Abstract
The effects of different Zr additions (0.05wt.%-0.5wt.%) on the structure and tensile properties of an Al-4.5Cu-0.3Mg-0.05Ti (wt.%) alloy solidified under a high cooling rate (18 °C·s-1), in as-cast and T6 heat-treated conditions were studied. The as-cast structure of the alloy consists of equiaxed grains of α-Al with an average size of 64 μm which is unaffected by the Zr additions, indicating the ineffectiveness of Zr in the grain refinement of the alloy. Scanning electron microscopy, along with X-ray diffraction analysis revealed the presence of elongated θ-Al2Cu at the grain boundaries; in addition, coarse Al3Zr particles exist in the intergranular regions of the 0.5wt.% Zr-containing alloy. After the T6 heat treatment, the elongated θ particles were fragmented; however, the coarse Al3Zr particles remained unchanged in the microstructure. Also, the formation of fine β′-Al3Zr and θ″-Al3Cu/θ′-Al2Cu phases during T6 heat treatment was revealed by transmission electron microscopy. The results of the tensile tests showed that the Zr additions increase the strength of the alloy in both as-cast and T6 heat-treated conditions, but reduce its elongation, especially with 0.5wt.% Zr addition. The 0.3wt.% Zr-added alloy in the T6 heat-treated condition has the highest quality index value (249 MPa). Fractography of the fracture surfaces of the alloys revealed ductile fracture mode including dimples and cracked intermetallic phases in both conditions.
Article PDF
Similar content being viewed by others
References
Polmear I J, StJohn D, Nie J F, et al. Light alloys: Metallurgy of the light metals. 5th edition, Arnold, London, 1995: 45–75, 284.
Plevachuk Y, Sklyarchuk V, Yakymovych A, et al. Density, viscosity, and electrical conductivity of hypoeutectic Al-Cu liquid alloys. Metall. Mater. Trans. A, 2008, 39A: 3040–3045.
Porter D A, and Esterling K E. Phase transformations in metals and alloys. 2nd edition, Chapman and Hall, London, 1992: 291–308.
Kovarik L, Court S A, Fraser H L, et al. GPB zones and composite GPB/GPBII zones in Al-Cu-Mg alloys. Acta Mater., 2008, 56: 4804–4815.
Wang S C, and Starink M J. Precipitates and intermetallic phases in precipitation hardening Al-Cu-Mg-(Li) based alloys. Inter. Mater. Rev., 2005, 50(4): 1–23.
Prasad K S, Prasad N E, and Gokhale A A. Microstructure and precipitate characteristics of aluminum-lithium alloys. In: N. E. Prasad, A. A. Gokhale, and R. J. H. Wanhill (Eds.), Aluminum-lithium alloys: Processing, properties, and applications. Butterworth-Heinemann, Oxford, 2013: 99–137.
Wang S C, and Starink M J. The assessment of GPB2/S″ structures in Al-Cu-Mg alloys. Mater. Sci. Eng. A, 2004, 386: 156–163.
Li Y Y, Guo G W, Zhang W W, et al. Effects of alloying elements on hot tearing trends of Al-Cu alloy. Trans. Nonferr. Met. Soc., 2001, 11: 765–791.
Ganjehfard K, Taghiabadi R, Noghani M T, et al. Tensile properties and hot tearing susceptibility of cast Al-Cu alloys containing excess Fe and Si. Int. J. Miner. Metall. Mater., 2021, 28(4): 718–728.
Kamga H K, Larouche D, Bournane M, et al. Hot tearing of aluminum-copper B206 alloys with iron and silicon additions. Mater. Sci. Eng. A, 2010, 527: 7413–7423.
Li Y, Li H, Katgerman L, et al. Recent advances in hot tearing during casting of aluminium alloys. Prog. Mater. Sci., 2021, 117: 100741. https://doi.org/10.1016/j.pmatsci.2020.100741.
Yoshida Y, Esaka H, and Shinozuka K. Effect of solidified structure on hot tear in Al-Cu alloy. IOP Conf. Ser.: Mater. Sci. Eng., 2015, 84: 1–6.
Kamali H, Emamy M, and Razaghian A. The influence of Ti on the microstructure and tensile properties of cast Al-4.5Cu-0.3Mg alloy. Mater. Sci. Eng. A, 2014, 590: 161–167.
Murty B S, Kori S A, and Chakraborty M. Grain refinement of aluminium and its alloys by heterogeneous nucleation and alloying. Inter. Mater. Rev., 2002, 47(1): 3–29.
Guan R G, and Tie D. A review on grain refinement of aluminum alloys: Progresses, challenges and prospects. Acta Metall. Sin. (Engl. Lett.), 2017, 30(5): 409–432.
He Y D, Zhang X M, and You J H. Effect of minor Sc and Zr on microstructure and mechanical properties of Al-Zn-Mg-Cu alloy. Trans. Nonferr. Met. Soc. China, 2006, 16: 1228–1235.
Robson J D, and Prangnell P B. Dispersoid precipitation and process modelling in zirconium containing commercial aluminum alloys. Acta Mater., 2001, 49: 599–613.
Mochugovskiy A G, Mikhaylovskaya A V, Zadorognyy M Y, et al. Effect of heat treatment on the grain size control, superplasticity, internal friction, and mechanical properties of zirconium-bearing aluminum-based alloy. J. Alloys Compd., 2021, 856: 157455. https://doi.org/10.1016/j.jallcom.2020.157455.
Davis J R, ed. Heat treating. ASM Handbook, ASM International, Materials Park, Ohio, 1991: 849.
Maxwell I, and Hellawell A. A simple model for grain refinement during solidification. Acta Metall., 1975, 23: 229–237.
Murray J, Peruzzi A, and Abriata J P. The Al-Zr (aluminum-zirconium) system. J. Phase Equilib., 1992, 13(3): 277–291.
Souza P H L, Oliveira de C A S, and Vale Quaresma do J M. Precipitation hardening in dilute Al-Zr alloys. J. Mater. Res. Technol., 2018, 7: 66–72.
Chen Y, Zhang Z, Chen Z, et al. The enhanced theta-prime (θ′) precipitation in an Al-Cu alloy with trace Au additions. Acta Mater., 2017, 125: 340–350.
Bourgeois L, Zhang Y, Zhang Z, et al. Transforming solid-state precipitates via excess vacancies. Nature Commun., 2020, 11: 1248. https://doi.org/10.1038/s41467-020-15087-1.
Song M, Chen K H, and Qi X W. Modeling effects of constituents and dispersoids on tensile ductility of aluminum alloy. Cent. South Univ. Technol., 2007, 14(4): 456–459.
Din T, Rashid A K M B, and Campbell J. High strength aerospace casting alloys: Quality factor assessment. Mater. Sci. Technol., 1996, 12: 269–273.
Ammar H R, Samuel A M, Samuel F H, et al. The concept of quality index and its application for Al-Si cast alloys. Inter. Metalcast., 2021, 15(4): 1197–1212. https://doi.org/10.1007/s40962-020-00556-6.
Van Stone R H, and Psioda J A. Discussion of “Metallurgical factors affecting fracture toughness of aluminum alloys”. Metall. Trans. A, 1975, 6: 668–670.
Acknowledgement
The University of Tehran is acknowledged for providing lab facilities for this work.
Author information
Authors and Affiliations
Corresponding author
Additional information
Hamed Kamali Male, born in 1987, Ph.D. His research interests mainly focus on processing-structure-property relationships in materials. He is also interested in conventional and high-resolution S/TEM.
Rights and permissions
About this article
Cite this article
Kamali, H., Kamali, E. & Emamy, M. Effects of Zr additions on structure and tensile properties of an Al-4.5Cu-0.3Mg-0.05Ti (wt.%) alloy. China Foundry 19, 9–16 (2022). https://doi.org/10.1007/s41230-022-1094-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s41230-022-1094-2
Keywords
- Al-Cu-Mg alloys
- casting
- T6 heat treatment
- structure
- precipitation hardening
- tensile properties
- fractography