Abstract
Two kinds of C-Si-Mn-Cr series tested steels were designed to obtain dual phase microstructures of ferrite (F) + martensite (M) or ferrite (F) + bainite (B) with different mechanical properties. Effects of strengthening phase on yielding and fracture behaviours during uniaxial tension of dual phase steel were discussed. Compared with hot-rolled martensite dual phase steel, ferrite-bainite dual phase steel has high ratio of yield strength to tensile strength (YS/TS) and low elongation. During necking process of uniaxial tension, microvoids of ferrite-martensite steel are generated by fracture of ferrite/martensite boundary or martensite islands with irregular shape. But ferrite matrix elongated remarkably along deformation direction, and strengthening phase also coordinated with ferrite matrix. Compatible deformation between ferrite and bainite is distinct. Ferrite-bainite dual phase steel has fine and less microvoid, and phase boundary of ferrite and bainite is beneficial for restraining generation and extending of microvoid.
Similar content being viewed by others
References
B. Q. Ao, Automobile Technology & Material 8 (2002) No. 9, 1–22.
M. Ma, M. Shi, Iron and Steel 39 (2004) No. 7, 68–72.
R. Rana, C. Liu, R. Ray, Scripta Mater. 68 (2013) 354–359.
F. Ozturk, A. Polat, S. Toros, R. C. Picu, J. Iron Steel Res. Int. 20 (2013) No. 6, 68–74.
R. B. Song, Q. F. Dai, J. Iron Steel Res. Int. 20 (2013) No. 8, 48–53.
F. Ozturk, S. Toros, S. Kilic, J. Iron Steel Res. Int. 16 (2009) No. 6, 41–46.
S. Kim, S. Lee, Metall. Mater. Trans. A 31 (2000) 1753–1760.
B. Hwang, T. Cao, S. Shin, S. Kim, S. Lee, S. Kim, Mater. Sci. Technol. 21 (2005) 967–975.
E. Ahmad, T. Manzoor, M. Ziai, N. Hussain, J. Mater. Eng. Perform. 21 (2012) 382–387.
Y. Fang, Y. Z. Liu, L. Y. Zhou, Iron and Steel 44 (2009) No. 8, 89–92.
J. Kadkhodapour, A. Butz, Rad S. Ziaei, Acta Mater. 59 (2011) 2575–2588.
Z. G. Hu, P. Zhu, J. Meng, Mater. Des. 31 (2010) 2884–2890.
C. Landron, O. Bouaziz, E. Maire, J. Adrien, Acta Mater. 61 (2013) 6821–6829.
D. I. Hyun, S. M. Oak, S. S. Kang, Y. H. Moon, J. Mater. Process. Technol. 130 (2002) 9–13.
L. Y. Zhou, Y. Z. Liu, X. W. Hu, J. Iron Steel Res. Int. 18 (2011) Suppl. 1, 792–795.
W. Tan, B. Han, S. Wang, Y. Yang, C. Zhang, J. Iron Steel Res. Int. 19 (2012) No. 6, 37–41.
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation Item: Item Sponsored by Fundamental Research Funds for Central Universities of China (FRF-TP-12-046A); Beijing Higher Education Young Elite Teacher Project of China (YETP0355)
Rights and permissions
About this article
Cite this article
Zhou, Ly., Jiang, B., Cui, Th. et al. Effect of Strengthening Phase on Deformation Behaviour During Uniaxial Tension of Hot-Rolled Dual Phase Steel. J. Iron Steel Res. Int. 21, 1111–1115 (2014). https://doi.org/10.1016/S1006-706X(14)60191-6
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(14)60191-6