Abstract
Layered transition-metal oxides have attracted intensive interest for cathode materials of sodium-ion batteries. However, they are hindered by the limited capacity and inferior phase transition due to the gliding of transition-metal layers upon Na+ extraction and insertion in the cathode materials. Here, we report that the large-sized K+ is riveted in the prismatic Na+ sites of P2-Na0.612K0.056MnO2 to enable more thermodynamically favorable Na+ vacancies. The Mn-O bonds are reinforced to reduce phase transition during charge and discharge. 0.901 Na+ per formula are reversibly extracted and inserted, in which only the two-phase transition of P2 ↔ P’2 occurs at low voltages. It exhibits the highest specific capacity of 240.5 mAh g−1 and energy density of 654 Wh kg−1 based on the redox of Mn3+/Mn4+, and a capacity retention of 98.2% after 100 cycles. This investigation will shed lights on the tuneable chemical environments of transition-metal oxides for advanced cathode materials and promote the development of sodium-ion batteries.
Similar content being viewed by others
Introduction
Sodium-ion batteries (SIBs) have been considered as one promising next-generation battery system for large-scale energy storage and smart electric grid, due to the low cost and wide distribution of Na resources1,2,3. The battery performance and cost are mainly governed by the applied cathode materials4,5,6,7. A wide range of host materials, such as transition-metal oxides, phosphates, Prussian blue analogs, and so on, have been investigated for reversible (de)intercalation of Na+. However, the intrinsic large ionic radius of 102 pm and molar weight of Na+ over its Li+ counterpart impose penalties on the specific capacity or the structure stability of cathode materials, which limit the deployment of SIBs8,9,10,11,12. It is rational to design and synthesize cathode materials with more available sites for Na+ storage and robust crystal structure for Na+ (de)intercalation, ensuring their large specific capacities and long cycle life.
Layered transition-metal oxides with earth-abundant elements have been actively studied as host materials for Na+ storage13,14. Sodium manganese oxide with a P2 phase (P2-NaxMnO2) is of significant importance for SIBs, which is consisted of two MnO6-octahedra slabs and sandwiched Na layers in each unit cell with the ABBA oxygen packing frameworks15,16. It usually delivers a capacity of ~160 mAh g−1, corresponding to insertion of 0.60 Na+ per formula for P2-NaxMnO217,18. The limited movable Na+ and phase transitions occurring upon its extraction and reinsertion are the major challenges. The Na+ extraction to x < 0.35 in P2-NaxMnO2 results in the irreversible P2 → OP4 phase transition, due to gliding of the MnO2-slabs, and consequently decaying capacities in cycles19,20. Fe-doping in the MnO2-slabs of NaxFe0.5Mn0.5O2 is beneficial for a high capacity of 200 mAh g−1 but with 35% capacity loss after 30 cycles, which is originated from the P2 → O2/OP4 phase transition21. The capacity can also be promoted to 185 mAh g−1 by co-doping Co and Ni for P2-Na0.7Mn0.6Ni0.3Co0.1O2 (Yoshida et al.22). Partial Mg substitution for Mn in P2-NaxMnO2 delays the formation of OP4 phase, leading to smooth electrochemical profiles and extended cycling performance with a capacity of 106 mAh g−1 (Clément et al.19). The substitution of Li or Al in NaxMnO2 can suppress the Jahn-Teller distortion and enhance its phase stability23,24. It is clear that finely tuning the chemical environments of the MnO6-octahedra with suitable dopants in the place of Mn allows for either more accessible Na+ sites for large capacities with limited cycles or minimized slab gliding for long cycles with moderate capacities. However, solutions to such paradox are challenging and highly desirable for the development of SIBs25.
Here, we show that the large-sized K+ of 138 pm is riveted in the edge-sharing sites of Na+ in P2-Na0.612K0.056MnO2, which leads to the small interslab distance of 0.56 nm in Na0.612K0.056MnO2 and results in high diffusion barrier of K+ and hence its immobility. The Na-O bond strength and Na+ vacancy formation energy are reduced to favor more extractable and insertional Na+. The reinforced MnO6-octahedra slabs are beneficial to the structure stability of P2-Na0.612K0.056MnO2. In situ X-ray diffraction (XRD) indicates that there is no inferior phase transition at the high charge voltages during cycles. It turns out to exhibit a high specific capacity of 240.5 mAh g−1 with Mn3+/Mn4+ as the redox couple and the highest energy density of 654 Wh kg−1 with good cycle stability and rate capability.
Results and discussion
Characterization and structure analysis
Na0.67−xKxMnO2 (0 ≤ x ≤ 0.2) was synthesized via a solid-state reaction at 900 °C in air, however, the pure P2 phase was only obtained with x ≤ 0.1, as confirmed by the XRD patterns in Fig. 1a and Supplementary Figs. 1 and 2. The optimized composition was found with nominal x = 0.1. Its exact composition was determined to P2-Na0.612K0.056MnO2 by inductively coupled plasma-optical emission spectrometry (ICP-OES) in Supplementary Table 1. The oxygen non-stoichiometry in the as-synthesized P2-Na0.612K0.056MnO2-δ was determined by iodine stoichiometry titration. As listed in Supplementary Table 2, it shows the atomic ratio of oxygen is 1.985, which is mainly attributed to oxygen vacancies on its surface26. The XRD pattern and Rietveld refinement of Na0.612K0.056MnO2 and Na0.706MnO2 are displayed in Fig. 1a and Supplementary Fig. 3, and all the diffraction peaks are assigned to a hexagonal lattice with a space group of P63/mmc. The refined structure of Na0.612K0.056MnO2 is depicted along the y and z axes in Fig. 1b, c, respectively. There exist two types of trigonal prismatic sites for Na+, which are sharing faces (Naf) and edges (Nae) with the MnO6-octahedra in the two adjacent slabs, respectively, as depicted in Fig. 1c and Supplementary Fig. 4. The two adjacent Na sites are not accessible at the same time, because of their large electrostatic repulsion. Rietveld refinement indicates that K+ is located at the Nae site (Supplementary Tables 3 and 4), which is mainly ascribed to the much higher stability of the Nae sites27,28. Moreover, the interlayer space (d(Na-O-Na)) is enlarged to 3.58 Å in Na0.612K0.056MnO2 (3.42 Å in Na0.706MnO2) due to the larger ionic radii for K+ versus Na+. On the contrary, the dMnO2 is reduced to 2.02 Å in Na0.612K0.056MnO2 (2.28 Å in Na0.706MnO2), which is resulted from the enhanced MnO2-slabs. Thus, the distances of adjacent MnO2-slabs (d-spacing) are reduced in K-doped compounds even with larger-sized K+ in the Na layers.
a XRD pattern and Rietveld refinement. Typical layered structure of Na0.612K0.056MnO2 viewed along the y axis (b) and the z axis (c) with K+ located at the Nae sites. d PDF pattern and structure of Na0.612K0.056MnO2. The representative peaks correspond to the bond length of Mn–O (blue line) and Mn–Mn (pale blue line) as labeled. e Fitting of Mn K-edge FT-EXAFS spectra of Na0.612K0.056MnO2.
Synchrotron X-ray pair distribution function (PDF) analysis was performed to study the local structure of Na0.612K0.056MnO2 in Fig. 1d. The P2-type layered structure is consistent with XRD refinement, as depicted in Supplementary Table 5. The Mn–O and Mn–Mn bond lengths are 1.890 and 2.891 Å, respectively, which are shorter than those in Na0.706MnO2 (1.897 and 2.901) in Supplementary Fig. 5 and Table 6. This suggests the strengthened chemical bonds and reinforced interaction of MnO6-octahedra slabs. X-ray adsorption near-edge structure (XANES) spectra in Supplementary Fig. 6a imply that Mn has the approximately same average oxidation states in Na0.612K0.056MnO2 and Na0.706MnO2. The fitted Mn K-edge Fourier-transformed extended X-ray adsorption fine structure (FT-EXAFS) spectrum of Na0.612K0.056MnO2 is shown in Fig. 1e, as well as Na0.706MnO2 in Supplementary Fig. 6b. As listed in Supplementary Tables 7 and 8, it shows shortened bond lengths of Mn–O (1.889 Å, 1.895 Å for Na0.706MnO2) and Mn–Mn (2.889 Å, 2.897 Å for Na0.706MnO2). This is in good agreement with the PDF results and the d-spacings of 0.56 and 0.57 nm between the (002) facets in Na0.612K0.056MnO2 and Na0.706MnO2, respectively, as observed by high-resolution transmission electron microscopy (HRTEM) in Supplementary Fig. 7.
Scanning transmission electron microscopy (STEM) equipped with the detectors of high-angle annular dark field (HAADF) and annular bright field (ABF) are employed to study the atomic structure of Na0.612K0.056MnO2 in Fig. 2a, b and Supplementary Fig. 8, which is 1–10 μm in size in Supplementary Fig. 9a. The bright dots in the STEM-HAADF images and the dark dots in STEM-ABF image are assigned to the atomic columns of Mn, between which are the atomic columns of Na or K. The STEM-HAADF and SEM images in Supplementary Figs. 9b and 10 indicate that Na0.706MnO2 has similar morphology and layered structure with Na0.612K0.056MnO2. Electron energy loss spectroscopy (EELS) in Fig. 2c and Supplementary Fig. 11 were collected in the selected areas as indicated, in which the peaks of K L-edge at 297 eV indicate the presence of K in the Na layers in Na0.612K0.056MnO2.
Dynamic secondary ion mass spectroscopy (SIMS) is performed to analyze the distribution of elements from the surface to the bulk of Na0.612K0.056MnO2 in Fig. 2d, as well as their elemental mappings in Supplementary Figs. 12 and 13. It is shown that the contents of K and Na are increased along with a slight decrease of Mn in the initial 50 s of sputtering, and then they are gradually dropped and become constant. The K profile shows a slight aggregation trend on the surface in the initial 50 s of sputtering, and then the intensity ratio of K and Na is gradually decreased to a stable value, indicating uniform distribution of K and Na in the bulk of Na0.612K0.056MnO2. Similar trends for Na, Mn, and O are observed in the SIMS spectra of Na0.706MnO2 in Supplementary Fig. 14. Solid-state 39K nuclear magnetic resonance (NMR) spectrum of Na0.612K0.056MnO2 with K0.67MnO2 as a reference is shown in Fig. 2e. The peak at ~0 ppm is assigned to K+ located in the K-layers in the crystal structure of K0.67MnO2. The other two weak peaks at 70 and −70 ppm appear symmetrically and are assigned to the spinning sidebands due to the rotation of sample tube29. A negative chemical shift is observed for Na0.612K0.056MnO2, which is attributed to the smaller electronic shielding effect of Na and O in Na0.612K0.056MnO2 than K and O in K0.67MnO2, and a larger d-spacing of 0.64 nm in K0.67MnO2 than in P2-Na0.612K0.056MnO2 with the similar layered structure, as shown in Supplementary Fig. 15 and Table 9. These imply that K+ exists only in the Na layer, not in the MnO2-layer, and has a uniform distribution in the bulk particles of Na0.612K0.056MnO2.
Reaction mechanism
The structure evolution of Na0.612K0.056MnO2 upon Na+ extraction and intercalation is monitored by in situ XRD in a home-made battery within a voltage window of 1.8–4.3 V. As shown in Fig. 3a, each XRD pattern is obtained during the battery operation and corresponding to the state as indicated in the charge and discharge curves in the right-hand panel. The pristine Na0.612K0.056MnO2 is identified by the characteristic diffraction peaks of the (002), (004), (100), (102), and (104) planes in Fig. 3a. The P2 phase of Na0.612K0.056MnO2 is sustained in the first charge process without phase transition, and 0.498 Na+ per formula is extracted to give the fully charged state (I) of Na0.114K0.056MnO2, which agrees well with the ICP-OES in Supplementary Table 1. In the following discharge process, the P2 phase of the host is kept until 0.536 Na+ is inserted for Na0.65K0.056MnO2 (II). Due to the slight distortion of the MnO6-octahedra slabs, the P’2 phase starts to appear with the co-existence of P2 phase, and becomes dominant in the fully discharged state (III) of Na1.015K0.056MnO2. In the reverse charge process, the P’2 phase is gradually transformed to the P2 phase (IV), and then it is sustained at high charge voltages till 4.3 V (V). It involves the reversible two-phase transition of P2 ↔ P′2 with total insertion or extraction of 0.901 Na+ in the cycles of discharge and charge, as schematically illustrated in Fig. 3b. In contrast, P2-Na0.706MnO2 involves large gliding of the MnO6-octahedra slabs for the phase transition of P2 → OP4 upon extraction of 0.455 Na+ at high charge voltages; it then converts from the OP4 phase into P2 and P′2 during discharge with total insertion or extraction of 0.671 Na+ in cycles, as shown in the schematic phase transitions of P2-Na0.706MnO2 in Fig. 3c and in situ XRD patterns in Supplementary Fig. 17. Rietveld refinements of the fully charged and discharged Na0.612K0.056MnO2 and P2-Na0.706MnO2 (Supplementary Figs. 18–21 and Supplementary Tables 10–13) show drastic changes in the crystal structure and lattice parameters of P2-Na0.706MnO2. It was found that the volume variation of NaxK0.065MnO2 is 7.8%, which is significantly smaller than 11.2% in NaxMnO2, and favors the structural stability during cycling. It reveals that more Na+ (0.901 vs. 0.671 Na+) can be extracted at the high charge voltages and re-inserted from/into P2-Na0.612K0.056MnO2 than P2-Na0.706MnO2, due to the reduced Na-O bond strength and reinforced MnO6-octahedra slabs for suppression of the inferior OP4 phase.
The redox of Na0.612K0.056MnO2 is further unveiled by X-ray photoelectron spectroscopy (XPS) and EELS. The XPS Mn 2p spectrum of Na0.612K0.056MnO2 in Fig. 4a shows the splitting Mn 2p3/2 and Mn 2p1/2 at 640.8/642.2 and 652.4/654.9 eV, respectively, suggesting the co-existence of Mn3+ and Mn4+ with a ratio of 2:1. Upon charging, the intensity of Mn4+ peaks increases with decrease of the intensity of Mn3+ peaks, indicating oxidation of Mn3+ to Mn4+ in Fig. 4a. The remaining Mn3+ is 0.08 per formula at the charge finish of 4.3 V, which is consistent with the phase transition in Fig. 3b. The reduction of Mn4+ to Mn3+ in the following discharge process is evidenced by the gradual intensity increase of Mn3+ peaks till the disappearance of Mn4+ peaks, as shown in Fig. 4b. The peaks at 646.5 eV in Fig. 4a, b are mainly attributed to Augers of C–F and Na–F30. In addition, the EELS spectra of the charged, discharged, and pristine states of Na0.612K0.056MnO2 in Fig. 4c further confirm the redox of Mn3+/Mn4+ with the reversible shifts of the two peaks of Mn-L2 and Mn-L3. It is notable that there is no peak shift or broadening in both of the O pre-peak and K-edge, which suggests no valence change of O2-. Therefore, the redox of Mn3+/Mn4+ is responsible for the charge compensation in the extraction and reinsertion of Na+ from/into Na0.612K0.056MnO2 in the discharge and charge processes. Also, no oxygen evolution was detected by in situ differential electrochemical mass spectrometry (DEMS) in the charge process (Supplementary Fig. 22).
Density functional theory (DFT) calculations using Vienna Ab-initio Simulation Package (VASP) are performed to optimize the crystal structures of the pristine and charged cathode materials31,32,33,34. Because the numbers of K and Na atoms can only be integral in a unit cell, there exists a slight difference between the simulated formula and the obtained composition, which can be reasonably ignored. Figure 5a and Supplementary Fig. 23 exhibit the first-principle molecular dynamics simulations of Na0.500K0.055MnO2 and Na0.555MnO2, respectively, where the mean square displacements (MSDs) from 0 to 5 ps reflect the diffusion capability of each element. It shows that Na+ is more facile to migrate in Na0.500K0.055MnO2, and K+ is immobile as riveted between layers. Its migration is energetically unfavorable as displayed in Supplementary Fig. 24, in which its migration energy barrier is as high as ~0.8 eV in contrast with ~0.4 eV for Na+ in Na0.500K0.055MnO2 (refs. 35,36,37). Its diffusion coefficient is accordingly five orders of magnitude lower than that of Na+ based on Arrhenius equation. This is consistent with ICP-OES and elemental mappings in Supplementary Table 1 and Figs. 25 and 26, in which the content of K remains almost constant, suggesting no K loss in the charge and discharge processes. The optimized Na0.500K0.055MnO2 in Supplementary Fig. 27a shows a pure P2 phase with K+ located in the Na layers. It can be sustained in the optimized structure of P2-Na0.220K0.055MnO2 at the fully charged state with similar structure parameters in Supplementary Fig. 27b. This indicates the significant role of K for the stabilization of the crystal structure of Na0.612K0.056MnO2 for extraction and insertion of Na+. It is robust to allow for the extraction of 0.498 Na+ in the first charge without phase transition, as depicted in Fig. 3.
a MSD of Mn, K, Na, and O as functions of time in Na0.500K0.055MnO2. b Total density of states (tDOS) of Na0.220K0.055MnO2 and partial density of states (pDOS) of Na 3 s, K 4 s, O 2p and Mn 3d orbitals, as labeled by yellow, purple, red and green, respectively. The Fermi energy (Ef) is set to 0 eV, and the pDOS of Na 3 s, K 4 s are enlarged by 100 times. c Partial charge density distribution along the blue plane in the left panel for Na0.500K0.055MnO2 (visualized by Visualization for Electronic and Structure Analysis (VESTA)). The red regions represent high charge density, and the blue regions indicate low charge density. d Plot of deformation charge densities of Na0.500K0.055MnO2. The charge accumulation region is rendered in yellow, and the charge depletion is in blue. e Schematic pDOS of Na0.555MnO2 and Na0.500K0.055MnO2. f COHP analysis on representative prismatic sites and the adjacent MnO6-octahedra sites of Na0.555MnO2 and Na0.500K0.055MnO2.
The electronic structures of Na0.500K0.055MnO2 and Na0.555MnO2 have been investigated by DFT calculations. As shown in the density of states (DOS) of Na0.220K0.055MnO2 in Fig. 5b, although K only accounts for one fourth of Na in the composition, the DOS contributed by K atoms is similar to that of Na atoms. In addition, the partial charge density distribution in Fig. 5c reflects the local status of electrons. The electron cloud overlap between K and O is stronger than that between Na and O. As seen from the deformation charge densities for Na0.500K0.055MnO2 in Fig. 5d, the electron population at O atoms increases. However, the crystal orbital Hamilton populations (COHP) in Supplementary Fig. 28 indicate that it falls in a K-O antibonding region around the Fermi level, which is different from the bonding area of Na–O in Na0.555MnO2. Schematic pDOS of Na0.500K0.055MnO2 and Na0.555MnO2 are shown in Fig. 5e and Supplementary Figs. 29 and 30. The increased spin-down electrons around Fermi energy indicate stronger hybridization interaction between Mn and O in the presence of K+, in good agreement with the analysis of FT-EXAFS in Fig. 1d. Also, the Na-O bond strength in Na0.500K0.055MnO2 is found to be reduced by COHP analysis in Supplementary Table 14. As indicated by COHP analysis in Fig. 5f and Supplementary Tables 15–17, the Mn–O bonds are reinforced for both adjacent and distant Mn atoms with a more obvious increase in xy-plane by the substitution of K. A slight fluctuation of Mn–O bond strength is found for different valence state of Mn. These lead to more thermodynamically favorable Na+ vacancies (Supplementary Table 18), which is the determining factor for Na+ extraction and insertion, consistent with MSD in Fig. 5a. Of note, the formation energy for K+ siting in the Nae site (0.675 eV) is higher than in the Naf site (−3.500 eV) of Na0.500K0.055MnO2, which indicates the higher thermodynamic stability of the Nae site for K+. Furthermore, the reinforced Mn–O bonds play an important role to suppress the phase transition during Na+ extraction and insertion and favor the cycle stability.
Electrochemical performance
The electrochemical performance of Na0.612K0.056MnO2 is evaluated against Na metal anodes with the electrolyte of 1.0 M NaPF6 in propylene carbonate (PC) and 5 wt.% of fluoroethylene carbonate (FEC) in coin cells. Figure 6a exhibits the typical charge and discharge profiles of Na0.612K0.056MnO2 and Na0.706MnO2 at 20 mA g−1. Na0.612K0.056MnO2 delivers a high initial charge capacity of 125.1 mAh g−1, corresponding to 0.498 Na+ per formula. In the following cycles, the reversible capacity of Na0.612K0.056MnO2 reaches up to 240.5 mAh g−1, which is much higher than that of Na0.706MnO2 (167.2 mAh g−1). This means that 0.901 Na+ per formula is inserted and extracted into/from Na0.612K0.056MnO2. It agrees well with the restricted phase transition in Fig. 3. At the same time, Na0.612K0.056MnO2 presents higher discharge voltages than Na0.706MnO2 does, which is consistent with the cyclic voltammetry (CV) curves in Supplementary Fig. 31. The energy density of Na0.612K0.056MnO2 is as high as 654 Wh kg−1, in comparison with the reported cathode materials in Fig. 6b. Of particular, it is even higher than that of Na0.72Li0.24Mn0.76O2, which works with both the O redox and Mn3+/Mn4+ to deliver the highest specific capacity in refs. 38,39,40,41,42,43,44,45.
a Typical charge/discharge curves of Na0.612K0.056MnO2 and Na0.706MnO2 at 20 mA g−1 in the third cycle. b Comparison of energy density and average voltages of Na0.612K0.056MnO2 with typical cathode materials in refs. 38–45. c Cycle performance of Na0.612K0.056MnO2 and Na0.706MnO2 at 50 mA g−1. d Variation of DNa + as functions of x in NaxK0.056MnO2 determined by GITT and CV, where the gray dotted area represents the two-phase region. e CV curves of Na0.612K0.056MnO2, HC and the full battery of HC//Na0.612K0.056MnO2 at 0.1 mV s−1. f Typical charge/discharge curves of HC//Na0.612K0.056MnO2 at 50 mA g−1.
The cycle stability of Na0.612K0.056MnO2 is tested at 50 mA g−1, and the selected charge/discharge profiles of the 1st, 5th, 10th, and 100th cycles are presented in Supplementary Fig. 32. Except for the 1st charge, the charge/discharge profiles are almost overlapped. The capacity after 100 cycles is sustained for 236.2 mAh g−1, corresponding to capacity retention of 98.2% with only 0.018% loss per cycle in Fig. 6c, which is highly contrasting with the fluctuating capacities of Na0.706MnO2. This implies that the structure of Na0.612K0.056MnO2 is robust upon extraction and insertion of Na+ in cycles, as confirmed by in situ XRD in Fig. 3.
The Na+ diffusion coefficients are estimated by Galvanostatic intermittent titration technique (GITT) in Supplementary Figs. 33–37. The obtained diffusion coefficients (DNa+) for the single-phase regions of both NaxK0.056MnO2 and NaxMnO2 are in the range of 10−12–10−10 cm2s−1, and they exhibit decreasing trends as the sodiation proceeds near the two-phase regions in Fig. 6d and Supplementary Fig. 38. Because the GITT method cannot be applicable to the two-phase regions, CVs at different scan rates are used to calculate the apparent values of DNa+ in Na0.612K0.056MnO2 and Na0.706MnO2, as presented in the gray region in Fig. 6d, Supplementary Fig. 39, and Supplementary Table 19. Na0.612K0.056MnO2 exhibits faster Na+ transport with the content change of Na during charge and discharge, though there is K+ riveted between the layers. Enhanced rate capability is presented in Na0.612K0.056MnO2 in Supplementary Fig. 40, in which the reversible capacities are kept from 238.8 mAh g−1 to 211.6 and 110.2 mAh g−1 at the currents from 50 mA g−1 to 100 and 2000 mA g−1, respectively. The demonstrated good cycle performance and rate capability of Na0.612K0.056MnO2 are attributed to the reinforced structure stability and facile Na+ transport.
A full battery with P2-Na0.612K0.056MnO2 cathode and presodiated hard carbon (HC) anode was demonstrated. The performance of HC anode was firstly investigated in half battery in Supplementary Fig. 41a. As displayed in Fig. 6e, a pair of redox peaks appear at 0.036/0.113 V for HC anode, and the obtained peaks of the full battery are similar to those of Na0.612K0.056MnO2, implying reversible electrochemical reactions. The full battery delivers a specific capacity of 230.6 mAh g−1 based on the mass of active cathode material at 50 mA g−1 in Fig. 6f, corresponding to a high energy density of 314.4 Wh kg−1 based on the total mass of active anode and cathode materials. It also exhibits good cycling stability and rate performance in Supplementary Fig. 41. The electrochemical performance can be optimized by selecting high efficient HC and Na compensation method. This implies that P2-Na0.612K0.056MnO2 will be of great potential for the high-performance SIBs.
In summary, a cathode material of P2-Na0.612K0.056MnO2 has been successfully obtained with the K+ riveted in the prismatic edge-sharing sites of Nae between the MnO6-octahedra slabs. The reinforced MnO6-octahedra slabs and reduced Na+ vacancy formation energy enable more active Na+ sites and favor its facile diffusion. This leads to the highest reversible capacity of 240.5 mAh g−1, corresponding to 0.901 Na+ per formula, and energy density of 654 Wh kg−1 based on the redox of Mn3+/Mn4+ among the reported transition-metal oxide cathodes for SIBs, and good capacity retention of 98.2% after 100 cycles. The reinforced interaction in the MnO6-octahedra slabs restricts the layer gliding and ensures the robust crystal structure of P2-Na0.612K0.056MnO2, in which two-phase transition of P2 ↔ P’2 occurs only at low charge and discharge voltages, favoring the structure stability and cycle performance. This strategy to finely tune the local chemistry for high energy density and long cycle life will shed lights into the design of electrode materials for SIBs and beyond.
Methods
Materials synthesis
P2-Na0.67-xKxMnO2 was synthesized via a solid-state reaction. For the synthesis of Na0.612K0.056MnO2, NaCH3COOH (99%, Alfa, 12.54 mmol, 10% in excess), K2CO3 (99%, Alfa, 2.1 mmol, 5% in excess), and MnO2 (99%, Alfa, 20 mmol) were mixed in a planetary ball mill (QM-3SP2) at 400 rpm for 12 h in the presence of a small amount of acetone. The as-synthesized precursors were dried at 80 °C for 12 h, and then pressed into a pallet under 20 MPa. It was heated at 500 °C for 2 h and 900 °C for 10 h in air at 5 °C/min. Then, it was cooled down to 200 °C at 5 °C/min and naturally to room temperature, and stored in an argon-filled glovebox. Similar processes were applicable to the synthesis of Na0.706MnO2 except the addition of K2CO3.
Electrochemical measurements
Coin cells (CR2032) were assembled in an argon-filled glovebox for all the electrochemical tests. The working electrode was prepared by coating the mixture of active material (80 wt.%), Super P (10 wt.%), and polytetrafluoroethylene (10 wt.%) in N-methyl-2-pyrrolidone onto an Al foil. The loading mass of active material in each electrode pellet of 12.0 mm in diameter was ~3.0 mg cm−2. For half battery, sodium foil was used as the anode, and 1.0 M NaPF6 in PC containing 5 wt.% of FEC was employed as the electrolyte with glass fiber filter papers as the separator. The charge/discharge tests and Galvanostatic intermittent titration technique (GITT) were carried out on a Land CT2001A battery test system (Land, Wuhan, China) in a voltage range of 1.8–4.3 V at 25 °C. GITT was measured by applying the repeated current pulses for 30 min at a current density of 10 mA g−1, followed by relaxation for 1.5 h. CV experiments were performed within the same potential range at 0.1 mV s−1. CV was carried out on a Solartron 1470E electrochemical workstation in a voltage range of 1.8–4.3 V. The full battery was assembled with P2-Na0.612K0.056MnO2 as the cathode, HC as the anode, and 1.0 M NaPF6 in PC containing 5 wt.% of FEC as the electrolyte, respectively. In order to supplement sufficient Na+ in HC before assembling full battery, the HC electrode was obtained by disassembling the half battery in the glove box after half-discharging at 50 mA g−1. The mass ratio of Na0.612K0.056MnO2/HC is around 1.2, corresponding to 4% excess of anode capacity. The charge/discharge and CV tests were carried out at 25 °C in a voltage range of 1.0–4.3 V.
Material characterizations
The chemical composition of the electrodes was determined by an inductively coupled plasma-optical emission spectrometer (ICP-OES, SPECTRO-BLUE). XRD was collected on Rigaku SmartLab equipped with a Cu Kα radiation source. Rietveld refinement was conducted with the Fullprof software46. The PDF analysis was carried out based on X-ray scattering data measured at the 11-ID-B beamline of the Advanced Photon Source at Argonne National Laboratory. High energy X-rays (λ = 0.1173 Å) were used to collect data to high values of momentum transfer (Q ~ 30 Å−1). Diffraction images were integrated within fit2D to obtain one-dimensional diffraction data47. Pair distribution functions, G(r), were extracted from the data within PDFgetX348, after correcting for background and Compton scattering. Mn K-edge X-ray absorption fine structure (XAFS) results were collected at the beamline 8C in Pohang Accelerator Laboratory (PAL). The XAFS data were collected by fluorescence mode and processed through Demeter software package49. The extended x-ray absorption fine structure (EXAFS) region was k3 weighted and Fourier-transformed in k-ranges of 3.0–10.0 Å−1. Schematic representations of the synthesized samples were obtained by using the VESTA software50. The morphology was examined by SEM (JEOL JSM-7500F, AEMC, 5 kV). The HRTEM images, SAED patterns and EDS mappings were recorded by TEM (FEI Taosl F200X G2, AEMC, 200 kV). HAADF and ABF images were obtained on a JEM-AR200F STEM with an accelerating voltage of 200 kV with cold filed-emission gun and double hexapole Cs correctors (CEOS GmbH, Heidelberg, Germany). Dynamic secondary ion mass spectroscopy (SIMS) was carried out on a Cameca IMS-5FE7 system using Cs+ primary ions with a beam current of 3 nA. Solid-state 39K NMR spectra were obtained on a JNM-ECZ600R widebore spectrometer.
DFT calculation
The crystal structures of Na0.500K0.055MnO2, Na0.220K0.055MnO2, and Na0.275MnO2 were simulated using Vienna ab-initio simulation package (VASP). The generalized gradient approximation (GGA) of exchange-correlation energy, Perdew-Burke-Eznerhof (PBE) functional, was used with its corresponding projector augmented-wave pseudopotentials31,32,33,34. A Hubbard U term of 3.9 is adopted to better describe the strong correlation of Mn 3d electrons. The slight difference between the simulated formulas and the obtained composition is due to that the number of K and Na atoms can only be integral in a unit cell, and such difference can be reasonably ignored. All optimization calculations adopted a 4 × 4 × 4 Monkhorst-Pack51 k-point grid and a cutoff energy of 400 eV, and a higher cutoff of 450 eV and a 6 × 6 × 4 k-point grid were applied for DOS and charge calculations for enhanced accuracy. First-principle molecular dynamics calculations, which adopt an NVT ensemble at 1000 K, were carried out using a single Γ point to balance the accuracy and cost. Atomic positions and cell vectors were fully optimized until all force components were less than 0.02 eV Å−1. The trajectory of MD simulation was further analyzed using Rigorous Investigation of Networks Generated using Simulations (R.I.N.G.S.) code to obtain MSD statistics. The COHP calculations were carried out using Local-Orbital Basis Suite towards Electronic-Structure Reconstruction (LOBSTER) code. The diffusion energy barriers are calculated using climbing-image nudged elastic band (CI-NEB) method with a single Γ point.
Data availability
The data that support the findings of this study are available from the corresponding author upon reasonable request.
References
House, R. A. et al. Superstructure control of first-cycle voltage hysteresis in oxygen-redox cathodes. Nature 577, 502–508 (2020).
Zhang, K. et al. Manganese based layered oxides with modulated electronic and thermodynamic properties for sodium ion batteries. Nat. Commun. 10, 5203 (2019).
Li, Q. et al. Both cationic and anionic co-(de)intercalation into a metal-oxide material. Joule 2, 1134–1145 (2018).
Lee, G.-H. et al. Reversible anionic redox activities in conventional LiNi1/3Co1/3Mn1/3O2 Cathodes. Angew. Chem. Int. Ed. 59, 8681–8688 (2020).
Liu, Y. et al. Mitigation of Jahn-Teller distortion and Na+/vacancy ordering in distorted manganese oxide cathode material by Li substitution. Chem. Sci. https://doi.org/10.1039/D0SC05427E (2020).
Ren, M., Fang, H., Wang, C., Li, H. & Li, F. Advances on manganese-oxide-based cathodes for Na-ion batteries. Energy Fuels 34, 13412–13426 (2020).
Wang, C., Du, D., Song, M., Wang, Y. & Li, F. A high-power Na3V2(PO4)3-Bi sodium-ion full battery in a wide temperature range. Adv. Energy Mater. 9, 1900022 (2019).
Wang, P. F. et al. An abnormal 3.7 volt O3-type sodium-ion battery cathode. Angew. Chem. Int. Ed. 57, 8178–8183 (2018).
Zhao, C. L. et al. Ti Substitution facilitating oxygen oxidation in Na2/3Mg1/3Ti1/6Mn1/2O2 cathode. Chem 5, 2913–2925 (2019).
You, Y. et al. Insights into the improved high-voltage performance of Li-incorporated layered oxide cathodes for sodium-ion batteries. Chem 4, 2124–2139 (2018).
Lei, K. et al. Dual interphase layers in situ formed on a manganese-based oxide cathode enable stable potassium storage. Chem 5, 3220–3231 (2019).
Li, X. et al. Direct visualization of the Jahn-Teller effect coupled to Na ordering in Na5/8MnO2. Nat. Mater. 13, 586–592 (2014).
Vergnet, J., Saubanère, M., Doublet, M.-L. & Tarascon, J.-M. The structural stability of P2-layered Na-based electrodes during anionic redox. Joule 4, 420–434 (2020).
Kobayashi, W. et al. Thermal expansion in layered NaxMO2. Sci. Rep. 8, 3988 (2018).
Zhao, C. L. et al. Revealing high Na-content P2-type layered oxide as advanced sodium-ion cathodes. J. Am. Chem. Soc. 142, 5742–5750 (2020).
Xiang, X., Zhang, K. & Chen, J. Recent advances and prospects of cathode materials for sodium-ion batteries. Adv. Mater. 27, 5343–5364 (2015).
Kumakura, S., Tahara, Y., Kubota, K., Chihara, K. & Komaba, S. Sodium and manganese stoichiometry of P2-Type Na2/3MnO2. Angew. Chem. Int. Ed. 55, 12760–12763 (2016).
Kulka, A. et al. Influence of Na/Mn arrangements and P2/P’2 phase ratio on the electrochemical performance of NaxMnO2 cathodes for sodium-ion batteries. J. Mater. Chem. A 8, 6022–6033 (2020).
Clément, R. J. et al. Structurally stable Mg-doped P2-Na2/3Mn1-yMgyO2 sodium-ion battery cathodes with high rate performance: insights from electrochemical, NMR and diffraction studies. Energy Environ. Sci. 9, 3240–3251 (2016).
Kumakura, S., Tahara, Y., Sato, S., Kubota, K. & Komaba, S. P’2-Na2/3Mn0.9Me0.1O2 (Me = Mg, Ti, Co, Ni, Cu, and Zn): correlation between orthorhombic distortion and electrochemical property. Chem. Mater. 29, 8958–8962 (2017).
Yabuuchi, N. et al. P2-type Nax[Fe1/2Mn1/2]O2 made from earth-abundant elements for rechargeable Na batteries. Nat. Mater. 11, 512–517 (2012).
Yoshida, J. et al. New P2-Na0.70Mn0.60Ni0.30Co0.10O2 layered oxide as electrode material for Na-ion batteries. J. Electrochem. Soc. 161, A1987–A1991 (2014).
Paulsena, J. M. & Dahn, J. R. Studies of the layered manganese bronzes, Na2/3[Mn1-xMx]O2 with M=Co, Ni, Li, and Li2/3[Mn1-xMx]O2 prepared by ion-exchange. Solid State Ion. 126, 3–24 (1999).
Pang, W. et al. P2-type Na2/3Mn1-xAlxO2 cathode material for sodium-ion batteries: Al-doped enhanced electrochemical properties and studies on the electrode kinetics. J. Power Sources 356, 80–88 (2017).
Wang, P.-F., You, Y., Yin, Y.-X. & Guo, Y.-G. Layered oxide cathodes for sodium-ion batteries: phase transition, air stability, and performance. Adv. Energy Mater. 8, 1701912 (2018).
Song, J. et al. Role of oxygen vacancies on the performance of Li[Ni0.5-xMn1.5+x]O4 (x = 0, 0.05, and 0.08) spinel cathodes for lithium-ion batteries. Chem. Mater. 24, 3101–3109 (2012).
Clément, R. J. et al. Structurally stable Mg-doped P2-Na2/3Mn1-yMgyO2 sodium-ion battery cathodes with high rate performance: insights from electrochemical, NMR and diffraction studies. Energy Environ. Sci. 9, 3240–3251 (2016).
Bianchini, M., Wang, J., Clément, R. & Ceder, G. A first-principles and experimental investigation of nickel solubility into the P2 NaxCoO2 sodium-ion cathode. Adv. Energy Mater. 8, 1801446 (2018).
Scheler, U., Blümich, B. & Spiess, H. W. Spinning sidebands from chemical shift anisotropy in 13C MAS imaging. Solid State Nucl. Magn. Reson. 2, 105–110 (1993).
Kövér, L. et al. Chemical effects on F KLL Auger spectra in fluorides. J. Vac. Sci. Technol. A 19, 1143–1149 (2001).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. J. Phys. Rev. B 54, 11169–11186 (1996).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Kang, K., Meng, Y. S., Bréger, J., Grey, C. P. & Ceder, G. Electrodes with high power and high capacity for rechargeable lithium batteries. Science 311, 977–980 (2006).
Chen, X. et al. Super charge separation and high voltage phase in NaxMnO2. Adv. Funct. Mater. 28, 1805105 (2018).
Li, X. et al. Jahn-Teller assisted Na diffusion for high performance Na ion batteries. Chem. Mater. 28, 6575–6583 (2016).
Li, Y. M. et al. Air-stable copper-based P2-Na7/9Cu2/9Fe1/9Mn2/3O2 as a new positive electrode material for sodium-ion batteries. Adv. Sci. 2, 1500031 (2015).
Talaie, E., Duffort, V., Smith, H. L., Fultz, B. & Nazar, L. F. Structure of the high voltage phase of layered P2-Na2/3-z[Mn1/2Fe1/2]O2 and the positive effect of Ni substitution on its stability. Energy Environ. Sci. 8, 2512–2523 (2015).
Rong, X. H. et al. Anionic redox reaction-induced high-capacity and low-strain cathode with suppressed phase transition. Joule 3, 503–517 (2019).
Ma, C. et al. Exploring oxygen activity in the high energy P2-type Na0.78Ni0.23Mn0.69O2 cathode material for Na-ion batteries. J. Am. Chem. Soc. 139, 4835–4845 (2017).
Luo, C., Langrock, A., Fan, X., Liang, Y. & Wang, C. P2-type transition metal oxides for high performance Na-ion battery cathodes. J. Mater. Chem. A 5, 18214–18220 (2017).
Yabuuchi, Y. et al. New O2/P2-type Li-excess layered manganese oxides as promising multi-functional electrode materials for rechargeable Li/Na batteries. Adv. Energy Mater. 4, 1301453 (2014).
Jian, Z. et al. Atomic structure and kinetics of NASICON NaxV2(PO4)3 cathode for sodium-ion batteries. Adv. Funct. Mater. 24, 4265–4272 (2014).
Kang, W. et al. Copper substituted P2-type Na0.67CuxMn1-xO2: a stable high-power sodium-ion battery cathode. J. Mater. Chem. A 3, 22846–22852 (2015).
Rodríguez-Carvajal, J. Recent advances in magnetic structure determination by neutron powder diffraction. Phys. B Condens. Matter 192, 55–69 (1993).
Hammersley, A. P. Fit2D version 9.129 reference manual version 3.1, ESRF Inter. Rep. No. ESRF98HA01T (1998).
Juhás, P. et al. PDFgetX3: a rapid and highly automatable program for processing powder diffraction data into total scattering pair distribution functions. J. Appl. Crystallogr. 46, 560–566 (2013).
Ravel, B. & Newville, M. ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT. J. Synchrotron. Radiat. 12, 537–541 (2005).
Momma, K. & Izumi, F. VESTA 3 for three-dimensional visualization of crystal, volumetric and morphology data. J. Appl. Crystallogr. 44, 1272–1276 (2011).
Monkhorst, H. J. & Pack, J. D. Special points for brillonin-zone integrations. Phys. Rev. B 13, 5188–5192 (1976).
Acknowledgements
Financial supports from National Natural Science Foundation of China (grant No. 21835004, 21822506, and 51671107), Tianjin Natural Science Foundation (grant No. 19JCJQJC62400), and the 111 project of B12015 are acknowledged. Dedicated to the 100th anniversary of Chemistry at Nankai University.
Author information
Authors and Affiliations
Contributions
F.L. conceived the concept and supervised the work; C.W. designed and performed the experiments; L.L. and J.C. performed the DFT calculations; L.L. and S.Z. analyzed the DFT data; C.W. and Y.L. carried out in situ and ex situ XRD; H.Y. and Y.Y. carried out the PDF experiments; S.L., G.-H.L., and Y.-M.K. performed the XAFS analyses; R.L. measured and analyzed SIMS data; F.L. and C.W. wrote the manuscript; all the authors contributed to discussion and revision of the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wang, C., Liu, L., Zhao, S. et al. Tuning local chemistry of P2 layered-oxide cathode for high energy and long cycles of sodium-ion battery. Nat Commun 12, 2256 (2021). https://doi.org/10.1038/s41467-021-22523-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-22523-3
- Springer Nature Limited
This article is cited by
-
Regulating bond structure and local electronic state optimizes the cycling stability of layered sodium-ion cathode materials
Applied Physics A (2024)
-
Advances in doping strategies for sodium transition metal oxides cathodes: A review
Frontiers in Energy (2024)
-
Layered oxide cathodes for sodium-ion batteries: microstructure design, local chemistry and structural unit
Science China Chemistry (2024)
-
Cycling performance of layered oxide cathode materials for sodium-ion batteries
International Journal of Minerals, Metallurgy and Materials (2024)
-
Entropy-modulated and interlayer-doped transition metal layered oxides enable high-energy-density sodium-ion capacitors
Nano Research (2024)