Hot Compression Behavior of Mg–Gd–Y–Zn–Zr Alloy Containing LPSO with Different Morphologies

  • Published:
Acta Metallurgica Sinica (English Letters) Aims and scope

Abstract

In this study, hot compression behavior of as-homogenized Mg-9Gd-4Y-2Zn-0.5Zr alloys containing long period ordered (LPSO) phases with different initial morphologies was investigated under a strain rate of 0.01 s−1 at 450 °C. The microstructure, texture evolution and dynamic recrystallization (DRX) mechanism under different strains (0.1, 0.3, 0.5, 0.7, and 1.4) were studied. Under compression conditions, the block-shape phase and deformed α-Mg matrix were regularly arranged vertically in the compression direction (CD). The particle phase (Mg5RE) and amount of kink bands were produced. The degree of kink increased initially and decreased significantly when the deformation strain reached 1.4. Three DRX mechanisms were produced during the compression process: (i) The block LPSO, Mg5RE and Zr–Zn phase activated DRX through the particle stimulated nucleation (PSN) mechanism. (ii) Several DRX activated on the serrated grain boundary between the two parent grains through discontinuous DRX (DDRX) mechanism. (iii) A large number of kink bands and larger spacing of lamellar LPSO increased the nucleation of DRX through continuous DRX (CDRX) mechanism. The combination of different recrystallization mechanisms has evident effects on grain refinement. DRX increased as compression proceeds, and the texture was gradually weakened.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13
Fig. 14
Fig. 15
Fig. 16
Fig. 17
Fig. 18
Fig. 19
Fig. 20
Fig. 21

Similar content being viewed by others

References

  1. B.L. Mordike, T. Ebert, Mater. Sci. Eng. A 302, 37 (2001)

    Article  Google Scholar 

  2. T.M. Pollock, Science 328, 986 (2010)

    Article  CAS  Google Scholar 

  3. Y.X. Zhang, Z. Wang, S.C. Li, X. Zhao, Z.M. Zhang, Y.J. Wu, X.W. Ren, F.F. Yan, B.B. Dong, Acta Metall Sin. -Engl. Lett. 36, 839 (2023)

    Article  CAS  Google Scholar 

  4. T. Chen, Z.Y. Chen, J.B. Shao, R.K. Wang, L.H. Mao, C.M. Liu, Mater. Des. 152, 1 (2018)

    Article  Google Scholar 

  5. A. Jana, M. Das, V.K. Balla, J. Alloy. Compd. 821, 153462 (2020)

    Article  CAS  Google Scholar 

  6. Y.H. Luo, Y.J. Wu, Q.C. Deng, Y. Zhang, J. Chen, L.M. Peng, J. Alloy. Compd. 820, 153405 (2020)

    Article  CAS  Google Scholar 

  7. Y. Kawamura, K. Hayashi, A. Inoue, T. Masumoto, Mater. Trans. 42, 1172 (2001)

    Article  CAS  Google Scholar 

  8. T. Homma, N. Kunito, S. Kamado, Scr. Mater. 61, 644 (2009)

    Article  CAS  Google Scholar 

  9. H. Liu, J. Ju, X.W. Yang, J.L. Yan, D. Song, J.H. Jiang, A. Ma, J. Alloy. Compd. 704, 509 (2017)

    Article  CAS  Google Scholar 

  10. Y.M. Zhu, A.J. Morton, J.F. Nie, Acta Mater. 60, 6562 (2012)

    Article  CAS  Google Scholar 

  11. M. Jiang, S. Zhang, Y.D. Bi, H.X. Li, Y.P. Ren, G.W. Qin, Intermetallics 57, 127 (2015)

    Article  CAS  Google Scholar 

  12. H.X. Liao, J. Kim, T. Lee, J.F. Song, J. Peng, B. Jiang, F.S. Pan, J. Magnes. Alloy. 8, 1120 (2020)

    Article  CAS  Google Scholar 

  13. D.J. Li, X.Q. Zeng, J. Dong, C.Q. Zhai, W.J. Ding, J. Alloy Compd. 468, 164 (2009)

    Article  CAS  Google Scholar 

  14. W.T. Sun, X.G. Qiao, M.Y. Zheng, C. Xu, N. Gao, M.J. Starink, Mater. Des. 135, 366 (2017)

    Article  CAS  Google Scholar 

  15. Z. Ma, G. Li, Z. Su, G. Wei, Y. Huang, N. Hort, J. Mater. Res. Technol. 19, 3536 (2022)

    Article  CAS  Google Scholar 

  16. X. Pan, L. Wang, L. Xue, M. Sabbaghian, P. Lu, W. Wu, J. Mater. Res. Technol. 19, 1627 (2022)

    Article  CAS  Google Scholar 

  17. H.L. Peng, J. Chen, Q. Yang, Q.X. Zhao, J. Mater. Res. Technol. 21, 1724 (2022)

    Article  Google Scholar 

  18. B.J. Lv, J. Peng, L.L. Zhu, Y.J. Wang, A.T. Tang, Mater. Sci. Eng. A 599, 150 (2014)

    Article  CAS  Google Scholar 

  19. X.J. Zhou, X.D. Yang, B.L. Liu, L.W. Lu, J. Mater. Eng. Perform. 32, 2041 (2023)

    Article  Google Scholar 

  20. H. Esmaeilpour, A. Zarei-Hanzaki, N. Eftekhari, H.R. Abedi, M.R.G. Ferdowsi, Mater. Sci. Eng. A 778, 139021 (2020)

    Article  CAS  Google Scholar 

  21. J. Zheng, Z. Chen, Z. Yan, Z. Zhang, Y. Xue, Mater. Sci. Eng. A 828, 142103 (2021)

    Article  CAS  Google Scholar 

  22. W. Xu, C. Su, X. Chen, X. Han, G. Zhang, F. Pan, Mater. Sci. Eng. A 873, 145006 (2023)

    Article  CAS  Google Scholar 

  23. M. Meng, H.L. Zhang, Z. Gao, G.X. Lei, J.M. Yu, Effect of aging treatment on the precipitation transformation and age hardening of Mg-Gd-Y-Zn-Zr alloy. J. Magnes. Alloy. (2022). https://doi.org/10.1016/j.jma.2022.02.012

    Article  Google Scholar 

  24. M. Meng, G.X. Lei, H.L. Zhang, X.H. Zhang, J.M. Yu, J. Mater Res Technol. 23, 5783 (2023)

    Article  CAS  Google Scholar 

  25. C. Xu, M.Y. Zheng, K. Wu, E.D. Wang, G.H. Fan, S.W. Xu, S. Kamado, X.D. Liu, G.J. Wang, X.Y. Lv, Mater. Sci. Eng. A 559, 615 (2013)

    Article  CAS  Google Scholar 

  26. X. Wu, F.S. Pan, R.J. Cheng, S.Q. Luo, Mater. Sci. Eng. A 726, 64 (2018)

    Article  CAS  Google Scholar 

  27. Y.Q. Ning, T. Wang, M.W. Fu, M.Z. Li, L. Wang, C.D. Zhao, Mater. Sci. Eng. A 642, 187 (2015)

    Article  CAS  Google Scholar 

  28. C.Y. Sun, L. Wan, D.J. Yang, Y. Cai, Z.H. Guo, Mater. Sci. Eng. A 687, 113 (2017)

    Article  Google Scholar 

  29. J.B. Shao, Z.Y. Chen, T. Chen, R.K. Wang, Y.L. Liu, C.M. Liu, Mater. Sci. Eng. A 731, 479 (2018)

    Article  CAS  Google Scholar 

  30. C. Zheng, S.F. Chen, M. Cheng, S.H. Zhang, Y.J. Li, Y.S. Yang, Controlling dynamic recrystallization via modified LPSO phase morphology and distribution in Mg-Gd-Y-Zn-Zr alloy. J. Magnes. Alloy. (2023). https://doi.org/10.1016/j.jma.2023.01.006

    Article  Google Scholar 

  31. N. Ding, W.B. Du, X.M. Zhu, L.S. Dou, Y.F. Wang, X.D. Li, K. Liu, S.B. Li, Mater. Sci. Eng. A 864, 144590 (2023)

    Article  CAS  Google Scholar 

  32. B.B. Dong, X. Che, Z.M. Zhang, J.M. Yu, M. Meng, J. Alloy. Compd. 853, 157066 (2021)

    Article  CAS  Google Scholar 

  33. B.B. Dong, Z.M. Zhang, J.M. Yu, X. Che, M. Meng, J.L. Zhang, J. Alloy. Compd. 823, 153776 (2020)

    Article  CAS  Google Scholar 

  34. D.X. Zhang, Z. Tan, Q.H. Huo, Z.Y. Xiao, Z.W. Fang, X.Y. Yang, Mater. Sci. Eng. A 715, 389 (2018)

    Article  CAS  Google Scholar 

  35. X.H. Shao, Z.Q. Yang, X.L. Ma, Acta Mater. 58, 4760 (2010)

    Article  CAS  Google Scholar 

  36. X.J. Zhou, C.M. Liu, Y.H. Gao, S.N. Jiang, W.H. Liu, L.W. Lu, J. Alloy. Compd. 724, 528 (2017)

    Article  CAS  Google Scholar 

  37. J.Z. Yang, J.J. Wu, H.N. Xie, Z.G. Li, K.W. Wang, Trans. Nonferr. Metal Soc. 33, 777 (2023)

    Article  CAS  Google Scholar 

  38. Q. Liu, L.M. Fang, Z.W. Xiong, J. Yang, Y. Tan, Y. Liu, Y.J. Zhang, Q. Tan, C.C. Hao, L.H. Cao, J. Li, Z.P. Gao, Mater. Sci. Eng. A 822, 141704 (2021)

    Article  CAS  Google Scholar 

  39. M.Y. Zhang, Y.Q. Zhang, H. Yu, H.X. Wang, X.F. Niu, L.F. Wang, H. Li, W.L. Cheng, Mater. Sci. Eng. A 853, 143788 (2022)

    Article  CAS  Google Scholar 

  40. G.Q. Wu, Z.C. Li, J.M. Yu, H.B. Hu, Y.L. Duan, B.B. Dong, Z.M. Zhang, J. Alloy. Compd. 938, 168666 (2023)

    Article  CAS  Google Scholar 

  41. J.P. Jason, K. Hantzsche, S.B. Yi, J. Bohlen, D. Letzig, J.A. Wollmershauser, S.R. Agnew, Matall. Mater. Trans. A 43, 1347 (2012)

    Article  Google Scholar 

  42. X. Zhao, S.C. Li, Z.M. Zhang, P.C. Gao, S.L. Kan, F.F. Yan, J. Magnes. Alloy. 8, 624 (2020)

    Article  CAS  Google Scholar 

  43. Z. Zhang, J.S. Xie, J.H. Zhang, S.J. Liu, R.Z. Wu, X.B. Zhang, J. Mater. Res. Technol. 24, 5486 (2023)

    Article  CAS  Google Scholar 

  44. T. Nakata, C. Xu, L. Geng, S. Kamado, J. Alloy. Compd. 928, 167154 (2022)

    Article  CAS  Google Scholar 

  45. X. Qin, R.Q. Zhang, P.N. Du, J.Y. Pei, Q.F. Pan, Y. Cao, H.Q. Liu, J. Nucl. Mater. 577, 154303 (2023)

    Article  CAS  Google Scholar 

  46. H.T. Jeong, W.J. Kim, J. Mater. Sci. Technol. 111, 152 (2022)

    Article  CAS  Google Scholar 

  47. G.T. Zhao, Z.R. Zhang, Y.X. Zhang, H.L. Peng, Z. Yang, N. Hiromi, X.Y. Yang, Mater. Sci. Eng. A 834, 142626 (2022)

    Article  CAS  Google Scholar 

  48. L. Zhang, Y.L. Li, X.Y. Wu, X.D. Yang, X.F. Zhang, J. Mater. Sci. 57, 20726 (2022)

    Article  CAS  Google Scholar 

  49. M.G. Jiang, H. Yan, R.S. Chen, Twinning. J. Alloy. Compd. 650, 399 (2015)

    Article  CAS  Google Scholar 

  50. J.Y. Shen, L.Y. Zhang, L.X. Hu, Y. Sun, F. Gao, W.C. Liu, H. Yu, Mater. Sci. Eng. A 823, 141745 (2021)

    Article  CAS  Google Scholar 

  51. X.D. Huang, Y.C. Xin, Y. Cao, W. Li, G.J. Huang, X. Zhao, Q. Liu, P.D. Wu, Int. J. Plast. 158, 103412 (2022)

    Article  CAS  Google Scholar 

  52. H. Li, D.E. Mason, T.R. Bieler, C.J. Boehlert, M.A. Crimp, Acta Mater. 61, 7555 (2013)

    Article  CAS  Google Scholar 

  53. A. Siahsarani, G. Faraji, Trans. Nonfree. Metal. Soc. 31, 1303 (2021)

    Article  CAS  Google Scholar 

  54. T. Al-Samman, K.D. Molodov, D.A. Molodov, G. Gottstein, S. Suwas, Acta Mater. 60, 537 (2012)

    Article  CAS  Google Scholar 

  55. A. Hadadzadeh, F. Mokdad, B.S. Amirkhiz, Mater. Sci. Eng. A 724, 421 (2018)

    Article  CAS  Google Scholar 

  56. M. Shahzad, L. Wagner, Scr. Mater. 60, 536 (2009)

    Article  CAS  Google Scholar 

  57. O. Sitdikov, R. Kaibyshev, Mater Trans. 42, 1928 (2005)

    Article  Google Scholar 

  58. M.G. Jiang, C. Xu, H. Yan, Acta Mater. 157, 53 (2018)

    Article  CAS  Google Scholar 

  59. C. You, C.M. Liu, Y.C. Wan, B. Tang, B.Z. Wang, Y.H. Gao, X.Z. Han, J. Magnes. Alloy. 7, 414 (2019)

    Article  CAS  Google Scholar 

  60. Y.Z. Meng, J.M. Yu, K. Liu, H.S. Yu, F. Zhang, Z.M. Zhang, H.H. Wang, J. Alloy. Compd. 828, 154454 (2020)

    Article  CAS  Google Scholar 

  61. H.T. Jeong, W.J. Kim, J. Magnes. Alloy. 10, 2901 (2022)

    Article  CAS  Google Scholar 

  62. S.Q. Zhu, H.G. Yan, J.H. Chen, Y.Z. Wu, B. Su, Y.G. Du, X.Z. Liao, Scr. Mater. 67, 404 (2012)

    Article  CAS  Google Scholar 

  63. D.H. Qin, M.J. Wang, C.Y. Sun, Z.X. Su, L.Y. Qian, Z.H. Sun, Mater. Sci. Eng. A 788, 139537 (2020)

    Article  CAS  Google Scholar 

  64. M.G. Jiang, C. Xu, H. Yan, G.H. Fan, T. Nakata, C.S. Lao, R.S. Chen, S. Kamado, E.H. Han, B.H. Lu, Acta Mater. 157, 53 (2018)

    Article  CAS  Google Scholar 

Download references

Acknowledgements

This research was financially supported by the Special Project of Science and Technology Cooperation and Exchange of Shanxi Province (No. 202104041101033), the ‘Shanxi Province's Key Core Technology and Common Technology Research and Development Special Project’ (No. 2020XXX015), the Joint Funds of the National Natural Science Foundation of China (Grant No. U20A20230), the Natural Science Foundation of Shanxi Province (No. 201901D111176), the Bureau of Science, Technology and Industry for National Defense of China (No. WDZC2019JJ006), the Key R&D Program of Shanxi Province (International Cooperation) (No. 201903D421036), the National Natural Science Foundation of China (Grant No. 52075501).

Author information

Authors and Affiliations

  1. School of Material Science and Engineering, North University of China, Taiyuan, 030051, China

    Rui Guo, Bo-Wen Hu, Qiang Wang & Zhi-Min Zhang

  2. School of Aeronautics and Astronautics, North University of China, Taiyuan, 030051, China

    Xi Zhao & Xue-Dong Tian

Authors
  1. Rui Guo
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Xi Zhao
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Bo-Wen Hu
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Xue-Dong Tian
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Qiang Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Zhi-Min Zhang
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Xi Zhao.

Ethics declarations

Conflict of interest

The authors state that there are no conflicts of interest to disclose.

Additional information

Available online at http://link.springer.com/journal/40195.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Guo, R., Zhao, X., Hu, BW. et al. Hot Compression Behavior of Mg–Gd–Y–Zn–Zr Alloy Containing LPSO with Different Morphologies. Acta Metall. Sin. (Engl. Lett.) 36, 1680–1698 (2023). https://doi.org/10.1007/s40195-023-01587-8

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s40195-023-01587-8

Keywords

Search

Navigation