Abstract
This study investigated the effect of pretreatment on the properties of kenaf fibre cement boards. Homogenous fibre cement boards were made from kenaf bast fibres, cement and water. The fibres were cut into smaller sizes, mixed with cement and water and formed in rectangular moulds. After demoulding, the boards were cured for 28 days. The fibres were treated at three levels which included hot water, calcium chloride (CaCl2), hot water + CaCl2 and a control (untreated). The fibre cement boards were tested for Modulus of Rupture (MOR), Modulus of Elasticity (MOE), Internal Bond (IB), Water Absorption (WA), Thickness Swelling (TS) and Linear Expansion (LE). The results showed that the mean MOR ranged from 1.31 to 8.25 MPa; the mean MOE from 78.0 to 1636.3 MPa for all treated boards. Mean water absorption ranged from 27.52 to 67.64% and the mean thickness swelling from 14.51 to 48.01% for all treated boards. Statistical analysis showed that the effect of the pretreatment was significant on the properties evaluated (p < 0.05). The study concluded that boards produced from hot water combined with CaCl2 treated fibres exhibited the best mechanical and physical properties.
Similar content being viewed by others
References
Alberto MM, Mougel E, Zoulalian A (2000) Compatibility of some tropical hardwood species with Portland cement using isothermal calorimetry. Forest Prod J 50:83–88
Amiandamhen SO, Izekor DN (2013) Effect of wood particle geometry and pretreatments on the strength and sorption properties of cement bonded particle boards. J Appl Nat Sci 5(2):318–322
Badejo SOO (1988) Effect of flake geometry on properties of cement-bonded particle board from mixed tropical hardwoods. Wood Sci Technol 22:357–370
Basher ABA (2013) Properties of Kenaf bast fibre cement composite board. Dessertation, Universiti Putra Malaysia, Peninsular Malaysia
Clausen CA, Kartal SN, Muehl J (2001) Particleboard made from remediated CCA-treated wood: evaluation of panel properties. Forest Prod J 51(7/8):61–64
Eusebio DA, Soriano FP, Cobangon RJ, Evans PD (2000) Manufacture of low-cost wood-cement composites in the Philippines using plantation-grown Australian species: I. Eucalyptus. Wood-Cement Composites in the Asia-Pacific Region, Canberra, pp 105–114
Ferraz MJ, Menezzi HS, Teixeira DE, Martins SA (2011) Coir fiber cement composites. Bioresources 6(3):3481–3492
Frybort S, Raimund M, Alfred T, Muller U (2008) Cement bonded composites—a mechanical review. BioResources 3(2):602–626
Ismail MA (2007) Compressive and tensile strength of natural fibre-reinforced cement based composite. Al-Rafidain Eng 15(2):42–45
Jevtic D, Zakic D, Savic A (2008) Modeling of properties of fibre reinforced cement composites. J Arch Civil Eng 6(2):165–172
Li W, Shupe TF, Hse CY (2004) Physical and mechanical properties of flake board produced from recycled CCA-treated wood. Forest Prod J 54(2):89–94
Lima AJM, Iwakiri S, Ramirez MGL (2015) Study of the interaction of Portland cement and Pinus wood for composites using Bragg sensors in optical fibers. BioResources 10(4):6690–6704
Mohr BJ, El-Ashkar NH, Kurtis KE (2004) Fibre cement composites for housing construction: state of the art review. NSF Housing Research Agenda Workshop, Orlando, FL, pp 112–128
Moslemi A (2008) Technology and market considerations for fibre cement composites. In: 11th international inorganic-bonded fibre composites conference (IIBCC), Nov 5–7, Madrid, pp 113–129
Omoniyi TM, Duna S, Othman MW (2015) Compressive strength characteristics of Kenaf fibre reinforced cement mortar. Adv Mater 4(1):6–10
Ribot NMH, Ahmad Z, Mustaffa NK (2011) Mechanical properties of Kenaf fiber composite using co cured inline fiber joint. Int J Eng Sci Technol 8(3):269–272
Semple KE, Evans PD (2004) Wood-cement composites—suitability of Western Australian mallee eucalypt, blue gum and melaleucas, RIRDC/Land and water, Australia/FWPRDC/MDBC
Simatupang MH, Habighorst C, Lange H, Neubauer A (1995) Investigations on the influence of the addition of carbon dioxide on the production and properties of rapidly set wood-cement composites. Cement Concrete Comp 17:187–197
Thygesen A, Daniel G, Lilholt H, Thomsen AB (2005) Hemp fiber microstructure and use of fungal defibration to obtain fibers for composite materials. J Nat Fibers 2:19–37
Acknowledgements
The authors wish to thank Dr Adeniran of the Institute of Agricultural Research and Training, Moore Plantation (IAR&T) Ibadan, Nigeria for the provision of Kenaf bast fibres.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Amiandamhen, S.O., Izekor, D.N. & Balogun, A.O. Performance characteristics of treated kenaf bast fibre reinforced cement composite. J Indian Acad Wood Sci 13, 156–160 (2016). https://doi.org/10.1007/s13196-016-0180-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13196-016-0180-8