Abstract
The production of cement releases an enormous amount of CO2 into the environment. Besides, industrial wastes like silica fume and fly ash need effective utilization to reduce their impacts on the environment. This research aims to explore the influence of silica fume (SF) and fly ash (FA) individually and combine them as binary cementitious material (BCM) on the hardened properties and embodied carbon of roller compacted concrete (RCC). A total of ten mixes were prepared with 1:2:4 mix ratio at the different water-cement ratios to keep the zero slump of roller compacted concrete. However, the replacement proportions for SF were 5%–15%, and FA were 5%–15% by the weight of cement individually and combine in roller compacted concrete for determining the hardened properties and embodied carbon. In this regard, several numbers of concrete specimens (cubes and cylinders) were cast and cured for 7 and 28 days correspondingly. It was observed that the compressive strength of RCC is boosted by 33.6 MPa and 30.6 MPa while using 10% of cement replaced with SF and FA individually at 28 days, respectively. Similarly, the splitting tensile strength of RCC is enhanced by 3.5 MPa at 10% cement replaced with SF and FA on 28 days, respectively. The compressive and splitting tensile strength of RCC is increased by 34.2 MPa and 3.8 MPa at SF7.5FA7.5 as BCM after 28 days consistently. In addition, the water absorption of RCC decreased while using SF and FA as cementitious material individually and together at 28 days. Besides, the embodied carbon of RCC decreased with increasing the replacement level of SF and FA by the mass of cement individually and combined.
Similar content being viewed by others
Availability of data and materials
The data used in this study will be made available upon the request.
References
Abdul-Wahab SA, Al-Dhamri H, Ram G, Chatterjee VP (2020) An overview of alternative raw materials used in cement and clinker manufacturing. Int J Sustain Eng:1–18 https://doi.org/10.1080/19397038.2020.1822949
Adamu M, Mohammed BS, Shahir Liew M (2018) Mechanical properties and performance of high volume fly ash roller compacted concrete containing crumb rubber and nano silica. Constr Build Mater 171:521–538. https://doi.org/10.1016/j.conbuildmat.2018.03.138
Ahmed I, Kumar A, Rizvi SH, Ali M, Ali S (2020) Effect of silica fume as partial replacement of cement on compressive strength of roller compacting concrete. Quaid-E-Awam Univ Res J Eng Sci Technol Nawabshah 18(2):145–149
Almusallam AA, Beshr H, Maslehuddin M, Al Amoudi OSB (2004) Effect of silica fume on the mechanical properties of low quality coarse aggregate concrete. Cem Concr Compos 26(7):891–900. https://doi.org/10.1016/j.cemconcomp.2003.09.003
Amato G, Campione G, Cavaleri L, Minafò G, Miraglia N (2012) The use of pumice lightweight concrete for masonry applications. Mater Struct 45:679–693. https://doi.org/10.1617/s11527-011-9789-7
ASTM C496-90 (1996) Standard test method for splitting tensile strength of cylindrical concrete specimens. ASTM International, West Conshohocken, PA 04:1–4
ASTM C1585-13 (2013) Standard test method for measurement of rate of absorption of water by hydraulic-cement concretes, ASTM International, West Conshohocken, PA, 2013, www.astm.org
ASTM C39M-15a (2015) Standard test method for compressive strength of cylindrical concrete specimens, ASTM International, West Conshohocken, PA, 2015, www.astm.org
ASTM C136M-19 (2019) Standard test method for sieve analysis of fine and coarse aggregates, ASTM International, West Conshohocken, PA, 2019, www.astm.org
ASTM C618-19 (2019) Standard specification for coal fly ash and raw or calcined natural pozzolan for use in concrete, ASTM International, West Conshohocken, PA, 2019, www.astm.org
ASTM C1240-20 (2020) Standard specification for silica fume used in cementitious mixtures, ASTM International, West Conshohocken, PA, 2020, www.astm.org
ASTM C143M-20 (2020) Standard test method for slump of hydraulic-cement concrete, ASTM International, West Conshohocken, PA, 2020, www.astm.org
Banu ST, Chitra G, Awoyera PO, Gobinath R (2019) Structural retrofitting of corroded fly ash based concrete beams with fibres to improve bending characteristics. Australian J Structural Eng 20:198–203. https://doi.org/10.1080/13287982.2019.1622490
Benli A (2019) Mechanical and durability properties of self-compacting mortars containing binary and ternary mixes of fly ash and silica fume. Struct Concr 20:1096–1108. https://doi.org/10.1002/suco.201800302
Bheel N, Adesina A (2021) Influence of binary blend of corn cob ash and glass powder as partial replacement of cement in concrete. Silicon 13:1647–1654. https://doi.org/10.1007/s12633-020-00557-4
Bheel N, Memon FA, Meghwar SL (2020) Study of fresh and hardened properties of concrete using cement with modified blend of millet husk ash as secondary cementitious material. Silicon:1–12. https://doi.org/10.1007/s12633-020-00906-3
Bheel N, Kumar A, Shahzaib J, Ali Z, Ali M (2021a) An investigation on fresh and hardened properties of concrete blended with rice husk ash as cementitious ingredient and coal bottom ash as sand replacement material. Silicon:1–12. https://doi.org/10.1007/s12633-020-00906-3
Bheel N, Mahro SK, Adesina A (2021b) Influence of coconut shell ash on workability, mechanical properties, and embodied carbon of concrete. Environ Sci Pollut Res 28:5682–5692. https://doi.org/10.1007/s11356-020-10882-1
Cascardi A, Longo F, Micelli F, Aiello MA (2017) Compressive strength of confined column with Fiber Reinforced Mortar (FRM): new design-oriented-models. Constr Build Mater 156:387–401. https://doi.org/10.1016/j.conbuildmat.2017.09.004
Cordeiro GC, Toledo Filho RD, Tavares LM, Fairbairn EMR (2008) Pozzolanic activity and filler effect of sugar cane bagasse ash in Portland cement and lime mortars. Cem Concr Compos 30(5):410–418. https://doi.org/10.1016/j.cemconcomp.2008.01.001
Dadsetan S, Bai J (2017) Mechanical and microstructural properties of self-compacting concrete blended with metakaolin, ground granulated blast-furnace slag and fly ash. Constr Build Mater 146:658–667. https://doi.org/10.1016/j.conbuildmat.2017.04.158
Delatte NJ (2014) Concrete pavement design, construction, and performance. 2nd Ed CRC Press, Boca Raton, FL, USA.
Fakhri M, Farshad Saberi K (2016) The effect of waste rubber particles and silica fume on the mechanical properties of roller compacted concrete pavement. J Clean Prod 129:521–530. https://doi.org/10.1016/j.jclepro.2016.04.017
Flower DJM, Sanjayan JG (2007) Green house gas emissions due to concrete manufacture. Int J Life Cycle Assess 12:282–288. https://doi.org/10.1065/lca2007.05.327
Habeeb GA, Fayyadh MM (2009) Rice husk ash concrete: the effect of RHA average particle size on mechanical properties and drying shrinkage. Aust J Basic Appl Sci 3:1616–1622
Hammond G, Jones C, Lowrie EF, Tse P (2011) Embodied carbon. Invent carbon energy (ICE) Version.
Hanumesh BM, Varun BK, Harish BA (2015) The mechanical properties of concrete incorporating silica fume as partial replacement of cement. Int J Emerging Technol Advanced Eng 5(9):270–275
Harrington D, Abdo F, Adaska W et al (2010) Guide for roller-compacted concrete pavements. Trans Project Reports, 102, Iowa State University.
Hemalatha T, Ramaswamy A (2017) A review on fly ash characteristics—towards promoting high volume utilization in developing sustainable concrete. J Clean Prod 147:546–559. https://doi.org/10.1016/j.jclepro.2017.01.114
Humphreys K, Mahasenan M (2002) Towards a sustainable cement industry: Substudy 8: Climate change. World Business Council for Sustainable Development (WBCSD): Geneva, Switzerland.
Kamaruddin S, Goh WI, Abdul Mutalib NAN, Jhatial AA, Mohamad N, Rahman AF (2021) Effect of combined supplementary cementitious materials on the fresh and mechanical properties of eco-efficient self-compacting concrete. Arab J Sci Eng. https://doi.org/10.1007/s13369-021-05656-x
Karbassi AR, Jafari HR, Yavari AR, Hoveidi H, Kalal HS (2010) Reduction of environmental pollution through optimization of energy use in cement industries. Int J Environ Sci Technol 7(1):127–134. https://doi.org/10.1007/BF03326124
Keerio MA, Abbasi SA, Kumar A, Bheel N, Rehaman K, Tashfeen M (2020) Effect of silica fume as cementitious material and waste glass as fine aggregate replacement constituent on selected properties of concrete. Silicon 1–12. https://doi.org/10.1007/s12633-020-00806-6
Kumar S, Murthi P, Awoyera P, Gobinath R, kumar S (2020) Impact resistance and strength development of fly ash based self-compacting concrete. Silicon:1–12. https://doi.org/10.1007/s12633-020-00842-2
Kumar R, Shafiq N, Kumar A, Jhatial AA (2021) Investigating embodied carbon, mechanical properties, and durability of high-performance concrete using ternary and quaternary blends of metakaolin, nano-silica, and fly ash. Environ Sci Pollut Res:1–15. https://doi.org/10.1007/s11356-021-13918-2
Kurama H, Kaya M (2008) Usage of coal combustion bottom ash in concrete mixture. Constr Build Mater 22:1922–1928. https://doi.org/10.1016/j.conbuildmat.2007.07.008
Kuruscu AO, Girgin ZC (2014) Efficiency of structural materials in sustainable design. J Civ Eng Archit 8. https://doi.org/10.17265/1934-7359/2014.10.007
Longo F, Cascardi A, Lassandro P, Aiello MA (2021) Thermal and seismic capacity improvements for masonry building heritage: a unified retrofitting system. Sustainability 13:1111. https://doi.org/10.3390/su13031111
Memon MJ, Jhatial AA, Murtaza A, Raza MS, Phulpoto KB (2021) Production of eco-friendly concrete incorporating rice husk ash and polypropylene fibres. Environ Sci Pollut Res 28:39168–39184. https://doi.org/10.1007/s11356-021-13418-3
Modani PO, Vyawahare MR (2013) Utilization of bagasse ash as a partial replacement of fine aggregate in concrete. Procedia Eng 51:25–29. https://doi.org/10.1016/j.proeng.2013.01.007
Mohammed BS, Adamu M (2018) Mechanical performance of roller compacted concrete pavement containing crumb rubber and nano silica. Constr Build Mater 159:234–251. https://doi.org/10.1016/j.conbuildmat.2017.10.098
Neville AM, Brooks JJ (2010) Concrete Technology, 2nd Editio. Edinburgh, Engl Pearson Educ Ltd.
Ombres L, Verre S (2018) Shear performance of FRCM strengthened RC beams. American Concrete Institute, ACI Special Publication (SP 324): Farmington Hills. MI, USA 324:1–7
Ramezanianpour AA, Malhotra VM (1995) Effect of curing on the compressive strength, resistance to chloride-ion penetration and porosity of concretes incorporating slag, fly ash or silica fume. Cem Concr Compos 17:125–133. https://doi.org/10.1016/0958-9465(95)00005-W
Rao SK, Sravana P, Rao TC (2016) Investigating the effect of M-sand on abrasion resistance of Fly Ash Roller Compacted Concrete (FRCC). Constr Build Mater 118:352–363. https://doi.org/10.1016/j.conbuildmat.2016.05.017
Roy DKS, Sil A (2012) Effect of partial replacement of cement by silica fume on hardened concrete. Int J Emerg Technol Adv Eng 2:472–475
Rukzon S, Chindaprasirt P (2012) Utilization of bagasse ash in high-strength concrete. Mater Des 34:45–50. https://doi.org/10.1016/j.matdes.2011.07.045
Saluja S, Kaur K, Goyal S, Bhattacharjee B (2019) Assessing the effect of GGBS content and aggregate characteristics on drying shrinkage of roller compacted concrete. Constr Build Mater 201:72–80. https://doi.org/10.1016/j.conbuildmat.2018.12.179
Sathanandam T, Awoyera PO, Vijayan V, Sathishkumar K (2017) Low carbon building: Experimental insight on the use of fly ash and glass fibre for making geopolymer concrete. Sustain Environ Res 27:146–153. https://doi.org/10.1016/j.serj.2017.03.005
Shen L, Li Q, Ge W, Xu S (2020) The mechanical property and frost resistance of roller compacted concrete by mixing silica fume and limestone powder: experimental study. Constr Build Mater 239:117882. https://doi.org/10.1016/j.conbuildmat.2019.117882
Siddique R (2011) Utilization of silica fume in concrete: review of hardened properties. Resour Conserv Recycl 55:923–932. https://doi.org/10.1016/j.resconrec.2011.06.012
Tavakoli D, Fakharian P, de Brito J (2021) Mechanical properties of roller-compacted concrete pavement containing recycled brick aggregates and silica fume. Road Mater Pavement Des:1–22. https://doi.org/10.1080/14680629.2021.1924236
Thilakarathna PSM, Seo S, Kristombu Baduge KS, Lee H, Mendis P, Foliente G (2020) Embodied carbon analysis and benchmarking emissions of high and ultra-high strength concrete using machine learning algorithms. J Clean Prod 262:121281. https://doi.org/10.1016/j.jclepro.2020.121281
Turner LK, Collins FG (2013) Carbon dioxide equivalent (CO2-e) emissions: a comparison between geopolymer and OPC cement concrete. Constr Build Mater 43:125–130. https://doi.org/10.1016/j.conbuildmat.2013.01.023
Vahedifard F, Nili M, Meehan CL (2010) Assessing the effects of supplementary cementitious materials on the performance of low-cement roller compacted concrete pavement. Constr Build Mater 24:2528–2535. https://doi.org/10.1016/j.conbuildmat.2010.06.003
Yang K-H, Song J-K, Song K-I (2013) Assessment of CO2 reduction of alkali-activated concrete. J Clean Prod 39:265–272. https://doi.org/10.1016/j.jclepro.2012.08.001
Yang KH, Jung YB, Cho MS, Tae SH (2017) Chapter 5—effect of supplementary cementitious materials on reduction of CO2 emissions from concrete. Handb Low Carbon Concr Nazari, A, Sanjayan, J, Eds 89–110.
Zarrin O, Shirazi MR (2015) Design of roller compacting concrete pavement. Int J Civ Environ Eng 9:785–788
Zhang S, Ren H, Zhou W, Yu Y, Chen C (2018) Assessing air pollution abatement co-benefits of energy efficiency improvement in cement industry: A city level analysis. J Clean Prod 185:761–771
Zhu Q (2011) CO2 abatement in the cement industry. IEA Clean Coal Centre.
Zhutovsky S, Hooton RD (2016) MAT-742: Effect of supplementary cementitious materials on the resistance of mortar to physical sulfate salt attack. 5th International Materials Specialty Conference, Annual Conference 595 of Canadian Society for Civil Engineering, Ontario, Canada
Acknowledgements
The authors are grateful to Mehran UET Jamshoro for providing required tools to conduct this research study.
Author information
Authors and Affiliations
Contributions
Aneel Kumar: Supervision, Methodology, Writing – Original Draft, Funding Acquisition, Writing – Review and Editing.
Naraindas Bheel: Conceptualization, Investigation, Data Analysis, Validation, Writing – Original Draft, Writing – Review and Editing.
Israr Ahmed: Data Analysis, Validation, Writing – Original Draft.
Samar Hussain Rizvi: Data Analysis, Validation, Writing – Original Draft
Rabinder Kumar: Formal Analysis, Validation.
Ashfaque Ahmed Jhatial: Review, Validation.
Corresponding author
Ethics declarations
Ethics approval and consent to participate
Not applicable.
Consent for publication
Not applicable.
Competing interests
The authors declare no competing interests.
Additional information
Responsible Editor: Philippe Garrigues
Publisher’s note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Kumar, A., Bheel, N., Ahmed, I. et al. Effect of silica fume and fly ash as cementitious material on hardened properties and embodied carbon of roller compacted concrete. Environ Sci Pollut Res 29, 1210–1222 (2022). https://doi.org/10.1007/s11356-021-15734-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11356-021-15734-0