An In-Situ X-Ray Microtomography Study of Split Cylinder Fracture in Cement-Based Materials

  • Published:
Experimental Mechanics Aims and scope Submit manuscript

Abstract

In an effort to quantify microstructure-property relationships, three dimensional imaging experiments were conducted on small cylinder specimens subjected to split cylinder fracture. 3-D images were made using synchrotron-based x-ray microtomography, and the experiments were conducted with an in-situ frame such that a specimen could be examined while under load at varying degrees of damage. The specimens were made of fine-grained portland cement mortar and 0.5 mm glass beads, which served as aggregates. The diameter of the specimens was 5 mm. 3-D image analysis routines were developed or adapted to characterize microstructure and internal damage, which could then be related to bulk splitting strength and fracture energy. For fracture energy calculation, crack surface area could be measured in a way that accounted for roughness, branching, and fragmentation. Results showed that, for the specimens tested, aggregate surface roughness had little effect on strength but significant effect on fracture energy. Split cylinder strength showed correlation with specimen porosity, although there was considerable scatter. Strength did not correlate with maximum flaw size, although flaw location was not evaluated.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8

Similar content being viewed by others

References

  1. van Mier J (2013) Concrete fracture – a multiscale approach. CRC Press

  2. Yip M, Li Z, Liao BS, Bolander J (2006) Irregular lattice models of fracture of multi-phase materials. Int J Fract 140(1–4):113–124

    Article  MATH  Google Scholar 

  3. Cusatis G, Pelessone D, Mencarelli A (2011) Lattice Discrete Particle Model (LDPM) for failure behavior of concrete. I: Theory. Cem Concr Compos 33(9):881–890. doi:10.1016/j.cemconcomp.2011.02.011

    Article  Google Scholar 

  4. Cusatis G, Mencarelli A, Pelessone D, Baylot J (2011) Lattice Discrete Particle Model (LDPM) for failure behavior of concrete. II: Calibration and validation. Cem Concr Compos 33(9):891–905. doi:10.1016/j.cemconcomp.2011.02.010

    Article  Google Scholar 

  5. Man HK, van Mier JGM (2011) Damage distribution and size effect in numerical concrete from lattice analyses. Cem Concr Compos 33(9):867–880. doi:10.1016/j.cemconcomp.2011.01.008

    Article  Google Scholar 

  6. Landis EN, Bolander JE (2009) Explicit representation of physical processes in concrete fracture. J Phys D: Appl Phys 42(21):214002 (17pp). doi:10.1088/0022-3727/42/21/214002

    Article  Google Scholar 

  7. Kozicki J, Tejchman J (2007) Effect of aggregate structure on fracture process in concrete using 2D lattice model. Arch Mech 59(4-5):365–384

    MATH  Google Scholar 

  8. Kak A, Slaney M (1988) Principles of computerized tomography. IEEE Press

  9. Stock SR (2008) Recent advances in x-ray microtomography applied to materials. Int Mater Rev 53(3):129–181

    Article  Google Scholar 

  10. Flannery BP, Deckman HW, Roberge WG, D’Amico KL (1987) Three-dimensional x-ray microtomography. Science 237(4821):1439–1444

    Article  Google Scholar 

  11. Kinney JH, Nichols MC (1992) X-ray tomographic microscopy (XTM) using synchrotron radiation. In: Annual review of materials science, pp 121–152

  12. Zauner M, Keunecke D, Mokso R, Stampanoni M, Niemz P (2012) Synchrotron-based tomographic microscopy (SbTM) of wood: development of a testing device and observation of plastic deformation of uniaxially compressed Norway spruce samples. Holzforschung 66(0):973–979. doi:10.1515/hf-2011-0192. http://www.degruyter.com/view/j/hfsg.ahead-of-print/hf-2011-0192/hf-2011-0192.xml

    Google Scholar 

  13. Brault R, Germaneau A, Dupré JC, Doumalin P,Mistou S, Fazzini M (2013) In-situ Analysis of laminated composite materials by Xray micro-computed tomography and digital volume correlation. Exp Mech. doi: 10.1007/s11340-013-9730-9. http://link.springer.com/10.1007/s11340-013-9730-9

  14. Mindess S, Young JF, Darwin D (2003) Concrete, 2nd edn. Prentice Hall

  15. de Wolski S (2011) Measurement of deformation and damage in cementitious split cylinders by employing x-ray microtomography. Orono, Master’s Thesis, University of Maine

  16. Zhang T (2004) Identification of structural changes from volumetric image sequence. Ph.D. Thesis, Rensselaer Polytechnic Institute, Troy, New York

  17. Otsu N (1979) A threshold selection method from gray-level histograms. IEEE Trans Syst Man Cybern smc-9(1):62–66

    MathSciNet  Google Scholar 

  18. Franklin WR (2006) Connect – find 3d connected components, http://wrfranklin.org/pmwiki/connectedcomponents

  19. Petroski HJ, Ojdrovic RP (1987) The concrete cylinder: stress analysis and failure modes. Int J Fract 34:263–279

    Article  Google Scholar 

  20. Landis EN, Nagy EN, Keane DT, Nagy G (1999) A technique to measure three-dimensional work-of-fracture of concrete in compression. J Eng Mech 125(6):599–605

    Article  Google Scholar 

  21. Landis EN (2006) Damage variables based on three-dimensional measurements of crack geometry. Strength Fract Complexity 3(2):163–173

    Google Scholar 

  22. Wnuk MP, Yavari A (2008) Discrete fractal fracture mechanics. Eng Fract Mech 75:1127–1142. doi:10.1016/j.engfracmech.2007.04.020

    Article  Google Scholar 

  23. Buyukozturk O, Wecharatana M (eds) (1995) Interface fracture and bond. American Concrete Institute

  24. Asahina D, Landis EN, Bolander JE (2011) Modeling of phase interfaces during pre-critical crack growth in concrete. Cem Concr Compos 33(9):966–977

    Article  Google Scholar 

Download references

Acknowledgments

The authors gratefully acknowledge the support of a collaborative grant from the U.S. National Science Foundation (0625030 and 0625593). Additionally, portions of this work were performed at the DuPont-Northwestern-Dow Collaborative Access Team (DND-CAT) located at Sector 5 of the Advanced Photon Source (APS). DND-CAT is supported by E.I. DuPont de Nemours & Co., The Dow Chemical Company and the State of Illinois. Use of the APS was supported by the U. S. Department of Energy, Office of Science, Office of Basic Energy Sciences, under Contract No. DE-AC02-06CH11357. An additional acknowledgement goes to Dr. Denis Keane, DND-CAT director, for his assistance at the beamline. Undergraduate research assistants Katie Dumas, Katrina Martin, and Lauren Flanders also contributed to the data analysis work.

Author information

Authors and Affiliations

  1. University of Maine, Orono, ME, USA

    S. C. de Wolski & E. N. Landis

  2. University of California, Davis, California, USA

    J. E. Bolander

Authors
  1. S. C. de Wolski
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. J. E. Bolander
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. E. N. Landis
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to E. N. Landis.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

de Wolski, S.C., Bolander, J.E. & Landis, E.N. An In-Situ X-Ray Microtomography Study of Split Cylinder Fracture in Cement-Based Materials. Exp Mech 54, 1227–1235 (2014). https://doi.org/10.1007/s11340-014-9875-1

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11340-014-9875-1

Keywords

Search

Navigation