Abstract
Multimodal platforms combining electrical neural recording and stimulation, optogenetics, optical imaging, and magnetic resonance (MRI) imaging are emerging as a promising platform to enhance the depth of characterization in neuroscientific research. Electrically conductive, optically transparent, and MRI-compatible electrodes can optimally combine all modalities. Graphene as a suitable electrode candidate material can be grown via chemical vapor deposition (CVD) processes and sandwiched between transparent biocompatible polymers. However, due to the high graphene growth temperature (≥ 900 °C) and the presence of polymers, fabrication is commonly based on a manual transfer process of pre-grown graphene sheets, which causes reliability issues. In this paper, we present CVD-based multilayer graphene electrodes fabricated using a wafer-scale transfer-free process for use in optically transparent and MRI-compatible neural interfaces. Our fabricated electrodes feature very low impedances which are comparable to those of noble metal electrodes of the same size and geometry. They also exhibit the highest charge storage capacity (CSC) reported to date among all previously fabricated CVD graphene electrodes. Our graphene electrodes did not reveal any photo-induced artifact during 10-Hz light pulse illumination. Additionally, we show here, for the first time, that CVD graphene electrodes do not cause any image artifact in a 3T MRI scanner. These results demonstrate that multilayer graphene electrodes are excellent candidates for the next generation of neural interfaces and can substitute the standard conventional metal electrodes. Our fabricated graphene electrodes enable multimodal neural recording, electrical and optogenetic stimulation, while allowing for optical imaging, as well as, artifact-free MRI studies.
![](http://media.springernature.com/lw685/springer-static/image/art%3A10.1038%2Fs41378-022-00430-x/MediaObjects/41378_2022_430_Figa_HTML.png)
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Introduction
Neural interfaces are tools that enable bidirectional interactions with the human nervous system. To allow for personalized therapies, which is the ultimate goal of bioelectronic medicine, the functional neural behavior has to be well understood. Conventional neural recording and stimulation methods provide insufficient spatio-temporal resolution for neuroscientific research1. In addition, it is of paramount importance to monitor neural activity systematically to uncover the interconnections between the neurons and neural clusters. In recent years, several methods such as optical imaging (e.g., calcium or fluorescence imaging)2,3, optogenetics3,4, and magnetic resonance imaging (MRI)5,6 have emerged to assist neuroscientists to decipher the neural structure and function. These, combined with electrical neural recording and stimulation in a multimodal fashion, can pave the way towards a much deeper understanding and mapping of the nervous system3,4,7.
Conventional noble metal electrodes, such as gold (Au) or platinum (Pt), are the most common tools for recording neural activity and stimulating neurons due to their good electrical performance, high biocompatibility, and chemical stability. However, due to their opaque nature, they prevent any in vivo optical imaging at the site of stimulation (underneath the electrodes). In addition, due to photoelectrochemical effects, Au electrodes might produce photo-induced artifacts when used for electrophysiology in optogenetic devices8,9. Platinum-iridium (Pt-Ir) alloy electrodes, on the other hand, cause image artifacts in MRI due to the magnetic susceptibility of Pt being different from that of the surrounding tissue10,11.
Therefore, there is a need for optically transparent and MRI-compatible electrodes. Indium-Tin-Oxide (ITO) and carbon-based electrodes are the most commonly used transparent conductive electrodes. However, ITO cannot be used in flexible devices due to its brittleness that might cause crack formation12,13,14. Among all transparent carbon-based electrodes, graphene is the most attractive material due to its high thermal/electrical conductivity, broad-spectrum transparency, and flexibility15. In addition, graphene-coated copper wires16 and graphene-fiber electrodes made of graphite oxide17 have been proven to be MRI compatible due to their magnetic susceptibilities being close to that of tissue. Therefore, graphene has the potential to be the ideal electrode material candidate for the next generation of optically transparent, and MRI-compatible multimodal neural interfaces.
The majority of research on graphene-related materials concerns graphene-oxide (GO) and reduced-graphene-oxide (rGO) materials. However, due to the electrically insulating properties of GO, its combination with other conducting materials, such as conductive polymers and metals, is necessary to fabricate electrodes. rGO’s large effective surface area leads to low impedance and high charge-injection capacity (CIC) that are both important for neural recording and stimulation18. However, its electrical conductivity does not reach that of pristine graphene19. More importantly, a cytotoxicity concern towards different types of cells using GO and rGO has been raised recently20.
The most common fabrication method for growing graphene is chemical vapor deposition (CVD) which has the advantage of simplicity and the possibility to create high-quality graphene on a metal catalyst that can span a large surface area21. However, the required high graphene growth temperature (usually ≥ 900 °C) prevents direct graphene growth on wafers with already present polymers, a fundamental component of flexible implants. Therefore, current state-of-the-art graphene electrode fabrication has been mostly focusing on graphene transfer processes, where graphene is grown on a copper (Cu) catalyst, and subsequently transferred to the required polymer used for the implant22,23,24,25. Sacrificial polymer supporting layers, such as polymethylmethacrylate (PMMA), facilitate the transfer process. This method, despite its popularity, has reliability and scaling issues26 regarding preserving the quality of the material after transfer, polymer residues from the supporting layer, or an additional cleaning process to remove any polymer residues27. Finally, metallic particles from the, typically, non-biocompatible Cu catalyst layer can impact the implant’s biocompatibility. Apart from that, in such processes the first polymer layer is present before the graphene transfer. This limits the electrode post-processing options that have the potential to e.g., improve the conductivity28.
Other techniques to fabricate graphene electrodes, such as direct laser pyrolysis of porous graphene on a polyimide substrate29, or laser carbonization of parylene-C to create graphitic carbon as a coating on metal electrodes30, have also been reported. However, to date, laser pyrolysis fabrication has been successfully used only for devices with relatively large electrodes (200–700 μm diameter). The main limitation of this technology is the laser resolution, in comparison with the resolution achieved by photolithographic methods, crucial for miniaturization and the formation of high-density arrays. In addition, these low-quality carbon-based electrodes are not highly optically transparent and suffer from reproducibility issues.
Therefore, using CVD graphene is, so far, the best approach for developing neural electrodes. CVD graphene itself can be created as a monolayer or multilayer, depending on the metal catalyst and the process parameters used31. Although monolayer graphene has shown compatibility with neuro-imaging and optogenetics27, previously reported works suggest that monolayer graphene in an undoped state suffers from low sheet conductivity32. This prevents the use of graphene instead of long metal tracks, reducing the total implant transparency. Moreover, graphene made of fewer layers is more prone to damage during the fabrication and implantation processes.
On the other hand, increasing the number of graphene layers reduces the sheet resistance but also reduces the optical transparency33,34. Recent research in the field of supercapacitors showed that multilayering of graphene (up to a threshold of 4 to 6 layers) could result in higher electrochemical capacitance35, and previously reported stacked four monolayer graphene neural electrodes have demonstrated good electrochemical characteristics36. However, literature suggests that adding graphene layers in a transfer-based process requires more transfer steps, which, in turn, leads to more polymer residues between layers and therefore lower optical transparency34.
The aim of the current study is to use CVD multilayer graphene to create fully-transparent and MRI-compatible neural electrodes with better electrochemical performance. To prevent the presence of polymer residues caused by the transfer process, but also, to make the process more compatible with conventional wafer-scale fabrication and post-processing technologies, we have adapted the process reported in37, which uses a transfer-free method to grow graphene on a Molybdenum (Mo) catalyst38, to create the neural electrodes. This method enables the fabrication of a multilayer graphene electrode without any transfer involved. The electrodes’ impedance, charge storage capacity (CSC), and CIC are assessed and compared to Pt and Au electrodes with the same size and geometry. In addition, the developed electrodes were assessed for compatibility with optogenetic stimulation and MRI, versus Au and Pt electrodes, respectively.
Methods
Fabrication process
Suspended graphene electrode
Multilayer graphene neural electrodes were fabricated as illustrated in Fig. 1.
Fabrication process steps a Oxide deposited on both sides of a DSP Si wafer, patterned, and etched on the backside, b Mo deposition and pattern, c Graphene growth, d Al (1%Si)/Ti deposition and pattern on the electrodes and contact pads, e Parylene-C deposition, f Al/Ti hard mask deposition and pattern for parylene etching followed by a DRIE process, g Frontside oxide removal followed by Mo wet etching, second parylene deposition on the backside, and parylene etching on the frontside, h Hard mask wet etching, i Cutting the sample.
First, 2 and 4 μm plasma-enhanced chemical vapor deposition (PECVD) oxide was deposited on the front-and backside of a double-sided polished (DSP) 100 mm silicon (Si) wafer (Fig. 1a). The backside oxide is patterned and etched to define the area for a subsequent deep reactive ion etching (DRIE) step. Next, 50 nm molybdenum (Mo) is sputter-deposited at 50 °C on the frontside of the wafer, which serves as the catalyst metal layer for graphene growth. After Mo deposition, lithography steps are employed to define the final design of the electrode array and tracks (Fig. 1b). Etching of the Mo layer is then performed at 25 °C using an ICP etcher with 50 W RF power, 500 W ICP power, 5 mTorr pressure, and 30 and 5 sccm Cl2 and O2 gas flows, respectively. Graphene is selectively grown on Mo as shown in Fig. 1c using a CVD process (Aixtron Black Magic Pro tool) at temperatures of about 935 °C using 960, 40, and 25 sccm of Ar, H2, and CH4 gas flows, respectively, at 25 mbar pressure for 20 min and cooled to room temperature under an Ar atmosphere.
The flexible, polymeric-based encapsulation is added in the next step and subsequently the electrodes and contact pads are exposed. A layer of aluminum (Al) is needed to prevent damaging the graphene layer while etching the polymer over the electrodes and contact pads. However, since the adhesion of Al to graphene is poor, an additional titanium (Ti) layer, due to a better microstructure of the film39, is needed to act as an adhesion promoter. Hence, prior to polymer deposition, the Al (1%Si)/Ti stack (100 nm of Ti, followed by 675 nm of Al) is sputtered at 50 °C on top of the existing graphene layer and photolithographically patterned (wet etching performed using a 0.55% hydrofluoric acid (HF) solution) to cover the graphene features (Fig. 1d).
Then, 10 μm of parylene-C is CVD deposited at room temperature (using a SCS PDS 2010 parylene coater) (Fig. 1e). Next, in preparation for the upcoming polymer etching step, a hard mask of 500 nm/100 nm Al (1%Si)/Ti is sputter-deposited (at 1 kW, 25 °C) and patterned (dry etched at 25 °C using an ICP etcher with 50 W RF power, 500 W ICP power, 5 mTorr pressure, and 30 and 40 sccm Cl2 and HBr gas flows, respectively, with a long over-etching time with 15 and 30 sccm Cl2 and HBr gas flows, respectively, to remove potential Al particles from the polymer layer) (Fig. 1f). The hard mask deposition temperature is intentionally kept low to prevent exceeding the parylene glass transition temperature and avoid crack formation.
Finally, a DRIE process on the backside of the wafer lands on the frontside oxide (Fig. 1g), which is then plasma-etched (using an AMS110 etcher (Alcatel) with 300 W RF power, and 17, 150, and 18 sccm C4F8, He, and CH4 gas flows, respectively). Mo is removed at this stage by wet etching in hydrogen peroxide (H2O2). Graphene will not be accidentally removed in this step as it has already adhered well to the top polymer. Subsequently, the second parylene layer is deposited on both sides of the wafer encapsulating the implant.
To remove the second deposited parylene layer on the frontside and expose the electrodes and contact pads, the frontside parylene is plasma-etched (using the AMS110 etcher (Alcatel) with 40 W LF power, 15 sccm of SF6 and 185 sccm of O2), landing on the Al protective layer, which is then, together with the hard mask, removed in 0.55% HF (Fig. 1h). At this point, the graphene layer sandwiched between two layers of parylene-C with exposed graphene on the electrodes and contact pads is ready to be cut out of the Si frame (Fig. 1i).
Details of the mask design used for the electrode arrays can be found in Fig. S1.
Graphene, Pt and Au electrodes on Si
For rapid prototyping and to investigate and compare the electrode properties of graphene with those of Pt and Au of similar size and geometry, non-suspended devices were fabricated. For this version, parylene insulation is substituted by photoresist to simplify the processing. The fabrication process for these devices is shown in Figs. S2, S3, for graphene and metal (Pt and Au) electrodes, respectively. To contact the electrodes, stainless steel wires are attached to the contact pads using silver (Ag) ink, subsequently covered with a drop of polydimethylsiloxane (PDMS) to enhance the mechanical stability.
For the graphene variant, the devices are at this point placed inside a H2O2 bath to remove Mo only on the electrodes. The Mo is kept on the contact pads to make a better contact with the attached metal wire.
Electrode characterization
Sheet resistance and optical transmittance
Different growth times (20, 40, and 60 min) were used to create graphene with various thicknesses. Longer growth times result in a larger number of layers. To compare these, both their sheet resistance and optical transmittance are measured. For the sheet resistance, Van der Pauw structures were made, and four-point probe measurements were performed with a Cascade Microtech probe station (see Fig. S4 for more details).
To evaluate the optical transmittance, graphene sheets were grown and transferred to a glass microscope slide (details on the transfer method can be found in Fig. S5). The optical transmittance measurement was conducted using a PerkinElmer Lambda 950 UV/Vis spectrophotometer (PerkinElmer, Waltham, Massachusetts). The wavelength range for the measurement was from 300 to 900 nm. Reference measurements were also performed for only the glass slide. The number of graphene layers can be calculated from the optical transmittance by calculating the total absorbance of the multilayer graphene and comparing it with 2.3% absorbance of a monolayer graphene40,41.
To evaluate the quality of a transparent conductive film, a figure of merit (FOM) is used; it is calculated for all graphene thicknesses based on the optical transmittance (T) at 550 nm wavelength and the sheet resistance (Rsh) and can be found in the Supplementary Notes.
Electrochemical impedance spectroscopy
Electrochemical impedance spectroscopy (EIS) was used to assess the electrochemical properties of the electrodes. The measurements were performed in phosphate-buffered saline (PBS) in a three-electrode setup with a Pt electrode (3 mm diameter (BASI Inc.)) as a counter electrode (CE), a leakless miniature silver/silver chloride (Ag/AgCl) (eDAQ) as a reference electrode (RE), and the graphene, Au and Pt electrodes fabricated in this work as the working electrodes (WE). The setup was kept inside a Faraday cage during the measurements. All the electrodes were connected to a potentiostat (Autolab PG-STAT302N) that applied a 10 mV RMS sinusoidal voltage between the WE and the RE and measured the current between the WE and the CE42. Finally, the impedance magnitude and phase were plotted over frequencies ranging from 1 Hz to 100 kHz.
Cyclic voltammetry
Cyclic voltammetry (CV) is frequently used to calculate the amount of charge that an electrode can inject into the tissue43. This measurement was also performed using the same three-electrode setup. The water window for graphene was chosen from −0.8 to 0.6 V and used as the CV potential range. As the CSC highly depends on the scan rate, the measurements were performed with various scan rates (0.1, 0.2, 0.6, and 1 V/s). Both the total and cathodic CSC were calculated.
Voltage-transient measurements
Voltage-transient measurements are used to estimate the maximum charge that can be injected by means of a constant current stimulation pulse42,43,44. The voltage transient was recorded in the same three-electrode configuration by applying a cathodic-first biphasic symmetric current pulse between the WE and CE (1 ms pulse width, 100 μs interphase delay) in the PBS solution. In the voltage transients between the WE and the RE, an immediate resistive potential drop (access potential (Va)) is observed at the onset of the cathodic pulse followed by a gradual potential decrease due to the capacitive charging of the electrode-tissue interface. The potential reaches its minimum value at the end of this pulse. The interface polarization (Ep) is evaluated by eliminating the resistive potential drop from this minimum potential (Ep = Emin − Va). Next, the applied current amplitude is increased until the interface polarization reaches the cathodic water window extracted from the CV measurement. It should be noted that the anodic interface polarization must also not exceed the anodic water window. Finally, the maximum cathodic CIC of the electrode is calculated based on the maximum current amplitude multiplied by the pulse width and divided by the electrode surface area44.
Photo-induced artifact test
When shining light on the metal electrode, electrons from the metal surface might be ejected and a small transient potential is created that could interfere with the recorded signal from the neurons. This signal is created due to the photoelectrochemical effect and is called a photo-induced artifact8,9.
Here, we tested our multilayer graphene in comparison with gold electrodes using an optical fiber coupled with an 470 nm LED. The setup used for this test is shown in Fig. S6. A safe range of light stimulation intensity for in vivo experiments is up to ~75 mW/mm2 for short pulses from 0.5 to 50 ms45. In this experiment, rhythmic rectangular pulse stimulation with 10 ms pulse duration at 10 Hz and 50 mW/mm2 light intensity was applied to both graphene and the Au electrodes while immersed in a PBS solution. The power spectrum of the recorded signal was investigated for light-induced artifacts. In addition, this test was performed for three different graphene thicknesses to compare the effect of thickness on the produced artifact.
MRI compatibility test
To investigate the MRI compatibility of multilayer graphene and Pt electrodes, samples were prepared as follows. To simulate a brain-tissue environment, a phantom was prepared by dissolving 1 g agarose in 100 ml PBS in a Petri dish, where the suspended graphene (Fig. 1) and Pt electrodes were subsequently immersed, and any bubbles were removed using a Q-tip. Finally, the phantom was solidified and placed in a water bath to mitigate the effect of susceptibility artifacts at the edge of the phantom caused by the phantom–air interface to be able to detect potential artifacts from the electrodes.
An image artifact is usually detected as a specific signal dropout that clearly obstructs a portion of the image around the electrodes and prevents visualization of brain structures where neural signals are recorded, or electrical stimulation is applied. The MR images of the phantom were acquired with a clinical 3 T scanner (Philips Ingenia, Best, The Netherlands). The following sequences were used to acquire MRI images: (1) High resolution 3D T2*-weighted dual-echo gradient recalled echo (GRE) sequence; (2) Multi-slice GRE sequence with single-shot EPI (echo-planar imaging) readout; (3) Low resolution T2* mapping performed with a multi-echo GRE sequence; (4) Ultra high resolution B0 mapping based on multi-echo GRE phase imaging.
B0 maps are analyzed to quantitatively assess B0 field distortion introduced by the electrodes. A region-of-interest (ROI) is defined to detect the field shifts induced by the electrodes. Then, a background field removal (BFR) method is performed using a high-pass or Gaussian filter with a standard deviation of 23 to remove the field distortions originating from outside of the ROI. The sequences and their corresponding parameters to acquire the MRI images are provided in detail in Table S1.
Results
Fabricated devices
The final suspended graphene electrode with parylene substrate is shown in (Fig. 2a). The polymer layer can also be substituted with PDMS based on the application and its required mechanical properties. The suspended graphene electrode with a larger number of electrodes and contact pads with PDMS substrate is shown in (Fig. 2b).
Optical images of the 340 μm diameter electrodes before and after Mo removal are shown in Fig. 2c. The holes on the electrode surface are related to the mask design leaving the device with a surface area of 68,320 μm2 as explained in Fig. S1.
Raman spectroscopy using a laser with a 633 nm wavelength on the electrode surface was performed after Mo removal to confirm the presence of graphene on the electrode surface. As shown in Fig. 2d, three distinct peaks can be observed: a D peak (gray) at 1337 cm−1 with a full-width at half maximum (FWHM) of 61.02 cm−1, a G peak (green) at 1586 cm−1 related to the sp2 C–C bonds forming the graphene lattice and having a FWHM of 33.32 cm−1, and a 2D peak (yellow) around 2670 cm−1 with a FWHM of 62.20 cm−1. The ratio between the intensities of the D and the G peaks (ID/IG = 0.38) indicates the defects in the graphene layer, which in this case indicates a low number of defects after Mo removal. This ratio matches with the reported values for graphene on Mo for gas sensing applications46. The ratio between the intensities of the 2D and the G peaks (I2D/IG = 0.74) confirms the presence of multilayer graphene as the ratio is less than 140. In addition, from the shape of the single-peaked 2D band, it can be postulated that the graphene is turbostratic47,48.
Sheet resistance and optical transmittance
The sheet resistance (Rsh) was measured on 27 Van der Pauw structures for different graphene growth times. The average (plus sign) values for Rsh are depicted in the box plot in Fig. 3a and reported in the Table 1 for 20, 40, and 60 min graphene growth times. There was a strong correlation between the Rsh and the location on the wafer for all conditions. The structures in the center of the wafer showed the lowest Rsh, and the structures towards the edge showed higher Rsh. This is possibly due to the single zone heating element in the chamber causing a higher temperature close to the center of the wafer, which results in thicker graphene with a lower defect density.
a Sheet resistance of three different graphene recipes (growth time: 20, 40, and 60 min) showing the maximum, upper quartile, median (red line), average (plus sign), lower quartile, and minimum values, b Optical transmittance measurements for different graphene growth times (the effect of the glass slide is removed).
Furthermore, the average Rsh was lower for a longer growth time. The variation of the Rsh over the wafer was smaller for the graphene with a longer growth time. That could be explained by the isothermal growth process of graphene, which indicates that with the increased thickness of graphene, the growth rate is slower as carbon has to diffuse through a thicker carbon layer. It has recently been shown for graphene grown on a Nickel (Ni) catalyst that the rate of isothermal graphite growth slows down with increasing exposure time, which might be due to the increased coverage of the catalyst surface with graphite that blocks the precursor supply from the Ni catalyst49. Another explanation is the low solubility of Mo (0.0026 weight % at 1000 °C) for carbon atoms. Mo will be saturated faster in the middle, and thus the thickness will not increase further. Therefore, we postulate that with a longer growth time, the thickness of the graphene on the edges of the wafer becomes more similar to the thickness in the center.
Optical transmittance measurements performed on graphene grown for 20, 40, and 60 min after removing the contribution of the glass slide are shown in Fig. 3b. The optical transmittances for graphene at 550 nm are presented in Table 1. The optical transmittance at 550 nm is typically used for the calculation of graphene number of layers41. According to these measurements, 20, 40, and 60 min graphene growth times lead to ~7, 10, and 17 graphene layers, respectively. These confirm that increasing the growth time increases the thicknesses of graphene and reduces the optical transmittance.
The calculated FOM is reported in Table 1 for three different growth times. These values are comparable with the result reported for CVD graphene50 and also higher than the theoretical value of (2.55) calculated from the same equation for an undoped monolayer graphene in51. Finally, a 20 min graphene growth time was chosen for the final electrode to achieve a higher optical transparency.
Electrochemical impedance spectroscopy
EIS measurements were performed on 15 graphene electrodes with 20 min growth time, and the obtained graphs can be found in Fig. 4a, b.
a Average impedance magnitude and b Phase angle plots (±standard deviation shaded in gray) for fifteen graphene electrodes, c Proposed equivalent circuit model for the multilayer graphene electrode and the average values of the parameters used in the equivalent circuit model, d Impedance magnitude and e Phase angle plots for fifteen graphene electrodes in black (average values), Au electrodes in orange, and Pt electrodes in blue. All electrodes are of the same size and geometry.
In the Bode plots, the deviation from the average impedance and phase is shown in the shaded gray area. This could be related to slight variations of graphene growth over the Si wafer. EIS measurements were performed for 3 graphene electrodes with 40 min growth time and 3 electrodes with 60 min growth time as shown in Fig. S7. To be able to draw a conclusion a larger number of samples is needed as there are noticeable variations in the impedance at 1 kHz.
The proposed equivalent circuit model for multilayer graphene electrodes is shown in Fig. 4c. In this model, Rs is the resistance of the solution, ZCPE is the constant phase element representing the Helmholtz double layer capacitance. Rct is the charge-transfer resistance used to simulate Faradaic reactions and ZWB is the bounded Warburg impedance used to simulate the diffusion process.
It was found that the double layer capacitance for graphene is in series with the quantum capacitance (Cq) caused by the limited electronic density of states (DOS)35,52. Cq is relatively small for monolayer graphene and therefore dominant at low frequencies. Recent research shows that, by increasing the number of graphene layers, Cq is increased and its effect on total capacitance becomes less dominant35. It has also been shown that for multilayer graphene another capacitance is added in series with Cq, which is called the dielectric capacitance (Cdiel). This capacitance is caused by a shielding effect inside the electrode due to a generated electric field. By increasing the number of graphene layers, this shielding region expands leading to a reduction in Cdiel53.
The equivalent circuit model was fitted to the Bode plots for all fifteen graphene electrodes (20 min growth time) using the equations presented in the Supplementary Notes. Then, the averages for all parameters were calculated and are presented in the table reported in Fig. 4c. Cs is the series equivalent capacitance of Cdiel and Cq. n is a constant in the range between 0 to 1 and equals 0.931, which shows the highly capacitive behavior of the constant phase element. Moreover, the high value of Rct proves that the electric behavior is mainly capacitive and thus there is little Faradaic current at the electrode-electrolyte interface.
EIS measurements were performed on Au and Pt electrodes with the same dimensions (Fig. 4d, e). The average impedances at 1 kHz, which are typically reported for neural electrodes, are ~7.5, 8.7, and 27.4 kΩ for the Au, Pt, and graphene electrodes, respectively. Furthermore, all electrodes exhibit capacitive behavior at low frequencies. The comparison between the impedance at 1 kHz of the graphene electrodes fabricated in this work and the CVD graphene electrodes fabricated in other works can be found in Table 2. The impedance is normalized to the electrode surface area to ease the comparison.
Cyclic voltammetry
Cyclic voltammetry was performed on the same 15 graphene electrodes. The CV curves for graphene (20 min growth time), Au, and Pt are shown in Fig. 5a at different scan rates. The CSC values were calculated based on the time integral of the CV curve and are reported in Table 2. The CSC calculated for Au is a lot lower than Pt and graphene. On the other hand, the CSC for graphene is comparable to that of Pt. However, the CSC values for graphene are higher at slower scan rates than those of Pt. This could be related to the high average surface roughness (6.75 nm) measured for 20 min graphene based on atomic force microscopy (AFM) measurements as shown in Fig. S8. At a high scan rate, for electrodes with a high surface roughness, only a fraction of the pores on the electrode surface are accessible for the electrochemical processes. On the other hand, a slower scan rate leads to a slower reactant flux, and therefore, increased accessibility to the electrode surface54.
The comparison between the CSC calculated for graphene electrodes with different thicknesses was inconclusive as the variation between the CSC of the electrodes is insignificant. Therefore, a larger number of samples is needed for 40 and 60 min graphene growth to be able to study the impact of thickness on the CSC.
Furthermore, as shown in Table 2, the CSC of our graphene electrodes is 1.8, 36, and 7 times higher compared with the graphene electrodes made from doped monolayer, two stacked monolayer, and four stacked monolayers, respectively22,23,25. Moreover, the graphene electrodes reported in24 show a high CSC at 1.0 V/s scan rate but still lower than the one reported in this work. Such a high CSC for the graphene electrode reported in24 was related to the larger potential window used for the CV measurement.
Voltage-transient measurements
The results of voltage-transient measurements for graphene, Au, and Pt are shown in Fig. 5b–d. The maximum current amplitude that could be applied to the electrodes before exceeding the safe potential window are 30, 8, and 46 μA, for graphene, Au, and Pt, respectively. The calculated CICs are 44, 11.7, and 67.33 μC/cm2 for graphene, Au, and Pt electrodes, respectively. It should be emphasized that by reducing the current pulse width, the current amplitude could be increased to ensure that the current is high enough to elicit neural activation, as pulse widths shorter than 0.6 ms are generally employed in neural stimulation43. However, this result still can be used as an indication of the CIC for neural stimulation.
Photo-induced artifact test
The power spectra of the recorded signals for Au and graphene electrodes while shining 10 Hz light pulses on their surface are shown in Fig. 6. The spectra are normalized to the first harmonic of Au electrode. No artifact was detected in the power spectrum of graphene electrodes. On the other hand, for Au electrodes, the fundamental frequency component, but also harmonic components at 20, 30, 40, 50 Hz, etc., are observed. The measurement was repeated for graphene grown with different thicknesses and no artifacts were revealed.
MRI compatibility test
As shown in Fig. 7a, an MRI compatibility test was performed for graphene and Pt electrodes in a 3 T MRI scanner. In this test, the eventual introduction of susceptibility artifacts that would then lead to signal dropout was investigated. To do this, T2*-weighted images were acquired because they accentuate local susceptibility effects. However, no electrode-related image artifact was detected in these images (Fig. 7b). Therefore, EPI images, which are even more sensitive to B0 inhomogeneity and then actual T2* maps were acquired. No image artifact was detected around the electrodes in the T2*-weighted image shown in Fig. 7c as well. The T2* maps represented in Fig. 7d also did not reveal any artifact around the electrodes. The lack of any artifact around the Pt electrode could be related to the very small thickness (100 nm) of the Pt electrodes.
a Immersed Pt and graphene electrodes in a phantom, b T2*-weighted image with no artifact from the electrodes, c T2*-weighted image acquired with EPI readout resulting in an artifact-free imaging, d T2* maps of the electrodes without any artifact, e Baseline magnitude image, B0 maps, and the high-pass filtered image of the B0 maps of the electrodes.
However, the B0 map acquired at a high resolution in a sagittal view shows a differential field response around Pt and graphene electrodes (Fig. 7e). The field shifts induced by the electrodes are much smaller than the spatial inhomogeneity of the main magnetic field. Therefore, the field distortions originating from outside the ROI need to be removed using BFR. Then, the field distortion introduced by the electrodes becomes vaguely visible, and it is apparent that the effect is much stronger for Pt than for graphene. The mean value of the field distortion around Pt and graphene was averaged over fifteen repetitions resulting in 63.33 ± 67.02 and 3.4 ± 5.42 Hz variations around the main magnetic field value (B0 = 3 T), respectively. This shows that the Pt electrode causes about 18.6 times higher magnetic field distortion than the graphene electrode due to its higher magnetic susceptibility than the surrounding tissue.
Discussion
Multilayer graphene electrodes were fabricated using a wafer-scale transfer-free process. The use of CVD processes for graphene synthesis gives the opportunity of developing graphene layers only over desired areas, since the catalyst used can be patterned before graphene growth. Mo is chosen as a catalyst layer due to the possibility of growing thin and uniform layers of graphene because of its extremely low carbon solubility, thus creating a self-limiting growth process55. Moreover, the thermal expansion coefficient (CTE) of Mo in comparison with Cu and Ni is much closer to the one of Si, hence, Mo is less prone to wrinkle creation during high temperature graphene growth56,57. Additionally, catalyst residues are an important concern in an implantable device. Cu has shown toxicity after histopathological evaluation in the cerebral cortex and categorized as a toxic material for the human body58,59. Mo has shown biocompatibility60and biodegradability61,62 and therefore, is a great substitute for Cu as a catalyst material for biomedical applications. In addition, energy dispersive X-ray (EDX) analysis performed on our graphene electrode after Mo removal revealed only 0.03% weight percentage of Mo residue on the electrode surface as shown in Fig. S9.
The use of a transfer-free process adds significant advantages to the fabrication process. The graphene transfer method is a complicated process and the graphene layer is prone to crack formation, polymer contamination, catalyst residues, wrinkling, and folding26. Therefore, the resulting graphene implant performance might have a variation from device-to-device and wafer-to-wafer.
However, due to the transfer-free process used in this work, less defects and misalignment are expected in a graphene layer compared to transferred graphene. Subsequently, the absence of any polymer residues results in high optical transparency. More importantly, the transfer-free process is more compatible with conventional wafer-scale fabrication processes and results in a higher yield, as shown by the authors in ref. 63. This could provide the possibility of monolithic integration of active circuitry to the device prior to graphene growth. The proposed fabrication process can be also an advantageous method for the fabrication of optoelectronic devices.
The process also allows for the addition of arbitrary polymers at the end of the fabrication process based on their mechanical characteristics and the application requirements. Reference64 and65 also shows the use of a multilayer stack for the encapsulation. In these cases, the mechanical properties of the device can be tuned by changing the thickness of each layer based on the application.
Multilayer graphene could cause a lower sheet resistance for graphene tracks compared to monolayer graphene as the sheet resistance is inversely proportional to the thickness of the film. Moreover, having multiple graphene layers provides additional transport paths for the charge carriers, which increases the conductivity of graphene. Recent research shows that increasing the number of layers to reduce the sheet resistance in a transfer process leads to optical transmittance reduction not only due to the added layers but also due to the polymer residues on each layer from the transfer process. Furthermore, since the transfer process can induce defects in the graphene lattice, for the same number of layers, fewer transfers show lower sheet resistance33.
The results obtained by the sheet resistance and optical transmittance measurements in this work show sheet resistance and optical transparency reductions by increasing the graphene growth time. Besides, the additional layers are expected to enhance the mechanical and electrical reliability66. Therefore, 20 min graphene growth was chosen to make graphene-based devices that are optically transparent enough to be used for modern neuroscientific research such as optogenetics and in vivo optical imaging. It should be noted that doping could decrease the sheet resistance even further but this was not the focus of this work.
A thorough characterization of the properties of the graphene electrodes presented here was conducted and results are summarized in Table 2.
A comparison between our multilayer graphene with Au and Pt electrodes showed only 3–4 times higher impedance (1 kHz) for graphene electrodes. The multilayer graphene electrodes fabricated in this work showed a lower area-normalized impedance compared to other undoped CVD-based graphene electrodes.
CV measurements showed that our graphene electrodes are comparable to Pt electrodes in terms of CSC. Graphene electrodes outperform Pt electrodes when using slower scan rates for CV measurements. This could be related to the high graphene surface roughness that could be more accessible for ion fluxes at lower frequencies. The CSC at different scan rates was measured to be able to compare the result with state-of-the-art graphene electrodes. It was shown that our multilayer graphene has the highest CSC reported so far for CVD graphene electrodes.
The significant improvement in CSC for the multilayer graphene compared to monolayer graphene could be explained by the effect of the quantum capacitance in series with the double layer capacitance. By increasing the number of graphene layers, the quantum capacitance is increased. Therefore, this capacitance is no longer dominant for multilayer graphene and the total capacitance will be increased.
On the other hand, voltage-transient measurements showed comparable CIC for both graphene and Pt. However, to substitute conventional metal electrodes, the CIC could be further improved using chemical dopants or surface functionalization methods to give graphene the possibility to compete with Pt electrodes. In fact, other transparent materials such as poly (3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) and carbon nanotube (CNT) with great CIC (up to 15 and 1.6 mC/cm2, respectively) and low impedance due to their high surface area are other electrode candidates43. These have been added as coating materials on graphene to improve its characteristics67,68.
The graphene electrodes in24 appear to be capable of higher CIC than what we achieved. This is probably related to the unusually large potential window used in the CV measurement in24. A detailed study on the safe potential limit used for CV measurement for graphene material is hence necessary to further appreciate the capabilities of graphene as a stimulation electrode.
Regarding photo-induced artifacts, a previous report for a monolayer graphene electrode tested with a 470 nm light emitting diode (LED) light source did not show any artifact27. However, a photo-induced artifact was observed with stacked four monolayer graphene tested using blue laser diodes25. Therefore, it was uncertain whether the artifact was induced due to a larger thickness of graphene or due to the different light sources used for this test.
The photo-induced artifact test performed in this work using an LED light source, showed no artifact on the power spectrum of the recorded signal picked up from the graphene electrode. However, visible peaks were observed using the Au electrode. The same measurement with different thicknesses of graphene still did not show any artifact. This could prove the lack of dependence of photoelectrochemical effect on the graphene thickness. However, to be able to conclusively argue about such independence, additional characterization would be needed. More importantly, LEDs were used as the light source in this test. It is possible that when a coherent light source, i.e., a laser diode, is used instead, photo-induced artifacts will be generated9.
Moreover, it should be noted that for a thorough investigation of the photo-induced artifact, this test must be performed in an in vivo condition as the light scattering and absorption in tissue differs from that in a simple PBS environment. However, this PBS test is a good first indicator and can additionally provide information about the effect of increased thickness on any generated artifact.
The MRI compatibility of graphene encapsulated Cu wires16 and graphene fibers17 has been recently confirmed. The MRI test performed in this work shows that CVD graphene electrodes encapsulated with parylene-C can be considered MRI compatible. This could be due to the small difference between the magnetic susceptibility of graphene and the human body. The exact value of magnetic susceptibility of graphene is unknown. However, carbon (C) in graphite form is reported to have a highly anisotropic diamagnetic susceptibility (−8.5 ppm)69, which is very close to that of brain tissue (−9.2 to −8.8 ppm)70.
On the other hand, Pt electrodes were expected to show image artifact in MRI. However no artifact was detected. Therefore, using Pt electrodes with a larger thickness or in an MRI scanner with a higher magnetic field strength (7 T or more) might generate even higher magnetic field distortion leading to more image artifacts.
No substantial heating was detected with a room temperature IR thermometer. However, the use of a phantom instead of real tissue might lead to a different temperature distribution and thus a different degree of image artifacts. Therefore, an in vivo MRI test with graphene electrodes implanted would be advantageous.
Apart from a magnetic susceptibility difference, the material conductivity and the eddy currents induced in the material by gradient switching and the RF field might cause MRI artifacts. However, the eddy current induced artifact was assumed to be negligible.
Conclusion
We presented the development and characterization of fully-transparent CVD-based multilayer graphene electrodes using a wafer-scale transfer-free process for the next generation of optically transparent and MRI-compatible neural interfaces. The electrodes were fabricated directly on a patterned Mo catalyst resulting in a multilayer graphene electrode.
The electrode showed low impedance (27.4 kΩ) at 1 kHz that is quite comparable to those of Au and Pt electrodes with the same size and geometry. A 3.5 mC/cm2 CSC was achieved based on CV measurements for graphene at a 100 mV/s scan rate that is the highest value reported for CVD graphene electrodes to date. The CIC was also calculated for graphene electrodes (44 μC/cm2) using voltage-transient measurements. Our graphene electrodes illuminated with light pulses with a repetition rate of 10 Hz did not reveal any photo-inducted artifacts for all thicknesses measured. Moreover, the fully-transparent electrodes did not show any image artifact in a 3 T MRI scanner. These results show that graphene multilayer electrodes with a high CSC and a low impedance could be used for the next generation of neural interfaces, enable multimodal electrical and optical recording and stimulation, and substitute the current standard metal electrodes, to additionally allow for MRI studies of the nervous system.
References
Giagka, V. & Serdijn, W. A. Realizing flexible bioelectronic medicines for accessing the peripheral nerves–technology considerations. Bioelectron. Med. 4, 1–10 (2018).
Grienberger, C. & Konnerth, A. Imaging calcium in neurons. Neuron 73, 862–885 (2012).
Scanziani, M. & Häusser, M. Electrophysiology in the age of light. Nature 461, 930–939 (2009).
Canales, A. et al. Multifunctional fibers for simultaneous optical, electrical and chemical interrogation of neural circuits in vivo. Nat. Biotechnol. 33, 277–284 (2015).
Shmuel, A., Augath, M., Oeltermann, A. & Logothetis, N. K. Negative functional MRI response correlates with decreases in neuronal activity in monkey visual area V1. Nat. Neurosci. 9, 569–577 (2006).
Logothetis, N. K., Pauls, J., Augath, M., Trinath, T. & Oeltermann, A. Neurophysiological investigation of the basis of the fMRI signal. Nature 412, 150–157 (2001).
Frank, J. A., Antonini, M.-J. & Anikeeva, P. Next-generation interfaces for studying neural function. Nat. Biotechnol. 37, 1013–1023 (2019).
Wu, F. et al. An implantable neural probe with monolithically integrated dielectric waveguide and recording electrodes for optogenetics applications. J. Neural Eng. 10, 056012 (2013).
Kozai, T. D. & Vazquez, A. L. Photoelectric artefact from optogenetics and imaging on microelectrodes and bioelectronics: new challenges and opportunities. J. Mater. Chem. B 3, 4965–4978 (2015).
Pollo, C. et al. Magnetic resonance artifact induced by the electrode Activa 3389: an in vitro and in vivo study. Acta Neurochir. 146, 161–164 (2004).
Schenck, J. F. The role of magnetic susceptibility in magnetic resonance imaging: MRI magnetic compatibility of the first and second kinds. Med. Phys. 23, 815–850 (1996).
Boehme, M. & Charton, C. Properties of ito on pet film in dependence on the coating conditions and thermal processing. Surf. Coat. Technol. 200, 932–935 (2005).
Alzoubi, K., Hamasha, M. M., Lu, S. & Sammakia, B. Bending fatigue study of sputtered ito on flexible substrate. J. Disp. Technol. 7, 593–600 (2011).
Liu, J., Yi, Y., Zhou, Y. & Cai, H. Highly stretchable and flexible graphene/ito hybrid transparent electrode. Nanoscale Res. Lett. 11, 1–7 (2016).
Guan, S., Wang, J. & Fang, Y. Transparent graphene bioelectronics as a new tool for multimodal neural interfaces. Nano Today 26, 13–15 (2019).
Zhao, S. et al. Graphene encapsulated copper microwires as highly MRI compatible neural electrodes. Nano Lett. 16, 7731–7738 (2016).
Zhao, S. et al. Full activation pattern mapping by simultaneous deep brain stimulation and fMRI with graphene fiber electrodes. Nat. Commun. 11, 1–12 (2020).
Apollo, N. V. et al. Soft, flexible freestanding neural stimulation and recording electrodes fabricated from reduced graphene oxide. Adv. Funct. Mater. 25, 3551–3559 (2015).
Gómez-Navarro, C. et al. Electronic transport properties of individual chemically reduced graphene oxide sheets. Nano Lett. 7, 3499–3503 (2007).
Singh, Z. Applications and toxicity of graphene family nanomaterials and their composites. Nanotechnol., Sci. Appl. 9, 15 (2016).
Angelova, P. et al. Chemistry of carbon nanostructures (Walter de Gruyter GmbH & Co KG, 2017).
Kuzum, D. et al. Transparent and flexible low noise graphene electrodes for simultaneous electrophysiology and neuroimaging. Nat. Commun. 5, 1–10 (2014).
Driscoll, N. et al. Multimodal in vivo recording using transparent graphene microelectrodes illuminates spatiotemporal seizure dynamics at the microscale. Commun. Biol. 4, 1–14 (2021).
Körbitzer, B., Krauß, P., Belle, S., Schneider, J. J. & Thielemann, C. Electrochemical characterization of graphene microelectrodes for biological applications. Chem. Nano. Mat. 5, 427–435 (2019).
Park, D.-W. et al. Electrical neural stimulation and simultaneous in vivo monitoring with transparent graphene electrode arrays implanted in gcamp6f mice. ACS Nano 12, 148–157 (2018).
Song, Y., Zou, W., Lu, Q., Lin, L. & Liu, Z. Graphene transfer: Paving the road for applications of chemical vapor deposition graphene. Small 17, 2007600 (2021).
Thunemann, M. et al. Deep 2-photon imaging and artifact-free optogenetics through transparent graphene microelectrode arrays. Nat. Commun. 9, 1–12 (2018).
Liu, X., Lu, Y., Iseri, E., Shi, Y. & Kuzum, D. A compact closed-loop optogenetics system based on artifact-free transparent graphene electrodes. Front. Neurosci. 12, 132 (2018).
Lu, Y., Lyu, H., Richardson, A. G., Lucas, T. H. & Kuzum, D. Flexible neural electrode array based-on porous graphene for cortical microstimulation and sensing. Sci. Rep. 6, 1–9 (2016).
Vomero, M., Oliveira, A., Ashouri, D., Eickenscheidt, M. & Stieglitz, T. Graphitic carbon electrodes on flexible substrate for neural applications entirely fabricated using infrared nanosecond laser technology. Sci. Rep. 8, 1–13 (2018).
Zhang, Y., Zhang, L. & Zhou, C. Review of chemical vapor deposition of graphene and related applications. Acc. Chem. Res. 46, 2329–2339 (2013).
Kireev, D. & Offenhäusser, A. Graphene and two-dimensional devices for bioelectronics and neuroprosthetics. 2D Mater. 5, 042004 (2018).
Lee, S., Lee, K., Liu, C.-H. & Zhong, Z. Homogeneous bilayer graphene film based flexible transparent conductor. Nanoscale 4, 639–644 (2012).
Kasry, A., Kuroda, M. A., Martyna, G. J., Tulevski, G. S. & Bol, A. A. Chemical doping of large-area stacked graphene films for use as transparent, conducting electrodes. ACS Nano 4, 3839–3844 (2010).
Zhan, C., Neal, J., Wu, J. & Jiang, D.-e Quantum effects on the capacitance of graphene-based electrodes. J. Phys. Chem. C. 119, 22297–22303 (2015).
Park, D.-W. et al. Graphene-based carbon-layered electrode array technology for neural imaging and optogenetic applications. Nat. Commun. 5, 1–11 (2014).
Velea, A. I., Vollebregt, S., Wardhana, G. K. & Giagka, V. Wafer-scale graphene-based soft electrode array with optogenetic compatibility. In 2020 IEEE 33rd International Conference on Micro Electro Mechanical Systems (MEMS), 421–424 (IEEE, 2020).
Vollebregt, S. et al. A transfer-free wafer-scale CVD graphene fabrication process for MEMS/NEMS sensors. In 2016 IEEE 29th International Conference on Micro Electro Mechanical Systems (MEMS), 17–20 (IEEE, 2016).
Watanabe, E., Conwill, A., Tsuya, D. & Koide, Y. Low contact resistance metals for graphene based devices. Diam. Relat. Mater. 24, 171–174 (2012).
Liu, Z., Lin, L., Ren, H. & Sun, X. CVD synthesis of graphene. In Thermal transport in carbon-based nanomaterials, 19-56 (Elsevier, 2017).
Zhu, S.-E., Yuan, S. & Janssen, G. Optical transmittance of multilayer graphene. EPL Europhys. Lett. 108, 17007 (2014).
Boehler, C., Carli, S., Fadiga, L., Stieglitz, T. & Asplund, M. Tutorial: guidelines for standardized performance tests for electrodes intended for neural interfaces and bioelectronics. Nat. Protoc. 15, 3557–3578 (2020).
Cogan, S. F. Neural stimulation and recording electrodes. Annu. Rev. Biomed. Eng. 10, 275–309 (2008).
Schiavone, G. et al. Guidelines to study and develop soft electrode systems for neural stimulation. Neuron 108, 238–258 (2020).
Cardin, J. A. et al. Targeted optogenetic stimulation and recording of neurons in vivo using cell-type-specific expression of channelrhodopsin-2. Nat. Protoc. 5, 247–254 (2010).
Ricciardella, F. et al. Influence of defect density on the gas sensing properties of multi-layered graphene grown by chemical vapor deposition. Carbon Trends 3, 100024 (2021).
Pimenta, M. et al. Studying disorder in graphite-based systems by raman spectroscopy. Phys. Chem. Chem. Phys. 9, 1276–1290 (2007).
Lenski, D. R. & Fuhrer, M. S. Raman and optical characterization of multilayer turbostratic graphene grown via chemical vapor deposition. J. Appl. Phys. 110, 013720 (2011).
Weatherup, R. S. et al. On the mechanisms of ni-catalysed graphene chemical vapour deposition. ChemPhysChem 13, 2544–2549 (2012).
Rosli, N. N., Ibrahim, M. A., Ludin, N. A., Teridi, M. A. M. & Sopian, K. A review of graphene based transparent conducting films for use in solar photovoltaic applications. Renew. Sustain. Energy Rev. 99, 83–99 (2019).
De, S. & Coleman, J. N. Are there fundamental limitations on the sheet resistance and transmittance of thin graphene films? ACS Nano 4, 2713–2720 (2010).
Xia, J., Chen, F., Li, J. & Tao, N. Measurement of the quantum capacitance of graphene. Nat. Nanotechnol. 4, 505–509 (2009).
Zhan, C. & Jiang, D.-e Contribution of dielectric screening to the total capacitance of few-layer graphene electrodes. J. Phys. Chem. Lett. 7, 789–794 (2016).
Norlin, A., Pan, J. & Leygraf, C. Investigation of electrochemical behavior of stimulation/sensing materials for pacemaker electrode applications: I. pt, ti, and tin coated electrodes. J. Electrochem. Soc. 152, J7 (2004).
Wu, Y. et al. Synthesis of large-area graphene on molybdenum foils by chemical vapor deposition. Carbon 50, 5226–5231 (2012).
Vasić, B. et al. Low-friction, wear-resistant, and electrically homogeneous multilayer graphene grown by chemical vapor deposition on molybdenum. Appl. Surf. Sci. 509, 144792 (2020).
Ricciardella, F. et al. Growth of multi-layered graphene on molybdenum catalyst by solid phase reaction with amorphous carbon. 2D Mater. 6, 035012 (2019).
Stensaas, S. S. & Stensaas, L. Histopathological evaluation of materials implanted in the cerebral cortex. Acta Neuropathol. 41, 145–155 (1978).
Geddes, L. A. & Roeder, R. Criteria for the selection of materials for implanted electrodes. Ann. Biomed. Eng. 31, 879–890 (2003).
Ribeiro, A. M., Flores-Sahagun, T. H. & Paredes, R. C. A perspective on molybdenum biocompatibility and antimicrobial activity for applications in implants. J. Mater. Sci. 51, 2806–2816 (2016).
Redlich, C., Quadbeck, P., Thieme, M. & Kieback, B. Molybdenum–a biodegradable implant material for structural applications? Acta Biomaterial. 104, 241–251 (2020).
Fernandes, C. & Taurino, I. Biodegradable molybdenum (mo) and tungsten (w) devices: One step closer towards fully-transient biomedical implants. Sensors 22, 3062 (2022).
Pezone, R., Baglioni, G., Sarro, P. M., Steeneken, P. G. & Vollebregt, S. Sensitive transfer-free wafer-scale graphene microphones. ACS Appl. Mater. Interfaces 14, 21705–21712 (2022).
Bakhshaee Babaroud, N., Dekker, R., Serdijn, W. & Giagka, V.PDMS-Parylene Adhesion Improvement via Ceramic Interlayers to Strengthen the Encapsulation of Active Neural Implants. In 2020 42nd Annual International Conference of the IEEE Engineering in Medicine & Biology Society (EMBC), 3399–3402 (IEEE, 2020).
Bakhshaee Babaroud, N. et al. Investigation of the long-term adhesion and barrier properties of a pdms-parylene stack with pecvd ceramic interlayers for the conformal encapsulation of neural implants. In 2021 23rd European Microelectronics and Packaging Conference & Exhibition (EMPC), 1–7 (IEEE, 2021).
Park, D.-W. et al. Fabrication and utility of a transparent graphene neural electrode array for electrophysiology, in vivo imaging, and optogenetics. Nat. Protoc. 11, 2201–2222 (2016).
Kshirsagar, P. et al. Transparent graphene/pedot: Pss microelectrodes for electro-and optophysiology. Adv. Mater. Technol. 4, 1800318 (2019).
Kim, G. H. et al. A high-performance transparent graphene/vertically aligned carbon nanotube (vacnt) hybrid electrode for neural interfacing. RsC Adv. 7, 3273–3281 (2017).
Lu, L. et al. Soft and mri compatible neural electrodes from carbon nanotube fibers. Nano Lett. 19, 1577–1586 (2019).
Duyn, J. H. & Schenck, J. Contributions to magnetic susceptibility of brain tissue. NMR Biomed. 30, e3546 (2017).
Acknowledgements
This work was supported by the POSITION-II project funded by the ECSEL JU under grant number Ecsel- 783132Position-II-2017-IA. Microfabrication was carried out in the Else Kooi Laboratory (EKL).
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflict of interest
The authors declare no competing interests.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Bakhshaee Babaroud, N., Palmar, M., Velea, A.I. et al. Multilayer CVD graphene electrodes using a transfer-free process for the next generation of optically transparent and MRI-compatible neural interfaces. Microsyst Nanoeng 8, 107 (2022). https://doi.org/10.1038/s41378-022-00430-x
Received:
Revised:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41378-022-00430-x
- Springer Nature Limited
This article is cited by
-
Highly-sensitive wafer-scale transfer-free graphene MEMS condenser microphones
Microsystems & Nanoengineering (2024)