The effect of Mn content on the microstructure and cryogenic mechanical properties of a 7% Ni steel was investigated within the Mn content range from 0.13% to 0.36%. The microstructure of the steel as determined by optical microscopy, scanning electron microscopy, transmission electron microscopy, electron backscattering diffraction and X-ray diffraction was presented, and the low-temperature mechanical properties were given. The size of prior austenite grain did not change a lot as Mn content increased. Film-like reversed austenite, having high stability, was found mainly in the specimens with lower Mn content; however, in the specimen with the highest Mn content, the role of Mn was not obvious in stabilizing reversed austenite. Besides, with increasing Mn content, the amount of reversed austenite at grain boundaries gradually decreased. The variable Mn content had a significant effect on cryogenic toughness, but not apparent on cryogenic tensile strength or yield strength. An excellent combination of cryogenic tensile and impact properties was obtained when Mn content of steel was 0.13%.
Similar content being viewed by others
References
K.J. Kim, L.H. Schwartz, Mater. Sci. Eng. A 33, 5 (1978)
C.K. Syn, S.G. Jin, J.W. Morris, Metall. Trans. A 7, 1827 (1976)
M. Yamashita, D. Knowels, M. Mitsumoto, T. Kawabata, Development of 7%Ni-TMCP steel plate for LNG storage tanks, in: the Asme Pressure Vessels and Piping Conference, New York, 17–21 July, 2011
R.J. Song, D. Ponge, D. Raabe, ISIJ Int. 45, 1721 (2005)
C.Y. Chao, C.H. Liu, Mater. Trans. 43, 2635 (2002)
H.M. Deng, C.Y. Chung, J.H. Zhang, S.C. Chen, Scr. Mater. 44, 87 (2001)
J.Y. Park, Y.S. Ahn, Acta Metall. Sin. (Engl. Lett.) 1, 32 (2015)
J.I. Kim, C.K. Syn, J.W. Morris, Metall. Trans. A 14, 93 (1983)
M. Wang, Z.L. Xie, C.G. Li, Z.Y. Liu, The development of Ni-containing cryogenic steels and their industrial manufacturing, in: Energy Materials Conference, Xi’an Shaanxi Province, 4–6 November, 2014
Y.H. Yang, Q.W. Cai, H.B. Wu, H. Wang, Acta Metall. Sin. 45, 270 (2009). (in Chinese)
M. Lei, Y.Y. Guo, Acta Metall. Sin. (Engl. Lett.) 4, 244 (1989)
J. Chiang, J.D. Boyd, A.K. Pilkey, Mater. Sci. Eng. A 638, 132 (2015)
Y.K. Lee, H.C. Shin, Y.C. Jang, S.H. Kim, C.S. Choi, Scr. Mater. 47, 805 (2002)
S. Morito, K. Ohishi, K. Hono, T. Ohba, ISIJ Int. 51, 1200 (2011)
B. Fultz, J.I. Kim, Y.H. Kim, J.W. Morris, Metall. Trans. A 17, 967 (1986)
E.D. Moor, D.K. Matlock, J.G. Speer, M.J. Merwin, Scr. Mater. 64, 185 (2011)
Y.Y. Song, J.P. Cui, L.J. Rong, J. Mater. Sci. Technol. 32, 189 (2016)
M. Wang, Z. Liu, C.G. Li, Acta Metall. Sin. (Engl. Lett.) 30, 238 (2017)
V. Raghavan, Metall. Mater. Trans. A 26, 237 (1995)
O. Dmitrieva, D. Ponge, G. Inden, J. Millan, P. Choi, J. Sietsma, D. Raabe, Acta Mater. 59, 364 (2011)
M. Kuzmina, D. Ponge, D. Raabe, Acta Mater. 86, 182 (2015)
J. Han, A.K. Silva, D. Ponge, D. Raabe, S.M. Lee, Y.K. Lee, S.I. Lee, B. Hwang, Acta Mater. 122, 199 (2017)
N.H. Heo, J.W. Nam, Y.U. Heo, S.J. Kim, Acta Mater. 61, 4022 (2013)
Acknowledgement
This work was financially supported by Wuhan Iron and Steel (Group) Corp.
Author information
Authors and Affiliations
Corresponding author
Additional information
Available online at http://link.springer.com/journal/40195
Rights and permissions
About this article
Cite this article
Cao, HW., Luo, XH., Zhan, GF. et al. Effect of Mn Content on Microstructure and Cryogenic Mechanical Properties of a 7% Ni Steel. Acta Metall. Sin. (Engl. Lett.) 31, 699–705 (2018). https://doi.org/10.1007/s40195-018-0700-1
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40195-018-0700-1