to obtain the melting temperatures of collagen samples.
Differential scanning calorimetry (DSC)
DSC was carried out for the collagen proteins in a NANO DSC instrument (TA Instruments) coupled with a thermal data analysis system, Nano-Analyze software. The collagen solution was at 5 mg/mL in 10 mM phosphate buffer at pH 7 and incubated at 4 °C for 3 days before measurements. The 10 mM phosphate buffer was used for the baseline scan at least three times. Sample solutions were loaded at 20 °C into the cell and heated at a rate of 1 °C/min.
MALDI-TOF mass spectrometry
MALDI-TOF was used to confirm the molecular mass of the designed collagen (Bruker Daltonics UltrafleXtreme, USA). 1 μL of 1 mg mL−1 sample was dropped in a 600 μm AnchorChip target plate (Bruker) and allowed to dry, using 5 mg mL−1 2,5-dihydroxyacetophenone, 25% (v/v) ethanol, 1.5 mg mL−1 diammonium hydrogen citrate as the matrix in linear mode, BSA was used for external calibration. Or using 10 mg mL−1 sinapinic acid in 50% acetonitrile, 0.1% TFA as the matrix. 1 μL of the sample was applied onto a plate with apo-myoglobin as the internal standard. Data was acquired with AB Sciex 4800 at positive linear mid-mass mode.
Transmission electron microscopy (TEM)
Solutions of the designed collagens at 0.5 mM in 10 mM phosphate buffer (pH 7.0) were incubated at 4 °C for 3 days. The solution was placed onto a copper grid and was incubated for 45 s, after which the excess solvent was absorbed from the grid using filter paper. The sample was negatively stained with 0.75% phosphotungstic acid for 20 s, and the excess stain was absorbed away and imaged with Hitachi H-7650 (Hitachi, Japan) Electron Microscope. The light- and dark-band widths were measured with ImageJ about 200 times from at least 5 TEM images.
Atomic force microscope (AFM)
Tapping mode was performed on a Cypher ES AFM (Asylum Research, Oxford Instruments) at room temperature. AC240 silicon nitride cantilevers sourced from Oxford Instruments were used for imaging in the air. These cantilevers have a nominal spring constant of kc = 2.0 N m−1, and radii of r = 7 nm. Sample solutions were deposited onto freshly cleaved mica, allowed 5 min for binding, and then washed with 2 mL of water. Samples were then allowed to air dry for 1 h in a laminar flow cabinet before being placed in the AFM for imaging and analyzed using Asylum Research software. Before the Fourier transform was used to analyze the banded fibers in AFM images, EMD denoising protocol was used to remove the baseline drift and noise53. The data processing was carried out with Matlab_R2016a with a source code, which was uploaded to GitHub (https://github.com/JinyuanHu/FFT_AFM.git)
Microrheology
Solutions of the designed collagens and Type I collagen at 1 and 5 mg mL−1 in 10 mM phosphate buffer (pH 7.0) were incubated at 4 °C for 3 days. Then Young’s moduli, G’ and G”, were determined as previously described54. Fluorescent polystyrene beads were added to the solution and record the trajectories of the fluorescent beads were by fluorescence microscopy, then determine the mean square displacement as a function of time and Young’s moduli, G’ and G”, were determined from the Generalized Stokes–Einstein relationship.
Calculation of inter-triple helical interactions
The interaction energy scores of the designed collagen were computed according to Hulmes et al. using a sequence-based model32. Charged pair (K/R, D/E) and hydrophobic pair (V, M, I, L, F, P) were given a score of one. Repulsion pairs were given a score of negative ones. All other pairs were scored zero. The segment length for computed is ±3 for charge interactions, and ±2 for hydrophobic interactions (Supplementary Fig. 16). The interaction score was computed at every one residue shift when the above chain shifts laterally from the N- to C-terminus of the neighboring chain. In order to mimic the natural arrangement of Type I collagen, 0.6 D gap (156 amino acids) was set when the interaction scores were calculated (Supplementary Fig. 17). For the PnXPn collagen, (PPG)10 was overlapped to match the full overlap of (PPG)10 in self-assembly process (Supplementary Fig. 16).
Computational modeling of association of attachment modules
The structural model of Pn was obtained by shortening or elongating a high-resolution (1.3 Å) crystal structure of (PPG)10 (PDB: 1K6F)55. Pn was aligned along the principal z-axis by minimizing the projection on the x–y plane. The relative positions of the other off-centered triple helices in Pn + Pn were described with five geometric parameters, Ω, θ, φ, r, and Δh31 (Supplementary Fig. 22). Ω was a tilting angle between two triple helices. φ was the self-rotation angle of the off-centered triple helices, which rotated around the centered one with the angle θ. r and Δh were the distances along x- and z-axis, respectively. When Ω = 0°or 180°, association energies of Pn + Pn were optimized with a Monte Carlo Simulated Annealing (MCSA) program with 16,000 steps from 40 to 0.001 °C. During the optimization, all atoms within the same triple helices were kept fixed in order to keep the intra-helical energies constant. The van der Waals energy between the two triple helices was calculated using a 12-6 Lenard–Jones potential with a distance cutoff 6.0 Å. The AMBER ff14SB force field parameters were used for nonbonding interactions30.
Rn + En association was modeled with a similar protocol used for Pn. Atomic models were generated by mutating (PPG)10 with protCAD. Parallel and antiparallel associations (Ω = 0°, 180°) were sampled. Together with the five geometric parameters, the side chain rotamers of Arg and Glu were optimized with MCSA.
Simulation of collagen self-assembly
A coarse-grained model of self-assembly simulating the process of diffusion-limited aggregation (DLA) was established with a modified Java script previously reported36. The simulation flowchart was presented in Supplementary Fig. 18. A triple helical fragment, [(PPG)10]3, was simplified as a sphere with 1 nm diameter. In P10BP10, the adhesive module P10 was simplified as 10 spheres. As the helical rise of a triplet with low Pro content is about 0.8–0.9 nm20, the 27-triplet functional-driver module of P10BP10 was modeled as 25 spheres. The spheres formed a rigid rod. A seed rod was placed initially at the center and additional rods were placed at the periphery to randomly diffuse along a 3D hexagonal lattice until contacting an existing rod. Considering viscous resistance, the probability of diffusing axially or radially was adjusted:
where f is viscous resistance; \(\eta\), viscosity of the fluid; S, cross-sectional area in the direction of movement; \(\frac{{{\rm {d}}v}}{{{\rm {d}}t}}\), fluid velocity gradient.
The probability of a movement P along axial (Pz) and radial (Pxy) is inversely proportional to the resistance.
In this simulation, it can be assumed that \(\frac{{{\rm {d}}v}}{{{\rm {d}}t}}\) and \(\eta\) have the same values in the axial and lateral movements. Collagen can be considered as a cylinder with length L and diameter D.
DLA models of fiber assembly were generated by repeating, 100 times, the simulation of seven sets of rods (50, 100, 300, 600, 1000, 1500, and 3000 rods), where each rod represented the P10BP10, P10BBP10, or P10ABCP10 construct. Fiber length and width were taken to be the weighted average of the total set of simulations per rod type.
Cell proliferation assay
A 96-well culture plate (3599, Corning, USA) was pre-coated by 10 μg cm−2 collagens, including B, P5BP5, P10BP10, P10BBP10 and Type I collagen (C7661, SIGMA, USA), at 4 °C overnight. Then the sample solution was removed and the plate was dried in the air for 12 h. After 2 h ultraviolet sterilization, the plate was blocked by 5% BSA (A600332-0100, Sangon Biotech, China) for 2 h. Then 2000 MC-3T3 cells were seeded into the wells and Cell Counting Kit-8 (BA00208, BIOSS, China) was used to detect the cell proliferation according to the manufacturer’s instructions. At days 0, 1, 3, and 5, 10 μl Cell Counting Kit-8 solution was added into each well and the absorbance at 450 nm was measured through SYNER GY H1 (BioTek, USA). The culture medium contains 90% α-MEM medium (SH30265.01, Hyclone, USA), 10% fetal bovine serum (FND500, ExCell, China), and 1% Penicillin–Streptomycin (KGY0023, KeyGEN, China). The culture medium was renewed every two days.
Cell adhesion assay
A 96-well culture plate was coated with the same samples as the cell proliferation assay. The 104 MC-3T3 cells were seeded into each well for 6 h. The culture medium was removed and the plate was washed with PBS gently 3 times. A new culture medium was supplemented and 10 μL Cell Counting Kit-8 solution (BA00208, BIOSS, China) was added to each well. The absorbance at 450 nm was measured through SYNER GY H1 (BioTek, USA). The adhesion percentage was calculated by dividing the number of adherent cells by the seeding cells.
Quantitative polymerase chain reaction assay (qPCR)
A 96-well culture plate was coated with the same samples as the cell proliferation assay. After cell seeding for 6 h, the adhesion-related gene expression of MC-3T3 cells was detected with qPCR. MC-3T3 cells were also cultured in the plate under osteoblastic differentiation induction for 7 days, and then osteoblastic gene expression was detected with qPCR. Total RNA was isolated from cells using TRIzol Reagent (15596-018, Invitrogen, USA) and cDNA synthesis was conducted using the Transcriptor First Strand cDNA Synthesis Kit (Roche, Switzerland) according to the manufacturer’s instruction. The qPCR experiments were performed with an SYBR Premix Ex Taq II kit (Takara, Japan). The gene expression levels were normalized to the Gapdh expression level. The sequence of the primers used is listed in Supplementary Table 3.
Cytoskeleton staining
A 24-well culture plate was coated with the same samples as those in the cell proliferation assay. About 4000 MC-3T3 cells were cultured in each well for 6 h. Then, the plate was washed through PBS 3 times and the cells were fixed by 4% PFA for 30 min. After incubation in 0.3% Triton X-100 (ST797, Beyotime, China) for 15 min, cells were stained with FITC-Phalloidin (KD0382, Kingmorn, China) for 30 min. Finally, cell nuclei were counterstained with DAPI (D9542, Sigma, USA) for 10 min. The images were taken using a fluorescence microscope. The area occupied by cells was determined by Image J56.
Alkaline phosphatase staining
A 24-well culture plate was coated with the same sample as those in the cell proliferation assay. MC-3T3 cells were cultured in a plate under osteoblastic differentiation induction for 7 days. The plate was washed with PBS 3 times, and 4% PFA was used to fix cells for 30 min. Then the Alkaline phosphatase (ALP) staining was performed using the ALP Staining Kit (P0321M, Beyotime, China) according to the manufacturer’s instructions. The cells were incubated with ALP staining solution at 37 °C for 1 h. The images were taken using a light microscope and the ALP staining area was determined by Image J.
Tomography data collection and analysis
EM grids for cryoET structural studies were prepared using a self-assembled collagen solution. P10BP10 and P10BBP10 samples were mixed with 6 nm nanogold particles to facilitate tilt series alignment during image processing. An aliquot of 3.5 μl of collagen fibers was then applied onto glow-discharged Quantifoil holey grids (R2/2, Cu, 200 mesh; Quantifoil) before plunge frozen using a Leica EM GP plunger (Leica Microsystems, Buffalo Grove, IL, USA) in a humidity (95%) and temperature (20 °C) controlled chamber. Images and tilt series of the samples were collected on a Talos Arctica cryo-electron microscope (Thermo Fisher Scientific, Waltham, MA, USA) operated at 200 kV, equipped with a post-column BioQuantum energy filter (the slit was set to 20 eV) and a K2 direct electron detector. Automated data collection was performed using SerialEM57. Tomographic data was acquired using a dose-symmetric tilt scheme with 3° intervals and ×31,000 microscope magnification with a corresponding pixel size of 4.36 Å/pixel. Data collection was performed in counting mode, with spot size 9, 100 μm condenser, and 70 μm objective apertures. Tilt series of both P10BP10 and P10BBP10 were collected at a defocus range of −8 to −11 μm with a cumulative dose of ~160 e−/Å2. The latest EMAN2 tomography workflow was used for all tilt series alignment and tomogram reconstruction58.
Quantitative measurements (bandwidths, periodicity, etc.) were performed using functionalities in EMAN2. Volume rendering and visualization of tomograms were done using UCSF Chimera59. Measurements of periodicity in real space involved calculating the length of the fiber along multiple periodicities, divided by the total number of periods. To evaluate whether measurements of periodicity in real space v. Fourier space were statistically different, we performed a two-sample t-test with equal variance.
Statistics and reproducibility
All numerical data are expressed as the mean ± s.d. The significance of differences among groups for cell culture were assessed using ordinary one-way ANOVA with multiple comparisons test using Prism 8.2.1 (**** P < 0.0001, ** P < 0.01, * P < 0.05). P < 0.05 was considered statistically significant. Experiments were repeated at least three times independently with similar results in all agarose gel electrophoresis, SDS-PAGE, TEM, Cryo-ET, and AFM experiments. The statistical analyses were performed with OriginPro 2019b software for the TEM at n = 200, and for the DLA models at n = 100.
Data availability
Electron density maps of P10BP10 and P10BBP10 synthetic collagen fibers have been deposited in the Electron Microscopy Data Bank under the accession codes EMD-27664 and EMD-27665, respectively. Scripts and code are available at https://github.com/JinyuanHu. The data that support the findings of this study are available from the corresponding author.
Code availability
The protCAD modeling platform used in this study is available at https://github.com/JinyuanHu/protcad/releases. The code for AFM data processing is available under https://github.com/JinyuanHu/FFT_AFM/releases. The code for DLA simulation is available at https://github.com/JinyuanHu/dla/releases.
References
Sasaki, N. & Odajima, S. Stress–strain curve and young’s modulus of a collagen molecule as determined by the X-ray diffraction technique. J. Biomech. 29, 655–658 (1996).
Buehler, M. J. Nature designs tough collagen: explaining the nanostructure of collagen fibrils. Proc. Natl Acad. Sci. USA 103, 12285–12290 (2006).
Shen, Z. L., Dodge, M. R., Kahn, H., Ballarini, R. & Eppell, S. J. Stress–Strain experiments on individual collagen fibrils. Biophys. J. 95, 3956–3963 (2008).
Lee, M. & Vasioukhin, V. Cell polarity and cancer-cell and tissue polarity as a non-canonical tumor suppressor. J. Cell Sci. 121, 1141–1150 (2008).
Landis, W. J. et al. Mineralization of collagen may occur on fibril surfaces: evidence from conventional and high-voltage electron microscopy and three-dimensional imaging. J. Struct. Biol. 117, 24–35 (1996).
Landis, W. J., Hodgens, K. J., Arena, J., Song, M. J. & McEwen, B. F. Structural relations between collagen and mineral in bone as determined by high voltage electron microscopic tomography. Microsc. Res. Tech. 33, 192–202 (1996).
Xu, Y. et al. Intermolecular channels direct crystal orientation in mineralized collagen. Nat. Commun. 11, 5068 (2020).
Rigby, B. J. Amino-acid composition and thermal stability of the skin collagen of the antarctic ice-fish. Nature 219, 166–167 (1968).
Nelson, D. L., Lehninger, A. L. & Cox, M. M. Lehninger Principles of Biochemistry (Macmillan, 2008).
Ramachandran, G. & Kartha, G. Structure of collagen. Nature 176, 593 (1955).
Bella, J., Eaton, M., Brodsky, B. & Berman, H. M. Crystal and molecular structure of a collagen-like peptide at 1.9 Å resolution. Science 266, 75–81 (1994).
Piez, K. A. & Miller, A. The structure of collagen fibrils. J. Supramol. Struct. 2, 121–137 (1974).
Hulmes, D. J. S. & Miller, A. Quasi-hexagonal molecular packing in collagen fibrils. Nature 282, 878 (1979).
Miller, A. & Wray, J. S. Molecular packing in collagen. Nature 230, 437–439 (1971).
Orgel, J. P., Irving, T. C., Miller, A. & Wess, T. J. Microfibrillar structure of type I collagen in situ. Proc. Natl Acad. Sci. USA 103, 9001–9005 (2006).
Vuorio, E. & De Crombrugghe, B. The family of collagen genes. Annu. Rev. Biochem. 59, 837–872 (2003).
Chi, H. L., Singla, A. & Lee, Y. Biomedical applications of collagen. Int. J. Pharm. 221, 1–22 (2001).
Brodsky, B. & Kaplan, D. L. Shining light on collagen: expressing collagen in plants. Tissue Eng. Part A 19, 1499–1501 (2013).
Rele, S. et al. d-periodic collagen-mimetic microfibers. J. Am. Chem. Soc. 129, 14780–14787 (2007).
Kaur, P. J. et al. The self-assembly of a mini-fibril with axial periodicity from a designed collagen-mimetic triple helix. J. Biol. Chem. 290, 9251–9261 (2015).
O’leary, L. E., Fallas, J. A., Bakota, E. L., Kang, M. K. & Hartgerink, J. D. Multi-hierarchical self-assembly of a collagen mimetic peptide from triple helix to nanofibre and hydrogel. Nat. Chem. 3, 821 (2011).
Tanrikulu, I. C., Forticaux, A., Jin, S. & Raines, R. T. Peptide tessellation yields micrometre-scale collagen triple helices. Nat. Chem. 8, 1008 (2016).
Seo, N. et al. An Engineered α1 Integrin-binding Collagenous Sequence. J. Biol. Chem. 285, 31046–31054 (2010).
Xu, Y., Keene, D. R., Bujnicki, J. M., Hook, M. & Lukomski, S. Streptococcal Scl1 and Scl2 proteins form collagen-like triple helices. J. Biol. Chem. 277, 27312–27318 (2002).
Yu, Z., An, B., Ramshaw, J. A. M. & Brodsky, B. Bacterial collagen-like proteins that form triple-helical structures. J. Struct. Biol. 186, 451–461 (2014).
Yu, Z., Brodsky, B. & Inouye, M. Dissecting a bacterial collagen domain from Streptococcus pyogenes: sequence and length-dependent variations in triple helix stability and folding. J. Biol. Chem. 286, 18960–18968 (2011).
Prockop, D. J., Kivirikko, K. I., Tuderman, L. & Guzman, N. A. The biosynthesis of collagen and its disorders. N. Engl. J. Med. 301, 77–85 (1979).
Yoshizumi, A. et al. Self-association of Streptococcus pyogenes collagen-like constructs into higher order structures. Protein Sci. 18, 1241–1251 (2009).
Summa, C. M., Rosenblatt, M. M., Hong, J.-K., Lear, J. D. & DeGrado, W. F. Computational de novo design, and characterization of an A2B2 diiron protein. J. Mol. Biol. 321, 923–938 (2002).
Pang, Y. P. FF12MC: a revised AMBER forcefield and new protein simulation protocol. Proteins Struct. Funct. Bioinforma. 84, 1490–1516 (2016).
Xu, F. et al. Self-assembly of left- and right-handed molecular screws. J. Am. Chem. Soc. 135, 18762–18765 (2013).
Hulmes, D. J. S., Miller, A., Parry, D. A. D., Piez, K. A. & Woodhead-Galloway, J. Analysis of the primary structure of collagen for the origins of molecular packing. J. Mol. Biol. 79, 137–148 (1973).
Brodsky, B. & Baum, J. Structural biology: modelling collagen diseases. Nature 453, 998 (2008).
Holmes, D. F., Chapman, J. A., Prockop, D. J. & Kadler, K. E. Growing tips of type I collagen fibrils formed in vitro are near-paraboloidal in shape, implying a reciprocal relationship between accretion and diameter. Proc. Natl Acad. Sci. USA 89, 9855–9859 (1992).
Parkinson, J., Kadler, K. E. & Brass, A. Simple physical model of collagen fibrillogenesis based on diffusion limited aggregation. J. Mol. Biol. 247, 823–831 (1995).
McGuinness, K., Khan, I. J. & Nanda, V. Morphological diversity and polymorphism of self-assembling collagen peptides controlled by length of hydrophobic domains. ACS Nano 8, 12514–12523 (2014).
Fry, D., Mohammad, A., Chakrabarti, A. & Sorensen, C. M. Cluster shape anisotropy in irreversibly aggregating particulate systems. Langmuir ACS J. Surf. Colloids 20, 7871 (2004).
Rezaei, N., Lyons, A. & Forde, N. R. Environmentally controlled curvature of single collagen proteins. Biophys. J. 115, 1457–1469 (2018).
Hafner, A. E., Gyori, N. G., Bench, C. A., Davis, L. K. & Šarić, A. Modeling fibrillogenesis of collagen-mimetic molecules. Biophys. J. 119, 1791–1799 (2020).
Xu, Y. et al. Intermolecular channels direct crystal orientation in mineralized collagen. Nat. Commun. 11, 1–12 (2020).
Xiao, P., Nelson, E. S., Maiers, J. L. & Demali, K. A. New insights into vinculin function and regulation. Int. Rev. Cell Mol. Biol. 287, 191 (2011).
Sjöblom, B., Salmazo, A. & Djinović-Carugo, K. α-Actinin structure and regulation. Cell. Mol. Life Sci. 65, 2688 (2008).
Stein, G. S., Lian, J. B. & Owen, T. A. Relationship of cell growth to the regulation of tissue-specific gene expression during osteoblast differentiation. FASEB J. Off. Publ. Fed. Am. Soc. Exp. Biol. 4, 3111 (1990).
Ghaemi, S. R., Delalat, B., Cetó, X., Harding, F. J. & Voelcker, N. H. Synergistic influence of Collagen I and BMP 2 drives osteogenic differentiation of mesenchymal stem cells: a cell microarray analysis. Acta Biomater. 34, 41–52 (2016).
Emsley, J., Knight, C. G., Farndale, R. W., Barnes, M. J. & Liddington, R. C. Structural basis of collagen recognition by integrin alpha2beta1. Cell 101, 47–56 (2000).
Jokinen, J. et al. Integrin-mediated cell adhesion to Type I collagen fibrils. J. Biol. Chem. 279, 31956–31963 (2004).
Wallace, J. M., Orr, B. G., Marini, J. C. & Holl, M. M. B. Nanoscale morphology of Type I collagen is altered in the Brtl mouse model of Osteogenesis Imperfecta. J. Struct. Biol. 173, 146–152 (2011).
Wallace, J. M., Erickson, B., Les, C. M., Orr, B. G. & Holl, M. M. B. Distribution of type I collagen morphologies in bone: relation to estrogen depletion. Bone 46, 1349–1354 (2010).
Li, T. et al. Studies of chain substitution caused sub-fibril level differences in stiffness and ultrastructure of wildtype and oim/oim collagen fibers using multifrequency-AFM and molecular modeling. Biomaterials 107, 15–22 (2016).
Rammelt, S. et al. Coating of titanium implants with collagen, RGD peptide and chondroitin sulfate. Biomaterials 27, 5561–5571 (2006).
Peng, Y. Y. et al. Towards scalable production of a collagen-like protein from Streptococcus pyogenes for biomedical applications. Microb. Cell Fact. 11, 146 (2012).
Vestling, M. M., Murphy, C. M. & Fenselau, C. Recognition of trypsin autolysis products by high-performance liquid chromatography and mass spectrometry. Anal. Chem. 62, 2391–2394 (1990).
Huang, N. E. et al. The empirical mode decomposition and the Hilbert spectrum for nonlinear and non-stationary time series analysis. Proc. Math. Phys. Eng. Sci. 454, 903–995 (1998).
Hu, J. et al. Design strategies to tune the structural and mechanical properties of synthetic collagen hydrogels. Biomacromolecules 22, 3440–3450 (2021).
Berisio, R., Vitagliano, L., Mazzarella, L. & Zagari, A. Crystal structure of the collagen triple helix model [(Pro-Pro-Gly)(10)](3). Protein Sci 11, 262–270 (2002).
Kim, H., Sengupta, A., Glogauer, M. & McCulloch, C. A. Filamin A regulates cell spreading and survival via beta1 integrins. Exp. cell Res. 314, 834–846 (2008).
Mastronarde, D. N. Automated electron microscope tomography using robust prediction of specimen movements. J. Struct. Biol. 152, 36–51 (2005).
Chen, M. et al. A complete data processing workflow for cryo-ET and subtomogram averaging. Nat. Methods 16, 1161–1168 (2019).
Pettersen, E. F. et al. UCSF Chimera—a visualization system for exploratory research and analysis. J. Comput. Chem. 25, 1605–1612 (2004).
Ricard-Blum, S. The collagen family. Cold Spring Harb. Perspect. Biol. 3, a004978 (2011).
Bella, J. A new method for describing the helical conformation of collagen: dependence of the triple helical twist on amino acid sequence. J. Struct. Biol. 170, 377–391 (2010).
Acknowledgements
We wish to thank the core imaging facilities at the School of Biotechnology, Jiangnan University, and Robert Wood Johnson Medical School, Rutgers University for help obtaining TEM images. This work was supported by the National Key R&D Program of China (No. 2018YFA0901600) and the National Natural Science Foundation of China (No. 22078129) to FX, National Institute of Health of US (No. R35- GM136431) to JB, NASA NAI 80NSSC18M0093 (VN), and National Natural Science Foundation of China (No. 82270963, No. 82061130222) and Foundation of SCST (No. 20XD1424000, 201409006400) to YS.
Author information
Authors and Affiliations
Contributions
F. X., J. H., and V. N. designed experiments, synthesized materials, performed experiments, analyzed data and wrote the manuscript. J. L. and Y. S. collected and analyzed the cell culture data and wrote the manuscript. J. J. and W. D. collected and analyzed the cryoET data and wrote the manuscript. L. W. collected the TEM data. K. M. took part in DLA simulation and discussions. J. R., and J. B. collected and analyzed the AFM data. F. X. and V. N. supervised the research and wrote the manuscript. All authors discussed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
Patent US20210079064A1—“Preparation of Type I Collagen-Like Fiber and Method for Regulating and Controlling the D-periodic of Fiber Thereof” Fei Xu, Jinyuan Hu, Vikas Nanda, David I. Shreiber, Meng Zhang, Sonal Gahlawat.
Peer review
Peer review information
Nature Communications thanks Biplab Sarkar and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hu, J., Li, J., Jiang, J. et al. Design of synthetic collagens that assemble into supramolecular banded fibers as a functional biomaterial testbed. Nat Commun 13, 6761 (2022). https://doi.org/10.1038/s41467-022-34127-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-022-34127-6
- Springer Nature Limited