Abstract
Synthesis of the Al2O3-B4C ceramic was carried out in this study via mechanochemical method. A highest value of 64.72 m2/g was obtained at the end of milling for 6 h during the BET analyses carried out for determining the surface area of synthesis powders. The bond structures between Al–O and B–C were determined in FT-IR analysis in accordance with the data acquired from relevant literature. Peaks for only the Al2O3 and B4C phases were determined by XRD analysis before and after the leaching process especially after an 8 h milling. The Al2O3-B4C composite powder obtained after milling under optimum milling conditions for 8 h was shaped into pellet with and without the addition of 2% by weight binder (paraffin) in a uniaxial press and cold isostatic press. The Al2O3-B4C composite obtained has a relative density value of 86% after sintering in the Ar atmospheric tube furnace at 1550 °C.
Similar content being viewed by others
References
Torabi, O., Ebrahimi-Kahrizsangi, R.: Combination of mechanochemical activation and self-propagating behavior for the synthesis of nanocomposite Al2O3/B4C powder. J. Alloys Compd. 514, 54–59 (2012)
Koc, U.: Synthesis and characterization of Al2O3-B4C composite at room temperature by mechanochemical method from aluminum-boron oxide-carbon mixtures at different ratios, (M.S.Thesis). Kütahya Dumlupınar University, Institute of Sciences, Department of Material Science and Engineering, (2018)
Sharifi, M.E., Karimzadeh, F., Enayati, M.H.: A study on mechanochemical behavior of B2O3–Al system to produce alumina-based nanocomposite. J. Alloys Compd. 482, 110–113 (2009)
Suri, A.K., Subramanian, C., Sonber, J.K., Murthy, T.S.R.Ch: Synthesis and consolidation of boron carbide: a review. Int. Mater. Rev. 55(1), 4–40 (2013)
Deng, F., Xie, H.Y., Wang, L.: Synthesis of submicron B4C by mechanochemical method. Mater. Lett. 60, 1771–1773 (2006)
Gokmese, H., Bostan, B.: Synthesis of Nano particle ceramic phase Al2O3/B4C by mechanochemical method and microstructural characterization. J. Fac. Eng. Archit. Gazi Univ. 29(2), 289–297 (2014)
Suryanarayana, C.: Mechanical alloying and milling. Prog. Mater. Sci. 46(1-2), 1–184 (2001)
Soni, P.R.: Mechanical Alloying: Fundamentals and Applications, pp. 35–49 ISBN 10: 1898326568. Cambridge International Science Publishing, UK (1999)
Torabi, O., Ebrahimi-Kahrizsangi, R.: Effect of the aluminum content on the mechanochemical behavior in ternary system Al–B2O3–C. Int. J. Refract. Met. Hard Mater. 36, 90–96 (2013)
Shaker, E., Sakaki, M., Jalaly, M., Bafghi, M.: Microwave synthesis of B4C-Al2O3 composite in a mechanically activated Al/B2O3/C powder mixture. Iran. J. Mater. Sci. Eng. 12(4), 89–99 (2015)
Torabi, O., Ebrahimi-Kahrizsangi, R.: Synthesis of B4C, Al2O3 and AlB12 reinforced Al matrix nano composites via mechanochemical method. J. Compos. Mater. 16, 1–11 (2011)
Waseda, Y., Matsubara, E., Shinoda, K.: X-Ray Diffraction Crystallography Introduction, Examples and Solved Problems. Springer, ISBN 978–3–642-16634-1 (2011)
Li, X., Jiang, D., Zhang, J., Lin, Q., Chen, Z., Huang, Z.: The dispersion of boron carbide powder in aqueous media. J. Eur. Ceram. Soc. 33, 1655–1663 (2013)
Gokmese, H., Bostan, B., Baris, M.: Fabrication and characterization of nanoceramic particle Al2O3/B4C composite by mechanochemical approach. Inorganic And Nano-Metal Chemistry. 47(3), 416–422 (2016)
Das, S., Datta, S., Mukhopadhyay, A.K., Pal, K.S., Basu, D.: Al-Al2O3 core-shell composite by microwave induced oxidation of aluminum powder. Mater. Chem. Phys. 122, 574–581 (2010)
Kipcak, A.S., Gurses, P., Derun, E.M., Tugrul, N., Piskin, S.: Characterization of boron carbide particles and its shielding behavior against neutron radiation. Energy Convers. Manag. 72, 39–44 (2013)
Zou, X., Qi, S., Xu, J., Suo, Z., An, L., Li, F.: Study on Au/Al2O3 catalysts for low-temperature CO oxidation in situ FT-IR. J. Nat. Gas Chem. 19, 307–312 (2010)
Suryanarayana, C., Al-Aqeeli, N.: Mechanically alloyed nanocomposites. Prog. Mater. Sci. 58, 383–502 (2013)
Sivasankaran, S., Sivaprasad, K., Narayanasamy, R., Satyanarayana, P.V.: X-ray peak broadening analysis of AA 6061100-x-xwt.% Al2O3 nanocomposite prepared by mechanical alloying. Mater. Charact. 62, 661–672 (2011)
De Castro, C.L., Mitchell, B.S.: Synthesis functionalization and surface treatment of nanoparticles, ed Baraton M.I, ‘Nanoparticles from Mechanical Attrition’ (American Scientific Publishers, USA), 1–15 (2001)
Balaz, P.: Mechanochemistry in nanoscience and minerals engineering, pp. 103–126. Springer Berlin Heidelberg, Germany (2008)
Lin, X., Ownby, P.D.: Pressureless sintering of B4C whisker reinforced Al2O3 matrix composites. J. Mater. Sci. 35, 411–418 (2000)
Huang, H.W., Wang, X.M., Yang, J., Xu, K., Dai, S.P.: Effect of carbide on Al2O3/B4C burnable poison sintered in Ar. Nucl. Eng. Des. 241, 4909–4912 (2011)
Laishram, K., Mann, R., Malhan, N.: A novel microwave combustion approach for single step synthesis of α-Al2O3 nanopowders. Ceram. Int. 38, 1703–1706 (2012)
Funding
The authors would like to thank for their financial support to the Kütahya Dumlupınar University Scientific Research Projects Department.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher’s note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Aydin, H., Goren, R. & Koc, U. Mechanochemical-assisted synthesis and characterization of Al2O3/B4C ceramics. J Aust Ceram Soc 56, 1271–1281 (2020). https://doi.org/10.1007/s41779-020-00467-z
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s41779-020-00467-z