Effect of alkaline excess on sintering, microstructural, and electrical properties of Li0.12Na0.88NbO3 ceramics

  • Original Paper
  • Published:
Journal of Materials Science Aims and scope Submit manuscript

Abstract

Sintering behavior in Li0.12Na0.88NbO3 (LNN-12) ceramics has been investigated by analyzing the microstructures of the samples sintered at different temperatures (1050–1250 °C) and durations (1–6 h) to optimize the sintering conditions. An excess amount of Li2CO3 was added (1, 3, 5 mol%) to stoichiometric LNN-12 in order to compensate for the probable alkaline element loss at higher optimized sintering temperature. The addition of excess Li2CO3 into the starting materials and the effect of it on microstructure and electrical properties were investigated. Microstructural study of Li2CO3-added samples revealed abnormal grain growth, a characteristic feature of liquid phase sintering due to the low melting Li2CO3. The temperature and frequency dependence of dielectric constant shows two phase transitions in temperature dependence and low-frequency dispersion in the frequency dependence of dielectric plot. The observed frequency dispersion is attributed to dominant DC conductivity. The conduction mechanism was identified as diffusion of intrinsic Li+ ion. The room-temperature dielectric constant and loss factor were found to increase with increase in Li2CO3 addition from 160 to 690 and 0.02 to 0.04, respectively. The electrical conductivity was found to increase two orders of magnitude (10−12–10−10 Ω−1 cm−1) in Li2CO3-added samples as compared to stoichiometric composition. The results obtained here give a strong evidence of the stoichiometry–microstructure and electrical properties correlation, thus emphasizing on the importance of processing parameters to tune the desired properties in Li0.12Na0.88NbO3 ceramics.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Figure 1
Figure 2
Figure 3
Figure 4
Figure 5
Figure 6
Figure 7
Figure 8
Figure 9
Figure 10

Similar content being viewed by others

References

  1. Henson RM, Zeyfang RR, Kiehl KV (1977) Dielectric and electromechanical properties of (Li, Na)NbO3 ceramics. J Am Ceram Soc 60:15–17

    Article  Google Scholar 

  2. Hardiman B, Henson RM, Reeves CP, Zeyfang RR (1976) Hot pressing of sodium lithium niobate ceramics with perovskite-type structures. Ferroelectrics 12:157–159

    Article  Google Scholar 

  3. Chen Q, Peng Z, Liu H, Xiao D, Zhu J, Zhu J (2010) The crystalline structure and phase-transitional behavior of (Li0.12Na0.88)(Nb1−x%Sb x%)O3 lead-free piezoelectric ceramics with high Q m . J Am Ceram Soc 93:2788–2794

    Article  Google Scholar 

  4. Mitra S, Kulkarni AR, Prakash O (2013) Densification behaviour and two stage master sintering curve in lithium sodium niobate ceramics. Ceram Int 39:S65–S68

    Article  Google Scholar 

  5. Pelton AD, Bale CW, Lin PL (1984) Calculation of phase diagrams and thermodynamic properties of 14 additive and reciprocal ternary systems containing Li2CO3, Na2CO3, K2CO3, Li2SO4, Na2SO4, K2SO4, LiOH, NaOH, and KOH. Can J Chem 62:457–474

    Article  Google Scholar 

  6. Maeder MD, Damjanovic D, Setter N (2004) Lead free ferroelectric materials. J Electroceram 13:385–392

    Article  Google Scholar 

  7. Jenko D, Malic B, Bernard JB, Cilensek J, Kosec M (2003) Synthesis and sintering of KNN 50/50 ceramics. Mater Technol 37:22–28

    Google Scholar 

  8. Li J-F, Wang K, Zhang B-P, Zhang L-M (2006) Ferroelectric and piezoelectric properties of fine-grained Na0.5K0.5NbO3 lead-free piezoelectric ceramics prepared by spark plasma sintering. J Am Ceram Soc 89:706–709

    Article  Google Scholar 

  9. Zhen Y, Li J-F (2006) Normal sintering of (K, Na)NbO3-based ceramics: influence of sintering temperature on densification, microstructure, and electrical properties. J Am Ceram Soc 89:3669–3675

    Article  Google Scholar 

  10. Bomlai P, Wichianrat P, Muensit S, Milne SJ (2007) Effect of calcination conditions and excess alkali carbonate on the phase formation and particle morphology of Na0.5K0.5NbO3 powders. J Am Ceram Soc 90:1650–1655

    Article  Google Scholar 

  11. Mitra S, Kulkarni AR, Prakash O (2013) Diffuse phase transition and electrical properties of lead-free piezoelectric (Li x Na1−x )NbO3 (0.04 ≤ x ≤ 0.20) ceramics near morphotropic phase boundary. J Appl Phys 114:064106

    Article  Google Scholar 

  12. Cheng L-Q, Wang K, Yao F-Z, Zhu F, Li J-F (2013) Composition inhomogeneity due to alkaline volatilization in Li-modified (K, Na)NbO3 lead-free piezoceramics. J Am Ceram Soc 96:2693–2695

    Article  Google Scholar 

  13. Shaw NJ (1989) Densification and coarsening during solid state sintering of ceramics: a review of the models. I. Densification. Powder Metall Intl 2(8):16–21

    Google Scholar 

  14. Rahaman MN (2003) Ceramic processing and Sintering. Marcel Dekker, New York

    Google Scholar 

  15. Zhen Y, Li J-F (2007) Abnormal grain growth and new core–shell structure in (K, Na)NbO3-based lead-free piezoelectric ceramics. J Am Ceram Soc 90:3496–3502

    Article  Google Scholar 

  16. Patro PK, Kulkarni AR, Harendranath CS (2004) Dielectric and ferroelectric behavior of SBN50 synthesized by solid-state route using different precursors. Ceram Int 30:1405–1409

    Article  Google Scholar 

  17. Huanosta A, West AR (1987) The electrical properties of ferroelectric LiTaO3 and its solid solutions. J Appl Phys 61:5386

    Article  Google Scholar 

  18. Nobre MAL, Lanfredi S (2001) Phase transition in sodium lithium niobate polycrystal: an overview based on impedance spectroscopy. J Phys Chem Solids 62:1999–2006

    Article  Google Scholar 

  19. Andrew KJ (1999) Dielectric relaxation in solids. J Phys D Appl Phys 32:R57

    Article  Google Scholar 

  20. Shulman HS, Testorf M, Damjanovic D, Setter N (1996) Electrical conductivity, and piezoelectric properties of bismuth titanate. J Am Ceram Soc 79:3124–3128

    Article  Google Scholar 

  21. Wu Y, Cao G (2000) Ferroelectric and dielectric properties of strontium bismuth niobate vanadates. J Mater Res 15:1583–1590

    Article  Google Scholar 

  22. Park BH, Hyun SJ, Bu SD, Noh TW, Lee J, Kim H-D, Kim TH, Jo W (1999) Differences in nature of defects between SrBi2Ta2O9 and Bi4Ti3O12. Appl Phys Lett 74:1907–1909

    Article  Google Scholar 

Download references

Acknowledgements

S.M. would like to thank SAIF, IIT, Bombay, for providing SEM facility.

Author information

Author notes

  1. Supratim Mitra

    Present address: NIIT University, Neemrana, Rajasthan, 301705, India

Authors and Affiliations

  1. Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology Bombay, Mumbai, 400076, India

    Supratim Mitra & Ajit R. Kulkarni

  2. Powder Metallurgy Division, Materials Group BARC, Vashi Complex, Navi, Mumbai, India

    Pankaj K. Patro

Authors
  1. Supratim Mitra
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Pankaj K. Patro
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Ajit R. Kulkarni
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Supratim Mitra.

Ethics declarations

Conflict of interest

All the authors certify that they have no affiliations or involvement in any organization or entity with any financial interest or non-financial interest in the subject matter or materials discussed in this manuscript.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Mitra, S., Patro, P.K. & Kulkarni, A.R. Effect of alkaline excess on sintering, microstructural, and electrical properties of Li0.12Na0.88NbO3 ceramics. J Mater Sci 51, 9031–9042 (2016). https://doi.org/10.1007/s10853-016-0156-5

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10853-016-0156-5

Keywords

Search

Navigation