Abstract
The influence of pre-deformation on aging precipitates of three near peak-aged Al–Cu–Li alloys, 1460 alloy with a low Cu/Li ratio (1.46), 2050 alloy with a high Cu/Li ratio (4.51) and 2A96 alloy with a medium Cu/Li ratio (2.97), was investigated. The strength of the aged alloys is enhanced by the pre-deformation. The effectiveness of pre-deformation on precipitates is dependent on the alloy’s composition. With increasing the pre-deformation, the population density of T1 (Al2CuLi) precipitates increases in all three Al–Cu–Li alloys and their diameter decreases in 2050 and 2A96 alloys, and the greatest effectiveness is observed in 2A96 alloy. The pre-deformation also increases the population density of θ′ (Al2Cu) precipitates and decreases their diameter in 2050 and 2A96 Al–Li alloys, but the effectiveness is smaller compared to that on T1 precipitates. In 1460 alloy subjected to two-step aging at 130 °C for 20 h followed by 160 °C for 12 h, the main precipitates are δ′ (Al3Li). At 2%–6% pre-deformation, GP-I zones form and pre-deformation displays little influence. Eight percentage pre-deformation promotes θ″/θ′ precipitation and increases their population density.
Similar content being viewed by others
References
R.J. Rioja, J. Liu, Metall. Mater. Trans. A 43, 3325 (2012)
T. Dursun, C. Soutis, Mater. Des. 56, 862 (2014)
T.R. Prabhu, Acta Metall. Sin. (Engl. Lett.) 28, 909 (2015)
J.F. Li, Z.W. Peng, C.X. Li, W.J. Chen, Trans. Nonferrous Met. Soc. China 18, 755 (2008)
J.F. Li, N. Birbilis, Z.Q. Jia, B. Cai, Z.Q. Zheng, Mater. Charact. 60, 1334 (2009)
J.T. Jiang, Q.J. Tang, L. Yang, K. Zhang, S.J. Yuan, L. Zhen, J. Mater. Process. Technol. 227, 110 (2016)
R.N. Lumley, I.J. Polmear, A.J. Morton, Mater. Sci. Technol. 19, 1483 (2003)
X.F. Li, K. Lei, P. Song, X.Q. Liu, F. Zhang, J.F. Li, J. Chen, J. Mater. Eng. Perform. 24, 3905 (2015)
H.M. Wang, C.Q. Xia, P. Lei, Z.W. Wang, J. Cent, South Univ. Technol. 18, 1349 (2011)
M. Wang, S.S. Chen, Acta Aeronaut. Astronaut. Sin. 18, 379 (1997). (in Chinese)
X.Y. Wei, Z.Q. Zheng, Z.R. Pan, Y.Y. Chen, S.C. Li, Q.N. Chen, Rare Metal Mater. Eng. 37, 1996 (2008). (in Chinese)
B.M. Gable, A.W. Zhu, A.A. Csontos, E.A. Starker Jr, J. Light Met. 1,1 (2000)
J.D. Kim, J.K. Park, Metall. Trans. A 24, 2613 (1993)
S.P. Ringer, B.C. Muddle, I.J. Polmear, Metall. Mater. Trans. A 26, 1659 (1995)
W.A. Cassada, G.J. Shiflet, E.A. Starker Jr., Metall. Trans. A 22, 287 (1991)
W.A. Cassada, G.J. Shiflet, E.A. Starker Jr., Metall. Trans. A 22, 299 (1991)
A.K. Hopkins, K.V. Jata, R.J. Rioja, Mater. Sci. Forum 217–222, 421 (1996)
Z.S. Yuan, Z. Lu, Y.H. Xie, S.L. Dai, C.S. Liu, Rare Metal Mat. Eng. 36, 493 (2007). (in Chinese)
C. Gao, Y. Luan, J.C. Yu, Y. Ma, Trans. Nonferrous Met. Soc. China 24, 2196 (2014)
B.I. Rodgers, P.B. Prangnell, Acta Mater. 108, 55 (2016)
H.Y. Li, W. Kang, X.C. Lu, J. Alloys Compd. 640, 210 (2015)
N. Gao, M.J. Starink, L. Davin, A. Cerezo, S.C. Wang, P.J. Gregson, Mater. Sci. Technol. 21, 1010 (2005)
S.C. Wang, M.J. Starink, Int. Mater. Rev. 50, 193 (2005)
J.C. Huang, A.J. Ardrell, Mater. Sci. Technol. 3, 176 (1987)
J.W. Cahn, Acta Metall. 5, 169 (1957)
D.Y. Li, L.Q. Chen, Acta Mater. 46, 2573 (1998)
S.F. Baumann, D.B. Williams, Scr. Metall. 18, 611 (1984)
S. Hirosawa, T. Sato, A. Kamio, Mater. Sci. Eng. A 242, 195 (1998)
J.F. Nie, B.C. Muddle, Mater. Sci. Eng. A 319–321, 448 (2001)
L. Loechte, A. Gift, G. Gottstein, I. Hurtado, Acta Mater. 48, 2969 (2000)
Acknowledgements
Authors thank the National High Technology Research and Development Program of China (No. 2013AA032401) and Teacher’s Research Foundation of Central South University (No. 2013JSJJ 001) for the financial support. The financial support from Nonferrous Metal Oriented Advanced Structural Materials and Manufacturing Cooperative Innovation Centre was also greatly appreciated.
Author information
Authors and Affiliations
Corresponding author
Additional information
Available online at http://link.springer.com/journal/40195
Rights and permissions
About this article
Cite this article
Li, JF., Ye, ZH., Liu, DY. et al. Influence of Pre-deformation on Aging Precipitation Behavior of Three Al–Cu–Li Alloys. Acta Metall. Sin. (Engl. Lett.) 30, 133–145 (2017). https://doi.org/10.1007/s40195-016-0519-6
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40195-016-0519-6