Abstract
Polyolefins with branches produced by ethylene alone via chain walking are highly desired in industry. Selective branch formation from uncontrolled chain walking is a long-standing challenge to generate exclusively branched polyolefins, however. Here we report such desirable microstructures in ethylene polymerization by using sterically constrained α-diimine nickel(II)/palladium(II) catalysts at 30 °C–90 °C that fall into industrial conditions. Branched polyethylenes with exclusive branch pattern of methyl branches (99%) and notably selective branch distribution of 1,4-Me2 unit (86%) can be generated. The ultrahigh degree of branching (>200 Me/1000 C) enables the well-defined product to mimic ethylene-propylene copolymers. More interestingly, branch distribution is predictable and computable by using a simple statistical model of p(1-p)n (p: the probability of branch formation). Mechanistic insights into the branch formation including branch pattern and branch distribution by an in-depth density functional theory (DFT) calculation are elucidated.
Similar content being viewed by others
Introduction
As the most important polymer by scale, polyolefins like polyethylene (PE) possess various architectures to form versatile products1,2,3. Branching is of great importance in these PEs to tune microstructures and thus determine material properties4,5,6,7,8,9. Via a traditional pathway, an exclusive branch in the PEs generally comes from a specific α-olefin, which is utilized as the comonomer in ethylene copolymerization. For instance, in the ethylene/propylene (EP) copolymer, linear low-density polyethylene (LLDPE), and polyolefin elastomer (POE) products, branch on the backbone of PEs is originated from C3, C4, C6, or C8 α-olefins. By comparison, the generation of branch from ethylene as the sole feedstock in the polymerization catalysis is highly attractive with regard to a simplified industrial process and the avoidable use of high-cost α-olefins10,11.
Since Brookhart’s seminal works in 199512,13,14 on α-diimine late transition metal such as nickel(II) and palladium(II) promoted olefin polymerization15,16,17,18,19,20,21, a unique chain walking mechanism that involves a successive β-H elimination followed by a re-insertion event with an opposite regiochemistry has emerged as a powerful tool to generate branches from ethylene alone, allowing for the production of a variety of polyethylene topologies4,22,23. For instance, the architecture of polyethylene could readily be adjusted by a simple variation of ethylene pressure4,24,25,26. Over the past more than two decades, however, precise control on branches to produce well-defined polymer microstructures is a long-standing challenge, because of the uncontrolled chain walking process. A mixture of branch patterns including methyl branch and higher branches (C2, C3, C4, and C4+) predominantly occur (Fig. 1). Therefore, selective branch formation is difficult in ethylene polymerization via a chain walking manner. This is particularly challenging when the reaction temperature is high or the degree of branching is very high, which easily induces the formation of a mixture of branch patterns. In view of the huge difficulty on controlling branch pattern, branch distribution (namely interval between two adjacent branches) on the backbone of PE is more elusive thus far. These events evidently inhibit the synthesis of ethylene-propylene copolymers from ethylene at industrial temperatures of 40–70 °C27.
We now report that the low-cost nickel(II) catalyst shows a superior control on selective branch formation in ethylene polymerization, enabling the production of an exclusive methyl branch pattern with an ultrahigh number in a particularly broad temperature range of 30–90 °C that meets the industrial process. Distribution of the formed branches in the obtained ethylene-propylene copolymers is highly selective based on a NMR analysis and is particularly predictable and computable based on a statistical model of probability. The underlying mechanism on the control of branch pattern and distribution is proposed and rationalized by an in-depth DFT calculation.
Results
Catalyst design and ethylene polymerization
As a rationale of catalyst design, the desired nickel precursor ipty-Ni was readily synthesized from the reaction of NiBr2(DME) with the rigid and sterically constrained α-diimine ligand28,29. The structure and purity of ipty-Ni was identified by multiple techniques including 1H NMR spectrum, elemental analysis, and X-ray diffraction analysis (Fig. 2; for detailed structural data, see Supplementary CIF file). As a comparison, ipty-Pd reported by us was also prepared (Fig. 2)28, which produced highly branched polyethylenes with unsolved microstructures at low temperatures of <30 °C as well. With the activator of modified methylaluminoxane (MMAO), ipty-Ni exhibited high activities for ethylene polymerization to produce high to ultrahigh molecular weight polyethylenes (Table 1). Notably, the degree of branching was very high, which rose with elevating temperature from 30 to 90 °C and further increased to reach an ultrahigh level of 200 brs/1000 C (calculated from 1H NMR data) with decreasing ethylene pressure from 8 bar to 2 bar30,31. Dependence of degree of branching on pressure and temperature is in agreement with previous results from a superficial analysis of 1H NMR spectroscopy32,33,34,35.
Exclusive branch pattern and selective branch distribution
To distinguish the branch pattern in these highly branched polyethylenes, instructive 13C NMR spectra were in depth analyzed to provide insightful information (Table 2). Generally, high reaction temperature leads to the generation of long-chain branches, making selective branch more difficult. In contrast, whatever pressure (2 bar–8 bar) or temperature (30–90 °C) varies in our nickel system, the smallest methyl branches are exclusively (99%) detected in all polyethylene samples of Table 1 (for all 13C NMR spectra, see Fig. 3). This is unprecedented that the branch pattern is unaltered and exclusive at such a high level of >200 brs/1000 C and at such high temperature of 90 °C. Importantly, the synthesis of ethylene-propylene copolymers from ethylene alone matches the industrial process of 40–70 °C27, thanks to the ability of this nickel catalyst on controlling chain walking. Based on pioneering insights4,12,13,14, high molecular weight of the obtained polyethylene implies the suppression of chain transfer that involves the replacement of the formed α-olefin by incoming ethylene. High degree of branching is attributed to high frequency of β-H elimination and subsequent re-insertion. Notably, the key exclusive formation of methyl branches means that 2,1-insertion of α-olefins predominates and no event occurs from 2,1-insertion of internal olefin that generates longer branches.
The exclusive methyl branches further allow for an in-depth analysis on branch distribution via 13C NMR spectra36,37,38,39. As depicted in Fig. 3 (205 Me/1000 C), extremely low signal intensities in the range of 10.0–18.0 ppm corroborate trace amounts of long-chain branches and 1,2-Me2 unit. By combining previously reported resonances with DEPT-135 and 2D NMR spectra, 1,4-Me2 unit, 1,6-Me2 unit, and 1,x-Me2 units (x = 8, 10, 12…) are unambiguously identified. Most notably, the content of both 1,4-Me2 unit and 1,6-Me2 unit can be calculated as 70.5% and 21.0%, respectively, according to the quantitative 13C NMR spectrum. However, beyond the resolution of NMR technique in the experimental scale, 1,x-Me2 units (x = 8, 10, 12…) are hardly distinguished due to the unidentified long (CH2)n units.
Proposed mechanism and computable branch distribution
To address this issue, we propose a mechanism for the formation of branch pattern and branch distribution (Fig. 4), which will be comprehensively discussed in the DFT calculation section (see below)40. Preliminarily, two distinct features should be noted: distribution of two neighboring methyl branches separated by an odd number of methylene (CH2) group is impossible, this means 1,3-Me2 unit, 1,5-Me2 unit, and 1,(x-1)-Me2 units (x = 8, 10, 12…) cannot be generated via a chain walking manner in ethylene polymerization; on the other hand, the formation of 1,2-Me2 unit and long-chain branches such as 1,(x-1)-Me/Et units (x = 4, 6, 8, 10, 12…) is proposed, despite trace amounts.
In terms of branch distribution, we envision a statistical model of probability. We set up a simple calculation (Table 3, and for details, see Supplementary Excel file for statistic model) that assumes on each step of the proposed scheme (Fig. 4) either formation of a branch occurs (with probability p) or chain growth occurs (with probability 1-p). That is the 1,4-Me2 unit structure is formed by a branch formation (probability: p), the 1,6-Me2 unit structure is formed by one growth step and a branch formation [probability: p(1-p)], and so on. Notably, this model that assumes the probability of branch formation vs. growth is independent of the distance from the previous branch. This calculated data based on the model agrees with experimental quantitative 13C NMR data quite well (see branch distribution in Table 3). For example, in the Supplementary Excel file we set with p = 70.5% of 1,4-Me2 unit (type into field B1 as 0.705), and then 20.8% of 1,6-Me2 unit (21.0% from NMR data), 6.1% of 1,8-Me2 unit, 1.8% of 1,10-Me2 unit, 0.5% of 1,12-Me2 unit and more units are automatically generated (also input the other p value in Supplementary Excel).
This advanced method solves the shortcoming of NMR technique and enables branch distribution predictable and computable, where the ratio of (1,4)-α, [(1,6)-α+(1,x)-α], (1,6)-β, (1,x)-β, (1,x)-γ, (1,x)-δ, CH, and Me signals in the statistical model set by us well fits in the calculated value from 13C NMR data in Fig. 3. As an extension, branch number (brs) is also easily calculated and predicted by setting an equation of I[Me branches]/I[all signals] (entry 7: 205/1000 C (13C NMR) vs 207/1000 C (Model)) (Supplementary Excel file).
These highly branched polyethylenes with exclusive methyl branches produced by the palladium precursor ipty-Pd were further analyzed with regard to branch distribution (Table 2, entries 8–10). At 0 °C, the selectivity of methyl branch pattern is 99%, and most notably the selectivity of 1,4-Me2 branch distribution reaches the highest value of 86%. As anticipated, distribution of these branches is also computable. Note that long-chain branches generate at elevated temperatures of >30 °C in palladium species, indicating a reduced control on chain walking relative to nickel species. To the best of our knowledge, in chain walking polymerization selective branch pattern of methyl group generally occurs in the α-olefin reaction via a 1,2-insertion and subsequent ω, 2-enchainment41,42,43,44; however, highly selective 1,4-Me2 branch distribution is thus far only generated in 1-butene or trans-2-butene reactions at low temperatures such as −40 °C45,46,47,48,49.
Focusing on the microstructure of these ethylene-propylene copolymers produced by ethylene polymerization, only 1,4-, 1,6-, 1,8-, and 1,(2n + 2)- (n = 1, 2, 3…) units with an even interval between two neighboring methyl branches are observed in chain walking polymerization with ethylene as the sole monomer. As a comparison, the microstructure of ethylene-propylene copolymer produced by copolymerization of ethylene and propylene is distinct (Fig. 3). 1,2-, 1,3-, 1,4-, 1,5-, 1,x- (x = 2, 3, 4…) units generated by H-H, H-T, T-T linkages and H-E-H, H-E-T, T-E-T linkages between ethylene and propylene 36.
Mechanistic insight into branch formation (nickel system)
For more detailed discussion, Cf. Supplementary Notes, and Figs. 1–10. All structures of transition states and intermediates can be found in Supplementary coordinates.XYZ file. The intriguing branching character stimulated us to study the related mechanism of ethylene polymerization by nickel species ipty-Ni through using DFT calculations (Fig. 5). At first, the reaction starts from the β-H elimination (BHE) based on a β-agostic species 1β-T to give a propylene-coordinated complex 1. This process, which overcomes a free energy barrier (TS1BHE) of 12.9 kcal mol-1, is endergonic by 9.5 kcal mol−1. This unstable 1 goes through a slightly lower TS12reins with an energy barrier of 12.0 kcal mol−1 to complete propylene re-insertion with a 2,1-manner, generating a new β-agostic intermediate 2. By comparison, 2 is the more both kinetically and themodynamically favorable than 1β-T. Therefore, a new ethylene coordination separating β-agostic-H based on 2 is considered, and is found to be feasible via an energy barrier of 12.7 kcal mol−1, leading to 3. Finally, an ethylene insertion into the Ni−isopropyl bond of 3 occurs via a TS34ins with an energy barrier of 10.0 kcal mol−1 to generate a methyl-branching 4, accompanied with an energy release of 15.1 kcal mol−1.
Starting from 4, two possible pathways, viz., the direct ethylene coordination−insertion (4 → TS45coor→5 → TS56ins → 6) and the BHE−2,1-reinsertion (4 → TS5BHE → 5BHE-C → TS56reins → 6reins), were calculated. The former pathway has a total energy barrier of 14.2 (ΔG1‡, −3.4−(−17.6), TS45coor) kcal mol−1 and is exergonic by 11.4 (−29.0−(−17.6)) kcal mol−1. By contrast, a higher energy barrier of 18.1 (ΔG2‡, 0.5−(−17.6), TS56reins) kcal mol−1 and an endergonic character (5.0 = −12.6−(−17.6), 6reins) in the latter case suggest that 1,2-Me2 unit (6reins) is inaccessible in both kinetics and thermodynamics, which is in line with the experimental observation. Subsequent ethylene insertion into 6reins (6reins → TS'67coor → 7’ → TS'78ins → 8’) has a higher energy barrier of 21.9 (ΔG3‡, 4.3−(−17.6), TS'67coor) kcal mol−1, further confirming that the reverse reaction of 1,2-Me2 unit formation more easily occurs.
To further theoretically access the origin of selectivity on exclusive methyl branches, that is why 1,4-Me2 unit can be produced but longer-chain branch units such as 1,3-Me/Et unit are unavailable, we also investigated further ethylene insertion and BHE based on 6. As indicated in Fig. 5, the direct ethylene coordination-insertion overcomes a total energy barrier of 13.1 (ΔG4‡, −15.9−(−29.0), TS67coor) kcal mol−1 and releases an energy of 12.4 (−41.4−(−29.0)) kcal mol−1, yielding a precursor (8) of 1,x-Me2 units (x = 2n + 4, n = 1, 2, 3…). To obtain 1,4-Me2 unit and 1,3-Me/Et unit, a BHE and 2,1-reinsertion from 6 was calculated. Notably, locating 5-methyl-1-hexene-coordinated intermediate 7BHE-C is fruitless, and just one transition state TS78reins with an energy barrier of 13.9 (ΔG5‡, −15.1−(−29.0)) kcal mol-1 is obtained between 6 and 8reins (1,4-Me2 unit, observed in the experiment) (Detailed discussion for the not located 7BHE-C in Supplementary Figs. 5 and 6). Then, 8reins (−29.7 kcal mol−1, the β-agostic H from CH3 of methyl branches) isomerizes to a more stable 8reins-iso (−33.3 kcal mol−1, the β-agostic H from CH2 of backbone, also 1,4-Me2 unit). It is noteworthy that the generations of 1,6-Me2 unit precursor (ΔG4‡ = 13.1 kcal mol−1) and 1,4-Me2 unit (ΔG5‡ = 13.9 kcal mol−1) indicate the similar energy barriers, suggesting that they both can be obtained. This shows a good agreement with experimental results.
Furthermore, in following BHE and reinsertion from 8reins-iso to 9reins (1,3-Me/Et unit), we cannot also locate 5-methyl-2-hexene (MH)-coordinated intermediate 8BHE-C and just obtain one transition state TS8BHE (Supplementary Figs. 7 and 8). Unlike 1,4-Me2 unit, the formation of 1,3-Me/Et unit needs going through a higher TS8BHE with an energy barrier of 24.3 (ΔG8‡, −9.0−(−33.3)) kcal mol-1 and is an apparently unfavorable process, which is consistent with experimental findings.
Beyond those, the possibilities of further polymerization based on 8reins and 8reins-iso were also considered. It was found that the ethylene coordination-insertion (8reins → TS89coor → 9 → TS910ins → 10) into 8reins owns an energy barrier of 10.3 (ΔG6‡, −19.4−(−29.7)) kcal mol−1 and is exergonic by 14.5 ((−44.2−(−29.7))) kcal mol−1, while the process (8reins-iso → TS'89coor → 9’ → TS'910ins → 10’) involving 8reins-iso overcomes a higher energy barrier of 24.2 (ΔG7‡, −9.1−(−33.3)) kcal mol−1 and is a less exergonic process (−7.9 = −41.2−(−33.3) kcal mol−1) (Detailed discussion for TS910ins and TS'910ins in Supplementary Fig. 9). Therefore, the subsequent insertion on the basis of 8reins is smooth. Aforementioned findings allow us to conclude that the unique ancillary ligand forms a suitable channel for an exclusive formation of small methyl branches and a precise distribution of 1,2n + 4-Me2 units (n = 0, 1, 2, 3…) in highly branched polyethylenes.
Mechanistic insight into branch formation (difference of nickel and palladium system)
The entire discussion and the related Supplementary Notes and Fig. 3 and 10 can be found in Supplementary Information. Herein, we only focus on the difference of the origin of selectivity based on the same unique ligand. Inaccessible 1,2-Me2 unit (distribution): (Ni) the unfavorable kinetics (+3.9 kcal mol−1) and thermodynamics (+5.0 kcal mol−1) and high barrier (21.9 kcal mol−1) of subsequent ethylene insertion; (Pd) the favorable kinetics (−5.8 kcal mol−1) but both unfavorable thermodynamics (+2.3 kcal mol−1) and high barrier (17.8 kcal mol−1) of subsequent ethylene insertion. Inaccessible 1,3-Me/Et unit (longer branches): (Ni) the extremely unfavorable kinetics (+14.0 kcal mol−1); (Pd) the slightly unfavorable kinetics (+2.2 kcal mol−1), indicating an impossibility at low temperature but a possibility at higher temperature. Available 1,4-Me2 unit: (Ni) comparable barrier of isomerization (chain walking) with the precursor of 1,6-Me2 unit (13.9 vs 13.1 kcal mol−1) but lower barrier (10.3 kcal mol−1) of subsequent ethylene insertion to form 1,4-Me2 unit (10); (Pd) easy isomerization (chain walking) (7.3 kcal mol−1) and comparable barrier (15.0 vs 15.5 kcal mol−1) of subsequent ethylene insertion to form 1,4-Me2 unit (10).
Discussion
In summary, we have demonstrated that challenging selective branch formation in ethylene polymerization via a chain walking manner is now achieved by a sterically constrained nickel catalyst at broad reaction temperatures (also by the corresponding palladium analog at low temperatures). This overcomes the general propensity of complex microstructures produced by uncontrollably successive β-H elimination and opposite re-insertion events. Thus, an exclusive pattern of ultrahigh methyl branches is accessible, along with a highly selective branch distribution of 1,4-Me2 unit. Notably, branch distribution is unprecedentedly predictable and can be easily calculated by a simple statistical model of probability. The obtained polymers with methyl branches generated by ethylene alone mimic the commercial ethylene-propylene copolymers but possess tailored microstructures. Mechanistic insights by an in-depth DFT calculation on the selective branch pattern and distribution fully unravel the difference of nickel and palladium system. This work provides creative perspectives for chain walking polymerization and beyond, particularly shows how to generate, control, analyze, and predict branch in polymer synthesis. This work also for the first time demonstrates the precise synthesis of ethylene-propylene copolymer from ethylene alone at industrial temperatures.
Methods
Methods and detailed experiments are provided in Supplementary Information.
Data availability
The authors declare that all data supporting the findings of this study are available in the text or the Supplementary Materials. (1) Supplementary Information: 1) General synthesis and polymerization procedures, characterization and analysis data (NMR, DSC, XRD, and GPC) for ligand, nickel complex, and polymers. 2) DFT calculated details. Detailed mechanistic insights into nickel and palladium system. (2) Supplementary XYZ file for DFT calculation: The optimized Cartesian coordinates of all stationary points together with their single-point energy (a.u.) in solution. (3) Supplementary CIF file for ipty-Ni catalyst: The X-ray crystallographic data for ipty-Ni has been deposited at the Cambridge Crystallographic Data Center (CCDC) under the deposition number 1974098. These data can be obtained free of charge via www.ccdc.cam.ac.uk/data_request/cif. (4) Supplementary Excel file for statistic model: An Excel file including the statistic model for the calculation of branch degree, branch pattern, and branch distribution.
References
Hustad, P. D. Frontiers in olefin polymerization: reinventing the world’s most common synthetic polymers. Science 325, 704–707 (2009).
Baier, M. C., Zuideveld, M. A. & Mecking, S. Post-metallocenes in the industrial production of polyolefins. Angew. Chem. Int. Ed. 53, 9722–9744 (2014).
Stürzel, M., Mihan, S. & Mülhaupt, R. From multisite polymerization catalysis to sustainable materials and all-polyolefin composites. Chem. Rev. 116, 1398–1433 (2016).
Guan, Z., Cotts, P. M., McCord, E. F. & McLain, S. J. Chain walking: a new strategy to control polymer topology. Science 283, 2059–2062 (1999).
Zhong, S. et al. Precision synthesis of ethylene and polar monomer copolymers by palladium-catalyzed living coordination copolymerization. Macromolecules 50, 5661–5669 (2017).
Padilla-Vélez, O., O’Connor, K. S., LaPointe, A. M., MacMillan, S. N. & Coates, G. W. Switchable living nickel(ii) α-diimine catalyst for ethylene polymerisation. Chem. Commun. 55, 7607–7610 (2019).
Basbug Alhan, H. E., Jones, G. R. & Harth, E. Branching regulation in olefin polymerization via lewis acid triggered isomerization of monomers. Angew. Chem. Int. Ed. 59, 4743–4749 (2020).
Jones, G. R., Basbug Alhan, H. E., Karas, L. J., Wu, J. I. & Harth, E. Switching the reactivity of palladium diimines with “ancillary” ligand to select between olefin polymerization, branching regulation, or olefin isomerization. Angew. Chem. Int. Ed. 60, 1635–1640 (2021).
Zhang, Y. & Jian, Z. Polar additive triggered branching switch and block polyolefin topology in living ethylene polymerization. Macromolecules 54, 3191–3196 (2021).
Ittel, S. D., Johnson, L. K. & Brookhart, M. Late-metal catalysts for ethylene homo- and copolymerization. Chem. Rev. 100, 1169–1204 (2000).
Chen, Z. & Brookhart, M. Exploring ethylene/polar vinyl monomer copolymerizations using Ni and Pd α-diimine catalysts. Acc. Chem. Res. 51, 1831–1839 (2018).
Johnson, L. K., Killian, C. M. & Brookhart, M. New Pd(II)- and Ni(II)-based catalysts for polymerization of ethylene and.alpha.-olefins. J. Am. Chem. Soc. 117, 6414–6415 (1995).
Johnson, L. K., Mecking, S. & Brookhart, M. Copolymerization of ethylene and propylene with functionalized vinyl monomers by palladium(II) catalysts. J. Am. Chem. Soc. 118, 267–268 (1996).
Mecking, S., Johnson, L. K., Wang, L. & Brookhart, M. Mechanistic studies of the palladium-catalyzed copolymerization of ethylene and α-olefins with methyl acrylate. J. Am. Chem. Soc. 120, 888–899 (1998).
Boffa, L. S. & Novak, B. M. Copolymerization of polar monomers with olefins using transition-metal complexes. Chem. Rev. 100, 1479–1494 (2000).
Nakamura, A., Ito, S. & Nozaki, K. Coordination−insertion copolymerization of fundamental polar monomers. Chem. Rev. 109, 5215–5244 (2009).
Mu, H., Pan, L., Song, D. & Li, Y. Neutral nickel catalysts for olefin homo- and copolymerization: relationships between catalyst structures and catalytic properties. Chem. Rev. 115, 12091–12137 (2015).
Guo, L., Dai, S., Sui, X. & Chen, C. Palladium and nickel catalyzed chain walking olefin polymerization and copolymerization. ACS Catal. 6, 428–441 (2016).
Chen, C. Designing catalysts for olefin polymerization and copolymerization: beyond electronic and steric tuning. Nat. Rev. Chem. 2, 6–14 (2018).
Tan, C. & Chen, C. Emerging palladium and nickel catalysts for copolymerization of olefins with polar monomers. Angew. Chem. Int. Ed. 58, 7192–7200 (2019).
Mu, H., Zhou, G., Hu, X. & Jian, Z. Recent advances in nickel mediated copolymerization of olefin with polar monomers. Coord. Chem. Rev. 435, 213802 (2021).
Dockhorn, R. et al. Polyolefins formed by chain walking catalysis—a matter of branching density only? J. Am. Chem. Soc. 141, 15586–15596 (2019).
Zanchin, G. & Leone, G. Polyolefin thermoplastic elastomers from polymerization catalysis: advantages, pitfalls and future challenges. Prog. Polym. Sci. 113, 101342 (2021).
Dong, Z. & Ye, Z. Hyperbranched polyethylenes by chain walking polymerization: synthesis, properties, functionalization, and applications. Polym. Chem. 3, 286–301 (2012).
Xu, L. & Ye, Z. A Pd–diimine catalytic inimer for synthesis of polyethylenes of hyperbranched-on-hyperbranched and star architectures. Chem. Commun. 49, 8800–8802 (2013).
Guan, Z. Recent progress of catalytic polymerization for controlling polymer topology. Chem. Asian J. 5, 1058–1070 (2010).
Quadri, G. P., Pmicheletti, F. & Susa, A. Process for the production of EPDM elastomers in solution and polymerisation reactor for use in said process. Patent WO2014202715 A1 (2014).
Zhang, Y., Wang, C., Mecking, S. & Jian, Z. Ultrahigh branching of main-chain-functionalized polyethylenes by inverted insertion selectivity. Angew. Chem. Int. Ed. 59, 14296–14302 (2020).
Zhang, Y. & Jian, Z. Comprehensive picture of functionalized vinyl monomers in chain-walking polymerization. Macromolecules 53, 8858–8866 (2020).
Liu, F.-S. et al. Thermostable α-diimine nickel(II) catalyst for ethylene polymerization: effects of the substituted backbone structure on catalytic properties and branching structure of polyethylene. Macromolecules 42, 7789–7796 (2009).
Vignesh, A., Zhang, Q., Ma, Y., Liang, T. & Sun, W.-H. Attaining highly branched polyethylene elastomers by employing modified α-diiminonickel(II) catalysts: probing the effects of enhancing fluorine atom on the ligand framework towards mechanical properties of polyethylene. Polymer 187, 122089 (2020).
Svejda, S. A., Johnson, L. K. & Brookhart, M. Low-temperature spectroscopic observation of chain growth and migratory insertion barriers in (α-diimine)Ni(II) olefin polymerization catalysts. J. Am. Chem. Soc. 121, 10634–10635 (1999).
Leatherman, M. D., Svejda, S. A., Johnson, L. K. & Brookhart, M. Mechanistic studies of nickel(II) alkyl agostic cations and alkyl ethylene complexes: investigations of chain propagation and isomerization in (α-diimine)Ni(II)-catalyzed ethylene polymerization. J. Am. Chem. Soc. 125, 3068–3081 (2003).
Gates, D. P. et al. Synthesis of branched polyethylene using (α-diimine)nickel(II) catalysts: influence of temperature, ethylene pressure, and ligand structure on polymer properties. Macromolecules 33, 2320–2334 (2000).
Gottfried, A. C. & Brookhart, M. Living and block copolymerization of ethylene and α-olefins using palladium(II)−α-diimine catalysts. Macromolecules 36, 3085–3100 (2003).
Randall, J. C. Methylene sequence distributions and number average sequence lengths in ethylene-propylene copolymers. Macromolecules 11, 33–36 (1978).
McCord, E. F. et al. 13C and 2D NMR analysis of propylene polymers made with α-diimine late metal catalysts. Macromolecules 34, 362–371 (2001).
McCord, E. F. et al. 13C NMR analysis of α-olefin enchainment in poly(α-olefins) produced with nickel and palladium α-diimine catalysts. Macromolecules 40, 410–420 (2007).
Ruiz-Orta, C., Fernandez-Blazquez, J. P., Anderson-Wile, A. M., Coates, G. W. & Alamo, R. G. Isotactic polypropylene with (3,1) chain-walking defects: characterization, crystallization, and melting behaviors. Macromolecules 44, 3436–3451 (2011).
Escher, F. F. N., Mauler, R. S. & Souza, R. F. D. Control of branch formation in ethylene polymerization by a [Ni(η3-2-MeC3H4)(diimine)] PF6/DEAC catalyst system. J. Brazil. Chem. Soc. 12, 47–51 (2001).
Möhring, V. M. & Fink, G. Novel polymerization of α-olefins with the catalyst system nickel/aminobis(imino)phosphorane. Angew. Chem. Int. Ed. 24, 1001–1003 (1985).
Schubbe, R., Angermund, K., Fink, G. & Goddard, R. Struktur der aktiven Spezies und Erklärung des Wanderungsmechanismus bei der 2,ω-polymerisation von α-olefinen. Macromol. Chem. Phys. 196, 467–478 (1995).
Liu, F. et al. Poly(1-hexene) with long methylene sequences and controlled branches obtained by a thermostable α-diimine nickel catalyst with bulky camphyl backbone. J. Poly. Sci. Pol. Chem. 50, 3859–3866 (2012).
Hu, H. et al. Ligand-directed regioselectivity in amine–imine nickel-catalyzed 1-hexene polymerization. ACS Catal. 5, 122–128 (2015).
Leatherman, M. D. & Brookhart, M. Ni(II)-catalyzed polymerization of trans-2-butene. Macromolecules 34, 2748–2750 (2001).
Liu, W. & Brookhart, M. Mechanistic studies of palladium(II)-α-diimine-catalyzed polymerizations of cis- and trans-2-butenes. Organometallics 23, 6099–6107 (2004).
Cherian, A. E., Lobkovsky, E. B. & Coates, G. W. Chiral anilines: development of C2-symmetric, late-transition metal catalysts for isoselective 2-butene polymerization. Chem. Commun. 2003, 2566–2567 (2003).
Rose, J. M., Cherian, A. E. & Coates, G. W. Living polymerization of α-olefins with an α-diimine Ni(II) catalyst: formation of well-defined ethylene−propylene copolymers through controlled chain-walking. J. Am. Chem. Soc. 128, 4186–4187 (2006).
Vaccarello, D. N. et al. Synthesis of semicrystalline polyolefin materials: precision methyl branching via stereoretentive chain walking. J. Am. Chem. Soc. 140, 6208–6211 (2018).
Acknowledgements
We greatly appreciate Prof. Dr. Stefan Mecking from University of Konstanz for the discussion of branch formation and the statistical model of analyzing branch. We are also thankful for financial support from the National Natural Science Foundation of China (Nos. 22122110 and 21871250 for Z.J. and 22171038 for X.K.), the Jilin Provincial Science and Technology Department Program (No. 20200801009GH for Z.J.), and the Dalian Young Star of Science and Technology Project (No. 2019RQ88 for X.K.).
Author information
Authors and Affiliations
Contributions
Z.J. conceived the study and supervised this project. Y.Z. prepared all catalysts and performed polymerization experiments. X.K. performed DFT calculations and wrote the corresponding part in the manuscript. Z.J. wrote the manuscript. All authors have given approval to the final version of the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhang, Y., Kang, X. & Jian, Z. Selective branch formation in ethylene polymerization to access precise ethylene-propylene copolymers. Nat Commun 13, 725 (2022). https://doi.org/10.1038/s41467-022-28282-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-022-28282-z
- Springer Nature Limited
This article is cited by
-
Concerted Steric and Electronic Strategy in Thermostable Salicylaldiminato Nickel Catalysts for Ethylene (Co)polymerization
Chinese Journal of Polymer Science (2024)
-
A co-anchoring strategy for the synthesis of polar bimodal polyethylene
Nature Communications (2023)
-
Controllable Preparation of Branched Polyolefins with Various Microstructural Units via Chain-walking Ethylene and Pentene Polymerizations
Chinese Journal of Polymer Science (2023)