Abstract
A large negative magnetoresistance (NMR) is anticipated in topological semimetals in parallel magnetic fields, demonstrating the chiral anomaly, a long-sought high-energy-physics effect, in solid-state systems. Recent experiments reveal that the Dirac semimetal Cd3As2 has the record-high mobility and positive linear magnetoresistance in perpendicular magnetic fields. However, the NMR has not yet been unveiled. Here we report the observation of NMR in Cd3As2 microribbons in parallel magnetic fields up to 66% at 50 K and visible at room temperatures. The NMR is sensitive to the angle between magnetic and electrical fields, robust against temperature and dependent on the carrier density. The large NMR results from low carrier densities in our Cd3As2 samples, ranging from 3.0 × 1017 cm−3 at 300 K to 2.2 × 1016 cm−3 below 50 K. We therefore attribute the observed NMR to the chiral anomaly. In perpendicular magnetic fields, a positive linear magnetoresistance up to 1,670% at 14 T and 2 K is also observed.
Similar content being viewed by others
Introduction
Searching for the signature of the Adler-Bell-Jackiw chiral anomaly1,2,3 in three-dimensional topological semimetals is one of the focuses in condensed matter physics. The topological semimetals have a band structure with the conduction and valence energy bands touching at a finite number of paired Weyl nodes4,5,6 (Fig. 1a). In each pair, the two Weyl nodes carry opposite chirality, and paired monopoles and anti-monopoles of Berry curvature in momentum space7 (Fig. 1b). The nontrivial Berry curvature can couple an external magnetic field (B) to the velocity of electrons, leading to a chiral current that is linearly proportional to the field. The correlation of chiral currents further contributes to an extra conductivity that quadratically grows with increasing magnetic field, in a magnetic field and an electric field applied parallel to each other. This B2-positive conductivity in weak parallel magnetic fields, or negative magnetoresistance (negative MR), is rare in non-ferromagnetic materials, thus can serve as one of the transport signatures of the topological semimetals. More importantly, because of its relation to the chiral charge pumping between paired Weyl nodes, the negative magnetoresistance is also believed to be a signature of the chiral anomaly8,9.
(a) A schematic of the energy spectrum of a topological semimetal. (kx, ky, kz) is the wave vector. . (b) The vector plot of the Berry curvature in momentum space. The conduction and valence bands of a topological semimetal touch at the Weyl nodes, at which a pair of monopoles is hosted. The arrows show that the flux of the Berry curvature flows from one monopole (red) to the other (blue), defining the nontrivial topological properties of a topological semimetal.
Among the recently identified candidates for topological semimetals (for example, HgCr2Se4 (refs 10, 11, Bi1−xInx)2Se3 (ref. 12), Na3Bi (refs 13, 14, 15), TlBiSSe (ref. 16) and TaAs (refs 17, 18, 19, 20, 21)), the Dirac semimetal Cd3As2 (refs 22, 23, 24, 25, 26, 27) has peculiar transport properties, such as a giant MR in perpendicular magnetic fields and record-high mobility28,29,30,31,32,33, thus is of great potential in device applications. The negative MR possibly associated with the chiral anomaly has been claimed in several topological semimetals, including BiSb alloy34, ZrTe5 (ref. 35), TaAs (refs 36, 37), Na3Bi (ref. 38) and TaP (ref. 39). However, the chiral anomaly in Cd3As2 is not yet observed. One of the reasons is that the carrier density in earlier samples was too high (over 1018 cm−3). The chiral anomaly arises because of the nontrivial Berry curvature, which diverges at the Weyl nodes, so the Fermi energy EF has to be as close to the Weyl nodes as possible for a clear signal of the negative MR.
In this work, we systematically investigate the magnetotransport properties of Cd3As2 microribbons, in which the carrier density is found to obey an Arrhenius’s law, decreasing from 3.0 × 1017 cm−3 at 300 K to 2.2 × 1016 cm−3 below 50 K. In perpendicular magnetic fields, the ribbon exhibits a very large non-saturating positive linear MR (linear MR) up to 300 K. In contrast, when the magnetic field is applied in parallel with the measurement electric field, a negative MR is observed. It is sensitive to the angle between magnetic and electrical field, and shows a parabolic dependence on the low magnetic fields (<1 T) and persists up to 300 K. More importantly, our analysis reveals a characteristic carrier density dependence of the observed negative MR that is in agreement with the semiclassical theory about the chiral anomaly in topological semimetals. All the experimental evidence makes us believe that the chiral anomaly induced negative MR is indeed realized in our Cd3As2 ribbons with low carrier density. By studying the carrier density dependence of the observed linear MR in perpendicular magnetic fields, possible physical origins are also discussed. Our work shows that the carrier density plays an important role in the observation of the negative and linear MR and their magnitudes.
Results
Device characteristics
Figure 2a shows the scanning electron microscopy image of the four-terminal Cd3As2 devices studied in this work. The width w and inter-voltage-probe distance l are 1,210 and 1,600 nm, respectively. According to the atomic force microscopy measurement shown in Fig. 2b, the ribbon thickness t is about 327 nm (Fig. 2c). Figure 2d shows the measured temperature (T) dependence of the resistance (R) of the Cd3As2 ribbon. With decreasing temperature, the ribbon changes from an insulating behaviour to a metallic one, with a resistance peak appearing around 50 K. We note that similar R–T curves were also observed in recent studies of Dirac semimetals, where chiral anomaly induced transport features were reported40,41. One of the important properties of Dirac semimetals is the giant non-saturating linear magnetoresistance (linear MR) in high magnetic fields28,29,30,31,32,33. Indeed, our Cd3As2 ribbons do exhibit such an intriguing linear MR. Figure 2e shows the MR measured at T=2 K with varying angle between magnetic and electric field applied (see inset). When the magnetic field (B) is applied perpendicular to the ribbon in the z direction, that is, the B-field tilting angle θ=90o, a linear MR up to 1670% at 14 T is observed. This linear MR decreases at smaller titling angles when we rotate the B-field in the x–z plane. For θ≤10o, a negative MR begins to emerge in low magnetic fields, as shown in the Fig. 2f. For θ=0o, that is, the B-field is parallel to the electric field direction, the negative MR is the most prominent. We also rotate the B-field in the x–y plane and study the in-plane angle dependence of this negative MR (see Supplementary Note 1 and Supplementary Fig. 1 for details). The emergence of such a negative MR when B||E is recently ascribed to the chiral anomaly of topological semimetals8,9.
(a) The scanning electron microscopy and (b) atomic force microscopy images of the device. Scale bars, 1 μm (a); 200 nm (b). (c) The height profile of the Cd3As2 microribbon in b. (d)The measured resistance (R) as a function of temperature (T) at zero magnetic field. (e) The magnetoresistance (MR) measured at 2 K with applied magnetic field (B) direction changing from perpendicular (θ=90°) to parallel (θ=0°) to the electric field (E) direction in the z–x plane. (f) The replot of MR with θ<10° showing the negative MR at low magnetic fields.
Linear MR in perpendicular fields
To gain more physical insights into the observed linear MR and negative MR, we further study the temperature dependence of these two phenomena. Figure 3a shows the R–B curves measured at θ=90o and different temperatures indicated. As temperature increases from 2 to 50 K, the linear MR in high magnetic fields (>8 T) is almost unchanged but it starts to weaken gradually as T further increases. At low temperatures, some wiggles are superimposed on the linear MR but quickly disappear as temperature increases. In addition, we note that the R–B curves show a quadratic B-field dependence in low magnetic fields (<1 T) distinct from the linear MR in high magnetic fields. As shown in the inset of Fig. 3b, the R–B curves at T=2 to 300 K can be well fitted by parabolas within a small B-field range. Such a parabolic MR is believed to arise from the Lorentz deflection of carriers and the B2 fitting allows us to deduce the carrier mobility, μ, by42
(a) The MR measured at different T indicated. (b) The T dependence of the carrier mobility, which is calculated using Kohler’s rule or equation (1). Inset: the MR at small magnetic fields and the parabola fittings (solid lines) at different T indicated. (c) The carrier density as a function of T. The solid red curve is the fitting using Arrhenius’s law. (d) The slope k of the linear MR at high B (from 8 to 14 T, obtained in a, see solid curves) as a function of carrier density, n. The solid red and blue curves are the fittings using n−1 and n−2, respectively. The corresponding temperature for each data point is also indicated.
![](http://media.springernature.com/lw306/springer-static/image/art%3A10.1038%2Fncomms10301/MediaObjects/41467_2016_Article_BFncomms10301_Equ1_HTML.gif)
The obtained mobility of our Cd3As2 ribbon at different temperatures is shown in Fig. 3b. It increases monotonically with decreasing temperature. At T=2 K, the mobility reaches 104 cm2V−1 s−1, which is comparable to those reported in previous studies of Cd3As2 (refs 29, 30, 32, 33). It has to be pointed out that equation (1) is valid when B<<1/μ. Considering the high mobility, we restrict the fitting range of the magnetic field below 0.15 T throughout the work. On the basis of Drude model of electric conduction, the carrier density n of our ribbon can be derived by
![](http://media.springernature.com/lw318/springer-static/image/art%3A10.1038%2Fncomms10301/MediaObjects/41467_2016_Article_BFncomms10301_Equ2_HTML.gif)
where e is the elementary charge, ρ is the resistivity of the ribbon and the resistance R at different temperatures is shown in Fig. 2c. Figure 3c shows the obtained carrier density as a function of temperature. Below 50 K, the carrier density is almost a constant. From 50 to 300 K, it increases with temperature by about one order of magnitude from 2.2 × 1016 to 3.0 × 1017 cm−3, following Arrhenius’s law (solid curve in Fig. 3c):
![](http://media.springernature.com/lw308/springer-static/image/art%3A10.1038%2Fncomms10301/MediaObjects/41467_2016_Article_BFncomms10301_Equ3_HTML.gif)
where kB is the Boltzmann constant and the thermal activation energy Δ is about 51 meV. Such a thermally activated process of carriers accounts for the insulator-like R–T behaviour above 50 K shown in Fig. 2d, while the metallic behaviour below 50 K is mainly due to the increase of the carrier mobility with decreasing temperature. Since the intrinsic carriers will not follow Arrhenius’s law for Dirac fermions43, we tentatively ascribe the thermal activation of carriers to some traps present in our Cd3As2 ribbons. It is worth pointing out that both the observed linear MR and the carrier density are almost temperature independent when T<50 K and become temperature dependent when T>50 K. This coincidence implies that the observed strength of the linear MR is related to the change of carrier density. We can thus examine the temperature dependence of the linear MR in the temperature range from 50 to 300 K in terms of the carrier density. The slope k of the linear MR is extracted by linearly fitting the R–B curves between 8 and 14 T, as shown in Fig. 3a. The obtained k as a function of n is shown in Fig. 3d.
A giant non-saturating linear MR has been observed in various Dirac semimetals28,29,30,31,32,33, but its physical origin is still under debate. One possible mechanism is the quantum linear MR model proposed by Abrikosov44, where a non-saturating linear MR would appear in three-dimensional gapless semiconductors with linear energy dispersion when all the carriers are condensed into the lowest bands of Landau levels, that is, in the quantum limit. According to this model, the linear MR is temperature independent but should follow the 1/n2 dependence, that is, , where n2 arises because the longitudinal resistance
in the limit that the longitudinal conductivity σ is much smaller than the Hall conductivity σH and the Hall conductivity is proportional to n. Abrikosov’s model with linear dispersion leads to a longitudinal σ independent on the carrier density, which may be violated in real materials. If σ is also proportional to n, as in most cases, the carrier density dependence should be corrected to
. As a result, the slope of the quantum linear MR is inversely proportional to the carrier density. For comparison we plot k∝n−1 (red solid line) and k∝n−2 (blue solid line) curves in Fig. 3d. As it can be seen, the measured k follows n−1 dependence. In addition, our system is believed to enter the quantum limit in the fitting magnetic field range from 8 to 14 T, as will be discussed later in this work. All these seem to suggest the quantum model as the underlying physical origin of the observed linear MR in high fields shown in Fig. 3a. Besides this quantum model, there is another classical model proposed by Parish and Littlewood45 to account for the linear MR observed in polycrystalline silver chalcogenides. It is the disorder-induced admixture of the Hall signal that gives rise to the linear MR. Considering the low carrier density and quite high mobility of our Cd3As2 ribbons, this classical model is unlikely applicable to the observed linear MR. Also, there is explanation in the presence of balanced electron and hole carriers46, which is apparently not our case. The linear transverse MR observed in different systems may have various origins, and is still a challenging theoretical question47,48.
Negative MR in parallel fields
In Fig. 4a, the R–B curves obtained at θ=0o are shown at different temperatures. There exists a critical B-field for each curve, below which a pronounced negative MR is observed even with temperature up to 300 K. At T=50 K and B=8 T, the highest negative MR of 66% can be obtained. It is also noted in Fig. 4a that some MR ripples are superimposed on the negative MR especially as low temperatures. Besides the apparent negative MR, a small resistance dip appears in low fields with T<20 K, as shown in Fig. 4b. Such a dip is believed to arise from the weak anti-localization effect in Dirac semimetals34,49. In Fig. 4c, the low-field-negative MR is shown at different temperatures. Note that the measured resistance has been converted to the conductivity σ and Δσ=σ−σ0, where σ0 is the conductivity at zero magnetic field. Remarkably, all the data in Fig. 4c show a quadratic dependence on the magnetic field, as indicated by the fitting curves with Δσ=CaB2. This is consistent with the prediction in previous theoretical studies8,9. When an external electric field is applied in parallel with the magnetic field, chiral charges will be pumped from one Weyl node to the other, as a result of the nontrivial Berry curvature (see Fig. 1b). The chiral charge is therefore not conserved at each Weyl node. Such a chiral anomaly is expected to give rise to a prominent positive conductivity proportional to B2 based on a semiclassical transport calculation8,9. It should be noted that such a quadratic field dependence of the conductivity is only valid in weak magnetic fields or high temperatures such that the Landau quantization can be ignored. Indeed, the quadratic field dependence of Δσ in Fig. 4c occurs in low magnetic fields (<0.8 T).
(a) The MR measured at different T indicated. (b) The weak anti-localization effect at low temperatures and very small magnetic fields. (c) The positive conductivity Δσ=σ–σ0, where σ0 is the conductivity at B=0, converted from measured negative MR at different T indicated. The solid red curves are the fittings using Δσ=CaB2. (d) Ca as a function of the carrier density, n. The solid red curve is a fitting using n−2/3. The corresponding temperature for each data point is also indicated.
Furthermore, because the chiral anomaly arises from the nontrivial Berry curvature, which diverges at the Weyl nodes, the positive conductivity will increase with decreasing Fermi energy and carrier density. More specifically, the theory predicts if the Fermi level EF is close to the Weyl nodes8,9. As a result, we plot the obtained fitting parameter Ca as a function of the carrier density in Fig. 4d together with a
curve (solid red line). One can see that Ca does obey the n−2/3 relationship reasonably well. All these experimental evidences, that is, measured Δσ=CaB2 and
, lead us to believe that it is the chiral anomaly that gives rise to the observed negative MR shown in Fig. 4a. In the above discussion, we only consider the influence of n on Ca. But Ca is also proportional to the internode scattering time τa (refs 8, 9). Since the momentum transfer assisted by phonons is suppressed at low temperatures, τa will increase with decreasing temperature. As shown in Fig. 3c, the carrier density of our sample follows Arrhenius’s law. τa is thus expected to increase with decreasing n. At higher carrier density, the deviation from perfect linear dispersion can also lead to a correction to the power law of n. Therefore, the n−2/3 fitting of Ca in Fig. 4d, which assumes a constant τa for different n, would over- and underestimate the value of Ca at high and low carrier densities, respectively. This accounts for the deviation of Ca from the fitting at 300 K and below 50 K shown in Fig. 4d. The observation of chiral anomaly induced negative MR also requires τaτ, where τ is the momentum relaxation time. In Supplementary Note 2 and Supplementary Fig. 2, the ratio of τa/τ has been estimated. τa is at least one order of magnitude larger than τ, in consistent with the theories8,9.
It is well known that, in solids, negative MR may have other physical origins. It can arise from the weak localization effect due to the quantum interference of time-reversed scattering loops. Since the phase coherence length decreases rapidly with increasing temperature, the weak localization can only be observed at low temperatures. The negative MR observed in Cd3As2 ribbons persists up to 300 K; therefore, cannot be attributed to the weak localization effect. Magnetic scattering might be another mechanism for negative MR, as reported in some magnetic systems50, but our Cd3As2 ribbons are non-magnetic.
MR in the quantum limit
As mentioned above, a critical magnetic field BC exists for each MR curve to characterize the change of MR from negative to positive in Fig. 4a, as illustrated by the arrows. We believe that this sign change in MR is an indication of the system to enter the quantum limit at BC, that is, the Fermi energy crosses only the lowest Landau bands with the band index v=0 and lies right below the bottom of the v=1 Landau bands, as shown in the inset of Fig. 5a. The energy spacing between the v=1 and v=0 bands is roughly related to the cyclotron frequency as , with m* as the effective mass of carriers in Cd3As2. On the other hand,
, where the Fermi wave vector in the v=0 bands is related to the carrier density according to
. Note that there is no spin degeneracy for the lowest Landau band of Dirac semimetal (Supplementary Note 3; Supplementary Fig. 3). Combing them, we can deduce a relationship between the critical field and the carrier density as
To justify this scenario, we extract BC from the MR curves at different temperatures (except 300 K curve) in Fig. 4a, and plot them in terms of the carrier density n2/3 as it is shown in Fig. 5a. As the carrier density only changes within the temperature range of 50–200 K, a straight line fitting of the data in this range with BC=βn2/3 yields β=3.0 × 10−11, which is close to the above theoretical value. Such a good agreement strongly supports our assumption that our system is indeed in the quantum limit above BC. The deviation of data below 50 K, where the carrier density is almost constant, is probably caused by the superimposed ripples on the MR that prevent an accurate extraction of BC. As it is shown in Fig. 4a, after the system is in the quantum limit, the measured magnetoresistance becomes positive, or the magnetoconductivity becomes negative. We find at high fields approaching 14 T, the magnetoconductivity follows a good B−1 dependence, as indicated by the linear fittings in Fig. 5b (red solid curves). We also find that the obtained slope
of these linear fittings is inversely proportional to the carrier density n (see Fig. 5c). This observed negative linear magnetoconductivity at high fields is contrary to the theoretical expectation, in which a positive linear magnetoconductivity is predicted as an additional signature of the chiral anomaly8,51,52. However, in reality, the relaxation time and Fermi velocity can bring extra magnetic field dependences, leading to either positive or negative magnetoconductivity in Dirac semimetals53.
(a) BC as a function of n2/3, n is the carrier density. The corresponding temperature for each data point is also indicated. The solid red line is a linear fitting. BC is defined as the critical field at which the MR in B parallel to E is minimum. At BC, the system enters the quantum limit with a structure of the Landau bands illustrated as in the inset. v is the index of the Landau bands and ω is the cyclotron frequency. (b) The high-B-field magnetoconductivity in B parallel to E as a function of 1/B. The magnetoconductivity is found to follow a k′/B dependence while approaching 14 T (see solid red lines). (c) The slope k′ as a function of the carrier density. The solid red line is a linear fitting.
Discussion
In conclusion, we have performed a systematic magnetotransport study of Cd3As2 microribbons. Due to the low carrier density in our samples, we can observe both the non-saturating linear MR in a high perpendicular magnetic field and the quadratic negative MR when a weak magnetic field is in parallel with the measurement electric field. Furthermore, the thermally activated behaviour of carriers in our Cd3As2 ribbons allows us to study the carrier density dependence of these two phenomena. Although the mechanism for the linear MR is still not well understood, the quadratic negative MR can be safely ascribed to the chiral anomaly intrinsic to the Dirac semimetal Cd3As2. Our work provides new physical insights into the intriguing transport properties of Dirac semimetals, revealing the importance of carrier density in mediating the linear MR in perpendicular fields and the quadratic negative MR in parallel fields. It also calls for the thin-film growth of Dirac semimetals. By applying an external gate to effectively tune the Fermi level of the film towards the Weyl nodes, much larger linear MR and prominent negative MR would be expected.
Methods
Growth
The Cd3As2 microribbon was grown by a chemical vapour deposition method. Cd3As2 powders and Si (001) covered with 2-nm Au layer were used as the precursor and substrates, respectively, and argon were used as a carrier gas. Before each growth, the furnace was pumped and flushed for several times to remove water and oxygen using dry argon. The precursor powder boat was placed in the hot centre of the furnace, while the Si (100) substrates were placed downstream about 32 cm away from the precursor powders. The furnace was gradually heated up to 750 °C in 40 min, and the Ar flow was kept as 100 s.c.c.m. during the growth process. The typical growth time is 60 min, and after then the furnace was cooled down to room temperature naturally.
Characterization
Structural investigations have been performed on scanning electron microscopy (JEOL-6300) and atomic force microscopy (Dimension 3100) at room temperature. The growth direction of the Cd3As2 microribbon has been confirmed by the transmission electron microscopy (JEM 2010, JEOL) measurements. The high-resolution transmission electron microscopy identified [110] as the growth or axial direction of the ribbon (Supplementary Note 4 and Supplementary Fig. 4).
Devices fabrication and magnetoresistance measurements
To study the magnetotransport properties, a four-terminal device was fabricated with standard electron-beam lithography and lift-off processes. Au/Cr electrodes with the thickness of 275/25 nm were deposited using thermal evaporation methods. The transport properties of the device were then investigated in a Quantum Design PPMS system with the highest magnetic field up to 14 T.
Additional information
How to cite this article: Li, H. et al. Negative magnetoresistance in Dirac semimetal Cd3As2. Nat. Commun. 7:10301 doi: 10.1038/ncomms10301 (2016).
References
Adler, S. L. Axial-vector vertex in spinor electrodynamics. Phys. Rev. 177, 2426–2438 (1969) .
Bell, J. S. & Jackiw, R. A PCAC puzzle: π0→γγ in the σ-model. Il Nuovo Cimento A 60, 47–61 (1969) .
Nielsen, H. B. & Ninomiya, M. Absence of neutrinos on a lattice: (i). Proof by homotopy theory. Nucl. Phys. B 185, 20–40 (1981) .
Wan, X., Turner, A. M., Vishwanath, A. & Savrasov, S. Y. Topological semimetal and Fermi-arc surface states in the electronic structure of pyrochlore iridates. Phys. Rev. B 83, 205101 (2011) .
Yang, K. Y., Lu, Y. M. & Ran, Y. Quantum Hall effects in a Weyl semimetal: possible application in pyrochlore iridates. Phys. Rev. B 84, 075129 (2011) .
Burkov, A. A. & Balents, L. Weyl semimetal in a topological insulator multilayer. Phys. Rev. Lett. 107, 127205 (2011) .
Volovik, G. E. The Universe in a Helium Droplet Clarendon Press (2003) .
Son, D. T. & Spivak, B. Z. Chiral anomaly and classical negative magnetoresistance of Weyl metals. Phys. Rev. B 88, 104412 (2013) .
Burkov, A. A. Chiral anomaly and diffusive magnetotransport in Weyl metals. Phys. Rev. Lett. 113, 247203 (2014) .
Xu, G., Weng, H., Wang, Z., Dai, X. & Fang, Z. Chern semimetal and the quantized anomalous Hall effect in HgCr2Se4 . Phys. Rev. Lett. 107, 186806 (2011) .
Guan, T. et al. Evidence for half-metallicity in n-type HgCr2Se4 . Phys. Rev. Lett. 115, 087002 (2015) .
Brahlek, M. et al. Topological-metal to band-insulator transition in (Bi1−xInx)2Se3 thin films. Phys. Rev. Lett. 109, 186403 (2012) .
Wang, Z. et al. Dirac semimetal and topological phase transitions in A3Bi (A=Na, K, Rb). Phys. Rev. B 85, 195320 (2012) .
Liu, Z. K. et al. Discovery of a three-dimensional topological Dirac semimetal, Na3Bi. Science 343, 864–867 (2014) .
Xu, S. Y. et al. Observation of Fermi arc surface states in a topological metal. Science 347, 294–298 (2015) .
Novak, M., Sasaki, S., Segawa, K. & Ando, Y. Large linear magnetoresistance in the Dirac semimetal TlBiSSe. Phys. Rev. B 91, 041203 (2015) .
Weng, H., Fang, C., Fang, Z., Bernevig, B. A. & Dai, X. Weyl semimetal phase in noncentrosymmetric transition-metal monophosphides. Phys. Rev. X 5, 011029 (2015) .
Huang, S. M. et al. A Weyl fermion semimetal with surface Fermi arcs in the transition metal monopnictide TaAs class. Nat. Commun. 6, 7373 (2015) .
Lv, B. Q. et al. Experimental discovery of Weyl semimetal TaAs. Phys. Rev. X 5, 031013 (2015) .
Lv, B. Q. et al. Observation of Weyl nodes in TaAs. Nat. Phys. 11, 724–727 (2015) .
Xu, S. Y. et al. Discovery of a Weyl fermion semimetal and topological Fermi arcs. Science 349, 613–617 (2015) .
Wang, Z., Weng, H., Wu, Q., Dai, X. & Fang, Z. Three-dimensional Dirac semimetal and quantum transport in Cd3As2 . Phys. Rev. B 88, 125427 (2013) .
Liu, Z. K. et al. A stable three-dimensional topological Dirac semimetal Cd3As2 . Nat. Mater. 13, 677–681 (2014) .
Neupane, M. et al. Observation of a three-dimensional topological Dirac semimetal phase in high-mobility Cd3As2 . Nat. Commun. 5, 3786 (2014) .
Jeon, S. et al. Landau quantization and quasiparticle interference in the three-dimensional Dirac semimetal Cd3As2 . Nat. Mater. 13, 851–856 (2014) .
Yi, H. et al. Evidence of topological surface state in three-dimensional Dirac semimetal Cd3As2 . Sci. Rep. 4, 6106 (2014) .
Borisenko, S. et al. Experimental realization of a three-dimensional Dirac semimetal. Phys. Rev. Lett. 113, 027603 (2014) .
Liang, T. et al. Ultrahigh mobility and giant magnetoresistance in the Dirac semimetal Cd3As2 . Nat. Mater. 14, 280–284 (2015) .
Feng, J. et al. Large linear magnetoresistance in Dirac semi-metal Cd3As2 with Fermi surfaces close to the Dirac points. Phys. Rev. B 92, 081306 (R) (2015) .
He, L. P. et al. Quantum transport evidence for the three-dimensional Dirac semimetal phase in Cd3As2 . Phys. Rev. Lett. 113, 246402 (2014) .
Zhao, Y. et al. Anisotropic Fermi surface and quantum limit transport in high mobility three-dimensional Dirac semimetal Cd3As2 . Phys. Rev. X 5, 031037 (2015) .
Cao, J. et al. Landau level splitting in Cd3As2 under high magnetic fields. Nat. Commun. 6, 7779 (2015) .
Narayanan, A. et al. Linear magnetoresistance caused by mobility fluctuations in n-doped Cd3As2 . Phys. Rev. Lett. 114, 117201 (2015) .
Kim, H. J. et al. Dirac versus Weyl fermions in topological insulators: Adler-Bell-Jackiw anomaly in transport phenomena. Phys. Rev. Lett. 111, 246603 (2013) .
Li, Q. et al. Observation of the chiral magnetic effect in ZrTe5. Preprint at http://arxiv.org/abs/1412.6543 (2014) .
Huang, X. et al. Observation of the chiral anomaly induced negative magneto-resistance in 3D Weyl semi-metal TaAs. Phys. Rev. X 5, 031023 (2015) .
Zhang, C. et al. Observation of the Adler-Bell-Jackiw chiral anomaly in a Weyl semimetal. Preprint at http://arxiv.org/abs/1503.02630 (2015) .
Xiong, J. et al. Evidence for the chiral anomaly in the Dirac semimetal Na3Bi. Science 10, 1126 (2015) .
Shekhar, C. et al. Extremely large magnetoresistance and ultrahigh mobility in the topological Weyl semimetal NbP. Nat. Phys. 11, 645–649 (2015) .
Li, C.-Z. et al. Giant negative magnetoresistance induced by the chiral anomaly in individual Cd3As2 nanowires. Preprint at http://arxiv.org/abs/1504.07398 (2015) .
Zhang, C. et al. Detection of chiral anomaly and valley transport in Dirac semimetals. Preprint at http://arxiv.org/abs/1504.07698 (2015) .
Olsen, J. L. Electron Transport in Metals Interscience (1962) .
Fang, T., Konar, A., Xing, H. & Jena, D. Carrier statistics and quantum capacitance of graphene sheets and ribbons. Appl. Phys. Lett. 91, 092109 (2007) .
Abrikosov, A. A. Quantum magnetoresistance. Phys. Rev. B 58, 2788–2794 (1998) .
Parish, M. M. & Littlewood, P. B. Non-saturating magnetoresistance in heavily disordered semiconductors. Nature 426, 162–165 (2003) .
Alekseev, P. S. et al. Magnetoresistance in two-component systems. Phys. Rev. Lett. 114, 156601 (2015) .
Ramakrishnan, N., Milletari, M. & Adam, S. Magnetoresistance in 3D Weyl semimetals. Preprint at http://arxiv.org/abs/1501.03815 (2015) .
Song, J. C. W., Refael, G. & Lee, P. A. Guiding center linear magnetoresistance in the semiclassical regime. Preprint at http://arxiv.org/abs/1507.04730 (2015) .
Lu, H.-Z. & Shen, S.-Q. Weak antilocalization and localization in disordered and interacting weyl semimetals. Phys. Rev. B 92, 035203 (2015) .
Matsukura, F., Ohno, H., Shen, A. & Sugawara, Y. Transport properties and origin of ferromagnetism in (Ga,Mn)As. Phys. Rev. B 57, R2037–R2040 (1998) .
Nielsen, H. B. & Ninomiya, M. The Adler-Bell-Jackiw anomaly and Weyl fermions in a crystal. Phys. Lett. B 130, 389–396 (1983) .
Gorbar, E. V., Miransky, V. A. & Shovkovy, I. A. Chiral anomaly, dimensional reduction, and magnetoresistivity of Weyl and Dirac semimetals. Phys. Rev. B 89, 085126 (2014) .
Lu, H.-Z., Zhang, S.-B. & Shen, S.-Q. High-field magnetoconductivity of topological semimetals with short-range potential. Phys. Rev. B 92, 045203 (2015) .
Acknowledgements
This work was supported in part by the Research Grants Council of the Hong Kong SAR under Grant Nos. 16305514, 17303714 and AoE/P-04/08, and in part by the National Natural Science Foundation of China under Grant Nos. 11204183 and 11374135. The electron-beam lithography facility is supported by the Raith-HKUST Nanotechnology Laboratory at MCPF (SEG HKUST08).
Author information
Authors and Affiliations
Contributions
J.W. and S.-Q.S. conceived the project; H.L. grew the samples and fabricated devices with support from Z.F., H.Z., H.C.L. and R.M.; H.H. and H.L. performed transport experiments; H.-Z.L. and S.-Q.S. provided theoretical support; H.H., H.-Z.L., H.L., J.W. and S.-Q.S. analysed experimental data and wrote the manuscript with contribution from others.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-4, Supplementary Notes 1-4, and Supplementary References (PDF 688 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Li, H., He, H., Lu, HZ. et al. Negative magnetoresistance in Dirac semimetal Cd3As2. Nat Commun 7, 10301 (2016). https://doi.org/10.1038/ncomms10301
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms10301
- Springer Nature Limited
This article is cited by
-
Experimental observation of multiple topological nodal structure in LaSb2
Science China Physics, Mechanics & Astronomy (2024)
-
Correlation-driven organic 3D topological insulator with relativistic fermions
Nature Communications (2023)
-
Robust negative longitudinal magnetoresistance and spin–orbit torque in sputtered Pt3Sn and Pt3SnxFe1-x topological semimetal
Nature Communications (2023)
-
Quantum transport in topological semimetals under magnetic fields (III)
Frontiers of Physics (2023)
-
Room-temperature valley transistors for low-power neuromorphic computing
Nature Communications (2022)