Design, synthesis and physical properties of poly(styrene-butadiene-styrene)/poly(thiourea-azo-sulfone) blends

Abstract

A new aromatic azo-polymer, poly(thiourea-azo-sulfone), has been synthesized using 1-(4-thiocarbamoylaminophenylsulfonylphenyl)thiourea and diazonium salt solution. Conducting and thermally stable rubbery blends of poly(styrene-block-butadiene-block-styrene) (SBS) triblock copolymer and poly(thiourea-azo-sulfone) (PTAS) were produced by solution blending technique. PTAS possessed fine solubility in polar solvents and high molar mass 63 × 10₃ g moL⁻¹. Microscopic analysis on SBS/PTAS blends revealed good adhesion between the two polymers without macro phase separation. Electrical conductivity measurement recommended that blending of SBS with 60% PTAS was sufficiently conducting 1.43 S cm⁻¹. A relationship between PTAS loading and thermal stability of blends was observed. With the increasing PTAS content, 10% gravimetric loss was increased from 481 to 497 °C, while glass transition improved from 123 to 136 °C (better than neat SBS but lower than PTAS). The blends also established higher tensile strength (52.40–59.96 MPa) relative to SBS. Fine balance of properties renders new SBS/PTAS, potential engineering plastics for a number of aerospace relevance.