Abstract
Graphene has become an intensive research field of study in the material science due to its peculiar properties and various applications. Particularly, it is considered as the thinnest 2D material, which is used widely in many devices, and hence, this involves its interaction with supporting substrates; thus, free surface energy of graphene is very essential for its miscellaneous application in our life. Here, in this report, we present the measuring results of static contact angle of microscale liquid droplets adsorbed on graphene-coated copper and silicon substrates at room temperature to calculate the graphene surface free energy and its wettability. Both copper- and silicon-coated substrates increase the static water contact angle values, indicating hydrophobicity of graphene layers. On the other hand, variation of strength of aqueous ionic solution, sodium chloride solution, does not change the static water contact angle, indicating minor importance of polar component of surface free energy of graphene layers. For few layers of graphene, up to three, the graphene surface free energy is controlled by the Cassie state, while for more than three layers, the surface exhibits the Wenzel state of wetting.
Similar content being viewed by others
References
Wang, S.; Zhang, Y.; Abidi, N.; Cabrales, L.: Wettability and surface free energy of graphene films. Langmuir 25(18), 11078–11081 (2009)
Lee, H.C.; Liu, W.-W.; Chai, S.-P.; Mohamed, A.R.; Lai, C.W.; Khe, C.-S.; Voon, C.; Hashim, U.; Hidayah, N.: Synthesis of single-layer graphene: a review of recent development. Proc. Chem. 19, 916–921 (2016)
Suk, J.W., et al.: Transfer of CVD-grown monolayer graphene onto arbitrary substrates. ACS Nano 5(9), 6916–6924 (2011)
Kozbial, A.; Zhiting, L.; Conaway, C.; McGinley, R.; Dhingra, S.; Vahdat, V.; Zhou, F.; D’Urso, B.; Liu, H.; Li, L.: Study on the surface energy of graphene by contact angle measurements. Langmuir 30, 8598–8606 (2014)
Chibowski, E.; Jurak, M.: Comparison of contact angle hysteresis of different probe liquids on the same solid surface. Colli. Polym. Sci. 291(2), 391–399 (2013)
Kwok, D.Y.; Neumann, A.W.: Contact angle measurement and contact angle interpretation. Adv. Coll. Interface. Sci. 81, 167–249 (1999)
van Engers, C.D.; Cousens, N.E.A.; Babenko, V.; Britton, J.; Zappone, B.; Grobert, N.; Perkin, S.: Direct measurement of the surface energy of graphene. Nano Lett. 17, 3815–3821 (2017)
Rafiee, J., et al.: Wetting transparency of graphene. Nat. Mater. 11(3), 217–222 (2012)
Feng, D.; Huang, J.; Duan, H.; Xiong, C.; Wang, J.: Wetting transparency of supported graphene is regulated by polarities of liquids and substrates. Appl. Surf. Sci. 454, 249–255 (2018)
Khung, Y.L.; Cole, M.A.; McInnes, S.J.P.; Voelcker, N.H.: Control over wettability via surface modification of porous gradients. In: BioMEMS and Nanotechnology III. Progress in Biomedical Optics and Imaging - Proceedings of SPIE, vol. 6799, pp. 679909 (2008). https://doi.org/10.1117/12.759377
Acknowledgements
This research was supported by SQU Strategic Grant SR/SCI/PHYS/18/01. The authors thank SQU CAARU and Dr. Myo Tay Zar Myint from the Surface Science Laboratory, College of Science.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Al-Ruqeishi, M.S., Mohiuddin, T., Al-Amri, K. et al. Graphene Surface Energy by Contact Angle Measurements. Arab J Sci Eng 48, 757–762 (2023). https://doi.org/10.1007/s13369-022-06990-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13369-022-06990-4