Results of studying of the possibility of using clinker as a filler for producing refractory concrete based on high-alumina cement are presented. Clinker is used for cement and aggregate production. The main properties of clinker as an aggregate are studied. On the basis of high-alumina cement and its clinker a refractory concrete composition is developed that has compressive strength with normal hardening of 50 – 55 MPa, shrinkage of 0,2%, and a heat resistance of more than 35 thermal cycles (1300°C – water). Special attention is devoted to the contact zone formed between filler and cement. Refractory concrete pertains to class 16 and is recommended for lining heating units in the chemical industry.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
K. D. Nekrasov, Heat-Resistant Concrete [in Russian], Promstroizdat, Moscow (1957).
A. P. Tarasova, Heat-Resistant Binders in Molten Glass and Concrete Based Upon Them [in Russian], Stroiizdat, Moscow (1982).
K. D. Nekrasov and M. G. Maslennikova, Light Heat-Resistant Concretes Based on Porous Fillers [in Russian], Stroiizdat, Moscow (1982).
K. D. Nekrasov, V. V Zhukov, and V. F. Gulyaeva, Heavy Concrete Under Elevated temperature Conditions [in Russian], Stroiizdat, Moscow (1972).
Yu. R. Krivoborodov and A. A. Boiko, “Effect of mineral additives on alumina cement hydration,” Tekhnik Tekhnol. Silikatov, No 4, 12 – 15 (2011).
G. V. Kuznetsova and I. Talaber, Alumina Cement [in Russian], Stroiizdat, Moscow (1988).
Yu. A. Abzaev, Yu. S. Sarkisov, T. V. Kuznetsova, et al., “Analysis of the structure and phase composition of calcium mono-aluminate,” Inzh. Stroit. Zh., No. 3, 56 – 62 (2014).
A. N. Abyzov, V. M. Tytvin, V. A. Abyzov, et al., “Heat-resistant and refractory concretes based on binders and fillers form ferroalloy production slags,” Stroit. Materialy, No. 11, 67 – 69 (2012).
A. E. Sheikin, Yu. V. Chekovskii, and M. I. Brusser, Cement Structure and Concrete Properties [in Russian], Stroiizdat, Moscow (1979).
S. Kh. Yarlushkina, “Physicochemical processes and their role in forming cement stone strength with fillers,” in: Structure Formation fo Concretes and Physicochemical methods for Study Coll. NIIZhBa, Moscow (201980)
P. J. M. Monteiro and P. K. Mehta “Interaction between carbonate rock and cement paste,” Cem. Concr. Res., No. 2, 127 – 134 (1986).
L. Struble, “Microstructure and fracture at the cement paste-aggregate interface,” Bond. Cementitious Compos., Symp., Boston, Mass., Dec. 2 – 4, 1987. Pittsburgh (Pa), 1988.
Karen L. Scrivener, Alison K. Crumbie, and P. L. Pratt, “A study of the interfacial region between paste and aggregate in concrete, Bond. Cementitious Compos. Symp., Boston, Mass., Dec. 2 – 4, 1987. Pittsburgh (Pa), 1988.
H. F. W. Taylor, Cement Chemistry, Academic Press, London (1990).
T. V. Kuznetsova and S. V. Samchenko, Cement Production Material Microscopy [in Russian]. MIKKhiS, Moscow (2007).
Guide for Creating Heating Units from Heat-Resistant Concretes [in Russian], Stroiizdat, Moscow (1983).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Novye Ogneupory, No. 3, pp. 25 – 28, March, 2021.
Rights and permissions
About this article
Cite this article
Krivoborodov, Y.R., Samchenko, S.V. & Kuznetsova, T.V. Refractory Concrete Based on High-Alumina Cement and Clinker Filler. Refract Ind Ceram 62, 153–156 (2021). https://doi.org/10.1007/s11148-021-00575-8
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11148-021-00575-8