Abstract
Eco-friendly stannic oxide nanoparticles functionalized with gallic acid (SnO2/GA NP) were synthesized and employed as a novel photocatalyst for the degradation of citalopram, a commonly prescribed antidepressant drug. SnO2/GA NP were characterized using high-resolution transmission electron microscopy, Fourier transform infrared spectroscopy, Brunauer–Emmett–Teller measurements and X-ray diffraction. A validated RP-HPLC assay was developed to monitor citalopram concentration in the presence of its degradation products. Full factorial design (24) was conducted to investigate the effect of irradiation time, pH, SnO2/GA NP loading and initial citalopram concentration on the efficiency of the photodegradation process. Citalopram initial concentration was found to be the most significant parameter followed by irradiation time and pH, respectively. At optimum conditions, 88.43 ± 0.7% degradation of citalopram (25.00 µg/mL) was obtained in 1 h using UV light (1.01 mW/cm2). Citalopram kinetics of degradation followed pseudo-first order rate with Kobs and t0.5 of − 0.037 min−1 and 18.73 min, respectively. The optimized protocol was successfully applied for treatment of water samples collected during different cleaning validation cycles of citalopram production lines. The reusability of SnO2/GA NP was studied for 3 cycles without significant loss in activity. This approach would provide a green and economic alternative for pharmaceutical wastewater treatment of organic pollutants.
Graphical abstract
Similar content being viewed by others
Introduction
Many pharmaceutical compounds have been detected in different water sources including sewage effluents, surface, ground and even drinking water (Gadipelly et al. 2014). This raised a concern about their potential risks to aquatic species, environment and human health (Carter et al. 2019). Citalopram (1-[3-(dimethylamino)propyl]-1-(4-fluorophenyl)-3H-2-benzofuran-5-carbonitrile) (CIT) is a selective serotonin reuptake inhibitor antidepressant drug (Fig. 1). It had been detected in various aquatic systems (Castillo-Zacarías et al. 2021; Giebułtowicz and Nałęcz-Jawecki 2014; Lajeunesse et al. 2012). Antidepressants have received high attention after COVID-19 pandemic which triggered the consumption of such class (Melchor-Martínez et al. 2021). Different analytical techniques were used to quantitatively determine CIT in aquatic samples. Among these methods are liquid chromatography (Sarıkaya et al. 2021), gas chromatography (Behpour et al. 2020), differential pulse voltammetry (Madej et al. 2019), tandem mass spectrometry (Evans et al. 2015) and capillary electrophoresis (Himmelsbach et al. 2006). In order to avoid undesired accumulation of CIT in aquatic environments, different treatment methods were employed such as adsorption (Ek et al. 2014; Guillossou et al. 2019; Sharifabadi et al. 2013), membrane bioreactor process (Arola et al. 2017) and gamma radiation (Bojanowska-Czajka et al. 2022). Photocatalysis is considered one of the most widely investigated advanced oxidation processes (AOPs) for removal of emerging contaminants. Photocatalytic degradation of CIT based on TiO2 nanoparticles (NP) had been reported (Jiménez-Holgado et al. 2021). However, it was limited by high recombination rate of photo-induced electronic–hole pairs produced upon ultraviolet (UV) irradiation and the relatively high cost of the photocatalyst (Han et al. 2009; Wu et al. 2015). SnO2 NP is one of the most promising photocatalysts. This could be attributed to its high oxidation potential, high photo-absorption ability, surface reactivity, chemical inertness, relative non-toxicity and long-term photochemical stability (Honarmand et al. 2019; Sun et al. 2022). Various methods had been reported for the synthesis of SnO2 NP such as hydrothermal (Akhir et al. 2019), sonochemical (Khan et al. 2017), microwave assisted methods (Sathishkumar and Geethalakshmi 2020). All the previously reported techniques had shown satisfactory synthesis outcome. However, those methods depended particularly on the use of surfactants and various toxic or hazardous chemicals. Green chemistry principles are of great interest to reduce the use of toxic methodologies for nanostructures development. Gallic acid (GA) (3,4,5 trihydroxybenzoic acid) is a naturally occurring polyphenolic antioxidant compound. It is one of the main constituents of tea leaves (Badhani et al. 2015) (Fig. S1). The use of GA for functionalization of various NP had been previously reported in a variety of applications (Lee et al. 2017; Nadim et al. 2015; Sarker et al. 2012). To the best of our knowledge, the use of SnO2 functionalized with GA as a photocatalyst in treatment of pharmaceutical wastewater has not been reported yet. Upon UV irradiation of GA, reactive oxygen species (ROS) can be generated (Benitez et al. 2005; Du et al. 2014; Luna et al. 2016; Wang et al. 2019). This would enhance the photocatalytic activity of SnO2.
Chemical structure of Citalopram
In this study, GA was used to mediate the synthesis of SnO2 NP through a green approach, using a simple and economic method. GA was used not only as a reducing agent throughout the NP synthesis but also as a stabilizing agent through functionalization of SnO2 NP. The synthesized SnO2/GA NP were characterized and then used for the treatment of pharmaceutical wastewater containing CIT. A validated RP-HPLC assay was developed for monitoring CIT degradation throughout wastewater treatment. Optimization of the photocatalytic degradation process was carried out using full factorial experimental design. The kinetics of CIT degradation was studied. Application of the optimized protocol to incurred wastewater samples, collected during the pharmaceutical cleaning process of CIT production lines, was also investigated.
Experimental
Chemicals and samples
Stannous chloride dihydrate (SnCl2.2H2O) was purchased from Loba Chemie (Mumbai, India), whereas GA and titanium (IV) oxide NP (anatase, <25 nm) were purchased from Sigma-Aldrich (USA). CIT standard (purity 98.89% ± 0.53) as well as incurred water samples were kindly supplied by Delta Pharmaceutical Industries (Egypt). Two samples were obtained at two different stages of cleaning validation process: first wash of production lines using alkaline detergent and second wash using purified water. Double distilled water was used all through the synthesis of SnO2/GA NP. All other chemicals were of HPLC grade and obtained from Sigma-Aldrich (USA).
Instruments
UV irradiation was performed using a 6 W-UV lamp with irradiation of 1.01 mW/cm2 (Vilber Lourmat, France) kept in an air-ventilated chamber. Agilent (1260 Infinity) HPLC system controlled with Chemstation software (Agilent Technologies, Germany) was used for chromatographic separations. HPLC analysis was performed using Xbridge Shield RP18 5 µm, 4.6 × 250 mm (Waters, Ireland). Fourier transform infrared (FTIR) spectroscopy was carried out using Shimadzu IRAffinity-1. TEM images of SnO2/GA NP were collected using a high-resolution transmission electron microscope (TEM 2100; JEOL, Japan). Zeta potential was measured using Zetasizer Nano ZS-ZEN 3600 (Malvern Instruments Ltd, UK). The statistical analysis and experimental design of the results were performed using Minitab, ver. 16.1.1 (Minitab Inc., USA). UV–Vis absorption spectrum was observed using Shimadzu 1650 spectrophotometer (Japan). X-ray diffraction (XRD) graph was recorded on a Bruker D8-Advance diffractometer (Bruker AXS Inc., USA). The surface area and pore size of NP were obtained from Brunauer–Emmett–Teller (BET) measurements using NOVA touch 4LX analyzer (Quantachrome, USA).
Synthesis and characterization of SnO2/GA NP
A facile green chemical approach was used for the preparation of SnO2/GA NP by co-precipitation technique as previously reported but with slight modification (Tammina et al. 2019); 0.01 M GA aqueous solution was prepared and then added dropwise to 0.01 M SnCl2.2H2O aqueous solution. The two solutions were mixed and magnetically stirred at 500 rpm under a temperature of 90 °C for 6 h. A yellow-colored precipitate was produced then washed three times with water and centrifuged at 4000 rpm for 10 min to remove any unreacted substance. The precipitate was dried at 60 °C for 2 h and calcined at 300 °C for 2 h. Control SnO2 NP were prepared and recovered using the same procedure but with replacing GA with ammonia aqueous solution until pH had reached 9.0. Then, the mixture was stirred for 1 h at 90 °C. The synthesized SnO2/GA NP were inspected for their morphology using HR-TEM. One drop of the sample was put on a copper grid, air dried then examined at 200 kV. FT-IR was used to confirm the functionalization of SnO2 NP with GA. The sample was mixed with KBr to form flattened pellets. IR spectra were examined for the characteristic bands at 400–4000 cm−1. Average zeta potential was also determined using the Zetasizer at 25 °C for 120 s. Zeta potential measurements were carried out at pH range of 5.0, 7.0 and 9.0 in order to assess the colloidal stability of the NP. XRD graph of SnO2/GA NP was recorded on a Bruker D8-Advance diffractometer with backgroundless sample holders, and the X-ray generator was operated at 40 kV and 30 mA. Surface area measurements such as surface area (m2/g), total pore volume (cc/g), average pore radius (nm) and nitrogen adsorption–desorption isotherms of the SnO2/GA NP were also evaluated based on BET theory.
Reversed-phase liquid chromatography
A previously reported HPLC assay (Skibiński and Misztal 2005) was used with some modifications so as to determine CIT in the presence of its photodegradation products. Briefly, optimal mobile phase condition was 50 mM dipotassium hydrogen phosphate buffer (pH 2.5 ± 0.1):acetonitrile (55:45%v/v). Isocratic elution was carried out at a flow rate of 1 mL/min, and CIT was detected at 239 nm. Calibration curve for CIT was constructed using standard series covering a concentration range of 0.50–25.00 µg/mL. Regression equation was obtained and used for calculation of residual CIT concentration all through the study. Validation was done according to ICH Guidelines: Q2(R1) (ICH Harmonized Tripartite Guidelines 2005). Validation parameters were determined: accuracy, precision, linearity and limit of detection. System suitability parameters were then calculated according to US Pharmacopoeia (The Unites States Pharmacopoeia and National Formulary 2011).
Photocatalytic degradation study
Preliminary studies
Standard CIT samples were prepared (50.00 µg/mL) in phosphate buffer pH 5.0, 7.0 and 9.0 and were left in dark at room temperature for 2 h to assess CIT hydrolytic stability. Then, two CIT samples (50.00 µg/mL) were prepared in phosphate buffer pH 7.0 and exposed to UV irradiation (254 nm, 1.01 mW/cm2) for 1 h in the absence and presence of SnO2/GA NP (0.50 mg/mL). For comparative purposes, same experimental conditions were applied for two CIT control samples using (i) commercially available TiO2 NP and (ii) bare SnO2 NP. To assess the effect of pH on the activity of the photocatalyst, CIT samples (50.00 µg/mL) were prepared in phosphate buffer pH 5.0 and 9.0 then exposed to UV irradiation for 1 h. Finally, all samples had been analyzed using the described HPLC assay.
Adsorption isotherm
Adsorption equilibrium experiments were performed in dark conditions using 25-mL amber vials. Aliquots of 10 mL of various initial CIT concentrations (10.00–50.00 µg/mL, pH 7.0) were kept in contact with fixed concentration of SnO2/GA NP (0.5 mg/mL) under constant magnetic stirring for 30 min. Then, the solutions were filtered and analyzed by HPLC.
Experimental design
The effects of irradiation time, pH, SnO2/GA NP loading and initial CIT concentration were studied. Two levels were randomly assigned for each of the four factors (24) either low (− 1) or high (+ 1) as presented in Table 1. Sixteen sets of experimental conditions (two-level full factorial design 24) were conducted as illustrated in Table 2. All experiments were performed at room temperature, in air ventilated cabinet while continuously magnetically stirred. Before exposure to UV irradiation, CIT and NP mixture was stirred in the dark for 30 min to achieve adsorption equilibrium. All through the study, UV irradiation of 25 mL of buffered CIT solution and SnO2/GA NP was carried out as indicated in each experiment in Table 2. At the end of the incubation period, samples were completed to volume (25 mL) and filtered through a syringe filter (0.2 µm). Samples were then analyzed using the developed RP-HPLC assay.
Kinetics of CIT photocatalytic degradation
Kinetics of CIT photocatalytic degradation reaction was studied over 1 h at 10-min intervals at the optimum set of conditions: CIT (25.00 µg/mL, pH 7.0 ± 0.1) in the presence of SnO2/GA NP (0.50 mg/mL). RP-HPLC assay was used to monitor CIT concentration gradual decrease over time.
Application to incurred samples
After one production batch of CIT tablets, cleaning of production lines was conducted according to the manufacturer’s protocols. Two washing cycles were implemented for cleaning validation. A commercially available alkaline wash solution (Alcojet ®) was used in the first cycle, followed by purified water in the second cycle. Pooled samples were collected during each washing cycle and stored at − 20 °C. Upon analysis, the pH of the samples was adjusted to 7.0, and CIT concentration was then determined. Subsequently, the samples (25 mL each) were subjected to UV irradiation in the presence of SnO2/GA NP (0.50 mg/mL) for 1 h. After the irradiation period, CIT concentration and the percent of degradation were determined.
Results and discussion
Synthesis and characterization of NP
An ecofriendly SnO2/GA NP was synthesized using a facile co-precipitation method. GA was employed as a reducing agent for SnO2. This eliminated the use of any hazardous reducing agents and reduced the generation of toxic byproducts. GA was also employed as a stabilizing agent for SnO2. The functionalized NP with GA exhibited high photocatalytic efficiency owing to the ability of GA to generate ROS such as hydrogen peroxide and hydroxyl radicals upon UV irradiation (Benitez et al. 2005; Du et al. 2014; Luna et al. 2016; Wang et al. 2019). Thus, GA enhanced the stability as well as the catalytic activity of SnO2 NP. It should be noted that allowing the reaction mixture for 4 h had only resulted in reduction of SnCl2 (Tammina et al. 2019). Increasing the synthesis time up to 6 h had resulted in surface functionalizing of SnO2 NP with GA. This came into agreement with previous literature of functionalizing metal oxides NP with carboxylic acid moieties (Lee et al. 2017; Sarker et al. 2012). Further increase of the reaction time to 8 h gave the same yield and photocatalytic activity of NP. Therefore, 6-h synthesis was chosen as optimum.
The morphology and detailed crystal structure of SnO2/GA NP were investigated using HR-TEM (Fig. 2). Results showed the formation of spherical SnO2 NP coated with GA with a mean hydrodynamic diameter of 10 ± 3.85 nm. FTIR spectrum of pure GA was compared to that of SnO2/GA NP to confirm binding between GA and SnO2 (Fig. 3). Pure GA spectrum showed a broad peak at 3282 cm−1 due to carboxylic and phenolic hydroxyl groups (–OH) stretching. A sharp peak at 1701 cm−1 was observed indicating carbonyl (C = O) stretching of COOH group. Compared to SnO2/GA NP spectrum, the broad peak of (–OH) stretching was observed at 3263 cm−1 but with remarkable decrease in intensity. This indicated the interaction of hydroxyls groups in the functionalization of SnO2. A peak at 1570 cm−1 was also observed due to C = C aromatic stretching. Peaks were also observed at 1068 and 1485 cm−1 because of C–O and C–C stretching, respectively. These results indicated the formation of SnO2/GA NP (Sarker et al. 2012). Zeta potential measurement was also used to investigate the surface charge and the colloidal stability of SnO2/GA NP. Measurements were carried out at acidic (5.0), neutral (7.0) and alkaline pH (9.0). Optimum potential was achieved at pH 7.0 (− 30.8 ± 1.5 mv) which was sufficient to avoid aggregation. As the pH increased to 9.0, the value of zeta potential decreased to − 18.5 ± 3 mv, while pH 5.0 showed the least colloidal stability with zeta potential of − 14.4 ± 0.9 mv. The high negative charge at neutral pH was sufficient enough to form an intra molecular repulsive barrier. The absorption spectra of SnO2/GA NP showed an intense absorption in the range of 220–300 nm with a peak at 260 nm corresponding to GA UV absorption (Fig. S2). The crystalline structure of the synthesized SnO2/GA NP was analyzed by XRD (Fig. 4a). Data showed diffraction peaks at 2Ɵ, and the corresponding plane coordinates were 25.19° (112), 26.95° (211), 29.72° (202), 35.56° (310), 37.14° (311), 39.49° (004), 46.90° (313). This confirmed that the main composition of the nanoparticles was SnO2 (Ma et al. 2020). Also, some peaks for GA had appeared at 2Ɵ = 15.35°, 17.23° and 21.85°. This reflected the successful modification of the surface of SnO2 NP and confirmed the functionalization of SnO2 NP with GA (Hu et al. 2013; Patil and Killedar 2021). BET analysis revealed that the surface area and pore radius were 28.35 m2/g and 1.92 nm, respectively with total pore volume of 0.72 cc/g. The high surface area of NP obtained had allowed better contact for CIT and thus high photocatalytic properties. Nitrogen adsorption–desorption isotherm showed type IV isotherm with H3 hysteresis loop which is characteristic for mesoporous materials (Fig. 4b).
Transmission electron micrograph of SnO2/GA NP
FT-IR spectra of (A) pure GA and (B) SnO2/GA NP
(A) XRD graph of SnO2/GA NP. (B) Nitrogen adsorption–desorption isotherms surface area of SnO2/GA NP
Reversed-phase liquid chromatography
A CIT photodegraded sample was prepared and used for optimization of the RP-HPLC assay. Good resolution was obtained over 5 min using the assay conditions described above. An equivalent CIT sample was prepared and had not been subjected to UV irradiation as a control sample to verify the identity of CIT and calculate the percentage degradation as well. System suitability parameters were computed according to the US Pharmacopoeia (Table 3). Validation parameters and regression equation were also summarized in Table 3.
Photocatalytic degradation study
Preliminary studies
Initially, CIT hydrolytic stability at pH 5.0, 7.0 and 9.0 was confirmed at room temperature over 2 h (data not shown). Results were in agreement to the previously reported data showing the relative stability of CIT (Kwon and Armbrust 2005). Then, CIT samples (50 µg/mL) were subjected to UV irradiation at pH 7.0 for 1 h in the absence and presence of NP. In the presence of UV light only, 29% degradation was obtained while the addition of SnO2/GA NP had increased percentage degradation to 71% (Fig. 5). In the presence of a control sample (50.00 µg/mL, pH 7.0) containing TiO2 NP as photocatalyst, only 61% degradation was noted, while in the presence of bare SnO2 NP, 49% degradation was obtained. These results showed the possible promising effect of the synthesized SnO2/GA NP. Preliminary screening of the effect of pH was carried out in the presence of NP. A relatively low (47%) degradation was obtained at pH 5.0 owing to the colloidal stability of the NP as explained earlier, while the % degradation had increased to 71% and 65% at pH 7.0 and 9.0 respectively. Therefore, pH 7.0 and 9.0 were further studied.
HPLC chromatogram of (A) CIT sample (50.00 μg/mL) not subjected to UV irradiation. (B) CIT degradation upon exposure to UV light intensity (1.01 mW/cm2) at pH 7.0 for 1 h in the absence of SnO2/GA NP. (C) CIT photocatalytic degradation upon exposure to UV light intensity (1.01 mW/cm2) at pH 7.0 for 1 h in the presence of 0.50 mg/mL SnO2/GA NP
Adsorption isotherm
Initial experiments performed for 1 h under constant magnetic stirring indicated that the adsorption equilibrium was achieved after 25 min. No further adsorption was observed after 30 min. Adsorption in dark conditions had contributed to 16.42% removal of CIT. To investigate the interaction of CIT molecules and the adsorbent surface of NP, two well-known models, Langmuir and Freundlich isotherms, were studied to describe CIT adsorption equilibrium. The Langmuir isotherm is valid for monolayer adsorption onto a surface with a finite number of identical sites (Bouafıa-Cherguı et al. 2016; Meroufel et al. 2013). It is given as the following Eq. \(1/Qe=1/Qmax+1/\left(Qmax\times {K}_{L}\right)\times 1/Ce\). Qe is the adsorbed quantity of CIT (mg/g), Ce is CIT concentration (mg/L) at the adsorption equilibrium, KL is the Langmuir adsorption constant in the dark (L/mg) and Qmax is the maximum adsorbed quantity of CIT (mg/g). Upon plotting 1/Qe against 1/Ce (Fig. 6a), a straight line was obtained, and the Langmuir isotherm provided a good fit of the data. The Freundlich isotherm equation is log Qe = log KF + 1/n log Ce. KF and n are the constants of adsorption density and adsorption intensity, respectively (Fig. 6b). The Freundlich isotherm gives no information on the monolayer adsorption density. Langmuir isotherm model was found to be slightly better for describing the adsorption equilibrium than Freundlich model (Table 4).
Adsorption isotherm of CIT on SnO2/GA NP using (A) Langmuir model and (B) Freundlich model
Experimental design
Further investigation was conducted in order to optimize the effects of (A) irradiation time, (B) SnO2/GA NP loading, (C) pH and (D) initial CIT concentration on the efficiency of CIT photodegradation. A relatively high concentration of CIT up to 50.00 µg/mL was used to cover the expected range in pharmaceutical wastewater. NP loading of 0.50 mg/mL was chosen as it is a commonly starting point in different photocatalytic procedures (Lu et al. 2019a; Mugunthan et al. 2019; Štrbac et al. 2018). Full factorial design was used to assess the relative significance of the mentioned factors, their interactions as well as the optimal set of experimental conditions for CIT photocatalytic degradation (Table 1). Samples were then analyzed in duplicate using the developed RP-HPLC assay, and the percentage degradation was shown in Table 2.
Analysis of full factorial design results was done at 95% confidence level (P 0.05) using the percentage of degradation as the response factor. The relative magnitude of the studied factors and their interactions was visualized using pareto diagram, while the direction of effects was illustrated by the normal plot of the standardized effects. In this study, irradiation time (A) was found to have a significant impact with a positive effect indicating an increase in photocatalysis at high levels, while pH (C) and initial CIT concentration (D) have a significant impact with a negative effect revealing a decrease in response at high levels of these variables (Fig. 7). It should be noted that the interactions ABC (irradiation time-catalyst-pH) showed no significant effect but with P value of 0.076 as shown in Fig. 7 and Table S1. pH 7.0 showed superior catalytic efficiency compared to pH 9.0. At neutral conditions, CIT is fully ionized with positive charge (CIT pKa = 9.78) enabling facile attraction to the negatively charged catalyst, while at pH 9.0, the drug is partially ionized, and the NP is more aggregated. In addition, increasing SnO2/GA NP loading to 1.0 mg/mL was found to be non-significant. This could suggest a plateau effect for the catalyst over a range of 0.50–1.00 mg/mL. It could be concluded that the longer the irradiation time at neutral conditions, the higher percentage of photodegradation observed (Fig. S3). The same degradation efficiency (̴ 82%) was obtained for CIT 25.00 and 50.00 µg/mL but when irradiated for 1 and 2 h respectively. This indicated that treating samples containing low initial concentrations of CIT are required to improve the economics and efficiency and of the treatment process. This was illustrated in the surface plot (Fig. S3). Contour diagram was also constructed to predict the optimum experimental region for CIT photodegradation (Fig. 8). Maximum photodegradation can be achieved at pH 7.0 using lower initial CIT concentration (25.00–30.00 μg/mL) (Fig. 8a). Similarly, Fig. 8b showed that maximum photodegradation can be obtained after 2 h at the same pH.
(A) Pareto chart of the standardized effects of single and interaction factors on CIT photodegradation. (B) Normal plot of the standardized effects of single and interaction factors on CIT photodegradation
Contour plot for pH versus (A) CIT initial concentration (hold values: UV irradiation time 1 h, SnO2/GA NP loading 0.50 mg/mL). (B) UV irradiation time (hold values: initial concentration 25.00 μg/mL, SnO2/GA NP loading 0.50 mg/mL)
Maximum photodegradation (91%) was obtained at pH 7.0 in the presence of 25.00 µg/mL CIT and 1.00 mg/mL NP in 2 h. However, 88% degradation was obtained in 1 h at the same conditions except using less NP loading 0.50 mg/mL. Therefore, increasing the irradiation time by another 1 h has minimum effect ( ̴ 3%) on the photocatalytic efficiency. In order to improve the economics of CIT photodegradation, the 1-h treatment protocol using 0.50 mg/mL NP was chosen as optimum set and was used for further investigations (Table 2).
The regression equation summarizing the experimental design is given as follows:
where Y = % degradation, A = irradiation time, B = SnO2/GA NP loading, C = pH and D = initial CIT concentration.
Analysis of variance (ANOVA) was carried out, and the results were calculated in Table S1. A lack of fit value of 0.498 was observed indicating its non-significance and an acceptable predictability of the studied model.
Upon treatment of CIT samples (25.00 µg/mL, pH 7.0) with a commercially available TiO2 NP (0.50 mg/mL) for 1 h, 76% degradation was obtained. It should be noted that a previously reported literature had used a commercially available TiO2 NP for treatment of CIT (20.00 µg/mL) in water samples. Although full degradation was reported in 30 min, a high-intensity UV lamp was used (9 mW/cm2) compared to the low energy lamp used in this study (1 mW/cm2). This indicated that the synthesized SnO2/GA NP could spare the need of high-watt UV lamps. In addition, different forms of SnO2 NP had been used as photocatalysts with acceptable degradation efficiency. However, either lengthy procedure, hazardous chemicals, high energy UV light sources were used or small molecular weight organic molecules/ dyes were used as the studied model (Table 5). Although satisfactory results were obtained in our study under UV light, the synthesized SnO2/GA NP can be further modified in the future to work under visible range for an extra economical advantage.
Kinetics of CIT photocatalytic degradation
The kinetics of CIT photocatalytic degradation was studied at optimum set of experimental conditions (25.00 µg/mL CIT, pH 7.0, 0.50 mg/mL NP, 1 h). Upon plotting ln (Ct/Co) against time, a straight line was obtained which indicated a pseudo-first order kinetics. By applying Langmuir–Hinshelwood model (Gaya and Abdullah 2008), a relatively fast kinetics profile was obtained with Kobs and t0.5 of − 0.037 min−1 and 18.73 min, respectively (Fig. 9).
Kinetics profile of CIT photodegradation with initial CIT concentration 25.00 µg/mL at pH 7.0 with 0.50 mg/mL SnO2/GA NP
Reusability of SnO2/GA NP
The capability to regenerate SnO2/GA NP was investigated. SnO2/GA (0.50 mg/mL) was added to standard CIT buffered solution (25.00 µg/mL in phosphate buffer pH 7) and UV irradiated for 1 h. Then, the sample was centrifuged, washed well with double distilled water and left to dry in air for subsequent use. The recovered SnO2/GA NP were reused in second and third cycles for photocatalytic degradation of CIT under the same experimental conditions. Minimum decrease (̴ 9%) in the photocatalytic activity was observed after three cycles (Fig. S4). Therefore, the reusability of SnO2/GA NP did not significantly affect its catalytic activity offering an economical advantage.
Application to incurred samples
Incurred samples were collected during first wash cycle of the production lines, and CIT initial concentration was 35.22 ± 0.17 μg/mL, whereas CIT initial concentration in samples collected during second wash was found to be 1.20 ± 0.01 μg/mL. The developed photocatalytic degradation was used as a treatment protocol and investigated using first wash samples. The percentage of degradation was found to be 81.44 ± 0.61% and 82.35% ± 0.42% for the incurred and control samples under the optimum conditions. The absence of significant difference revealed lack of matrix interference. Upon application of the treatment protocol to second wash sample, CIT peak was not detected owing to its relatively low concentration (less than the assay LOD). These results showed the efficiency of SnO2/GA NP as a photocatalyst in treatment of wastewater collected during CIT cleaning validation.
Conclusion
SnO2/GA NP were employed as a novel and eco-friendly photocatalyst for treatment of pharmaceutical wastewater containing CIT. Synthesis was performed using a green, simple and low-cost chemical approach using GA. No hazardous chemicals were required during NP preparation. A percentage degradation of 88% was obtained in 1 h using a low-energy UV light source. SnO2/GA NP had the advantage of being effective, recyclable and economic. Analysis of full factorial design had revealed that the most prompting factors affecting the photodegradation process were initial CIT concentration, UV irradiation time and pH. The treatment protocol was successfully applied for samples collected during the cleaning validation process of CIT production lines. This protocol would offer a cost-effective and energy efficient platform for photocatalytic treatment of wastewater.
Data availability
The data that support this study are available in the article and accompanying online supplementary material.
References
Akhir MAM, Rezan SA, Mohamed K, Arafat MM, Haseeb ASMA, Lee HL (2019) Synthesis of SnO2 nanoparticles via hydrothermal method and their gas sensing applications for ethylene detection. Mater Today: Proc 17:810–819
Ahmed A, Siddique MN, Alam U, Ali T, Tripathi P (2019) Improved photocatalytic activity of Sr doped SnO2 nanoparticles: a role of oxygen vacancy. Appl Surf Sci 463:976–985
Arola K, Hatakka H, Mänttäri M, Kallioinen M (2017) Novel process concept alternatives for improved removal of micropollutants in wastewater treatment. Sep Purif Technol 186:333–341
Badhani B, Sharma N, Kakkar R (2015) Gallic acid: a versatile antioxidant with promising therapeutic and industrial applications. RSC Adv 5:27540–27557
Behpour M, Nojavan S, Asadi S, Shokri A (2020) Combination of gel-electromembrane extraction with switchable hydrophilicity solvent-based homogeneous liquid-liquid microextraction followed by gas chromatography for the extraction and determination of antidepressants in human serum, breast milk and wastewater. J Chromatogr A 1621:461041
Benitez FJ, Real FJ, Acero JL, Leal AI, Garcia C (2005) Gallic acid degradation in aqueous solutions by UV/H2O2 treatment, Fenton’s reagent and the photo-Fenton system. J Hazard Mater 126:31–39
Bojanowska-Czajka A, Pyszynska M, Majkowska-Pilip A, Wawrowicz K (2022) Degradation of selected antidepressants sertraline and citalopram in ultrapure water and surface water using gamma radiation. Processes 10:63
Bouafıa-Cherguı S, Zemmourı H, Chabanı M, Bensmaılı A (2016) TiO2-photocatalyzed degradation of tetracycline: kinetic study, adsorption isotherms, mineralization and toxicity reduction. Desalin Water Treat 57:16670–16677
Carter LJ, Chefetz B, Abdeen Z, Boxall AB (2019) Emerging investigator series: towards a framework for establishing the impacts of pharmaceuticals in wastewater irrigation systems on agro-ecosystems and human health. Environ Sci Process Impacts 21:605–622
Castillo-Zacarías C, Barocio ME, Hidalgo-Vázquez E, Sosa-Hernández JE, Parra-Arroyo L, López-Pacheco IY, Barceló D, Iqbal HN, Parra-Saldívar R (2021) Antidepressant drugs as emerging contaminants: occurrence in urban and non-urban waters and analytical methods for their detection. Sci Total Environ 757:143722
Du Y, Chen H, Zhang Y, Chang Y (2014) Photodegradation of gallic acid under UV irradiation: insights regarding the pH effect on direct photolysis and the ROS oxidation-sensitized process of DOM. Chemosphere 99:254–260
Ek M, Baresel C, Magnér J, Bergström R, Harding M (2014) Activated carbon for the removal of pharmaceutical residues from treated wastewater. Water Sci Technol 69:2372–2380
Evans SE, Davies P, Lubben A, Kasprzyk-Hordern B (2015) Determination of chiral pharmaceuticals and illicit drugs in wastewater and sludge using microwave assisted extraction, solid-phase extraction and chiral liquid chromatography coupled with tandem mass spectrometry. Anal Chim Acta 882:112–126
Gadipelly C, Pérez-González A, Yadav GD, Ortiz I, Ibáñez R, Rathod VK, Marathe KV (2014) Pharmaceutical industry wastewater: review of the technologies for water treatment and reuse. Ind Eng Chem Res 53:11571–11592
Gaya UI, Abdullah AH (2008) Heterogeneous photocatalytic degradation of organic contaminants over titanium dioxide: a review of fundamentals, progress and problems. J Photochem Photobiol C 9:1–12
Giebułtowicz J, Nałęcz-Jawecki G (2014) Occurrence of antidepressant residues in the sewage-impacted Vistula and Utrata rivers and in tap water in Warsaw (Poland). Ecotoxicol Environ Saf 104:103–109
Guillossou R, Le Roux J, Mailler R, Vulliet E, Morlay C, Nauleau F, Gasperi J, Rocher V (2019) Organic micropollutants in a large wastewater treatment plant: what are the benefits of an advanced treatment by activated carbon adsorption in comparison to conventional treatment? Chemosphere 218:1050–1060
Han F, Kambala VSR, Srinivasan M, Rajarathnam D, Naidu R (2009) Tailored titanium dioxide photocatalysts for the degradation of organic dyes in wastewater treatment: a review. Appl Catal a: Gen 359:25–40
Himmelsbach M, Buchberger W, Klampfl CW (2006) Determination of antidepressants in surface and waste water samples by capillary electrophoresis with electrospray ionization mass spectrometric detection after preconcentration using off-line solid-phase extraction. Electrophoresis 27:1220–1226
Honarmand M, Golmohammadi M, Naeimi A (2019) Biosynthesis of tin oxide (SnO2) nanoparticles using jujube fruit for photocatalytic degradation of organic dyes. Adv Powder Technol 30:1551–1557
Hu H, Nie L, Feng S, Suo J (2013) Preparation, characterization and in vitro release study of gallic acid loaded silica nanoparticles for controlled release. Pharmazie 68:401–405
ICH Harmonized Tripartite Guidelines (2005) Validation of analytical procedures: text and methodology Q2 (R1). In: International Conference on Harmonization of technical requirements for registration of pharmaceuticals for human use, Geneva
Jiménez-Holgado C, Calza P, Fabbri D, Dal Bello F, Medana C, Sakkas V (2021) Investigation of the aquatic photolytic and photocatalytic degradation of citalopram. Molecules 26:5331
Khan I, Yamani ZH, Qurashi A (2017) Sonochemical-driven ultrafast facile synthesis of SnO2 nanoparticles: growth mechanism structural electrical and hydrogen gas sensing properties. Ultrason Sonochem 34:484–490
Kwon JW, Armbrust KL (2005) Degradation of citalopram by simulated sunlight. Environ Toxicol 24:1618–1623
Lajeunesse A, Smyth S, Barclay K, Sauvé S, Gagnon C (2012) Distribution of antidepressant residues in wastewater and biosolids following different treatment processes by municipal wastewater treatment plants in Canada. Water Res 46:5600–5612
Lee J, Choi K-H, Min J, Kim H-J, Jee J-P, Park BJ (2017) Functionalized ZnO nanoparticles with gallic acid for antioxidant and antibacterial activity against methicillin-resistant S. aureus. Nanomaterials 7:365
Lu J, Batjikh I, Hurh J, Han Y, Ali H, Mathiyalagan R, Ling C, Ahn JC, Yang DC (2019a) Photocatalytic degradation of methylene blue using biosynthesized zinc oxide nanoparticles from bark extract of Kalopanax septemlobus. Optik 182:980–985
Lu Z, Zhao Z, Yang L, Wang S, Liu H, Feng Y, Zhao Y, Feng F (2019b) A simple method for synthesis of highly efficient flower-like SnO2 photocatalyst nanocomposites. J Mater Sci: Mater Electron 30:50–55
Luna AL, Valenzuela MA, Colbeau-Justin C, Vázquez P, Rodriguez JL, Avendaño JR, Alfaro S, Tirado S, Garduño A, José M (2016) Photocatalytic degradation of gallic acid over CuO–TiO2 composites under UV/Vis LEDs irradiation. Appl Catal a: Gen 521:140–148
Ma CM, Hong GB, Lee SC (2020) Facile synthesis of tin dioxide nanoparticles for photocatalytic degradation of Congo red dye in aqueous solution. Catalysts 10:792
Madej M, Kochana J, Baś B (2019) Selective and highly sensitive voltammetric determination of citalopram with glassy carbon electrode. J Electrochem Soc 166:H359–H369
Melchor-Martínez EM, Jiménez-Rodríguez MG, Martínez-Ruiz M, Peña-Benavides SA, Iqbal HMN, Parra-Saldívar R, Sosa- Hernández JE (2021) Antidepressants surveillance in wastewater: overview extraction and detection. CSCEE 3:100074
Meroufel B, Benali O, Benyahia M, Benmoussa Y, Zenasni M (2013) Adsorptive removal of anionic dye from aqueous solutions by Algerian kaolin: characteristics, isotherm, kinetic and thermodynamic studies. J Mater Environ Sci 4:482–491
Mohanta D, Ahmaruzzaman M (2020) Biogenic synthesis of SnO2 quantum dots encapsulated carbon nanoflakes: an efficient integrated photocatalytic adsorbent for the removal of bisphenol A from aqueous solution. J Alloys Compd 828:154093
Mugunthan E, Saidutta M, Jagadeeshbabu P (2019) Photocatalytic degradation of diclofenac using TiO2–SnO2 mixed oxide catalysts. Environ Technol 40:929–941
Nadim AH, Al-Ghobashy MA, Nebsen M, Shehata MA (2015) Gallic acid magnetic nanoparticles for photocatalytic degradation of meloxicam: synthesis, characterization and application to pharmaceutical wastewater treatment. RSC Adv 5:104981–104990
Najjar M, Hosseini HA, Masoudi A, Sabouri Z, Mostafapour A, Khatami M, Darroudi M (2021) Green chemical approach for the synthesis of SnO2 nanoparticles and its application in photocatalytic degradation of Eriochrome Black T dye. Optik 242:167152
Patil P, Killedar S (2021) Chitosan and glyceryl monooleate nanostructures containing gallic acid isolated from amla fruit: targeted delivery system. Heliyon 7:e06526
Puga F, Navío J, Hidalgo M (2021) Enhanced UV and visible light photocatalytic properties of synthesized AgBr/SnO2 composites. Sep Purif Technol 257:117948
Sarıkaya M, Ulusoy HI, Morgul U, Ulusoy S, Tartaglia A, Yılmaz E, Soylak M, Locatelli M, Kabir A (2021) Sensitive determination of Fluoxetine and Citalopram antidepressants in urine and wastewater samples by liquid chromatography coupled with photodiode array detector. J Chromatogr A 1648:462215
Sarker NH, Barnaby SN, Fath KR, Frayne SH, Nakatsuka N, Banerjee IA (2012) Biomimetic growth of gallic acid–ZnO hybrid assemblies and their applications. J Nanopart Res 14:1–12
Sathishkumar M, Geethalakshmi S (2020) Enhanced photocatalytic and antibacterial activity of Cu: SnO2 nanoparticles synthesized by microwave assisted method. Mater Today: Proc 20:54–63
Sharifabadi MK, Tehrani MS, Mehdinia A, Azar PA, Husain SW (2013) Fast removal of citalopram drug from waste water using magnetic nanoparticles modified with sodium dodecyl sulfate followed by UV-spectrometry. J Chem Health Risks 3:35–41
Skibiński R, Misztal G (2005) Determination of citalopram in tablets by HPLC, densitometric HPTLC, and videodensitometric HPTLC methods. J Liq Chromatogr Relat Technol 28:313–324
Štrbac D, Aggelopoulos CA, Štrbac G, Dimitropoulos M, Novaković M, Ivetić T, Yannopoulos SN (2018) Photocatalytic degradation of Naproxen and methylene blue: comparison between ZnO, TiO2 and their mixture. Process Saf Environ Prot 113:174–183
Sun C, Yang J, Xu M, Cui Y, Ren W, Zhang J, Zhao H, Liang B (2022) Recent intensification strategies of SnO2-based photocatalysts: a review. Chem Eng Sci 427:131564
Tammina SK, Mandal BK, Khan FN (2019) Mineralization of toxic industrial dyes by gallic acid mediated synthesized photocatalyst SnO2 nanoparticles. Environ Technol Innov 13:197–210
The Unites States Pharmacopoeia and National Formulary (2011). United States Pharmacopeial Convention Inc., Rockville
Wang Q, Leong WF, Elias RJ, Tikekar RV (2019) UV-C irradiated gallic acid exhibits enhanced antimicrobial activity via generation of reactive oxidative species and quinone. Food Chem 287:303–312
Wu W, Jiang C, Roy VA (2015) Recent progress in magnetic iron oxide–semiconductor composite nanomaterials as promising photocatalysts. Nanoscale 7:38–58
Zhu Z, Zhou J, Wang X, He Z, Liu H (2014) Effect of pH on photocatalytic activity of SnO2 microspheres via microwave solvothermal route. Mater Res Innov 18:8–13
Funding
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).
Author information
Authors and Affiliations
Contributions
VSN: methodology, investigation, formal analysis, visualization, writing—original draft. GMES: supervision, validation, resources, writing—review and editing. SMA: conceptualization, project administration, supervision. AHN: methodology, investigation, data curation, formal analysis, validation, resources, writing—review and editing.
Corresponding author
Ethics declarations
Ethics approval
Not applicable.
Consent to participate
Not applicable.
Consent for publication
Not applicable.
Competing interests
The authors declare no competing interests.
Additional information
Responsible Editor: Sami Rtimi
Publisher’s note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Nazim, V.S., El-Sayed, G.M., Amer, S.M. et al. Functionalized SnO2 nanoparticles with gallic acid via green chemical approach for enhanced photocatalytic degradation of citalopram: synthesis, characterization and application to pharmaceutical wastewater treatment. Environ Sci Pollut Res 30, 4346–4358 (2023). https://doi.org/10.1007/s11356-022-22447-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11356-022-22447-5