Abstract
Basalt fiber composites are beneficial for electrical equipment because of their low weight, strong strength, high temperature resistance, and corrosion resistance. Three different sizing agents were developed to modify basalt fibers in order to improve the interface bonding state of basalt fiber composites. The morphology, composition, and surface energy of the modified fibers were characterized by SEM, FT-IR, contact angle analysis, and other methods. The findings demonstrated that the sizing agent can be well adsorbed on the fiber surface, and the modification effect was best at a polyurethane lotion concentration of 1wt%. The mechanical properties of the composite, including flexural strength, flexural modulus, tensile strength, and interlaminar shear strength, were increased by 21.05%, 31.46%, 13.89%, and 41.46%, respectively. In terms of insulation performance, the breakdown strength can be increased by 31.73%, and the leakage current and dielectric loss factor can be reduced by 22.76% and 12.32%, respectively. The maximum decomposition rate and storage modulus of the composites dropped, while the glass transition temperature rose, according to the TGA and DMA data following the sizing agent treatment.
Similar content being viewed by others
Data and code availability
Not applicable.
References
Chang XJ, Wang ZX, Quan S, Xu YC, Jiang ZX, Shao L (2014) Exploring the synergetic effects of graphene oxide (GO) and polyvinylpyrrodione (PVP) on poly (vinylylidenefluoride) (PVDF) ultrafiltration membrane performance. Appl Surf Sci 316:537–548. https://doi.org/10.1016/j.apsusc.2014.07.202
Morova N (2013) Investigation of usability of basalt fibers in hot mix asphalt concrete. Constr Build Mater 47:175–180. https://doi.org/10.1016/j.conbuildmat.2013.04.048
Lou K, Kang A, Xiao P, Wu Z, Li B, Wang X (2021) Effects of basalt fiber coated with different sizing agents on performance and microstructures of asphalt mixture. Constr Build Mater 266:121–155. https://doi.org/10.1016/j.conbuildmat.2020.121155
Dhand V, Mittal G, Rhee KY, Park SJ, Hui D (2015) A short review on basalt fiber reinforced polymer composites. Compos Part B Eng 73:166–180. https://doi.org/10.1016/j.compositesb.2014.12.011
Krasnovskih MP, Maksimovich NG, Vaisman YI, Ketov AA (2014) Thermal stability of mineral-wool heat-insulating materials. Rus J Appl Chem 87:1430–1434. https://doi.org/10.1134/S1070427214100061
Liu H, Yu Y, Liu Y, Zhang M, Li L, Ma L, Sun Y, Wang W (2022) A Review on basalt fiber composites and their applications in clean energy sector and power grids. Polymers 14:2376. https://doi.org/10.3390/polym14122376
Yang Z, Liu J, Feng X, Li S, Xu Y, Ren J (2018) Investigation on mechanical properties and failure mechanisms of basalt fiber reinforced aluminum matrix composites under different loading conditions. J Compos Mater 52:1907–1914. https://doi.org/10.1177/0021998317733807
Balaji KV, Shirvanimoghaddam K, Rajan GS, Ellis AV, Naebe M (2020) Surface treatment of Basalt fiber for use in automotive composites. Mater Today Chem 17:100344. https://doi.org/10.1016/j.mtchem.2020.100334
Hou Y, Li M, Gu Y, Yang Z, Li R, Zhang Z (2018) Gamma ray shielding property of tungsten powder modified continuous basalt fiber reinforced epoxy matrix composites. Polym Compos 39:2106–2115. https://doi.org/10.1002/pc.24469
Blaznov AN, Atyasova EV, Shundrina IK, Samoilenko VV, Firsov VV, Zubkov AS (2017) Thermomechanical characterization of BFRP and GFRP with different degree of conversion. Polym Test 60:49–57. https://doi.org/10.1016/j.polymertesting.2017.03.011
Wang Q, Ding Y, Randl N (2021) Investigation on the alkali resistance of basalt fiber and its textile in different alkaline environments. Constr Build Mater 272:121670. https://doi.org/10.1016/j.conbuildmat.2020.121670
Arslan C, Dogan M (2018) The effects of silane coupling agents on the mechanical properties of basalt fiber reinforced poly (butylene terephthalate) composites. Compos B Eng 146:145–154. https://doi.org/10.1016/j.compositesb.2018.04.023
Wang G, Liu Y, Guo Y, Zhang Z, Xu M, Yang Z (2007) Surface modification and characterizations of basalt fibers with non-thermal plasma. Surf Coat Technol 20:6565–6568. https://doi.org/10.1016/j.surfcoat.2006.09.069
Zhu M, Ma J (2019) Basalt fiber modified with lanthanum-ethylenediaminetetraacetic acid as potential reinforcement of cyanate matrix composites. Appl Surf Sci 464:636–643. https://doi.org/10.1016/j.apsusc.2018.09.129
Berg J, Jones FR (1998) The role of sizing resins, coupling agents and their blends on the formation of the interphase in glass fiber composites. Compos A: Appl Sci Manuf 29:1261–1272. https://doi.org/10.1016/S1359-835X(98)00091-8
Xing D, Xi X, Qi M, Zheng Q, Ma P (2020) Optimization on the formulation of sizing to enhance the mechanical properties of basalt fiber. J Text Inst 112:515–525. https://doi.org/10.1080/00405000.2020.1771078
Guo X, Lu Y, Sun Y, Wang J, Li H, Yang C (2018) Effect of sizing on interfacial adhesion property of glass fiber-reinforced polyurethane composites. J Reinf Plast Compos 37:321–330. https://doi.org/10.1177/0731684417744664
Wei B, Cao H, Song S (2010) Tensile behavior contrast of basalt and glass fibers after chemical treatment. Mater Des 31:4244–4250. https://doi.org/10.1016/j.matdes.2010.04.009
Wang Z, Luo H, Zhang J, Chen H, Zhang L, Wu L, Jiang H (2021) Water-soluble polysiloxane sizing for improved heat resistance of basalt fiber. Mater Chem Phys 272:125024. https://doi.org/10.1016/j.matchemphys.2021.125024
Chen Z, Huang Y (2021) Preparation and performance of fumed silica-stabilized epoxy resin pickering emulsion for basalt fiber-sizing agents. Adv Compos Hybrid Mater 4:1205–1214. https://doi.org/10.1007/s42114-021-00210-7
Liu Y, Wang W, Liu H, Zhang M, Liu J, Qi J (2022) Blending modification of alicyclic resin and bisphenol a epoxy resin to enhance salt aging resistance for composite core rods. Polymers 14(12):2394. https://doi.org/10.3390/polym14122394
Shi F, Dai Z, Zhang B (2010) Characterization of the surface tension and solubility parameter of epoxy resin by using inverse gas chromatography. Se Pu 28:697–701. https://doi.org/10.3724/sp.j.1123.2010.00697
Sun Z, Zhang M, Zhang X, Liang C, Zhang H, Li Y, Ma MY (2021) Study on thermal stability of bisphenol⁃a⁃type epoxy matrix composites doped with nano glass powders. China Plastics 35:15–20. https://doi.org/10.19491/j.issn.1001-9278.2021.09.003
Saeed A, Shabir G (2013) Synthesis of thermally stable high gloss water dispersible polyurethane/polyacrylate resins. Prog Org Coat 76:1135–1143. https://doi.org/10.1016/j.porgcoat.2013.03.009
Liu Y, Zhang M, Liu H, Sun Y, Wang W, Liu J (2017) The influences of silane coupling agents on the heat and moisture resistance of basalt fibre-reinforced composites. High Volt 32:25–36. https://doi.org/10.1049/hve2.12217
Sima WX, He JH, Sun PT, Yang M, Yin Z, Li C (2020) Novel nanostructure composite dielectric with high insulation performance: silica-based nanometer-sized porous composite insulating paper reinforced by ceramic fibers. Scr Mater 181:58–61. https://doi.org/10.1016/j.scriptamat.2020.02.016
Li Z, Zhou W, Yang L, Chen P, Yan C, Cai C, Li H, Li L, Shi Y (2019) Glass fiber-reinforced phenol formaldehyde resin-based electrical insulating composites fabricated by selective laser sintering. Polymers 11(1):135. https://doi.org/10.3390/polym11010135
Acknowledgements
The authors acknowledge the financial support from the Fundamental Research Funds for the Central Universities (no. 20226934), and Science and technology project of China Southern Power Grid Co. (no. 073000KK52200014).
Author information
Authors and Affiliations
Contributions
HL was involved in conceptualization, methodology, validation, writing—review and editing, funding acquisition; YY contributed to software, investigation, data curation, writing—original draft preparation, project administration; MZ was involved in methodology, investigation, writing—review and editing, data curation; HY software, resources, data curation; LL contributed to visualization, supervision, methodology; YL was involved in resources, project administration, validation; HY contributed to formal analysis, visualization, resources; ZT was involved in visualization, supervision, project administration.
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Ethical approval
Not applicable.
Additional information
Handling Editor: Stephen Eichhorn.
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Liu, H., Yu, Y., Zhang, M. et al. Effect of sizing agent on properties of basalt fiber/blended resin matrix composites. J Mater Sci 58, 5642–5657 (2023). https://doi.org/10.1007/s10853-023-08373-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-023-08373-y