Abstract
Aiming at the security problems of pipeline steel application, the different positions of the welded joints of circumferentially welding pipeline of X80 steel were investigated by microstructure observation, the hardness, Charpy impact toughness and crack tip opening displacement (CTOD) test at low temperature. The Vickers hardness test results show that there are local softened regions in heat-affected zone (HAZ). Charpy impact test indicate that the ductile–brittle transition temperature of weld is below − 60 °C, the ductile–brittle transition temperature of HAZ is around − 38 °C. CTOD test reveal that the fracture toughness of HAZ shows a large fluctuation since it is in the ductile–brittle transition temperature regime.
Similar content being viewed by others
References
Sharma S K, and Maheshwari S, J Nat Gas Sci Eng 38 (2017) 203.
Miao C, Shang C, Wang X, and Subramanian M, Acta Metall Sin 46 (2010) 541.
Motohashi H, Hagiwara N, and Masuda T, Weld Int 19 (2005) 100.
Di X J, Cai L, Xing X X, Chen C X, and Xue Z K, Acta Metall Sin Engl Lett 28 (2015) 883.
Huda N, Lazor R, and Gerlich A P, Metall Mater Trans A 48 (2017) 1.
Gianetto J A, Bowker J T, Bouchard R, Dorling D V, and Horsley D, Weld World 51 (2007) 64.
Sang Y S, Metall Mater Trans A 44 (2013) 2613.
Xu C M, Li R B, Wang J L, and Zhang G G, Adv Mater Res 476–478 (2012) 321.
Batista G Z, Carvalho L D P, Da Silva M S, and Souza M P, Weld J 95, 363s–370s (2016).
BS7448: Fracture mechanics toughness tests, Part 2. Method for determination of KIC, critical CTOD and critical J values of welds in metallic materials. British Standard (1997).
API Standard 1104: Welding of Pipeline and Related Facilities (2013).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Wang, B., Xu, Y., Hu, J. et al. The Analysis of Low Temperature Toughness on X80 Pipeline Steel Welded Joint. Trans Indian Inst Met 71, 2517–2526 (2018). https://doi.org/10.1007/s12666-018-1382-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-018-1382-0