Abstract
This paper presents experimental results of some fresh and hardened state properties of self-compacting concrete (SCC) incorporating palm oil fuel ash (POFA). Three concrete mixes namely ordinary Portland cement (OPC) concrete i.e. concrete with 100% OPC as control, and concrete with 30% and 60% POFA having different water/binder (w/b) ratios of 0.4, 0.45 and 0.5 were prepared. Filling ability, passing ability and segregation resistance of SCC along with strength properties were determined and compared with those of the OPC based SCC. Test results revealed that replacement of POFA in general decreased the workability of concrete with acceptable range. The compressive strength, however, increased with lower w/b ratio and lower replacement of ash. The splitting tensile and flexural strength values have also followed the same trend. The results obtained and the observation made in this study suggest that POFA can suitably be used as supplementary cementing material in SCC.
Similar content being viewed by others
References
Abdul Awal A and Hussin M 1999 Durability of high performance concrete containing palm oil fuel ash. In: Eighth International Conference on Durability of Building Materials and Components, 8 dbmc: 465–474
Abdul Awal A and Shehu I 2013 Evaluation of heat of hydration of concrete containing high volume palm oil fuel ash. Fuel 105: 728–731
Alsubari B, Shafigh P and Jumaat M Z 2014 The effect of palm oil fuel ash as a cement replacement material on selfcompacting concrete. Appl. Mech. Mater. 567: 529–534
ASTM C618/C618M 2012 Standard specification for coal fly ash and raw or calcined natural pozzolan for use as a mineral admixture for concrete. American Society for Testing Materials
ASTM C1621/C1621M 2009 Standard test method for passing ability of self-consolidating concrete by J-ring. American Society for Testing Materials
ASTM C1611/C1611M 2009 Standard test method for slump flow of self-consolidating concrete. American Society for Testing and Materials
ASTM C293/C239M 2010 Standard test method for flexural strength of concrete (using simple beam with center-point loading). American Society for Testing Materials
ASTM C496/C496M 2011 Standard test method for splitting tensile strength of cylindrical concrete specimens. American Society for Testing Materials
Bouzoubaa N and Lachemi M 2011 Self-compacting concrete incorporating high volumes of class F fly ash preliminary results. Cement Concrete Res. 31: 413–420
BS 1881-116 1983 Testing concrete. Method for determination of compressive strength of concrete cubes. British Standard
Dinakar P, Kartik Reddy M and Sharma M 2013 Behaviour of self compacting concrete using Portland pozzolana cement with different levels of fly ash. Mater. Des. 46: 609–616
Domone P 2006 Self-compacting concrete: An analysis of 11 years of case studies. Cement Concrete Compos. 28: 197–208
Domone P 2007 A review of the hardened mechanical properties of self-compacting concrete. Cement Concrete Compos. 29: 1–12
EFNARC 2002 Specifications and guidelines for self-consolidating concrete. In: European Federation of Suppliers of Specialist Construction Chemicals (EFNARC)
Hossain K and Lachemi M 2010 Fresh, mechanical, and durability characteristics of self-consolidating concrete incorporating volcanic ash. J. Mater. Civil Eng. 22 (7): 651–657
Lachemi M, Hossain K M, Lambros V and Bouzoub 2003 Development of cost-effective self-consolidating concrete incorporating fly ash, slag cement, or viscosity-modifying admixtures. ACI Mater. J. 100 (5): 419–425
Liu M 2010 Self-compacting concrete with different levels of pulverized fuel ash. Constr. Build. Mater. 24: 1245–1252
Nikbin I et al 2014 A comperhensive investegation into the effect of water to cement ratio and powder content on mechanical properties of self-compacting concrete. Constr. Build Mater. 57: 69–80
Ozawa K, Maekawa K, Kunishima H and Okamura H 1989 Performance of concrete based on the durability design of concrete structures. Chiang Mai, Thailand. 445–456
Safiuddin M, Abdus Salam M and Jumaat M Z 2011a Correlations between fresh properties of self-consolidating concrete including palm oil fuel ash. Adv. Mater. Res. 250–253: 409–416
Safiuddin M, West J and Soudki K 2011b Flowing ability of the mortars formulated from self-compacting concretes incorporating rice husk ash. Constr. Build Mater. 25: 973–978
Siddique R 2011 Properties of self-compacting concrete containing class F fly ash. Mater. Des. 32: 1501–1507
Siddique R, Aggarwal P and Aggarwal Y 2012 Influence of water/powder ratio on strength properties of self-compacting concrete containing coal fly ash and bottom ash. Constr. Build Mater. 29: 73–81
Uysal M and Sumer M 2011 Performance of self-compacting concrete containing different mineral admixtures. Constr. Build Mater. 25: 4112–4120
Uysal M and Yilmaz K 2011 Effect of mineral admixtures on properties of self-compacting concrete. Cement Concrete Compos. 33: 771–776
Yurugi M 1998 Application of self-compacting concrete in Japan. In: Proceedings of 23rd OWICS conference, Singapore: CI-Premier Ptc. Ltd. 29–42
Acknowledgements
The authors are thankful to the technical support received from the staff of Structure and Materials laboratory of the Universiti Teknologi Malaysia (UTM) in conducting the experimental work.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
MOHAMMADHOSSEINI, H., ABDUL AWAL, A.S.M. & EHSAN, A.H. Influence of palm oil fuel ash on fresh and mechanical properties of self-compacting concrete. Sadhana 40, 1989–1999 (2015). https://doi.org/10.1007/s12046-015-0426-y
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12046-015-0426-y