Improvement of Bonding Strength at the Interfaces in Scrap Al Alloy Composites Using Electroless Ni-P Coated SiC

  • Original Paper
  • Published:
Silicon Aims and scope Submit manuscript

Abstract

In this work, fabrication of aluminium metal matrix composites reinforced with electroless coated SiC particles is carried out through stir-squeeze casting process. Composite is developed using scrap aluminium alloy wheel as matrix material and SiC as reinforcement. The SiC particles are coated with Ni-P using electroless coating process to improve the wetting and to promote the interfacial bonding strength between the matrix and reinforcement. For the purpose of testing and analysis of the results, composite specimens are prepared in four ways, i.e., scrap Al alloy, scrap Al alloy with uncoated SiC (5 wt%), scrap Al alloy with coated SiC (5 wt%) and scrap Al alloy with coated SiC (2.5 wt%) & coated Al2O3 (2.5 wt%). Using scanning electron microscope, energy dispersive X-ray analysis, optical microscope and X-Ray diffraction, metallurgical properties are studied. Further, mechanical properties such as porosity, hardness, tensile strength, and compressive strength are analysed. Results revealed that porosity is very less in the substrate produced with coated reinforcement compared to uncoated reinforcement. Also, hardness, tensile strength, compressive strength and bonding strength of the composite are increased significantly.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

Data Availability

The author may self-archive an author-created version of his article on his own website and his institution’s repository, including his final version; however he may not use Springer’s PDF version which is posted on www.springerlink.com. Furthermore, the author may only post his version provided acknowledgement is given to the Journal and Springer as one of the original places of publication and a link is inserted to the published article on Springer’s website. Please use the appropriate DOI for the article (go to the Linking Options in the article, then to Open URL and use the link with the DOI). Articles disseminated via www.springerlink.com are indexed, abstracted, and referenced by many abstracting and information services, bibliographic networks, subscription agencies, library networks, and consortia. The data that support the findings of this study are available from the corresponding author, [author initials], upon reasonable request.

Code Availability

Not Applicable.

References

  1. Ramanathan A, Krishnan PK, Muraliraja R (2019) A review on the production of metal matrix composites through stir casting–furnace design, properties, challenges, and research opportunities. J Manuf Process 42:213–245. https://doi.org/10.1016/j.jmapro.2019.04.017

    Article  Google Scholar 

  2. Kim CS, Cho K, Manjili MH, Nezafati M (2017) Mechanical performance of particulate-reinforced Al metal-matrix composites (MMCs) and Al metal-matrix nano-composites (MMNCs). J Mater Sci 52:13319–13349. https://doi.org/10.1007/s10853-017-1378-x

    Article  CAS  Google Scholar 

  3. Idusuyi N, Olayinka JI (2019) Dry sliding wear characteristics of aluminium metal matrix composites: a brief overview. J Mater Res Technol 8:3338–3346. https://doi.org/10.1016/j.jmrt.2019.04.017

    Article  CAS  Google Scholar 

  4. Fenghong C, Chang C, Zhenyu W, Muthuramalingam T, Anbuchezhiyan G (2019) Effects of silicon carbide and tungsten carbide in aluminium metal matrix composites. Silicon. 11:2625–2632. https://doi.org/10.1007/s12633-018-0051-6

    Article  CAS  Google Scholar 

  5. Jiang JT, Zhen L, Xu CY, Wu XL (2006) Microstructure and magnetic properties of SiC/co composite particles prepared by electroless plating. Surf Coat Technol 201:3139–3146. https://doi.org/10.1016/j.surfcoat.2006.06.036

    Article  CAS  Google Scholar 

  6. Muraliraja R, Elansezhian R (2015) Influence of nickel recovery efficiency on crystallinity and microhardness of electroless Ni–P coatings and optimisation using Taguchi technique. Trans IMF 93:126–132. https://doi.org/10.1179/0020296715Z.000000000238

    Article  CAS  Google Scholar 

  7. Rajan TP, Pillai RM, Pai BC (1998) Reinforcement coatings and interfaces in aluminium metal matrix composites. J Mater Sci 33:3491–3503. https://doi.org/10.1023/A:1004674822751

    Article  CAS  Google Scholar 

  8. Abraham S, Pal BC, Satyanarayana KG, Vaidyan VK (1990) Studies on nickel coated carbon fibres and their composites. J Mater Sci 25:2839–2845. https://doi.org/10.1007/BF00584890

    Article  CAS  Google Scholar 

  9. Krishnan PK, Christy JV, Arunachalam R, Mourad AH, Muraliraja R, Al-Maharbi M, Murali V, Chandra MM (2019) Production of aluminum alloy-based metal matrix composites using scrap aluminum alloy and waste materials: influence on microstructure and mechanical properties. J Alloys Compd 784:1047–1061. https://doi.org/10.1016/j.jallcom.2019.01.115

    Article  CAS  Google Scholar 

  10. Arunachalam R, Piya S, Krishnan PK, Muraliraja R, Christy JV, Mourad AH, Al-Maharbi M (2020) Optimization of stir–squeeze casting parameters for production of metal matrix composites using a hybrid analytical hierarchy process–Taguchi-Grey approach. Eng Optim 52:1166–1183. https://doi.org/10.1080/0305215X.2019.1639693

    Article  Google Scholar 

  11. Dwivedi SP, Sharma P, Saxena A (2020) Utilization of waste spent alumina catalyst and agro-waste rice husk ash as reinforcement materials with scrap aluminium alloy wheel matrix. Proc IME E J Process Mech Eng. https://doi.org/10.1177/0954408920930634

  12. Akash R, Muraliraja R, Suthan R, Shaisundaram VS (2020) Synthesis and testing of aluminium composite using industrial waste as reinforcement. Materials Today: Proceedings. https://doi.org/10.1016/j.matpr.2020.05.627

  13. Raju SS, Rao GS, Siva BV (2018) Experimental studies of mechanical properties and tribological behaviour of aluminium composite reinforced with coconut shell ash particulates. Int J Mater Eng Innov 9:140. https://doi.org/10.1504/IJMATEI.2018.093812

    Article  CAS  Google Scholar 

  14. Alaneme KK, Bamike BJ (2018) Characterization of mechanical and wear properties of aluminium based composites reinforced with quarry dust and silicon carbide. Ain Shams Eng J 9:2815–2821. https://doi.org/10.1016/j.asej.2017.10.009

    Article  Google Scholar 

  15. Sharma A, Belokar RM, Kumar S (2018) Dry sliding wear characterization of red mud reinforced aluminium composite. J Braz Soc Mech Sci Eng 40. https://doi.org/10.1007/s40430-018-1223-4

  16. Gireesh CH, Prasad KD, Ramji K, Vinay PV (2018) Mechanical characterization of aluminium metal matrix composite reinforced with aloe vera powder. Mater Today Proc 5:3289–3297. https://doi.org/10.1016/j.matpr.2017.11.571

    Article  CAS  Google Scholar 

  17. Khosroshahi NB, Khosroshahi RA, Mousavian RT, Brabazon D (2014) Effect of electroless coating parameters and ceramic particle size on fabrication of a uniform Ni–P coating on SiC particles. Ceram Int 40:12149–12159. https://doi.org/10.1016/j.ceramint.2014.04.055

    Article  CAS  Google Scholar 

  18. He P, Huang S, Wang H, Huang Z, Hu J, Cheng X, Pan C (2014) Electroless nickel–phosphorus plating on silicon carbide particles for metal matrix composites. Ceram Int 40:16653–16664. https://doi.org/10.1016/j.ceramint.2014.08.027

    Article  CAS  Google Scholar 

  19. Leon CA, Drew RA (2000) Preparation of nickel-coated powders as precursors to reinforce MMCs. J Mater Sci 35:4763–4768. https://doi.org/10.1023/A:1004860326071

    Article  CAS  Google Scholar 

  20. Erturun VE, Sahin O (2019) Investigation of microstructural evolution in ball-milling of SiC reinforced aluminum matrix composites. Powder Metall Metal Ceram 57:687–696. https://doi.org/10.1007/s11106-019-00032-9

    Article  CAS  Google Scholar 

  21. Sahin O, Erturun VE (2018) The effect of magnesium additives on aluminum-based composites structure. Powder Metall Metal Ceram 57:384–390. https://doi.org/10.1007/s11106-018-9995-8

    Article  CAS  Google Scholar 

  22. Erturun V, Çetin S, Sahin O (2020) Investigation of microstructure of aluminum based composite material obtained by mechanical alloying. Met Mater Int. https://doi.org/10.1007/s12540-019-00583-x

  23. Zuo R, Chen J, Han Z, Dong Y, Jow J (2020) Electroless silver plating on modified fly ash particle surface. Appl Surf Sci 513:145857. https://doi.org/10.1016/j.apsusc.2020.145857

    Article  CAS  Google Scholar 

  24. Kretz F, Gácsi Z, Kovács J, Pieczonka T (2004) The electroless deposition of nickel on SiC particles for aluminum matrix composites. Surf Coat Technol 180-181:575–579. https://doi.org/10.1016/j.surfcoat.2003.10.150

    Article  CAS  Google Scholar 

  25. Muraliraja R, Arunachalam R, Al-Fori I, Al-Maharbi M, Piya S (2019) Development of alumina reinforced aluminum metal matrix composite with enhanced compressive strength through squeeze casting process. Proc IME L J Mater Des Appl. https://doi.org/10.1177/1464420718809516

  26. Zhou HM, Jia Y, Li J, Yao SH (2016) Corrosion and wear resistance behaviors of electroless Ni–cu–P–TiN composite coating. Rare Metals. https://doi.org/10.1007/s12598-015-0663-6

  27. Umasankar V, Karthikeyan S, Xavior MA (2014) The influence of electroless nickel coated SiC on the interface strength and microhardness of aluminium composites. J Mater Environ Sci 5(1):153–158

    CAS  Google Scholar 

  28. Akbari MK, Mirzaee O, Baharvandi HR (2013) Fabrication and study on mechanical properties and fracture behavior of nanometric Al2O3 particle-reinforced A356 composites focusing on the parameters of vortex method. Mater Des 46:199–205. https://doi.org/10.1016/j.matdes.2012.10.008

    Article  CAS  Google Scholar 

  29. Reihani SS (2006) Processing of squeeze cast Al6061–30vol% SiC composites and their characterization. Mater Des 27:216–222. https://doi.org/10.1016/j.matdes.2004.10.016

    Article  CAS  Google Scholar 

  30. Leng J, Wu G, Zhou Q, Dou Z, Huang X (2008) Mechanical properties of SiC/gr/Al composites fabricated by squeeze casting technology. Scr Mater 59:619–622. https://doi.org/10.1016/j.scriptamat.2008.05.018

    Article  CAS  Google Scholar 

  31. Hossein-Zadeh M, Mirzaee O, Saidi P (2014) Structural and mechanical characterization of Al-based composite reinforced with heat treated Al2O3 particles. Mater Des (1980-2015) 54:245–250. https://doi.org/10.1016/j.matdes.2013.08.036

    Article  CAS  Google Scholar 

  32. Sajjadi SA, Ezatpour HR, Parizi MT (2012) Comparison of microstructure and mechanical properties of A356 aluminum alloy/Al2O3 composites fabricated by stir and compo-casting processes. Mater Des 34:106–111. https://doi.org/10.1016/j.matdes.2011.07.037

    Article  CAS  Google Scholar 

Download references

Acknowledgments

Authors are thankful to the management of VIT (Vellore Institute of Technology)-Vellore for providing experimental facilities to conduct experiments.

Author information

Authors and Affiliations

  1. School of Mechanical Engineering (SMEC), Vellore Institute of Technology (VIT), Vellore, Tamil Nadu, 632014, India

    P. Chandrasekar & Dega Nagaraju

Authors
  1. P. Chandrasekar
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Dega Nagaraju
    View author publications

    You can also search for this author in PubMed Google Scholar

Contributions

P. Chandrasekhar conducted experiments for studying material characterization and testing of mechanical properties.

Dr. Dega Nagaraju worked for analysis of results, i.e. SEM analysis, EDAX analysis and XRD analysis. Also, contributed in plotting all the graphs demonstrated in the paper.

Dr. Dega Nagaraju and P. Chandrasekhar worked for preparation of samples for experimentation purpose as well worked for manuscript preparation.

Corresponding author

Correspondence to Dega Nagaraju.

Ethics declarations

Not applicable.

Consent to Participate

All the authors are mutually agreed for the content and participated equally for the current research. The authors have no conflicts of interest to declare that they are relevant to the content of this article.

Consent for Publication

The Author transfers non-exclusive publication rights to Silicon Journal, and he warrants that his/her contribution is original. The author signs for and accepts responsibility for releasing this material on behalf of any and all co-authors. This transfer of publication rights covers the non-exclusive right to reproduce and distribute the article, including reprints, translations, photographic reproductions, microform, electronic form (offline, online) or any other reproductions of similar nature.

Additional information

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Chandrasekar, P., Nagaraju, D. Improvement of Bonding Strength at the Interfaces in Scrap Al Alloy Composites Using Electroless Ni-P Coated SiC. Silicon 14, 2941–2952 (2022). https://doi.org/10.1007/s12633-021-01078-4

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12633-021-01078-4

Keywords

Search

Navigation