Nitriding of a V–Al–N alloy during combustion in an industrial reactor was investigated. The optimum nitriding conditions were determined. Phases formed by nitriding of VnAl-65 alloy during combustion were characterized. Self-propagating high-temperature nitriding technology was developed. Test batches of nitrided V–Al–N alloy were prepared.
Similar content being viewed by others
References
B. N. Moiseev, “High-strength titanium alloys in aircraft construction,” Tekhnol. Legk. Splavov, No. 4, 95 – 105 (2002).
E. Fromm and E. Gebhart, Gases and Carbon in Metals [transl. from German], Metallurgiya, Moscow, 1980, 712 pp.
M. A. Khorev and A. I. Khorev, “Titanium alloys, their application and development potential,” Materialovedenie, No. 7, 25 – 34 (2005).
T. B. Massalski, Binary Alloy Phase Diagrams, ASM Int., Materials Park, Ohio (1990), 3589 pp.
V. V. Zakorzhevskii, I. P. Borovinskaya, A. Ya. Dubrovskii, A. V. Zelyanskii, I. P. Pazdnikov, and V. M. Chumarev, RU Pat. No. 2,422,246, Jun. 27, 2011, Appl. No. 2010111351/02, Mar.6., 2010, “Method of producing nitride-cased nitrogen-containing material for titanium foundry alloys and nitrogen-containing material for titanium foundry alloys.”
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Novye Ogneupory, No. 8, pp. 49 – 52, August, 2018.
A. Ya. Dubrovskii is deceased
Rights and permissions
About this article
Cite this article
Zakorzhevskii, V.V., Kovalev, I.D. & Dubrovskii, A.Y. Self-Propagating High-Temperature Synthesis of N-Containing Material Based on Aluminum and Vanadium Nitrides for Producing Titanium Primary Alloys. Refract Ind Ceram 59, 416–419 (2018). https://doi.org/10.1007/s11148-018-0246-9
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11148-018-0246-9