Abstract
X80 pipeline steel plates were friction stir welded (FSW) under air, water, liquid CO2 + water, and liquid CO2 cooling conditions, producing defect-free welds. The microstructural evolution and mechanical properties of these FSW joints were studied. Coarse granular bainite was observed in the nugget zone (NZ) under air cooling, and lath bainite and lath martensite increased significantly as the cooling medium temperature reduced. In particular, under the liquid CO2 cooling condition, a dual phase structure of lath martensite and fine ferrite appeared in the NZ. Compared to the case under air cooling, a strong shear texture was identified in the NZs under other rapid cooling conditions, because the partial deformation at elevated temperature was retained through higher cooling rates. Under liquid CO2 cooling, the highest transverse tensile strength and elongation of the joint reached 92% and 82% of those of the basal metal (BM), respectively, due to the weak tempering softening. A maximum impact energy of up to 93% of that of the BM was obtained in the NZ under liquid CO2 cooling, which was attributed to the operation of the dual phase of lath martensite and fine ferrite.
Similar content being viewed by others
References
H.K. Sung, S.Y. Shin, W. Cha, K. Oh, S. Lee, N.J. Kim, Mater. Sci. Eng. A 528, 3350 (2011)
S.Y. Shin, G. Gong, S. Kim, S. Lee, Metall. Mater. Trans. A 38, 1012 (2007)
C. Zhang, Y.F. Cheng, J. Mater. Eng. Perform. 19, 834 (2010)
A.R.H. Midawi, C.H.M. Simha, A.P. Gerlich, Int. J. Press. Vessels Pip. 168, 258 (2018)
A.R.H. Midawi, E.B.F. Santos, N. Huda, A.K. Sinha, R. Lazor, A.P. Gerlich, J. Mater. Process. Technol. 226, 272 (2015)
J.A. Avila, E. Lucon, J. Sowards, P.R. Mei, A.J. Ramirez, Metall. Mater. Trans. A 47, 2855 (2016)
H. Aydin, T.W. Nelson, Mater. Sci. Eng. A 586, 313 (2013)
H.S. Shin, K.T. Park, C.H. Lee, K.H. Chang, Ksce J. Civ. Eng. 19, 1431 (2015)
A. Elrefaey, Y. Javadi, J.A. Francis, M.D. Callaghan, A.J. Leonard, Int. J. Press. Vessels Pip. 165, 20 (2018)
R.S. Mishra, Z.Y. Ma, Mater. Sci. Eng. R 50, 1 (2005)
T.F.A. Santos, T.F.C. Hermenegildo, C.R.M. Afonso, R.R. Marinho, M.T.P. Paes, A.J. Ramirez, Eng. Fract. Mech. 77, 2937 (2010)
A. Ozekcin, H.W. Jin, J.Y. Koo, N.V. Bangaru, R. Ayer, G. Vaughn, R. Steel, S. Packer, Int. J. Offshore Polar Eng. 14, 284 (2004)
S.J. Barnes, A.R. Bhatti, A. Steuwer, R. Johnson, Metall. Mater. Trans. A 43, 2342 (2012)
A. Tribe, T.W. Nelson, Eng. Fract. Mech. 150, 58 (2015)
G.M. Xie, H.B. Cui, Z.A. Luo, R.D.K. Misra, G.D. Wang, Mater. Sci. Eng. A 704, 401 (2017)
H.B. Cui, G.M. Xie, Z.A. Luo, J. Ma, G.D. Wang, R.D.K. Misra, J. Alloys Compd. 681, 426 (2016)
H.J. Zhang, H.J. Liu, Mater. Des. 45, 206 (2013)
P. Xue, B.L. Xiao, Q. Zhang, Z.Y. Ma, Scr. Mater. 64, 1051 (2011)
P. Xue, H. Zhao, Y. Komizo, Z.Y. Ma, in Proceedings of the 1st International Joint Symposium on Joining and Welding, Osaka, Japan, November 6–8 (2013)
P. Xue, B.L. Xiao, W.G. Wang, Q. Zhang, D. Wang, Q.Z. Wang, Z.Y. Ma, Mater. Sci. Eng. A 575, 30 (2013)
M. Imam, R. Ueji, H. Fujii, J. Mater. Process. Technol. 230, 62 (2016)
H.K.D.H. Bhadeshia, Mater. Sci. Eng. A 273–275, 58 (1999)
P.H. Shipway, H.K.D.H. Bhadeshia, Mater. Sci. Technol. 11, 1116 (1995)
S.H.C. Park, Y.S. Sato, H. Kokawa, K. Okamoto, S. Hirano, M. Inagaki, Metall. Mater. Trans. A 40, 625 (2009)
J.K. Park, K.H. Kim, J.H. Chung, S.Y. Ok, Metall. Mater. Trans. A 39, 235 (2008)
P.D. Hodgson, M.R. Hickson, R.K. Gibbs, Scr. Mater. 40, 1179 (1999)
G.M. Xie, H.B. Cui, Z.A. Lou, W. Yu, J. Ma, G.D. Wang, J. Mater. Sci. Technol. 32, 326 (2016)
S.H.C. Park, Y.S. Sato, H. Kokawa, K. Okamoto, S. Hirano, M. Inagaki, Scr. Mater. 49, 1175 (2003)
H.B. Cui, G.M. Xie, Z.A. Lou, J. Ma, G.D. Wang, R.D.K. Misra, Mater. Des. 106, 463 (2016)
M. Abbasi, T.W. Nelson, C.D. Sorensen, Metall. Mater. Trans. A 43, 4940 (2012)
F.C. Liu, Y. Hovanski, M.P. Miles, C.D. Sorensen, T.W. Nelson, J. Mater. Sci. Technol. 34, 39 (2018)
H.F. Lan, L.X. Du, R.D.K. Misra, Mater. Sci. Eng. A 611, 194 (2014)
Y. You, C.J. Shang, W.J. Nie, S. Subramanian, Mater. Sci. Eng. A 558, 692 (2012)
J.S. Kang, J.B. Seol, C.G. Park, Mater. Charact. 79, 110 (2013)
Y.L. Zhou, T. Jia, X.J. Zhang, Z.Y. Liu, R.D.K. Misra, Mater. Sci. Eng. A 626, 352 (2015)
M. Calcagnotto, Y. Adachi, D. Ponge, D. Raabe, Acta Mater. 59, 658 (2011)
J.P. Wang, Z.G. Yang, B.Z. Bai, H.S. Fang, Mater. Sci. Eng. A 369, 112 (2004)
H.K.D.H. Bhadeshia, T. DebRoy, Sci. Technol. Weld. Join. 14, 193 (2009)
R. Dimitriu, H.K.D.H. Bhadeshia, Mater. Sci. Technol. 23, 1127 (2007)
Acknowledgements
This work was financially supported by the National Nature Science Foundation of China (Nos. 51774085 and 51671190), the Fundamental Research for the Chinese Central Universities (No. N170704013), and the National Key Research and Development Program of China (No. 2017YFB0305004).
Author information
Authors and Affiliations
Corresponding author
Additional information
Available online at http://link.springer.com/journal/40195
Rights and permissions
About this article
Cite this article
Xie, G.M., Duan, R.H., Xue, P. et al. Microstructure and Mechanical Properties of X80 Pipeline Steel Joints by Friction Stir Welding Under Various Cooling Conditions. Acta Metall. Sin. (Engl. Lett.) 33, 88–102 (2020). https://doi.org/10.1007/s40195-019-00940-0
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40195-019-00940-0