Smelting of Industrial Solid Waste for Recovery of Aluminum: Effect of Charge Material

  • Thematic Section: Molten Slags, Fluxes, and Salts for Sustainable Processing
  • Published:
Journal of Sustainable Metallurgy Aims and scope Submit manuscript

Abstract

The present paper deals with the effect of charge material on the recovery of aluminum from the industrial solid waste. For the efficient recovery of aluminum metal having a lower vaporization temperature, smelting was carried out in the presence of metal (iron) solvent bath inside a graphite crucible. Nitrogen plasma arc was generated by passing the current as well as the nitrogen gas through a hollow graphite electrode. Charge containing bottom ash or a mixture of iron ore slime and bottom ash along with a reductant of different reactivity was used either in the form of powder or pellets. Liquid iron bath below the plasma arc zone was utilized as a solvent for the absorption of reduced metals after reduction of the oxides present in the wastes. The quick absorption of aluminum in the liquid iron bath subsequent to the reduction of oxides under an inert atmosphere minimized the vaporization loss of aluminum. The effects of carbon content and its reactivity, form of charge material, charge-layer thicknesses for different charge compositions on the recovery of aluminum were studied for 30 min of plasma exposure times in all cases. Maximum recovery of aluminum was found for the charge in powder form having a mixture of bottom ash and iron ore slime along with the increased carbon content as well as charge-layer thickness, respectively. The recovery of aluminum was found to be up to 40.80% for the powder charge containing 50% bottom ash and 50% iron ore slime with the char in double stoichiometry carbon.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6

Similar content being viewed by others

References

  1. Rai A, Mandal AK, Singh KK, Mankhand TR (2013) Preparation and characterization of lime activated unfired bricks made with industrial wastes. Int J Waste Resour 3:40–46. doi:10.12777/ijwr.v3.i1.p40

    Article  Google Scholar 

  2. Mandal AK, Sinha OP (2016) Preparation and characterization of fired bricks made from bottom ash and iron slime. J Mater Civ Eng. doi:10.1061/(ASCE)MT.1943-5533.0001767

    Article  Google Scholar 

  3. Sibanda V, Ndlovu S, Dombo G et al (2016) Towards the utilization of fly ash as a feedstock for smelter grade alumina production: a review of the developments. J Sustain Metall 2:167–184. doi:10.1007/s40831-016-0048-6

    Article  Google Scholar 

  4. Lai-shi LI (2011) Extraction of alumina from coal fly ash with sulfuric acid leaching method. Chin J Process Eng Process Eng 11:4–8

    Google Scholar 

  5. Wu C, Yu H, Zhang H (2012) Extraction of aluminum by pressure acid-leaching method from coal fly ash. Trans Nonferrous Met Soc China 22:2282–2288. doi:10.1016/S1003-6326(11)61461-1

    Article  CAS  Google Scholar 

  6. Guan X, Pal UB, Jiang Y, Su S (2016) Clean metals production by solid oxide membrane electrolysis process. J Sustain Metall 2:152–166. doi:10.1007/s40831-016-0044-x

    Article  Google Scholar 

  7. Myklebust H, Runde P (2005) Greenhouse gas emissions from aluminum carbothermic technology compared to Hall–Heroult technology. In: Kvande H (ed) Light metals 2005. TMS, Warrendale, PA, pp 519–522

  8. Liu Z, Li H (2015) Metallurgical process for valuable elements recovery from red mud—a review. Hydrometallurgy 155:29–43. doi:10.1016/j.hydromet.2015.03.018

    Article  CAS  Google Scholar 

  9. Wang Y, Feng N, You J, Peng J (2010) Method for producing coarse aluminum–silicon alloy from bauxite flotation tailings by carbothermal reduction. Faming Zhuanli Shenqing, Patent CN 101632958 A

  10. Borra CR, Blanpain B, Pontikes Y et al (2016) Smelting of bauxite residue (red mud) in view of iron and selective rare earths recovery. J Sustain Metall 2:28–37. doi:10.1007/s40831-015-0026-4

    Article  Google Scholar 

  11. Borra CR, Blanpain B, Pontikes Y et al (2016) Recovery of rare earths and major metals from bauxite residue (red mud) by alkali roasting, smelting, and leaching. J Sustain Metall. doi:10.1007/s40831-016-0103-3

    Article  Google Scholar 

  12. Kriskova L, Machiels L, Pontikes Y (2015) Inorganic polymers from a plasma convertor slag: effect of activating solution on microstructure and properties. J Sustain Metall 1:240–251. doi:10.1007/s40831-015-0022-8

    Article  Google Scholar 

  13. Mandal AK, Sinha OP (2014) Review on current research status on bottom ash: an indian prospective. J Inst Eng Ser A 95:277–297. doi:10.1007/s40030-014-0100-0

    Article  CAS  Google Scholar 

  14. Pickles CA, Mclean A, Alcoc CB, Nikolic RN (1990) Plasma recovery of metal values from fly ash. Can Metall Q 29:193–200

    Article  CAS  Google Scholar 

  15. Mandal AK, Sinha OP (2016) Recovery of multi-metallic components from bottom ash by smelting reduction under plasma environment. Metall Mater Trans B 47:19–22. doi:10.1007/s11663-015-0484-x

    Article  CAS  Google Scholar 

  16. Mandal AK, Sinha OP (2016) Smelting reduction of bottom ash in presence of liquid steel bath for recovery of aluminium. In: Reddy RG, Chaubal P, Pistorius PC, Pal U (eds) Advances in molten slags, fluxes, and salts. TMS, Warrendale, PA; John Wiley & Sons, Hoboken, pp 873–877

    Chapter  Google Scholar 

  17. Kumar M, Gupta RC (1994) Influence of carbonization conditions and wood species on carbon dioxide reactivity of resultant wood char powder. Fuel Process Technol 38:223–233. doi:10.1016/0378-3820(94)90050-7

    Article  CAS  Google Scholar 

  18. Gupta RC (2010) Theory and laboratory experiments in ferrous metallurgy, 1st edn. PHI Learning Private Limited, New Delhi

    Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Department of Metallurgical Engineering, IIT (BHU), Varanasi, Varanasi, Uttar Pradesh, 221005, India

    A. K. Mandal & O. P. Sinha

Authors
  1. A. K. Mandal
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. O. P. Sinha
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to A. K. Mandal.

Additional information

The contributing editor for this article was Veena Sahajwalla.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Mandal, A.K., Sinha, O.P. Smelting of Industrial Solid Waste for Recovery of Aluminum: Effect of Charge Material. J. Sustain. Metall. 3, 696–702 (2017). https://doi.org/10.1007/s40831-017-0129-1

Download citation

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s40831-017-0129-1

Keywords

Search

Navigation