Abstract
This research aims to study the effect of accelerated weathering conditions on the photodegradation characteristics for fibrillar silicate clay-filled Polypropylene (PP) nanocomposites in the presence of metallocene linear low density polyethylene (m-LLDPE). Silane-treated attapulgite (ATP) clay along with ethylene octene elastomer-grafted maleic anhydride (POE-g-MAH) was used to compatibilize both blend and nanocomposite system. The result showed that developed PP/m-LLDPE nanocomposites displayed good UV resistance with little change in retained stress-at-break and elongation-at-break values. Balanced loss of toughness values noted maintaining higher fracture toughness values for nanocomposites containing 5 phr ATP clay. Infrared analysis was used to detect progress of degradation followed by change in carbonyl index revealed predominated chain scission in late irradiation, while crosslinking was dominant for initial irradiation period. An increase in crystallinity during UV exposure (chemi-crystallization) was detected with exposure time for all compositions and virtually independent of initial structure of the polymer. The highest value of crystallization observed for PP and the lowest one for nanocomposites containing 5 phr of ATP clay revealed good oxidation stability. Surface morphology revealed induced degradation throughout cross-section of PP, while severity of the surface degradation was significantly reduced for developed nanocomposites.
Similar content being viewed by others
Reference
L. Mingguang, H. Richard, and E. Michael, Correlation of Physiochemical Changes in UV-Exposed Polyethylene Films Containing Various UV Stabilizers, Polym. Degrad. Stab., 1995, 49, p 151–161
A. Valenza and F.P.L. Mantia, Recycling of Polymer Waste: Part I-Photooxidised Polypropylene, Polym. Degrad. Stab., 1987, 19, p 135–146
A. Rivaton, S. Cambon, and J.L. Gardette, Radiochemical Ageing of Ethylene Propylene Diene Elastomers. 4. Evaluation of Some Anti-Oxidants, Polym. Degrad. Stab., 2006, 91, p 136–143
J.R. White and A. Turnbull, Weathering of Polymers: Mechanism of Degradation and Stabilization, Testing Strategies and Modeling, J. Mater. Sci., 1994, 29, p 13–584
C. Sadrmohaghegh, G. Scott, and E. Setoudeh, Effects of Reprocessing on Polymers—Part III: Photo-Oxidation of Polyethylene-Polypropylene Blends, Polym. Degrad. Stab., 1981, 3, p 469–476
P.K. Roy, P. Surekha, C. Rajagopal, S.N. Chatterjee, and V. Choudhary, Studies on the Photo-Oxidative Degradation of LDPE Films in the Presence of Oxidised Polyethylene, Polym. Degrad. Stab., 2007, 92, p 1151–1160
S. Rouif, Radiation Cross-Linked Polymers: Recent Developments and New Applications, Nucl. Instrum. Methods Phys. Res., 2005, 236, p 68–72
M. Zhang, D.T. Lynch, and S.E. Wanke, Effect of Molecular Structure Distribution on Melting and Crystallization Behavior of 1-Butene/Ethylene Copolymers, Polymer, 2001, 42, p 3067–3075
S. Bensason, J. Minick, A. Moet, S. Chum, A. Hiltner, and E. Baer, Classification of Homogeneous Ethylene-Octene Copolymers Based on Comonomer Content, J. Polym. Sci.: Polym. Phys., 1996, 34, p 1301–1315
P. Starck, P. Lehmus, and V. Seppala, Thermal and Mechanical Analysis of Metallocene-Catalyzed Ethene-α-Olefin Copolymers: The Influence of the Length and Number of the Crystallizing Side Chains, J. Polym. Sci.: Polym. Chem., 2006, 44, p 1600–1612
C. Wang, M.C. Chu, T.L. Lin, S.M. Lai, H.H. Shih, and J.C. Yang, Microstructures of a Highly Short-Chain Branched Polyethylene, Polymer, 2001, 42, p 1733–1741
P.S. Chum, W.J. Kruper, and M.J. Guest, Materials Properties Derived from INSITE Metallocene Catalysts, Adv. Mater., 2002, 12, p 1759–1767
J. Li, R.A. Shanks, and Y.J. Long, Miscibility and Crystallization of Metallocene Polyethylene Blends with Polypropylene, J. Appl. Polym. Sci., 2003, 87, p 1179–1189
Q.Q. Ke, X.Y. Huang, P. Wei, G.L. Wang, and P.K. Jiang, Thermal, Mechanical, and Dielectric Behaviors of Crosslinked Linear Low Density Polyethylene/Polyolefin Elastomers Blends, J. Appl. Polym. Sci., 2007, 104, p 1920–1927
W. Zhong, X. Qiao, K. Sun, G. Zhang, and X.J. Chen, Polypropylene-Clay Blends Compatibilized with MAH-g-POE, J. Appl. Polym. Sci., 2006, 2006, p 2558–2564
J. Zhang, L. Wang, and Y. Zhao, Improving Performance Of Low-Temperature Hydrogenated Acrylonitrile Butadiene Rubber Nanocomposites by Using Nano-Clays, Mater. Des., 2013, 50, p 322–331
B.P. Panda, S. Mohanty, and S.K. Nayak, Plasticty/Damage Coupling in Fibrillar Silicate-Reinforced Polypropylene/Ethylene-Octene Copolymer Composite Under Strain-Controlled Loading: Correlation Between Micromechanical and Damage Behavior, J. Thermoplast. Compos. Mater., 2013. doi:10.1177/0892705713503851
N.S. Allen, M. Edge, T. Corrales, A. Childs, C.M. Liauw, and F. Catalina, Ageing and Stabilisation of Filled Polymers: An Overview, Polym. Degrad. Stab., 1998, 61, p 183–199
A. Galeski, in Polypropylene: An A–Z reference, ed. by J. Karger-Kocsis (Kluwer, Dordrecht, 1999), pp. 135–141
F.S. Qureshi, M.B. Amin, A.G. Maadhah, and S.H. Hamid, Weather Induced Degradation of Linear Low Density Polyethylene: Mechanical Properties, J. Poly. Eng., 1990, 9, p 67–84
I.A. Hussein, Melt Miscibility and Mechanical Properties of Metallocene Linear Low-Density Polyethylene Blends with High-Density Polyethylene: Influence of Comonomer Type, Polym. Int., 2005, 54, p 1330–1336
F. Benkhenafou, M. Chemingui, B. Fayolle, J. Verdu, A.K. Ferouani, and J.M. Lefebvre, Fracture Behaviour of a Polypropylene Film, Mater. Des., 2011, 32, p 1515–1519
A. Tidjani, Photooxidation of Polypropylene Under Natural and Accelerated Weathering Conditions, J. Appl. Polym. Sci., 1997, 64, p 03–2497
H. Yin and D. Chen, Hydrogen Bond Interaction in Poly(Acrylonitrile-co-methylacrylate)/Attapulgite Nanocomposites, Polym. Eng. Sci., 2010, 50, p 312–319
F.C. Chiu, H.Z. Yen, and C.E. Lee, Characterization of PP/HDPE Blend-Based Nanocomposites Using Different Maleated Polyolefins as Compatibilizers, Polym. Test., 2010, 29, p 06–397
M.S. Rabello and J.R. White, The Role of Physical Structure and Morphology in the Photodegradation Behaviour of Polypropylene, Polym. Compos., 1996, 17, p 04–691
L. Audouin, V. Langlois, J. Verdu, and J.C.M. De Bruijn, Role of Oxygen Diffusion in Polymer Ageing: Kinetic and Mechanical Aspects, J. Mater. Sci., 1994, 29, p 569–583
J.W. Gillman, Flammability and Thermal Stability Studies of Polymer Layered-Silicate (Clay) Nanocomposites, J. Appl. Clay Sci., 1999, 15, p 31–49
A.P. Gupta, U.K. Saroop, and G. Gupta, Studies on the Photo-Oxidation of PP and PP/mLLDPE Blend Systems: Thermal Physicochemical, and Mechanical Behavior, J. Appl. Polym. Sci., 2007, 106, p 917–925
W.R. Waldman and A.M. DePaoli, Thermo-Mechanical Degradation of Polypropylene, Low-Density Polyethylene and their 1:1 Blend, Polym. Degrad. Stab., 1998, 60, p 301–308
A. Riga, D. Young, G. Mlachak, and P. Kovach, Thermoanalytical Evaluation of Readily Available Reference Polymers, J. Therm. Anal. Calorim., 1997, 49, p 425–435
A.S. Araujo, V.J. Fernandes, and G.J.T. Fernandes, Thermogravimetric Kinetics of Polyethelyne Degradation Over Silicoaluminophosphate, Thermochim. Acta., 2002, 392, p 55–61
Y. Hama, K. Hamanaka, H. Matsumoto, H. Kudoh, and T. Sasuga, Inhomogeneous Degradation of Polymers Irradiated by x-Ray, Gamma-Ray and Ion-Beam as Studied by Micro-FT-IR, Radiat. Phys. Chem., 1995, 46, p 819–822
A.R. Bhattacharyya, T.V. Sreekumar, T. Liu, S. Kumar, L.M. Ericson, R.H. Hauge, and R.E. Smalley, Crystallization and Orientation Studies in Polypropylene/Single Wall Carbon Nanotube Composite, Polymer, 2003, 44, p 2373–2377
A. Hassan, M.U. Wahit, and C.Y. Chee, Mechanical and morphological properties of PP/ NR/LLDPE ternary blend-Effect of HVA-2, Polym. Test., 2003, 22, p 281–291
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Panda, B.P., Mohanty, S. & Nayak, S.K. Polyolefin Nanocomposites with Enhanced Photostability Weathering Effect on Morphology and Mechanical Properties. J. of Materi Eng and Perform 23, 3229–3244 (2014). https://doi.org/10.1007/s11665-014-1066-9
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-014-1066-9