Abstract
An investigation has been conducted on AZ91 magnesium alloy processed in high-pressure torsion (HPT) at 296, 423 and 473 K for different numbers of turns. The microstructure has altered significantly after processing at all processing temperatures. Extensive grain refinement has been observed in the alloy processed at 296 K with apparent grain sizes reduced down to 35 nm. Segmentation of coarse grains by twinning has been observed in the alloy processed at 423 K and 473 K with average apparent grain sizes of 180 nm and 250 nm. Substantial homogeneity in microhardness has been observed in the alloy processed at 296 K compared to that found at 423 K and 473 K. The ultrafine-grained AZ91 alloy exhibited a significant dependence of the yield strength on grain size as shown by the microhardness measurements, and it obeys the expected Hall–Petch relationship. The alloying elements, fraction of nano-sized particles of β-phase, and the dominance of basal slip and pyramidal modes have additional effects on the strengthening of the alloy processed at 296 K.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Avoid common mistakes on your manuscript.
Introduction
Magnesium alloys are promising alternatives to replace denser materials, such as steel and aluminium alloys, with the objective of meeting requirements to save fuel by manufacturing light weight/high strength parts [1]. The mechanisms of deformation in magnesium alloys at room temperature are basal slip and twinning, which result in a limitation in their workability at room temperature [2]. The limited ductility and workability of these alloys can be improved at higher temperatures by the activation of additional slip systems [1]. Thermo-mechanical processing is used to improve the workability of these alloys, although such processing is associated with grain growth and a greater consumption of energy [3]. Several processing routes have been introduced to achieve optimization of the microstructure, and these routes include dynamic recrystallization under high-temperatures in ECAP processing [4], HPT processing [5, 6], ECAP processing at relatively low temperatures assisted by a back-pressure [7], or through the use of a higher channel angle of pressing die in ECAP processing [8]. The majority of the earlier work in SPD processing of magnesium alloys, especially for AZ91 alloy, has been conducted using ECAP at elevated temperatures (≥473 K) [2, 4, 9] with resultant grain refinement being achieved in the micrometre range. The AZ91 alloy (Mg–9wt%Al–1wt%Zn–0.3wt%Mn) is a common alloy in the Mg–Al–Zn family. This alloy has a good strength-to-density ratio, good corrosion resistance and ease of production and machining [3]. To date, only one investigation has been conducted on Mg–9wt%Al alloy [6] using HPT at room temperature. The development of microstructure and microhardness across horizontal and vertical cross-sections of AZ91 samples processed by HPT has not been reported to date. This research describes the microstructural homogeneity and development of microhardness in AZ91 alloy after processing by HPT at different processing temperatures. The dislocation density, distribution of β-phase and Hall–Petch relationship have also been investigated.
Experimental materials and procedures
AZ91 alloy (Mg–9 %Al–1 %Zn) in the form of an extruded rod was used in this work, the alloy was supplied by Magnesium Elektron Co. (Manchester, UK). Thin discs were made of the extruded rod with thicknesses of 1.5 mm and final thicknesses of 0.85 mm. The HPT processing was conducted at 296, 423 and 473 K using a HPT facility that has been previously discussed in detail elsewhere [10]. The HPT processing was conducted under a quasi-constrained condition at a speed of 1 rpm using an applied pressure of 3.0 GPa for differing numbers of turns: N = 1/2, 1, 5 and 10 turns. The as-received and processed microstructures were observed using optical microscopy (OM, OLYMPUS-BX51, Japan) and scanning electron microscopy (SEM, JEOL JSM-6500F, Japan). Subsequently, a transmission electron microscope (TEM, JEOL JEM-3010) was used for microstructural observation of the alloy after HPT processing. The chemical compositions of the as-received and processed alloy were analysed using energy-dispersive spectroscopy (EDS). The area fraction and average size of the β-phase particles in the as-received alloy and processed alloy were determined by ImageJ software using a point count technique [11]. X-ray diffraction was used to determine the crystallite size and dislocation density in the processed alloy using an XRD facility (D2 Phaser, Germany). The diffraction data were analysed using Rietveld refinement based software program (MAUD). Microstructural observations and microhardness testing were conducted over the horizontal and vertical cross-sections that are illustrated schematically in Fig. 1a, b. The microhardness measurements of the processed disc were conducted using a Vickers microhardness tester (FM-300, Japan) and using an applied load of 100 gf and a dwell time of 15 s. The microhardness data were recorded at separation distances of 0.3 and 0.1 mm throughout the entire horizontal and vertical cross-sections, as reported earlier [5, 12].
An illustration of a HPT disc shows a the horizontal cross-section, and b The vertical cross-section. These cross-sections were used in the microstructural and microhardness observations. The arrow from the centre to the edge refers to the longitudinal (radial) direction, whereas the arrow from the upper surface to lower surface refers to the through-thickness (vertical) direction
Experimental results
The microstructure of the AZ91 magnesium alloy prior to and after HPT processing is shown in Fig. 2. The as-received AZ91 alloy has an average grain size of 30 µm and an average value of Vickers microhardness of 70 ± 5. The initial and processed microstructures consist of two main phases: α-Mg matrix, β-phase and Al8Mn5 particles as shown in Fig. 2a, b. The chemical analysis obtained by EDS of alloying elements in the alloy processed at 296 K for N = 5 turns is shown in Fig. 3. The alloy constituents were identical before and after HPT as shown earlier [13]. The processed microstructure at 296 K showed extensive grain refinement, and the original decoration of the grain boundaries by β-phase disappeared with increasing number of turns as shown in Fig. 2b, c. The β-phase fragmented into nano-sized particles as observed in Fig. 2b–d and appears aligned along the direction of torsional straining. A strong degree of grain refinement after processing at 296 K was observed with an apparent grain size down to 500 and 50 nm observed after N = 1/2 and 1 turn, respectively, as shown in Fig. 2e, f. A reduction in the crystallite size from 60 to 35 nm was found with increasing number of turns up to N = 10 turns. The processed microstructures at 296 K across the vertical cross-sections are shown in Fig. 4. The microstructure seems slightly deformed with the presence of twinning as shown in Fig. 4a. Shear bands decorated by the β-phase were observed aligned parallel to the radial direction across the vertical cross-section as observed in Fig. 4b. Recorded peaks by XRD as shown in Fig. 5 are prismatic planes \( \left( {10\bar{1}0} \right) \), \( \left( {11\bar{2}0} \right) \), \( (20\bar{2}0) \), basal plane \( (0002) \) and pyramidal planes \( (10\bar{1}1) \), \( (10\bar{1}2) \), \( (10\bar{1}3) \). The microstructures of the alloy processed at 423 and 473 K are shown in Fig. 6. The samples showed twinning, and the distribution of twinning increased and spread gradually with increasing number of turns. The microstructures were effectively refined by the segmentation of the coarse grains by twinning as observed in Fig. 6a, b. However, grain growth has been observed at 473 K with increasing number of turns up to N = 5 turns as shown in Fig. 6b. The apparent area fraction has increased (which may reflect a sampling effect once the second phase is more homogeneously distributed), and the average size of the β-phase particles has been refined down to 200 nm in the processed alloy compared to the as-received alloy as shown in Fig. 7. A gradual development in the microhardness over the horizontal and vertical cross-sections has been achieved with increasing number of turns up to N = 10 turns as shown in Figs. 8 and 9. The distributions of microhardness were relatively lower for the alloy processed at 423 and 473 K than at 296 K. A significant increase in the microhardness has been observed as shown in Fig. 10, with increasing equivalent strain imposed during HPT for the alloy processed at 296 K. A significant dependency of the microhardness on the crystallite size of the AZ91 alloy processed at 296 K is shown in Fig. 11. The lower processing temperature leads to finer crystallite size, higher microhardness and dislocation density, and at elevated temperatures, these outcomes decreased significantly as the number of turns increased as shown in Fig. 12.
Microstructural observations using SEM for a the as-received alloy, b the alloy processed for N = 1 turn (296 K), c the alloy processed for N = 10 turns (296 K) and d the nano-sized particles of β-phase in the alloy processed for N = 10 turns (296 K), and TEM observation of the alloy processed for e N = 1/2 turn (296 K) and f N = 1 turn (296 K). The corresponding numbers (1, 2, 3) in the micrograph a represent the lamellar, agglomerate forms of the β-phase (Mg17Al12) and Al8Mn5 particle, respectively
The colour-coded maps of the microhardness over the horizontal cross-sections of the AZ91 discs processed forf a N = 1/2 turn (296 K), b N = 1 turn (296 K), c N = 5 turns (296 K), d N = 10 turns (296 K), e N = 10 turns (423 K) and f N = 10 turns (473 K). The small inset in the figure shows the scale of the microhardness with regard to each colour (Color figure online)
The colour-coded maps of the microhardness distributions over the vertical cross-sections of the AZ91 discs processed for N = 10 turns at 296 K (upper), 423 K (centre) and 473 K (lower). The small inset in the figure shows the scale of the microhardness with regard to each colour (Color figure online)
Discussion
Feasibility of HPT processing of AZ91 magnesium alloy
The TEM and XRD revealed the occurrence of extensive grain refinement in the AZ91 alloy due to the imposition of a very high plastic strain by HPT at 296 K. However, for the sample processed for N = 1/2 turn, it is noteworthy that the value of the crystallite size obtained by XRD was significantly lower than the apparent grain size measured by TEM. This difference between the measurements via XRD and TEM is expected in SPD-processed materials, because the grains in these materials are made of subgrains and/or dislocation cells. Thus, coherent scattering of the X-ray from these substructures represents the (smaller) mean crystallite size rather than grains which can be more easily observed in TEM [14]. The feasibility of HPT processing at 296 K for the AZ91 magnesium alloy can be attributed to the presence of hydrostatic pressure, which prevents propagation of fracture during processing [6–8]. Furthermore, the geometry of the processing zone constrains the alloy within a specific volume as illustrated earlier and thus activation of twinning [8, 15, 16]. The XRD observations indicate the orientation of the processed microstructure towards twinning and basal deformation modes under HPT conditions that facilitate processing at room temperature [16]. The unidirectional nature of straining during HPT processing may have contributed to re-orientation of the microstructure towards easy slip [17]. The twinning activity has persisted in the processed alloy at 296 K with increasing number of turns, which confirms its accommodation for the higher imposed strain produced by HPT [18].
Grain refinement in AZ91 alloy
The relatively high content of aluminium in the AZ91 magnesium alloy leads to a significant reduction in the stacking fault energy through the solute–dislocation interaction and results in smaller grain sizes under SPD processing [19]. The effect of dynamic recovery was absent as the alloy has been processed at room temperature. It is anticipated that the homogeneity developed gradually with further straining at room temperature as mentioned by several investigators [20–23]. The grain refinement in the processed alloy at 423 K has developed efficiently by twinning intersections and the grain subdivision mechanism. At this temperature, dynamic recrystallization was absent or had a minor effect on the refinement process compared to the twinning activity. It is likely that dynamic recrystallization may have contributed to grain refinement in the processed alloy at 473 K. However, the formation and fragmentation of twinning appears to be the dominant mechanism for refinement at 473 K. The HPT-processed alloy at 423 and 473 K has significantly refined apparent grain sizes of 180 and 250 nm, respectively, which are finer than in the previously reported ECAP [20, 24–26], FSP [27] and ARB-processed alloys [28]. In the aforementioned SPD techniques, grain refinement occurs mainly by dynamic recrystallization with resultant microstructures of micrometre size grains. The severe levels of deformation in the alloy and the deformation incompatibility between α-Mg matrix and β-phase have resulted in fragmentation of the β-phase [29]. The significant dispersion of nano-sized particles of the β-phase during processing had a pinning effect on grain growth at a higher number of turns and elevated temperatures [23]. The alloy processed at 296 K showed microstructural homogeneity at the initial stage of HPT processing rather than the heterogeneity observed in the alloy processed at 423 and 473 K, which required further processing turns and/or higher processing temperature to achieve a reasonable homogeneity [10]. The temperature rise expected during HPT processing at room temperature does not exceed 293 K for samples processed at 296 K for N = 10 turns. This value of temperature rise has been calculated using the equation stated in [30], and is similar to the experimental value (290 K) measured directly from the thermocouple located in the upper anvil. The low value of temperature rise can be attributed to (1) the heat loss from relatively small samples in contact with the much larger HPT anvils and (2) due to the low strain rates of deformation in HPT processing [31]. A further factor, making the heat generated low, is the lower friction expected between the relatively lower strength magnesium alloy and the high strength (high speed tool steel) anvils [15, 31]. As a result, any temperature rise due to processing is considered negligible and unlikely to produce any occurrence of recrystallization or grain growth during processing at room temperature [32].
Development of microhardness
The initial heterogeneity of microstructures leads to an initial heterogeneity in the distribution of microhardness [10, 33, 34]. The difference in grain sizes at the centre and edge regions was diminished by further straining, where a gradual evolution towards homogeneity was found in the observed microstructure and microhardness at both centre and edge regions at a higher number of turns [10, 35]. The existence of misalignment between the anvils at a high number of turns causes an additional deformation at the centre region of the processed disc, which appears as an increase in the measured microhardness [36, 37]. The development of microhardness after HPT processing depends on the stacking fault energy of the alloy [10, 19]. The AZ91 alloy with a low stacking fault energy [38] shows a slow rate of dynamic recovery during processing at room temperature, thus strain hardening occurs at a fast rate during processing [20, 32]. The AZ91 alloy processed in HPT showed an earlier saturation in the microhardness distribution than for the AZ31 alloy [21] processed in HPT at room temperature. The stacking fault energy is lower, and the fraction of particles of β-phase is higher in the AZ91 alloy than for the AZ31 alloy [38, 39]. Therefore, the evolution of grain refinement and strain hardening occurred at faster rates in the AZ91 alloy than for the AZ31 alloy. The overall microhardness values for the alloy processed at 473 K were significantly lower than for their counterparts processed at 296 and 423 K, due to the variation in dislocation density with processing temperature [14]. However, the level and homogeneity of strengthening are still higher when processing by HPT at elevated temperatures than observed in ECAP [26], and FSP [27], where strengthening has been lowered by dynamic recrystallization, over-ageing and precipitate coarsening [26, 27]. The microhardness distributions in the AZ91 alloy are heterogeneous along the through-thickness directions in the initial stage of deformation. This is supported by the differences in microstructural observations along this direction. A sufficient high number of turns may reduce heterogeneity, by filling the alloy in-between the anvils and achieving a significant sticking condition which then increases the deformation and microstructural homogeneity [5, 12, 15, 40, 41]. The distribution of microhardness along the vertical and horizontal cross-sections showed considerable consistency for the current alloy processed at each specific processing temperature. This indicates the development of microstructural homogeneity with increasing imposed strain at each condition [8]. This consistency in the AZ91 alloy has not been observed in the AZ31 alloy or AZ91 alloy processed by ECAP [26] and FSP [27]. This is attributed to the difference in the aluminium content and stacking fault energy in both alloys, which control the extent of grain refinement, dislocation density, achieved homogeneity and resultant mechanical properties [14, 21, 38]. The behaviour of strain hardening and homogeneity of microhardness in the AZ91 alloy follows a standard model of hardness evolution with increasing equivalent strain reported in earlier work [20].
The effect of the equivalent strain on the Hall–Petch relation and dislocation density
The increase in the equivalent strain resulted in an evolution in microstructure and a gradual development in the microhardness [10]. The strength of the alloy in terms of its microhardness improved significantly with grain refinement at room temperature. This proportionality has been expressed by the Hall–Petch relationship for hardness measurements: \( Hv = H_{0} + k_{H} d^{ - 1/2} \) [42]. The effect of grain refinement on the strength of the ultrafine-grained alloy AZ91 alloy showed a significant consistency with this Hall–Petch relationship. The material constants are \( H_{0} \) = 76 MPa and \( k_{H} \) = 233 MPa μm1/2, which is relatively higher than those found for AZ31 and AZ61 alloys (\( H_{0} \) = 647–697 MPa and \( k_{H} \) = 118–170 MPa μm1/2) [7, 22, 43]. Thus, the ultrafine-grained AZ91 alloy shows a relatively higher level of hardness than for AZ31 and AZ61 alloys processed by HPT and ECAP processing at room temperature and elevated temperatures [21, 22, 44]. The difference in \( k_{H} \) can be attributed to the difference in alloying constituents in the mentioned alloys, where the high content of alloying element in the AZ91 alloy resulted in a lowering of its stacking fault and thus a finer microstructure and a higher dislocation density in the AZ91 alloy after processing than in the AZ61 and AZ31 alloy [19, 21, 22]. The evolution in dislocation density with increase of imposed strain in HPT has a major effect on the achieved strengthening in the AZ91 alloy. The evolution of dislocation density is affected by the fraction of nano-sized particles of β-phase, value of applied pressure in HPT, and value of stacking fault energy. The widely distributed β-phase fine particles are reported as acting as barriers for mobile dislocations during deformation [39]. The high value of applied pressure has also been reported to enhance the obstruction of defect migration in the processed material and then promotes the suppression of dislocation annihilation [45, 46]. The low stacking fault energy in the AZ91 alloy leads to a significant inhibition of dislocation cross-slip, and formation of a high density of planar arrays of dislocations has also been reported [10, 38].
Conclusions
-
1.
AZ91 magnesium alloy has been effectively processed in HPT processing at room temperature with an ultrafine-grained microstructure down to 35 nm. The alloy processed at 423 and 473 K has been significantly refined by twinning segmentation of the original grains into fine grains with average apparent grain sizes of 180 and 250 nm, respectively.
-
2.
Fragmentation and alignment of the β-phase in the direction of torsional strain have been observed during processing. This phase has been refined down to nanometre sizes with a higher fraction as the number of turns increased, indicating the very high level of plastic deformation that is imparted to the alloy during HPT.
-
3.
Existence of twins at all processing temperatures and their distribution was proportional to processing temperature and the number of turns. The occurrence of twinning has been induced by the need for re-orientation of the microstructure towards the slip direction and to accommodate severe plastic deformation.
-
4.
Lower processing temperature has resulted in homogenous microstructure and significant development of strength. Higher processing temperatures have resulted in heterogeneous microstructures especially in the initial stages of HPT and this heterogeneity decreased gradually at higher numbers of turns.
-
5.
A considerable dislocation density has developed with increasing the number of turns at lower processing temperature rather than at higher processing temperatures. The values of dislocation density after HPT were higher than earlier reported data for the same alloy.
-
6.
The ultrafine-grained AZ91 alloy follows the Hall–Petch relationship, and this emphasizes the significant dependence of strength on grain size. The higher alloying content, fraction of nano-sized particles of β-phase and the dominance of basal slip and pyramidal modes after processing also have a significant effect on the strengthening of the alloy processed at 296 K.
References
Ravi Kumar NV, Blandin JJ, Desrayaud C, Montheillet F, Suéry M (2003) Grain refinement in AZ91 magnesium alloy during thermomechanical processing. Mater Sci Eng A 359:150–157
Yamashita A, Horita Z, Langdon TG (2001) Improving the mechanical properties of magnesium and a magnesium alloy through severe plastic deformation. Mater Sci Eng A 300:142–147
Kubota K, Mabuchi M, Higashi K (1999) Processing and mechanical properties of fine-grained magnesium alloys. J Mater Sci 34:2255–2262. doi:10.1023/A:1004561205627
Mabuchi M, Iwasaki H, Yanase K, Higashi K (1997) Low temperature superplasticity in an AZ91 magnesium alloy processed by ECAE. Scr Mater 36:681–686
Figueiredo RB, Langdon TG (2011) Development of structural heterogeneities in a magnesium alloy processed by high-pressure torsion. Mater Sci Eng A 528:4500–4506
Kai M, Horita Z, Langdon TG (2008) Developing grain refinement and superplasticity in a magnesium alloy processed by high-pressure torsion. Mater Sci Eng A 488:117–124
Xia K, Wang JT, Wu X, Chen G, Gurvan M (2005) Equal channel angular pressing of magnesium alloy AZ31. Mater Sci Eng A 410–411:324–327
Valiev RZ, Zhilyaev AP, Langdon TG (2013) Bulk nanostructured materials: fundamentals and applications. Wiley, New Jersey
Gubicza J, Máthis K, Hegedűs Z, Ribárik G, Tóth AL (2010) Inhomogeneous evolution of microstructure in AZ91 Mg-alloy during high temperature equal-channel angular pressing. J Alloy Compd 492:166–172
Zhilyaev AP, Langdon TG (2008) Using high-pressure torsion for metal processing: fundamentals and applications. Prog Mater Sci 53:893–979
Vander Voort GF (2004) Metals handbook: metallography and microstructures, vol 9. ASM International, Cleveland
Kawasaki M, Figueiredo RB, Langdon TG (2011) An investigation of hardness homogeneity throughout disks processed by high-pressure torsion. Acta Mater 59:308–316
Al-Zubaydi ASJ, Zhilyaev AP, Wang SC, Reed PAS (2015) Superplastic behaviour of AZ91 magnesium alloy processed by high-pressure torsion. Mater Sci Eng A 637:1–11
Máthis K, Gubicza J, Nam NH (2005) Microstructure and mechanical behavior of AZ91 Mg alloy processed by equal channel angular pressing. J Alloy Compd 394:194–199
Hohenwarter A, Bachmaier A, Gludovatz B, Scheriau S, Pippan R (2009) Technical parameters affecting grain refinement by high pressure torsion. Int J Mater Res 100:1653–1661
Myshlyaev MM, McQueen HJ, Mwembela A, Konopleva E (2002) Twinning, dynamic recovery and recrystallization in hot worked Mg–Al–Zn alloy. Mater Sci Eng A 337:121–133
del Valle JA, Pérez-Prado MT, Ruano OA (2003) Texture evolution during large-strain hot rolling of the Mg AZ61 alloy. Mater Sci Eng A 355:68–78
Al-Samman T, Gottstein G (2008) Room temperature formability of a magnesium AZ31 alloy: examining the role of texture on the deformation mechanisms. Mater Sci Eng A 488:406–414
Zhao YH, Liao XZ, Zhu YT, Horita Z, Langdon TG (2005) Influence of stacking fault energy on nanostructure formation under high pressure torsion. Mater Sci Eng A 410–411:188–193
Kawasaki M, Figueiredo RB, Huang Y, Langdon TG (2014) Interpretation of hardness evolution in metals processed by high-pressure torsion. J Mater Sci 49:6586–6596. doi:10.1007/s10853-014-8262-8
Stráská J, Janeček M, Gubicza J, Krajňák T, Yoon EY, Kim HS (2015) Evolution of microstructure and hardness in AZ31 alloy processed by high pressure torsion. Mater Sci Eng A 625:98–106
Harai Y, Kai M, Kaneko K, Horita Z, Langdon TG (2008) Microstructural and mechanical characteristics of AZ61 magnesium alloy processed by high-pressure torsion. Mater Trans 49:76–83
Matsubara K, Miyahara Y, Horita Z, Langdon TG (2003) Developing superplasticity in a magnesium alloy through a combination of extrusion and ECAP. Acta Mater 51:3073–3084
Braszczyńska-Malik KN, Froyen L (2005) Microstructure of AZ91 alloy deformed by equal channel angular pressing. Int J Mater Res (former: Zeitschrift für Metallkunde) 96:913–917
Braszczyńska-Malik KN (2009) Spherical shape of γ-Mg17Al12 precipitates in AZ91 magnesium alloy processed by equal-channel angular pressing. J Alloy Compd 487:263–268
Zhao Z, Chen Q, Hu C, Shu D (2009) Microstructure and mechanical properties of SPD-processed an as-cast AZ91D + Y magnesium alloy by equal channel angular extrusion and multi-axial forging. Mater Des 30:4557–4561
Cavaliere P, De Marco PP (2007) Superplastic behaviour of friction stir processed AZ91 magnesium alloy produced by high pressure die cast. J Mater Process Technol 184:77–83
Pérez-Prado MT, Valle D, Ruano OA (2004) Grain refinement of Mg–Al–Zn alloys via accumulative roll bonding. Scr Mater 51:1093–1097
Kim WJ, Hong SI, Kim YH (2012) Enhancement of the strain hardening ability in ultrafine grained Mg alloys with high strength. Scr Mater 67:689–692
Figueiredo RB, Pereira PHR, Aguilar MTP, Cetlin PR, Langdon TG (2012) Using finite element modeling to examine the temperature distribution in quasi-constrained high-pressure torsion. Acta Mater 60:3190–3198
Edalati K, Miresmaeili R, Horita Z, Kanayama H, Pippan R (2011) Significance of temperature increase in processing by high-pressure torsion. Mater Sci Eng A 528:7301–7305
Al-Zubaydi A, Figueiredo RB, Huang Y, Langdon TG (2013) Structural and hardness inhomogeneities in Mg-Al-Zn alloys processed by high-pressure torsion. J Mater Sci 48:4661–4670. doi:10.1007/s10853-013-7176-1
Zhilyaev AP, Nurislamova GV, Kim B-K, Baró MD, Szpunar JA, Langdon TG (2003) Experimental parameters influencing grain refinement and microstructural evolution during high-pressure torsion. Acta Mater 51:753–765
Zhilyaev AP, Oh-ishi K, Langdon TG, McNelley TR (2005) Microstructural evolution in commercial purity aluminum during high-pressure torsion. Mater Sci Eng A 410–411:277–280
Zhilyaev AP, Lee S, Nurislamova GV, Valiev RZ, Langdon TG (2001) Microhardness and microstructural evolution in pure nickel during high-pressure torsion. Scr Mater 44:2753–2758
Vorhauer A, Pippan R (2004) On the homogeneity of deformation by high pressure torsion. Scr Mater 51:921–925
Huang Y, Kawasaki M, Langdon TG (2013) Influence of anvil alignment on shearing patterns in high-pressure torsion. Adv Eng Mater 15:1–755
Somekawa H, Hirai K, Watanabe H, Takigawa Y, Higashi K (2005) Dislocation creep behavior in Mg–Al–Zn alloys. Mater Sci Eng A 407:53–61
Tahreen N, Chen DL, Nouri M, Li DY (2014) Effects of aluminum content and strain rate on strain hardening behavior of cast magnesium alloys during compression. Mater Sci Eng A 594:235–245
Figueiredo RB, Aguilar MTP, Cetlin PR, Langdon TG (2012) Analysis of plastic flow during high-pressure torsion. J Mater Sci 47:7807–7814. doi:10.1007/s10853-012-6506-z
Kawasaki M, Figueiredo RB, Langdon TG (2012) Twenty-five years of severe plastic deformation: recent developments in evaluating the degree of homogeneity through the thickness of disks processed by high-pressure torsion. J Mater Sci 47:7719–7725. doi:10.1007/s10853-012-6507-y
Furukawa M, Horita Z, Nemoto M, Valiev RZ, Langdon TG (1996) Microhardness measurements and the Hall-Petch relationship in an Al-Mg alloy with submicrometer grain size. Acta Mater 44:4619–4629
Xu J, Shirooyeh M, Wongsa-Ngam J, Shan D, Guo B, Langdon TG (2013) Hardness homogeneity and micro-tensile behavior in a magnesium AZ31 alloy processed by equal-channel angular pressing. Mater Sci Eng A 586:108–114
Chang S-Y, Lee S-W, Kang KM, Kamado S, Kojima Y (2004) Improvement of mechanical characteristics in severely plastic-deformed Mg alloys. Mater Trans 45:488–492
Setman D, Schafler E, Korznikova E, Zehetbauer MJ (2008) The presence and nature of vacancy type defects in nanometals detained by severe plastic deformation. Mater Sci Eng A 493:116–122
Gubicza J, Dobatkin SV, Khosravi E, Kuznetsov AA, Lábár JL (2011) Microstructural stability of Cu processed by different routes of severe plastic deformation. Mater Sci Eng A 528:1828–1832
Acknowledgements
One of the authors (Ahmed S. J. Al-Zubaydi) is grateful to The Higher Committee for Education Development (HCED) of the Government of Iraq for the provision of Ph.D. scholarship.
Funding
This work was supported in part by the Russian Science Foundation under Grant No. 14-29-00199 (APZ).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of Interest
The authors declare that they have no conflict of interest.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Al-Zubaydi, A.S.J., Zhilyaev, A.P., Wang, S.C. et al. Evolution of microstructure in AZ91 alloy processed by high-pressure torsion. J Mater Sci 51, 3380–3389 (2016). https://doi.org/10.1007/s10853-015-9652-2
Received: