Abstract
The effect of intercritical annealing at Ac1, Ac1f, and Ac3 temperatures followed by water quenching was studied on the microstructure and mechanical properties of a 0.035C-0.27Mn low-carbon steel. During short-term holding at Ac1 and Ac1f, some pearlite remained after quenching and the yield-point phenomenon was still detectable, which was related to the formation of small amount of martensite inside pearlite colonies and on ferrite grain boundaries with marginal effect on the surrounding ferrite phase. By increasing holding time at Ac1f, pearlite disappeared and DP microstructures were achieved with the disappearance of the yield-point phenomenon and the enhancement of the work-hardening capacity. At long holding times, however, the mechanical properties deteriorated mainly due to the coarsening of martensitic islands and disappearance of dynamic strain aging (Portevin–Le Chatelier) effect at room temperature.
Similar content being viewed by others
References
C.C. Tasan, M. Diehl, D. Yan, M. Bechtold, F. Roters, L. Schemmann, C. Zheng, N. Peranio, D. Ponge, M. Koyama, K. Tsuzaki, and D. Raabe, An Overview of Dual-Phase Steels: Advances in Microstructure-Oriented Processing and Micromechanically Guided Design, Ann. Rev. Mater. Res., 2015, 45, p 19.1–19.41
W. Bleck, S. Papaefthymiou, and A. Frehn, Microstructure and Tensile Properties in Dual Phase and Trip Steels, Steel Res. Int., 2004, 75, p 704–710
U. Prahl, S. Papaefthymiou, V. Uthaisangsuk, W. Bleck, J. Sietsma, and S. van der Zwaag, Micromechanics-Based Modelling of Properties and Failure of Multiphase Steels, Comput. Mater. Sci., 2007, 39, p 17–22
C. Thomser, V. Uthaisangsuk, and W. Bleck, Influence of Martensite Distribution on the Mechanical Properties of Dual Phase Steels: Experiments and Simulation, Steel Res. Int., 2009, 80, p 582–587
A. Kalhor and H. Mirzadeh, Tailoring the Microstructure and Mechanical Properties of Dual Phase Steel Based on the Initial Microstructure, Steel Res. Int., 2017, 88, p 1600385
Z. Nasiri and H. Mirzadeh, Enhancement of Work-Hardening Behavior of Dual Phase Steel by Heat Treatment, Materialwiss. Werkstofftech., 2018, 49, p 1081–1086
M. Alibeyki, H. Mirzadeh, and M. Najafi, Fine-Grained Dual Phase Steel Via Intercritical Annealing of Cold-Rolled Martensite, Vacuum, 2018, 155, p 147–152
S. Ghaemifar and H. Mirzadeh, Refinement of Banded Structure Via Thermal Cycling and Its Effects on Mechanical Properties of Dual Phase Steel, Steel Res. Int., 2018, 89, p 1700531
R.G. Davies, Influence of Martensite Composition and Content on the Properties of Dual Phase Steels, Metall. Trans. A, 1978, 9, p 671–679
M. Alibeyki, H. Mirzadeh, M. Najafi, and A. Kalhor, Modification of Rule of Mixtures for Estimation of the Mechanical Properties of Dual-Phase Steel, J. Mater. Eng. Perform., 2017, 26, p 2683–2688
G.R. Speich, V.A. Demarest, and R.L. Miller, Formation of Austenite During Intercritical Annealing of Dual-Phase Steels, Metall. Trans. A, 1981, 12, p 1419–1428
F.L.G. Oliveira, M.S. Andrade, and A.B. Cota, Kinetics of Austenite Formation During Continuous Heating in a Low Carbon Steel, Mater. Charact., 2007, 58, p 256–261
F. Najafkhani, H. Mirzadeh, and M. Zamani, Effect of Intercritical Annealing Conditions on Grain Growth Kinetics of Dual Phase Steel, Metals Mater. Int., 2019. https://doi.org/10.1007/s12540-019-00241-2
B. Pawłowski, Critical Points of Hypoeutectoid Steel-Prediction of the Pearlite Dissolution Finish Temperature Ac1f, J. Achiev. Mater. Manuf. Eng., 2011, 49, p 331–337
M. Zamani, H. Mirzadeh, and H.M. Ghasemi, Mechanical Properties and Fracture Behavior of Intercritically Annealed AISI, 4130 Chromoly Steel, Mater. Res. Express, 2018, 5, p 066548
R. Esterl, M. Sonnleitner, and R. Schnitzer, Microstructural Analysis of the Recrystallization Behavior of Low Alloyed Steels, Steel Res. Int., 2019, 90, p 1800500 (in press)
M. Maleki, H. Mirzadeh, and M. Zamani, Effect of Intercritical Annealing on Mechanical Properties and Work-Hardening Response of High Formability Dual Phase Steel, Steel Res. Int., 2018, 89, p 1700412
M. Nouroozi, H. Mirzadeh, and M. Zamani, Effect of Microstructural Refinement and Intercritical Annealing Time on Mechanical Properties of High-Formability Dual Phase Steel, Mater. Sci. Eng. A, 2018, 736, p 22–26
M. Zamani, H. Mirzadeh, and M. Maleki, Enhancement of Mechanical Properties of Low Carbon Dual Phase Steel Via Natural Aging, Mater. Sci. Eng. A, 2018, 734, p 178–183
H.Y. Song, H.H. Lu, H.T. Liu, H.Z. Li, D.Q. Geng, R.D.K. Misra, Z.Y. Liu, and G.D. Wang, Microstructure and Texture of Strip Cast Grain-Oriented Silicon Steel after Symmetrical and Asymmetrical Hot Rolling, Steel Res. Int., 2014, 85, p 1477–1482
H. Preßlinger, M. Mayr, E. Tragl, and C. Bernhard, Assessment of the Primary Structure of Slabs and the Influence on Hot- and Cold-Rolled Strip Structure, Steel Res. Int., 2006, 77, p 107–115
S. Ghaemifar and H. Mirzadeh, Enhanced Mechanical Properties of Dual Phase Steel by Repetitive Intercritical Annealing, Can. Metall. Q., 2017, 56, p 459–463
S.W. Thompson and P.R. Howell, Factors Influencing Ferrite/Pearlite Banding and Origin of Large Pearlite Nodules in a Hypoeutectoid Plate Steel, Mater. Sci. Technol., 1992, 8, p 77–86
S. Deldar, H. Mirzadeh, and M.H. Parsa, Prevention of Surface Hot Shortness, Development of Banded Structure, and Mechanical Properties of Hot Rolled Cu-Bearing Steel, Eng. Fail. Anal., 2016, 68, p 132–137
H. Mirzadeh, M. Alibeyki, and M. Najafi, Unraveling the Initial Microstructure Effects on Mechanical Properties and Work-Hardening Capacity of Dual-Phase Steel, Metall. Mater. Trans. A, 2017, 48, p 4565–4573
E.O. Hall, The Deformation and Ageing of Mild Steel: III, Discussion of Results, Proc. Phys. Soc. Lond. Sect. B, 1951, 64, p 747–753
T.L. Russell, D.S. Wood, and D.S. Clark, The Influence of Grain Size on the Yield Phenomenon in Steel, Acta Metall., 1961, 9, p 1054–1063
P.H. Chang and A.G. Preban, The Effect of Ferrite Grain Size and Martensite Volume Fraction on the Tensile Properties of Dual Phase Steel, Acta Metall., 1985, 33, p 897–903
A.N. Holden and J.H. Hollomon, Homogeneous Yielding of Carburized and Nitrided Single Iron Crystals, J. Metals, 1949, 1, p 179–185
E.O. Hall, Yield Point Phenomena in Metals and Alloys, Plenum Press, New York, 1970
S. Nikkhah, H. Mirzadeh, and M. Zamani, Fine Tuning the Mechanical Properties of Dual Phase Steel via Thermomechanical Processing of Cold Rolling and Intercritical Annealing, Mater. Chem. Phys., 2019, 230, p 1–8
F. Jamei, H. Mirzadeh, and M. Zamani, Synergistic Effects of Holding Time at Intercritical Annealing Temperature and Initial Microstructure on the Mechanical Properties of Dual Phase Steel, Mater. Sci. Eng. A, 2019, 750, p 125–131
S. Saadatkia, H. Mirzadeh, and J.M. Cabrera, Hot Deformation Behavior, Dynamic Recrystallization, and Physically-Based Constitutive Modeling of Plain Carbon Steels, Mater. Sci. Eng. A, 2015, 636, p 196–202
H. Mirzadeh, J.M. Cabrera, J.M. Prado, and A. Najafizadeh, Hot Deformation Behavior of a Medium Carbon Microalloyed Steel, Mater. Sci. Eng. A, 2011, 528, p 3876–3882
B. Pourbahari, H. Mirzadeh, M. Emamy, and R. Roumina, Enhanced Ductility of a Fine-Grained Mg–Gd–Al–Zn Magnesium Alloy by Hot Extrusion, Adv. Eng. Mater., 2018, 20, p 1701171
N.K. Balliger and T. Gladman, Work Hardening of Dual-Phase Steels, Metal Sci., 1981, 15, p 95–108
A. Portevin and F. Le Chatelier, Sur un phénomène observé lors de l’essai de traction d’alliages en cours de transformation, Comptes Rendus de l’Académie des Sciences Paris, 1923, 176, p 507–510
G. Krauss, Martensite in Steel: Strength and Structure, Mater. Sci. Eng. A, 1999, 273–275, p 40–57
W.C. Leslie and R.J. Sober, The Strength of Ferrite and of Martensite as Functions of Composition, Temperature, and Strain Rate, ASM Trans. Q., 1967, 60, p 459–484
M.J. Roberts and W.S. Owen, Unstable Flow in Martensite and Ferrite, Metall. Trans., 1970, 1, p 3203–3213
Acknowledgments
The authors would like to greatly thank the members of the Advanced Steels and Thermomechanically Processed Engineering Materials Laboratory for their help and support. Financial support by the University of Tehran is also gratefully acknowledged.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Maleki, M., Mirzadeh, H. & Zamani, M. Effect of Intercritical Annealing Time at Pearlite Dissolution Finish Temperature (Ac1f) on Mechanical Properties of Low-Carbon Dual-Phase Steel. J. of Materi Eng and Perform 28, 2178–2183 (2019). https://doi.org/10.1007/s11665-019-04009-y
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-019-04009-y