Highlights
-
A multifunctional Janus film is fabricated by integrating highly-crystalline and oxidation-resistant Ti3C2Tx MXene with carbon nanotube (CNT) film through strong hydrogen bonding, which exhibits high electrical conductivity of 4250 S cm−1 and robust mechanical strength of 77 MPa.
-
The MXene/CNT Janus film of 15 μm thickness demonstrates efficient electromagnetic interference shielding of 72 dB, low infrared (IR) emissivity of 0.09 and hence superior thermal camouflage performance, and outstanding IR detection capability, while maintaining its integrity equally at room temperature as well as under extreme conditions.
-
This multifunctional MXene/CNT Janus film offers a practical solution for electromagnetic shielding and IR shielding/detection in challenging conditions.
Abstract
Multifunctional, flexible, and robust thin films capable of operating in demanding harsh temperature environments are crucial for various cutting-edge applications. This study presents a multifunctional Janus film integrating highly-crystalline Ti3C2Tx MXene and mechanically-robust carbon nanotube (CNT) film through strong hydrogen bonding. The hybrid film not only exhibits high electrical conductivity (4250 S cm−1), but also demonstrates robust mechanical strength and durability in both extremely low and high temperature environments, showing exceptional resistance to thermal shock. This hybrid Janus film of 15 μm thickness reveals remarkable multifunctionality, including efficient electromagnetic shielding effectiveness of 72 dB in X band frequency range, excellent infrared (IR) shielding capability with an average emissivity of 0.09 (a minimal value of 0.02), superior thermal camouflage performance over a wide temperature range (− 1 to 300 °C) achieving a notable reduction in the radiated temperature by 243 °C against a background temperature of 300 °C, and outstanding IR detection capability characterized by a 44% increase in resistance when exposed to 250 W IR radiation. This multifunctional MXene/CNT Janus film offers a feasible solution for electromagnetic shielding and IR shielding/detection under challenging conditions.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
The need for multifunctional, flexible, robust, and ultrathin films has surged to meet the evolving requirements in electronics, thermal management, military, and aerospace technologies. However, bestowing these films with multifunctional characteristics such as electromagnetic interference (EMI) shielding and the capability to conceal and detect infrared (IR) radiation is particularly challenging under harsh environmental conditions involving extremely low and high temperatures [1,2,3,4,5,6,7,8].
Conventional metals such as Cu and Al exhibit superior EMI and IR-shielding capabilities owing to their highly conductive nature and low IR emissivity [9,10,11,12,13,14]. However, their high density, processing complexity, and susceptibility to corrosion in harsh environments limit their practical use [11, 15, 16]. Carbon-based materials such as carbon nanotubes (CNTs) and graphene have emerged as promising alternatives to EMI-shielding IR-detecting materials, owing to their excellent mechanical strength and IR-absorbing capabilities [14, 17,18,19]. However, their moderate electrical conductivity requires the use of thicker films for achieving satisfactory EMI shielding [20,21,22] and their high IR emissivity impairs their utility for IR shielding and thermal camouflage applications [22].
Recently, two-dimensional transition metal carbides/nitrides (also known as MXenes) have garnered attention as multifunctional nanomaterials owing to their excellent metallic conductivity, low IR emissivity, tunable composition and surface chemistry, and outstanding solution processibility for various applications including EMI shielding, energy storage, sensing, and thermal camouflage [23,24,25,26,27,28,29,30,31,32,33,34]. These materials have the general formula Mn+1XnTx (n = 1–4), where M, X, and Tx represent a transition metal, carbon or nitrogen, and surface terminal groups (–OH/ = O/–F), respectively. However, despite their promising attributes, MXenes face challenges associated with their inferior mechanical properties and poor environmental stability under harsh conditions, primarily owing to their defective atomic structure, which restricts their practical applications [35].
MXenes are typically synthesized by selectively etching the element A from their parent MAX crystals using strong acids. However, they tend to contain atomic defects or vacancies along their edges and surfaces, which initiate oxidative degradation in the presence of water and/or oxygen, leading to the degradation of their physical properties [36,37,38]. In particular, the atomic defects in Ti-based MXenes (Ti3C2Tx) function as active sites for Ti oxidation, with Ti vacancies acting as positively charged regions and C4− ions losing electrons to promote the formation of TiO2 [39]. Recently, highly crystalline Al-rich Ti3AlC2 MAX crystals have been synthesized by introducing excess Al precursor. The reported process substantially reduced the defect density, enhanced the oxidation resistance, and improved the electrical conductivity by up to 20,000 S cm−1 [40]. However, the insufficient mechanical flexibility, strength, and durability of the MXenes—both at room temperature and under harsh environmental conditions—constrain their practical applications.
MXene-based polymer composites and hybrids have been extensively studied to improve the mechanical strength and durability of MXenes in harsh environments [41,42,43,44,45,46,47,48,49,50]. Hydrophilic terminal groups on the MXene surface, such as –OH, =O, and –F, facilitate the formation of strong hydrogen bond interactions with polar polymeric chains, thereby improving the mechanical strength and durability [44, 51,52,53,54,55,56,57]. However, non-conducting feature of polymers suppresses the electrical conductivity, thereby retarding the EMI-shielding as well as IR-shielding capabilities of MXenes, and increases their IR emissivity [24, 58]. Combining MXenes with carbon-based materials, such as CNT, graphene, and reduced graphene oxide (rGO), can result in mechanical properties and EMI-shielding capability superior to those of MXene–polymer composites, owing to the conductive nature of carbon materials [59]. However, this combination strategy significantly impairs the IR-shielding ability of MXenes, owing to the strong IR-absorbing capability of carbon materials, leading to higher emissivity [60]. Consequently, research is focusing on optimizing a composite structure that fully leverages the high conductivity, low IR emissivity, and impressive EMI-shielding capability of MXenes in addition to the mechanical robustness of carbon materials. In this regard, Janus structures, which exhibit different microstructures and chemical components on opposite sides, have recently gained prominence because of their tunable mechanical properties and synergistic multifunctionality, without sacrificing intrinsic properties [47, 61, 62]. However, existing literature lacks comprehensive coverage of MXene's challenges concerning oxidation and its inferior mechanical characteristics, as well as the retention of these properties under extreme temperature conditions. Furthermore, there also remains a significant gap in the exploration of the infrared shielding and detection functionalities, particularly in challenging environments.
In this study, a bi-layer Janus-type hybrid film composed of highly-conductive and environmentally-stable Al–Ti3C2Tx MXene coating on a robust CNT film was developed. The robust CNT film with an average thickness of 10 µm was prepared using an aerogel spinning method based on a modified chemical vapor deposition followed by roller pressing (calendaring). A highly crystalline Ti3C2Tx MXene (Al–Ti3C2Tx) with improved electrical conductivity and environmental stability was synthesized by selectively etching of A elements from Ti3AlC2 MAX phase, which was synthesized with excess Al precursor. Subsequently, Janus films of Ti3C2Tx MXene/CNT (denoted as MC) were fabricated by coating the CNT film with delaminated Ti3C2Tx MXene sheets using various MXene/CNT weight ratios (1:4 (MC14), 1:2 (MC12), and 1:1 (MC11)) by vacuum-assisted filtration. The resulting Janus films exhibited outstanding mechanical strength and durability, as well as impressive multifunctional properties including superior EMI shielding and IR shielding/detection capabilities, even at extremely low and high temperatures, rendering it highly desirable for integrated electronics, thermal management systems, and military and aerospace applications.
2 Experimental Section
2.1 Materials and Chemicals
Conventional Ti3AlC2 MAX phase (99.9% purity) was purchased from INNOMXENE Co., Ltd., Republic of Korea. Powder of titanium oxide (TiO2, 99.5%, 400 mesh) was purchased from Junsei Chemical Co., Ltd. Lithium fluoride (LiF, 98.5%), Ti (99.5%, 325 mesh), graphite (99.8%, 325 mesh), and Al (99.5%, 325 mesh) powders were sourced from Alfa Aesar. Hydrochloric acid (HCl, 37%), hydrofluoric acid (HF, ACS reagent grade, 48%), ferrocene (0.2 wt%, 98%), polysorbate (1.0 wt%), and thiophene (0.8 wt%, 99%) were purchased from Sigma Aldrich. Acetone (98.0 wt%) and N-methyl-2-pyrrolidone (NMP) were procured from Samchun Chemical, Republic of Korea. The CNTs powder (97%, diameter 20 nm, and length 10 μm) were purchased from Applied Carbon Nano Technology, Republic of Korea. All chemicals were used as received.
2.2 Synthesis of Al–Ti3AlC2 MAX and Al–Ti3C2Tx MXene
To synthesize highly crystalline Al-rich Al–Ti3AlC2 MAX, we synthesized the high-quality TiC powder through a high-energy ball milling-assisted carbothermal reduction method, employing titanium oxide (TiO2) and carbon powder with a molar ratio of TiO2:C = 1:2.4 [36]. The TiO2 and graphite powder mixture underwent high-energy ball milling in a planetary mill (OMBMNN-1507231, MTDI Inc., Korea). Subsequently, the powder mixture underwent heat-treatment at 1500 °C for 3 h under a vacuum of 6.7 × 10−3 Pa to synthesize a high-quality TiC powder. The synthesized TiC was mixed with Ti and accessed Al precursors in a molar ratio of 2:1.2:2.2 and subsequently subjected to continuous ball milling for 12 h at 100 rpm. The resulting mixture was molded into a Ø50 mm disk using a hydraulic press with 4000 psi, followed by thermal annealing at 1450 °C for 3 h in argon atmosphere at atmospheric pressure. The resulting Al–Ti3AlC2 MAX disk was pulverized using a jaw crusher, followed by washing with 9 M HCl for 12 h and rinsing with deionized water multiple times to remove impurities. Subsequently, the purified MAX powder was then dried at 60 °C for 12 h in a vacuum oven. The dried powder was sieved through a 270-mesh (53 µm) sieve and used for the synthesis of Al–Ti3C2Tx MXene.
The Al–Ti3C2Tx MXene was synthesized using a modified minimally intensive layer delamination (MILD) method, which involved selectively etching Al from the parent Al–Ti3AlC2 MAX phase [63]. Briefly, LiF (1.6 g) was dissolved in a mixture of HCl (20 mL, 9 M) and an aqueous HF solution (3 mL) in a polypropylene container and stirred. To prevent the sudden temperature increase caused by exothermic reaction, the Al–Ti3AlC2 MAX powder (1 g) was gradually added to the LiF/HCl/HF solution while stirring continuously with a magnetic stirrer. Under these conditions, the etching reaction was allowed to proceed for 24 h at 35 °C. The product obtained after etching was washed several times with deionized water by centrifugation at 3500 rpm for 5 min until the pH of the supernatant reached 5–6. Subsequently, the obtained delaminated Al–Ti3C2Tx flakes in an aqueous dispersion were used for sample preparation and characterization. For comparison, the conventional Ti3C2Tx MXene was synthesized using the Ti3AlC2 MAX phase (InnoMXene) by following the same synthesis protocol.
2.3 Synthesis of CNT Film
CNT film was synthesized through a modified chemical vapor deposition method [64]. In this synthesis, a precursor solution was prepared by mixing ferrocene (Fe(C5H5)2, 0.2 wt%, 98% purity), thiophene (C4H4S, 0.8 wt%, 99% purity), (C3H6O, 98.0%, 99.7% purity), and polysorbate (1 wt%) [65, 66]. The resulting mixture was injected into a vertically oriented reactor heated to 1250 °C at a rate of 10 mL h−1. Hydrogen carrier gas (H2) was introduced at a flow rate of 1000 sccm. During the synthesis, ferrocene decomposed into catalyst iron nanoparticles at 400 °C [67]. As the reactor temperature ranged between 800 and 900 °C, thiophene degraded into sulfur, acting as a catalyst activator and combining with iron to create iron sulfide [67]. Subsequently, carbon from acetone diffused into iron sulfide, initiating the nucleation of carbon nanotube. The carbon nanotubes grew and integrated into an aerogel CNT sock, continuously winding onto a cylindrical winder, ultimately producing a CNT film at the bottom of the reactor. The modified chemical vapor deposition process allows for adjustable thickness of the CNT film, ranging sub-micron to as thick as required. In this study, the synthesized CNT film with an average thickness of 10 µm and a large area of 100 × 300 cm2 was used throughout the experiments.
2.4 Fabrication of MXene/CNT (MC) Janus Film
The CNT sheet was subjected to UV–ozone treatment (UV–Ozone cleaner AC-3) for 5 min to introduce hydrophilic oxygen-containing functional groups on its surface. The ozone-treated CNT sheet was then cut into a circular shape with the same diameter as that of the filtration flask (38 mm) and placed on a polyvinylidene fluoride filter membrane (pore size, 0.45 µm). Subsequently, an Al–Ti3C2Tx MXene dispersion (4 mg mL−1) was poured on top of the CNT film at different loading concentrations to obtain Janus films with different MXene/CNT (MC) mass ratios (1:4, 1:2, and 1:1; denoted as MC14, MC12, and MC11, respectively). The resulting MC Janus films were vacuum dried at 100 °C for 8 h. The MXene and CNT sides of the Janus films are denoted as MC-M and MC-C, respectively. For comparison, an Al–Ti3C2Tx MXene/CNT (1:1) blend film (MC11-Blend) was prepared by simply mixing the Al–Ti3C2Tx MXene and multiwalled CNT (with a diameter of 20 nm) powder, followed by vacuum filtration.
2.5 Characterization
Surface and cross-sectional morphologies of the MXene flakes, CNT sheets, and MC Janus films were examined by field-emission SEM (JSM-7600F, Japan) coupled with energy dispersive spectroscopy (EDS). The crystal structure was investigated by XRD (D8, Bruker, USA) using Cu Kα radiation. The XRD scans covered a 2θ range of 4°–80° at a rate of 2° min−1, with a window slit dimension of 10 × 10 mm2. For the atomic-scale structural analysis, HRTEM (JEM-2100F, Japan) was performed at an acceleration voltage of 200 kV to obtain high-resolution images of individual MXene flakes. To investigate the elemental compositions of the specimens, XPS was performed using Al Kα radiation (1486.6 eV) with an ESCALAB250 (USA) instrument. FTIR spectroscopy (JASCO-4700, Japan) was conducted to identify and analyze the chemical compositions of the materials based on their interactions with IR light. Electrical conductivity was measured using a four-pin probe (MCP-TP06P PSP) connected to a Loresta-GP meter (Model MCP-T610, Mitsubishi Chemical, Japan). EMI-shielding measurements were performed using a two-port network analyzer (ENA5071C, Agilent Technologies, USA) with a rectangular WR-90 waveguide in TE10 mode in the X-band (frequency range of 8.2–12.4 GHz), and Ku band (frequency range 12.4–18 GHz).
The mechanical properties were explored at ambient, low (− 65 °C), and high temperatures (200 °C) using a universal testing machine (Instron 5567A) having environmental chamber with a crosshead speed of 5 mm min−1 and a 2 KN load cell. Each specimen was rectangular and had a length, width, and variable thickness of 30 mm, 10 mm, and 10–17 µm, respectively. Each sample underwent tensile testing five times.
IR images and temperature data were acquired using an IR camera (FLIR A310, FLIR, Sweden) with an emissivity of 0.94. An FTIR spectrometer (JASCO-4700, Japan) was employed to determine the reflectivity (R) of the MXene coatings in the 2.5–15 μm range at room temperature. The reflectance of the thin film was directly measured, and the emissivity ε was calculated using Kirchhoff’s law as ε = 1 − R.
The performance of the IR detector was evaluated using a digital multimeter (Keysight 34450A). Essentially, an IR lamp (HH2500) was used to illuminate the MC11-C sample measuring 2 cm × 2.5 cm, and the resulting changes in resistance and temperature were measured using the digital multimeter. The water contact angles of the MXene thin films were determined using a camera (UI-1220LE-M-GL, IDS, Germany).
3 Results and Discussion
3.1 Preparation and Characterization of Ti3C2Tx/CNT Janus Films
The MC Janus film was prepared by sequentially depositing Al–Ti3C2Tx MXene onto a CNT film by vacuum-assisted filtration, which formed strong hydrogen bonds between the oxygen-containing functional groups at the interfaces (Fig. 1a). The Al–Ti3C2Tx MXene synthesis was validated by the shift of (002) X-ray diffractometry (XRD) peak toward a lower angle from 9.7° to 6.95°, indicating an increase in the interlayer spacing from 0.91 to 1.26 nm by the selective chemical etching of Al from the parent Ti3AlC2 MAX phase (red profile in Fig. 1b) [63]. The obtained aqueous dispersion of synthesized Al–Ti3C2Tx MXene was greenish in color (Fig. S1a), where the Scanning electron microscopy (SEM; Fig. S1b) and transmission electron microscopy (TEM) with selected area electron diffraction (SAED) analyses (Fig. 1c) of MXene flakes revealed their transparency and monolayer nature, which featured a smooth surface, sharp edges, and a maintained hexagonal lattice structure. High-resolution TEM (HRTEM) image of a single Al–Ti3C2Tx MXene flake (Fig. 1d) verified its highly crystalline atomic structure. The configured structure minimized Ti vacancies and oxygen impurities in the carbon sublattice, resulting in improved flake quality, which helped enhance the ensuing electrical conductivity and oxidative stability [36, 40]. Free-standing film of Al–Ti3C2Tx MXene was fabricated by vacuum filtration and its surface and cross-sectional morphologies, along with elemental compositions were examined by SEM (Fig. S1c–e). X-ray photoelectron spectroscopy (XPS) profiles demonstrate the successful elimination of Al 2p peak at 74.5 eV (Fig. S2a). The deconvoluted Ti 2p (Fig. S2b) peaks reveal that four pairs of doublets at 454.6 eV (460.9 eV), 455.6 eV (462.0 eV), 456.5 eV (463.3 eV), and 458.0 eV (465.3 eV) are assigned to the Ti–C, Ti2+, Ti3+, and Ti4+ (TiO2) respectively [38, 68]. The C 1s profile displays two major peaks at 282.2 and 284.4 eV, assigned to Ti–C and C–C respectively (Fig. S2c), and the elemental composition is shown in Fig. S2d [38, 68]. The pronounced Ti–C peak in both Ti 2p, and C 1s corroborated successful synthesis of Al–Ti3C2Tx MXene. For comparison, a conventional Ti3C2Tx MXene was synthesized from the Ti3AlC2 MAX phase using a stoichiometric ratio of Al precursor, following the aforementioned procedure (Fig. S3a–c). The UV–vis spectra with time indicates that Al–Ti3C2Tx MXene shows excellent oxidation stability as compared to the conv. Ti3C2Tx due to its highly crystalline atomic structure (Fig. S4a, b).
A conductive, robust, and large-area CNT film was fabricated using an aerogel spinning technique based on modified chemical vapor deposition, followed by roll pressing (Figs. 1e and S5) [64]. The presence of (002) peak at 2θ value of 26.1° is attributed to the CNT film, which is similar to the less-defective stacked neighboring graphene sheets (JCPDS 26-1079) (blue profile in Fig. 1b) [69, 70]. The CNT film had an average thickness of 10 µm over a large area of 100 × 300 cm2 (Fig. S6a). Low- and high-magnification SEM analyses of the CNT film indicated that individual CNT with an average diameter of approximately 21 nm (Fig. S6b) were aligned in the in-plane direction (Fig. 1f). The deconvoluted XPS of C 1s profile of the CNT film exhibited the presence of strong C–C peak at 284.8 eV, and the absence of peaks associated with oxygen impurities (e.g., C=O, and C–OH), indicating its high purity and excellent quality (Fig. S6c). The pristine CNT film had a hydrophobic surface with a water contact angle of 84° (Fig. 1g, Movie S1), presumably owing to its pure graphitic sp2 carbon bonds [71]. However, this led to poor compatibility with the hydrophilic surface terminations of Al–Ti3C2Tx. To overcome this, the CNT film was subjected to UV–ozone treatment for 5 min to introduce enough oxygen-containing functional polar groups (–COOH, –OH, and C=O). Consequently, UV–ozone treated film showed improved hydrophilicity (contact angle, 65°), comparable to that of the Al–Ti3C2Tx MXene film (contact angle, 58°) (Fig. 1g, Movie S2) [72, 73]. Moreover, the EDS analysis shows increase in oxygen content from 3.5% for untreated CNT, to 9.1% for ozone treated CNT film (Figure S6d-e).
The flexible Janus films, comprising the Al–Ti3C2Tx MXene and ozone-treated CNT film, were fabricated by vacuum-assisted filtration with varying MXene content, followed by drying in a vacuum oven at 100 °C for 12 h, and analyzed for their XRD pattern (green profile in Fig. 1b, h). Cross-sectional SEM image (Fig. 1i) revealed a 15-μm-thick MC11 Janus film with robust integration between the two distinct layers, suggesting strong interlayer interactions. The respective EDS mapping (Fig. S7) confirmed the distribution of Ti and C, which primarily originated from Al–Ti3C2Tx MXene and CNT, respectively, thereby validating the formation of a Janus-type layered structure.
The interfacial interactions between Al–Ti3C2Tx MXene and CNT film were substantiated by Fourier-transform infrared (FTIR) spectroscopy. The FTIR spectrum of as-prepared CNT film showed peaks at 3430 cm−1 (O–H) and at 1580 and 1405 cm−1 (C=O) (black spectrum in Fig. 1j). After ozone treatment, a substantial increase in the intensity and broadness of the –OH and C=O peaks was observed, manifesting increased content of oxygen-containing functional groups; consistent with the decreased water contact angle. The Al–Ti3C2Tx MXene displayed characteristic peaks at 3430 and 1630 cm−1, corresponding to –OH vibrations of surface functional groups and adsorbed water, while the peak at 2920 cm−1 corresponds to C–H stretching [74,75,76,77,78]. Notably, the MC11 Janus film showed slight shift in the hydroxyl peak from 3432 to 3403 cm−1 compared with that of the as-prepared CNT and MXene films, indicating the formation of hydrogen bond interactions between the surface terminations of MXene (–OH and =O) and the oxygen-containing functional groups of the ozone-treated CNTs (magnified –OH peak in Fig. 1j) [61, 79]. The hydrogen bond interactions resulted in robust structural integration of the MXene–CNT Janus film. Hence, large-area MXene/CNT Janus films could also be fabricated using different processing techniques, such as spray coating, for potential applications. For comparison, a homogeneous composite film of Al–Ti3C2Tx MXene and CNT (denoted as MC11-Blend) was prepared by solution blending (Fig. S8a). The cross-sectional SEM and EDS results certified the distribution of MXene and CNTs throughout the MC11-Blend film (Fig. S8b–d).
3.2 Mechanical and Electrical Properties Measurement
Mechanical flexibility, strength, and durability are crucial parameters for next-generation electronics, military, and aerospace applications, particularly under challenging environmental conditions, encompassing extremely low and high temperatures. Therefore, tensile stress–strain curves of the MC11 Janus, MC11-Blend, CNT, and Al–Ti3C2Tx MXene films were acquired at room temperature (Figs. 2a and S9a). The Al–Ti3C2Tx MXene film exhibited tensile strength and elongation-at-break values of 41 MPa and 0.5%, respectively. The MC11 Janus film demonstrated an improved elongation at break and tensile strength (77 MPa and 30%, respectively), primarily owing to the high tensile strength and elongation-at-break values of the CNT film (199.2 MPa and 18.5%). Notably, the MC11 Janus film exhibited considerably higher elongation at break and tensile strength values than those of the MC11-Blend film (48 MPa and 7%) of comparable thickness. It was also observed that the tensile strength improved with increasing CNT content (Fig. 2b). The Young's modulus of the Janus film also exhibited an increasing trend with the increase in MXene content due to its brittle nature (Fig. S9b). These results indicated that the enhanced strength and flexibility were due to the strong hydrogen bond interactions between the MXene and CNT layers, as well as the robustness of the CNT film.
Interestingly, electrical conductivity of Al–Ti3C2Tx MXene film (17,500 S cm−1) was double the value of conventional Ti3C2Tx MXene (8500 S cm−1), owing to its high crystallinity. The electrical conductivity of the Janus films decreased with increasing CNT content owing to relatively low conductivity of the CNT film (2130 S cm−1) (Fig. 2c and S10a). Therefore, MC11 Janus exhibited an electrical conductivity of 4250 S cm−1.
To assess mechanical flexibility, the MC11-Blend, MC11-Janus, and Al–Ti3C2Tx MXene films were subjected to bending cycles with a 6 mm curvature at room temperature (Fig. 2d), and evaluated for their retained electrical conductivities. The MC11-Blend film was highly brittle and hence, ruptured during the first bending cycle. The Al–Ti3C2Tx MXene film exhibited high electrical conductivity retention for 50 bending cycles but fractured thereafter. Notably, the MC11-Janus film showed efficient electrical conductivity retention for 300 bending cycles without any breakage, owing to its excellent flexibility. Furthermore, in tensile tests conducted at the extreme temperatures of − 65 and 200 °C, the MC11 Janus film showed marginal decreases in tensile strength (13% at − 65 °C and 12% at 200 °C), whereas the Al–Ti3C2Tx MXene film exhibited substantially reduced values (61% at − 65 °C and 65% at 200 °C; Fig. 2e). Essentially, owing to the excellent mechanical properties of the CNT and the formed hydrogen bonds, the Janus film retained its mechanical flexibility and electrical conductivity even under extreme environmental conditions [79]. Additionally, to assess the flexibility under high-temperature conditions, the CNT, MC11-Janus, and Al–Ti3C2Tx MXene films were subjected to a thermal shock of Δ396 °C (annealing in oven (200 °C, 30 s) followed by dipping into liquid nitrigen (− 196 °C, 30 s) Fig. 2f). Interestingly, the CM11-Janus film exhibited outstanding flexibility and durability even against severe thermal shocks. Also, the MC11-Janus film retained its flexibility even after exposure to liquid nitrogen and folding, in contrast to the Al–Ti3C2Tx MXene that became very brittle and ruptured (Movies S3–S5).
3.3 Electromagnetic Shielding Effectiveness (SE) Measurement
The fabricated films of CNT, MC14, MC12, MC11-Janus, MC11-Blend, and Al–Ti3C2Tx were investigated for their total EMI-shielding effectiveness (SET), shielding effectiveness by reflection (SER), and shielding effectiveness by absorption (SEA) in the X-band frequency range of 8.2–12.4 GHz (Fig. 3a–c), and Ku band frequency range of 12.4–18 GHz (Fig. S12). A 10-µm-thick Al–Ti3C2Tx MXene film with the highest electrical conductivity exhibited higher SET value (88 dB) than that of the CNT and conventional Ti3C2Tx MXene films (57 and 73 dB, respectively). In the fabricated MC Janus films, the resulting EMI SET increased with increasing MXene content (and increased electrical conductivity), where the MC11 Janus film exhibited a value of 72 dB Fig. 3a. The conventional-MXene-based MC Janus films also showed a similar trend (Fig. S10b), however, the absolute values were lower than their counterparts. The SER values of all films saturated at approximately 25 dB (Fig. 3b), whereas the SEA values of all the samples followed a trend similar to that of the SET values (Fig. 3c). Interestingly, the MC11 Janus film also exhibited outstanding specific shielding effectiveness (SSE/t) of 34,006 dB cm2 g−1 which is higher than most of the reported literature (Fig. S11 and Table S1). The large SSE/t value indicates that the fabricated MC11 Janus film have strong capability for potential use as lightweight and ultrathin EMI shielding material [34]. Furthermore, the SET, SER, and SEA values of all the samples have been analyzed in the Ku band, ranging from 12.4 to 18 GHz (Fig. S12a–c). The increasing trend in SET, and SEA is observed for all samples in the Ku band compared to the X band, attributable to the increase in frequency. Conversely, the SER of all the samples exhibits a slight decrease in the Ku band. This behavior can be explained by Simon’s formulae for conductive materials, where SEA, SER have a direct and inverse relation, respectively, to the frequency, as represented in the following equation:
Here, σ, f, and d denote the electrical conductivity (S cm-1), frequency (MHz), and thickness (m), respectively. The first and second parts of the equation represent the shielding effectiveness reflection (SER) and the shielding effectiveness absorption (SEA), respectively [80].
Additionally, the MC11-Janus film demonstrated significant retention of EMI-shielding capability after undergoing 300 bending cycles and 30 cycles of thermal shock with a temperature difference of Δ396 °C (Fig. 3d). Similarly, Al–Ti3C2Tx MXene exhibited good EMI-shielding retention, experiencing only a marginal decrease of 2 dB in EMI SET, from 88 to 86 dB, after the large thermal shock of Δ396 °C. This minimal reduction was attributed to a slight decrease in electrical conductivity from 17,500 to 16,700 S cm−1. In contrast, conv.Ti3C2Tx MXene revealed relatively higher reduction in EMI shielding, dropping from 73 to 65 dB after the same thermal shock, manily due to a decrease in its electrical conductivity from 8500 to 5200 S cm−1 (Fig. S13). Therefore, these outstanding EMI shielding performance and its retention ability against large thermal shock were attributed to the excellent oxidative stability of the Al–Ti3C2Tx MXene, the outstanding mechanical flexibility of the CNT film, and the robust interfacial integration between the Al–Ti3C2Tx MXene and CNT films, even in harsh environments.
3.4 Infrared Shielding and Thermal Camouflage
All the materials emit thermal radiation in the IR spectrum when their temperature exceeds absolute zero (0 K) [81]. According to the Stefan–Boltzmann law, expressed as P = εσT4 (where P, ε, σ, and T represent the thermal radiation emitted by an object, IR emissivity, Stefan–Boltzmann constant, and the surface-level thermodynamic temperature of the object, respectively), the thermal radiation emitted by an object is directly proportional to the fourth power of the surface temperature and the IR emissivity of the material [82].
The IR emissivity values of the CNT, Al–Ti3C2Tx, MC11-C (CNT side), MC11-M (MXene side), and MC11-Blend films were measured at room temperature in the wavelength range of 2.5–15 μm (Fig. 4a, Table S2). The Al–Ti3C2Tx and MC11-M Janus films exhibited remarkably low average IR emissivity values of 0.05 and 0.09, respectively, with the corresponding minimum IR emissivity recorded for both the materials to be 0.02 (Table S2); the obtained values are lower than those of most previously reported MXenes (Fig. S14 and Table S3). The low IR emissivity was likely due to significantly high electrical conductivity of Al–Ti3C2Tx (17,500 S cm−1), given the inverse relationship between surface IR emissivity and electrical conductivity [83]. Similarly, the Al–Ti3C2Tx MXene films exhibited a lower average IR emissivity (0.05) than that of the conv. Ti3C2Tx MXene (0.13) (Fig. S15a). Therefore, the Al–Ti3C2Tx MXene film showed a considerably larger temperature reduction (33.5 °C) than that of the conv. Ti3C2Tx (38.7 °C) when placed on a hot plate to achieve a surface radiation temperature of 100 °C. This difference was ascribed to the higher electrical conductivity of Al–Ti3C2Tx (Fig. S15b, c).
The CNT, MC11-C, and MC11-Blend specimens showed high emissivity values of 0.94, 0.88, and 0.76, respectively, owing to the intrinsically-strong IR absorption capability of the CNT [84]. To comprehensively analyze the thermal camouflage performance of the fabricated samples, a heating stage (hot plate) was employed to simulate a background temperature of 100 °C. Initially, films featuring the CNTs, conv. Ti3C2Tx, Al–Ti3C2Tx, MC Janus specimens having CNTs and MXene as the top-sides (MC-C and MC-M, respectively), and MC11-Blend were positioned on the hot plate being heated at 100 °C. Subsequently, the increase in the radiation temperature over time was recorded using an IR camera for the MC-C and MC-M specimens. The surface radiation temperature of a 10-µm-thick Al–Ti3C2Tx film (33.5 °C) was significantly lower than that of the CNTs (83 °C) and MC-C (86 °C) (Fig. S16), due to its higher electrical conductivity. Unlike the MC-C film, the MC-M film exhibited a low surface radiation temperature of 33.9 °C, which was comparable to that of the Al–Ti3C2Tx MXene film. An analysis of the relationship between IR emissivity and the radiation temperature reduction for the Al–Ti3C2Tx MXene, MC11-M, MC11-C, CNT, and MC11-Blend specimens (Fig. 4b) indicated that the lower the IR emissivity of the materials, the higher the reduction in radiation temperature and the better the thermal camouflage performance of the sample. These results are consistent with those reported previously [83].
The thermal camouflage performance of MC11-M Janus film was evaluated at low, ambient, and high temperatures. At a low temperature, the MC11-M film was attached to a ceramic cup filled with ice. The temperature increased from − 0.5 to 20.2 °C, close to that of air (22 °C) (Fig. 4c). For the room-temperature test, a 10 × 12 cm2 MC11-M Janus film was attached to a volunteer’s t-shirt, following which the temperature decreased from 34.5 °C (clothes temperature) to 25.1 °C (sample temperature) (Fig. 4d). For high temperature case, the high-temperature thermal camouflage performance of the MC11-M film was evaluated by putting film onto hot plate with the background temperature of 300 °C. The temperature recorded on the surface of the sample was 57.5 °C (Fig. 4e). Overall, these results underscored the viability of using low-emissivity MC Janus films as IR camouflage materials, potentially permitting the concealment of human bodies from IR detection not only at room temperature but also at extremely low and high temperatures. Furthermore, subjecting the MC11 film to a thermal shock of Δ396 °C for 30 cycles and mechanical bending (6 mm curvature) for 300 cycles did not hamper its thermal camouflage performance (Fig. S17).
The reduction in radiation temperature is a key parameter for evaluating thermal camouflage capability of a material. Notably, the MC11-M Janus film exhibited a significantly higher reduction in the radiation temperature against background temperatures of 100–300 °C than that of several other materials (Fig. 4f, g). This reduction is considerably higher than that of competing nanomaterials including CNTs and graphene, and comparable to that of a Cu metal film, which is deemed the ideal candidate for IR shielding applications because of its exceptionally high electrical conductivity and significantly low IR emissivity.
3.5 Infrared Detection
A system featuring a 15-µm-thick MC11-C film placed between two Cu electrodes as the IR radiation detector was constructed to assess its IR detection capability (Fig. 5a). The change in resistance caused by IR radiation is expressed as (R − R0)/R0 (%), where R0 is the sample resistance before the IR lamp is switched on, and R is the maximum resistance of the sample after IR illumination. The detector sensitivity was quantified as percentage (%) increase in resistance under IR illumination. The Al–Ti3C2Tx MXene, MC14, MC12, and MC11 Janus films with both MXene and CNT sides were exposed to 250 W IR radiation (Fig. S18). The CNT and MC-C Janus films exhibited a noteworthy increase in resistance (44%) owing to the excellent IR absorption of the CNT, whereas Al–Ti3C2Tx MXene and MC-M films showed a minimal increase in resistance (3.6%) owing to the strong IR-reflecting attributes of the MXene. Furthermore, the increase in resistance of the MC11-blend film fabricated by uniformly mixing the MXene and CNTs was lower (10%) that that of the MC11-C Janus film, but higher than that of the Al–Ti3C2Tx MXene film under 6 s on–off cycling (3 s-on, and 3 s-off) (Fig. 5b). The cyclic behavior of the resistance—increase and decrease in the presence and absence of IR illumination, respectively—aligns with the tendencies of a previously reported CNT-based IR detector [85].
The relationship between temperature-increase and change in resistance for the different samples (Fig. 5c) revealed a direct correlation between the two parameters under IR illumination. Notably, the MC11-Blend film showed a smaller change in resistance (10%) than that of the MC11-C Janus film. Uniform mixing helped numerous MXene flakes covering the surface of CNT, thereby increasing the reflection of IR radiation, and consequently reducing the detection sensitivity. The observed increase in resistance can be attributed to the increase in temperature and the presence of photoexcited electrons and holes [86]. Additionally, subjecting the MC11 film to a thermal shock of Δ396 °C for 30 cycles and mechanical bending (6 mm curvature) for 300 cycles barely affected the IR-detecting capability of the MC11-C film (Fig. 5d).
The MC11-C Janus film was illuminated with IR radiation at varying intensities (100, 150, and 250 W) to analyze the effect of the IR intensity on its sensitivity. The acquired IR images (Fig. 5e) and temperature–time spectra (Fig. S19) indicate that under 250 W IR light, the sample exhibited the highest increase in temperature (59 °C), which decreased with decreasing light intensity, c.a., 45 °C for 150 W and 40 °C for 100 W. This increase in temperature can be attributed to the IR-absorbing ability of the sample, which led to an increase in resistance. The thermal energy of the atoms increases with increasing temperature, leading to more frequent collisions between electrons and lattice defects, which impedes electron flow and thereby increases resistance [86]. Additionally, a direct correlation between the increase in temperature and resistance revealed light-intensity-dependent behavior of the change in temperature and resistance (Fig. 5f).
4 Conclusion
Electrically-conductive, flexible, robust, and multifunctional MXene/CNT Janus films were fabricated by vacuum-assisted filtration. Incorporating highly crystalline Al–Ti3C2Tx MXene on the ozone-treated CNT film facilitated the formation of a Janus film with strong interfacial assembly via hydrogen bonds. The MXene/CNT Janus film exhibited high electrical conductivity as well as excellent tensile strength and mechanical durability, even in harsh environments of extremely high and low temperatures. Consequently, the fabricated Janus film showed an efficient and stable EMI-shielding effectiveness of 72 dB at 15 μm in the X-band, outstanding thermal camouflage performance over a wide temperature range (− 1 to 300 °C) owing to its considerably low IR emissivity (0.09), and high sensitivity (44% increase in resistance under 250 W IR light) towards IR radiation exposure revealing excellent IR detection capability. Therefore, the MXene/CNT Janus film—characterized by an excellent EMI SE value, low IR emissivity, and notable IR detection ability, which were retained in harsh environments—holds strong promise for electronics, military, and aerospace applications.
References
F. Shahzad, M. Alhabeb, C.B. Hatter, B. Anasori, S. Man Hong et al., Electromagnetic interference shielding with 2D transition metal carbides (MXenes). Science 353, 1137–1140 (2016). https://doi.org/10.1126/science.aag2421
A. Iqbal, F. Shahzad, K. Hantanasirisakul, M.K. Kim, J. Kwon et al., Anomalous absorption of electromagnetic waves by 2D transition metal carbonitride Ti3CNT x (MXene). Science 369, 446–450 (2020). https://doi.org/10.1126/science.aba7977
M. Han, C.E. Shuck, R. Rakhmanov, D. Parchment, B. Anasori et al., Beyond Ti3C2Tx: MXenes for electromagnetic interference shielding. ACS Nano 14, 5008–5016 (2020). https://doi.org/10.1021/acsnano.0c01312
X. Fan, S. Li, W. Zhang, W. Xu, Recent progress in two-dimensional nanomaterials of graphene and MXenes for thermal camouflage. Ceram. Int. 49, 5559–5572 (2023). https://doi.org/10.1016/j.ceramint.2022.12.034
K. Shafique, B.A. Khawaja, F. Sabir, S. Qazi, M. Mustaqim, Internet of Things (IoT) for next-generation smart systems: a review of current challenges, future trends and prospects for emerging 5G-IoT scenarios. IEEE Access 8, 23022–23040 (2020). https://doi.org/10.1109/ACCESS.2020.2970118
K.Y. Fang, Y.J. Wang, Y.C. Zhao, F. Fang, Infrared stealth nanofibrous composites with thermal adaptability and mechanical flexibility. Compos. Sci. Technol. 201, 108483 (2021). https://doi.org/10.1016/j.compscitech.2020.108483
X. Ni, S. Yu, X. Su, F. Chen, Detection spectrum optimization of stealth aircraft targets from a space-based infrared platform. Opt. Quantum Electron. 54, 151 (2022). https://doi.org/10.1007/s11082-021-03451-4
Z.H. Zeng, N. Wu, J.J. Wei, Y.F. Yang, T.T. Wu et al., Porous and ultra-flexible crosslinked MXene/polyimide composites for multifunctional electromagnetic interference shielding. Nano-Micro Lett. 14, 59 (2022). https://doi.org/10.1007/s40820-022-00800-0
D.D.L. Chung, Electromagnetic interference shielding effectiveness of carbon materials. Carbon 39, 279–285 (2001). https://doi.org/10.1016/S0008-6223(00)00184-6
N.C. Das, Y. Liu, K. Yang, W. Peng, S. Maiti et al., Single-walled carbon nanotube/poly(methyl methacrylate) composites for electromagnetic interference shielding. Polym. Eng. Sci. 49, 1627–1634 (2009). https://doi.org/10.1002/pen.21384
M.H. Al-Saleh, W.H. Saadeh, U. Sundararaj, EMI shielding effectiveness of carbon based nanostructured polymeric materials: a comparative study. Carbon 60, 146–156 (2013). https://doi.org/10.1016/j.carbon.2013.04.008
H.-B. Zhang, Q. Yan, W.-G. Zheng, Z. He, Z.-Z. Yu, Tough graphene–polymer microcellular foams for electromagnetic interference shielding. ACS Appl. Mater. Interfaces 3, 918–924 (2011). https://doi.org/10.1021/am200021v
J.-M. Thomassin, C. Jérôme, T. Pardoen, C. Bailly, I. Huynen et al., Polymer/carbon based composites as electromagnetic interference (EMI) shielding materials. Mater. Sci. Eng. R. Rep. 74, 211–232 (2013). https://doi.org/10.1016/j.mser.2013.06.001
H. Liu, S. Wu, C. You, N. Tian, Y. Li et al., Recent progress in morphological engineering of carbon materials for electromagnetic interference shielding. Carbon 172, 569–596 (2021). https://doi.org/10.1016/j.carbon.2020.10.067
P. Kumar, F. Shahzad, S. Yu, S.M. Hong, Y.-H. Kim et al., Large-area reduced graphene oxide thin film with excellent thermal conductivity and electromagnetic interference shielding effectiveness. Carbon 94, 494–500 (2015). https://doi.org/10.1016/j.carbon.2015.07.032
S.H. Lee, S. Yu, F. Shahzad, W.N. Kim, C. Park et al., Density-tunable lightweight polymer composites with dual-functional ability of efficient EMI shielding and heat dissipation. Nanoscale 9, 13432–13440 (2017). https://doi.org/10.1039/C7NR02618H
R. Kumar, S. Sahoo, E. Joanni, R.K. Singh, W.K. Tan et al., Recent progress on carbon-based composite materials for microwave electromagnetic interference shielding. Carbon 177, 304–331 (2021). https://doi.org/10.1016/j.carbon.2021.02.091
N. Wu, Q. Hu, R. Wei, X. Mai, N. Naik et al., Review on the electromagnetic interference shielding properties of carbon based materials and their novel composites: recent progress, challenges and prospects. Carbon 176, 88–105 (2021). https://doi.org/10.1016/j.carbon.2021.01.124
P. Kumar, S. Yu, F. Shahzad, S.M. Hong, Y.-H. Kim et al., Ultrahigh electrically and thermally conductive self-aligned graphene/polymer composites using large-area reduced graphene oxides. Carbon 101, 120–128 (2016). https://doi.org/10.1016/j.carbon.2016.01.088
F. Shahzad, P. Kumar, S. Yu, S. Lee, Y.-H. Kim et al., Sulfur-doped graphene laminates for EMI shielding applications. J. Mater. Chem. C 3, 9802–9810 (2015). https://doi.org/10.1039/c5tc02166a
F. Shahzad, P. Kumar, Y.-H. Kim, S.M. Hong, C.M. Koo, Biomass-derived thermally annealed interconnected sulfur-doped graphene as a shield against electromagnetic interference. ACS Appl. Mater. Interfaces 8, 9361–9369 (2016). https://doi.org/10.1021/acsami.6b00418
S.H. Lee, J.Y. Kim, C.M. Koo, W.N. Kim, Effects of processing methods on the electrical conductivity, electromagnetic parameters, and EMI shielding effectiveness of polypropylene/nickel-coated carbon fiber composites. Macromol. Res. 25, 936–943 (2017). https://doi.org/10.1007/s13233-017-5113-x
S.-U. Chae, S. Yi, J. Yoon, J.C. Hyun, S. Doo et al., Highly defective Ti3CNTx-MXene-based fiber membrane anode for lithium metal batteries. Energy Storage Mater. 52, 76–84 (2022). https://doi.org/10.1016/j.ensm.2022.07.025
Z. Deng, L. Li, P. Tang, C. Jiao, Z.Z. Yu et al., Controllable surface-grafted MXene inks for electromagnetic wave modulation and infrared anti-counterfeiting applications. ACS Nano 16, 16976–16986 (2022). https://doi.org/10.1021/acsnano.2c07084
Y. Li, H. Shao, Z. Lin, J. Lu, L. Liu et al., A general Lewis acidic etching route for preparing MXenes with enhanced electrochemical performance in non-aqueous electrolyte. Nat. Mater. 19, 894–899 (2020). https://doi.org/10.1038/s41563-020-0657-0
V. Kamysbayev, A.S. Filatov, H. Hu, X. Rui, F. Lagunas et al., Covalent surface modifications and superconductivity of two-dimensional metal carbide MXenes. Science 369, 979–983 (2020). https://doi.org/10.1126/science.aba8311
A. VahidMohammadi, J. Rosen, Y. Gogotsi, The world of two-dimensional carbides and nitrides (MXenes). Science 372, eabf1581 (2021). https://doi.org/10.1126/science.abf1581
M.R. Lukatskaya, S. Kota, Z. Lin, M.-Q. Zhao, N. Shpigel et al., Ultra-high-rate pseudocapacitive energy storage in two-dimensional transition metal carbides. Nat. Energy 2, 17105 (2017). https://doi.org/10.1038/nenergy.2017.105
C. Zhang, L. McKeon, M.P. Kremer, S.-H. Park, O. Ronan et al., Additive-free MXene inks and direct printing of micro-supercapacitors. Nat. Commun. 10, 1795 (2019). https://doi.org/10.1038/s41467-019-09398-1
K. Hantanasirisakul, Y. Gogotsi, Electronic and optical properties of 2D transition metal carbides and nitrides (MXenes). Adv. Mater. 30, e1804779 (2018). https://doi.org/10.1002/adma.201804779
S.J. Kim, H.-J. Koh, C.E. Ren, O. Kwon, K. Maleski et al., Metallic Ti3C2Tx MXene gas sensors with ultrahigh signal-to-noise ratio. ACS Nano 12, 986–993 (2018). https://doi.org/10.1021/acsnano.7b07460
T.H. Park, S. Yu, M. Koo, H. Kim, E.H. Kim et al., Shape-adaptable 2D titanium carbide (MXene) heater. ACS Nano 13, 6835–6844 (2019). https://doi.org/10.1021/acsnano.9b01602
X. Xie, C. Chen, N. Zhang, Z.-R. Tang, J. Jiang et al., Microstructure and surface control of MXene films for water purification. Nat. Sustain. 2, 856–862 (2019). https://doi.org/10.1038/s41893-019-0373-4
T. Yun, H. Kim, A. Iqbal, Y.S. Cho, G.S. Lee et al., Electromagnetic shielding of monolayer MXene assemblies. Adv. Mater. 32, e1906769 (2020). https://doi.org/10.1002/adma.201906769
M. Malaki, A. Maleki, R.S. Varma, MXenes and ultrasonication. J. Mater. Chem. A 7, 10843–10857 (2019). https://doi.org/10.1039/c9ta01850f
A. Iqbal, H. Kim, J.M. Oh, J. Chae, J. Kim et al., Effect of substitutional oxygen on properties of Ti3 C2Tx MXene produced using recycled TiO2 source. Small Methods 7, e2201715 (2023). https://doi.org/10.1002/smtd.202201715
A. Iqbal, J. Hong, T.Y. Ko, C.M. Koo, Improving oxidation stability of 2D MXenes: synthesis, storage media, and conditions. Nano Converg. 8, 9 (2021). https://doi.org/10.1186/s40580-021-00259-6
S. Doo, A. Chae, D. Kim, T. Oh, T.Y. Ko et al., Mechanism and kinetics of oxidation reaction of aqueous Ti3C2Tx suspensions at different pHs and temperatures. ACS Appl. Mater. Interfaces 13, 22855–22865 (2021). https://doi.org/10.1021/acsami.1c04663
X. Sang, Y. Xie, M.W. Lin, M. Alhabeb, K.L. Van Aken et al., Atomic defects in monolayer titanium carbide (Ti3C2Tx) MXene. ACS Nano 10, 9193–9200 (2016). https://doi.org/10.1021/acsnano.6b05240
T.S. Mathis, K. Maleski, A. Goad, A. Sarycheva, M. Anayee et al., Modified MAX phase synthesis for environmentally stable and highly conductive Ti3C2 MXene. ACS Nano 15, 6420–6429 (2021). https://doi.org/10.1021/acsnano.0c08357
A. Iqbal, P. Sambyal, J. Kwon, M. Han, J. Hong et al., Enhanced absorption of electromagnetic waves in Ti3C2Tx MXene films with segregated polymer inclusions. Compos. Sci. Technol. 213, 108878 (2021). https://doi.org/10.1016/j.compscitech.2021.108878
X. Wu, B. Han, H.-B. Zhang, X. Xie, T. Tu et al., Compressible, durable and conductive polydimethylsiloxane-coated MXene foams for high-performance electromagnetic interference shielding. Chem. Eng. J. 381, 122622 (2020). https://doi.org/10.1016/j.cej.2019.122622
C.-Z. Qi, X. Wu, J. Liu, X.-J. Luo, H.-B. Zhang et al., Highly conductive calcium ion-reinforced MXene/sodium alginate aerogel meshes by direct ink writing for electromagnetic interference shielding and Joule heating. J. Mater. Sci. Technol. 135, 213–220 (2023). https://doi.org/10.1016/j.jmst.2022.06.046
L.-X. Liu, W. Chen, H.-B. Zhang, L. Ye, Z. Wang et al., Super-tough and environmentally stable aramid. Nanofiber@MXene coaxial fibers with outstanding electromagnetic interference shielding efficiency. Nano-Micro Lett. 14, 111 (2022). https://doi.org/10.1007/s40820-022-00853-1
G.-M. Weng, J. Li, M. Alhabeb, C. Karpovich, H. Wang et al., Layer-by-layer assembly of cross-functional semi-transparent MXene-carbon nanotubes composite films for next-generation electromagnetic interference shielding. Adv. Funct. Mater. 28, 1803360 (2018). https://doi.org/10.1002/adfm.201803360
Y. Zhang, Q. Gao, S. Zhang, X. Fan, J. Qin et al., rGO/MXene sandwich-structured film at spunlace non-woven fabric substrate: application to EMI shielding and electrical heating. J. Colloid Interface Sci. 614, 194–204 (2022). https://doi.org/10.1016/j.jcis.2022.01.030
L. Li, S. Zhao, X.-J. Luo, H.-B. Zhang, Z.-Z. Yu, Smart MXene-Based Janus films with multi-responsive actuation capability and high electromagnetic interference shielding performances. Carbon 175, 594–602 (2021). https://doi.org/10.1016/j.carbon.2020.10.090
J. Liu, Z. Liu, H.-B. Zhang, W. Chen, Z. Zhao et al., Ultrastrong and highly conductive MXene-based films for high-performance electromagnetic interference shielding. Adv. Electron. Mater. 6, 1901094 (2020). https://doi.org/10.1002/aelm.201901094
K. Chen, M. Liu, Y. Shi, H. Wang, L. Fu et al., Multi-hierarchical flexible composites towards superior fire safety and electromagnetic interference shielding. Nano Res. 15, 9531–9543 (2022). https://doi.org/10.1007/s12274-022-4883-6
L. Liu, Z. Ma, M. Zhu, L. Liu, J. Dai et al., Superhydrophobic self-extinguishing cotton fabrics for electromagnetic interference shielding and human motion detection. J. Mater. Sci. Technol. 132, 59–68 (2023). https://doi.org/10.1016/j.jmst.2022.05.036
T. Oh, S. Lee, H. Kim, T.Y. Ko, S.J. Kim et al., Fast and high-yield anhydrous synthesis of Ti3C2Tx MXene with high electrical conductivity and exceptional mechanical strength. Small 18, 2270246 (2022). https://doi.org/10.1002/smll.202270246
W.-T. Cao, F.-F. Chen, Y.-J. Zhu, Y.-G. Zhang, Y.-Y. Jiang et al., Binary strengthening and toughening of MXene/cellulose nanofiber composite paper with nacre-inspired structure and superior electromagnetic interference shielding properties. ACS Nano 12, 4583–4593 (2018). https://doi.org/10.1021/acsnano.8b00997
Y. Shi, C. Liu, Z. Duan, B. Yu, M. Liu et al., Interface engineering of MXene towards super-tough and strong polymer nanocomposites with high ductility and excellent fire safety. Chem. Eng. J. 399, 125829 (2020). https://doi.org/10.1016/j.cej.2020.125829
F. Xie, F. Jia, L. Zhuo, Z. Lu, L. Si et al., Ultrathin MXene/aramid nanofiber composite paper with excellent mechanical properties for efficient electromagnetic interference shielding. Nanoscale 11, 23382–23391 (2019). https://doi.org/10.1039/c9nr07331k
Y. Liu, Y. Wang, N. Wu, M. Han, W. Liu et al., Diverse structural design strategies of MXene-based macrostructure for high-performance electromagnetic interference shielding. Nano-Micro Lett. 15, 240 (2023). https://doi.org/10.1007/s40820-023-01203-5
T. Tang, S. Wang, Y. Jiang, Z. Xu, Y. Chen et al., Flexible and flame-retarding phosphorylated MXene/polypropylene composites for efficient electromagnetic interference shielding. J. Mater. Sci. Technol. 111, 66–75 (2022). https://doi.org/10.1016/j.jmst.2021.08.091
H. Wang, K. Chen, Y. Shi, Y. Zhu, S. Jiang et al., Flame retardant and multifunctional BC/MXene/MSiCnw/FRTPU aerogel composites with superior electromagnetic interference shielding via “Consolidating” method. Chem. Eng. J. 474, 145904 (2023). https://doi.org/10.1016/j.cej.2023.145904
T. Okada, R. Ishige, S. Ando, Analysis of thermal radiation properties of polyimide and polymeric materials based on ATR-IR spectroscopy. J. Photopolym. Sci. Technol. 29, 251–254 (2016). https://doi.org/10.2494/photopolymer.29.251
A. Iqbal, T. Hassan, Z. Gao, F. Shahzad, C.M. Koo, MXene-incorporated 1D/2D nano-carbons for electromagnetic shielding: a review. Carbon 203, 542–560 (2023). https://doi.org/10.1016/j.carbon.2022.11.104
X. Huang, J. Huang, G. Zhou, Y. Wei, P. Wu et al., Gelation-assisted assembly of large-area, highly aligned, and environmentally stable MXene films with an excellent trade-off between mechanical and electrical properties. Small 18, e2200829 (2022). https://doi.org/10.1002/smll.202200829
R. Cheng, B. Wang, J. Zeng, J. Li, J. Xu et al., Janus-inspired flexible cellulose nanofiber-assisted MXene/Silver nanowire papers with fascinating mechanical properties for efficient electromagnetic interference shielding. Carbon 202, 314–324 (2023). https://doi.org/10.1016/j.carbon.2022.10.079
C. Ma, W.-T. Cao, W. Zhang, M.-G. Ma, W.-M. Sun et al., Wearable, ultrathin and transparent bacterial celluloses/MXene film with Janus structure and excellent mechanical property for electromagnetic interference shielding. Chem. Eng. J. 403, 126438 (2021). https://doi.org/10.1016/j.cej.2020.126438
M. Alhabeb, K. Maleski, B. Anasori, P. Lelyukh, L. Clark et al., Guidelines for synthesis and processing of two-dimensional titanium carbide (Ti3C2Tx MXene). Chem. Mater. 29, 7633–7644 (2017). https://doi.org/10.1021/acs.chemmater.7b02847
H. Song, S.-Y. Jeon, Y. Jeong, Fabrication of a coaxial high performance fiber lithium-ion battery supported by a cotton yarn electrolyte reservoir. Carbon 147, 441–450 (2019). https://doi.org/10.1016/j.carbon.2019.02.081
J. Song, S. Kim, S. Yoon, D. Cho, Y. Jeong, Enhanced spinnability of carbon nanotube fibers by surfactant addition. Fibres Polym. 15, 762–766 (2014). https://doi.org/10.1007/s12221-014-0762-2
S. Ji, W.H. Tanveer, W. Yu, S. Kang, G.Y. Cho et al., Surface engineering of nanoporous substrate for solid oxide fuel cells with atomic layer-deposited electrolyte. Beilstein J. Nanotechnol. 6, 1805–1810 (2015). https://doi.org/10.3762/bjnano.6.184
S.-H. Lee, J. Park, H.-R. Kim, J. Lee, K.-H. Lee, Synthesis of high-quality carbon nanotube fibers by controlling the effects of sulfur on the catalyst agglomeration during the direct spinning process. RSC Adv. 5, 41894–41900 (2015). https://doi.org/10.1039/C5RA04691B
J. Halim, K.M. Cook, M. Naguib, P. Eklund, Y. Gogotsi et al., X-ray photoelectron spectroscopy of select multi-layered transition metal carbides (MXenes). Appl. Surf. Sci. 362, 406–417 (2016). https://doi.org/10.1016/j.apsusc.2015.11.089
A. Abnavi, M. Faramarzi, Z. Sanaee, S. Ghasemi, SnO2 nanowires on carbon nanotube film as a high performance anode material for flexible Li-ion batteries. J. Nanostruct. 8, 288–293 (2018). https://doi.org/10.22052/JNS.2018.03.008
M.M. Ngoma, M. Mathaba, K. Moothi, Effect of carbon nanotubes loading and pressure on the performance of a polyethersulfone (PES)/carbon nanotubes (CNT) membrane. Sci. Rep. 11, 23805 (2021). https://doi.org/10.1038/s41598-021-03042-z
S. Iijima, Helical microtubules of graphitic carbon. Nature 354, 56–58 (1991). https://doi.org/10.1038/354056a0
S.-J. Park, S.-J. Park, Effect of ozone-treated single-walled carbon nanotubes on interfacial properties and fracture toughness of carbon fiber-reinforced epoxy composites. Compos. Part A Appl. Sci. Manuf. 137, 105937 (2020). https://doi.org/10.1016/j.compositesa.2020.105937
J. Luo, Y. Liu, H. Wei, B. Wang, K.-H. Wu et al., A green and economical vapor-assisted ozone treatment process for surface functionalization of carbon nanotubes. Green Chem. 19, 1052–1062 (2017). https://doi.org/10.1039/C6GC02806C
J. Chen, X. Yuan, F. Lyu, Q. Zhong, H. Hu et al., Integrating MXene nanosheets with cobalt-tipped carbon nanotubes for an efficient oxygen reduction reaction. J. Mater. Chem. A 7, 1281–1286 (2019). https://doi.org/10.1039/c8ta10574j
Q. Xue, H. Zhang, M. Zhu, Z. Pei, H. Li et al., Photoluminescent Ti3 C2 MXene quantum dots for multicolor cellular imaging. Adv. Mater. 29, 1604847 (2017). https://doi.org/10.1002/adma.201604847
X. Li, C. Zeng, G. Fan, Magnetic RuCo nanoparticles supported on two-dimensional titanium carbide as highly active catalysts for the hydrolysis of ammonia borane. Int. J. Hydrog. Energy 40, 9217–9224 (2015). https://doi.org/10.1016/j.ijhydene.2015.05.168
Y. Li, X. Zhou, J. Wang, Q. Deng, M. Li et al., Facile preparation of in situ coated Ti3C2Tx/Ni0.5Zn0.5Fe2O4 composites and their electromagnetic performance. RSC Adv. 7, 24698–24708 (2017). https://doi.org/10.1039/C7RA03402D
X. He, S. Li, R. Shen, Y. Ma, L. Zhang et al., A high-performance waterborne polymeric composite coating with long-term anti-corrosive property based on phosphorylation of chitosan-functionalized Ti3C2Tx MXene. Adv. Compos. Hybrid Mater. 5, 1699–1711 (2022). https://doi.org/10.1007/s42114-021-00392-0
S. Wan, X. Li, Y. Chen, N. Liu, Y. Du et al., High-strength scalable MXene films through bridging-induced densification. Science 374, 96–99 (2021). https://doi.org/10.1126/science.abg2026
J. Hong, J. Kwon, D. Im, J. Ko, C.Y. Nam et al., Best practices for correlating electrical conductivity with broadband EMI shielding in binary filler-based conducting polymer composites. Chem. Eng. J. 455, 140528 (2023). https://doi.org/10.1016/j.cej.2022.140528
X. Xu, The nature of heat and the absolute zero temperature. Int. J. Fundam. Phys. Sci. 10, 35–39 (2020). https://doi.org/10.14331/ijfps.2020.330140
C. Wen, B. Zhao, Y. Liu, C. Xu, Y. Wu et al., Flexible MXene-based composite films for multi-spectra defense in radar, infrared and visible light bands. Adv. Funct. Mater. 33, 2214223 (2023). https://doi.org/10.1002/adfm.202214223
M. Han, D. Zhang, A. Singh, T. Hryhorchuk, C. Eugene Shuck et al., Versatility of infrared properties of MXenes. Mater. Today 64, 31–39 (2023). https://doi.org/10.1016/j.mattod.2023.02.024
Y. Li, C. Xiong, H. Huang, X. Peng, D. Mei et al., 2D Ti3C2Tx MXenes: visible black but infrared white materials. Adv. Mater. 33, e2103054 (2021). https://doi.org/10.1002/adma.202103054
R. Afrin, N.A. Shah, M. Abbas, M. Amin, A.S. Bhatti, Design and analysis of functional multiwalled carbon nanotubes for infrared sensors. Sens. Actuators A Phys. 203, 142–148 (2013). https://doi.org/10.1016/j.sna.2013.08.018
B. Pradhan, R.R. Kohlmeyer, K. Setyowati, H.A. Owen, J. Chen, Advanced carbon nanotube/polymer composite infrared sensors. Carbon 47, 1686–1692 (2009). https://doi.org/10.1016/j.carbon.2009.02.021
Acknowledgements
This study was supported by grants from the Basic Science Research Program (2021M3H4A1A03047327 and 2022R1A2C3006227) through the National Research Foundation of Korea, funded by the Ministry of Science, ICT, and Future Planning; the Fundamental R&D Program for Core Technology of Materials and the Industrial Strategic Technology Development Program (20020855), funded by the Ministry of Trade, Industry, and Energy, Republic of Korea; and the National Research Council of Science & Technology (NST), funded by the Korean Government (MSIT) (CRC22031-000). Furthermore, this study was partially supported by POSCO and Hyundai Mobis, a start-up fund (S-2022-0096-000) and the Postdoctoral Research Program of Sungkyunkwan University (2022).
Author information
Authors and Affiliations
Contributions
T.H, Y.J, and C.M.K. conceived the idea. T.H., B.K.Y., J.Y.J., designed and performed the experiments. T.H., B.K.Y., A.I., S.M.N., H.K., S.J., N.H., U.Z., S.Y.C., S.J., J.M.O., S.P., N.C., J.K., Y.J, and C.M.K. discussed the results and analyzed the data. T.H, and C.M.K. wrote the manuscript, with contributions from all the authors. Y.J. and C.M.K. supervised the study.
Corresponding authors
Ethics declarations
Conflict of interest
The authors declare no interest conflict. They have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Supplementary Information
Below is the link to the electronic supplementary material.
Supplementary file1 (MP4 6513 KB)
Supplementary file2 (MP4 5821 KB)
Supplementary file3 (MP4 8336 KB)
Supplementary file4 (MP4 8507 KB)
Supplementary file5 (MP4 9303 KB)
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hassan, T., Iqbal, A., Yoo, B. et al. Multifunctional MXene/Carbon Nanotube Janus Film for Electromagnetic Shielding and Infrared Shielding/Detection in Harsh Environments. Nano-Micro Lett. 16, 216 (2024). https://doi.org/10.1007/s40820-024-01431-3