Abstract
A cobalt-based alloy coating was prepared on the surface of 300 M steel using magnetic field-assisted laser cladding technology. The effects of different frequencies of an alternating magnetic field on the properties of the coating, such as the microstructure, phase characteristics, mechanical properties, thermal stress, and wear and corrosion resistance were investigated. The results showed that the electromagnetic field optimized the microstructure of the coating, and the microstructural refinement was most significant at a magnetic field of 65 Hz. As the magnetic field frequency increased, the degree of microstructural refinement decreased. Modification of the magnetic field frequency did not produce any change in the phase composition of the laser cladding coating. However, the application of a magnetic field reduces the thermal expansion coefficient and elastic modulus of the coating, thus decreasing its thermal stress. The laser cladding coating formed in a magnetic field exhibited enhanced resistance to wear and corrosion. In particular, the coating formed in a magnetic field with a frequency of 65 Hz exhibited a lower friction coefficient and less surface plastic deformation. Further, the corrosion resistance of the coating improved significantly owing to the magnetic field effect, leading to a substantial improvement in the mechanical performance of the laser cladding coatings.
Similar content being viewed by others
References
A.A. Siddiqui, and A.K. Dubey, Opt. Laser Technol. 134, 106619 (2021).
L. Zhu, P. Xue, Q. Lan, G. Meng, Y. Ren, Z. Yang, P. Xu, and Z. Liu, Opt. Laser Technol. 138, 106915 (2021).
F. Zhao, T. Guo, Y. Zhang, X. Wei, R. Zhang, X. Nan, K. Dong, and D. Hu, Steel Res. Int. 94(1), 2200398 (2023).
Y. Xie, W. Chen, L. Liang, B. Huang, and J. Zhuang, Weld. World. 66, 1551 (2022).
C. Li, D. Zhang, X. Gao, H. Gao, and X. Han, Weld. World. 66, 423 (2022).
K. Qi, Y. Yang, G. Hu, X. Lu, and J. Li, Surf. Coat. Technol. 397, 125983 (2020).
H. Wang, M. Zhang, R. Sun, S. Cui, and J. Mo, J. Mater. Process. Technol. 319, 118078 (2023).
Q. Zhang, Q. Wang, B. Han, M. Li, C. Hu, and J. Wang, J. Alloys Compd. 947, 169517 (2023).
H.Z. Wang, Y.H. Cheng, J.Y. Yang, Q.Q. Wang, and J. Non-Cryst, Solids. 550, 120351 (2020).
Y.J. Tian, and M. Pang, J. Mater. Sci. 58, 9038 (2023).
Y. Liu, Y. Ding, L. Yang, R. Sun, T. Zhang, and X. Yang, J. Manuf. Process. 66, 341 (2021).
T. Yu, L. Yang, Y. Zhao, J. Sun, and B. Li, Opt. Laser Technol. 108, 321 (2018).
C. Ding, X. Cui, J. Jiao, and P. Zhu, Materials 11, 2401 (2018).
G. Bidron, A. Doghri, T. Malot, F. Fournier-dit-Chabert, M. Thomas, and P. Peyre, J. Mater. Process. Technol. 277, 116461 (2020).
G. Li, Z. Wang, L. Yao, D. Xie, and G. Chen, Surf. Coat. Technol. 445, 128732 (2022).
Q. Wang, L.L. Zhai, L. Zhang, J.W. Zhang, and C.Y. Ban, J. Mater. Res. Technol. 17, 2145 (2022).
L.L. Zhai, C.Y. Ban, and J.W. Zhang, Opt. Laser Technol. 114, 81 (2019).
K. Huo, J. Zhou, F. Dai, and J. Xu, Appl. Surf. Sci. 545, 149078 (2021).
T.A. El-Bassyouni, J. Jpn. Inst. Light Met. 33(12), 733 (1983).
L.L. Zhai, C.Y. Ban, and J.W. Zhang, Surf. Coat. Technol. 358, 531 (2019).
L. Zhai, Q. Wang, J. Zhang, and C. Ban, Ceram. Int. 45(14), 16873 (2019).
D.D.L. Chung, and M. Ozturk, J. Build. Eng. 52, 104393 (2022).
H.H. Liu, L.B. Wang, W.J. Liu, L.Y. Li, and J.F. Yue, Int. J. Adv. Manuf. Technol. 97, 3459 (2018).
T. Zhang, J. Zhou, J. Lv, X. Meng, P. Li, and S. Huang, J. Mater. Process. Technol. 307, 117658 (2022).
Y. Zhang, Z. Zeng, L. Yao, L. Qiao, L. Yin, and Y. Lu, Int. J. Appl. Electrom 53, 283 (2017).
P. Waldow, and I. Wolff, IEEE Trans. Microwave Theory Tech 33, 1076 (1985).
K. Qi, Y. Yang, W. Liang, K. Jin, and L. Xiong, Surf. Coat. Technol. 423, 127575 (2022).
A. Leyland, and A. Matthews, Wear 246, 1 (2000).
R.A. Miller, and C.E. Lowell, Thin Solid Films 95, 265 (1982).
F. Liu, X. Lin, M. Song, K. Song, F. Wang, Q. Li, Y. Han, and W. Huang, Steel Res. Int. 88, 1 (2017).
Q. Guo, S. Chen, M. Wei, J. Liang, C. Liu, and M. Wang, J. Mater. Eng. Perform. 29, 6439 (2020).
M. Masanta, S.M. Shariff, and A.R. Choudhury, Mat. Sci. Eng A-Struct. 528, 5327 (2011).
H. Wu, S. Zhang, C.L. Wu, C.H. Zhang, X.Y. Sun, and X.L. Bai, Surf. Coat. Technol. 460, 129425 (2019).
J. Yang, F. Wu, B. Bai, G. Wang, L. Yang, S. Zhou, and J. Lei, Surf. Coat. Technol. 381, 125215 (2020).
Acknowledgements
This work was financially supported by Shandong Provincial Natural Science Foundation, China (ZR2023QE084) and the doctoral fund of Shandong Jianzhu University, Shandong province, China.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
We declare that we do not have any commercial or associative interests that represent a conflict of interest in connection with the submitted work.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Qi, K., Jiang, L. Magnetic Field-Assisted Laser Cladding of Cobalt-Based Alloy on 300 M Steel. JOM 76, 238–249 (2024). https://doi.org/10.1007/s11837-023-06161-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11837-023-06161-2