Abstract
Vast bulk recombination of photo-generated carriers and sluggish surface oxygen evolution reaction (OER) kinetics severely hinder the development of photoelectrochemical water splitting. Herein, through constructing a vertically ordered ZnInS nanosheet array with an interior gradient energy band as photoanode, the bulk recombination of photogenerated carriers decreases greatly. We use the atomic layer deposition technology to introduce Fe-In-S clusters into the surface of photoanode. First-principles calculations and comprehensive characterizations indicate that these clusters effectively lower the electrochemical reaction barrier on the photoanode surface and promote the surface OER reaction kinetics through precisely affecting the second and third steps (forming processes of O* and OOH*) of the four-electron reaction. As a result, the optimal photoanode exhibits the high performance with a significantly enhanced photocurrent of 5.35 mA cm−2 at 1.23 VRHE and onset potential of 0.09 VRHE. Present results demonstrate a robust platform for controllable surface modification, nanofabrication, and carrier transport.
Similar content being viewed by others
Introduction
Photoelectrochemical (PEC) water splitting can convert solar light into hydrogen energy, providing a promising path to solve the energy crisis and environmental pollution1,2. Zn–In–S-based ternary chalcogenide semiconductors have been widely applied as photocatalysts and PEC photoelectrodes owing to their efficient optical absorption in the visible-light region together with superior stability over binary chalcogenides3,4,5. Nevertheless, the serious recombination of photogenerated charge carriers and dull surface oxygen evolution reaction (OER) kinetics limit their application6. The bulk recombination of photoelectrodes can be alleviated by doping7,8, morphology9,10, and heterojunction engineering11,12,13. Among these strategies, constructing photoelectrodes with vertically ordered morphology is facile and effective14,15. However, there is usually a disordered layer between the substrate and ordered ZnIn2S4 (ZIS) nanostructures, which lowers the bulk separation efficiency (ηsep) of the photoanode16,17,18. As another major factor limiting the PEC performance, the OER involving four-electron reaction is dynamically slow on account of required two steps of O–H bond cleavage and O–O bond generation19,20,21. The complicated OER processes have a high reaction barrier, which are described by Eqs. (1)–(4)22. The symbol * marks the activation site of photoanode, and OH*, O*, and OOH* indicate the reaction intermediate groups:
Various cocatalysts (Ni/FeOOH23,24,25, CoOx26, and layered double hydroxide (LDH)27, etc.28,29,30) have been designed to enhance OER kinetics. These cocatalysts may lead to the decreased light-harvesting capability and increased charge recombination rate of photoanodes, owing to the thickness of cocatalyst layer and additional interface defects introduced between cocatalysts and photoanodes31. Alternatively, the in situ grown bonding-effect-based catalytic groups, such as oxysulfide photocatalyst32,33, Zn–O–Co–O–Zn configuration34, Ir–O–V groups35, and Fe–O–Ni bridge19, et al.36,37, can tackle the above problems. They can provide catalytic sites for water dissociation and adjust the adsorption energies of water molecules and intermediates35. This efficient strategy mostly acts on the entire bulky electrode in the water electrolysis. For the PEC, more attention should be paid to the OER reactions that take place on the photoanode surface38. It is still challenging to generate cocatalyst groups only on the photoanode surface without affecting the bulk to improve OER reaction kinetics.
To address the above critical issues, the atomic layer deposition (ALD) technique is used to introduce Fe and O atoms into two-dimensional Zn10In16S34 (ZISZ) ordered nanosheet arrays (denoted as ZISZ/Fe), where the Fe–In–S clusters are formed on the surface while the Zn–O bond is formed at bottom of the ZISZ photoanode. The Fe–In–S clusters greatly reduce the surface overpotential (η) and interfacial recombination, and thus boost the kinetics of OER through precisely affecting the forming processes of O* and OOH*. The change of element content and species along the cross-section of ZISZ causes the gradient energy level alignment within the photoanode, together with the uniformly ordered morphology without disordered layer, promoting the ηsep in the bulk. The ZISZ/Fe photoanode shows a largely increased photocurrent (J) of 5.35 mA cm−2 at 1.23 VRHE and onset potential (Von, the potential at which 0.02 mA cm−2 current density was first measured) of 0.08 VRHE, which is 32 and 6.3 times higher than that of ZIS and ZISZ. The performance is comparable to and even better than other up-to-date reported photoanodes-based sulfides (Supplementary Table 1).
Results and discussion
Preparation and characterization of photoanodes
Figure 1a displays the fabrication process of photoanodes with different morphology through controlling the solvent of precursors. The scanning electron microscopy (SEM) images of ZIS, ZISZ, and ZISZ/Fe nanosheet arrays are shown in Fig. 1b–g. They have the same morphology except that a lot of disordered small nanosheets are at the bottom of ZIS sample. The transmission electron microscopy (TEM) images (Supplementary Fig. 1) further reveal a typical nanosheet morphology. The vertically ordered two-dimensional nanosheets provide a direct transport path for photogenerated carriers, thereby reducing the bulk recombination of photoanode. The phase of the samples was determined by X-ray diffraction (XRD) pattern (Supplementary Fig. 2). ZIS reveals the typical hexagonal ZnIn2S4 (JCPDS: 72-0773)18. ZISZ exhibits a characteristic peak of Zn10In16S34 (JCPDS: 27-0989)39. When the ZISZ is treated by ALD, its peak position does not shift obviously. The corresponding high-resolution TEM (HRTEM, Supplementary Fig. 3) and selected area electron diffraction (SAED, inset in Supplementary Fig. 3) results show that all the samples have similar crystal structure, and the crystallinity of ZISZ and ZISZ/Fe is improved. The energy dispersive spectroscopy (EDS) elemental mapping of ZISZ/Fe in Supplementary Fig. 4a–f reveals that Zn, In, S, Fe, and O elements are uniformly distributed across the entire nanosheets.
The X-ray photoelectron spectroscopy (XPS) spectrum was conducted to characterize the surface chemical environment of elements (Fig. 2a–d). Zn, In, and S peak position of ZISZ change slightly compared with ZIS, indicating that they have similar chemical composition and state. Once the Fe and O elements are introduced by ALD treatment, the characteristic Fe peak appears (Fig. 2d). The Zn, In, and S peak position of ZISZ/Fe shifts obviously toward higher energy and the intensity is reduced greatly. This shift may be due to the formation of Fe–In–S clusters or the increased number of O elements with strong electronegativity, which will be discussed later. Supplementary Fig. 5 shows that the lattice O is not formed, and the peak intensity of O related with the surface-absorbed H2O (531.81 eV) and the OH group (529.86 eV) is enhanced because the O3 treatment increases the hydrophilicity of surface during the ALD process38. The reduced intensity of In results from the replacement of Fe to build Fe–In–S cluster. This is further confirmed by XPS of samples treated under different ALD cycles (Supplementary Fig. 6). With the increased cycles, the peak intensity of In gradually decreases while that of Fe increases. Furthermore, peaks located at 712.92 and 710.86 eV correspond to Fe3+ and Fe2+, respectively, indicating the chemical state of substituted Fe changes with increased Fe40. By performing DFT calculations using the models shown in Supplementary Fig. 7, we find that substitution of an In with an Fe requires smaller formation energy than replacement of a Zn with an Fe, which suggests that the former substitution is energetically favorable. The calculated Bader charge and magnetic moment on the Fe ion correspond to 1.687 and 2.662, indicating that the oxidation state and spin state of the Fe in the ZISZ/Fe system are +2 and 3. Furthermore, the replaced Fe atom is distant from the Zn atom and facilitates to form Fe–In–S bond between the Fe dopant and its surrounding In and S atoms.
a Zn 2p, b In 3d, c S 2p, and d Fe 2p XPS of ZIS, ZISZ, and ZISZ/Fe. e The Fe K-edge XANES spectra. f The Fe K-edge EXAFS as functions k2χ(k) and FT-EXAFS of ZISZ/Fe with different ALD cycles (40, 70, and 100 cycles); k = wave vector and χ(k) = oscillation as a function of the photoelectron wavenumber.
In order to reveal the state of Fe in the whole ZISZ/Fe, XPS at different depths through Ar ion etching was measured (Supplementary Fig. 8). As the etching depth increases, the peak intensity of Zn gradually increases and its peak position shifts toward higher energy (Supplementary Fig. 8a). The peak intensity of In also increases while the peak position shifts toward lower energy (Supplementary Fig. 8b). When the etching depth increases to 50 nm, the signal of Fe substantially disappears (Supplementary Fig. 8c), but the peak position of O shifts toward lower energy (Supplementary Fig. 8d). According to these data, we can get the following conclusions: (1) Fe is mainly deposited on the surface with a thickness of about 50 nm, which may be due to the limited diffusion rate of Fe in the ALD chamber. (2) The Zn peak shifts toward higher energy and O peak shifts toward lower energy is due to the formed Zn–O. The Zn–O bond is shorter than Zn–S bond, thus the binding energy of Zn–O is larger. (3) The opposite trend of the peak intensity of In and Fe also indicates the successful substitution. To further convince the construction of Fe–In–S clusters on the photoanode surface, X-ray absorption spectroscopy (XAS) was used to survey the Fe L3 absorption edges. As observed in Fig. 2e, the K-edge dotted lines located at around 7090 and 7190 eV represent the standard curves of FeO and Fe2O3, respectively. The peak region (7110–7170 eV) suggests that the photoanode contains different Fe content. Unlike Fe2O3 standard sample, there is no feature at the energy range between 7140 and 7165 eV of our prepared samples. The different characteristics of curves from standard FeO and Fe2O3 samples manifests that no oxides are formed. Furthermore, Fig. 2f shows the Fe K-edge extended X-ray absorption fine structure (EXAFS) as functions k2χ(k) and its Fourier-transformation (FT-EXAFS) (FT-κ2χ(κ)) for ZISZ/Fe prepared with different ALD cycles. The peaks at 2.1 and 3.5 Å are assigned to Fe–S bond and Fe–In bond, respectively, and the content of Fe–S bond increases with the increased deposition cycles. These characterizations indicate that the Fe–In–S clusters are successfully formed on the surface of photoanode.
PEC performance and characterizations for mechanism
Supplementary Fig. 9 displays the SEM images of ZISZ/Fe samples prepared with different ALD cycles. The surface morphology has no apparent difference owing to the slow growth rate (about 0.05 Å per cycle) of Fe during the ALD process. The photocurrent–voltage (J–V) curves of samples indicate the J increases first and then decreases, and the optimal performance appears in the 70th cycle (Supplementary Fig. 10). Compared to ZIS, the performance of ZISZ and ZISZ/Fe photoanodes is significantly improved (Fig. 3a), and the J reaches 0.84 and 5.35 mA cm−2 at 1.23 V vs. RHE, respectively. the Von is related to photovoltage and surface OER barriers, and the photovoltage can be determined by the open-circuit potential (OCP) measurement. The greater photovoltage and reduced surface OER barriers can cause the cathodic shift of Von in photoanode. The Von of ZISZ has a slightly positive shift compared with ZIS, as is also revealed by OCP (Supplementary Fig. 11), that ZISZ possesses the smallest value. Although the OCP of ZISZ/Fe is still smaller than ZIS, it possesses a cathodic Von, because the existence of Fe–In–S cluster reduces the surface electrochemical reaction barrier of ZISZ/Fe photoanode41,42. The applied bias photon-to-current efficiency (ηABPE) of photoanode demonstrates the evident performance improvement of ZISZ/Fe under different bias voltages (Supplementary Fig. 12). The capability of light harvesting gradually increases with the decreased bandgap for ZIS, ZISZ, and ZISZ/Fe (Fig. 3b). The incident photo-to-current efficiency (IPCE) and absorbed photon-to-current efficiency (APCE) show the increased IPCE and APCE value over the whole wavelength range (Supplementary Fig. 13), indicating the outstanding PEC performance of ZISZ/Fe. The IPCE and APCE are in accordance with the variation of photocurrents shown in Fig. 3a. This superior performance confirms the excellent light absorption, ηsep, and injection efficiency (ηinj), which we will discuss as follows. The ηsep and ηinj were evaluated using 0.25 M Na2SO3 + 0.25 M Na2S as a hole sacrificial agent (Supplementary Fig. 14). The ηsep of ZISZ is higher than that of ZIS (Fig. 3c), mostly thanks to the vertically ordered nanosheet distribution at the bottom as efficient transport path. The little improvement in ηinj (Fig. 3d) also signs that this ordered morphology mainly raises the ηsep. To investigate the bulk carrier dynamics, room-temperature photoluminescence (PL) was conducted (Supplementary Fig. 15). The PL intensity of ZISZ is lower than that of ZIS, suggesting the faster separation of electron-hole pairs and reduced bulk recombination in the ZISZ. When Fe is introduced into the sample by ALD, both the ηsep and ηinj are improved evidently. The enhanced ηsep is ascribed to the formation of lattice oxygen and the modification of the energy band, which will be discussed in detail below. The improved ηinj of ZISZ/Fe confirms the role of Fe–In–S cluster played in improving the surface OER dynamics. To rationalize the improved catalytic performance of the ZISZ/Fe photoanode, we obtained the η for OER of the ZISZ and ZISZ/Fe systems based on the DFT calculated free energy changes (Supplementary Table 2) using the two structures shown in Supplementary Fig. 7a and e. The computational details are described in Supplementary Material. The η decreases to 2.499 V in the ZISZ/Fe from 3.522 V in the pristine ZISZ (Fig. 3e and f). The notable 1.023 V drop in η provides a solid evidence that the catalytic performance is enhanced in the ZISZ/Fe photoanode once the Fe–In–S clusters are formed, because the Fe dopant alters the rate-determining step of *O to *OOH (step 3) in the ZISZ system (Fig. 3e) into *OH to *O (step 2) in the ZISZ/Fe (Fig. 3f) system, leading to that the OOH* is preferred for formation on the ZISZ/Fe catalyst and favors O2 production. The DFT calculations provide an excellent explanation for the experimental results. The electrochemical impedance spectroscopy (EIS) was further measured to probe the interface reaction dynamics of electrode (Supplementary Fig. 16). The series resistance (Rs) represents the resistance between FTO and sample, and the charge transfer resistance (Rct) indicates the resistance between photoanode and electrolyte22. ZISZ and ZIS perform the similar Rct, further demonstrating that the activity improvement of ZISZ is attributed to the reduced bulk recombination instead of interface charge transfer. ZISZ/Fe possesses the smallest Rct, suggesting that the enhanced surface OER reaction kinetics is caused by Fe–In–S clusters. In order to prove that the promotion of surface OER is not related to O, only O3 was introduced into the ALD chamber (samples are denoted as ZISZ/O) to avoid the formation of Fe–In–S. The J of ZISZ/O is lower (Supplementary Fig. 17a) and the surface resistance is higher (Supplementary Fig. 17b), therefore, the Fe–In–S clusters are critical for enhanced OER reaction.
a Linear sweep voltammogram curves. b UV-visible absorption spectra (the inset is the corresponding Tauc-plots). c The ηsep and d the ηinj of ZIS, ZISZ, and ZISZ/Fe. Free energies of OER reaction steps for e ZISZ and f ZISZ/Fe systems, the entire structure of the OER four-step reaction are shown in Supplementary Fig. 19.
Charge transfer and recombination kinetics
Intensity-modulated photocurrent spectroscopy (IMPS) kinetic analysis was performed to study the charge transfer and transit dynamics processes, including surface charge-transfer efficiency (ηtran), surface charge-transfer rate constants (Ktran), and surface charge recombination rate constants (Krec). The relationship between them can be described by the following formula43:
The IMPS curves of ZIS, ZISZ, and ZISZ/Fe were measured with different voltages (0.6–1.2 V) under λ = 365 nm irradiation (Supplementary Fig. 18). The calculation details of the rate and time constants are presented in the supporting information. The ηtran of ZISZ are basically unchanged while ZISZ/Fe has a huge improvement compared with ZIS (Fig. 4a), in accordance with the trend of ηinj. This confirms that IMPS is feasible to analyze surface OER reaction kinetics38. The values of the Ktran over the entire voltage range are much larger than those of the Krec (Fig. 4b and c), indicating that most of the carriers on the photoanode surface are effectively transferred into the electrolyte, which is consistent with the ηtran. With the increased voltage, the Ktran of the three samples increases obviously only in the low voltage range, and then keeps unchanged basically, while the Krec remains almost constant. It is suggested that the improvement in the performance of ZISZ/Fe at a lower voltage is mainly due to the increase of the transfer rate of photogenerated carriers on the photoanode surface, proving that Fe–In–S clusters could effectively improve its interface transfer efficiency and promote the OER reaction kinetics on the photoanode surface. The ηtran, Ktran, and Krec of ZIS and ZISZ have no large difference across the entire voltage range, indicating the improved PEC performance of ZISZ is mainly ascribed to the increased ηsep once again. Compared with ZISZ, both the ηtran and Ktran of ZISZ/Fe are significantly improved, while the Krec is obviously reduced. This is because the construction of Fe–In–S clusters on the surface of the photoanode effectively reduces the electrochemical barrier of the photoanode surface reaction, promotes the surface OER reaction kinetics, and reduces interfacial recombination, so that ZISZ/Fe exhibits the best PEC activity. In addition, electron transfer time (τd) of photoanodes can be calculated from the formula:
where the fmin is the frequency of the lowest point of the imaginary part in IMPS. The IMPS results show longer τd of ZISZ/Fe owing to the frequency at the minimum imaginary part of ZISZ is higher than ZISZ/Fe (Supplementary Fig. 18), which is consistent with the reduced bulk recombination. The time-resolved transient photoluminescence decay (TRPL, Fig. 4d) spectra were measured to calculate carrier lifetime also. ZISZ/Fe (τ = 2.18 ns) and ZISZ (τ = 1.57 ns) display a slower recombination rate and the carrier lifetime is longer than ZIS (τ = 1.31 ns). The prolonged lifetime manifests enhanced carrier transfer efficiency and decreased recombination. The ultraviolet photoemission spectroscopy (UPS) results show that the ZISZ/Fe possesses a gradient band structure throughout the nanosheets with the etching depth. The infinite number of Type-II heterojunctions causes the stepped distribution of energy level, further enhancing the ηsep of ZISZ/Fe.
In summary, we developed the ALD technology to manipulate the surface chemical state and bulk energy band structure in ZnInS nanosheet ordered arrays, which are utilized as efficient photoanodes of PEC water splitting. The performance improvement is mainly ascribed to the following points: (1) The disordered part at the bottom of nanosheet arrays is eliminated and thus a direct transport channel of photogenerated carriers is formed, together with a gradient energy band structure, enhancing the ηsep. (2) The surface-rich Fe–In–S clusters greatly reduce the OER reaction barrier through precisely controlling the forming processes of O* and OOH* of the OER four-electron reactions. These effects largely improve the PEC activity of ZnInS photoanode with a J of 5.35 mA cm−2 at 1.23 VRHE and negative Von of 0.09 VRHE. The present results prove the feasibility of ALD to manipulate chemical bonds and energy band structure of photoelectrodes towards improved energy conversion technology.
Methods
Synthesis of ZnIn2S4 (ZIS) nanosheet array
The fluorine-doped tin oxide glass (FTO) was first sonicated three times with acetone, ethanol, and deionized water for 10 min each time. The ZIS precursor solution was prepared through the following steps: 0.2045 g Zinc dichloride (ZnCl2) and 0.8795 g Indium chloride tetrahydrate (InCl3·4H2O) were dissolved into 150 mL of ultrapure water (H2O), and then 0.4565 g Thioacetamide (CH3CSNH2, TAA) was added and stirred for 15 min. The cleaned FTO was placed in a 25 ml Teflon-lined stainless steel autoclave, with the conductive side of the FTO facing down. Each lining was pipetted with 10 mL of the prepared precursor solution, and then the vessel was sealed and heated up to 160 °C for 360 min. After cooling down to room temperature, the ZIS nanosheet was formed and rinsed with absolute ethanol, and stored in a vacuum oven.
Synthesis of Zn10In16S34 (ZISZ) nanosheet array
The reaction process is basically the same as that of obtaining the ZIS, except for the solution of hydrothermal reaction. the ZISZ precursor solution was prepared through the following steps: 0.2045 g ZnCl2 and 0.8795 g InCl3·4H2O were dissolved into 150 mL of H2O, and then 0.6 g Thiourea (CH4N2S) was added and stirred for 15 min. The remaining steps are the same as the synthesis steps of ZIS nanosheet array.
Loading Fe–In–S clusters onto ZISZ (ZISZ/Fe) nanosheet array
Fe–In–S clusters were deposited on the surface of ZISZ by atomic layer deposition method (ALD) (LabNano 9100, ENSURE NANOTECH, Beijing, China). Ferrocene and ozone were used as iron and oxygen precursors, respectively. The growth rate of Fe2O3 was 0.05 Å per cycle at 250 °C based on the data analysis from silicon substrates, the pulse time of both O3 and Ferrocene was 0.02 s, and the interval time was 8 s. Fe–In–S cluster with different thicknesses were obtained by controlling cycle numbers.
Materials characterization
Scanning electron microscopy (FE-SEM, SU8100, Hitachi) was used to characterize the morphology of samples. The microstructure and lattice structures of materials were observed by transmission electron microscopy (TEM) and high-resolution TEM (HRTEM, Tecnai G2 F20 200 KV, FEI). X-ray diffraction (XRD) patterns (Cu Kα radiation, λ = 0.15418 nm, D/MAX-III-B-40KV) were obtained to evaluate the phase of the samples. The element distribution was conducted by energy-dispersive X-ray spectroscopy (EDX) under the TEM with an annular dark-field (ADF) detector. X-ray photoelectron spectroscopy (XPS) measurement (Thermo Fisher Scientific, ESCALAB 250Xi) was performed to determine the surface chemical environment of elements. X-ray absorption spectroscopy (XAS) measurements were studied in both X-ray absorption near edge structure (XANES) for Fe K-edge and Extended X-ray absorption fine structure (EXAFS) regions for Fe K-edge. The XAS experiments were carried out at the SUT-NANOTEC-SLRI XAS Beamline (BL5.2) at the Synchrotron Light Research Institute (SLRI), Nakhon Ratchasima, Thailand. The measurements were collected in transmission mode for both S K-edge and Fe L3 absorption edge. Ionization chambers were installed in front of and behind the sample to detect the incident (I0) and transmitted (I1) beam. Data analysis was carried out by IFEFFIT. In order to obtain the oxidation state of S, In, and Fe, the XANES spectra were analyzed by Athena software. The UV-visible absorption spectra were recorded to characterize the light absorption of the sample by an UV-vis spectrophotometer (Shimadzu, UV-3600). The room photoluminescence (PL) spectra (excited by 325 nm illumination) were record on a RenishawRM3000 Micro-Raman system, and the excitation pulse came from a 325 W Xe lamp (Edinburgh Instruments, FLS920). The time-resolved transient photoluminescence (TRPL) decay spectra were measured by using an Edinburgh Instruments as LifeSpec II with 373 nm laser (2 Bain Square, Kirkton Campus, and Livingston EH54 7DQ). The ultraviolet photoemission spectroscopy (UPS, Thermo Scientific, Escalab 250Xi) was used to evaluate the energy band.
Photoelectrochemical (PEC) and electrochemical measurements
All the measurements were carried out on an electrochemical workstation (Autolab, PGSTAT 302N) with a conventional three-electrode cell, and the electrolyte was 0.5 M Na2SO4 with pH ≈ 6.8. The photocurrent–voltage (J–V) curves were performed under AM 1.5G illumination (100 mW cm−2) from a solar light simulator (Newport, 94043A). Electrochemical impedance spectra (EIS) were measured on the workstation with the frequency ranging from 0.1 Hz to 100 kHz at an open-circuit voltage under light illumination.
The measured potential versus Ag/AgCl was converted to the reversible hydrogen electrode (RHE) scale using the Nernst equation29
where EoAg/AgCl = 0.1976 V at 25 °C and EAg/AgCl is the experimentally measured potential versus Ag/AgCl reference.
The intensity-modulated photocurrent spectroscopy (IMPS) kinetic analysis was measured on an electrochemical workstation (CIMPS, Zennium Zahner) in a three-electrode system as that of the PEC measurements. The irradiation source is a LED (s/n Ls 1272, Zennium Zahner) with 365 nm wavelength, and the power intensity is 30 W m−2. The frequency range is 1 kHz–0.1 Hz, and the ±5% modulation intensity is around 30 W m−2. The Nyquist plots were used to get the rate constants of the surface charge-transfer and recombination43.
The applied bias photon-to-current efficiency (ηABPE) was calculated from the current-potentiometry data using the following equation5
where VRHE is the potential of the working electrode versus the reversible hydrogen electrode, Jdark and Jlight are the measured current density in dark and under illumination, respectively, and Psunlight is 100 mW cm−2.
During the testing of injection efficiency (ηinj) and charge separation efficiency (ηsep), we employed Na2S/Na2SO3 electrolyte as the hole scavenger. Here, ηsep represents the proportion of the electrode/electrolyte interface photo-generated holes, while ηinj represents the proportion of those holes at the photoanode/electrolyte interface for water oxidation5
where Jabs represents the unity converted photocurrent density that is achievable, \({J}_{{{{\mbox{H}}}}_{2}{{\mbox{O}}}}\) and \({J}_{{{{\mbox{Na}}}}_{2}{{{\mbox{SO}}}}_{3{{\mbox{}}}}}\) represent the photocurrent density tested in 0.5 M Na2SO4 and Na2S/Na2SO3, respectively.
The unity converted photocurrent density (Jabs) is calculated by integrating ηabs over the standard solar spectrum:
where λmax is the maximum light absorption edge of a photoelectrode, λ (nm) is the light wavelength, and E (λ) is the power density (mW cm−2) at a specific wavelength (λ) of the standard solar spectrum.
The IPCE and APCE can be calculated from the formula44,45:
J refers to the photocurrent density (mA cm−2) produced by the photoelectrode, whereas Plight is the power density obtained at a specific wavelength (λ), respectively. ηabs. is the efficiency of the light harvested, and it can be calculated from the obtained light absorbance curves:
where the A is light absorbance measured by a UV-vis spectroscopy.
Computational details
Density functional theory (DFT) calculations are performed with the Vienna ab initio simulation package (VASP)46. The Pedrew–Burke–Ernzerhof (PBE) functional is used to describe the electron exchange-correlation interactions47, and the projected augmented approach wave is adopted to construct the pseudopotential for treat the ion-electron interaction48. A pane-wave cutoff energy of 400 eV and 4 × 4 × 1 Γ-centered Monhorst-Pack k-point mesh are used for all calculations49. DFT-D3 method of Grimme is employed to describe the van der Waals interactions50. The dipole correction is taken into account for all calculations. The stoichiometric 4 × 4 one-layer 112-atom ZIS (001) surface with 64 S atoms, 16 Zn atoms, and 32 In atoms is built using the ZnIn2S4 unit cell51 based on previous DFT calculations52,53,54, because the hexagonal ZnIn2S4 has a sandwiched layered structure, and the layers are connected by van der Waals interaction. The interlayer interaction is rather weak that allows one to use a monolayer structure instead of a multi-layer model in the simulations52. Such settings not only maintain the major properties of the ZnIn2S4 because the catalytic reactions generally occur on the materials surface, but also reduce the computational cost. According to the previous DFT calculations on the WO3-x/ZnIn2S453 and the Li2Sx/ZnIn2S4 systems, we add an 8-atom ZnS cluster into the ZIS (001) surface and leads to the stoichiometric ZISZ system, Supplementary Fig. 7a, consistent with present experimental conditions. The ZISZ/Fe system is obtained by replacing an In atom or a Zn atom with an Fe atom on the topmost ZISZ surface, displayed in Supplementary Fig. 7b–e. To eliminate the interactions between periodic images, a vacuum region of 20 Å is added normal to the surface.
In order to verify the stability of the four geometries, we have performed the 8 ps adiabatic molecular dynamic simulations at 300 K in the microcanonical ensemble with a 1 fs time step after heating up all the systems to 300 K via repeated velocity rescaling lasting for 2 ps. The obtained evolution of total energy cumulative average over time for four systems oscillates only in a narrow window, shown in Supplementary Fig. 19, suggesting that the used structures are reasonable and thermodynamically stable. The four-electron OER processes are described as the aforementioned Eqs. (1)–(4).
The Gibbs free energy G is calculated according to the equation as follows:
where E, EZPE, and S are the single point energy, zero-point energy, and entropy of the ZISZ and ZISZ/Fe slabs adsorbed with and without various oxygen intermediates, respectively. \(U\) represents the potential versus standard hydrogen electrode. T is set to 298.15 K.
The overpotential (η) for OER is estimated according to the following equation when U equals to 0.
Here, ΔG1, ΔG2, ΔG3, and ΔG4 denote the Gibbs free energy difference for each reaction, (1)–(4), respectively.
Data availability
The data that support the findings of this study are available from the corresponding authors upon reasonable request, and the source data are provided with this paper (10.11922/sciencedb.00033).
References
Yang, W., Prabhakar, R. R., Tan, J., Tilley, S. D. & Moon, J. Strategies for enhancing the photocurrent, photovoltage, and stability of photoelectrodes for photoelectrochemical water splitting. Chem. Soc. Rev. 48, 4979–5015 (2019).
Landman, A. et al. Photoelectrochemical water splitting in separate oxygen and hydrogen cells. Nat. Mater. 16, 646–651 (2017).
Chandrasekaran, S. et al. Recent advances in metal sulfides: from controlled fabrication to electrocatalytic, photocatalytic and photoelectrochemical water splitting and beyond. Chem. Soc. Rev. 48, 4178–4280 (2019).
Zhou, M. et al. Hybrid 0D/2D edamame shaped ZnIn2S4 photoanode modified by Co-Pi and Pt for charge management towards efficient photoelectrochemical water splitting. Appl. Catal. B Environ. 244, 188–196 (2019).
Wang, H. et al. Highly active deficient ternary sulfide photoanode for photoelectrochemical water splitting. Nat. Commun. 11, 3078 (2020).
Fountaine, K. T., Lewerenz, H. J. & Atwater, H. A. Efficiency limits for photoelectrochemical water-splitting. Nat. Commun. 7, 13706 (2016).
Jian, J. et al. Embedding laser generated nanocrystals in BiVO4 photoanode for efficient photoelectrochemical water splitting. Nat. Commun. 10, 2609 (2019).
Kim, M. et al. Oxygen-vacancy-introduced BaSnO3-δ photoanodes with tunable band structures for efficient solar-driven water splitting. Adv. Mater. 31, 1903316 (2019).
Browne, M. P., Plutnar, J., Pourrahimi, A. M., Sofer, Z. & Pumera, M. Atomic layer deposition as a general method turns any 3D-printed electrode into a desired catalyst: case study in photoelectrochemisty. Adv. Energy Mater. 9, 1900994 (2019).
Tang, S., Qiu, W., Xiao, S., Tong, Y. & Yang, S. Harnessing hierarchical architectures to trap light for efficient photoelectrochemical cells. Energy Environ. Sci. 13, 660–684 (2020).
Yu, Y. et al. Enhanced photoelectrochemical efficiency and stability using a conformal TiO2 film on a black silicon photoanode. Nat. Energy 2, 17045 (2017).
Zhang, H. et al. Gradient tantalum-doped hematite homojunction photoanode improves both photocurrents and turn-on voltage for solar water splitting. Nat. Commun. 11, 4622 (2020).
Ye, K. H. et al. Enhancing photoelectrochemical water splitting by combining work function tuning and heterojunction engineering. Nat. Commun. 10, 3687 (2019).
Deng, J. et al. Nanowire photoelectrochemistry. Chem. Rev. 119, 9221–9259 (2019).
Han, H. S. et al. Boosting the solar water oxidation performance of a BiVO4 photoanode by crystallographic orientation control. Energy Environ. Sci. 11, 1299–1306 (2018).
Zhang, G. et al. Preparation of ZnIn2S4 nanosheet-coated CdS nanorod heterostructures for efficient photocatalytic reduction of Cr(VI). Appl. Catal. B Environ. 232, 164–174 (2018).
Bai, Z. et al. Photoelectrochemical performance enhancement of ZnO photoanodes from ZnIn2S4 nanosheets coating. Nano Energy 14, 392–400 (2015).
Fan, B., Chen, Z., Liu, Q., Zhang, Z. & Fang, X. One-pot hydrothermal synthesis of Ni-doped ZnIn2S4 nanostructured film photoelectrodes with enhanced photoelectrochemical performance. Appl. Surf. Sci. 370, 252–259 (2016).
Song, J. et al. A review on fundamentals for designing oxygen evolution electrocatalysts. Chem. Soc. Rev. 49, 2196–2214 (2020).
Roger, I., Shipman, M. A. & Symes, M. D. Earth-abundant catalysts for electrochemical and photoelectrochemical water splitting. Nat. Rev. Chem. 1, 0003 (2017).
Kuang, Y. et al. Ultrastable low-bias water splitting photoanodes via photocorrosion inhibition and in situ catalyst regeneration. Nat. Energy 2, 16191 (2016).
Wang, S. et al. In situ formation of oxygen vacancies achieving near‐complete charge separation in planar BiVO4 photoanodes. Adv. Mater. 32, 2001385 (2020).
Zhang, B. et al. Unveiling the activity and stability origin of BiVO4 photoanodes with FeNi oxyhydroxides for oxygen evolution. Angew. Chem. Int. Ed. 59, 1–7 (2020).
Zhang, B., Wang, L., Zhang, Y., Ding, Y. & Bi, Y. Ultrathin FeOOH nanolayers with abundant oxygen vacancies on BiVO4 photoanodes for efficient water oxidation. Angew. Chem. Int. Ed. 57, 2248–2252 (2018).
Chen, D., Liu, Z. & Zhang, S. Enhanced PEC performance of hematite photoanode coupled with bimetallic oxyhydroxide NiFeOOH through a simple electroless method. Appl. Catal. B Environ. 265, 118580 (2020).
Li, J. et al. Dynamic role of cluster cocatalysts on molecular photoanodes for water oxidation. J. Am. Chem. Soc. 141, 12839–12848 (2019).
Ning, F. et al. TiO2/graphene/NiFe-layered double hydroxide nanorod array photoanodes for efficient photoelectrochemical water splitting. Energy Environ. Sci. 9, 2633–2643 (2016).
Lin, H., Long, X., An, Y., Zhou, D. & Yang, S. Three-dimensional decoupling co-catalyst from a photoabsorbing semiconductor as a new strategy to boost photoelectrochemical water splitting. Nano Lett. 19, 455–460 (2019).
Zhang, K. et al. Black phosphorene as a hole extraction layer boosting solar water splitting of oxygen evolution catalysts. Nat. Commun. 10, 2001 (2019).
Zhang, Z. et al. Interfacial oxygen vacancies yielding long-lived holes in hematite mesocrystal-based photoanodes. Nat. Commun. 10, 4832 (2019).
Xu, X.-T., Pan, L., Zhang, X., Wang, L. & Zou, J.-J. Rational design and construction of cocatalysts for semiconductor-based photo-electrochemical oxygen evolution: a comprehensive review. Adv. Sci. 6, 1801505 (2019).
Wang, Q. et al. Oxysulfide photocatalyst for visible-light-driven overall water splitting. Nat. Mater. 18, 827–832 (2019).
Zou, X. et al. In situ generation of bifunctional, efficient Fe-based catalysts from mackinawite iron sulfide for water splitting. Chem 4, 1139–1152 (2018).
Huang, Z.-F. et al. Chemical and structural origin of lattice oxygen oxidation in Co-Zn oxyhydroxide oxygen evolution electrocatalysts. Nat. Energy 4, 329–338 (2019).
Li, S. et al. Ir-O-V catalytic group in Ir-doped NiV(OH)2 for overall water splitting. ACS Energy Lett. 4, 1823–1829 (2019).
Li, Y. et al. Implanting Ni-O-VOx sites into Cu-doped Ni for low-overpotential alkaline hydrogen evolution. Nat. Commun. 11, 2720 (2020).
Yan, J. et al. Single atom tungsten doped ultrathin alpha-Ni(OH)2 for enhanced electrocatalytic water oxidation. Nat. Commun. 10, 2149 (2019).
Zhang, Y. et al. Improvement of BiVO4 photoanode performance during water photo‐oxidation using Rh-doped SrTiO3 perovskite as a co-catalyst. Adv. Funct. Mater. 29, 1902101 (2019).
Meng, L. et al. Simultaneous manipulation of O-doping and metal vacancy in atomically thin Zn10In16S34 nanosheet arrays toward improved photoelectrochemical performance. Angew. Chem. Int. Ed. 57, 16882–16887 (2018).
Quintanilla, A., Casas, J. A., Miranzo, P., Osendi, M. I. & Belmonte, M. 3D-Printed Fe-doped silicon carbide monolithic catalysts for wet peroxide oxidation processes. Appl. Catal. B Environ. 235, 246–255 (2018).
Yang, X., Du, C., Liu, R., Xie, J. & Wang, D. Balancing photovoltage generation and charge-transfer enhancement for catalyst-decorated photoelectrochemical water splitting: a case study of the hematite/MnOx combination. J. Catal. 304, 86–91 (2013).
Du, C. et al. Hematite-based water splitting with low turn-on voltages. Angew. Chem. Int. Ed. 125, 12924–12927 (2013).
Zhou, Z., Wu, S., Li, L., Li, L. & Li, X. Regulating the silicon/hematite microwire photoanode by the conformal Al2O3 intermediate layer for water splitting. ACS Appl. Mater. Int. 11, 5978–5988 (2019).
Chen, Z. et al. Accelerating materials development for photoelectrochemical hydrogen production: standards for methods, definitions, and reporting protocols. J. Mater. Res. 25, 3–16 (2010).
Fu, Y. et al. Surface electronic structure reconfiguration of hematite nanorods for efficient photoanodic water oxidation. Sol. Rrl. 4, 1900349 (2020).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B Condens. Matter 54, 11169–11186 (1996).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 78, 1396 (1996).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B Condens. Matter 50, 17953–17979 (1994).
Chadi, D. J. Special points for Brillouin-zone integrations. Phys. Rev. B Condens. Matter 16, 1746–1747 (1977).
Grimme, S., Antony, J., Ehrlich, S. & Krieg, H. A consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J. Chem. Phys. 132, 154104 (2010).
Hu, X., Yu, J., Gong, J. & Li, Q. Rapid mass production of hierarchically porous ZnIn2S4 submicrospheres via a microwave-solvothermal process. Cryst. Growth Des. 7, 2444–2448 (2007).
Shi, X. et al. Ultrathin ZnIn2S4 nanosheets with active (110) facet exposure and efficient charge separation for cocatalyst free photocatalytic hydrogen evolution. Appl. Catal. B Environ. 265, 118616 (2020).
Luo, D. et al. Highly efficient photocatalytic water splitting utilizing a WO3-x/ZnIn2S4 ultrathin nanosheet Zscheme catalyst. J. Mater. Chem. A 9, 908–914 (2021).
Zhang, Z. et al. Reasonably introduced ZnIn2S4@C to mediate polysulfide redox for long-life lithium–sulfur batteries. ACS Appl. Mater. Int. 13, 141169–14180 (2021).
Acknowledgements
We acknowledge the support from the National Natural Science Foundation of China (52025028, 51972218), 1000 Youth Talents Plan, Key University Science Research Project of Jiangsu Province (17KJA430013), Six Talents Peak Project of Jiangsu Province, 333 High-level Talents Cultivation Project of Jiangsu Province, and the Priority Academic Program Development (PAPD) of Jiangsu Higher Education Institutions. We thank the support from the BL5.2 SUT-NANOTEC-SLRI XAS beamline, at the Synchrotron Light Research Institute, Nakhon Ratchasima, Thailand for XAS measurements.
Author information
Authors and Affiliations
Contributions
L.L. initially conceptualized and designed the project. L.M. and W.X. carried out all sample synthesis and characterization. L.L., L.M. and K.D. wrote the manuscript. R.L. and J.H. calculated the DFT results and wrote this part. P.K., X.Z. and Y.T. performed the XAS analyses. All authors contributed to the overall scientific interpretation and revised this paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Meng, L., He, J., Zhou, X. et al. Atomic layer deposition triggered Fe-In-S cluster and gradient energy band in ZnInS photoanode for improved oxygen evolution reaction. Nat Commun 12, 5247 (2021). https://doi.org/10.1038/s41467-021-25609-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-25609-0
- Springer Nature Limited
This article is cited by
-
Large electronegativity differences between adjacent atomic sites activate and stabilize ZnIn2S4 for efficient photocatalytic overall water splitting
Nature Communications (2024)
-
A restricted dynamic surface self-reconstruction toward high-performance of direct seawater oxidation
Nature Communications (2024)
-
High-performance Bi2S3/ZnO photoanode enabled by interfacial engineering with oxyanion for efficient photoelectrochemical water oxidation
Nano Research (2024)
-
Modular design of solar-powered photocathodic metal protection device
Carbon Neutrality (2023)