Abstract
The silver (Ag) thin films were deposited on silicon substrates by DC magnetron sputtering method under different substrate temperatures of 100–500 °C. Then the as-deposited films were subjected to annealing treatment. The XRD results revealed that the Ag thin films have a good nanocrystalline structure and a considerable increase in the crystallinity of Ag (111) peak was observed at substrate temperature of 200 °C. The average crystalline size of Ag films varied between 18 and 44 nm which confirms the presence of nanocrystal’s in the films. The AFM and SEM images demonstrated that the grain size and surface roughness of the films are sensitive to substrate temperature during deposition of the films and annealing treatment. The SEM results is in good agreement with the results of XRD and AFM analysis.
Similar content being viewed by others
References
K. Soderstrom, F.-J. Haug, J. Escarre, C. Pahud, R. Biron, C. Ballif, Sol. Ener. Mater. Sol. Cells 95, 3585–3591 (2011)
C. Guillén, J. Herrero, Appl. Surf. Sci. 32, 4245–4250 (2015)
L.Z. Hsieh, Y.F.C. Chau, C.M. Lim, M.H. Lin, H.J. Huang, C.T. Lin, N.S.M. Idris, Opt.Commun. 370, 85–90 (2016)
G. Schmidl, J. Dellith, H. Schneidewind, D. Zopf, O. Stranik, A. Gawlik, S. Andersa, V. Tympel, C. Katzer, F. Schmidl, W. Fritzsche, Mater. Sci. Eng. B 193, 207–216 (2015)
C.T. Lin, M.N. Chang, H.J. Huang, C.H. Chen, R.J. Sun, B.H. Liao, Y.F.C. Chau, C.N. Hsiao, M.H. Shiao, F.G. Tseng, Electrochim. Acta 192, 15–21 (2016)
M. Ocwieja, M. Morga, Z. Adamczyk, J. Nanopart. Res. 15, 1460 (2013)
P. Zhao, W. Su, R. Wang, X. Xu, F. Zhang, Phys. E 41, 387–390 (2009)
F. Hajakbari, M. Ensandoust, Acta. Phys. Pol. A 129(4), 680–682 (2016)
M. Novotny, J. Bulir, P. Pokorny, J. Lancok, L. Fekete, J. Musil, M. Cekada, Suf. Coat. Technol. 228, S466–S469 (2013)
W.M. Kim, D.Y. Ku, K.S. Lee, B. Cheong, Appl. Surf. Sci. 257, 1331–1336 (2010)
Z. Ghoranneviss, E. Akbarnejad, A. Salar Elahi, M. Ghoranneviss, J. Inorg. Organomet. Polym. 25(6), 1486–1489 (2015)
A.H. Sari, S. Ghorbani, D. Dorranian, P. Azadfar, A.R. Hojabri, M. Ghoranneviss, Appl. Sur. Sci. 255, 2180–2218 (2008)
F. Hajakbari, F. Shafienejad, Jpn. J. Appl. Phys. 55(3), 035503–035508 (2016)
A. Hojabri, F. Hajakbari, A. Emami Meibodi, J. Theor. Appl. Phys. 9, 67–73 (2015)
A. Hojabri, F. Hajakbari, A. Emami Meibodi, M.A. Moghri Moazzen, Acta. Phys. Pol. A 123(2), 307–308 (2013)
S. Firoozbakht, E. Akbarnejad, A. Salar Elahi, M. Ghoranneviss, J. Inorg. Organomet. Polym. 26(4), 889–894 (2016)
D. Dorranian, E. Solati, M. Hantezadeh, M. Ghoranneviss, A. Sari, Vaccum 86, 51–55 (2011)
D. Dorranian, L. Dejam, A.H. Sari, A. Hojabri, J. Theor. Appl. Phys. 3, 37–41 (2009)
I. Horcas, J.M. Fernandez, j. Gomez-Roderiguez, J. Colchero, J. Gomez-Herrero, A.M. Baro, Rev, Sci. Instrum. 78, 013705–013713 (2007)
V. Saravanan, P. Shankar, G.K. Mani, J.B.B. Rayappan, J. Anal. Appl. Pyrolysis 111, 272–277 (2015)
A. Hojabri, N. Haghighian, K. Yasserian, M. Ghoranneviss, IOP Conf. Ser. 12, 012004–012007 (2010).
S. He, Y. Li, X. Liu, B. Tao, D. Li, Q. Lu, Thin Solid Films 478, 261 (2005)
D.C. Tsai, S.C. Liang, Z.C. Chang, T.N. Lin, M.H. Shiao, F.S. Shieu, Surf. Coat. Technol. 207, 293–299 (2012)
R.M. Jafer, H.C. Swart, A. Yousif, E. Coetsee, Solid State Sci. 53, 30–36 (2016)
M.R. Hantezadeh, R. Bavadi, A.H. Sari, M. Ghoranneviss, J. Fusion Energy 30, 333–337 (2011)
Acknowledgments
This work was supported by Islamic Azad University, Karaj Branch, Karaj, Iran.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Hojabri, A., Kavyani, Z. & Ghoranneviss, M. Effect of Substrate Temperatures on Structural and Morphological Properties of Nano-Crystalline Silver Thin Films Grown on Silicon Substrates. J Inorg Organomet Polym 27, 53–60 (2017). https://doi.org/10.1007/s10904-016-0443-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10904-016-0443-2