Technology for low-temperature carbonitriding combined with high temperature tempering of cold-worked die steel 6Kh4M2FS (DI55) is proposed. The high efficiency of a paste-like coating based on amorphous carbon and nitrogen-containing components (carbamide and potassium ferricyanide) during die steel cyaniding in the temperature range from 500 to 580°C is demonstrated. The effect of thermochemical treatment regimes on diffusion layers formed on steel, their phase composition, and properties is investigated.
Similar content being viewed by others
Notes
Friction path Sfr = πdspe × n × 60 (where dspe = 0.05 m, i.e. specimen diameter; n is specimen rotation frequency 1000 rpm; test duration time 60 min); then Sfr = 3.14 × 0.05 × 1000 × 60 = 9420 m.
References
Yu. N. Stasovskii and V. L. Chukhleb, “Production planning in forging and stamping manufacture. State of the question, problems, and prospects for development at a new level,” Obrab. Mater. Davleniem, No. 3(28), 66 – 71 (2011).
A. É. Artes, “Development of forging production in domestic machine building,” Vestn. MGTU, Stankin, No. 2, 6 – 12 (2010).
B. F. Trakhtenberg, “Contemporary trends in the problem of die life,” Kuzn.-Shtamp. Proizvod., No. 8, 27 – 29 (1981).
Ya. M. Okhrimenko, L. I. Antonenko, and I. A. Izakov, “Reasons for failure short-life dies,” Izv. Vysh. Uchebn. Zaved., Chern. Met., No. 1, 113 – 116 (1971).
E. V. Trusova, V. I. Kolmykov, A. I. Dyagtyarev, et al., “Wear and improvement of die life,” in: Materials and Strengthening Technologies [in Russian], YuZGU, Kursk (2010), Part 1, pp. 178 – 191.
N. A. Kostin and E. V. Trusova, “Study of the impregnating capacity of nitride paste at low and elevated temperatures for die steel carbonitriding,” Uch. Zapiski, Élektron. Zh. Kursk. Gos. Univ., No. 1, 80 – 86 (2013).
A. M. Adaskin, Tools Materials in Engineering [in Russian], Infra-M, Moscow (2018).
Yu. A. Geller, Tool Steels [in Russian], Metallurgiya, Moscow 91983).
G. A. Okolovich, Die Steels for Metal Cold Deformation. Monograph [in Russian], AltGTU, Barnaul (2010).
Yu. A. Geller, A. T. Evtushenko, and V. F. Moiseev, “Steels with increased toughness for cold upsetting dies and stamping,” Metalloved. Term. Obrab. Met., No. 8, 49 – 52 (1971).
L. A. Pozdnyak, Yu. M. Skrynchenko, and S. I. Tishaev, Die Steels [in Russian] Metallurgiya, Moscow (180).
N. A. Kostin, V. I. Kolmykov, and E. V. Trusova, “Carbonitriding of die tool steel Kh12F in active paste,” Izv. Yugo-Zapad. Gos. Univ., No. 1, 137 – 139 (2013).
N. A. Kostin and E. V. Trusova, “Carbonitriding of tool steel in an active paste medium,” Metal. Mashinostr., No. 3, 43 – 45 (2014).
N. A. Kostin, V. I. Kolmykov, et al., “RF patent 2501884 C2. Method for carbonitriding die steel components, Patent holder FGBOU VO Kursk State University,” Byull. Izobr. Polezn. Modeli, No. 35 (2013), publ. 12.30.13.
N. A. Kostin, V. I. Kolmykov, et al., “RF patent 2600612 C1. Method for carbonitriding die steel components, Patent holder FGBOU VO Kursk State University,” Byull. Izobr. Polezn. Modeli, No. 30 (2016), publ. 10.27.16.
B. Przhenosil, Carbonitriding [in Russian], Mashinostroenie (1969).
D. A. Prokoshkin, Chemical Heat Treatment of Metals — Carbonitriding [in Russian], Metallurgiya, Moscow 1984).
Yu. M. Lakhtin, G. N. Neustroev, and Yu. P. Ivanov, “Low-temperature cyaniding of tool steels,” Metalloved. Term. Obrab. Met., No. 12, 27 – 31 (1973).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 5, pp. 35 – 40, May, 2020.
Rights and permissions
About this article
Cite this article
Kostin, N.A. Pack Cyaniding of Steel 6Kh4M2FS in Order to Increase Heavily-Loaded Die Durability. Met Sci Heat Treat 62, 331–335 (2020). https://doi.org/10.1007/s11041-020-00565-6
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11041-020-00565-6