Abstract
Colloidal dispersions of MoS2 in DMF were obtained, and a procedure for the preparation of the fraction of particles with the size distribution 1.5 times narrower than that in the original dispersion was developed. It was shown that for the gradual centrifugation of dispersions with an increase in the acceleration from 126g to 2016g the average thickness of nanosheets decreased from 35 to 8 nm and the average lateral sizes decreased from 250 nm to a constant value of 160 nm. A linear dependence of the absorbance of the dispersions on the concentration of MoS2 was established.
Similar content being viewed by others
References
V. E. Fedorov, Khalkogenidy perekhodnykh tugoplavkikh metallov. Kvaziodnomernye soedineniya [Chalcogenides of Refractory Transition Metals. Quasi-one-dimensional Compounds], Nauka, Sib. Otd., Novosibirsk, 1988, 222 pp. (in Russian).
V. L. Kalikhman, Y. S. Umanskii, Sov. Phys. Usp., 1973, 15, 728.
M. Chhowalla, H. S. Shin, G. Eda, L. J. Li, K. P. Loh, H. Zhang, Nat. Chem., 2013, 5, 263.
H. Li, J. M. T. Wu, Z. Y. Yin, H. Zhang, Acc. Chem. Res., 2014, 47, 1067.
V. Nicolosi, M. Chhowalla, M. G. Kanatzidis, M. S. Strano, J. N. Coleman, Science, 2013, 340, 1420.
X. Huang, C. L. Tan, Z. Y. Yin, H. Zhang, Adv. Mater., 2014, 26, 2185.
Q. H. Wang, K. Kalantar-Zadeh, A. Kis, J. N. Coleman, M. S. Strano, Nat. Nanotechnol., 2012, 7, 699.
M. Chhowalla, Z. F. Liu, H. Zhang, Chem. Soc. Rev., 2015, 44, 2584.
G. Eda, H. Yamaguchi, D. Voiry, T. Fujita, M. W. Chen, M. Chhowalla, Nano Lett., 2011, 11, 5111.
D. Gopalakrishnan, D. Damien, M. M. Shaijumon, ACS Nano, 2014, 8, 5297.
V. Stengl, J. Henych, Nanoscale, 2013, 5, 3387.
X. Zhang, Z. C. Lai, Z. D. Liu, C. L. Tan, Y. Huang, B. Li, M. T. Zhao, L. H. Xie, W. Huang, H. Zhang, Angew. Chem. Int. Ed., 2015, 54, 5425.
B. Radisavljevic, A. Radenovic, J. Brivio, V. Giacometti, A. Kis, Nat. Nanotechnol., 2011, 6, 147.
K. S. Novoselov, D. Jiang, F. S chedin, T. J. Booth, V. V. Khotkevich, S. V. Morozov, A. K. Geim, Proc. Natl. Acad. Sci. U. S. A., 2005, 102, 10451.
J. N. Coleman, M. Lotya, A. O’Neill, S. D. Bergin, P. J. King, U. Khan, K. Young, A. Gaucher, S. De, R. J. Smith, I. V. Shvets, S. K. Arora, G. Stanton, H. Y. Kim, K. Lee, G. T. Kim, G. S. Duesberg, T. Hallam, J. J. Boland, J. J. Wang, J. F. Donegan, J. C. Grunlan, G. Moriarty, A. Shmeliov, R. J. Nicholls, J. M. Perkins, E. M. Grieveson, K. Theuwissen, D. W. McComb, P. D. Nellist, V. Nicolosi, Science, 2011, 331, 568.
S. B. Artemkina, T. Y. Podlipskaya, A. I. Bulavchenko, A. I. Komonov, Y. V. Mironov, V. E. Fedorov, COLLOID SURFACE A, 2014, 461, 30.
V. E. Fedorov, S. B. Artemkina, E. D. Grayfer, N. G. Naumov, Y. V. Mironov, A. I. Bulavchenko, V. I. Zaikovskii, I. V. Antonova, A. I. Komonov, M. V. Medvedev, J. Mater. Chem. C, 2014, 2, 5479.
P. Joensen, R. F. Frindt, S. R. Morrison, Mater. Res. Bull., 1986, 21, 457.
D. Yang, S. J. Sandoval, W. M. R. Divigalpitiya, J. C. Irwin, R. F. Frindt, Phys. Rev. B, 1991, 43, 12053.
M. N. Kozlova, Y. V. Mironov, E. D. Grayfer, A. I. Smolentsev, V. I. Zaikovskii, N. A. Nebogatikova, T. Y. Podlipskaya, V. E. Fedorov, Chem.-Eur. J., 2015, 21, 4639.
V. A. Kuznetsov, A. S. Berdinsky, A. Y. Ledneva, S. B. Artemkina, M. S. Tarasenko, V. E. Fedorov, Sens. Actuators A, 2015, 226, 5.
P. A. Poltarak, S. B. Artemkina, A. I. Bulavchenko, T. Yu. Podlipskaya, V. E. Fedorov, Russ. Chem. Bull., 2015, 64, 1850.
A. I. Romanenko, V. E. Fedorov, S. B. Artemkina, O. B. Anikeeva, P. A. Poltarak, Phys. Sol. State, 2015, 57, 1850.
K. G. Zhou, N. N. Mao, H. X. Wang, Y. Peng, H. L. Zhang, Angew. Chem., Int. Ed., 2011, 50, 10839.
R. J. Smith, P. J. King, M. Lotya, C. Wirtz, U. Khan, S. De, A. O´Neill, G. S. Duesberg, J. C. Grunlan, G. Moriarty, J. Chen, J. Z. Wang, A. I. Minett, V. Nicolosi, J. N. Coleman, Adv. Mater., 2011, 23, 3944.
T. Y. Wang, H. C. Zhu, J. Q. Zhuo, Z. W. Zhu, P. Papakonstantinou, G. Lubarsky, J. Lin, M. X. Li, Anal. Chem., 2013, 85, 10289.
S. Mukherjee, R. Maiti, A. Midya, S. Das, S. K. Ray, Acs Photonics, 2015, 2, 760.
J. Kang, J. W. T. Seo, D. Alducin, A. Ponce, M. J. Yacaman, M. C. Hersam, Nat. Commun., 2014, 5.
S. Krumm, European Powder Diffraction: Epdic Iv, Pts 1 and 2, 1996, 228, 183.
C. F. Bohren, D. R. Huffman, Absorption and Scattering of Light by Small Particles, Wiley-Interscience, New York, 1998, 530.
J. L. Verble, T. J. Wieting, Phys. Rev. Lett., 1970, 25.
C. Lee, H. Yan, L. E. Brus, T. F. Heinz, J. Hone, S. Ryu, ASC Nano, 2010, 4, 2695.
A. Molina-Sanchez, L. Wirtz, Phys. Rev. B, 2011, 84.
I. V. Klimenko, A. S. Golub´, T. S. Zhuravleva, N. D. Lenenko, Y. N. Novikov, Russ. J. Phys. Chem., 2009, 83, 276.
N. A. Mazer, M. C. Carey, R. F. Kwasnick, G. B. Benedek, Biochemistry, 1979, 18, 3064
Author information
Authors and Affiliations
Corresponding author
Additional information
Published in Russian in Izvestiya Akademii Nauk. Seriya Khimicheskaya, No. 6, pp. 0963—0968, June, 2017.
Rights and permissions
About this article
Cite this article
Kozlova, M.N., Artemkina, S.B., Podlipskaya, T.Y. et al. Colloidal dispersions of molybdenum disulfide with a narrow particle size distribution. Russ Chem Bull 66, 963–968 (2017). https://doi.org/10.1007/s11172-017-1839-z
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11172-017-1839-z