Abstract
In optics, the refractive index of a material and its spatial distribution determine the characteristics of light propagation. Therefore, exploring both low- and high-index materials/structures is an important consideration in this regard. Hollow cavities, which are defined as low-index bases, exhibit a variety of unusual or even unexplored optical characteristics and are used in numerous functionalities including diffraction gratings, localised optical antennas and low-loss resonators. In this report, we discuss the fabrication of hollow cavities of various sizes (0.2–5 μm in diameter) that are supported by conformal dielectric/metal shells, as well as their specific applications in the ultraviolet (photodetectors), visible (light-emitting diodes, solar cells and metalenses), near-infrared (thermophotovoltaics) and mid-infrared (radiative coolers) regions. Our findings demonstrate that hollow cavities tailored to specific spectra and applications can serve as versatile optical platforms to address the limitations of current optoelectronic devices. Furthermore, hollow cavity embedded structures are highly elastic and can minimise the thermal stress caused by high temperatures. As such, future applications will likely include high-temperature devices such as thermophotovoltaics and concentrator photovoltaics.
Similar content being viewed by others
Introduction
Increasing the refractive index contrast (Δn) of the components of an optoelectronic device can improve its optical functionality1,2,3. This assertion can be verified by calculating the diffraction strength of a grating with a sinusoidal variation of the refractive index n(r), which is given by:
where n0 and k are the average refractive index and the propagation vector of the grating, respectively. The electric field of the diffracted light \(E\left( {\vec r} \right)\) is then obtained by applying Bloch’s theorem, which is expressed as
where \(A\left( {\vec r} \right)\) is a periodic function with the same periodicity as n(r) and \(\vec k_{inc}\) is the wave vector of the incident light. For the right-hand side of Eq. (2), the second and third terms indicate the first-order diffraction modes, for which their amplitudes and Δn have a linear relationship. Therefore, a void (i.e. n = 1) grating imparts maximum diffraction strength if it is embedded in a high-n medium. As a result, a void, also known as an air gap or hollow cavity (HC), produces a variety of enhanced or even unexplored optical features, particularly when combined with a high-n ambient medium. The term ‘cavity’ technically refers to an optical structure supporting resonant modes. Nevertheless, any hollow morphology, including air voids and gaps, will also be referred to as HC, as discussed below, for the sake of convenience.
An individual HC or an array of HCs can be exploited as a localised optical antenna4, a low-loss resonator5 or a strong-diffraction grating6, depending on the scale of the HC relative to the working spectrum. The range of applications can be categorised by function: antireflective films for lenses and solar cells7, strong scattering particles for colouration8, strong diffraction gratings for light-emitting diodes (LEDs)9 and high-reflectivity radiative coolers5 and mirrors for lasers10 (Fig. 1a). For example, Xi et al. reported that incorporation of voids much smaller than considered wavelengths into dielectrics (e.g. SiO2 and TiO2) suppressed the surface reflection by adjusting their refractive indices7. Kim et al. demonstrated angle-insensitive structural colouration by embedding monodisperse HC particles in a solid matrix8. The average spacing between the embedded HCs was readily tuned by adjusting their shell thickness, and the resulting colour was altered over the visible spectrum. Mandal et al. also created hierarchically designed polymers with micro- and nanoscale voids that efficiently backscattered sunlight at wavelengths ranging from the ultraviolet to near-infrared region, corresponding to their sizes11. They demonstrated ultrahigh solar reflectance with a near-unity thermal emittance, thus observing a 6 °C drop below the ambient temperature in the daytime. Pruessner et al. constructed high-quality microcavities using periodically arranged quarter-wavelength air gaps and integrated them into silicon waveguides10.
In addition, LEDs must minimise the ‘internal’ reflection losses for incident angles (θ) above the critical angle to improve their outcoupling efficiencies12. To this end, two-dimensional (2D) periodic9 or pseudorandom gratings13 are essential for extracting trapped photons owing to total internal reflections (TIRs). However, the diffraction strength of the gratings is impeded by Δn, given that the refractive index of the LED medium is fixed. Therefore, there have been few breakthroughs regarding light extraction. Embedding the array of HCs into LED media is an effective way to overcome this index barrier and improve the outcoupling efficiency. The HC grating is also useful for application to directional light sources. For direct-lit LED displays, substrate-side emission must be suppressed because it degrades the image resolution owing to crosstalk between adjacent pixels14. The HC grating preferentially excites high-order diffraction modes and can thus steer substrate-side emission into vertical emission through the top faces of LED devices15. Likewise, an HC-embedded high-n medium can serve as a broadband optical diffuser owing to its strong scattering characteristics, which is evident from the results of electromagnetic simulations (Fig. 1b). In the simulations, to demonstrate the Δn dependent scattering, a single hollow (n = 1.0) or silica (n = 1.5) nanoparticle was incorporated into a high-n medium (n = 1.8), and each scattering spectrum was obtained for a variety of diameters (D) of the nanoparticle. A comparison of the simulated spectra revealed that even at D < 400 nm, the hollow nanoparticles exhibited a high-amplitude scattering over the visible region.
HCs and their arrays can serve as multifunctional elements that enhance the mechanical and material properties of optoelectronic devices, as well as their optical performance (Fig. 2). In general, HC-embedded structures are highly flexible, thus alleviating the thermal stress triggered by high temperatures16. Therefore, their applications can be extended to high-temperature devices, such as thermophotovoltaics and concentrator photovoltaics. Furthermore, HCs that are sustained by a thin (<100 nm) alumina shell can assist in the release of the thermal stress that accumulates during heteroepitaxial GaN growth on a sapphire substrate, resulting in a reduced wafer bow. These mechanical features can improve the internal quantum efficiency of GaN-based LED devices. In addition, the alumina shell acts as a GaN growth template because it is transformed into an α-phase crystallinity during the fabrication of HCs at high temperatures.
We emphasise that HCs with appropriate scales can be leveraged for use in a variety of photonic applications with different spectra (Fig. 3), which is indicative of their practical versatility. In the following sections, we review specific HC-based applications: light-emission devices (e.g. LEDs and metalenses), light-absorption devices (e.g. solar cells and photodetectors) and thermal-radiation devices (e.g. thermophotovoltaics and radiative coolers). The morphological parameters (e.g. size, shape, shell material, shell thickness and density in an array) of the HCs are tailored for the intended purpose. Hence, a deep understanding of the fundamental physics regarding the propagation of light and the establishment of generic design principles is important. Furthermore, this knowledge can lead to new insights into a variety of index engineering problems at specific or broad wavelengths.
Fabrication of HCs
Various top-down approaches have been employed to fabricate HCs and their arrays. For GaN-based LED devices, the epitaxial overgrowth of GaN on a patterned GaN medium, which is prepared using lithography and etching processes, produces multiple nanoscale voids embedded in the GaN medium17,18 (Fig. 4a). This is because of the different GaN growth rates that depend on the crystalline faces. These overgrowth-induced voids improve the outcoupling efficiency because they significantly disturb the waveguide modes that carry photons trapped via TIRs. However, precise control over the morphology of voids is challenging because the initial pattern on the GaN medium tends to deform during overgrowth. This limits the enhancement of the outcoupling efficiency. Furthermore, the addition of manufacturing stages degrades the electrical properties (e.g. leakage current and threshold voltage) of LED devices, resulting in higher fabrication costs19. HCs can be embedded in a general dielectric using a wafer-bonding process20,21 (Fig. 4b). First, a pattern is defined on a dielectric substrate using standard semiconductor processes. Then, another substrate is bonded to the patterned dielectric substrate using an adhesive gel, by which an array of voids is formed. This method was used to improve the outcoupling efficiencies of organic LEDs by bonding to a transparent glass or polymer substrate. However, wafer-bonding using an adhesive gel is vulnerable to thermal stress and is not suitable for mass production. These HCs in Fig. 4c can be arranged regularly in space and sustained using thin dielectric or metal shells. To fabricate them, a resist was initially patterned using a standard lithography system (e.g. electron-beam lithography, nanoimprinting and a stepper). The pitch, diameter and height of the fabricated HCs were solely determined at the lithography step, whereas their shapes (e.g. cylinder, pyramid, and dome) were controlled to some extent by adopting appropriate thermal reflow conditions after the lithography process. The pitch, diameter (i.e. the base of a dome) and height of the HC array were readily preserved during the thermal reflow process, ensuring their strong diffraction6. Then, an alumina shell was deposited to conformally cover the resist pattern using atomic layer deposition (ALD) and removed the inner resist via calcination and/or wet etching. Additional dielectric and metal shells can be deposited with the shell material and thickness varied depending on the intended use.
To iterate, for GaN-based LED devices, an alumina shell was crystallised into the α-phase at high temperatures (typically, >1000 °C) during the calcination step22 (Fig. 4d). Therefore, the HCs with a crystalline alumina shell can be simultaneously used as a strong diffraction grating and a pristine GaN growth template. It is noteworthy that the shape of HCs varies by applications with distinct functionalities. For example, a cone is beneficial for light absorption devices such as photovoltaics because they require broadband, antireflecting performance23. In comparison, for thermophotovoltaics and radiative coolers (RCs), a cylinder is ideal because it serves as a Fabry-Pérot resonator that can augment light absorption at specific or broad wavelengths5. A dome is well suited to the growth template of GaN-based LEDs because GaN grown on a dome-shaped sapphire has fewer dislocations as well as alleviated residual strains, thus improving the internal quantum efficiency24.
Light emission devices
Optical outcouplers
III–V semiconductor light-emitting diodes
The development of high-performance III-V semiconductor LEDs has created a new lighting market. One of the key factors in the fabrication of LEDs with higher brightness and efficiency is the improvement of their outcoupling efficiencies, that is, their ability to steer light trapped within a high-n medium into a low-n background medium against TIRs. The most common strategy for improving the outcoupling efficiency of LEDs is the introduction of quasi-random or periodically patterned surfaces on a doped semiconductor layer25, reflector26, or substrate2. For example, commercial GaN-based flip-chip LEDs utilize a 3-µm-pitch periodic pattern at the interface between n-type doped GaN and a sapphire substrate (right, Fig. 5a). Although a patterned sapphire substrate (PSS) can serve as a dielectric grating to transfer the Bloch momentum to trapped photons, its outcoupling performance is restricted because the refractive indices of GaN and sapphire materials are fixed (right, Fig. 5a). To address this index barrier problem, Moon et al. fabricated the same 3-μm-pitch array of HCs on a sapphire substrate and achieved high-quality epitaxial GaN growth2 (left, Fig. 5a). An HC-embedded GaN wafer induces more vivid interference colours relative to its filled-cavity counterpart (Fig. 5b), which is indicative of its strong diffraction owing to a large Δn. Consequently, HC-based InGaN LEDs outperform commercial PSS devices in terms of optical performance (Fig. 5c). Importantly, the ultrathin (80 nm) crystalline alumina shells that cover the HCs provide a GaN growth template that is as excellent as PSS, resulting in negligible electrical degradation (inset, Fig. 5c).
Measurements of photonic band dispersion (i.e. angular transmittance spectra) on the HC and PSS samples illustrate how a high-Δn grating can yield enhanced outcoupling efficiency6 (Fig. 5d). The practical significance of photonic band dispersion was revealed as an accurate method for quantifying the outcoupling performance of a given grating. A side-by-side comparison of the results indicates that the HC sample has a greater average transmittance over angles higher than θTIR compared to the PSS sample, which explains the competitive advantage of the HC-based InGaN LEDs in terms of optical performance. Electromagnetic simulations provided the key insight that an HC structure interacts more strongly with an incoming plane wave (Fig. 5e). Snapshots of the electric field indicate that the array of HCs significantly perturbs the propagation direction of the incident plane wave. In other words, it acts as an optical disturbance for incident light, resulting in a marked phase distortion in the vicinity of each HC structure (Fig. 5e). For a HC-based outcoupler, both a dramatic change in the phase and a high outcoupling efficiency with respect to the angles higher than θTIR facilitate the implementation of directive light sources. To demonstrate this assertion, the far-field intensity distributions of 2D gratings embedded in InGaN flip-chip LEDs were obtained at a variety of ∆n values by conducting integrated ray-wave optics simulations (Fig. 5f)15. In general, the ray-optics simulation is inappropriate to interpret the interaction of light with wavelength-scale structures (i.e. diffraction). In comparison, the wave-optics simulation properly accounts for diffraction-related phenomena, but due to a problem with computation memory, it is fundamentally incapable of designing ‘macroscopic’ optical devices that contain diffractive elements. Therefore, wave-optics simulation cannot be used to determine the extraction efficiency for each escape route and the far-field intensity distribution for an actual-scale GaN-based LED with a grating outcoupler.
An integrated ray-tracing simulation was developed to solve these serious issues with conventional optics simulations15. In the integrated ray-wave optics simulation, all diffracting light is converted into multiple rays propagating in predetermined directions. The procedure of the integrated ray-optics simulation for a 2D-grating-embedded InGaN flip-chip LED with a 100-μm-thick sapphire substrate is shown in Fig. 5f. First, wave-optics simulations were conducted to determine all orders of forward and backward diffraction efficiencies for the 2D grating under consideration as a function of incident angles. Then, the 2D grating was represented as a diffuse surface in a ray-optics model. The far-field intensity distributions of 2D grating-embedded LEDs were obtained at a variety of ∆n values (Fig. 5g). The results show that the beam divergence is monotonically reduced by increasing ∆n, owing to the improved extraction of light through the top side of the sapphire substrate as a result of diffraction. The PSS grating (∆n = 0.7) yields the maximum far-field amplitude at a polar angle of approximately 60°, with a local minimum at 0° to 30°. In comparison, the HC grating (∆n = 1.5) exhibits a Gaussian-like far-field distribution, which is useful for developing vertically directed light sources, including micro-LED-based near-eye displays in which substrate-side emission is not utilised.
Organic light-emitting diodes
HC gratings can be utilised in other semiconductors and organic LEDs (OLEDs) to enhance their outcoupling efficiencies. The active layer of OLEDs is covered with an optically thick and low-n glass substrate, such that the majority of the photons generated via electron-hole recombination are trapped and lost27,28. Therefore, the incorporation of an appropriately designed HC grating can efficiently extract tightly bound photons in such a waveguide configuration, thereby enhancing the optical performance of OLEDs (left, Fig. 6a). Recently, Kim et al. reported on a 500-nm-pitch hexagonal array of HCs covered with a TiO2 (n = 2.5) planarization layer (right, Fig. 6a)29. It is noteworthy that a ‘submicron’ HC grating is more effective for extracting light trapped in OLEDs because their active layer has a relatively low n (typically, n ~ 1.7) (left, Fig. 6b). The fabrication technology of HC arrays, as shown in Fig. 4c, can be readily extended to the submicron scale with high-resolution lithography systems (e.g. nanoimprint, stepper, etc.). The TiO2 planarization layer allows for a large Δn to amplify the diffraction strength of the HC grating. Integrated ray-wave simulations of millimetre-scale OLEDs demonstrate that the TiO2-covered HC grating improves its outcoupling efficiency with reduced beam divergence because it steers horizontally guided photons into the ambient medium via the top surface of a glass substrate (right, Fig. 6b). As previously indicated, the addition of an HC grating to inorganic GaN-based LEDs also leads to a narrowing of the emission divergence (Fig. 5f).
Metalenses
Another good application in terms of active devices using regularly arranged HCs is the development of metalens-integrated LEDs. A metalens is a virtually flat optical system composed of multiple subwavelength units with engineered phase retardation to mould the wavefront of scattered light30,31,32. Traditionally, metalenses have been employed to redirect incoming photons in free space to a focal point, making them highly competitive with bulk geometric lenses and refractive/diffractive Fresnel lenses33,34. When metalenses are monolithically incorporated into LEDs, new potential applications may emerge35,36. When the location of an active layer is coordinated at the focal point of an integrated metalens, the spherical waves generated by the active layer can be transformed into plane waves, which is a result of reciprocity37 (Fig. 7a). The integrated metalens can negate TIRs and shape the distribution of the emitted light, thereby contributing to the improvement of the outcoupling efficiency. Consequently, metalens -integrated LEDs are directional, efficient and compact light sources, which are of particular importance for augmented reality and virtual reality displays26,38. Most metalenses employ ‘high-n’ nanostructured units to cover the full range of 2π phase retardation with minimal plasma etching (Fig. 7b). Nonetheless, the manufacture of low-cost metalenses has proven to be difficult, and large-scale metalenses will exacerbate this problem. High-n dielectric-coated HCs, however, behave as similar phase retarders, and are more scalable and cost-effective to manufacture because of the absence of plasma etching (Fig. 7c). In addition, given that the fabrication temperature can be maintained low (<100 °C) throughout the entire process, as shown in Fig. 4c, incorporating an HC-based metalens into a working LED does not degrade the device characteristics.
Light absorption devices
Light trapping antennas
The strong scattering and diffraction of light induced by HCs and their arrays can enhance the optical performance of photon absorption devices, such as photovoltaics, solar absorbers and photodetectors. In principle, the introduction of a grating contributes to the improvement of absorption efficiency by (i) reducing the surface reflectance, for which a grating serves as a graded-index film39 and (ii) augmenting volumetric absorption, for which a grating converts incident light in free space into horizontally propagating guided light23. Owing to its large Δn, the array of HCs embedded in a photovoltaic medium can be a good mode converter if appropriately designed, thereby dramatically increasing the absorption efficiency. A periodic pattern in a high-n thin film on a low-n substrate can convert incoming light into waveguide modes, which effectively arises with the use of a large Δn pattern such as an array of HCs (Fig. 8a). Figure 8b shows simulated absorptivity spectra of crystalline Si thin films (300 nm in thickness) with and without embedded 2D HCs. The simulated data reveal that the HCs-embedded Si thin film creates multiple absorption peaks that are assigned to various orders of waveguide modes40. The emergence of the new waveguide modes finally leads to broadband absorption that is essential to the development of high-efficiency solar cells.
In addition to this functionality, individual HCs can act as localised light-trapping antennas when wrapped with a high-n absorption material (left, Fig. 8c). This strategy is particularly useful for the implementation of ultrathin photodetectors, including 2D transition metal dichalcogenide (TMDC) devices. A MoS2 monolayer is a well-known 2D TMDC material with a direct bandgap, but its absorptivity is inherently poor owing to its atomic thickness41,42,43. As a result, the 2D-TMDC-based photodetectors or photovoltaics can yield only up to ~10% absorptivity or ~1% power conversion efficiency44. Thus, to further improve the light absorption efficiency, light-trapping strategies have been investigated, including Fabry-Pérot cavities42,45, photonic crystals46,47 and plasmonic antennas48,49. HCs can funnel incoming light into their absorptive shell region, thereby serving as an effective light trapping platform for ultrathin absorbers. The simulation results clearly illustrate that the HC (n = 1.0) antenna gathers incident light most efficiently, even beyond its projected area, thus assuring strong light-matter interactions with the MoS2 monolayer. Consequently, the absoptivity of the MoS2 monolayer is greatly improved over the entire visible spectrum (Fig. 8d).
The same strategy can be adopted to develop high-efficiency amorphous gallium oxide (GaOX)-based thin-film (30 nm or less in GaOX thickness) photodetectors. To date, crystalline and amorphous gallium oxide materials have generated significant research interest owing to their wide bandgaps, exceeding 5 eV50,51,52. Therefore, they are used for the development of deep ultraviolet (DUV) photodetectors that must respond to light of wavelength <300 nm, while precluding the absorption of light of longer wavelengths, including the visible spectrum. DUV photodetectors are indispensable for missile tracking53,54, space communication55,56, water and air purification57,58 and the sensing of biological molecules (e.g. food-borne fungi)59,60. In particular, GaOX-based DUV photodetectors facilitate fast and sensitive responses and are compatible with any substrate; GaOX thin films on polymer substrates enable the implementation of flexible DUV photodetectors61. Snapshots of the electric-field intensity of the hollow (n = 1.0) and sapphire-filled (n = 1.78) cavities wrapped with a 30-nm-thick GaOX layer reveal that the incident light is tightly bound in the GaOX layer only for the HC (Fig. 8e). Owing to the light trapping effect, a HC-based 30-nm-thick GaOX film exhibits an absorptivity of >0.8 at 200 nm and an average absorptivity of 0.48 within the DUV band (200–300 nm), which outperforms the filled cavity and planar samples (Fig. 8f). The array of HCs with a diameter of 200 nm was fabricated using nanoimprint lithography for these GaOX film studies (inset, Fig. 8f).
Thermal radiation devices
Thermal emitters for thermophotovoltaics
Thermophotovoltaics (TPVs) are thermal emission-harnessed energy devices. TPVs use low-bandgap (e.g. GaSb, InGaAs and InGaAsSb) photovoltaic cells to convert photon energy released by high-temperature (typically >800 °C) thermal emitters into electrical energy62,63,64. Thermal emitters require a nanophotonic strategy to match their emission spectrum to the spectral response of photovoltaic cells (e.g. 0.5–1.7 µm for a GaSb photovoltaic cell)65,66. An ideal thermal emitter features a stepwise spectrum in which its emissivity is unity only at the working wavelengths of the photovoltaic cells. Such wavelength-selective thermal emitters have been implemented based on optical resonators67, photonic crystals68,69, one-dimensional hyperbolic metamaterials70,71,72 and nonintuitive complex patterns73. Previous solutions were effective at regulating the spectrum, but they lacked the thermal stability that is required for continuous and steady operation at high temperatures. For example, Stelmakh et al. achieved wavelength-selective thermal radiation from 2D optical cavities composed of refractory metal (e.g. tantalum and tungsten). The spectrum of thermal radiation was readily tuned by modulating the diameter of the optical cavities74. However, thermally induced stress, the oxidation of metal surfaces and the diffusion of metal elements deteriorated the level of thermal radiation over time. Recently, Oh et al. developed cermet (i.e. carbon-ceria hybrid composites) based thermal emitters75. The fabricated structure exhibited marginal changes in its absorptivity spectra after a 48-h heating test at 1000 °C. However, the average absorptivity at the working wavelengths of the GaSb photovoltaic cell was limited to 0.5, which needs further improvement.
Recently, Cho et al. demonstrated photon-tunnelling-mediated thermal emission from an array of HCs covered with a deep subwavelength-thick (t = 10 nm) tungsten layer4. For bulk metal, the electric field of light is rapidly attenuated within the skin depth (d), which makes it highly reflective (i.e. less absorptive) (left, Fig. 9a). In comparison, for metals with t < d, light penetrates through them and the absorptivity improves (right, Fig. 9a). Electromagnetic simulations of tungsten films with various thicknesses show that they maintain reflectance less than 0.2 over the visible and near-infrared spectra (0.5–1.7 µm, the working spectrum of the GaSb cell) at t < d (top panel, Fig. 9b). The reduced reflectance enables the tungsten films with t < d to retain large absorptivity values over the same wavelengths (0.5–1.7 µm), despite their deep-subwavelength-thick nature (bottom panel, Fig. 9b). To improve the absorptivity of tungsten, a 2D array (950 nm in pitch) of HCs covered with alumina/tungsten/alumina (50/17/50 nm) multi-shells was fabricated using nanoimprinting lithography (Fig. 9c). Photon-tunnelling-mediated absorption/emission occurred in the structured tungsten, and the absorptivity of this metal was further augmented by optical resonance (Fig. 9d). Notably, the alumina shell and HC suppressed temperature-triggered oxidation and stress, respectively, thus improving thermal stability. As a result, the developed HC-based thermal emitter produced stable electric power during repeated temperature cycling tests between 500 K and 1200 K (Fig. 9e). The TPV generated electric power at discrete temperatures is in good agreement with the simulated data (unfilled circles, Fig. 9e) acquired from a one-dimensional energy conversion model based on the radiative heat transfer and diode equations. The TPV electric power density was approximately 1 W cm−2 at 1200 K, which is competitive with the performance of state-of-the-art TPVs at similar operation temperatures. The scalable and facile fabrication of structured metals leads to the development of thermal emitters with high-temperature stability and a tailored thermal radiation spectrum, which are essential for high-efficiency TPVs.
On-chip antireflective radiative coolers
Mid-infrared (5–30 µm) photonics have inspired a surge of applications, including quantum cascade lasers76, molecule sensors77, thermal camouflage78,79,80,81,82 and radiative coolers83,84,85,86. In particular, research on RCs has attracted significant interest because it facilitates effective and passive (i.e. without energy consumption) heat dissipation channels87. RCs are classified into two categories: solar reflective83,88,89 and solar transmissive5,87,90, depending on whether the cooled object harnesses the solar energy. The ultimate goal of solar reflective RCs is to maintain the object temperature below the ambient temperature. To achieve sub-ambient radiative cooling, solar reflective RCs must be reflective in the solar spectrum (0.3–2.5 µm) and thermally black in the atmospheric window (8–13 µm)11,91. In contrast, to apply RCs to solar energy harvesting devices, such as solar cells, they must be transparent in the solar spectrum5,90. Visibly transparent but thermally absorptive/emissive materials, such as oxides (e.g. SiO2, TiO2, HfO2 and Al2O3) and various polymers (e.g. polydimethylsiloxane, polymethyl pentene and poly(methyl methacrylate)), are used in solar transmissive RCs. A few attempts have been made to apply RCs to solar energy devices87,92. For example, Zhu et al. reported a 6-µm-pitch square-lattice array of optical cavities with a 10 µm depth into a 500-μm-thick quartz wafer92. This patterned quartz wafer lowered the temperature of a Si wafer by 13 °C under one-sun illumination. In addition, Heo et al. constructed a 2D micron-grating (8.5 µm in pitch) with a 2 µm depth on a quartz wafer87. The fabricated structure cooled an integrated solar device (i.e. multijunction InGaP/GaAs/Ge photovoltaics) by 6 °C, thus yielding a 1.32% increase in the power conversion efficiency under sunlight of 900 W m−2. Although both approaches demonstrated effective cooling performance on a passive substrate or working optoelectronic device, they employed a dry-etching process that is not scalable and costly in fabrication. Moreover, they adopted an additional bonding process with an adhesive material to be integrated into devices, which could limit high-temperature applications such as concentrated photovoltaics.
Cho et al. recently reported on-chip solar transmissive RCs for application to solar cells and concentrated solar energy devices (Fig. 10a)5. Each HC works as an optical resonator; thus, its height must be larger than a few microns to effectively trap mid-infrared light. It should be noted that micron-depth plasma etching is expensive. Furthermore, the deposition of a few micron-thick oxide films typically causes fracturing, which could be exacerbated at high temperatures because of internal stress. However, the fabrication of HC-based RCs involves the use of submicron oxide films. Moreover, a depth of a few microns is readily achieved by selecting an appropriate photoresist with an appropriate coating thickness. These features account for the economic feasibility of HC-based RCs.
A hexagonal array (8 μm pitch) of SiO2/AlOx (500/300 nm) double-shell HCs is antireflective in the solar spectrum and highly absorptive/emissive in the thermal radiation spectrum (Fig. 10b). The strong absorption of the subwavelength-thick oxide double shell originates from the same photon-tunnelling mechanism discussed in Fig. 9. To elucidate the excellent thermal emittance of the developed HC-based RC, the absorptivity of each oxide shell in the thermal-radiation spectrum was obtained (bottom panel, Fig. 10c). For comparison, the real parts of the permittivity (εr) curves of the SiO2 and AlOx materials are plotted in (middle panel, Fig. 10c). The simulation results convey two key points related to the large absorptivity/emissivity of the ultrathin double shell. First, the absorptivity of the outer SiO2 shell was significantly large near 9.1 μm and 21 μm, which is consistent with the local minima of εr of SiO2, originating from the different phonon-polariton resonances of SiO2. Second, the absorptivity spectrum is further broadened owing to the inner AlOx shell; the εr of AlOx exhibited a relatively flat material dispersion with a local minimum at 11.8 μm. Consequently, the total absorptivity of the SiO2/AlOx double-shell materials is larger than 0.6 at broad mid-infrared wavelengths (8−24 μm), which predominantly overlaps with the blackbody spectrum at 300 K. A proper figure of merit for each application should be established to characterise its performance; a figure of merit for RCs is an absorptivity/emissivity. Electromagnetic simulations prior to fabrication and characterization were carried out to determine the dependence of emissivity on the structural parameters of HCs. According to electromagnetic simulations, the diameter (D) and depth (H) of the HC-based RC have a significant impact on its emissivity5. The emissivity improves steadily with increasing D and H, revealing the importance of fabricating closely packed HCs with a few micron depths. The structural parameters of the fabricated HCs slightly deviate from the optimal ones. However, employing a thick (>7 μm) photoresist with a high-resolution mask aligner could result in an average emissivity that is greater than the current value, thus providing improved cooling performance.
The HC-based RC was used to conduct daytime cooling studies on Si wafers (Fig. 10d). An AlOx (50 nm) film-coated Si wafer (labelled ‘antireflecting (AR) film-coated’ in Fig. 10d) was investigated for comparison, and exhibited the same amount of Si absorptivity as the HC sample while emitting negligible thermal radiation. During the day, the HC sample maintained lower temperatures than the reference, lowering the Si wafer temperature by 8 °C at a maximum solar irradiation of 881 W m−2, or approximately one-sun intensity. HC-embedded structures can minimise the thermal stress caused at high temperatures owing to their large vacancy fraction. After a 24 h heating test at high temperatures up to 800 °C under atmospheric pressure, the developed HC-based RC maintained its original thermal radiation spectrum and average Si absorptivity. Indoor cooling tests on Si wafers containing the developed HC film and the reference film were conducted using high-power (1000 W) xenon light and a Fresnel lens to determine the applicability of the concentrator photovoltaics (Fig. 10e). The temperature of both samples increased linearly when the light intensity increased from five to 20 sun. When both samples were heated at 200 °C under twenty-sun illumination, the HC sample exhibited a 31 °C temperature reduction compared to the reference film. Given that thermal radiation is amplified proportionate to the temperature to a power of four, according to the Stefan-Boltzmann equation, the temperature differential increases steadily (inset, Fig. 10e). It is worth noting that the blackbody spectrum of an object blueshifts as its temperature rises. Considering that the HC-based RC has a marginal emissivity at <8 μm, its average emissivity decreases as the solar intensity increases. At twenty-sun intensity, it maintains an average emissivity of approximately 0.6. Therefore, to apply the developed radiative coolers to solar energy devices operating at higher temperatures (e.g. >300 °C), more studies are required to investigate different dielectric shell materials with absorptivity/emissivity at shorter mid-infrared wavelengths (5−8 μm). Even at >8 µm, a Si3N4 material, for example, is relatively emissive. This study demonstrates that micron-depth HC films can be utilised to create thin-film mid-infrared emitters with readily tunable emission spectra by carefully choosing the shell materials.
Perspectives
We have thus far discussed the diverse optical functionalities of HCs with properly designed morphology including their shell material and thickness. The array of HCs, for example, are unique diffracting elements that can be used in both organic and III–V semiconductor LEDs. These optical features aid in the recovery of photons trapped by TIRs, hence increasing the wall-plug efficiency of LEDs. The use of HC arrays can be further applied to light absorption devices such as solar cells and photodetectors to improve their photon-to-electron conversion efficiencies. Furthermore, individual HCs acting as optical resonators improve the performance of near-infrared thermophotovoltaics and mid-infrared radiative coolers, demonstrating their practical versatility. We emphasize that such an index engineering strategy for boosting diffraction and scattering strength is not restricted to the ‘optoelectronic devices explored herein, but will be acceptable to other devices. Understanding the underlying physics on the propagation of light and creating general design guidelines will enable a new horizon of optoelectronic devices that require high Δn optical components.
HCs also offer exceptional thermal, electrical and mechanical characteristics. They can act as good thermal insulators, depending on the amount of interior voids93,94. Because HC-based composites have a low permittivity, they can be used to fabricate low-loss printed circuit boards95. In general, HC-embedded structures can help reduce weight and improve surface area, both of which are beneficial for drug delivery and catalysts96. The ability to withstand mechanical and thermal stresses may be advantageous in energy storage applications, particularly for lithium-ion batteries that are limited by volumetric changes during electrochemical cycling97,98. Because these features work independently (e.g., HC-based solar-transmissive RCs with mechanical flexibility, thermal insulation and high-temperature stability), HCs are regarded as a multifunctional and multiwavelength platform.
Fabrication of HCs and their arrays can be accomplished using both top-down and bottom-up methods. A self-templating method can be employed to implement HC particles of various sizes (e.g. from a few tens of nanometres to a few microns) in a scalable and low-cost manner because it avoids complicated processes such as core generation/removal and shell coating99. Synthesised HC particles can be mixed with printable pastes, thus creating new functionalities. They hold the promise of implementing three-dimensionally printed devices with reliable performance by providing antifouling and passive cooling functions with demanding heat and corrosion resistance.
References
Chang-Hasnain, C. J. & Yang, W. J. High-contrast gratings for integrated optoelectronics. Adv. Opt. Photonics 4, 379–440 (2012).
Moon, Y. J. et al. Microstructured air cavities as high-index contrast substrates with strong diffraction for light-emitting diodes. Nano Lett. 16, 3301–3308 (2016).
Kim, S. et al. Mie-coupled bound guided states in nanowire geometric superlattices. Nat. Commun. 9, 2781 (2018).
Cho, J. W. et al. Optical tunneling mediated sub-skin-depth high emissivity tungsten radiators. Nano Lett. 19, 7093–7099 (2019).
Cho, J. W. et al. Scalable on-chip radiative coolers for concentrated solar energy devices. ACS Photonics 7, 2748–2755 (2020).
Moon, Y. J. et al. Microstructured void gratings for outcoupling deep-trap guided modes. Opt. Express 26, A450–A461 (2018).
Xi, J. Q. et al. Optical thin-film materials with low refractive index for broadband elimination of Fresnel reflection. Nat. Photonics 1, 176–179 (2007).
Kim, S. H. et al. Inverse photonic glasses by packing bidisperse hollow microspheres with uniform cores. ACS Appl. Mater. Interfaces 9, 24155–24160 (2017).
Wierer, J. J. Jr., David, A. & Megens, M. M. III-nitride photonic-crystal light-emitting diodes with high extraction efficiency. Nat. Photonics 3, 163–169 (2009).
Pruessner, M. W., Stievater, T. H. & Rabinovich, W. S. Integrated waveguide Fabry-Perot microcavities with silicon/air Bragg mirrors. Opt. Lett. 32, 533–535 (2007).
Mandal, J. et al. Hierarchically porous polymer coatings for highly efficient passive daytime radiative cooling. Science 362, 315–319 (2018).
Schubert, E. F. Light-Emitting Diodes. (Cambridge: Cambridge University Press, 2006).
Cao, Y. et al. Perovskite light-emitting diodes based on spontaneously formed submicrometre-scale structures. Nature 562, 249–253 (2018).
Gou, F. W. et al. Angular color shift of micro-LED displays. Opt. Express 27, A746–A757 (2019).
Na, J. Y. et al. Integrated ray-wave optics modeling for macroscopic diffractive lighting devices. Opt. Express 27, 37910–37919 (2019).
Kim, J. et al. Less strained and more efficient GaN light-emitting diodes with embedded silica hollow nanospheres. Sci. Rep. 3, 3201 (2013).
David, A. et al. GaN∕InGaN light emitting diodes with embedded photonic crystal obtained by lateral epitaxial overgrowth. Appl. Phys. Lett. 92, 113514 (2008).
Chiu, C. H. et al. High efficiency GaN-based light-emitting diodes with embedded air voids/SiO2 nanomasks. Nanotechnology 23, 045303 (2012).
Kim, T. S. et al. Increase of light extraction from GaN based light emitting diodes incorporating patterned structure by colloidal lithography. Appl. Phys. Lett. 91, 171114 (2007).
Jeon, S. et al. Vacuum nanohole array embedded phosphorescent organic light emitting diodes. Sci. Rep. 5, 8685 (2015).
Jeon, S. et al. High-quality white OLEDs with comparable efficiencies to LEDs. Adv. Optical Mater. 6, 1701349 (2018).
Jang, J. et al. Incorporation of air-cavity into sapphire substrate and its effect on GaN growth and optical properties. J. Cryst. Growth 430, 41–45 (2015).
Moon, Y. J., Na, J. Y. & Kim, S. K. Design principles for morphologies of antireflection patterns for solar absorbing applications. Appl. Opt. 54, 6053–6058 (2015).
Chen, P. H. et al. Defect reduction in GaN on dome-shaped patterned-sapphire substrates. Optical Mater. 76, 368–374 (2018).
Fu, X. Y. et al. Directional polarized light emission from thin-film light-emitting diodes. Adv. Mater. 33, 2006801 (2021).
Joo, W. J. et al. Metasurface-driven OLED displays beyond 10,000 pixels per inch. Science 370, 459–463 (2020).
Reineke, S. et al. White organic light-emitting diodes: status and perspective. Rev. Mod. Phys. 85, 1245–1293 (2013).
Salehi, A. et al. Recent advances in OLED optical design. Adv. Funct. Mater. 29, 1808803 (2019).
Kim, Y. B. et al. Hexagonally connected submicron hollow veins for high efficiency, narrow beam organic emitters. Photonics Nanostruct. - Fundamentals Appl. 43, 100902 (2021).
Khorasaninejad, M. & Capasso, F. Metalenses: versatile multifunctional photonic components. Science 358, eaam8100 (2017).
Kovach, A. et al. Emerging material systems for integrated optical Kerr frequency combs. Adv. Opt. Photonics 12, 135–222 (2020).
Moon, S. W. et al. Tutorial on metalenses for advanced flat optics: design, fabrication, and critical considerations. J. Appl. Phys. 131, 091101 (2022).
Engelberg, J. & Levy, U. The advantages of metalenses over diffractive lenses. Nat. Commun. 11, 1991 (2020).
Yoon, G. et al. Printable nanocomposite metalens for high-contrast near-infrared imaging. ACS Nano 15, 698–706 (2021).
Iyer, P. P. et al. Unidirectional luminescence from InGaN/GaN quantum-well metasurfaces. Nat. Photonics 14, 543–548 (2020).
Xie, Y. Y. et al. Metasurface-integrated vertical cavity surface-emitting lasers for programmable directional lasing emissions. Nat. Nanotechnol. 15, 125–130 (2020).
Huang, T. Y. et al. A monolithic immersion metalens for imaging solid-state quantum emitters. Nat. Commun. 10, 2392 (2019).
Huang, J. P. et al. Unidirectional-emitting GaN-based micro-LED for 3D display. Opt. Lett. 46, 3476–3479 (2021).
Du, Y. et al. Hollow silica nanoparticles in UV−Visible antireflection coatings for poly(methyl methacrylate) substrates. ACS Nano 4, 4308–4316 (2010).
Brongersma, M. L., Cui, Y. & Fan, S. H. Light management for photovoltaics using high-index nanostructures. Nat. Mater. 13, 451–460 (2014).
Manzeli, S. et al. 2D transition metal dichalcogenides. Nat. Rev. Mater. 2, 17033 (2017).
Kim, E. et al. MoS2 monolayers on Si and SiO2 nanocone arrays: influences of 3D dielectric material refractive index on 2D MoS2 optical absorption. Nanoscale 10, 18920–18925 (2018).
Jeong, K. Y. et al. Integration of single-photon emitters in 2D materials with plasmonic waveguides at room temperature. Nanomaterials 10, 1663 (2020).
Bernardi, M., Palummo, M. & Grossman, J. C. Extraordinary sunlight absorption and one nanometer thick photovoltaics using two-dimensional monolayer materials. Nano Lett. 13, 3664–3670 (2013).
Jeong, H. Y. et al. Optical gain in MoS2 via coupling with nanostructured substrate: fabry–Perot interference and plasmonic excitation. ACS Nano 10, 8192–8198 (2016).
Piper, J. R. & Fan, S. H. Broadband absorption enhancement in solar cells with an atomically thin active layer. ACS Photonics 3, 571–577 (2016).
Huang, L. J. et al. Atomically thin MoS2 narrowband and broadband light superabsorbers. ACS Nano 10, 7493–7499 (2016).
Britnell, L. et al. Strong light-matter interactions in heterostructures of atomically thin films. Science 340, 1311–1314 (2013).
Lin, J. D. et al. Plasmonic enhancement of photocurrent in MoS2 field-effect-transistor. Appl. Phys. Lett. 102, 203109 (2013).
Guo, D. Y. et al. Oxygen vacancy tuned Ohmic-Schottky conversion for enhanced performance in β-Ga2O3 solar-blind ultraviolet photodetectors. Appl. Phys. Lett. 105, 023507 (2014).
Zhai, Y. et al. Scalable-manufactured randomized glass-polymer hybrid metamaterial for daytime radiative cooling. Science 355, 1062–1066 (2017).
Kim, S. H. et al. Solution-processable photonic inks of Mie-resonant hollow carbon-silica nanospheres. Small 15, 1900931 (2019).
Chen, H. Y. et al. New concept ultraviolet photodetectors. Mater. Today 18, 493–502 (2015).
Cai, Q. et al. Progress on AlGaN-based solar-blind ultraviolet photodetectors and focal plane arrays. Light Sci. Appl. 10, 94 (2021).
Razeghi, M. & Rogalski, A. Semiconductor ultraviolet detectors. J. Appl. Phys. 79, 7433–7473 (1996).
Alaie, Z., Mohammad Nejad, S. & Yousefi, M. H. Recent advances in ultraviolet photodetectors. Mater. Sci. Semiconductor Process. 29, 16–55 (2015).
Würtele, M. A. et al. Application of GaN-based ultraviolet-C light emitting diodes – UV LEDs – for water disinfection. Water Res. 45, 1481–1489 (2011).
Li, T. et al. A radiative cooling structural material. Science 364, 760–763 (2019).
Zhang, J. P. et al. AlGaN deep-ultraviolet light-emitting diodes. Jpn. J. Appl. Phys. 44, 7250–7253 (2005).
Ghisaidoobe, A. B. T. & Chung, S. J. Intrinsic tryptophan fluorescence in the detection and analysis of proteins: a focus on Förster resonance energy transfer techniques. Int. J. Mol. Sci. 15, 22518–22538 (2014).
Lee, S. H. et al. High-responsivity deep-ultraviolet-selective photodetectors using ultrathin gallium oxide films. ACS Photonics 4, 2937–2943 (2017).
Bierman, D. M. et al. Enhanced photovoltaic energy conversion using thermally based spectral shaping. Nat. Energy 1, 16068 (2016).
Fan, D. J. et al. Near-perfect photon utilization in an air-bridge thermophotovoltaic cell. Nature 586, 237–241 (2020).
LaPotin, A. et al. Thermophotovoltaic efficiency of 40%. Nature 604, 287–291 (2022).
Rinnerbauer, V. et al. Recent developments in high-temperature photonic crystals for energy conversion. Energy Environ. Sci. 5, 8815–8823 (2012).
Li, W. & Fan, S. H. Nanophotonic control of thermal radiation for energy applications [Invited]. Opt. Express 26, 15995–16021 (2018).
Cho, J. W. et al. Visible to near-infrared thermal radiation from nanostructured tungsten anntennas. J. Opt. 20, 09LT01 (2018).
Fleming, J. G. et al. All-metallic three-dimensional photonic crystals with a large infrared bandgap. Nature 417, 52–55 (2002).
Lenert, A. et al. A nanophotonic solar thermophotovoltaic device. Nat. Nanotechnol. 9, 126–130 (2014).
Dyachenko, P. N. et al. Controlling thermal emission with refractory epsilon-near-zero metamaterials via topological transitions. Nat. Commun. 7, 11809 (2016).
Lee, T. I. et al. Pt/Alumina hyperbolic metafilms with high-temperature stability, wide wavelength tunability, and omnidirectional absorption. Phys. Status Solidi (A) 215, 1800287 (2018).
Hu, R. et al. Machine learning-optimized Tamm emitter for high-performance thermophotovoltaic system with detailed balance analysis. Nano Energy 72, 104687 (2020).
Rephaeli, E., Raman, A. & Fan, S. H. Ultrabroadband photonic structures to achieve high-performance daytime radiative cooling. Nano Lett. 13, 1457–1461 (2013).
Stelmakh, V. et al. Sputtered tantalum photonic crystal coatings for high-temperature energy conversion applications. IEEE Trans. Nanotechnol. 15, 303–309 (2016).
Oh, S. et al. High-temperature carbonized ceria thermophotovoltaic emitter beyond tungsten. ACS Appl. Mater. Interfaces 13, 42724–42731 (2021).
Yao, Y., Hoffman, A. J. & Gmachl, C. F. Mid-infrared quantum cascade lasers. Nat. Photonics 6, 432–439 (2012).
Rodrigo, D. et al. Mid-infrared plasmonic biosensing with graphene. Science 349, 165–168 (2015).
Salihoglu, O. et al. Graphene-based adaptive thermal camouflage. Nano Lett. 18, 4541–4548 (2018).
Liu, Y. D. et al. Dynamic thermal camouflage via a liquid-crystal-based radiative metasurface. Nanophotonics 9, 855–863 (2020).
Song, J. L. et al. Radiative metasurface for thermal camouflage, illusion and messaging. Opt. Express 28, 875–885 (2020).
Hu, R. et al. Thermal camouflaging metamaterials. Mater. Today 45, 120–141 (2021).
Liu, Y. D. et al. Flexible Janus functional film for adaptive thermal camouflage. Adv. Mater. Technol. 7, 2100821 (2022).
Raman, A. P. et al. Passive radiative cooling below ambient air temperature under direct sunlight. Nature 515, 540–544 (2014).
Sun, X. S. et al. Radiative sky cooling: fundamental physics, materials, structures, and applications. Nanophotonics 6, 997–1015 (2017).
Cho, J. W., Lee, E. J. & Kim, S. K. Radiative cooling technologies: a platform for passive heat dissipation. J. Korean Phys. Soc. (in the press).
Xi, W. et al. Colored radiative cooling: how to balance color display and radiative cooling performance. Int. J. Therm. Sci. 170, 107172 (2021).
Heo, S. Y. et al. Determining the effectiveness of radiative cooler-integrated solar cells. Adv. Energy Mater. 12, 2103258 (2022).
Heo, S. Y. et al. A Janus emitter for passive heat release from enclosures. Sci. Adv. 6, abb1906 (2020).
Lee, E. J. et al. Nanometer-optical-coating-based visibly tinted films with 24-h sub-atmospheric passive cooling. Opt. Lett. 46, 5043–5046 (2021).
Kim, M. et al. Visibly transparent radiative cooler under direct sunlight. Adv. Optical Mater. 9, 2002226 (2021).
Cho, J. W. et al. Cooling metals via gap plasmon resonance. Nano Lett. 21, 3974–3980 (2021).
Zhu, L. X., Raman, A. P. & Fan, S. H. Radiative cooling of solar absorbers using a visibly transparent photonic crystal thermal blackbody. Proc. Natl Acad. Sci. USA 112, 12282–12287 (2015).
Cui, Y. et al. A thermally insulating textile inspired by polar bear hair. Adv. Mater. 30, 1706807 (2018).
Leroy, A. et al. High-performance subambient radiative cooling enabled by optically selective and thermally insulating polyethylene aerogel. Sci. Adv. 5, eaat9480 (2019).
Grill, A. et al. Progress in the development and understanding of advanced low k and ultralow k dielectrics for very large-scale integrated interconnects-State of the art. Appl. Phys. Rev. 1, 011306 (2014).
Park, J. et al. Hollow nanoparticles as emerging electrocatalysts for renewable energy conversion reactions. Chem. Soc. Rev. 47, 8173–8202 (2018).
Wang, J. Y., Cui, Y. & Wang, D. Design of hollow nanostructures for energy storage, conversion and production. Adv. Mater. 31, 1801993 (2019).
Schmidt, H. et al. Volume expansion of amorphous silicon electrodes during potentiostatic lithiation of Li-ion batteries. Electrochem. Commun. 115, 106738 (2020).
Feng, J. & Yin, Y. D. Self-templating approaches to hollow nanostructures. Adv. Mater. 31, 1802349 (2019).
Acknowledgements
This study was supported by the Materials, Components, and Equipment Research Program of Gyeonggi-do (AICT-004-T1), the National Research Foundation of Korea through the Basic Science Research Program (2020R1A2B5B01002261) and the Nano Material Technology Development Program (2021M3D1A2049865 and 2022M3H4A1A02085336).
Author information
Authors and Affiliations
Contributions
S.-K.K. proposed the overall framework and supervised the project. S.-K.K. wrote the Introduction and Light absorption devices section. D.-K.B. wrote the Fabrication of HCs section. Y.-B.K. wrote the Light emission devices section. J.-W.C. wrote the Thermal radiation devices section. Y.-J.L. mainly contributed to visualization and editing. S.-K.K. supervised the overall project and approved the manuscript. All author contributed to revision, correction, and editing.
Corresponding author
Ethics declarations
Conflict of interest
The authors declare no competing interests.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Kim, YB., Cho, JW., Lee, YJ. et al. High-index-contrast photonic structures: a versatile platform for photon manipulation. Light Sci Appl 11, 316 (2022). https://doi.org/10.1038/s41377-022-01021-1
Received:
Revised:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41377-022-01021-1
- Springer Nature Limited
This article is cited by
-
Building an optics and photonics research ecosystem in South Korea: Collaborative innovation between academia and industry
Light: Science & Applications (2023)
-
General deep learning framework for emissivity engineering
Light: Science & Applications (2023)