Abstract
Simulation studies are vital to understanding solar cell performance and in optimal device design for high-efficiency solar cells. Cell performance is sensitive to many factors, including device architecture, energy band alignment at the interfaces, materials used for photogeneration, charge extraction, doping density and thickness of various layers. The role of electron transport layer (ETL) thickness and its doping density on device performance is explored in this work. As the ETL thickness is increased from 10 nm to 200 nm, both fill factor (FF) and efficiency remain high up to 40 nm, at 0.85 and 28.04%, respectively, and beyond 40 nm, they decrease gradually due to a sharp increase in series resistance, reaching zero at 200 nm. However, Jsc and Voc remained unchanged up to an ETL thickness of about 150 nm and 160 nm, respectively. These results were confirmed by contour plots of the simulated Voc, Jsc, FF and efficiency results. We observed that when ETL approached 200 nm, Jsc and Voc decreased to zero and 0.88 V, respectively. This can be attributed to very high series resistance and recombination in the cell. Donor concentration variation in the ETL from 1017/cm3 to 1020/cm3 has much less impact on Jsc, and Voc remains unchanged. However, fill factor and efficiency improved, which might be due to an increase in conductivity in the ETL. Our result shows that for an optimized device, with an AM 1.5 spectrum, a cell efficiency of 29.64% was achieved with Voc, Jsc and fill factor of 1.241 V, 28.70 mA/cm2 and 0.83, respectively.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Q. Dong, Y. Fang, Y. Shao, P. Mulligan, J. Qiu, L. Cao, and J. Huang, Science 347, 967 (2015).
A. Kooijman, L.A. Muscarella, and R.M. Williams, Appl. Sci. 9, 1678 (2019).
S. Ruhle, Sol. Energy 130, 139 (2016).
M. Ye, C. He, J. Iocozzia, X. Liu, X. Cui, X. Meng, M. Rager, X. Hong, X. Liu, and Z. Lin, J. Phys. D Appl. Phys. 50, 373002 (2017).
Y. Zhao, J. Wei, H. Li, Y. Yan, W. Zhou, D. Yu, and Q. Zhao, Nat. Commun. (2016). https://doi.org/10.1038/ncomms10228.
R.A. Belisle, W.H. Nguyen, A.R. Bowring, P. Calado, X. Li, S.J.C. Irvine, M.D. McGehee, P.R.F. Barnes, and B.C. O’Regan, Energy Environ. Sci. 10, 192 (2017).
J. Krysa, H. Krysova, Z. Hubicka, S. Kment, J. Maixner, and L. Kavan, Photochem. Photobiol. Sci. 18, 891 (2019).
H. Hu, B. Dong, H. Hu, F. Chen, M. Kong, Q. Zhang, T. Luo, L. Zhao, Z. Guo, J. Li, Z. Xu, S. Wang, D. Eder, and L. Wan, ACS Appl. Mater. Interfaces 8, 17999 (2016).
M.M. Lee, J. Teuscher, T. Miyasaka, T.N. Murakami, and H.J. Snaith, Science 338, 643 (2014).
J. Burschka, N. Pellet, S.J. Moon, R. Humphry-Baker, P. Gao, M.K. Nazeeruddin, and M. Gratzel, Nature 499, 316 (2013).
M. Seetharaman, P. Nagarjuna, P. Naresh Kumar, S.P. Singh, M. Deepa, and M.A.G. Namboothiry, Phys. Chem. Chem. Phys. 16, 24691 (2014).
H. Zhu, A.K. Kalkan, J. Hou, and S.J. Fonash, AIP Conf. Proc. 462, 309 (1999).
Y. Liu, Y. Sun, and A. Rockett, Sol. Energy Mater. Sol. Cells 98, 124 (2012).
K.L. Kearney and A.A. Rockett, J. Electrochem. Soc. 163, H598 (2016).
S.J. Fonash, J. Arch, J. Cuiffi, J. Hou, W. Howland, P.J. McElheny, A. Moquin, M. Rogosky, T. Tran, H. Zhu, and F. Rubinelli, A Manual for AMPS-1D for Windows 95/NT (Happy Valley: The Pennsylvania State University, 1997).
G.A.M. Hurkx, D.B.M. Klaassen, and M.P.G. Knuvers, IEEE Trans. Electron Devices 39, 331 (1992).
K. Yang, Solid-State Electron. 36, 321 (1993).
S. Yasar, S. Kahraman, S. Cetinkaya, S. Apaydın, I. Bilican, and I. Uluer, Optik 127, 8827 (2016).
R. Jeyakumar, A. Bag, and R. Reza Nekovei, Solar Energy 190, 104 (2019).
W.J. Yin, T.T. Shi, and Y.F. Yan, Adv. Mater. 26, 4653 (2014).
G. Xosrovashvilia and N.E. Gorjib, J. Mod. Opt. 60, 936 (2013).
Q. Zhou, D. Jiao, K. Fu, X. Wu, Y. Chen, J. Lu, and S. Yang, Sol. Energy 123, 51 (2016).
T. Minemoto and M. Murata, J. Appl. Phys. 116, 054505 (2014).
A. Poglitsch and D. Weber, J. Chem. Phys. 87, 6373 (1987).
D. Poplavskyy and J. Nelson, J. Appl. Phys. 93, 341 (2003).
H.S. Kim, C.R. Lee, J.H. Im, K.B. Lee, T. Moehl, A. Marchioro, S.J. Moon, R.H. Baker, J.H. Yum, J.E. Moser, M. Grätzel, and N.G. Park, Sci. Rep. 2, 591 (2012).
T. Leijtens, I. Ding, T. Giovenzana, J.T. Bloking, M.D. McGehee, and A. Sellinger, ACS Nano 6, 1455 (2012).
H.J. Du, W.C. Wang, and J.Z. Zhu, Chin. Phys. B 25, 108802 (2016).
L. Huang, X. Sun, C. Li, R. Xu, J. Xu, Y. Du, Y. Wu, J. Ni, H. Cai, J. Li, Z. Hu, and J. Zhang, Sol. Energy Mater. Sol. Cells 157, 1038 (2016).
T. Minemoto and M. Murata, Sol. Energy Mater. Sol. Cells 133, 8 (2015).
W.A. Laban and L. Etgar, Energy Environ. Sci. 6, 3249 (2013).
M.I. Hossain, F.H. Alharbi, and N. Tabet, Sol. Energy 120, 370 (2015).
S.D. Stranks, G.E. Eperon, G. Grancini, C. Menelaou, M.J. Alcocer, T. Leijtens, L.M. Herz, A. Petrozza, and H.J. Snaith, Science 342, 341 (2013).
L.S. Mende and M. Gratzel, Thin Solid Films 500, 296 (2006).
A. Bag, R. Radhakrishnan, R. Nekovei, and R. Jeyakumar, Solar Energy 196, 177 (2020).
J. Cui, T. Allen, Y. Wan, J. McKeon, C. Samundsett, D. Yan, X. Zhang, Y. Cui, Y. Chen, P. Verlinden, and A. Cuevasa, Sol. Energy Mater. Sol. Cells 158, 115 (2016).
P. Löper, M. Stuckelberger, B. Niesen, J. Werner, M. Filipic, S. Moon, J. Yum, M. Topic, S. De Wolf, and C. Ballif, J. Phys. Chem. Lett. 6, 66 (2015).
M. Filipic, P. Löper, B. Niesen, S. De Wolf, J. Krc, C. Ballif, and M. Topic, Opt. Express 23, A263 (2015).
A.N. Cho and N.G. Park, ChemSusChem 10, 3687 (2017).
S.S. Reddy, K. Gunasekar, J.H. Heo, S.H. Im, C.S. Kim, D.H. Kim, J.H. Moon, J.Y. Lee, M. Song, and S.H. Jin, Adv. Mater. 28, 686 (2016).
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Jeyakumar, R., Bag, A., Nekovei, R. et al. Influence of Electron Transport Layer (TiO2) Thickness and Its Doping Density on the Performance of CH3NH3PbI3-Based Planar Perovskite Solar Cells. J. Electron. Mater. 49, 3533–3539 (2020). https://doi.org/10.1007/s11664-020-08041-w
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-020-08041-w