Laser Surface Modification of Single-Crystal Nickel-Based Superalloy: Geometry, Microstructure, Crack Morphology, and Microhardness

  • Original Research Article
  • Published:
Journal of Materials Engineering and Performance Aims and scope Submit manuscript

Abstract

The present work investigates the surface modification of a second-generation, SX nickel-based superalloy by using a continuous wave laser with various laser powers under the conductive mode of heat penetration. The aim was to reduce the surface strength to improve the machinability. The results show that the laser surface modified (LSM) geometry and their surface irregularities increase with an increase in laser power. The cross section of the LSM geometry under lower powers is semi-elliptical in shape, whereas it becomes a top-hat shape under higher laser powers. Fine dendrites of around 10 µm with various morphologies are formed in the LSM geometry. The dendrite size increases with an increase in laser power except at the highest laser power. The LSM geometry consists of longitudinal and transverse cracks along the scanning direction. The longitudinal cracks are formed near the centerline at lower laser powers, whereas the transverse cracks are formed at a faraway distance from the centerline at higher laser powers. The longitudinal cracks have vertical cracking and transverse cracks have zig-zagged cracking beneath the surface. The total crack length increases with an increase in laser power. The LSM interface consists of dense micropores and microcracks at the inter-dendric region. However, the LSM region consists of lesser microsegregation and fine dendrites than the base metal, its microhardness is lower than the base metal due to the formation of laser-induced defects.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13
Fig. 14
Fig. 15
Fig. 16
Fig. 17
Fig. 18
Fig. 19
Fig. 20

Similar content being viewed by others

References

  1. T.M. Pollock and S. Tin, Nickel-Based Superalloys for Advanced Turbine Engines: Chemistry, Microstructure, and Properties, J. Propuls. Power, 2006, 22, p 361–374.

    Article  CAS  Google Scholar 

  2. R.C. Roger, The Superalloys: Fundamentals and Applications, Cambridge University Press, Cambridge, 2006.

    Google Scholar 

  3. R. Arunachalam and M.A. Mannan, Machinability of Nickel-Based High Temperature Alloys, Mach. Sci. Technol., 2000, 4(1), p 127–168.

    Article  CAS  Google Scholar 

  4. W. Akhtar, J. Sun, P. Sun, W. Chen, and Z. Saleem, Tool Wear Mechanisms in the Machining of Nickel Based Super-Alloys: A Review, Front. Mech. Eng., 2014, 9(2), p 106–119.

    Article  Google Scholar 

  5. M. Anderson, R. Patwa, and Y.C. Shin, Laser-Assisted Machining of Inconel 718 with an Economic Analysis, Int. J. Mach. Tools Manuf., 2006, 46(14), p 1879–1891.

    Article  Google Scholar 

  6. A. Onyszko, K. Kubiak, and J. Sieniawski, Turbine Blades of the Single Crystal Nickel Based CMSX-6 Superalloy, J. Achiev. Mater. Manuf. Eng., 2009, 32(1), p 66–69.

    Google Scholar 

  7. P.K. Samantaroy, S. Girija, R. Kaul, and U.K. Mudali, Enhancement of Corrosion Resistance of Nickel Based Superalloys by Laser Surface Melting, Surface Eng., 2013, 29(7), p 522–530.

    Article  CAS  Google Scholar 

  8. S. Ruppik, F. Becker, F.-P. Grundmann, W. Rath, and U. Hefter, High-Power Disk and Fiber Lasers: A Performance Comparison, Solid State Lasers XXI: Technol. Devices, 2012, 8235, p 82350V.

    Google Scholar 

  9. T.D. Anderson, J.N. DuPont, and T. DebRoy, Origin of Stray Grain Formation in Single-Crystal Superalloy Weld Pools from Heat Transfer and Fluid Flow Modeling, Acta Mater., 2010, 58(4), p 1441–1454.

    Article  CAS  Google Scholar 

  10. Y.J. Liang and H.M. Wang, Origin of Stray-Grain Formation and Epitaxy Loss at Substrate during Laser Surface Remelting of Single-Crystal Nickel-Base Superalloys, Mater. Des., 2016, 102, p 297–302. https://doi.org/10.1016/j.matdes.2016.04.051

    Article  CAS  Google Scholar 

  11. A. Basak, S. Holenarasipura Raghu, and S. Das, Microstructures and Microhardness Properties of CMSX-4® Additively Fabricated Through Scanning Laser Epitaxy (SLE), J. Mater. Eng. Perform., 2017, 26(12), p 5877–5884.

    Article  CAS  Google Scholar 

  12. B. Rottwinkel, C. Nölke, S. Kaierle, and V. Wesling, Laser Cladding for Crack Repair of CMSX-4 Single-Crystalline Turbine Parts, Lasers Manuf. Mater. Process., 2017, 4(1), p 13–23.

    Article  Google Scholar 

  13. Z. Zhou, L. Huang, Y. Shang, Y. Li, L. Jiang, and Q. Lei, Causes Analysis on Cracks in Nickel-Based Single Crystal Superalloy Fabricated by Laser Powder Deposition Additive Manufacturing, Mater. Des., 2018, 160, p 1238–1249. https://doi.org/10.1016/j.matdes.2018.10.042

    Article  CAS  Google Scholar 

  14. R. Korsmik, O. Klimova-Korsmik, E. Valdaytseva, and I. Udin, Investigation of Cracking Causes during Multi-Pass Laser Cladding of Heat-Resistant Single Crystal Nickel Alloy, Procedia CIRP, 2020, 94, p 314–319. https://doi.org/10.1016/j.procir.2020.09.059

    Article  Google Scholar 

  15. K. Harris, G.L. Erickson, R.E. Schwer, F.D.J., and W.J.R. “Process and Alloy Optimization for CMSX-4 Superalloy Single Crystal Airfoils High Temperature Materials for Power Engineering,” Proc. Cost Conf. Liege 24-26 September ed Bachelet E. et al (ed), 1990.

  16. A. Szczotok and R. Przeliorz, Phase Transformations in CMSX-4 Nickel-Base Superalloy, IOP Conf. Ser. Mater. Sci. Eng., 2012, 35(1), p 012005.

    Article  Google Scholar 

  17. M.S.A. Karunaratne, S. Kyaw, A. Jones, R. Morrell, and R.C. Thomson, Modelling the Coefficient of Thermal Expansion in Ni-Based Superalloys and Bond Coatings, J. Mater. Sci., 2016, 51(9), p 4213–4226.

    Article  CAS  Google Scholar 

  18. T. Matsushita, H.J. Fecht, R.K. Wunderlich, I. Egry, and S. Seetharaman, Studies of the Thermophysical Properties of Commercial CMSX-4 Alloy, J. Chem. Eng. Data., 2009, 54(9), p 2584–2592.

    Article  CAS  Google Scholar 

  19. K. Harris, B.W. Jacqueline, Improved Single Crystal Superalloys, CMSX-4 and CMSX-486, in: Green, K.A., Pollock, T.M., Harada, H., Howson, T.E., Reed, R.C., Schirra, J.J., Walston, S., (Eds.), Superalloys 2004, TMS, pp. 45- 52.

  20. Rofin Fiber Laser System, FL-010 operating manual, 2014. Coherent, Inc. Santa Clara, USA.

  21. C. Qiu, C. Panwisawas, M. Ward, H.C. Basoalto, J.W. Brooks, and M.M. Attallah, On the Role of Melt Flow into the Surface Structure and Porosity Development during Selective Laser Melting, Acta Mater., 2015, 96, p 72–79.

    Article  CAS  Google Scholar 

  22. W.M. Steen and J. Mazumder, “Laser Material Processing: Fourth Edition”, Laser Material Processing, 4th ed. Springer, London, 2010.

    Book  Google Scholar 

  23. S. Gobbi, L. Zhang, J. Norris, K.H. Richteff, and J.H. Loreau, High Powder CO2 and Nd-Yag Laser Welding of Wrought Inconel 718, J. Mater. Process Technol., 1996, 56, p 333–345.

    Article  Google Scholar 

  24. N.J. Grant, “Rapid-Solidification-III-Mehrabian-Cohen-83-2758,” Claitor’s Publication Division, 1978, p 1–712.

  25. S.R. Nandam, A. Venugopal Rao, A.A. Gokhale, and S.S. Joshi, Experimental Study on Laser-Induced Surface Damage of a Single-Crystal Nickel-Based Superalloy Under Continuous Wave Fiber Laser Scanning Process, J. Eng. Mater. Technol., 2022 https://doi.org/10.1115/1.4054228

    Article  Google Scholar 

  26. K.R. Vishwakarma, N.L. Richards, and M.C. Chaturvedi, Microstructural Analysis of Fusion and Heat Affected Zones in Electron Beam Welded ALLVAC® 718PLUSTM Superalloy, Mater. Sci. Eng., A, 2008, 480(1–2), p 517–528.

    Article  Google Scholar 

  27. Standard Test Method for Microindentation Hardness of Materials, E 384, ASTM International, 2017, doi:https://doi.org/10.1520/E0384-17

Download references

Acknowledgments

The authors wish to extend their gratitude to Director, DMRL for his encouragement. The authors are thankful to Prof. Deepak Marla, IIT Bombay for his valuable insights and discussions. The authors also express their gratitude to the officers and staff of DSG, MEG, SFAG, and EMG of DMRL for their support. Additionally, they thank Dr. P. Mastanaiah, Scientist-F, SFD of DOE, DRDL and his team, for their support in carrying out the LSM experiments. Finally, the authors acknowledge the financial assistance provided by Defence Research and Development Organization (DRDO), New Delhi.

Author information

Authors and Affiliations

  1. Department of Mechanical Engineering, IIT Bombay, Powai, Mumbai, India

    Srinivasa Rao Nandam, Amol A. Gokhale & Suhas S. Joshi

  2. Defence Metallurgical Research Laboratory (DMRL), DRDO, Kanchanbagh, Hyderabad, India

    Srinivasa Rao Nandam & A. Venugopal Rao

  3. Department of Mechanical Engineering, IIT Indore, Simrol, Indore, India

    Suhas S. Joshi

Authors
  1. Srinivasa Rao Nandam
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. A. Venugopal Rao
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Amol A. Gokhale
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Suhas S. Joshi
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Srinivasa Rao Nandam.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Nandam, S.R., Rao, A.V., Gokhale, A.A. et al. Laser Surface Modification of Single-Crystal Nickel-Based Superalloy: Geometry, Microstructure, Crack Morphology, and Microhardness. J. of Materi Eng and Perform (2023). https://doi.org/10.1007/s11665-023-08482-4

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1007/s11665-023-08482-4

Keywords

Search

Navigation