Abstract
Graphene-based moiré superlattices have recently emerged as a unique class of tuneable solid-state systems that exhibit significant optoelectronic activity. Local probing at length scales of the superlattice should provide deeper insight into the microscopic mechanisms of photoresponse and the exact role of the moiré lattice. Here, we employ a nanoscale probe to study photoresponse within a single moiré unit cell of minimally twisted bilayer graphene. Our measurements reveal a spatially rich photoresponse, whose sign and magnitude are governed by the fine structure of the moiré lattice and its orientation with respect to measurement contacts. This results in a strong directional effect and a striking spatial dependence of the gate-voltage response within the moiré domains. The spatial profile and carrier-density dependence of the measured photocurrent point towards a photo-thermoelectric induced response that is further corroborated by good agreement with numerical simulations. Our work shows sub-diffraction photocurrent spectroscopy is an exceptional tool for uncovering the optoelectronic properties of moiré superlattices.
Similar content being viewed by others
Introduction
The photoresponse of semiconductor heterostructures is at the heart of modern optoelectronics1,2. A general prerequisite for photo-induced currents is the lack of an inversion centre, whether it is extrinsically defined by doping inhomogeneities in the form of PN junctions, or due to a broken inversion symmetry in the crystal structure. In this regard, the structures of moiré superlattices3,4,5,6,7 are well suited for photoresponse applications, since the crystal symmetry can be easily reduced by a twist-angle (θ)-induced atomic-scale reconstruction8,9. Minimally twisted bilayer graphene (mTBG, θ < 0.1°) represents such a class of moiré superlattices, in which lattice reconstruction of the twisted bilayer is energetically favourable and generates alternating triangular domains of AB/BA Bernal-stacked regions separated by narrow domain wall networks8,10,11 (Fig. 1a). Whereas the AB/BA regions locally are identical to Bernal stacked bilayer graphene, the atomic registry between AB sublattices in each layer changes smoothly through the domain walls, dramatically changing the local electronic properties over length scales of ~10 nm10. From the perspective of photoresponse, those sharp changes in electronic spectra can serve as local junctions, thus providing an intrinsic photoactive region created by the moiré superlattice. Although these domain wall networks have already been shown to strongly influence the DC transport12,13,14,15 and optical properties16,17,18,19,20,21,22,23 of mTBG, their optoelectronic properties have not yet been explored. In part, this is challenging due to the sub-diffraction scale of the moiré structure that makes it difficult to resolve superlattice scale features in typical far-field photoresponse experiments24,25.
In this work, we perform near-field photocurrent nanoscopy in mTBG. With this, we probe nanoscale photocurrents in mTBG and observe a unique photo-thermoelectric effect26,27,28,29 governed by the symmetry breaking of the domain wall network. Our measurements are supported by simulations of the spatial photocurrent profile in our devices that shows the photoresponse originates from microscopic variations in the Seebeck coefficient intrinsic to the moiré lattice. By varying the doping, we observe anomalous sign reversals in the photocurrent that hints to the importance of strain gradients in mTBG. In addition, we observe a localised photoresponse close to the domain walls of the moiré unit cell that is attributed to additional electron heating from propagating polaritons.
Results
Experimental techniques and device characterisation
To study the photoresponse of our samples, we employed infrared scanning near-field photocurrent microscopy30,31,32. The technique involves local photoexcitation of carriers using a scattering-type scanning near-field optical microscope33 (s-SNOM) combined with an electrical current read out at one of the device contacts (see “Methods” section). For local photoexcitation, we focus infrared light (with photon energy ~100–200 meV) onto a sharp tip (Fig. 1a), inducing a strongly localised electric field at the tip apex in an area similar to the tip radius (20–30 nm). By scanning the tip around our sample, we build spatial maps of the photocurrent generated by this localised field. We note that in some cases we measured photovoltage, which is linearly related to the photocurrent through the device resistance R as IPC = VPV/R. In this way, we can measure the photoresponse between two pairs of contact simultaneously. On the same sample, we measured the near-field optically scattered light from the tip using interferometric detection34 (see “Methods” section). This provides a complementary characterisation of the local optical response in our samples.
The studied mTBG samples were fabricated using the tear and stack method7,35 (see “Methods” section). In brief, the heterostructure structure consists of a Van der Waals stack of mTBG fully encapsulated with hexagonal boron-nitride (hBN) and deposited on top of a Si/SiO2 wafer36. A sample (Fig. 1b) also contains gold contacts for photocurrent/photovoltage read out and simultaneous electrostatic gating of the channel with the silicon backgate.
To characterise the local structure in our devices, we first measured the near-field optical scattering signal of our samples. Figure 1c shows a near-field image of the optically scattered light measured at high doping n ~ 5 × 1012 cm−2 in our mTBG sample (see Supplementary Note 1 for doping estimation). It reveals a set of bright fringes forming a triangular network of alternating AB/BA domains; the purple/yellow triangles highlight two neighbouring AB/BA domains. These features have already been studied extensively in near-field scattering experiments and were attributed to enhanced optical conductivity at the domain walls20,21,22 of mTBG. Their observation in our experiment thus confirms the presence of atomic reconstruction8 expected in mTBG and allows direct structural mapping of the moiré lattice in our samples.
Photoresponse in mTBG
Figure 1d shows a near-field photocurrent map of our sample measured in the mTBG region with an excitation energy E = 188 meV, which exhibits a number of interesting features. First, a clear periodicity in the photocurrent is observed throughout the entire sample. It can be easily seen by following the zeros in photocurrent (white lines and white features) that trace the periodicity intrinsic to mTBG. Notably, the periodicity varies from ~100 to ~1000 nm in different regions of the device. We attribute this behaviour to local variations in the twist angle (θ ~ 0.1–0.01°) inherent to twisted moire superlattices37,38. Second, the photocurrent exhibits alternating domains of a negative response (blue regions) and positive response (red regions). This is most clearly seen in the device region with the largest moiré periodicity (centre area in Fig. 1d). Third, in these larger areas, a second fringe can be seen running parallel to the domain walls. This double step-like feature closely resembles that of propagating polaritons typically observed in near-field scattering and photocurrent experiments on graphene31,39,40 and hBN41,42 close to crystal edges, and will be discussed in detail below. Importantly, this periodic structure in the photocurrent was characteristic in our other studied mTBG devices (Supplementary Note 2).
The spatial pattern of photoresponse is highly sensitive to the position of measurement contacts with respect to the moiré periodicity. Figure 2a shows a zoomed photovoltage map of the region with the largest domains in Fig. 1d. This triangular pattern resembles the moiré pattern of mTBG (Fig. 1a), with zero crossings seemingly tracing the domain wall network of the moiré superlattice. However, when comparing our photoresponse data with our optical scattering data (Fig. 1c), we find that the actual structure of the moiré lattice is rather different. The purple/yellow shaded triangles in Fig. 2a highlight the positions and orientation of two neighbouring AB/BA domains measured by optical scattering (see corresponding triangles in Fig. 1c). From this, we can see that this measurement does not capture the entire structure of the moiré lattice, and we lose a set of domain walls at ~45° to those observed in Fig. 2a. Strikingly, those additional domain walls appear simply by measuring between a different pair of contacts (Fig. 2b). In this scheme, the actual structure of the moiré lattice is clearly visible and the spatial profile of the photoresponse is more complex than anticipated. For example, we find that the measured photovoltage exhibits sign reversals not only at domain wall boundaries (Fig. 2c) but also within the AB/BA stacked domains. Moreover, the spatial patterns of the photoresponse within each moiré unit cell varies significantly between AB and BA stacking configurations.
To elucidate the role and mechanism of photoresponse in mTBG, we studied the gate-voltage dependence of the photocurrent within the moiré domains. In Fig. 2d, we plot the line trace of the measured photocurrent made across domain walls (see black dashed line in Fig. 2a) for different gate voltages VG – VD, where VD is the position of the charge neutrality point (CNP) determined from the gate dependence of the optically scattered signal (Supplementary Note 3). The positions of domain walls are marked by the black arrows. The first thing to note is that the gate-voltage dependence of the photoresponse is sensitive to the position of the excitation spot within the moiré unit cell. On top of that, it is non-monotonic, such that for some excitation positions it exhibits up to three sign changes. Figure 2e plots line cuts of the gate-voltage dependence for two excitation positions (marked by coloured dashed lines in Fig. 2d). On one hand, the observed non-monotonic behaviour strongly resembles that of the photo-thermoelectric effect in graphene26,27,29 that is strongest for lower n and exhibits sign reversals around CNP. This is not surprising considering the unit cell of mTBG is comprised mostly of AB Bernal stacked bilayer graphene, whose photoresponse is dominated by the photo-thermoelectric effect in the presence of spatially varying Seebeck coefficients26,27,29. On the other hand, some other features such as the two additional sign changes away from charge neutrality, which depend on the spatial location, are rather peculiar.
Photo-thermoelectric effect
With Fig. 2 in mind, we constructed a model based on the photo-thermoelectric effect (PTE) to describe the observed photocurrent features in our device. Photocurrent generation due to the PTE proceeds in four steps. First, the electric field generated by the tip induces an oscillating current density in the sample at the excitation frequency \(\omega _{{{{\mathrm{ph}}}}}\). Second, this oscillating current causes Joule heating of the electron gas. The power density produced is proportional to the square of the current and has a rectified component \(Q( {{{{\mathbf{r}}}},{{{\mathbf{r}}}}_{{{{\mathrm{tip}}}}}} )\), where r is the position and rtip the position of the tip. Third, the generated heat spreads in the sample on a characteristic length scale referred to as the cooling length28 (Lcool) before being dissipated to the substrate. Finally, since the heat transport is coupled to the charge transport via the Seebeck–Peltier effect, the heat flux is able to generate a net electric current in the presence of Seebeck coefficient gradients. The current and heat flux are governed (at least for small incident power) by a set of linear equations with respect to the source term \(Q( {{{{\mathbf{r}}}},{{{\mathbf{r}}}}_{{{{\mathrm{tip}}}}}} )\). As a consequence, the PTE-induced photovoltage \(V_{{{{\mathrm{PTE}}}}}^{(m)}\) at the contact m, with respect to a grounded contact used as a common reference, is then given (see details in Supplementary Note 4) by a linear relation of the type
where \({{{\mathcal{R}}}}_{{{{\mathrm{PTE}}}}}^{\left( m \right)}({{{\mathbf{r}}}})\) is the photovoltage responsivity function that encodes the PTE response of the system. An analogous formula holds for photocurrents. In absence of strong resonant features, for example plasmonic excitations, the response of the system at the energy \(\hbar \omega _{{{{\mathrm{ph}}}}}\), and therefore \(Q( {{{{\mathbf{r}}}},{{{\mathbf{r}}}}_{{{{\mathrm{tip}}}}}} )\), rapidly decays with \(|{{{\mathbf{r}}}} - {{{\mathbf{r}}}}_{{{{\mathrm{tip}}}}}|\). This means that \(V_{{{{\mathrm{PTE}}}}}^{(m)} \propto {{{\mathcal{R}}}}_{{{{\mathrm{PTE}}}}}^{\left( m \right)}( {{{{\mathbf{r}}}}_{{{{\mathrm{tip}}}}}} )\) and the photovoltage (or photocurrent) maps are essentially measuring the responsivity (apart from the convolution with a spread function due to the finite tip dimension).
To gain some intuition into the origin of the spatial profile of the photoresponse generated in our devices, we consider the form of the photovoltage responsivity function for a one-dimensional device (see derivation in Supplementary Note 5). This reads
where W is the width of the device and κ its electronic thermal conductivity. In this example (in open-circuit configuration), an infinitely sharp tip creates a spatial profile of electron temperature (Fig. 3a) in the form \(\delta T(x) \equiv T\left( x \right) - T_0 \propto e^{ - \left| {x - x_{{{{\mathrm{tip}}}}}} \right|/L_{{{{\mathrm{cool}}}}}}\), with T0 being the temperature of the substrate. From (2), we clearly see that the PTE requires an inhomogeneous Seebeck coefficient S with a gradient parallel to the path between measurement contacts. In addition to that, the responsivity decays away from the Seebeck coefficient fluctuations on a length scale Lcool, since that is the distance that heat is able to travel in the sample. Finally, in a system with particle-hole symmetry, \({{{\mathcal{R}}}}_{{{{\mathrm{PTE}}}}}(x)\) is an odd function of the electronic density because S(x) is odd. This behaviour is clearly observed in the gate-voltage dependence of the measured photoresponse (Fig. 2e), where the photoresponse changes sign around the Dirac point due to a change in sign of the carriers’ charge.
In the moiré superlattice of mTBG, the local layer alignment transitions smoothly in the region of the domain walls, which is expected to cause local gradients in the Seebeck coefficient, as required for the PTE. To corroborate this, we calculated (see Supplementary Note 6 and “Methods” section for full details on the calculation) the Seebeck coefficient of bilayer graphene as a function of the layer alignment in the Relaxation Time Approximation43 and mapped the local alignment to the distance from a domain wall using the result in ref. 10. By this procedure, we obtained the spatial profile of the Seebeck coefficient across a domain wall, as depicted in Fig. 3b. This shows that the Seebeck coefficient dips sharply at the domain walls of the moiré superlattice. By considering Eq. (2) and recalling that \(V_{{{{\mathrm{PTE}}}}}^{(m)} \propto {{{\mathcal{R}}}}_{{{{\mathrm{PTE}}}}}^{\left( m \right)}\), we plot the expected photovoltage profile in the vicinity of the domain walls (Fig. 3c). Notably, the photovoltage follows a non-monotonic dependence with the position through the domain wall, changing sign as it crosses the middle of the domain wall. Such behaviour can indeed be seen in our data along certain domain walls (Fig. 2c).
Although the one-dimensional model (Fig. 3c) describes well the sign changes across certain domain walls (Fig. 2c), the full two-dimensional spatial map can be more complex as one must consider the photocurrent contributions from different domain walls due to the finite cooling length Lcool. The full spatial profile of \({{{\mathcal{R}}}}_{{{{\mathrm{PTE}}}}}^{\left( m \right)}({{{\mathbf{r}}}})\) can be calculated if the entire measurement geometry of the system (Fig. 3d) and the spatial profile of the Seebeck coefficient (Fig. 3e) are known. We perform this calculation using the Finite Element Method (see Supplementary Note 4 and “Methods” section for details). The calculation is greatly simplified thanks to an elegant reciprocity relation44,45.
Figure 3f, g plots the simulated photocurrent for the two measured contact configurations (Fig. 3d) in the same area corresponding to the measurement in Fig. 2a and b, respectively. The simulations are carried out at a fixed doping n = 1 × 1012 cm−2. Comparing Fig. 3f, g with Fig. 2a, b, we find good agreement between our measurements and the simulations. Not only do our simulations accurately capture the spatial sign changes observed in our sample, but also the differing local photoresponse between AB and BA stacked regions (Figs. 2b and 3g). Importantly, the simulations also capture the strong directional effect observed. To understand this behaviour, we recall that the PTE can generate a global current only in regions where the gradients of the Seebeck coefficient contain a part running parallel to the projection of current flows between contacts. This means that the domain walls perpendicular to the projection of current flows contribute strongest to the measured photocurrent and are minimum for those that run parallel. The current projections for the two contact configurations are sketched in Fig. 3d, where the red and white lines depict projections for the contact configuration of Fig. 2a and b, respectively. They are also drawn in Fig. 3e to illustrate their orientation relative to the domain wall networks measured in Fig. 2a, b. In the first configuration (red lines) we find that some domain walls run almost parallel to the current projections. Therefore, photoexcitation at these domain walls does not contribute to the globally measured current, and they remain completely hidden in our measurement (Fig. 2a). Whereas in the second case (white lines), there is always a component perpendicular to all sets of domain walls such that they all contribute to the globally measured current (Fig. 2b). This result also demonstrates the crucial importance of measurement geometry46 in understanding the nanoscale photoresponse of solid-state crystals.
Good agreement between the simulations and experiment points towards a photo-thermoelectric dominated photoresponse in the moiré lattice of mTBG. Indeed, qualitatively the spatial sign changes across domain walls and doping dependent sign changes around the CNP are well described by our photo-thermoelectric model; we attribute the slight shift of zero crossings from VG – VD = 0 (Fig. 2d, e) to additional photocurrent mechanisms that may play a role at the CNP47. Even the additional sign changes observed away from CNP (see the purple trace in Fig. 2e), can be explained within the framework of the PTE by considering an enhanced Seebeck coefficient at the domain walls with respect to the calculated one (Supplementary Note 7). That said, it does not accurately describe the spatial dependence of the gate-voltage response, specifically, the sign reversal of the photoresponse within the moiré domains shifting with applied gate-voltage (dashed line in Fig. 2d). This behaviour points towards a spatially varying parameter not considered in our model, for example, a spatially varying Seebeck coefficient within the AB/BA domains themselves that is not localised at the domain walls. Such behaviour might be expected in the case that lattice reconstruction in mTBG imposes significant strain in the AB regions48, which might enhance the Seebeck coefficient of bilayer graphene locally49. A simplified model, which includes a spatially varying Seebeck within the AB/BA domains, is presented in Supplementary Note 7 and shows similar features as the experimental data.
Another peculiarity in the data is the high doping behaviour (|VG − VD| > 40 V), in which the spatial sign changes across domain walls become nearly absent (Fig. 2d) and the spatial profile resembles that of a constant background, which changes sign when changing carrier polarity. This is illustrated in Fig. 4a that plots a photocurrent map for a doping n ~ 4 × 1012 cm−2, where we observe large areas of the moiré lattice exhibiting either a constant positive or negative photoresponse. In the simplest case, we might attribute this additional photocurrent to nearby PN junctions caused by deformations/stacking faults in our heterostructure. However, our measurements of the cooling length from these interfaces (Lcool = 240 nm) show a fast decay of such contributions (Supplementary Note 8). Hence, the data suggests another photocurrent mechanism might be present in mTBG. For example, we considered the possibility of photogalvanic currents (Supplementary Note 9). Further work is required to understand these additional background phenomena.
Photoresponse from hyperbolic phonon–polaritons
Finally, we address the double step-like feature that is observed close to the domain walls (Figs. 1d, 2d and 4a). At first inspection, those features resemble that of propagating polaritons in graphene/hBN heterostructures typically observed in s-SNOM experiments39,40,41,50,51. As shown in this work, the domain walls also act as local photoactive junctions which would thus enable thermoelectric detection of polariton modes42,52. For the investigation, we studied the wavelength dependence of the double-step feature focussing on energies 150–200 meV where it appeared strongest (Fig. 1d). Figure 4b plots the photoresponse as a function of excitation wavelength for a line trace made across several domain walls in one of our mTBG samples. For all energies, we observe the expected photocurrent profile generated at domain walls by the photo-thermoelectric effect (Fig. 3c). However, we also observe an additional feature that disperses with energy in the specific range 180–200 meV but is completely absent for lower energies. This spectral range corresponds to the upper reststrahlen band of hBN and suggests those features originate from propagating phonon–polaritons in hBN.
For further analysis, we compare in Fig. 4c line traces of the measured photoresponse (green arrow in Fig. 4b) at different energies after subtraction of a smooth background. Note, whereas we plot the modulus to make analysis easier, we draw attention to the fact that the actual response is a reduction in the measured photocurrent compared to the background (Fig. 4b). Following this procedure for all traces in Fig. 4b, we plot in Fig. 4d the distance between peaks and the domain wall as a function of excitation energy (red dots). When the excitation energy is inside the reststrahlen bands of hBN, the s-SNOM tip can excite hyperbolic phonon–polaritons that travel in hBN as collimated rays that propagate with a fixed angle \(\theta _{{{{\mathrm{BN}}}}} = {{{\mathrm{tan}}}}^{ - 1}\left[ {{{{\mathrm{Re}}}}\left( {\frac{{i\sqrt { \in _{x,y}} }}{{\sqrt { \in _z} }}} \right)} \right]\) relative to the vertical direction53 (\(\in _i\) being the components of the dielectric function of hBN). This produces a series of maxima of electric field intensity close to the surface separated by a distance λray = 2t·tanθBN, where t is the total thickness of the hBN. We note our photocurrent measurements are more sensitive to ray-like modes rather than the first eigenmode typically observed in s-SNOM experiments41,54,55 (see details in Supplementary Note 10). Following this insight, we fit the distance d between the dispersing feature and the DW (Fig. 4d) with the function \(d\left( \omega \right) = a\lambda _{{{{\mathrm{ray}}}}}\left( \omega \right)\), with a as a proportionality constant. The fit yields \(a = 0.63\) and shows good agreement with experimental data (Fig. 4d) providing strong evidence that the dispersing feature is caused by hBN hyperbolic phonon–polaritons. We observe that \(a\, < \, \frac{{t_{{{{\mathrm{top}}}}} + 2t_{{{{\mathrm{bot}}}}}}}{{2t_{{{{\mathrm{top}}}}} + 2t_{{{{\mathrm{bot}}}}}}} = 0.95\) (hBN ray passing once through the top-hBN and twice through the bottom hBN), which suggests that phonon-polariton rays launched by the s-SNOM tip propagate beyond the DW into neighbouring domains. This is consistent with the fact that the dispersing feature traces a reduction in the measured photocurrent because propagating phonon–polaritons heat the mTBG on the side of the domain wall opposite to the tip (sketched in the inset of Fig. 4d). This produces photocurrents that counteracts the one generated by the heat directly produced by the tip, leading to a small reduction of the photocurrent signal (Fig. 4b). We note that Figs. 2d and 4a also show a fainter double-step feature, while the data are taken outside the reststrahlen bands of hBN. We speculate that the double-step feature, in this case, might originate from heating by propagating plasmon polaritons that have been shown to scatter/reflect from domain walls of mTBG20,21,22.
Discussion
To conclude, we show that near-field photocurrent spectroscopy is a valuable tool for studying the optoelectronic properties of moiré superlattices. Our moiré-scale resolved measurements reveal a spatially rich photoresponse governed by the symmetries of the reconstructed lattice that would go unnoticed in typical far-field photoresponse experiments. Good agreement of our simulations with experimental data shows the importance of hot carriers in the photoresponse of mTBG and, at the same time, shows the crucial link between global measurements and local excitation in photocurrent experiments. Our work should thus motivate further near-field photocurrent studies on related moiré superlattices including twisted transition metal dichalcogenides9 and small-angle twisted bilayer graphene. In the course of preparing this manuscript, we became aware of related work56.
Methods
Device fabrication
The mTBG device discussed in the main text was fabricated using a standard tear-and-stack method7,35 with a set twist angle of 0.15°. Here we use a polycarbonate film to pick up the individual flakes to form an hBN(30 nm)/mTBG/hBN(6 nm), which is released at 180 °C on a Si/SiO2(285 nm) substrate. 1D contacts are patterned by photolithography, followed by Cr(5 nm)/Au(50 nm) deposition36. To avoid picking up contamination during our measurements, we clean the surface from polymers residues by AFM-brooming57. Other samples were fabricated in a similar manner. The data discussed in Fig. 4b–d are taken in an hBN(75 nm)/mTBG/hBN(8 nm) stack.
Measurement details
We used an s-SNOM from Neaspec that allows simultaneous measurement of the scattered near-field signal and any photocurrent/photovoltage signals. We used a CO2 laser (Access Laser) and a tunable QCL laser (Daylight Solutions) as infrared light sources between 110 and 250 meV (5–11 μm), at a typical power between 20 and 40 mW. This light is focused on a PtIr-coated AFM tip (Nanoworld), which is oscillating above the sample surface at ~250 kHz with a tapping amplitude of 80–100 nm. The modulated scattering signal is detected by a fast cryogenic HgCdTe detector (Kolmar Technologies), and by operating the s-SNOM in pseudoheterodyne mode we can independently measure the scattering amplitude and phase34. For photocurrent measurements, we used a fast current amplifier (Femto DLPCA-100). For simultaneous measurement of the photovoltage between two pairs of contacts, we used two differential voltage amplifiers (Ithaco 1201) with one common contact grounded. The carrier doping in our samples is tuned by applying a DC voltage between the Si backgate and our device. To avoid detecting unwanted far-field contributions to the scattered or photocurrent/voltage signal, we detect the near-field signals at the 2nd or 3rd harmonic of the cantilever oscillation.
The measured photocurrent/voltage signal is demodulated with the driving signal of the AFM cantilever as a reference signal. However, the actual motion of the AFM cantilever can have a phase offset that varies with the position on the sample (due to tip–sample interaction). This phase offset is given at each pixel by the measured phase delay between the tip driving signal and the actually detected motion. To correct our photocurrent/voltage signal measured at harmonic i, we subtract at every point i times this phase delay. In addition to this, there remains a global phase offset in the corrected photocurrent/voltage signal due to the electronics in the circuit. Since the photocurrent/voltage signal is a real-valued quantity, we subtract this global phase offset, which we determine by taking the most frequent phase within a scan.
Numerical simulations
Finite element method (FEM) simulations of the PTE response of the device were performed using an open-source (LGPLv3), home-made, python package (available at https://gitlab.com/itorre/diffusive_solver)44 based on the FEniCS library58, that allows the solution of coupled diffusion equations systems in realistic sample geometries. Band-structure calculations of shifted graphene bilayers and the extraction of the corresponding physical properties were carried out using an open-source (LGPLv3) python package (available at https://gitlab.com/itorre/bandstructure-calculation), which allows the computation of the spectrum and of optical and thermoelectric properties of simple electronic band-structure models.
Data availability
The data that support the plots within this paper and other findings of this study are available from the corresponding authors upon reasonable request.
Change history
07 March 2022
A Correction to this paper has been published: https://doi.org/10.1038/s41467-022-29014-z
References
Parker, M. Physics of Optoelectronics: 104 (Optical Science and Engineering) 1st edn (2005).
Steiner, T. Semiconductor Nanostructures for Optoelectronic Applications (2004).
Song, J. C. W. & Gabor, N. M. Electron quantum metamaterials in van der Waals heterostructures. Nat. Nanotechnol. 13, 986–993 (2018).
Hunt, B. et al. Massive dirac fermions and Hofstadter butterfly in a van der Waals heterostructure. Science 340, 1427–1430 (2013).
Ponomarenko, L. A. et al. Cloning of Dirac fermions in graphene superlattices. Nature 497, 594–597 (2013).
Dean, C. R. et al. Hofstadter’s butterfly and the fractal quantum Hall effect in moiré superlattices. Nature 497, 598–602 (2013).
Cao, Y. et al. Superlattice-induced insulating states and valley-protected orbits in twisted bilayer graphene. Phys. Rev. Lett. 117, 116804 (2016).
Yoo, H. et al. Atomic and electronic reconstruction at the van der Waals interface in twisted bilayer graphene. Nat. Mater. 18, 448–453 (2019).
Weston, A. et al. Atomic reconstruction in twisted bilayers of transition metal dichalcogenides. Nat. Nanotechnol. 15, 592–597 (2020).
Alden, J. S. et al. Strain solitons and topological defects in bilayer graphene. Proc. Natl Acad. Sci. USA 110, 11256–11260 (2013).
Huang, S. et al. Topologically protected helical states in minimally twisted bilayer graphene. Phys. Rev. Lett. 121, 037702 (2018).
Koshino, M. Electronic transmission through AB-BA domain boundary in bilayer graphene. Phys. Rev. B 88, 115409 (2013).
Rickhaus, P. et al. Transport through a network of topological channels in twisted bilayer graphene. Nano Lett. 18, 6725–6730 (2018).
Xu, S. G. et al. Giant oscillations in a triangular network of one-dimensional states in marginally twisted graphene. Nat. Commun. 10, 4008 (2019).
Jiang, L., Wang, S., Zhao, S., Crommie, M. & Wang, F. Soliton-dependent electronic transport across bilayer graphene domain wall. Nano Lett. 20, 5936–5942 (2020).
Moon, P. & Koshino, M. Optical absorption in twisted bilayer graphene. Phys. Rev. B 87, 205404 (2013).
Moon, P. & Koshino, M. Optical properties of the Hofstadter butterfly in the moiré superlattice. Phys. Rev. B 88, 241412 (2013).
Tomadin, A., Guinea, F. & Polini, M. Generation and morphing of plasmons in graphene superlattices. Phys. Rev. B 90, 161406 (2014).
Yin, L.-J., Jiang, H., Qiao, J.-B. & He, L. Direct imaging of topological edge states at a bilayer graphene domain wall. Nat. Commun. 7, 11760 (2016).
Jiang, L. et al. Soliton-dependent plasmon reflection at bilayer graphene domain walls. Nat. Mater. 15, 840–844 (2016).
Jiang, B.-Y. et al. Plasmon reflections by topological electronic boundaries in bilayer graphene. Nano Lett. 17, 7080–7085 (2017).
Sunku, S. S. et al. Photonic crystals for nano-light in moiré graphene superlattices. Science 362, 1153–1156 (2018).
Hesp, N. C. H. et al. Collective excitations in twisted bilayer graphene close to the magic angle. Preprint at https://arxiv.org/abs/1910.07893 (2019).
Yin, J. et al. Selectively enhanced photocurrent generation in twisted bilayer graphene with van Hove singularity. Nat. Commun. 7, 10699 (2016).
Deng, B. et al. Strong mid-infrared photoresponse in small-twist-angle bilayer graphene. Nat. Photonics 14, 549–553 (2020).
Xu, X., Gabor, N. M., Alden, J. S., Van Der Zande, A. M. & McEuen, P. L. Photo-thermoelectric effect at a graphene interface junction. Nano Lett. 10, 562–566 (2010).
Lemme, M. C. et al. Gate-activated photoresponse in a graphene p–n junction. Nano Lett. 11, 4134–4137 (2011).
Song, J. C. W., Rudner, M. S., Marcus, C. M. & Levitov, L. S. Hot carrier transport and photocurrent response in graphene. Nano Lett. 11, 4688–4692 (2011).
Gabor, N. M. et al. Hot carrier–assisted intrinsic photoresponse in graphene. Science 334, 648–652 (2011).
Woessner, A. et al. Near-field photocurrent nanoscopy on bare and encapsulated graphene. Nat. Commun. 7, 10783 (2016).
Lundeberg, M. B. et al. Thermoelectric detection and imaging of propagating graphene plasmons. Nat. Mater. 16, 204–207 (2017).
Sunku, S. S. et al. Nano-photocurrent mapping of local electronic structure in twisted bilayer graphene. Nano Lett. 20, 2958–2964 (2020).
Hillenbrand, R., Taubner, T. & Keilmann, F. Phonon-enhanced light–matter interaction at the nanometre scale. Nature 418, 159–162 (2002).
Ocelic, N., Huber, A. & Hillenbrand, R. Pseudoheterodyne detection for background-free near-field spectroscopy. Appl. Phys. Lett. 89, 101124 (2006).
Kim, K. et al. van der Waals heterostructures with high accuracy rotational alignment. Nano Lett. 16, 1989–1995 (2016).
Wang, L. et al. One-dimensional electrical contact to a two-dimensional material. Science 342, 614–617 (2013).
Uri, A. et al. Mapping the twist-angle disorder and Landau levels in magic-angle graphene. Nature 581, 47–52 (2020).
Halbertal, D. et al. Moiré metrology of energy landscapes in van der Waals heterostructures. Nat. Commun. 12, 242 (2021).
Fei, Z. et al. Gate-tuning of graphene plasmons revealed by infrared nano-imaging. Nature 487, 82–85 (2012).
Chen, J. et al. Optical nano-imaging of gate-tunable graphene plasmons. Nature 487, 77–81 (2012).
Dai, S. et al. Tunable phonon polaritons in atomically thin van der Waals Crystals of boron nitride. Science 343, 1125–1129 (2014).
Woessner, A. et al. Electrical detection of hyperbolic phonon-polaritons in heterostructures of graphene and boron nitride. npj 2D Mater. Appl. 1, 25 (2017).
Novelli, P., Torre, I., Koppens, F. H. L., Taddei, F. & Polini, M. Optical and plasmonic properties of twisted bilayer graphene: Impact of interlayer tunneling asymmetry and ground-state charge inhomogeneity. Phys. Rev. B 102, 125403 (2020).
Torre, I. Diffusive solver: a diffusion-equations solver based on FEniCS. Preprint at https://arxiv.org/abs/2011.04351 (2020).
Lundeberg, M. B. & Koppens, F. H. L. Thermodynamic reciprocity in scanning photocurrent maps. Preprint at https://arxiv.org/abs/2011.04311 (2020).
Song, J. C. W. & Levitov, L. S. Shockley-Ramo theorem and long-range photocurrent response in gapless materials. Phys. Rev. B 90, 075415 (2014).
Ma, Q. et al. Giant intrinsic photoresponse in pristine graphene. Nat. Nanotechnol. 14, 145–150 (2019).
Kazmierczak, N. P. et al. Strain fields in twisted bilayer graphene. Preprint at https://arxiv.org/abs/2008.09761 (2020).
Nguyen, M. C., Nguyen, V. H., Nguyen, H.-V. V., Saint-Martin, J. & Dollfus, P. Enhanced Seebeck effect in graphene devices by strain and doping engineering. Phys. E Low Dimension. Syst. Nanostruct. 73, 207–212 (2015).
Low, T. et al. Polaritons in layered two-dimensional materials. Nat. Mater. 16, 182–194 (2017).
Basov, D. N., Fogler, M. M. & Garcia de Abajo, F. J. Polaritons in van der Waals materials. Science 354, aag1992 (2016).
Alonso-González, P. et al. Acoustic terahertz graphene plasmons revealed by photocurrent nanoscopy. Nat. Nanotechnol. 12, 31–35 (2017).
Caldwell, J. D. et al. Sub-diffractional volume-confined polaritons in the natural hyperbolic material hexagonal boron nitride. Nat. Commun. 5, 5221 (2014).
Dai, S. et al. Subdiffractional focusing and guiding of polaritonic rays in a natural hyperbolic material. Nat. Commun. 6, 6963 (2015).
Li, P. et al. Hyperbolic phonon-polaritons in boron nitride for near-field optical imaging and focusing. Nat. Commun. 6, 7507 (2015).
Sunku, S. S. et al. Hyperbolic enhancement of photocurrent patterns in minimally twisted bilayer graphene. Nat. Commun. https://doi.org/10.1038/s41467-021-21792-2 (2021).
Goossens, A. M. et al. Mechanical cleaning of graphene. Appl. Phys. Lett. 100, 073110 (2012).
Alnæs, M. S. et al. The FEniCS Project Version 1.5. Arch. Numer. Softw. 3, 9–23 (2015).
Acknowledgements
We thank Justin Song for fruitful discussions and are grateful to Matteo Ceccanti for providing the illustration in Fig. 1a. The research leading to these results has received funding from the European Union’s Horizon 2020 research and innovation programme under grant agreement Ref. 881603 (Graphene Flagship Core Project 3). Furthermore, this work was supported by the ERC TOPONANOP under grant agreement Ref. 726001. N.C.H.H. also acknowledges funding from the European Union’s Horizon 2020 programme under the Marie Skłodowska-Curie grant agreement Ref. 665884. I.T. also acknowledges funding from the Spanish Ministry of Science, Innovation and Universities (MCIU) and State Research Agency (AEI) via the Juan de la Cierva fellowship Ref. FJC2018-037098-I. D.B.R. also acknowledges funding from the Secretaria d’Universitats i Recerca del Departament d’Empresa i Coneixement de la Generalitat de Catalunya, as well as from the European Social Fund. H.H.S. also acknowledges funding from the European Union’s Horizon 2020 programme under the Marie Skłodowska-Curie grant agreement Ref. 843830. K.W. and T.T. also acknowledge support from Japan’s MEXT under the Elemental Strategy Initiative (grant Ref. JPMXP0112101001), from a KAKENHI grant by the JSPS (Ref. JP20H00354), and from the JST under the CREST programme (grant Ref. JPMJCR15F3). R.K.K. also acknowledges funding from the European Union’s Horizon 2020 programme under the Marie Skłodowska-Curie grant agreements with Ref. 754510 and Ref. 893030. F.H.L.K. also acknowledges support from the Government of Spain (FIS2016-81044; Severo Ochoa CEX2019-000910-S), Fundació Cellex, Fundació Mir-Puig, and Generalitat de Catalunya (CERCA, AGAUR, SGR 1656). F.H.L.K. also acknowledges support from the PID2019-106875GB-I00 project funded by MCIN/ AEI /10.13039/501100011033.
Author information
Authors and Affiliations
Contributions
F.H.L.K. and N.C.H.H. conceived the experiment. N.C.H.H. and R.K.K. conducted the experiments, with assistance from D.B.R. and H.H.S. Devices were fabricated by N.C.H.H. and R.K.K., with K.W. and T.T. providing hBN crystals. N.C.H.H., I.T., R.K.K. and F.H.L.K. analysed and interpreted the results. N.C.H.H. and I.T. performed numerical simulations using the band-structure calculator and FEM solver developed by I.T. The manuscript was written by R.K.K., I.T., N.C.H.H. and F.H.L.K. with input from all authors. F.H.L.K. supervised the work.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. Peer review reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hesp, N.C.H., Torre, I., Barcons-Ruiz, D. et al. Nano-imaging photoresponse in a moiré unit cell of minimally twisted bilayer graphene. Nat Commun 12, 1640 (2021). https://doi.org/10.1038/s41467-021-21862-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-21862-5
- Springer Nature Limited
This article is cited by
-
One-dimensional proximity superconductivity in the quantum Hall regime
Nature (2024)
-
Multifunctional Nanomaterials: Recent Advancements in Cancer Therapeutics and Vaccines
Indian Journal of Microbiology (2024)
-
Multiple and spectrally robust photonic magic angles in reconfigurable α-MoO3 trilayers
Nature Materials (2023)
-
Photocurrent as a multiphysics diagnostic of quantum materials
Nature Reviews Physics (2023)
-
A nanotherapeutic approach for fighting the odds against the malignant disorders
Journal of Nanoparticle Research (2023)