Abstract
Achieving efficient photon upconversion under low irradiance is not only a fundamental challenge but also central to numerous advanced applications spanning from photovoltaics to biophotonics. However, to date, almost all approaches for upconversion luminescence intensification require stringent controls over numerous factors such as composition and size of nanophosphors. Here, we report the utilization of dielectric microbeads to significantly enhance the photon upconversion processes in lanthanide-doped nanocrystals. By modulating the wavefront of both excitation and emission fields through dielectric superlensing effects, luminescence amplification up to 5 orders of magnitude can be achieved. This design delineates a general strategy to converge a low-power incident light beam into a photonic hotspot of high field intensity, while simultaneously enabling collimation of highly divergent emission for far-field accumulation. The dielectric superlensing-mediated strategy may provide a major step forward in facilitating photon upconversion processes toward practical applications in the fields of photobiology, energy conversion, and optogenetics.
Similar content being viewed by others
Introduction
As a distinctive group of photon upconversion phosphors, lanthanide-doped upconversion nanoparticles (UCNPs) are capable of nonlinearly converting near-infrared (NIR) excitation into wavelength-programmable UV-Visible emission with large anti-Stokes shift, superior photostability, and long excited state lifetime1,2. However, given the inherently weak photon response of upconversion materials, a beam of laser light with coherent pump intensities above a certain threshold range is typically required to achieve detectable upconversion luminescence3,4,5,6,7. This is particularly true for UCNPs because their practical utilities in the biological and biomedical fields have been overly reliant on coherent excitation8,9,10,11. In recent years, a few implementations, based on surface passivation12,13, surface plasmon coupling14,15,16,17, photonic crystal engineering18,19,20, and broadband sensitization21,22,23,24, have led to experimental realizations with up to four orders of magnitude enhancement in upconversion emission intensity. Nevertheless, the conventional strategies have considerable limitations, such as the need for excitation at a specific wavelength, complex near-field configurations, critical atmosphere and humidity control, and stringent surface modification of the UCNPs. Direct realization of significant upconversion responses at subthreshold input intensities from an incoherent source remains an outstanding challenge.
Herein, we develop an approach that exploits bidirectional light confinement through the use of dielectric microbeads for giant upconversion luminescence enhancement. It should be noted that conventional dielectric optical nano-antennas (such as Si and Ge nanoparticles) feature high refractive indices and the ability to enhance the radiative emission rate of nearby emitters through Mie resonance25,26,27,28,29. By comparison, our approach is largely inspired by the fact that a transparent dielectric microbead can function as a superlens to confine an incident light beam into a sub-wavelength photonic hotspot with high local intensity for applications in super-resolution imaging30,31,32, optical data storage33,34, single nanoparticle detection35,36, and nanojet lithography37,38. We reason that the dielectric microbead-guided wavefront modulation would be feasible for achieving efficient photon upconversion under low irradiance, as the high excitation fluence boosted by superlensing effects could surpass the pump threshold that is required for the practical realization of detectable upconversion.
Results
Spectroscopic study of upconversion amplification
To validate our hypothesis, we fabricated polymeric microbeads made of highly transparent poly (ethylene glycol) diacrylate via a microfluidic technique and examined these microbeads for wavefront modulation (Fig. 1a). When two crossed LED light beams with green and orange color emission shined upon the microbeads obliquely, the beams passing through the microbeads converged into two small and bright spots on the substrate. (Fig. 1a inset). In a wide-field reflection mode, the subdiffractional groove features (~100 nm in width) of a blue-ray disk could be readily resolved through the combined use of the microbeads and a conventional optical microscope with a ×20 objective lens (Fig. 1b). These results suggest that the dielectric microbeads provide an excellent platform to enhance the local electric field intensity and confine the optical energy within the nanoscale domain39.
To shed light on the wavefront-shaping feature of these polymeric microbeads, a three-dimensional finite-difference-time-domain (3D-FDTD) simulation was performed (Fig. 1c). For our simulation, we modeled a polymeric microbead (20 μm in diameter) monolayer resting on an UCNP-embedded polydimethylsiloxane (PDMS) substrate, and a periodic boundary condition was selected. Upon orthogonally polarized NIR plane-wave excitation at 980 nm, our simulation results showed that this polymeric microbead is able to confine the propagating incident energy from the far-field into a subwavelength photonic hotspot, with a full-width at half-maximum (FWHM) of about 680 nm, in the PDMS substrate. The intensity profiles derived from the cross-section analysis of the hotspot are highly symmetric, implying the reconstruction of a converging spherical wavefront to a focal point source, as verified by the simulated result of propagating phase mapping. The existence of the photonic hotspot was further experimentally confirmed by 3D confocal microscopic imaging of the spatial upconversion luminescence distribution of green-emitting UCNPs. Indeed, we recorded the formation of a green-emitting lobe, located near the rear side of the microbead, with dimensions spanning several micrometers in the PDMS substrate (Fig. 1d). Notably, the photonic crystal effect of the dielectric microbead monolayer was also numerically investigated and no reflection or transmission band appear in the visible-to-NIR region (Supplementary Fig. 1).
In a further set of experiments, we synthesized NaYF4:Yb/Er@NaYF4 and NaGdF4:Yb/Tm@NaGdF4:Eu UCNPs of ~20 nm in diameter (Fig. 2a, Supplementary Fig. 2 and 3)40,41. Upon 980 nm excitation, Er3+-activated UCNPs showed yellow-green emission with two characteristic bands centered around 540 and 654 nm. For UCNPs coactivated with Tm3+/Eu3+ dopants, characteristic bands centered around 450 and 614 nm were observed, arising from 1D2 \(\rightarrow\) 3F4 transition of Tm3+ and 5D0 \(\rightarrow\) 7F2 transition of Eu3+, respectively. It is important to note that the Eu3+ emission stems from the energy-migration-mediated upconversion by accepting the down-shifting energy from Gd3+ sublattice which is pre-populated by Tm3+ activators in the core. To prove the effect of dielectric superlensing for enhanced upconversion processes, we prepared a monolayer array of hexagonal close-packed microbeads onto the UCNP-embedded PDMS substrate and compared the upconversion luminescence intensities of UCNPs with or without the microbead coverage (Fig. 2b, Supplementary Fig. 4). Figure 2c shows the upconversion luminescence images of the upconverting PDMS substrate containing UCNPs. The region covered with the microbeads showed bright visible emission, while only inconspicuous luminescence was captured in the absence of the microbeads (Supplementary Movie 1). Furthermore, we quantified the enhancement factor for the upconversion luminescence intensity of each activator under different power densities by comparing the peak intensities of its emission bands with and without the coverage of dielectric microbeads (Fig. 2d). Our data indicate that the utilization of the dielectric microbeads can induce an immense luminescence enhancement in optical transitions of the activators under investigation. It is important to note that in all cases the luminescence-enhancing effect dominates to a much bigger extent under low-power excitation. We also observed that the luminescence enhancement features of dielectric superlensing are strongly dependent on the upconversion population processes of different activators. For instance, under 1.5 W cm−2 power excitation, the upconversion luminescence at 614 nm could be enhanced by more than five orders of magnitude (up to 103,000) for the 5D0 \(\rightarrow\) 7F2 transition of Eu3+. However, under the identical conditions, we recorded only ~100 fold-enhancement for emission band centered at 540 nm, corresponding to the 4S3/2 \(\rightarrow\) 4I15/2 transition of Er3+.
Mechanistic investigation
In a given lanthanide-mediated upconversion system, the sequential population of a specific emitting state is made possible through intermediate excited states42,43. In principle, the intensity of emission I, arising from an n-photon populated excited state, increases as a power function of excitation power P (I∝Pn) at the low-power end, and tends to reach a plateau at the high-power regime, because the excited state depopulation pathway is gradually dominated through population to higher excited states instead of relaxation to the ground state43. For illustration, let us consider the case of an UCNP-embedded PDMS substrate featuring dual activators (Tm@Eu). Power-dependent studies of luminescence enhancement revealed that the effect of pump fluence on emission intensity is more predominant under low power than that under high power excitation (Fig. 3a). At the lowest fluences, the emission intensities of Tm3+ and Eu3+ activators are largely increased. As the fluence increases, the enhancing factor for both activators becomes continuously smaller. However, when using dielectric microbeads to guide the excitation, the differences in the effect of power-dependent emission intensity could be brought down drastically, with much smaller increments in intensity at the low-power end than obtainable in the absence of the microbeads. This strongly suggests the presence of high excitation fluence occurring in UCNPs, which accounts for the main cause of enormous luminescence enhancement empowered by the microbeads.
The fluence dependence of a given upconversion transition is strongly dictated by its preceding population pathway44,45. For example, when comparing the 1D2 \(\rightarrow\) 3F4 transition of Tm3+ with the 5D0 \(\rightarrow\) 7F2 transition of Eu3+, one would recognize that Eu3+ involves one additional step (1D2 \(\rightarrow\) 1I6) of population (Fig. 3b), shows higher excitation fluence sensitivity (Fig. 3a), and thus more significant luminescence enhancement induced by dielectric microbeads (Fig. 2d). Consistent with this, the green emission of Er3+ at 540 nm, as already described in Fig. 2d, shows the lowest enhancement in upconversion luminescence, because its associated optical transition (4S3/2 \(\rightarrow\) 4I15/2) involves only a two-step population regime and thus has the lowest sensitivity to the excitation fluence. Numerically, we constructed a universal energy transfer model involving two to five-photon upconversion population (Fig. 3c, Supplementary Fig. 5). The simulation results reveal a clear trend in pump power sensitivity related to multiphoton upconversion process. Indeed, higher-order upconversion emission exhibits higher sensitivity to the excitation fluence and more prominent luminescence enhancement (Fig. 3c). At high excitation fluence, we observed a significant decrease in power sensitivity and a simultaneous decline in luminescence enhancement factor for all upconversion transitions under investigation.
Quite different from commonly used dielectric and metal optical nano-antennas for fluorescence enhancement by boosting radiative emission rate, our dielectric superlensing strategy for upconversion luminescence enhancement does not rely on the acceleration of radiative emission. According to the simulation results (Supplementary Fig. 6a, b), although a single dielectric microbead has a high-quality factor in whispering gallery mode, the large distance (>3 μm) between the dielectric microbead and emitting UCNPs around the focal point would make the potential Purcell effect negligible in affecting the spontaneous emission processes in UCNPs. For instance, although the upconversion emission from Eu3+ (5D0 \(\rightarrow\) 7F2) could be amplified up to five orders of magnitude, the dielectric superlensing effect introduced negligible changes in the fluorescence decay lifetimes throughout the whole emission band (Supplementary Fig. 6c, d). Therefore, the Purcell effect contributes negligibly to the overall upconversion luminescence enhancement under the current experimental design.
Apart from the ability to create photonic hotspots with high excitation field intensity, dielectric microbeads can enhance the efficiency of far-field light collection and in turn contribute to the emission amplification of photon upconversion to some extent. As shown in Fig. 3d, the wavefront of a point light source could be efficiently converted to a quasi-plane-wave and the divergent upconversion emission is well collimated into the far-field after passing through the dielectric microbeads (Supplementary Fig. 7). For example, in a divergence half-angle of about 17° with a numerical aperture of 0.3, our simulation shows that the use of a microbead leads to an approximately 8-fold increase in upconversion luminescence collection efficiency. Next, taking the NaYF4:Nd/Yb nanocrystal emitting at ~980 nm from Yb3+ ions by accepting the energy from Nd3+ ions as an example, we investigated dielectric superlensing effects for down-shifting fluorescence enhancement. The Stokes emission from Yb3+ ions was amplified about eight times and the enhancement factors are independent of the excitation power intensity (Fig. 3e). The distinct fluorescence enhancement features for down-shifting fluorophores was further confirmed using Rhodamine B, which also showed a constant Stokes emission enhancement factor of 8 under a wide range of pumping power at 520 nm (Fig. 3f, Supplementary Fig. 8a). Therefore, although a large portion of one-photon emitters placed beneath the dielectric microbead is not illuminated, the overall enhancement in luminescence can still be observed benefiting from the superior light collection effect of the microbead. However, upon 800 nm femtosecond laser excitation, the anti-Stokes emission from Rhodamine B through the two-photon absorption could be amplified by a factor of more than 1100 (Fig. 3g, Supplementary Fig. 8b). Taken together, these data indicate a strong correlation between dielectric superlensing and nonlinear fluorescence amplification regardless of the type of fluorophores.
Our further experiments involving poly(ethylene glycol) diacrylate microbeads with a mean diameter of ~50 μm resulted in slightly inferior upconversion luminescence enhancement compared to that of 20 μm-sized microbeads (Supplementary Fig. 9). This might be due to incomplete polymerization for large-sized microbeads during UV-curing and the associated increase in focal length beyond the upconversion thin film. Despite the difference in physical parameters such as diameter, transmittance, and refractive index, commonly used dielectric microbeads made of polystyrene, poly(methyl methacrylate) or ceramic SiO2 and BaTiO3 materials could also be used to boost upconversion luminescence (Supplementary Fig. 10).
Optogenetic application
For convenience and improved mechanical strength, we combined an ensemble of close-packed, one-layer-thick BaTiO3 microbeads (50 μm) with a PDMS precursor by curing, producing a transparent, planar composite PDMS sheet (Fig. 4a). This composite sheet showed superlensing effects similar to those of bare poly (ethylene glycol) diacrylate microbeads due to a good contrast in the refractive index between BaTiO3 (n = 2.1) and PDMS (n = 1.4) (Supplementary Fig. 11). Importantly, the availability of this PDMS sheet allowed us to develop a convenient tool that can immediately apply to improve document security application involving upconversion-based encoding techniques. As shown in Fig. 4b–e, with the help of the as-fabricated PDMS sheet, an encrypted quick-response code, printed on a piece of paper using green-emitting NaYF4:Yb/Er@NaYF4 nanoparticle inks, could be readily decoded with a tungsten lamp at sub-solar irradiance (~0.012 W cm−2) (Supplementary Fig. 12). In contrast, in the absence of the PDMS sheet the decoding process was not successful. Interestingly, with this flexible dielectric superlensing film, imaging single UCNP or a PDMS film embedded with heavily Tm3+-doped (4%) UCNPs could be realized under pumping power density of ~500 W cm−2 and 80 W cm−2, respectively, through the use of a common wide-field optical microscope (Supplementary Fig. 13)46,47.
We next examined whether it would be possible to harness the effect of dielectric superlensing for advanced optogenetic applications48,49. The deep-tissue penetration ability of NIR light renders upconversion-mediated optogenetic stimulation a feasible solution for the remote, noninvasive optical interrogation of neurons with substantially improved spatial resolution and sensitivity. However, the recent implementation of upconversion-based optogenetics has been largely hindered by the requirement of high-power light excitation (higher than 200 W cm−2), as the strong intensity of light may cause harmful temperature rises in brain tissue50,51. A protocol involving low-power excitation would be extremely valuable for safe design of optogenetic experiments. Accordingly, we examined the combined utility of dielectric microbeads and NIR-mediated optogenetics for controlled neuronal depolarization and enhanced action potential firing. We first prepared a flexible PDMS chip that comprises layered BaTiO3 microbeads and blue-emitting NaYF4:Yb/Tm@NaYF4 nanoparticles. We then placed the PDMS chip directly underneath a brain slice (~300 μm thick) that was connected to a patch clamp recording device. This design allows us to record the electrophysiological response of neurons containing melanin-concentrating hormone (MCH) (Fig. 4f, Supplementary Fig. 14). As shown in Fig. 4g, compared to the use of blue-emitting PDMS layer alone, the combined use of the UCNP/PDMS layer and the microbead monolayer led to a blue emission with significantly increased power output (Supplementary Movie 2). Although the placement of the 300 μm thick brain slice in the light path would cause the aberration of the irradiation beam from the laser to some extent (Fig. 4h, i), we confirmed the validity of our approach under low-power NIR excitation by the observation of neuronal activities with exclusive channelrhodopsin-2 (ChR2) expression (Fig. 4j). The photocurrent ratios indicated that on 980 nm illumination at three different pump power settings, the dielectric superlensing effect boosted the current by 496% (3.5 W cm−2), 415% (7.0 W cm−2), and 340% (11 W cm−2), compared to controls without the microbead layer (Fig. 4k). These data imply that the use of dielectric microbeads may be able to overcome the current limitations associated with visible light scattering and attenuation in thick brain slices. At a low-power excitation of 11 W cm−2, we were able to evoke a sufficient action potential to activate neuron cells, a feat which is inaccessible by conventional upconversion-based optogenetics (Fig. 4l).
Discussion
In conclusion, our combined experimental and theoretical work has provided proof of the superlensing nature of a dielectric microbead suitable for boosting photon-photon interactions in UCNPs at sub-threshold light intensities. Unlike conventional strategies for upconversion amplification whose feasibilities are strongly dependent on many parameters of UCNPs such as particle size, composition, the choice of surface ligands, the approach described here provides a general solution for any given upconversion phosphors. Through this strategy, the magnitude of the upconversion response and, consequently, the physical process responsible for efficient upconversion can be controlled by modulating the wavefront of both excitation and emission fields through the use of dielectric microbeads. Our study also provides an experimental basis for facilitating two- or multiphoton pumped upconversion in organic systems. Importantly, the dielectric superlensing strategy may hold great promise in enabling triplet-triplet annihilation upconversion under sub-solar irradiance. In addition, our design is readily scalable for mass production and does not need stringent control over fabrication conditions or imaging atmosphere. These discoveries, when combined with recent advances in nanoscale synthesis and imaging technology, are expected to find applications in the fields of wide-bandgap solar cells, optical nanosensing, optical memory storage, biophotonics, and potentially many others.
Methods
Nanocrystal synthesis
The designed NaYF4:Yb/Er@NaYF4 core-shell upconversion nanocrystals were synthesized following previously reported protocols with some modifications40. In a typical procedure, to a 50-mL two-neck round-bottomed flask charged with 1-octadecene (7 mL) and oleic acid (3 mL) was added an aqueous solution (2 mL) of Y(CH3CO2)3, Yb(CH3CO2)3 and Er(CH3CO2)3 at varied molar ratios (78/20/2) with a total lanthanide content of 0.4 mmol. After removal of the water by heating at 150 °C for 1 h, lanthanide complexes were formed. The mixture was cooled down to 50 °C, and a methanol solution (6 mL) of NH4F (1.6 mmol) and NaOH (1 mmol) was subsequently added. After stirring for 30 min at 50 °C, the reaction was heated to 100 °C and pumped for 15 min to remove the methanol. The remaining residue was heated to 290 °C and then maintained at this temperature for 2 h under an argon flow. After cooling down to room temperature, the resulting nanocrystals were collected by centrifugation, washed with ethanol several times, and redispersed in 4 mL of cyclohexane for succeeding shell growth. To the synthesis of NaYF4:Yb/Er@NaYF4 core-shell nanocrystals, a shell precursor containing 0.4 mmol Y(CH3CO2)3 was prepared by the same procedure as those mentioned above and cooled down to 80 °C. Then as-synthesized NaYF4:Yb/Er core nanocrystals dispersed in cyclohexane was added. After 40 min, the resultant mixture was cooled down to 50 °C, and a methanol solution (6 mL) of NH4F (1.6 mmol) and NaOH (1 mmol) was added subsequently. After stirring for another 30 min at 50 °C, the reaction was heated to 100 °C for 15 min before reaching 290 °C. After reaction completion in 2 h, the as-synthesized core-shell nanocrystals were isolated by centrifugation, washed with ethanol several times, and then redispersed in 4 mL cyclohexane.
The preparation of NaGdF4:Yb/Tm@NaGdF4:Eu core-shell nanocrystals follows the same procedure as mentioned above except for the use of different ratios of lanthanide ions. For the NaGdF4:Yb/Tm core nanoparticles, the ratios of Gd/Yb/Tm was set at 50/49/1, and for the shell precursor, the ratio of Gd/Eu was set at 90/10.
Preparation of polymeric microbeads
For aqueous phase preparation, 1 mL water containing 0.4 mL PEGDA and 25 mg photo-initiator (2-hydroxy-4′-(2-hydroxythoxy)-2-methylpropiophenone) was sonicated for 5 min to yield a homogenous and transparent solution. For oil phase, 0.5% Krytox (modified) surfactant was added to fluorocarbon oil HFE 7500 to help to stabilize the microdroplets. The prepolymer microdroplets were polymerized by UV exposure (500 mW).
Preparation of PDMS film with different phosphors
Upconversion nanocrystals of 100 mg were redispersed in 2 mL CHCl3 by sonication. Then 1.1 g PDMS (prepolymer and crosslinker in a 10:1 weight ratio) was mixed with the above solution and sonicated for 10 min to ensure a uniform distribution of UCNPs. Then the solution containing UCNPs was spin-coated onto a cover slide substrate at 7000 rpm for 1 min and the obtained film was solidified at 50 °C for 12 h. For the preparation of Rhodamine B imbedded PDMS film, Rhodamine B dye molecules (2 mg) was first dispersed in 2 mL CHCl3, then 2.2 g PDMS (prepolymer and crosslinker in a 10:1 weight ratio) was mixed with the dye solution while stirring for 2 h. Then the mixture was spin-coated onto a cover slide at 10,000 rpm for 1 min and then kept at 50 °C in an oven for 12 h.
Characterization
The size and morphology of the as-prepared core-shell nanocrystals were characterized using a JEOL-1400 (Transmission electron microscope) TEM operating at an acceleration voltage of 100 kV. The powder (X-ray diffraction) XRD patterns were recorded by an ADDS X-ray diffractometer with CuKa radiation (40 kV, 40 mA, λ = 1.54184 Å). The luminescence spectra of samples dispersed in cyclohexane were recorded with an Edinburgh FSP920 spectrofluorometer equipped with a photomultiplier (PMT), in conjunction with a continuous-wave 980-nm diode laser (MDL-III). For film sample characterization, a home-built Olympus BX51 fluorescence microscope coupled with a 980-nm diode laser for excitation and an Ocean Optics Pro spectrometer (QE-Pro) for emission spectra collection is used. The divergence of the light beam was tuned with a convex lens system to make sure a collimated excitation laser beam can be obtained after passing through the objective lens (×10 , NA = 0.3). For measurements of simultaneous two-photon excited fluorescence of rhodamine B with and without the superlensing layer, a home-built fluorescence microscope coupled with a femtosecond amplified-pulsed laser system was used for excitation, and a visible monochromator (Acton, Spectra Pro 2750i) coupled with CCD (Princeton Instruments, Pixis 100B) was applied for emission collection. The excitation laser pulses were generated by a regenerative amplified femtosecond Ti:Sapphire laser system (~50 fs, 800 nm, 1 kHz; Libra, Coherent). The Coherent Libra regenerative amplifier was seeded by a femtosecond Ti:Sapphire oscillator (~50 fs, 80 MHz, Vitesse, Coherent). The temporal and spatial profiles of the applied excitation laser source follow a Gaussian distribution.
Materials and methods for optogenetic study
All experimental protocols involving animals were approved and performed in accordance by Institutional Animal Care and Use Committees, Research Institute of Environmental Medicine, Nagoya University, Japan.
Acute brain slice preparation
Male and female mice aged 3–4 months were used for electrophysiological recordings. Mice were deeply anesthetized using isoflurane (Wako Pure Chemical Industries, Osaka, Japan) and decapitated. The brain was then quickly isolated and chilled in ice-cold cutting solution (in mM: 110 K-gluconate, 0.05 EGTA, 15 KCl, 5 HEPES, 26.2 NaHCO3, 3.3 MgCl2, 25 glucose, and 0.0015 (±)-3-(2-carboxypiperazin-4-yl)propyl-1-phosphonic acid) gassed with 5% CO2 and 95% O2. Coronal brain slices of 300 µm thickness that contain lateral hypothalamus were generated using a vibratome (VT-1200S; Leica, Wetzlar, Germany) and were temporarily placed in an incubation chamber containing bath solution (in mM: 3 KCl, 124 NaCl, 2 MgCl2, 2 CaCl2, 26 NaHCO3, 1.23 NaH2PO4, and 25 glucose) gassed with 5% CO2 and 95% O2 in a 35 °C water bath for at least 60 min. Slices were then incubated in the same incubation chamber at room temperature for another 30–60 min for recovery. Cutting and bath solutions were modified from Pressler and Regehr.
Electrophysiological recording using brain slice
Acute brain slices of MCH-tTA; TetO ChR2 mice were transferred to a recording chamber (RC-26G; Warner Instruments, Hamden, CT, USA) on an upright fluorescence microscope (BX51WI; Olympus, Tokyo, Japan) stage and superfused with 95% O2 and 5% CO2 gassed bath solution at a rate of 1.2 mL/min using a peristaltic pump (Dynamax; Rainin, Oakland, CA, USA). An infrared camera (C3077-78; Hamamatsu Photonics, Hamamatsu, Japan) was installed in the fluorescence microscope along with an electron multiplying charge-coupled device (EMCCD) camera (Evolve 512 delta; Photometrics, Tucson, AZ, USA) and both images were separately displayed on monitors. Micropipettes of 4–7 MΩ resistance were prepared from borosilicate glass capillaries (GC150-10; Harvard Apparatus, Cambridge, MA, USA) using a horizontal puller (P-1000; Sutter Instrument, Novato, CA, USA). Patch pipettes were filled with KCl-based internal solution (in mM: 145 KCl, 1 MgCl2, 10 HEPES, 1.1 EGTA, 2-Mg-ATP, 0.5 Na2-GTP; pH 7.3 with KOH) with osmolality between 280 and 290 mOsm. Positive pressure was introduced in the patch pipette as it approached the cell. A giga-seal of resistance >1 GΩ was made between the patch pipette and the cell membrane by releasing the positive pressure upon contacting the cell. Then the patch membrane was ruptured by suction to form a whole-cell configuration. Electrophysiological properties of cells were monitored by an Axopatch 200B amplifier (Axon Instrument, Molecular Devices, Sunnyvale, CA). Output signals were low-pass filtered at 5 kHz and digitized at a sampling rate of 10 kHz. Patch clamp data were recorded through an analog-to-digital (AD) converter (Digidata 1550A; Molecular Devices) using pClamp software (Molecular Devices). Blue light of 475 ± 17.5 nm wavelength was generated by a light-emitting diode (Spectra light engine; Lumencor, Beaverton, OR, USA) and was guided to the microscope stage with a 1 cm diameter optical fiber. Near-infrared light of 976-nm wavelength was generated by LuOcean Mini 4 laser (Lumics GmbH, Berlin, Germany) and was guided by an optical fiber to illuminate brain slices.
Data are given as mean ± SEM. Nonparametric Mann–Whitney U-test was used for statistical analysis. All data were obtained from brain slices from 3 mices, where n = 11 cells for all beads experiment, n = 8 for all control experiments without beads, n = 10 for blue light LED experiments, and n = 5 for control experiments with only NIR excitation.
Numerical simulation
Simulations of the light converging effect of microbeads were performed by a three-dimensional finite-difference-time-domain (3D-FDTD) method with periodic boundary conditions. The light source for excitation was set as plane wave at a wavelength of 980 nm. For light harvesting ability simulation of upconversion emission, dipole source was used at a wavelength of 600 nm. The refractive index of PEGDA, PDMS, BaTiO3 were set as 1.4, 1.4, and 2.1, respectively. For plane wave simulation, two simulations with orthogonally polarized beams were performed and the resulted fields were averaged incoherently. For dipole source simulation, three simulations with orthogonally polarized dipole sources were also performed. In order to evaluate the incoherent illumination situation, 11 models with light sources at different positions (varying over a region (−λ/2, λ/2)) were carried for simulation and the obtained light intensity distributions from each model were superimposed. To obtain the quality factor of dielectric microbead, a dipole source was placed on the surface of the microbead and an analysis group containing 36 time monitors was placed close to the surface of the microbead to record the decay of electric field. Additionally, Purcell factors of a dipole source were simulated when the dipole was placed inside the PDMS film with different distances (0.01–5 μm) from the microbead surface. During the simulation, a transmission box was applied to obtain the power emitted by the source.
The Monte Carlo method was used to simulate photon transport in a brain slice (300 μm in thickness) using the MATLAB software package mcxyz (http://omlc.org/software/mc/mcxyz/). The light source was modeled as a collimated beam with a waist of 0.5 mm. The source was placed on the top of the brain slice with 5 mm. This simulation domain was a cuboid with a length, width, and height of 0.5 cm, 0.5 cm and 0.8 cm, respectively. Tissue optical properties were set using the scattering and absorption parameters extracted from ref. 52, and the simulation time was set to 30 min.
For the numerical simulation of the sensitizer-activator upconversion system, we built a general sensitizer-activator upconversion system involving up to 5-photon upconversion population processes53,54,55. To show the universal features of the evolution of upconversion emissions, we kept the main upconversion transition processes (such as sensitizer absorption, energy transfer from sensitizer to activator, and intrinsic decay of excited states), and the secondary processes (such as activator absorption, energy back transfer from activator to sensitizer, and cross-relaxation between activators) were not taken into consideration. In addition, the energy gap between adjacent main excited states was set as equal, and the upconversion coefficients between sensitizers and each active state of activators shared the same value. Thus, the following rate equations for a typically simplified sensitizer-activator upconversion system was established.
where P980 is the absorption rate of sensitizer; wi is the intrinsic excited state decay rate of activators; ws is the intrinsic decay rate of sensitizers; bij is the branching ratio for activator decaying from excited state i to j; ci is the upconversion coefficient between the sensitizer and activator residing at the excited state i. The steady state population density evolution of each excited state (n3, n4, n5, n6) of activators was obtained by solving the rate equation at different P980 values. It should be noted that the modeling conducted here means to build a universal sensitizer-activator upconversion model involving essential transition processes for general lanthanide-doped upconversion, so that the simulation results can reveal the general trends of population evolution regardless of the selection of sensitizers or activators.
Reporting summary
Further information on experimental design is available in the Nature Research Reporting Summary linked to this article.
References
Auzel, F. Upconversion and anti-stokes processes with f and d ions in solids. Chem. Rev. 104, 139–174 (2004).
Zhou, B., Shi, B., Jin, D. & Liu, X. Controlling upconversion nanocrystals for emerging applications. Nat. Nanotechnol. 10, 924–936 (2015).
Zheng, Q. et al. Frequency-upconverted stimulated emission by simultaneous five-photon absorption. Nat. Photonics 7, 234–239 (2013).
Chen, X. et al. Confining energy migration in upconversion nanoparticles towards deep ultraviolet lasing. Nat. Commun. 7, 10304 (2016).
Brites, C. D. et al. Instantaneous ballistic velocity of suspended Brownian nanocrystals measured by upconversion nanothermometry. Nat. Nanotechnol. 11, 851–856 (2016).
Jin, D. et al. Nanoparticles for super-resolution microscopy and single-molecule tracking. Nat. Methods 15, 415–423 (2018).
Nam, S. H. et al. Long-term real-time tracking of lanthanide ion doped upconverting nanoparticles in living cells. Angew. Chem. 123, 6217–6221 (2011).
Liu, Y. et al. Amplified stimulated emission in upconversion nanoparticles for super-resolution nanoscopy. Nature 543, 229–233 (2017).
Gargas, D. J. et al. Engineering bright sub-10-nm upconverting nanocrystals for single-molecule imaging. Nat. Nanotechnol. 9, 300–305 (2014).
Zhou, J., Liu, Z. & Li, F. Upconversion nanophosphors for small-animal imaging. Chem. Soc. Rev. 41, 1323–1349 (2012).
Liang, L. et al. Designing upconversion nanocrystals capable of 745 nm sensitization and 803 nm emission for deep-tissue imaging. Chem. Eur. J. 22, 10801–10807 (2016).
Wang, F., Wang, J. & Liu, X. Direct evidence of a surface quenching effect on size‐dependent luminescence of upconversion nanoparticles. Angew. Chem. 122, 7618–7622 (2010).
Su, Q. et al. The effect of surface coating on energy migration-mediated upconversion. J. Am. Chem. Soc. 134, 20849–20857 (2012).
Schietinger, S., Aichele, T., Wang, H.-Q., Nann, T. & Benson, O. Plasmon-enhanced upconversion in single NaYF4: Yb3+/Er3+ codoped nanocrystals. Nano. Lett. 10, 134–138 (2009).
Saboktakin, M. et al. Plasmonic enhancement of nanophosphor upconversion luminescence in Au nanohole arrays. ACS Nano 7, 7186–7192 (2013).
Luu, Q. et al. Two-color surface plasmon polariton enhanced upconversion in NaYF4: Yb: Tm nanoparticles on Au nanopillar arrays. J. Phys. Chem. C. 118, 3251–3257 (2014).
He, J. et al. Plasmonic enhancement and polarization dependence of nonlinear upconversion emissions from single gold nanorod@SiO2@CaF2:Yb3+,Er3+ hybrid core–shell–satellite nanostructures. Light Sci. Appl. 6, e16217 (2017).
Yin, Z. et al. Remarkable enhancement of upconversion fluorescence and confocal imaging of PMMA Opal/NaYF4: Yb3+, Tm3+/Er3+ nanocrystals. Chem. Commun. 49, 3781–3783 (2013).
Yin, Z. et al. Local field modulation induced three‐order upconversion enhancement: combining surface plasmon effect and photonic crystal effect. Adv. Mater. 28, 2518–2525 (2016).
Niu, W. et al. 3-Dimensional photonic crystal surface enhanced upconversion emission for improved near-infrared photoresponse. Nanoscale 6, 817–824 (2014).
Zou, W., Visser, C., Maduro, J. A., Pshenichnikov, M. S. & Hummelen, J. C. Broadband dye-sensitized upconversion of near-infrared light. Nat. Photonics 6, 560–564 (2012).
Chen, G. et al. Energy-cascaded upconversion in an organic dye-sensitized core/shell fluoride nanocrystal. Nano. Lett. 15, 7400–7407 (2015).
Wang, X. et al. Dye-sensitized lanthanide-doped upconversion nanoparticles. Chem. Soc. Rev. 46, 4150–4167 (2017).
Garfield, D. J. et al. Enrichment of molecular antenna triplets amplifies upconverting nanoparticle emission. Nat. Photonics 12, 402–407 (2018).
Regmi, R. et al. All-dielectric silicon nanogap antennas to enhance the fluorescence of single molecules. Nano. Lett. 16, 5143–5151 (2016).
Sun, S., Wu, L., Bai, P. & Png, C. Fluorescence enhancement in visible light: dielectric or noble metal? Phys. Chem. Chem. Phys. 18, 19324–19335 (2016).
Albella, P. et al. Low-loss electric and magnetic field-enhanced spectroscopy with subwavelength silicon dimers. J. Phys. Chem. C. 117, 13573–13584 (2013).
Krasnok, A. E., Miroshnichenko, A. E., Belov, P. A. & Kivshar, Y. S. All-dielectric optical nanoantennas. Opt. Express 20, 20599–20604 (2012).
Caldarola, M. et al. Non-plasmonic nanoantennas for surface enhanced spectroscopies with ultra-low heat conversion. Nat. Commun. 6, 7915 (2015).
Lee, J. Y. et al. Near-field focusing and magnification through self-assembled nanoscale spherical lenses. Nature 460, 498–501 (2009).
Wang, F. et al. Scanning superlens microscopy for non-invasive large field-of-view visible light nanoscale imaging. Nat. Commun. 7, 13748 (2016).
Wang, Z. et al. Optical virtual imaging at 50 nm lateral resolution with a white-light nanoscope. Nat. Commun. 2, 218 (2011).
Terris, B., Mamin, H., Rugar, D., Studenmund, W. & Kino, G. Near‐field optical data storage using a solid immersion lens. Appl. Phys. Lett. 65, 388–390 (1994).
Gu, M., Li, X. & Cao, Y. Optical storage arrays: a perspective for future big data storage. Light Sci. Appl. 3, e177 (2014).
Li, Y. et al. Enhancing upconversion fluorescence with a natural bio-microlens. ACS Nano 11, 10672–10680 (2017).
Yang, H., Cornaglia, M. & Gijs, M. A. M. Photonic nanojet array for fast detection of single nanoparticles in a flow. Nano. Lett. 15, 1730–1735 (2015).
Gonidec, M. et al. Fabrication of nonperiodic metasurfaces by microlens projection lithography. Nano. Lett. 16, 4125–4132 (2016).
Kato, J.-i, Takeyasu, N., Adachi, Y., Sun, H.-B. & Kawata, S. Multiple-spot parallel processing for laser micronanofabrication. Appl. Phys. Lett. 86, 044102 (2005).
Yang, H., Trouillon, Rl, Huszka, G. & Gijs, M. A. Super-resolution imaging of a dielectric microsphere is governed by the waist of its photonic nanojet. Nano. Lett. 16, 4862–4870 (2016).
Wang, F., Deng, R. & Liu, X. Preparation of core-shell NaGdF4 nanoparticles doped with luminescent lanthanide ions to be used as upconversion-based probes. Nat. Protoc. 9, 1634 (2014).
Wang, F. et al. Tuning upconversion through energy migration in core–shell nanoparticles. Nat. Mater. 10, 968–973 (2011).
Suyver, J., Aebischer, A., García-Revilla, S., Gerner, P. & Güdel, H. Anomalous power dependence of sensitized upconversion luminescence. Phys. Rev. B 71, 125123 (2005).
Pollnau, M., Gamelin, D. R., Lüthi, S., Güdel, H. & Hehlen, M. Power dependence of upconversion luminescence in lanthanide and transition-metal-ion systems. Phys. Rev. B 61, 3337–3346 (2000).
Zhang, C. et al. White-light emission from an integrated upconversion nanostructure: toward multicolor displays modulated by laser power. Angew. Chem. Int. Ed. 54, 11531–11535 (2015).
Wang, L. et al. Reversible near-infrared light directed reflection in a self-organized helical superstructure loaded with upconversion nanoparticles. J. Am. Chem. Soc. 136, 4480–4483 (2014).
Wang, F. et al. Microscopic inspection and tracking of single upconversion nanoparticles in living cells. Light Sci. Appl. 7, 18007 (2018).
Zhao, J. et al. Single-nanocrystal sensitivity achieved by enhanced upconversion luminescence. Nat. Nanotechnol. 8, 729 (2013).
Boyden, E. S., Zhang, F., Bamberg, E., Nagel, G. & Deisseroth, K. Millisecond-timescale, genetically targeted optical control of neural activity. Nat. Neurosci. 8, 1263–1268 (2005).
Wang, Y. et al. Tetherless near-infrared control of brain activity in behaving animals using fully implantable upconversion microdevices. Biomaterials 142, 136–148 (2017).
Wu, X. et al. Dye-sensitized core/active shell upconversion nanoparticles for optogenetics and bioimaging applications. ACS Nano 10, 1060–1066 (2016).
Chen, S. et al. Near-infrared deep brain stimulation via upconversion nanoparticle–mediated optogenetics. Science 359, 679–684 (2018).
Jacques, S. L. Optical properties of biological tissues: a review. Phys. Med. Biol. 58, R37 (2013).
Villanueva-Delgado, P., Krämer, K. W. & Valiente, R. Simulating energy transfer and upconversion in β-NaYF4: Yb3+, Tm3+. J. Phys. Chem. C. 119, 23648–23657 (2015).
Hossan, M. Y. et al. Explaining the nanoscale effect in the upconversion dynamics of β-NaYF4: Yb3+, Er3+ core and core–shell nanocrystals. J. Phys. Chem. C. 121, 16592–16606 (2017).
Zhan, Q. et al. Achieving high-efficiency emission depletion nanoscopy by employing cross relaxation in upconversion nanoparticles. Nat. Commun. 8, 1058 (2017).
Acknowledgements
This work is supported by the Singapore Ministry of Education (Grant R143000627112, R143000642112), Agency for Science, Technology and Research (A*STAR) (Grant R143000684305), National Research Foundation, Prime Minister’s Office, Singapore under its Competitive Research Program (CRP Award No. NRF-CRP15-2015-03), National Basic Research Program of China (973 Program, Grant 2015CB932200), Japan Science and Technology Agency CREST (Grant JPMJCR1656), the CAS/SAFEA International Partnership Program for Creative Research Teams, and National Natural Science Foundation of China (21771135, 21471109). T.C.S. acknowledges the support from JSPS-NTU Joint Research Project M4082176, the Ministry of Education AcRF Tier 1 grant (RG173/16) and Tier 2 grants (MOE2015-T2-2-015 and MOE2016-T2-1-034), the Singapore National Research Foundation through the Competitive Research Programme (NRF-CRP14-2014-03), and the NRF Investigatorship Programme (NRF-NRFI-2018-04).
Author information
Authors and Affiliations
Contributions
L.L. and X.L. conceived and initiated the project. X.L., A.H.A., N.V.T., C.H.C., T.C.S., and A.Y. supervised the project and led the collaboration efforts. L.L and Y.W synthesized the upconversion nanocrystals and performed theoretical simulations. L.L. and W.C. conducted the optical experiments. N.D.D., Q.C., and L.L. prepared polymeric microbeads. D.B.L.T. and S.C. conducted the optogenetic experiments. L.L. and X.L. wrote the manuscript. All authors participated in the discussion and analysis of the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Journal peer review information: Nature Communications thanks Jean-Claude Bünzli and the other anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Liang, L., Teh, D.B.L., Dinh, ND. et al. Upconversion amplification through dielectric superlensing modulation. Nat Commun 10, 1391 (2019). https://doi.org/10.1038/s41467-019-09345-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-019-09345-0
- Springer Nature Limited
This article is cited by
-
Giant excitonic upconverted emission from two-dimensional semiconductor in doubly resonant plasmonic nanocavity
Light: Science & Applications (2022)
-
Upconversion luminescence enhancement of the composite films by coupling local surface plasmon effect and photonic crystals effect
Applied Physics A (2022)
-
Anomalous upconversion amplification induced by surface reconstruction in lanthanide sublattices
Nature Photonics (2021)
-
Internal OH− induced cascade quenching of upconversion luminescence in NaYF4:Yb/Er nanocrystals
Light: Science & Applications (2021)
-
Lipid droplets as endogenous intracellular microlenses
Light: Science & Applications (2021)