Effect of CdTe Addition on the Electrical Properties and AC Susceptibility of YBa₂Cu₃O_7−δ Superconductor

Abstract

The effect of CdTe addition on YBa₂Cu₃O_7−δ (CdTe) _x (x = 0–0.10) has been studied. XRD patterns showed the presence of impurities including CdTe for x ≥ 0.05 wt%. The resistance versus temperature curves showed metallic behavior for all samples. The onset temperature T _{c onset} for all samples is between 90 and 92 K. The superconducting transition width, ΔT _c = 4 K for all samples except for x = 0.1 wt% where ΔT _c = 6 K. The superconducting transition determined by AC susceptibility measurement also showed little change in $T_{\mathrm {c}\chi ^{\prime }}$ (between 89 and 92 K). However, the peak temperature T _p of the imaginary part of the susceptibility χ″, showed a drastic decrease for samples with x > 0.05 wt%. This indicated that the superconducting grains were strongly decoupled for x > 0.05 wt% due to the impurities as observed in the XRD pattern. The intergrain critical current density, J _c at T _p for the x = 0 sample is J _c (82 K) = 17 A cm⁻². These results can be useful in the fabrication of semiconductor/YBCO superconductor hybrid systems.