Microstructure Evolution in Cast Al-Zn-Mg Alloys Processed by Equal Channel Angular Pressing

  • Technical Article
  • Published:
Metallography, Microstructure, and Analysis Aims and scope Submit manuscript

Abstract

In the present work, microstructure development and enhancement in the microhardness of Al-Zn-Mg alloys (with 5, 10, and 15% zinc) during equal channel angular pressing (ECAP) were investigated. Dendritic morphology was observed in the cast condition of all three alloys, and precipitates were situated along the inter-dendritic regions. After homogenization, precipitates in the inter-dendritic regions were uniformly distributed in the aluminum matrix and grain boundaries were developed. After 4 passes in route BC, large reduction in the grain size was observed. X-ray diffractometry showed that MgZn2 precipitate was developed in the ECAP-processed samples. Increase in the intensity of MgZn2 peaks was observed when the quantity of zinc is increased in the material. Also, changes in the intensity of XRD peaks were observed in ECAP-processed samples due to shear deformation. After ECAP, substantial increase in the microhardness was perceived. After four passes, microhardness increased to 109, 67, and 58% from the initial condition in A1, A2, and A3 alloys, respectively. Also, improvement in the microhardness was also observed when the quantity of zinc is increased in the material.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10

Similar content being viewed by others

References

  1. R.Z. Valiev, R.K. Islamgaliev, I.V. Alexandrov, Bulk nanostructured materials from severe plastic deformation. Prog. Mater Sci. 45(2), 103–189 (2000)

    Article  Google Scholar 

  2. R.Z. Valiev, T.G. Langdon, Principles of equal-channel angular pressing as a processing tool for grain refinement. Prog. Mater Sci. 51(7), 881–981 (2006)

    Article  Google Scholar 

  3. V.M. Segal, V.I. Raznikov, A.E. Drobyshewsky, V.I. Kopylov, Plastic working of metals by simple shear. Russ. Metall. 1, 99–106 (1981)

    Google Scholar 

  4. Y.T. Zehetbauer, M.J. Zhu, Bulk Nanostructured Materials (Wiley-VCH, Weinheim, 2009)

    Book  Google Scholar 

  5. M.H. Shaeri, M.T. Salehi, S.H. Seyyedein, M.R. Abutalebi, J.K. Park, Microstructure and mechanical properties of Al-7075 alloy processed by equal channel angular pressing combined with aging treatment. Mater. Des. 57, 250–257 (2014)

    Article  Google Scholar 

  6. Y.H. Zhao, X.Z. Liao, Y.T. Zhu, R.Z. Valiev, Enhanced mechanical properties in ultrafine grained 7075 Al alloy. J. Mater. Res. 20(2), 288–291 (2005)

    Article  Google Scholar 

  7. M.J. Starink, N. Gao, M. Furukawa, Z. Horita, C. Xu, T.G. Langdon, Microstructural developments in a spray-cast Al-7034 alloy processed by equal-channel angular pressing. Rev. Adv. Mater. Sci. 7(1), 1–12 (2004)

    Google Scholar 

  8. M. Ebrahimi, S. Attarilar, C. Gode, F. Djavanroodi, Damage prediction of 7025 aluminium alloy during equal-channel angular pressing. Int. J. Miner. Metall. Mater. 21(10), 990–998 (2014)

    Article  Google Scholar 

  9. J. Valder, M. Rijesh, A.O. Surendranathan, Failure analysis of cast tubular specimens of Al-5Zn-Mg while processing at room temperature by equal channel angular pressing (ECAP). J. Fail. Anal. Prev. 14(5), 690–695 (2014)

    Article  Google Scholar 

  10. S.C. Wang, M.J. Starink, N. Gao, X.G. Qiao, C. Xu, T.G. Langdon, Texture evolution by shear on two planes during ECAP of a high-strength aluminium alloy. Acta Mater. 56(15), 3800–3809 (2008)

    Article  Google Scholar 

  11. C.M. Cepeda-Jimenez, J.M. Garcia-Infanta, O.A. Ruano, F. Carreno, Mechanical properties at room temperature of an Al-Zn-Mg-Cu alloy processed by equal channel angular pressing. J. Alloys Compd. 509(35), 8649–86560 (2011)

    Article  Google Scholar 

  12. C. Xu, T.G. Langdon, Creep and superplasticity in a spray-cast aluminium alloy processed by ECA pressing. Mater. Sci. Eng. A 410–411, 398–401 (2005)

    Article  Google Scholar 

  13. G. Purcek, M. Aydin, O. Saray, T. Kucukomeroglu, Enhancement of tensile ductility of severe plastically deformed two-phase Zn-12Al alloy by equal channel angular extrusion. Mater. Sci. Forum 633–634, 437–447 (2010)

    Google Scholar 

  14. M. Aydin, Y. Heyal, Effect of equal channel angular pressing on microstructural and mechanical properties of as cast Al-20 wt%Zn alloy. Mater. Sci. Technol. 29(6), 679–688 (2013)

    Article  Google Scholar 

  15. M. Aydin, High-cycle fatigue behaviour of severe plastically deformed binary Zn-60Al alloy by equal-channel angular extrusion. J. Mater. Process. Technol. 212(8), 1780–1789 (2012)

    Article  Google Scholar 

  16. G.K. Manjunath, G.V. Preetham Kumar, K. Udaya Bhat, Tensile properties and tensile fracture characteristics of cast Al-Zn-Mg alloys processed by equal channel angular pressing. Trans. Indian Inst. Met. 70(3), 833–842 (2017)

    Article  Google Scholar 

  17. K. Nakashima, Z. Horita, M. Nemoto, T.G. Langdon, Development of a multi-pass facility for equal-channel angular processing to high total strains. Mater. Sci. Eng. A 281(1–2), 82–87 (2000)

    Article  Google Scholar 

  18. K.R. Cardoso, D.N. Travessa, W.J. Botta, A.M. Jorge Jr., High strength AA7050 Al alloy processed by ECAP: microstructure and mechanical properties. Mater. Sci. Eng. A 528(18), 5804–5811 (2011)

    Article  Google Scholar 

  19. Y.H. Zhao, X.Z. Liao, Z. Jin, R.Z. Valiev, Y.T. Zhu, Microstructures and mechanical properties of ultrafine grained 7075 Al alloy processed by ECAP and their evolutions during annealing. Acta Mater. 52(15), 4589–4599 (2004)

    Article  Google Scholar 

  20. J. Gubicza, I. Schiller, N.Q. Chinh, J. Illy, Z. Horita, T.G. Langdon, The effect of severe plastic deformation on precipitation in supersaturated Al-Zn-Mg alloys. Mater. Sci. Eng. A 460–461, 77–85 (2007)

    Article  Google Scholar 

  21. S. Zhang, W. Hu, R. Berghammer, G. Gottstein, Microstructure evolution and deformation behaviour of ultrafine-grained Al-Zn-Mg alloys with fine η′ precipitates. Acta Mater. 58(20), 6695–6705 (2010)

    Article  Google Scholar 

  22. N.Q. Chinh, J. Gubicza, T. Czeppe, J. Lendvai, C. Xu, R.Z. Valiev, T.G. Langdon, Developing a strategy for the processing of age-hardenable alloys by ECAP at room temperature. Mater. Sci. Eng. A 516(1–2), 248–252 (2009)

    Article  Google Scholar 

  23. S.G. Chowdhury, C. Xu, T.G. Langdon, Texture evolution in an aluminium alloy processed by ECAP with concurrent precipitate fragmentation. Mater. Sci. Eng. A 473(1–2), 219–225 (2008)

    Article  Google Scholar 

  24. M. Furukawa, Z. Horita, T.G. Langdon, Factors influencing the shearing patterns in equal-channel angular pressing. Mater. Sci. Eng. A 332(1–2), 97–109 (2002)

    Article  Google Scholar 

  25. L.J. Zheng, C.Q. Chen, T.T. Zhou, P.Y. Liu, M.G. Zeng, Structure and properties of ultrafine-grained Al-Zn-Mg-Cu and Al-Cu-Mg-Mn alloys fabricated by ECA pressing combined with thermal treatment. Mater. Charact. 49(5), 455–461 (2002)

    Article  Google Scholar 

  26. W.J. Kim, J.K. Kim, H.K. Kim, J.W. Park, Y.H. Jeong, Effect of post equal-channel-angular-pressing aging on the modified 7075 Al alloy containing Sc. J. Alloys Compd. 450(1–2), 222–228 (2008)

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Department of Metallurgical and Materials Engineering, National Institute of Technology Karnataka, Surathkal, Mangalore, 575025, India

    G. K. Manjunath, K. Udaya Bhat & G. V. Preetham Kumar

Authors
  1. G. K. Manjunath
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. K. Udaya Bhat
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. G. V. Preetham Kumar
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to G. K. Manjunath.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Manjunath, G.K., Udaya Bhat, K. & Preetham Kumar, G.V. Microstructure Evolution in Cast Al-Zn-Mg Alloys Processed by Equal Channel Angular Pressing. Metallogr. Microstruct. Anal. 7, 77–87 (2018). https://doi.org/10.1007/s13632-017-0412-3

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s13632-017-0412-3

Keywords

Search

Navigation