Abstract
The effect of aging treatment on the mechanical properties of 45 vol.% SiCp/6061Al composite fabricated by hot isostatic pressing has been investigated. The results indicate that the hardness and strength of the composite can be strongly improved after solid-solution and aging treatment, with the observations of the accelerated aging kinetic and the double-peak phenomenon. The double-peak phenomenon observed in the 190°C-aged composite is attributed to the substantial amount of G.P. zones and the remarkable precipitation of the β″ and β′ phases, respectively. At 170°C and 180°C, the hardness of the first peak-aged composites were about 216.5 HBW and 217.7 HBW, respectively, and the subsequent fluctuation in hardness was because of the progressive precipitation of the β″ phase and subsequent β′ phase. The maximum yield strength and bending strength were achieved in the composite aged at 170°C for 9 h, being about 688.2 MPa and 798.2 MPa, respectively, with the corresponding increments being about 110.9% and 37% in comparison to that of the as-fabricated composite.
Similar content being viewed by others
References
S.B. Ren, X.H. Qu, J. Guo, X.B. He, M.L. Qin, and X.Y. Shen, J. Alloy. Compd. 484, 256 (2009).
Y. Cui, L.F. Wang, and J.Y. Ren, Chin. J. Aeronaut. 21, 578 (2008).
F. Teng, K. Yu, J. Luo, H.J. Fang, C.L. Shi, Y.L. Dai, and H.Q. Xiong, Trans. Nonferrous Met. Soc. China 26, 2647 (2016).
W. Wang, Q. Li, R. Ma, Y.Q. Cui, X.M. Cao, and X.H. Wang, Ceram. Int. 43, 12526 (2017).
P. Shen, Y. Wang, L.H. Ren, S.X. Li, Y.H. Liu, and Q.C. Jiang, Appl. Surf. Sci. 355, 930 (2015).
H.T. Tong, F. Qiu, R. Zuo, P. Shen, X.S. Cong, J.S. Liu, H.Y. Yang, and Q.C. Jiang, Appl. Surf. Sci. 501, 144265 (2020).
P. Liu, A. Wang, J.P. Xie, and S.M. Hao, J. Wuhan Univ. Technol., Mater. Sci. Ed. 30, 1229 (2015).
Z. Chaudhury, M. Hailat, Y. Liu, and G. Newaz, J. Mater. Sci. 46, 1945 (2010).
N. Bharat and P.S.C. Bose, Int. J. Metalcast. 17, 2849 (2023).
E. Recep, K. Ertan, and D. Mert, Ceram. Int. 48, 5338 (2022).
G.N. Ma, D. Wang, Z.Y. Liu, B.L. Xiao, and Z.Y. Ma, Mater. Charact. 158, 109966 (2019).
A.J. Kulkarni, K. Krishnamurthy, S.P. Deshmukh, and R.S. Mishra, J. Mater. Res. 19, 2765 (2011).
J.Y. He, H. Wang, H.L. Huang, X.D. Xu, M.W. Chen, Y. Wu, X.J. Liu, T.G. Nieh, K. An, and Z.P. Lu, Acta Mater. 102, 187 (2016).
N. Tian, X. Jiang, Y.Z. Zhang, Z.J. Zeng, T.S. Wang, G. Zhao, and G.W. Qin, Materials 15, 5951 (2022).
Y.M. Ding, L. Chang, B.X. Guo, J. Ding, X.G. Chen, Y. Tang, K.H. Song, and X.C. Xia, Mater. Res. Express 9, 026507 (2022).
Y.F. Wang, Y.L. Lu, S.Y. Zhang, H.P. Zhang, H. Wang, and Z. Chen, J. Alloys Compd. 885, 161028 (2021).
M.J. Yang, A. Orekhov, Z.Y. Hu, M. Feng, S.B. Jin, G. Sha, K. Li, V. Samaee, M. Song, Y. Du, T.G. Van, and D. Schryvers, Acta Mater. 220, 117310 (2021).
H.K. Ahn and C.H. Yu, Met. Mater. Int. 7, 1 (2001).
U. Cocen, K. Onel, and I. Ozdemir, Compos. Sci. Technol. 57, 801 (1997).
K.K. Chawla, A.H. Esmaeili, A.K. Datye, and A.K. Vasudevan, Scr. Metall. Mater. 25, 1315 (1991).
S.Z. Zhu, D. Wang, B.L. Xiao, and Z.Y. Ma, Compos. Part B 236, 109851 (2022).
M. Zhao, G.H. Wu, and L.T. Jiang, J. Mater. Sci. 39, 1759 (2004).
Y. Cui, T.Z. Jin, L.G. Cao, and F.B. Liu, J. Alloys Compd. 681, 233 (2016).
T. Yildiz, N. Kati, and A.K. Gür, J. Alloys Compd. 737, 8 (2018).
R.H. Dong, W.S. Yang, Z.H. Yu, P. Wu, M. Hussain, L.T. Jiang, and G.H. Wu, J. Alloys Compd. 649, 1037 (2015).
P.J. Mane and K.L. Vishnu, Proc. Eng. 97, 642 (2014).
M. Song, X. Li, and K.H. Chen, Metall. Mater. Trans. A 38, 638 (2007).
F. Ozturk, A. Sisman, S. Toros, S. Kilic, and R.C. Picu, Mater. Des. 31, 972 (2010).
W. Xue, L.T. Jiang, B. Zhang, D. Jing, T. He, G.Q. Chen, Z.Y. Xiu, and G.H. Wu, Mater. Charact. 163, 110305 (2020).
J. Sun, G.H. Chen, B.H. Wang, G.D. Chen, and W.M. Tang, J. Mater. Eng. Perform. 28, 2697 (2019).
Y.W. Yan, L. Geng, and D.Y. Liu, Int. J. Mod. Phys. B 23, 1455 (2009).
Z. Xiao, Y.J. Huang, C.X. Chen, Z. Li, S. Gong, Y.X. Huang, C. Zhang, and X.X. Zhang, J. Alloys Compd. 781, 490 (2019).
X.F. Wang, G.H. Wu, D.L. Sun, C.J. Qin, and Y.L. Tian, Mater. Lett. 58, 333 (2004).
W.C. Yang, M.P. Wang, Y.L. Jia, and R.R. Zhang, Metall. Mater. Trans. A 42, 2917 (2011).
B. Li, B.H. Luo, K.J. He, L.Z. Zeng, W.L. Fan, and Z.H. Bai, J. Alloys Compd. 649, 495 (2015).
X.Z. Zhang, T.J. Chen, and Y.H. Qin, Mater. Des. 99, 182 (2016).
X.D. Liu, P.C. Zhang, Q.D. Xu, S.X. He, Z.Y. Dou, and H.J. Wang, J. Alloys Compd. 764, 460 (2018).
D. Aldun, P. Martin, and J. Sun, J. Mater. Eng. Perform. 1, 615 (1992).
J.C. Lee, J.I. Lee, and H.I. Lee, J. Mater. Sci. Lett. 15, 1539 (1996).
N.P. Cheng, S.M. Zeng, and Z.Y. Liu, J. Mater. Process. Technol. 202, 27 (2008).
I. Dutta, S.M. Allen, and J.L. Hafley, Metall. Trans. A 22, 2553 (1991).
C.G. Li, W. Zeng, Y.H. Xie, J. Wang, J.M. Liang, R.E. Loge, and D.L. Zhang, Mater. Sci. Eng. A 778, 139126 (2020).
Acknowledgements
This work was financially supported by National Key R&D Program of China (2022YFB3707402).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Cao, L., Zhu, M., Yang, Y. et al. Effect of Aging Treatment on the Mechanical Properties of 45 vol.% SiCp/6061Al Composite. JOM (2024). https://doi.org/10.1007/s11837-024-06581-8
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s11837-024-06581-8